WO2004101678A1 - 熱伝導性材料用樹脂組成物および熱伝導性材料 - Google Patents
熱伝導性材料用樹脂組成物および熱伝導性材料 Download PDFInfo
- Publication number
- WO2004101678A1 WO2004101678A1 PCT/JP2004/007113 JP2004007113W WO2004101678A1 WO 2004101678 A1 WO2004101678 A1 WO 2004101678A1 JP 2004007113 W JP2004007113 W JP 2004007113W WO 2004101678 A1 WO2004101678 A1 WO 2004101678A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- resin composition
- conductive material
- polymer
- parts
- sheet
- Prior art date
Abstract
Description
Claims