WO2006028198A1 - シリコーンゴム成形体およびその製造方法 - Google Patents
シリコーンゴム成形体およびその製造方法 Download PDFInfo
- Publication number
- WO2006028198A1 WO2006028198A1 PCT/JP2005/016577 JP2005016577W WO2006028198A1 WO 2006028198 A1 WO2006028198 A1 WO 2006028198A1 JP 2005016577 W JP2005016577 W JP 2005016577W WO 2006028198 A1 WO2006028198 A1 WO 2006028198A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- silicone rubber
- resin powder
- weight
- thermoplastic resin
- molded body
- Prior art date
Abstract
Description
Claims