WO2010071037A1 - 共役ジエン重合体の製造方法、ポリブタジエンおよびそれを用いたゴム組成物 - Google Patents
共役ジエン重合体の製造方法、ポリブタジエンおよびそれを用いたゴム組成物 Download PDFInfo
- Publication number
- WO2010071037A1 WO2010071037A1 PCT/JP2009/070406 JP2009070406W WO2010071037A1 WO 2010071037 A1 WO2010071037 A1 WO 2010071037A1 JP 2009070406 W JP2009070406 W JP 2009070406W WO 2010071037 A1 WO2010071037 A1 WO 2010071037A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polymerization
- yttrium
- added
- solution
- polybutadiene
- Prior art date
Abstract
Description
(1)25℃で測定した5重量%トルエン溶液粘度(Tcp)と100℃におけるム-ニ-粘度(ML1+4)との比(Tcp/ML1+4)が0.1~1.2
(2)シス-1,4構造含有率が80%以上、かつ1,2構造含有量が5%未満
(1)25℃で測定した5重量%トルエン溶液粘度(Tcp)と100℃におけるム-ニ-粘度(ML1+4)との比(Tcp/ML1+4)が0.1~1.0
(2)シス-1,4構造含有率が80%以上、かつ1,2構造含有率が5%未満
(3)GPC/MALLS法(ゲルろ過クロマトグラフィー/多角度レーザー光散乱検出法)により測定された絶対分子量と平均回転半径の関係において、300,000g/molおける分子の平均回転半径が30~20nm、かつ1,000,000g/molおける分子の平均回転半径が50~40nm
(1)不活性有機溶媒に(C)成分を添加し、(A)成分と(B)成分を任意の順序で添加する。
(2)不活性有機溶媒に(C)成分を添加し、上述した分子量調節剤を添加した後、(A)成分と(B)成分を任意の順序で添加する。
(3)不活性有機溶媒に(A)成分を添加し、(C)成分と上述した分子量調節剤を任意の順序で添加した後、(B)成分を添加する。
(4)不活性有機溶媒中に(B)成分を添加し、(C)成分と上述した分子量調節剤を任意の順序で添加した後、(A)成分を添加する。
(5)不活性有機溶媒中に(C)成分を添加し、(A)成分と(B)成分を任意の順序で添加した後、上述した分子量調節剤を添加する。
(1)ムーニー粘度(ML1+4):JIS K 6300に準じて100℃で測定した。
(2)5重量%トルエン溶液粘度(Tcp):25℃における5重量%トルエン溶液の粘度を測定した。
(3)ミクロ構造:赤外吸収スペクトル分析によって行った。シス740cm-1、トランス967cm-1、ビニル910cm-1の吸収強度比からミクロ構造を算出した。
(4)固有粘度([η]):トルエン溶液を使用して30℃で測定した。
(5)重量平均分子量(Mw)、数平均分子量(Mn)、および分子量分布(Mw/Mn):40℃でテトラヒドロフランを溶媒としたGPC(カラム:Shodex KF-805L×2本)により測定した重合体の溶出曲線より、標準ポリスチレン換算の値として求めた。
(6)GPC/MALLS法(ゲルろ過クロマトグラフィー/多角度レーザー光散乱検出法)による絶対分子量と平均回転半径の測定:40℃でテトラヒドロフランを溶媒としたGPC(カラム:TSKgel GMHHR-H、およびTSKgel GMHXL各1本)において、多角度光散乱検出器としてWyatt Technology製DAWN EOSを用いておこなった。
(7)貯蔵弾性率(G’)のひずみ依存性(ペイン効果):アルファーテクノロジー社製のゴム加工性解析装置RPA-2000を使い、120℃、1Hzの周波数の条件で動的ひずみ分析を行った。ペイン効果は、ひずみ0.5%時のG’とひずみ10%時のG’との差ΔG’を比較例7(BR150L)を100とした指数で表示した。ΔG’が小さいほど、補強剤の分散性が良好であることを示す。
(8)硬度:JIS K6253に規定されている測定法に従って測定した。
(9)引張強度:JIS K6251に規定されている測定法に従って測定した。同時に100%および300%伸長時の引張応力(M100およびM300)も測定した。
(10)発熱特性:JIS K6265に準拠し、グッドリッチフレクソメーターを用い、100℃、歪み0.175インチ、荷重55ポンド、振動数毎分1,800回の条件で発熱量(ΔT)と永久歪み(PS)を測定した。
(11)耐摩耗性:JIS K6264規定されているランボーン摩耗測定法に従って、スリップ率60%で測定し、比較例7(BR150L)を100とした指数で表示した。
(12)低ロス性:GABO社製固体粘弾性測定装置を用いて、温度範囲-120℃~100℃、周波数10Hz、動的歪み0.3%で測定し、50℃における損失正接(tanδ)を算出した。tanδが小さいほど低ロス性に優れることを示す。
内容量1.5Lのオートクレーブの内部を窒素置換し、トルエン390ml及びブタジエン210mlからなる溶液を仕込み、溶液の温度を30℃とした後、トリエチルアルミニウム(TEA)のシクロヘキサン溶液(2mol/L)1.5mlを添加し、毎分500回転で3分間攪拌した。次に、イットリウム(III)トリス(2,2,6,6-テトラメチル-3,5-ヘプタンジオエート)のトルエン溶液(0.05mol/L)0.15mlを添加して40℃まで加温した。2分間攪拌したのち、トリフェニルカルベニウムテトラキス(ペンタフルオロフェニル)ボレートのトルエン溶液(0.004mol/L)3.75mlを添加し、80℃まで昇温した。80℃で15分重合後、老化防止剤を含むエタノール溶液3mlを添加し、重合を停止した。オートクレーブの内部を放圧した後、重合液をエタノールに投入し、ポリブタジエンを回収した。次いで回収したポリブタジエンを80℃で3時間真空乾燥した。重合結果を表1に示した。
内容量1.5Lのオートクレーブの内部を窒素置換し、トルエン650ml及びブタジエン350mlからなる溶液を仕込み、溶液の温度を30℃とした後、トリエチルアルミニウム(TEA)のシクロヘキサン溶液(2mol/L)5.63mlを添加し、毎分500回転で3分間攪拌した。次に、イットリウム(III)トリス(2,2,6,6-テトラメチル-3,5-ヘプタンジオエート)のトルエン溶液(0.05mol/L)0.25mlを添加して40℃まで加温した。2分間攪拌したのち、トリフェニルカルベニウムテトラキス(ペンタフルオロフェニル)ボレートのトルエン溶液(0.004mol/L)6.25mlを添加し、80℃まで昇温した。80℃で15分重合後、老化防止剤を含むエタノール溶液10mlを添加し、重合を停止した。オートクレーブの内部を放圧した後、重合液をエタノールに投入し、ポリブタジエンを回収した。次いで回収したポリブタジエンを80℃で3時間真空乾燥した。重合結果を表1に示した。
トリエチルアルミニウム(TEA)のシクロヘキサン溶液(2mol/L)を6.25mlとしたほかは、実施例1と同様に重合を行った。重合結果を表1に示した。
トリエチルアルミニウム(TEA)のシクロヘキサン溶液(2mol/L)を6.88mlとしたほかは、実施例1と同様に重合を行った。重合結果を表1に示した。
内容量1.5Lのオートクレーブの内部を窒素置換し、トルエン390ml及びブタジエン210mlからなる溶液を仕込み、溶液の温度を30℃とした後、トリエチルアルミニウム(TEA)のシクロヘキサン溶液(2mol/L)3.0mlを添加し、毎分500回転で3分間攪拌した。次に、イットリウム(III)トリス(2,2,6,6-テトラメチル-3,5-ヘプタンジオエート)のトルエン溶液(0.05mol/L)0.15mlを添加して40℃まで加温した。2分間攪拌したのち、トリフェニルカルベニウムテトラキス(ペンタフルオロフェニル)ボレートのトルエン溶液(0.004mol/L)3.75mlを添加し、60℃まで昇温した。60℃で25分重合後、老化防止剤を含むエタノール溶液3mlを添加し、重合を停止した。オートクレーブの内部を放圧した後、重合液をエタノールに投入し、ポリブタジエンを回収した。次いで回収したポリブタジエンを80℃で3時間真空乾燥した。重合結果を表1に示した。
トリエチルアルミニウム(TEA)のシクロヘキサン溶液(2mol/L)を3.75mlとしたほかは、実施例5と同様に重合を行った。重合結果を表1に示した。
内容量1.5Lのオートクレーブの内部を窒素置換し、トルエン390ml及びブタジエン210mlからなる溶液を仕込んだ。次いで水素ガス0.04MPa/cm2を添加した。溶液の温度を30℃とした後、トリエチルアルミニウム(TEA)のシクロヘキサン溶液(2mol/L)1.5mlを添加し、毎分500回転で3分間攪拌した。次に、イットリウム(III)トリス(2,2,6,6-テトラメチル-3,5-ヘプタンジオエート)のトルエン溶液(0.05mol/L)0.15mlを添加して40℃まで加温した。2分間攪拌したのち、トリフェニルカルベニウムテトラキス(ペンタフルオロフェニル)ボレートのトルエン溶液(0.004mol/L)3.75mlを添加し、60℃まで昇温した。60℃で25分間重合後、老化防止剤を含むエタノール溶液3mlを添加し、重合を停止した。オートクレーブの内部を放圧した後、重合液にエタノールを投入し、ポリブタジエンを回収した。次いで回収したポリブタジエンを80℃で3時間真空乾燥した。重合結果を表1に示した。
水素ガスの圧力を0.06MPa/cm2としたほかは、実施例7と同様に重合を行った。重合結果を表1に示した。
水素ガスの圧力を0.08MPa/cm2としたほかは、実施例7と同様に重合を行った。重合結果を表1に示した。
内容量1.5Lのオートクレーブの内部を窒素置換し、トルエン390ml及びブタジエン210mlからなる溶液を仕込み、溶液の温度を30℃とした後、トリエチルアルミニウム(TEA)のシクロヘキサン溶液(2mol/L)1.5mlを添加し、毎分500回転で3分間攪拌した。次に、イットリウム(III)トリス(2,2,6,6-テトラメチル-3,5-ヘプタンジオエート)のトルエン溶液(0.05mol/L)0.15mlを添加して40℃まで加温した。2分間攪拌したのち、トリフェニルカルベニウムテトラキス(ペンタフルオロフェニル)ボレートのトルエン溶液(0.004mol/L)3.75mlを添加して重合を開始した。40℃で15分重合後、老化防止剤を含むエタノール溶液3mlを添加し、重合を停止した。重合液にエタノールを投入した後、オートクレーブの内部を放圧し、ポリブタジエンを回収した。次いで回収したポリブタジエンを80℃で3時間真空乾燥した。重合結果を表1に示した。
内容量1.5Lのオートクレーブの内部を窒素置換し、トルエン390ml及びブタジエン210mlからなる溶液を仕込み、溶液の温度を30℃とした後、トリエチルアルミニウム(TEA)のシクロヘキサン溶液(2mol/L)4.0mlを添加し、毎分500回転で3分間攪拌した。次に、イットリウム(III)トリス(2,2,6,6-テトラメチル-3,5-ヘプタンジオエート)のトルエン溶液(0.05mol/L)0.8mlを添加して40℃まで加温した。2分間攪拌したのち、トリフェニルカルベニウムテトラキス(ペンタフルオロフェニル)ボレートのトルエン溶液(0.43mol/L)0.185mlを添加して重合を開始した。40℃で30分重合後、老化防止剤を含むエタノール溶液3mlを添加し、重合を停止した。重合液にエタノールを投入した後、オートクレーブの内部を放圧し、ポリブタジエンを回収した。次いで回収したポリブタジエンを80℃で3時間真空乾燥した。重合結果を表1に示した。
内容量1.5Lのオートクレーブの内部を窒素置換し、トルエン390ml及びブタジエン210mlからなる溶液を仕込んだ。次いで水素ガス0.06MPa/cm2を添加した。溶液の温度を30℃とした後、トリエチルアルミニウム(TEA)のシクロヘキサン溶液(2mol/L)1.5mlを添加し、毎分500回転で3分間攪拌した。次に、イットリウム(III)トリス(2,2,6,6-テトラメチル-3,5-ヘプタンジオエート)のトルエン溶液(0.05mol/L)0.15mlを添加して40℃まで加温した。2分間攪拌したのち、トリフェニルカルベニウムテトラキス(ペンタフルオロフェニル)ボレートのトルエン溶液(0.004mol/L)3.75mlを添加し、60℃まで昇温した。60℃で25分間重合後、老化防止剤を含むエタノール溶液3mlを添加し、重合を停止した。オートクレーブの内部を放圧した後、重合液にエタノールを投入し、ポリブタジエンを回収した。次いで回収したポリブタジエンを80℃で3時間真空乾燥した。重合結果を表2に示した。
水素ガスの圧力を0.04MPa/cm2としたほかは、実施例10と同様に重合を行った。重合結果を表2に示した。
水素ガスの圧力を0.08MPa/cm2としたほかは、実施例10と同様に重合を行った。重合結果を表2に示した。
内容量1.5Lのオートクレーブの内部を窒素置換し、トルエン390ml及びブタジエン210mlからなる溶液を仕込んだ。次いで水素ガス0.06MPa/cm2を添加した。溶液の温度を30℃とした後、トリエチルアルミニウム(TEA)のシクロヘキサン溶液(2mol/L)1.5mlを添加し、毎分500回転で3分間攪拌した。次に、イットリウム(III)トリス(2,2,6,6-テトラメチル-3,5-ヘプタンジオエート)のトルエン溶液(0.05mol/L)0.15mlを添加して40℃まで加温した。2分間攪拌したのち、トリフェニルカルベニウムテトラキス(ペンタフルオロフェニル)ボレートのトルエン溶液(0.004mol/L)3.75mlを添加し、80℃まで昇温した。80℃で15分間重合後、老化防止剤を含むエタノール溶液3mlを添加し、重合を停止した。オートクレーブの内部を放圧した後、重合液にエタノールを投入し、ポリブタジエンを回収した。次いで回収したポリブタジエンを80℃で3時間真空乾燥した。重合結果を表2に示した。
水素ガスの圧力を0.04MPa/cm2としたほかは、実施例13と同様に重合を行った。重合結果を表2に示した。
水素ガスの圧力を0.08MPa/cm2としたほかは、実施例13と同様に重合を行った。重合結果を表2に示した。
内容量1.5Lのオートクレーブの内部を窒素置換し、トルエン390ml及びブタジエン210mlからなる溶液を仕込んだ。次いで水素ガス0.08MPa/cm2を添加した。溶液の温度を30℃とした後、トリエチルアルミニウム(TEA)のシクロヘキサン溶液(2mol/L)1.25mlを添加し、毎分500回転で3分間攪拌した。次に、イットリウム(III)トリス(2,2,6,6-テトラメチル-3,5-ヘプタンジオエート)のトルエン溶液(0.05mol/L)0.2mlを添加して40℃まで加温した。2分間攪拌したのち、トリフェニルカルベニウムテトラキス(ペンタフルオロフェニル)ボレートのトルエン溶液(0.004mol/L)5.0mlを添加し、80℃まで昇温した。80℃で15分間重合後、老化防止剤を含むエタノール溶液3mlを添加し、重合を停止した。オートクレーブの内部を放圧した後、重合液にエタノールを投入し、ポリブタジエンを回収した。次いで回収したポリブタジエンを80℃で3時間真空乾燥した。重合結果を表2に示した。
内容量1.5Lのオートクレーブの内部を窒素置換し、トルエン390ml及びブタジエン210mlからなる溶液を仕込んだ。次いで水素ガス0.08MPa/cm2を添加した。溶液の温度を30℃とした後、トリエチルアルミニウム(TEA)のシクロヘキサン溶液(2mol/L)1.0mlを添加し、毎分500回転で3分間攪拌した。次に、イットリウム(III)トリス(2,2,6,6-テトラメチル-3,5-ヘプタンジオエート)のトルエン溶液(0.05mol/L)0.3mlを添加して40℃まで加温した。2分間攪拌したのち、トリフェニルカルベニウムテトラキス(ペンタフルオロフェニル)ボレートのトルエン溶液(0.43mol/L)0.07mlを添加し、80℃まで昇温した。80℃で15分間重合後、老化防止剤を含むエタノール溶液3mlを添加し、重合を停止した。オートクレーブの内部を放圧した後、重合液にエタノールを投入し、ポリブタジエンを回収した。次いで回収したポリブタジエンを80℃で3時間真空乾燥した。重合結果を表2に示した。
水素ガスの圧力を0.06MPa/cm2としたほかは、実施例16と同様に重合を行った。重合結果を表2に示した。
内容量1.5Lのオートクレーブの内部を窒素置換し、トルエン390ml及びブタジエン210mlからなる溶液を仕込んだ。次いで水素ガス0.08MPa/cm2を添加した。溶液の温度を30℃とした後、トリエチルアルミニウム(TEA)のシクロヘキサン溶液(2mol/L)1.25mlを添加し、毎分500回転で3分間攪拌した。次に、イットリウム(III)トリス(2,2,6,6-テトラメチル-3,5-ヘプタンジオエート)のトルエン溶液(0.05mol/L)0.2mlを添加して、30℃で30分間攪拌したのち、40℃まで加温した。2分間攪拌したのち、トリフェニルカルベニウムテトラキス(ペンタフルオロフェニル)ボレートのトルエン溶液(0.004mol/L)5.0mlを添加し、80℃まで昇温した。80℃で15分間重合後、老化防止剤を含むエタノール溶液3mlを添加し、重合を停止した。オートクレーブの内部を放圧した後、重合液にエタノールを投入し、ポリブタジエンを回収した。次いで回収したポリブタジエンを80℃で3時間真空乾燥した。重合結果を表2に示した。
内容量1.5Lのオートクレーブの内部を窒素置換し、トルエン390ml及びブタジエン210mlからなる溶液を仕込んだ。次いで水素ガス0.06MPa/cm2を添加した。溶液の温度を30℃とした後、トリエチルアルミニウム(TEA)のシクロヘキサン溶液(2mol/L)1.5mlを添加し、毎分500回転で3分間攪拌した。次に、イットリウム(III)トリス(2,2,6,6-テトラメチル-3,5-ヘプタンジオエート)のトルエン溶液(0.05mol/L)0.1mlを添加して40℃まで加温した。2分間攪拌したのち、トリフェニルカルベニウムテトラキス(ペンタフルオロフェニル)ボレートのトルエン溶液(0.004mol/L)2.5mlを添加し、80℃まで昇温した。80℃で15分間重合後、老化防止剤を含むエタノール溶液3mlを添加し、重合を停止した。オートクレーブの内部を放圧した後、重合液にエタノールを投入し、ポリブタジエンを回収した。次いで回収したポリブタジエンを80℃で3時間真空乾燥した。重合結果を表2に示した。
内容量1.5Lのオートクレーブの内部を窒素置換し、トルエン300ml及びブタジエン300mlからなる溶液を仕込んだ。次いで水素ガス0.06MPa/cm2を添加した。溶液の温度を30℃とした後、トリエチルアルミニウム(TEA)のシクロヘキサン溶液(2mol/L)1.5mlを添加し、毎分500回転で3分間攪拌した。次に、イットリウム(III)トリス(2,2,6,6-テトラメチル-3,5-ヘプタンジオエート)のトルエン溶液(0.05mol/L)0.15mlを添加して40℃まで加温した。2分間攪拌したのち、トリフェニルカルベニウムテトラキス(ペンタフルオロフェニル)ボレートのトルエン溶液(0.004mol/L)3.75mlを添加し、80℃まで昇温した。80℃で15分間重合後、老化防止剤を含むエタノール溶液3mlを添加し、重合を停止した。オートクレーブの内部を放圧した後、重合液にエタノールを投入し、ポリブタジエンを回収した。次いで回収したポリブタジエンを80℃で3時間真空乾燥した。重合結果を表2に示した。
トリエチルアルミニウム(TEA)のシクロヘキサン溶液(2mol/L)を2.25mlとしたほかは、実施例21と同様に重合を行った。重合結果を表2に示した。
トルエンを350ml及びブタジエンを250mlとしたほかは、実施例21と同様に重合を行った。重合結果を表2に示した。
水素ガスの圧力を0.07MPa/cm2としたほかは、実施例21と同様に重合を行った。重合結果を表2に示した。
内容量1.5Lのオートクレーブの内部を窒素置換し、トルエン350ml及びブタジエン250mlからなる溶液を仕込んだ。溶液の温度を30℃とした後、トリエチルアルミニウム(TEA)のシクロヘキサン溶液(2mol/L)1.5mlを添加し、毎分500回転で3分間攪拌した。次に、イットリウム(III)トリス(2,2,6,6-テトラメチル-3,5-ヘプタンジオエート)のトルエン溶液(0.05mol/L)0.15mlを添加して40℃まで加温した。2分間攪拌したのち、トリフェニルカルベニウムテトラキス(ペンタフルオロフェニル)ボレートのトルエン溶液(0.004mol/L)3.75mlを添加し、80℃まで昇温した。80℃で7.5分間重合した時点で、水素ガス0.08MPa/cm2を添加し、さらに7.5分間重合を行った。老化防止剤を含むエタノール溶液3mlを添加し、重合を停止した。オートクレーブの内部を放圧した後、重合液にエタノールを投入し、ポリブタジエンを回収した。次いで回収したポリブタジエンを80℃で3時間真空乾燥した。重合結果を表2に示した。
水素ガスの圧力を0.06MPa/cm2としたほかは、実施例25と同様に重合を行った。重合結果を表2に示した。
水素ガスの添加時間を重合開始から5分後とし、添加後の重合時間を10分間としたほかは、実施例25と同様に重合を行った。重合結果を表2に示した。
水素ガスの添加時間を重合開始から2.5分後とし、添加後の重合時間を12.5分間としたほかは、実施例25と同様に重合を行った。重合結果を表2に示した。
水素ガスの添加時間を重合開始から4分後とし、添加後の重合時間を11分間としたほかは、実施例25と同様に重合を行った。重合結果を表2に示した。
内容量1.5Lのオートクレーブの内部を窒素置換し、トルエン580ml及びブタジエン420mlからなる溶液を仕込んだ。次いで水素ガス0.1MPa/cm2を添加した。溶液の温度を30℃とした後、トリエチルアルミニウム(TEA)のシクロヘキサン溶液(2mol/L)1.5mlを添加し、毎分500回転で3分間攪拌した。次に、イットリウム(III)トリス(2,2,6,6-テトラメチル-3,5-ヘプタンジオエート)のトルエン溶液(0.05mol/L)0.25mlを添加して40℃まで加温した。2分間攪拌したのち、トリフェニルカルベニウムテトラキス(ペンタフルオロフェニル)ボレートのトルエン溶液(0.43mol/L)0.06mlを添加し、80℃まで昇温した。80℃で15分間重合後、老化防止剤を含むエタノール溶液5mlを添加し、重合を停止した。オートクレーブの内部を放圧した後、重合液を取り出し、ポリブタジエンを回収した。次いで回収したポリブタジエンを80℃で3時間真空乾燥した。重合結果を表2に示した。
水素ガスの圧力を0.15MPa/cm2としたほかは、実施例30と同様に重合を行った。重合結果を表2に示した。
内容量1.5Lのオートクレーブの内部を窒素置換し、トルエン390ml及びブタジエン210mlからなる溶液を仕込んだ。次いで水素ガス0.03MPa/cm2を添加した。溶液の温度を30℃とした後、トリエチルアルミニウム(TEA)のシクロヘキサン溶液(2mol/L)1.25mlを添加し、毎分500回転で3分間攪拌した。次に、イットリウム(III)トリス(2,2,6,6-テトラメチル-3,5-ヘプタンジオエート)のトルエン溶液(0.05mol/L)0.15mlを添加して40℃まで加温した。2分間攪拌したのち、トリフェニルカルベニウムテトラキス(ペンタフルオロフェニル)ボレートのトルエン溶液(0.004mol/L)3.75mlを添加し、60℃まで昇温した。60℃で30分間重合後、老化防止剤を含むエタノール溶液3mlを添加し、重合を停止した。オートクレーブの内部を放圧した後、重合液にエタノールを投入し、ポリブタジエンを回収した。次いで回収したポリブタジエンを80℃で3時間真空乾燥した。重合結果を表2に示した。また、GPC/MALLSによる測定結果を表2に示した。
内容量1.5Lのオートクレーブの内部を窒素置換し、トルエン390ml及びブタジエン210mlからなる溶液を仕込んだ。次いで水素ガス0.03MPa/cm2を添加した。溶液の温度を30℃とした後、トリエチルアルミニウム(TEA)のシクロヘキサン溶液(2mol/L)1.25mlを添加し、毎分500回転で3分間攪拌した。次に、イットリウム(III)トリス(2,2,6,6-テトラメチル-3,5-ヘプタンジオエート)のトルエン溶液(0.05mol/L)0.15mlを添加して40℃まで加温した。2分間攪拌したのち、トリフェニルカルベニウムテトラキス(ペンタフルオロフェニル)ボレートのトルエン溶液(0.004mol/L)3.75mlを添加し、80℃まで昇温した。80℃で15分間重合後、老化防止剤を含むエタノール溶液3mlを添加し、重合を停止した。オートクレーブの内部を放圧した後、重合液にエタノールを投入し、ポリブタジエンを回収した。次いで回収したポリブタジエンを80℃で3時間真空乾燥した。重合結果を表2に示した。また、GPC/MALLSによる測定結果を表2に示した。
内容量1.5Lのオートクレーブの内部を窒素置換し、トルエン390ml及びブタジエン210mlからなる溶液を仕込んだ。次いで水素ガス0.04MPa/cm2を添加した。溶液の温度を30℃とした後、トリエチルアルミニウム(TEA)のシクロヘキサン溶液(2mol/L)1.5mlを添加し、毎分500回転で3分間攪拌した。次に、イットリウム(III)トリス(2,2,6,6-テトラメチル-3,5-ヘプタンジオエート)のトルエン溶液(0.05mol/L)0.6mlを添加して40℃まで加温した。2分間攪拌したのち、トリフェニルカルベニウムテトラキス(ペンタフルオロフェニル)ボレートのトルエン溶液(0.43mol/L)0.14mlを添加した。40℃で25分間重合後、老化防止剤を含むエタノール溶液3mlを添加し、重合を停止した。オートクレーブの内部を放圧した後、重合液にエタノールを投入し、ポリブタジエンを回収した。次いで回収したポリブタジエンを80℃で3時間真空乾燥した。重合結果を表2に示した。
水素ガスの圧力を0.06MPa/cm2としたほかは、比較例3と同様に重合を行った。重合結果を表2に示した。
宇部興産株式会社製ポリブタジエンゴム BR150Lについて、GPC/MALLSにより絶対分子量および平均回転半径の測定を行った。測定結果を表3に示した。
宇部興産株式会社製ポリブタジエンゴム BR150Bについて、GPC/MALLSにより絶対分子量および平均回転半径の測定を行った。測定結果を表3に示した。
実施例32と同様に重合を行って得られたポリブタジエンを用いて、以下に示す配合表により硫黄と加硫促進剤以外をバンバリーミキサー中で混合する一次配合を行い、次に、硫黄および加硫促進剤をロールで混合する二次配合を行なった。得られた配合ゴムを150℃で15分間プレス加硫して加硫物を得た。各物性の測定結果を表4に示した。
実施例32と同様に重合を行って得られたポリブタジエンの代わりに、宇部興産株式会社製ポリブタジエンゴム BR150Lを用いた以外は実施例34と同様に行った。各物性の測定結果を表4に示した。
実施例32と同様に重合を行って得られたポリブタジエンの代わりに、宇部興産株式会社製ポリブタジエンゴム BR150Bを用いた以外は実施例34と同様に行った。各物性の測定結果を表4に示した。
Claims (7)
- (A)イットリウム化合物、(B)非配位性アニオンとカチオンとからなるイオン性化合物、および(C)有機アルミニウム化合物から得られる触媒の存在下、50~120℃で共役ジエンを重合することを特徴とする以下の特性を有する共役ジエン重合体の製造方法。
(1)25℃で測定した5重量%トルエン溶液粘度(Tcp)と100℃におけるム-ニ-粘度(ML1+4)との比(Tcp/ML1+4)が0.1~1.2
(2)シス-1,4構造含有率が80%以上、かつ1,2構造含有量が5%未満 - 共役ジエンが1,3-ブタジエンであることを特徴とする請求項1または2に記載の共役ジエン重合体の製造方法。
- 下記の特性(1)~(3)を有するポリブタジエン。
(1)25℃で測定した5重量%トルエン溶液粘度(Tcp)と100℃におけるム-ニ-粘度(ML1+4)との比(Tcp/ML1+4)が0.1~1.2
(2)シス-1,4構造含有率が80%以上、かつ1,2構造含有率が5%未満
(3)GPC/MALLS法(ゲルろ過クロマトグラフィー/多角度レーザー光散乱検出法)により測定された絶対分子量と分子の平均回転半径の関係において、300,000g/molおける分子の平均回転半径が30~20nm、かつ1,000,000g/molおける分子の平均回転半径が50~40nm - イットリウムを含有する触媒で1,3-ブタジエンを重合して得られること特徴とする請求項4に記載のポリブタジエン。
- 請求項4または5に記載のポリブタジエンを10重量%以上含有することを特徴とするゴム組成物。
- 請求項4または5に記載のポリブタジエンを10重量%以上含有し、補強剤として少なくともシリカを含有することを特徴とするタイヤ用ゴム組成物。