WO2005015555A1 - 光学情報記録媒体及びその製造方法 - Google Patents
光学情報記録媒体及びその製造方法 Download PDFInfo
- Publication number
- WO2005015555A1 WO2005015555A1 PCT/JP2004/011239 JP2004011239W WO2005015555A1 WO 2005015555 A1 WO2005015555 A1 WO 2005015555A1 JP 2004011239 W JP2004011239 W JP 2004011239W WO 2005015555 A1 WO2005015555 A1 WO 2005015555A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- recording medium
- guide groove
- information recording
- optical information
- Prior art date
Abstract
Description
Claims