WO2002001020A1 - Procede de renfort de structure, materiau contenant des fils de fibre de renfort destine au renfort de structure, materiau de renfort de structure et structure renforcee - Google Patents
Procede de renfort de structure, materiau contenant des fils de fibre de renfort destine au renfort de structure, materiau de renfort de structure et structure renforcee Download PDFInfo
- Publication number
- WO2002001020A1 WO2002001020A1 PCT/JP2001/005621 JP0105621W WO0201020A1 WO 2002001020 A1 WO2002001020 A1 WO 2002001020A1 JP 0105621 W JP0105621 W JP 0105621W WO 0201020 A1 WO0201020 A1 WO 0201020A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- reinforcing
- sheet
- yarn
- reinforced
- resin
- Prior art date
Description
Claims