WO2004086520A1 - ＺｎＯ系半導体素子およびその製造方法 - Google Patents

ＺｎＯ系半導体素子およびその製造方法 Download PDF

Info

Publication number
WO2004086520A1
WO2004086520A1 PCT/JP2003/016323 JP0316323W WO2004086520A1 WO 2004086520 A1 WO2004086520 A1 WO 2004086520A1 JP 0316323 W JP0316323 W JP 0316323W WO 2004086520 A1 WO2004086520 A1 WO 2004086520A1
Authority
WO
WIPO (PCT)
Prior art keywords
zno
layer
substrate
buffer layer
main surface
Prior art date
Application number
PCT/JP2003/016323
Other languages
English (en)
French (fr)
Inventor
Jun-Ya Ishizaki
Original Assignee
Shin-Etsu Handotai Co.,Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shin-Etsu Handotai Co.,Ltd. filed Critical Shin-Etsu Handotai Co.,Ltd.
Publication of WO2004086520A1 publication Critical patent/WO2004086520A1/ja

Abstract

基板として水熱合成法にて形成されたＺｎＯ単結晶基板Ｓを用いるとともに、該ＺｎＯ単結晶基板Ｓの主表面上に、エピタキシャル成長法にてＺｎＯ系化合物からなる素子層１１を形成させる。これにより、簡便に素子層の品質向上を可能とするとともに、コストの観点からも適したＺｎＯ系半導体素子およびその製造方法を提供する。

Description

明 細 書
Z η θ系半導体素子およびその製造方法 技術分野
本発明は、 Z η θ系半導体素子およびその製造方法に関する。 背景技術
近年の酸化物材料における薄膜ェピタキシャル成長技術の向上により、 Z n Oま たは Z η θを母物質とした Z η θ系化合物は、 発光ダイオードやレーザーなどの発 光素子、 トランジスタ素子といった半導体素子における素子層の構成材料として有 望視されている。 このような半導体素子を製造するにあたっては、 基板の主表面上 に Z η θ系化合物からなる素子層をェピタキシャル成長させる必要がある。 例えば C V T (Chemical Vapor Transport) 法にて製造されている Z n O単結晶基板は 製造コストに起因して安価なものではなく、 半導体素子のコスト高に繋がるので、 一般的にサファイア基板などの素子層とは異種の基板が用いられている (例えば、 特開 2 0 0 1— 6 8 4 8 5号公報） 。
しかしながら、 上記のように、 Z η θ系化合物からなる素子層をサファイア基板 といつた素子層とは異種の基板上にェピタキシャル成長させる場合、 これら基板と 素子層との間には必然的に格子不整合が発生してしまう。 そして、 この格子不整合 は過大であるため、 該格子不整合に起因した結晶欠陥、 ミスフィット転位や貫通転 位などの転位が素子層に誘起されやすい。 そのため、 これら結晶欠陥や転位の発生 を抑制させるための結晶成長条件の適正化が必要となり、 半導体素子の製造に係わ る製造条件の複雑化を招くとともに、 素子層の品質を向上させるにも自ずと限界が 生じてしまう。 そこで、 基板として Z η θ単結晶基板を用いればよいのだが、 上述のごとく、 C V T法にて製造される Z η θ単結晶基板は安価なものではなく、 半導体素子のコス ト高を考慮すると、 とても使用できるものではない。
上記問題を鑑みてなされたのが本発明であって、 本発明の課題は、 簡便に素子層 の品質向上を可能とするとともに、 コストの観点からも適した Z n O系半導体素子 および、 その製造方法を提供することを目的とする。 発明の開示
上記課題を解決するための本発明の Z n O系半導体素子は、
水熱合成法により形成された Z η θ単結晶基板の主表面上に、 ェピタキシャル成 長法にて Z η θ系化合物からなる素子層が形成されてなることを特徴とする。 上記本発明の Z η θ系半導体素子において、 Z n O系化合物からなる素子層は、 Z 11 O単結晶基板の主表面上に形成されてなる。 そのため、 これら基板と素子層と の間には、 従来のサファイア基板などを用いた場合に問題となった過大な格子不整 合は存在しない。 つまり、 該格子不整合に起因して素子層に誘起される結晶欠陥や 転位の発生を、 確実に抑制ないし防止することができる。 その結果、 素子層の品質 を簡便に効果的に向上させることが可能となる。 また、 本発明において用いられる Z η θ単結晶基板は、 水熱合成法にて形成されたものとされる。 水熱合成法とは、 単結晶育成すべき材料 （本発明では Z n O) を溶媒に混合し、 その混合液を降温過 程にて過飽和濃度以上の状態にすることで、 単結晶育成すべき材料を単結晶として 析出育成する合成法である。 この水熱合成法を採用することで、 従来の C V T法に て形成された Z n O単結晶基板より格段に安価な Z n O単結晶基板とすることがで きる。 例えば、 同一径、 同一膜厚のゥエーハで比較した場合、 水熱合成法にて形成 した Z η θ単結晶基板は、 C V T法にて形成したものに比べて、 コスト面にて 5 0 %〜 9 0 %程度もコストの削減化が可能となる。 このように、 水熱合成法により 形成された Z η θ単結晶基板を用いることで、 該 Z η θ単結晶基板の主表面上に形 成される Z n O系化合物からなる素子層の品質を簡便に効果的に向上させることが 可能となるとともに、 安価な半導体素子とすることが可能となる。
上述の素子層を構成する Z η θ系化合物としては、 具体的には、 Z n Oや、 Z n Oを母物質として Z n (亜鉛） サイトの一部を M g (マグネシウム) などで置換さ せたものや、 Z n Oにおける O (酸素） サイトの一部を S (硫黄） 、 S e (セレ ン） 、 T e (テルル） などで置換させたものなどを例示することができる。 ただし、 素子層の構成材料は、 半導体素子において求められる素子特性に応じて、 例えば、 発光素子であれば素子層にて得るべき発光波長などに応じて適宜選択されるもので ある。
本発明の Z η θ系半導体素子における素子層は、 ェピタキシャル成長法にて形成 されてなる Z n O系化合物からなるバッファ層を介して、 Z η θ単結晶基板の主表 面上に形成されてなることが望ましい。
上記のように、 水熱合成法にて形成された Z η θ単結晶基板を用いることで、 安 価な半導体素子とするとともに、 基板との格子不整合に起因した結晶欠陥や転位の 発生を効果的に抑制した品質に優れた素子層とすることが可能となる。 しかしなが ら、 Z η θ単結晶基板の主表面やその表面近傍には、 水熱合成法による Z 11 O単結 晶形成時に起因した界面不純物が過度に存在する場合がある。 この界面不純物が過 度に存在する場合、 その上にェピタキシャル成長させる層に結晶欠陥や転位が発生 しゃすくなる。 そこで、 特には、 素子層は、 ェピタキシャル成長法にて形成された Z η θ系化合物からなるバッファ層を介した形で、 Z η θ単結晶基板の主表面上に 形成されるのが望ましいと言える。 このようにバッファ層を形成することで、 Z n O単結晶基板の主表面やその表面近傍に界面不純物が過度に存在した場合にも、 該 界面不純物に伴う結晶欠陥や転位の層厚方向への成長をバッファ層内にて効果的に 抑止ないしは抑制させることが可能となり、 ひいては、 素子層の品質をさらに向上 させることを可能とする。 また、 このようにバッファ層を形成することで、 Z n O 単結晶基板の主表面に有機物やパーティクルが過度に付着した場合にも、 これら有 機物やパーティクルに伴う結晶欠陥や転位の層厚方向への成長をバッファ層内にて 効果的に抑止ないしは抑制させることが可能となる。 また、 水熱合成法にて成長さ せた Z η θ単結晶を基板に成形する際に施されるスライス加工などの切削加工に起 因する意図しない加工歪が、 表面歪の形にて基板表面に過大に存在する場合がある。 この表面歪が過大である場合、 その上にェピタキシャル成長させる層には結晶欠陥 や転位が発生しやすくなるが、 バッファ層を形成することで、 該表面歪が過度に存 在した場合にも、 該表面歪に伴う結晶欠陥や転位の層厚方向への成長をバッファ層 内にて効果的に抑止ないしは抑制させることが可能となる。
また、 Z η θ単結晶基板の主表面の平滑性について言えば、 より平滑性が高いほ ど、 その上にェピタキシャル成長させる層への結晶欠陥や転位の発生を抑制するこ とができ、 かつェピタキシャル成長が容易となる。 勿論、 平滑性が低い、 つまりは、 表面が過度に粗い状態であっても、 上記のようにバッファ層を形成することにより、 この平滑性に伴う結晶欠陥や転位の層厚方向への成長をバッファ層内にて効果的に 抑止ないし抑制させることは可能である。 しかしながら、 特には、 Z n O単結晶基 板の主表面の平滑性としては、 該平滑性の指標として J I S規格に基づく RM S
(Root Mean Square：二乗平均粗さ) を代表させた場合、 該 RM Sにて規定される 表面粗さが 2 n m以下とされるものが望ましい。 このように、 RM Sが 2 n m以下 とされる主表面の Z n O単結晶基板を用いることにより、 該主表面上にェピタキシ ャル成長させる層への結晶欠陥や転位の発生を効果的に抑制することができ、 ひい ては、 素子層の品質をより高めることが可能となる。 なお、 ここで規定される RM Sの下限値としては、 小さいほどより望ましいが、 例えば、 0 . 5 n m以上として おけば十分である。
上述のバッファ層を構成する Z η θ系化合物としては、 具体的には、 上述の素子 層と同様に、 ZnOや、 2110を母物質として211 (亜鉛） サイトの一部を Mg
(マグネシウム） などで置換させたものや、 Z nOにおける O (酸素） サイトの一 部を S (硫黄） 、 S e (セレン） 、 T e (テルル） などで置換させたものを例示す ることができる。 ただし、 バッファ層の構成材料としては、 この中でも、 Z nO単 結晶基板との間の格子不整合がより小さい、 Z ηθが特には好適であると言える。 また、 バッファ層の構成材料として Z ηθを採用することで、 混晶系において問題 とされる過度の組成揺らぎの発生をより確実に抑制することができる。
本発明の Z ηθ系半導体素子は、 例えば、 素子層が発光層部とされる。
本発明の Z ηθ系半導体素子としては、 発光ダイォードゃレーザーなどの発光素 子、 トランジスタ素子といった公知の半導体素子に適用可能であり、 その素子層に おける素子構造は特に限定されない。 つまり、 第一には、 Z nO単結晶基板の主表 面上に素子層がェピタキシャル成長法にて形成されてなる半導体素子に適用可能で ある。 その中でも特に限定するならば、 素子層が発光層部とされる発光素子である。 Z n Oは、 バンドギヤップエネルギーが 3. 4 e Vを有する直接遷移型の半導体で あり、 Z n Oまたは∑ n Oを母物質とした Z n O系化合物は、 青色から紫外域の発 光を可能とする発光層部の構成材料として特に有望視されている。 つまり、 Z nO 系化合物の材料特性に対して特に期待されている分野が、 発光素子なのである。 発 光層部としての素子層は、 その品質確保が必要とされている。
次に、 本発明の Z ηθ系半導体素子の製造方法は、
水熱合成法により形成された Z n O単結晶を基板として、 該基板の主表面上に、 ZnO系化合物からなる素子層をェピタキシャル成長させる素子層形成工程を有す ることを特徴とする。
上記本発明の製造方法は、 上述してきた本発明の Z ηθ系半導体素子の製造方法 である。 本発明の製造方法において用いる基板は、 水熱合成法により形成された Z ηθ単結晶である。 そして、 素子層形成工程にて、 この Z ηθ単結晶基板の主表面 上に、 Z η θ系化合物からなる素子層をェピタキシャル成長させる。 このように素 子層を形成することで、 基板との格子不整合に起因した結晶欠陥や転位の発生を簡 便に抑止ないし抑制することが可能となるとともに、 効果的に素子層の品質を向上 させることが可能となる。 使用する Z η θ単結晶基板は、 水熱合成法にて形成され た Z η θ単結晶をスライス加工などの切削加工を施すことにより得られるものであ るので、 コストの観点からも安価な半導体素子とすることが可能となる。
上曾己本発明の製造方法における素子層を構成する Z η θ系化合物としては、 具体 的には、 上述した本発明の Z η θ系半導体素子に係わるものと同様のものを用いる ことができる。 また、 素子層をェピタキシャル成長させる具体的な方法としては、 MO V P E (Metal Organic Vapor Phase Epitaxy) 法や、 MB E (Molecular
Beam Epitaxy) 法などの公知の気相ェピタキシャル成長法を用いることができる。 本発明の製造方法においては、 基板の主表面に対して、 酸化性ガス雰囲気下にて 表面熱処理を行う基板表面熱処理工程を有することが望ましい。
用いる基板の主表面もしくはその表面近傍においては、 上述したような界面不純 物が過度に存在する場合があり、 該界面不純物は結晶欠陥や転位の発生要因となる。 そこで、 基板表面熱処理工程にて、 基板の主表面に対して、 N 2 0、 N O、 C O、 H 20等の酸化性ガス雰囲気下にて表面熱処理を行う。 このような基板表面熱処理 工程を行うことで、 界面不純物を酸化物などの形にて基板外部に効果的に離脱させ ることができ、 基板の主表面もしくは表面近傍に存在する界面不純物の濃度を効果 的に減少させることができる。 また、 表面の平滑性を高める効果も期待できる。 そ の結果、 基板の主表面における表面状態を良好なものとすることができるので、 該 基板の主表面上に上記素子層形成工程にて素子層を形成する際に、 該素子層の品質 をさらに高めることが可能となる。
上記基板表面熱処理工程における表面熱処理の条件としては、 基板をなす Z η θ 単結晶における酸素が基板表面から外部に離脱するのを防止する目的もあり、 酸化 性ガス雰囲気下が必須とされるが、 それ以外における熱処理温度などは特には限定 されない。 勿論、 熱処理温度が高いほど、 界面不純物を基板外部に離脱させる効果 は向上する。 そこで、 熱処理温度について言えば、 特には、 4 0 0 °じ以上9 0 0で 以下とするのが望ましい。 熱処理温度を 4 0 0 °C以上とすることで、 より効果的に 界面不純物を基板外部に離脱させることが可能となる。 一方、 熱処理温度が 9 0 0 °Cを超えると、 基板をなす Z η θ単結晶における酸素が基板表面から外部に離脱 しゃすくなる。
本発明の製造方法においては、 基板として、 該基板の主表面の表面粗さが RM S にて 2 n m以下のものを用いることが望ましい。
上述のごとく、 基板の主表面における界面不純物に係わる表面状態は、 その上に 形成される素子層の品質に大きく影響を及ぼす。 また、 平滑性に係わる表面状態に 関しては、 基板の主表面の平滑性がより高いほど、 その上に形成される素子層への 結晶欠陥や転位の発生を抑制することができる。 そこで、 基板として、 その主表面 の表面粗さが RM Sにて 2 n m以下のものを用いることが望ましい。 このように、 RM Sが 2 n m以下とされる主表面の基板を用いることで、 該主表面上に形成され る素子層の品質をさらに高めることができる。 ここで、 RM Sにて規定される表面 粗さの下限値であるが、 勿論、 小さいほど平滑性がより高いものとされるが、 例え ば、 0 . 5 n m以上としておけば十分である。 また、 基板の主表面における表面粗 さは、 水熱合成法にて形成された Z n O単結晶をスライス加工などの切削加ェを施 すことで基板に成形した後に、 該基板の主表面に対して機械的研磨、 化学的研磨や 機械的化学的研磨を施すことにより調整することが可能である。
本発明の製造方法においては、 素子層形成工程の前に、 基板の主表面上に、 Z n O系化合物からなるバッファ層をェピタキシャル成長させるバッファ層形成工程を 有することが望ましい。
基板の主表面には、 水熱合成法にて形成された Z n O単結晶を基板に成形する際 に施されるスライス加工などの切削加工に起因する意図しない加工歪が、 表面歪の 形にて過大に存在する場合がある。 この表面歪が過大である場合、 その上にェピタ キシャル成長させる層には結晶欠陥や転位が発生しやすくなる。 しかしながら、 ノ ッファ層形成工程にてパッファ層を形成することで、 例え基板の主表面に意図しな い表面歪が過大に存在している場合においても、 該表面歪に伴う結晶欠陥や転位の 層厚方向への成長をパッファ層内にて効果的に抑止ないしは抑制させることが可能 となり、 ひいては、 素子層の品質をさらに向上させることを可能とする。 また、 界 面不純物や表面粗さに伴う結晶欠陥や転位の層厚方向への成長についても、 パッフ ァ層内にて効果的に抑止ないしは抑制させることが可能となる。
上記本発明の製造方法におけるバッファ層を構成する Z η θ系化合物としては、 具体的には、 上述した本発明の Z η θ系半導体素子に係わるものと同様のものを用 いることができるとともに、 同様の理由にて、 特には Z η θを用いるのが望ましい。 また、 バッファ層をェピタキシャル成長させる具体的な方法としては、 MO V P E (Metal Organic Vapor Phase Jipitaxy) 法や、 M B E (Molecular Beam
Epitaxy) 法などの公知の気相ェピタキシャル成長法を用いることができる。
本発明の製造方法においては、 バッファ層を、 素子層の成長温度よりも低温にて 成長させることが望ましい。
バッファ層は、 上記のように、 基板の主表面の表面状態に起因して発生する結晶 欠陥や転位が素子層に至るのを効果的に抑制な V、し抑止する役割を担うものである。 このように、 バッファ層を素子層の成長温度よりも低温とされる温度にて低温成長 させることで、 バッファ層の形成過程において、 層厚方向も含めた結晶欠陥や転位 の成長を効果的に抑制することができる。 その結果、 素子層の品質をさらに高める ことが可能となる。
このような低温成長させる際のバッファ層の形成温度は、 1 5 0 °C以上 5 0 0 °C 以下とするのが望ましい。 1 5 0 °C未満であると、 配向性を十分に高めるための結 晶化エネルギーを熱エネルギーとして付与できない場合があり、 バッファ層の結晶 性を十分に確保できず、 ひいては素子層の結晶性も確保し難くなる。 一方、 5 0 0 °Cを超えると、 バッファ層内にて、 結晶欠陥や転位の層厚方向への成長を十分に 抑制できない場合がある。 一方、 素子層の成長温度は、 4 0 0 °C以上 9 0 0 °C以下 としておけば、 素子層を、 結晶の連続性や周期性といった結晶性が十分に確保され た単結晶層とすることができる。
本発明の製造方法においては、 バッファ層形成工程の後、 バッファ層の成長温度 よりも高温にて熱処理を行うバッファ層熱処理工程を有することが望ましい。
上記のようにバッファ層を低温成長させると、 形成されるバッファ層内において、 局所的に結晶の連続性や周期性が確保されずに多結晶粒が介在する不具合や、 局所 的に結晶が成長せずに隙間が介在する不具合などの結晶性の低下に繋がる不具合が 発生してしまう場合がある。 そこで、 このようなバッファ層熱処理工程を行うこと で、 バッファ眉に対して再結晶化を促進させることが可能となり、 ひいてはバッフ ァ層の結晶性を十分に確保することが可能となる。 なお、 このバッファ層熱処理ェ 程は、 素子層形成工程の前に独立した工程として行ってもよいし、 例えば、 パッフ ァ層形成工程の後に、 素子層形成工程にて素子層の形成を行うために必要とされる、 バッファ層の成長温度よりも少なくとも昇温させる昇温過程をバッファ層熱処理ェ 程とすることもできる。 図面の簡単な説明
図 1は、 本発明に係わる半導体素子の要部となるべき積層構造の概略断面図。 図 2は、 本発明に係わる Z n O単結晶基板の製造方法を説明するための模式図。 図 3は、 本発明に係わる発光素子の要部となるべき積層構造の概略断面図。
図 4は、 本発明の Z η θ系半導体素子に係わる発光素子の概略断面図。 発明を実施するための最良の形態
以下、 本発明を実施するための最良の形態を、 図面を用いて説明する。
図 1は、 本発明の一実施形態を説明するための Z η θ系半導体素子の要部となる べき積層構造を模式的に示すものである。 該積層構造 1においては、 水熱合成法に て形成された Z η θ単結晶基板 Sの主表面上に、 Z η θからなるバッファ層 1 0を 介して、 Z η θ系化合物からなる素子層 1 1が形成されてなる。 ここで、 バッファ 層 1 0および素子層 1 1はェピタキシャル成長法にて形成されてなり、 このェピタ キシャル成長法としては、 MO V P E法もしくは MB E法などを用いることができ る。 なお、 本明細書において MB Eは、 金属元素成分源と非金属元素成分源との両 方を固体とする狭義の MB Eに加え、 金属元素成分源を有機金属とし非金属元素成 分源を固体とする MOMB E (Metal Organic Molecular Beam Epitaxy) 、 金属 元素成分源を固体とし非金属元素成分源を気体とするガスソース MB E、 金属元素 成分源を有機金属とし非金属元素成分源を気体とする化学ビームェピタキシ （C B E (Chemical Beam Epitaxy) ) を概念として含む。
図 1に示すように、 Z η θ系化合物からなる素子層 1 1は Z η θ単結晶基板 Sの 主表面上に形成されてなるので、 素子層 1 1を、 基板との格子不整合に起因した結 晶欠陥や転位の発生が効果的に抑制された品質に優れたものとすることができる。 さらに、 バッファ層 1 0が形成されてなるので、 Z η θ単結晶基板 Sの主表面にお ける、 表面歪、 界面不純物や平滑性といった表面状態に起因する結晶欠陥や転位の 層厚方向への成長をバッファ層 1 0内にて効果的に抑制することができる。 その結 果、 素子層 1 1をさらに品質に優れたものとすることができる。
上記のような役割を担うバッファ層 1 0の層厚は、 Z η θ単結晶基板 Sの表面状 態にもよるが、 例えば、 1 n m以上 1 0 0 n m以下の範囲としておくのがよい。 1 n m未満であると、 十分に結晶欠陥や転位の層厚方向への成長を抑制できない場合 があり、 一方、 1 0 0 n mを超えると、 十分に結晶欠陥や転位の層厚方向への成長 を抑制できるものの、 層厚の過大化のためにコスト高を招くことになるからである また、 2110単結晶基板3は、 水熱合成法にて形成されたものであるので、 単結 晶基板に基づくコスト高を招くことなく、 安価な半導体素子とすることができる。 水熱合成法にて形成される Z n O単結晶基板 Sは、 例えば以下のような方法および 装置により製造される。
図 2は水熱合成法にて Z ηθ単結晶を育成するための装置 20の概略を示すもの である。 P tルツポ 25内に、 Z ηθ種結晶 26と、 棒状の Z ηθ焼結体 24が配 置されている。 これら Z ηθ種結晶 26と Z ηθ焼結体 24とは、 P tパッフル板 27で分離されており、 P tルツボ 25内には、 KOHおよび L i OHの水溶液が 充填されている。 そして、 この P tルツボ 25は、 耐圧釜 23でシールされており この耐圧釜 23がヒータ 21、 22内に配置されている。 そして、 この耐圧釜 23 の温度を約 400°Cに上昇させるとともに、 0. 1 GP a程度の圧力を印加させる, このとき、 ヒータ 21、 22により、 Z ηθ種結晶 26が配置されている領域の温 度を、 Z ηθ焼結体 24が配置されている領域の温度よりも約 10°C程度低く設定 しておく。 このような育成条件にて、 Z ηθ種結晶 26を種結晶として Z 11 O単結 晶を育成するとともに、 Z ηθ単結晶を得ることができる。 そして、 このように作 製した Z n O単結晶に対してスライス加工などの切削加工を施し、 Z ηθ単結晶基 板 Sの形状に成形することで、 Z n O単結晶基板 Sを得る。
図 1に示す積層構造 1は、 本発明に係わる Z n O系半導体素子の要部となるべき ものであり、 該積層構造 1を用いて発光素子やトランジスタ素子といった種々の素 子構造が形成される。 以下、 発光素子を代表させて、 本発明の Z ηθ系半導体素子 および製造方法に係わる実施形態について説明する。
図 3は、 本発明に係わる発光素子の要部となるべき積層構造を模式的に示すもの である。 図 3における積層構造 1においては、 Z ηθ単結晶基板 Sの主表面上に、 Z ηθからなるバッファ層 10を介して素子層 1 1が形成されてなり、 この点につ いては図 1の積層構造と同様である。 しかしながら、 図 3における素子層 1 1は、 発光素子の素子構造に対応する形にて、 Z ηθ単結晶基板 S側から、 Mg l— a Z n aO (0≤ a≤ 1) (以下、 Mg Z nOとも言う） からなる n型 Mg Z n O層 3、 Z ηθ系化合物からなる活性層 4、 さらに p型 Mg Z ηθ層 5が順にェピタキシャ ル成長法にて形成されたダブルへテロ型の発光層部 1 1とされる。 また、 活性層 4 の構成材料としては、 目的とする発光波長に応じた Z ηθ系化合物が選定される。 図 3に示す積層構造 1の製造方法について説明する。 まず、 バッファ層形成工程 にて、 Z ηθ単結晶基板 Sの主表面上に Z ηθからなるバッファ層をェピタキシャ ル成長させる。 そして、 素子層形成工程にて発光層部とされる素子層 1 1を、 ェピ タキシャル成長させる。 これら、 バッファ層形成工程および素子層形成工程をとも に、 MOVP E法や MB E法などの気相ェピタキシャル成長法を用いて行うことが できる。 その際、 それぞれバッファ層おょぴ素子層の成長温度としては、 構成材料 にもよるが、 例えば、 1 50°C以上 5 00°C以下とされる。 また、 それぞれバッフ ァ層および素子層の主原料としては次のようなものを用いることができる。
'酸化性ガス ：酸素ガス、 N20、 NO、 N02、 CO、 H20など。
• S源ガス： H 2 Sなど。
• S e源ガス ： H 2 S eなど。
• T e源ガス ： H2T eなど。
• Z n源 (金属成分源) ガス：ジメチル亜鉛 （DMZ n) 、ジェチル亜鉛 （DE Z n) など。
• Mg源 （金属成分源） ガス ： ビスシクロペンタジェニルマグネシウム （C p 2M g) など。
また、 発光層部とされる素子層 1 1を構成するそれぞれ n型 Mg Z ηθ層 3およ ぴ！)型 Mg Z ηθ層 5には、 それぞれ n型ドーパントおよび p型ドーパントが含有 されてなる。 n型ドーパントとしては、 B、 A l、 G a、 I nの 1種又は 2種以上 が含有される。 I I I族元素である B、 A l、 Ga、 I nは、 I I族元素である M g、 Z n元素を置換し、 n型キャリアをドーピングすることが可能である。 n型 M g Z ηθ層の結晶性を考慮し、 Z n元素のイオン半径に近い G aを、 n型ドーパン トとして選択することが好適である。 他方、 p型ドーパントとしては、 L i、 Na、 Cu、 N、 P、 A s、 A l、 Ga、 I nの 1種又は 2種以上が含有される。 I族元 素である L i、 Naは、 I I族元素である Mg、 Znサイトを置換し、 V族元素で ある N、 P、 Asは、 V I族である Oサイトを置換することにより p型キャリアを ドーピングすることが可能である。 CuOは、 ソンドーピングで p型半導体である ので、 Cuをドーピングし CuOを生成することにより、 Cuは p型ドーパントと して機能することになる。 また、 A l、 Ga、 I n、 L iは、 Nと共添加すること により、 良好な p型特性をより確実に得ることができる。 さらに、 p型 Mg Z nO 層 5の結晶性を考盧して、 Z nもしくは O元素にイオン半径が近い Nと、 Ga、 A 1及び I nの一種又は 2種以上、 特に Gaとを選択することが好適である。
上記のように、 p型ドーパントとして、 A l、 G a及び I nの 1種又は 2種以上 を、 Nとの共添加により良好な] 3型ドーパントとして機能させることができる。 ド 一パントガスとしては以下のようなものを使用できる。
• A 1源ガス ： トリメチルアルミニウム （TMA 1 ) 、トリエチルアルミニウム
(TEA 1 ) など。
• G a源ガス ： トリメチルガリゥム (TMG a) 、トリェチルガリゥム (TEG a) など。
• I n源ガス ： トリメチルインジウム (TMI n) 、トリェチルインジウム (TE I n) など。
p型ドーパントとして金属元素 （Ga) とともに Nが使用される場合、 p型 Mg Z ηθ層のェピタキシャル成長を行なう際に、 N源となる気体 （例えば NH3、 モ ノメチルヒ ドラジンなど） を、 Ga源となる有機金属ガスとともに供給するように する。 また、 例えば、 酸化性ガスとして使用可能な N20を N源としても機能させ る形にしてもよい。
他方、 上述のように、 n型ドーパントとして、 A l、 G a及ぴ I nの 1種又は 2 種以上を添加することにより n型キャリアをドーピングすることができる。 ドーパ ントガスとしては、 上記同様なものが使用できる。
また、 Mg Z nOは真空雰囲気中での層成長時に、 酸素欠損が非常に生じやすく、 導電型が n型となる傾向がある。 そこで、 図 3における n型 Mg Z nO層 3の成長 に際しては酸素欠損を積極的に生じさせて n型とする方法をとることも可能で、 活 性層 4及ぴ p型 Mg ZnO層 5を成長する場合よりも圧力雰囲気を下げる （例えば 1 X 103P a未満とする) ことが有効である。 また、 同時に n型ドーパントを導 入する形で層成長を行なうことにより積極的に n型キヤリァをドーピングすること も可能である。
他方、 活性層 4及ぴ p型 Mg Z n O層 5を成長させる場合、 l X 1 03P a以上、 特には 2. 5 X 103P a以上の圧力雰囲気下で行なうことにより、 成膜中の酸素 欠損発生をより効果的に抑制でき、 良好な特性の活性層 4あるいは p型 Mg Z nO 層 5を得ることができる。 この場合、 より望ましくは、 酸素分圧 （02以外の酸素 含有分子も、 含有される酸素を〇2に換算して組み入れるものとする） が 1 X 10 3P a以上とするのがよい。 さらに、 p型 Mg Z nO層 5を成長させる場合、 p型 Mg Z nO層 5の主原料となるガス流量を間欠的に中断させ、 酸化を促進すること で酸素欠損発生をさらに抑制することもできる。
以上のようにしてバッファ層 10および発光層部とされる素子層 1 1の形成が終 了すれば、 図 4に示すように活性層 4及ぴ p型 Mg Z nO層 5の一部をフォトリソ グラフィ一等により一部除去して、 I TO等からなる透明電極 32を形成する。 そ して、 残余の p型 Mg Z nO層 5上には金属電極 3 1を形成し、 その後、 Z nO単 結晶基板 Sとともにダイシングすれば、 発光素子とされる Z nO系半導体素子 10 0が得られる。
以上、 本発明の一実施形態を説明したが、 本発明はこれに限定されるものではな く、 請求項の記載に基づく技術的範囲を逸脱しない限り、 種々の変形ないし改良を 付加することができる。 例えば、 図 3および図 4において、 Z n O系半導体素子は 素子層を発光層部とする発光素子とされるが、 例えばレーザ素子やトランジスタ素 子といった種々の半導体素子に適用可能である。 また、 図 3およぴ図 4における発 光層部はダブルへテロ型とされるが、 シングルヘテロ型のものとしてもよいし、 さ らには、 基板側より p型層、 n型層の順に形成される形としてもよい。

Claims

1. 水熱合成法により形成された ZnO単結晶基板の主表面上に、 ェピタキシ ャル成長法にて Z n O系化合物からなる素子層が形成されてなることを特徴とする Z nO系半導体素子。
2. 前記素子層は、 ェピタキシャル成長法にて形成されてなる ZnO系化合物 からなるバッファ層を介して、 前記求 Z n O単結晶基板の主表面上に形成されてなる ことを特徴とする請求の範囲第 1項記載のの Z n O系半導体素子。
3. 前記素子層が発光層部とされる発光素子であることを特徴とする請求の範 囲
囲第 1項または第 2項に記載の Z ηθ系半導体素子。
4. 水熱合成法により形成された ZnO単結晶を基板として、 該基板の主表面 上に、 Z nO系化合物からなる素子層をェピタキシャル成長させる素子層形成工程 を有することを特徴とする Z n O系半導体素子の製造方法。
5. 前記基板の主表面に対して、 酸化性ガス雰囲気下にて表面熱処理を行う基 板表面熱処理工程を有することを特徴とする請求の範囲第 4項記載の Z 11 O系半導 体素子の製造方法。
6. 前記基板としては、 該基板の主表面の表面粗さが RMSにて 2 nm以下の ものを用いることを特徴とする請求の範囲第 4項または第 5項に記載の Z n O系半 導体素子の製造方法。
7. 前記素子層形成工程の前に、 前記基板の主表面上に、 ZnO系化合物から なるバッファ層をェピタキシャル成長させるバッファ層形成工程を有することを特 徴とする請求の範囲第 4項ないし第 6項のいずれか 1項に記載の Z n O系半導体素 子の製造方法。
8. 前記バッファ層を、 前記素子層の成長温度よりも低温にて成長させること を特徴とする請求の範囲第 7項記載の Z ηθ系半導体素子の製造方法。
9 . 前記バッファ層形成工程の後、 前記バッファ層の成長温度よりも高温にて 熱処理を行うバッファ層熱処理工程を有することを特徴とする請求の範囲第 8項記 载の Z n O系半導体素子の製造方法。
PCT/JP2003/016323 2003-03-27 2003-12-19 ＺｎＯ系半導体素子およびその製造方法 WO2004086520A1 (ja)