WO2004041740A1 - 情報記録媒体用基板ならびに情報記録媒体およびその製造方法 - Google Patents
情報記録媒体用基板ならびに情報記録媒体およびその製造方法 Download PDFInfo
- Publication number
- WO2004041740A1 WO2004041740A1 PCT/JP2003/013846 JP0313846W WO2004041740A1 WO 2004041740 A1 WO2004041740 A1 WO 2004041740A1 JP 0313846 W JP0313846 W JP 0313846W WO 2004041740 A1 WO2004041740 A1 WO 2004041740A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- glass
- substrate
- information recording
- recording medium
- total amount
- Prior art date
Abstract
Description
Claims