WO2004046419A1 - 環状オレフィン系樹脂成形品表面への金属複合方法及び金属複合化環状オレフィン系樹脂成形品 - Google Patents
環状オレフィン系樹脂成形品表面への金属複合方法及び金属複合化環状オレフィン系樹脂成形品 Download PDFInfo
- Publication number
- WO2004046419A1 WO2004046419A1 PCT/JP2003/014461 JP0314461W WO2004046419A1 WO 2004046419 A1 WO2004046419 A1 WO 2004046419A1 JP 0314461 W JP0314461 W JP 0314461W WO 2004046419 A1 WO2004046419 A1 WO 2004046419A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- cyclic olefin
- metal
- olefin resin
- metal composite
- molded article
- Prior art date
Abstract
Description
Claims