WO2000021752A1 - Film a couche detachable - Google Patents
Film a couche detachable Download PDFInfo
- Publication number
- WO2000021752A1 WO2000021752A1 PCT/JP1999/005675 JP9905675W WO0021752A1 WO 2000021752 A1 WO2000021752 A1 WO 2000021752A1 JP 9905675 W JP9905675 W JP 9905675W WO 0021752 A1 WO0021752 A1 WO 0021752A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- film
- release
- resin
- release film
- release layer
- Prior art date
Description
Claims