WO2002089153A1 - Materiau solide pour aimant - Google Patents
Materiau solide pour aimant Download PDFInfo
- Publication number
- WO2002089153A1 WO2002089153A1 PCT/JP2002/004089 JP0204089W WO02089153A1 WO 2002089153 A1 WO2002089153 A1 WO 2002089153A1 JP 0204089 W JP0204089 W JP 0204089W WO 02089153 A1 WO02089153 A1 WO 02089153A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- magnetic
- magnet
- solid material
- solid
- magnets
- Prior art date
Description
Claims