WO2001078980A1 - Film multicouche tendu anticondensation a action rapide, et son procede de production - Google Patents
Film multicouche tendu anticondensation a action rapide, et son procede de production Download PDFInfo
- Publication number
- WO2001078980A1 WO2001078980A1 PCT/JP2001/003212 JP0103212W WO0178980A1 WO 2001078980 A1 WO2001078980 A1 WO 2001078980A1 JP 0103212 W JP0103212 W JP 0103212W WO 0178980 A1 WO0178980 A1 WO 0178980A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- film
- resin layer
- fog
- stretched film
- Prior art date
Description
Claims