WO2009128459A1 - 永久磁石及び永久磁石の製造方法 - Google Patents
永久磁石及び永久磁石の製造方法 Download PDFInfo
- Publication number
- WO2009128459A1 WO2009128459A1 PCT/JP2009/057531 JP2009057531W WO2009128459A1 WO 2009128459 A1 WO2009128459 A1 WO 2009128459A1 JP 2009057531 W JP2009057531 W JP 2009057531W WO 2009128459 A1 WO2009128459 A1 WO 2009128459A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- magnet
- permanent magnet
- sintering
- metal element
- raw material
- Prior art date
Abstract
Description
(1)磁石原料を粒径が3μm以下の微粒子に粉砕する工程と、
前記粉砕された磁石原料と、高融点金属元素を含む有機化合物又は高融点セラミックのプリカーサが溶解された防錆オイルとを混合してスラリーを生成する工程と、
前記スラリーを圧縮成形することで成形体を形成する工程と、
前記成形体を焼結する工程と、により製造される永久磁石。
尚、「高融点金属元素を含む有機化合物」とは、炭素、窒素、酸素、硫黄、燐など、通常の有機化合物が有する原子を介して、イオン結合、及び又は、共有結合、及び又は、配位結合を形成した高融点金属原子、又は高融点金属イオンを含む化合物をいう。
(2)前記高融点金属元素を含む有機化合物又は高融点セラミックのプリカーサが、焼結後に前記磁石原料の粒界に偏在している(1)に記載の永久磁石。
(3)磁石原料を粒径が3μm以下の微粒子に粉砕する工程と、
前記粉砕された磁石原料と、高融点金属元素を含む有機化合物又は高融点セラミックのプリカーサが溶解された防錆オイルとを混合してスラリーを生成する工程と、
前記スラリーを圧縮成形することで成形体を形成する工程と、
前記成形体を焼結する工程と、
を含む永久磁石の製造方法。
先ず、図1~図3を用いて永久磁石1の構成について説明する。
本実施形態に係る永久磁石1はNd-Fe-B系磁石である。また、永久磁石1の焼結時における粒成長を抑制する為の高融点金属元素を含む有機化合物又は高融点セラミックのプリカーサが添加されている。尚、各成分の含有量はNd:27~30wt%、高融点金属元素を含む有機化合物に含まれる金属成分(又は高融点セラミックのプリカーサに含まれるセラミック成分):0.01~8wt%、B:1~2wt%、Fe(電解鉄):60~70wt%とする。また、本実施形態に係る永久磁石1は、図1に示すように円柱形状を備えるが、永久磁石1の形状は成形に用いるキャビティの形状によって変化する。図1は本実施形態に係る永久磁石1を示した全体図である。
その結果、図3に示すように磁石粒子の界面に高融点金属元素を含む有機化合物又は高融点セラミックのプリカーサが偏在化される。そして、この偏在化された高融点金属元素を含む有機化合物又は高融点セラミックのプリカーサにより、高温時に発生する粒界の移動が妨げられ、粒成長を抑制することができる。
また、本実施形態では湿式成形により成形された磁石粉末を適切な焼成条件で焼成すれば、前記したように高融点金属元素を含む有機化合物又は高融点セラミックのプリカーサが磁石粒子35内へと拡散浸透(固溶化)することを防止できる。ここで、高融点金属元素を含む有機化合物又は高融点セラミックのプリカーサが磁石粒子35内へと拡散浸透すると、その磁石の残留磁化(磁場の強さを0にしたときの磁化)が低下することが知られている。従って、本実施形態では、永久磁石1の残留磁化が低下することを防止できる。
尚、粒成長抑制層36は高融点金属元素を含む有機化合物又は高融点セラミックのプリカーサのみから構成される層である必要はなく、高融点金属元素を含む有機化合物又は高融点セラミックのプリカーサとNdとの混合体からなる層であっても良い。その場合には、Nd化合物を添加することによって、高融点金属元素を含む有機化合物又は高融点セラミックのプリカーサとNd化合物との混合体からなる層を形成する。その結果、Nd磁石粉末の焼結時の液相焼結を助長することができる。尚、添加するNd化合物としては、酢酸ネオジム水和物、ネオジム(III)アセチルアセトナート三水和物、2-エチルヘキサン酸ネオジム(III)、ネオジム(III)ヘキサフルオロアセチルアセトナート二水和物、ネオジムイソプロポキシド、リン酸ネオジニウム(III)n水和物、ネオジムトリフルオロアセチルアセトナート、トリフルオロメタンスルホン酸ネオジム等が望ましい。
次に、本実施形態に係る永久磁石1の製造方法について図4を用いて説明する。図4は本実施形態に係る永久磁石1の製造工程を示した説明図である。
また、溶解させる高融点金属元素を含む有機化合物又は高融点セラミックのプリカーサの量は特に制限されないが、磁石粉末に対して有機化合物に含まれる金属成分又は高融点セラミックのプリカーサに含まれるセラミック成分が0.01~8wt%となる量とするのが好ましい。
また、成形装置50には一対の磁界発生コイル55、56がキャビティ54の上下位置に配置されており、磁力線をキャビティ54に充填されたスラリー42に印加する。また、モールド51にはキャビティ54に開口するスラリー注入孔57が設けられている。
また、キャビティ54に磁場を印加しながらスラリーを注入し、注入途中又は注入終了後に、当初の磁場より強い磁場を印加して湿式成形しても良い。また、加圧方向に対して印加方向が垂直となるように磁界発生コイル55、56を配置しても良い。
また、混合した防錆オイル中に溶解された高融点金属元素を含む有機化合物又は高融点セラミックのプリカーサが、粉砕された磁石粒子の表面に被覆することによって、焼結時の磁石粒子の粒成長を抑制することができる。従って、焼結体の結晶粒径を3μm以下とし、永久磁石の磁気性能を向上させることが可能となる。
また、高融点金属元素を含む有機化合物又は高融点セラミックのプリカーサが、焼結後に磁石原料の粒界に偏在するので、磁石の残留磁化を低下させることなく焼結時の磁石粒子の粒成長を抑制することができる。
また、磁石粉末の粉砕条件、混練条件、焼結条件などは上記実施例に記載した条件に限られるものではない。
なお、本出願は、2008年4月15日付けで出願された日本特許出願(特願2008-105760)に基づいており、その全体が引用により援用される。
また、ここに引用されるすべての参照は全体として取り込まれる。
35 Nd磁石粒子
36 粒成長抑制層
42 スラリー
Claims (3)
- 磁石原料を粒径が3μm以下の微粒子に粉砕する工程と、
前記粉砕された磁石原料と、高融点金属元素を含む有機化合物又は高融点セラミックのプリカーサが溶解された防錆オイルとを混合してスラリーを生成する工程と、
前記スラリーを圧縮成形することで成形体を形成する工程と、
前記成形体を焼結する工程と、
により製造される永久磁石。 - 前記高融点金属元素を含む有機化合物又は高融点セラミックのプリカーサが、焼結後に前記磁石原料の粒界に偏在している請求項1に記載の永久磁石。
- 磁石原料を粒径が3μm以下の微粒子に粉砕する工程と、
前記粉砕された磁石原料と、高融点金属元素を含む有機化合物又は高融点セラミックのプリカーサが溶解された防錆オイルとを混合してスラリーを生成する工程と、
前記スラリーを圧縮成形することで成形体を形成する工程と、
前記成形体を焼結する工程と、
を含む永久磁石の製造方法。