WO2006134042A1 - Heissversiegelungsmasse für aluminium- und polyethylenterephthalatfolien gegen polypropylen- polyvinylchlorid- und polystyrolbehälter - Google Patents
Heissversiegelungsmasse für aluminium- und polyethylenterephthalatfolien gegen polypropylen- polyvinylchlorid- und polystyrolbehälter Download PDFInfo
- Publication number
- WO2006134042A1 WO2006134042A1 PCT/EP2006/062933 EP2006062933W WO2006134042A1 WO 2006134042 A1 WO2006134042 A1 WO 2006134042A1 EP 2006062933 W EP2006062933 W EP 2006062933W WO 2006134042 A1 WO2006134042 A1 WO 2006134042A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- weight
- polymer
- polymer type
- amount
- heat
- Prior art date
Abstract
Description
Claims