WO1998055529A1 - Polyester, technique de production et recipient etanche aux gaz fabrique a l'aide de ce polyester - Google Patents

Polyester, technique de production et recipient etanche aux gaz fabrique a l'aide de ce polyester Download PDF

Info

Publication number
WO1998055529A1
WO1998055529A1 PCT/JP1998/002520 JP9802520W WO9855529A1 WO 1998055529 A1 WO1998055529 A1 WO 1998055529A1 JP 9802520 W JP9802520 W JP 9802520W WO 9855529 A1 WO9855529 A1 WO 9855529A1
Authority
WO
WIPO (PCT)
Prior art keywords
polyester
blood collection
collection tube
ethylene
acid value
Prior art date
Application number
PCT/JP1998/002520
Other languages
English (en)
Japanese (ja)
Inventor
Masahiko Yoshimura
Osamu Doi
Original Assignee
Unitika Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Unitika Ltd. filed Critical Unitika Ltd.
Priority to AU75518/98A priority Critical patent/AU7551898A/en
Publication of WO1998055529A1 publication Critical patent/WO1998055529A1/fr

Abstract

Ce polyester, de belle apparence comme d'une remarquable transparence et qui est également très résistant aux chocs et à la chaleur, peut être moulé pour donner un récipient étanche aux gaz pouvant parfaitement être utilisé comme corps de tube pour prélèvement sanguin. Ce polyester, qui est constitué de 99 à 50 %, en pourcentage molaire, de motifs de téréphtalate d'éthylène et de 1 à 50 %, en pourcentage molaire, de motifs d'isophtalate d'éthylène, est doté d'un indice d'acidité égal ou inférieur à 40 eq/t et d'une pénétration de l'aiguille à 60 °C, égale ou inférieure à 50 νm, comme mesuré à la température de ramollissement Vicat pour un échantillon d'une épaisseur d'un millimètre, d'une charge de 1 kg/mm2, d'une vitesse d'élévation de température de 0,83 °C/min ainsi que d'une constante de perméabilité à l'oxygène égale ou inférieure à 2,8 ml.mm/m2. par 24 h.atm.
PCT/JP1998/002520 1997-06-06 1998-06-05 Polyester, technique de production et recipient etanche aux gaz fabrique a l'aide de ce polyester WO1998055529A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU75518/98A AU7551898A (en) 1997-06-06 1998-06-05 Polyester, process for producing the same, and gas-barrier container made by using the polyester

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP14835297 1997-06-06
JP9/148352 1997-06-06

Publications (1)

Publication Number Publication Date
WO1998055529A1 true WO1998055529A1 (fr) 1998-12-10

Family

ID=15450849

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP1998/002520 WO1998055529A1 (fr) 1997-06-06 1998-06-05 Polyester, technique de production et recipient etanche aux gaz fabrique a l'aide de ce polyester

Country Status (2)

Country Link
AU (1) AU7551898A (fr)
WO (1) WO1998055529A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2003102709A (ja) * 2001-09-28 2003-04-08 Kanebo Ltd 真空採血管用有底管体用樹脂及びそれからなる真空採血管用有底管体
EP1696000A4 (fr) * 2003-12-12 2006-12-13 Kaneka Corp Composition de resine polyester et objet moule
WO2020004174A1 (fr) * 2018-06-26 2020-01-02 積水メディカル株式会社 Récipient de collecte de sang
JP2021528635A (ja) * 2018-06-14 2021-10-21 ベクトン・ディキンソン・アンド・カンパニーＢｅｃｔｏｎ， Ｄｉｃｋｉｎｓｏｎ Ａｎｄ Ｃｏｍｐａｎｙ 真空容器による血液ガスサンプル安定化のための大気平衡真空

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5964658A (ja) * 1982-09-07 1984-04-12 ザ・グツドイア−・タイヤ・アンド・ラバ−・コンパニ− ガスバリヤ−性のすぐれたポリエステル溶融ブレンド
JPS6166716A (ja) * 1984-09-07 1986-04-05 ザ・グツドイヤー・タイヤ・アンド・ラバー・カンパニー 固相重合方法
JPH0245040A (ja) * 1988-08-03 1990-02-15 Terumo Corp 減圧採血管
JPH03237969A (ja) * 1989-09-11 1991-10-23 Sam Yang Co Ltd 真空採血管
JPH04293920A (ja) * 1991-03-22 1992-10-19 Teijin Ltd 熱成形用材料および熱成形品

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5964658A (ja) * 1982-09-07 1984-04-12 ザ・グツドイア−・タイヤ・アンド・ラバ−・コンパニ− ガスバリヤ−性のすぐれたポリエステル溶融ブレンド
JPS6166716A (ja) * 1984-09-07 1986-04-05 ザ・グツドイヤー・タイヤ・アンド・ラバー・カンパニー 固相重合方法
JPH0245040A (ja) * 1988-08-03 1990-02-15 Terumo Corp 減圧採血管
JPH03237969A (ja) * 1989-09-11 1991-10-23 Sam Yang Co Ltd 真空採血管
JPH04293920A (ja) * 1991-03-22 1992-10-19 Teijin Ltd 熱成形用材料および熱成形品

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2003102709A (ja) * 2001-09-28 2003-04-08 Kanebo Ltd 真空採血管用有底管体用樹脂及びそれからなる真空採血管用有底管体
EP1696000A4 (fr) * 2003-12-12 2006-12-13 Kaneka Corp Composition de resine polyester et objet moule
JP2021528635A (ja) * 2018-06-14 2021-10-21 ベクトン・ディキンソン・アンド・カンパニーＢｅｃｔｏｎ， Ｄｉｃｋｉｎｓｏｎ Ａｎｄ Ｃｏｍｐａｎｙ 真空容器による血液ガスサンプル安定化のための大気平衡真空
JP7411581B2 (ja) 2018-06-14 2024-01-11 ベクトン・ディキンソン・アンド・カンパニー 真空容器による血液ガスサンプル安定化のための大気平衡真空
US11986297B2 (en) 2018-06-14 2024-05-21 Becton, Dickinson And Company Atmospheric-balanced vacuum for blood gas sample stabilization with an evacuated container
WO2020004174A1 (fr) * 2018-06-26 2020-01-02 積水メディカル株式会社 Récipient de collecte de sang
JPWO2020004174A1 (ja) * 2018-06-26 2021-07-15 積水メディカル株式会社 採血容器
JP7244162B2 (ja) 2018-06-26 2023-03-22 積水メディカル株式会社 採血容器

Also Published As

Publication number Publication date
AU7551898A (en) 1998-12-21

Similar Documents

Publication Publication Date Title
CN1263783C (zh) 改性的聚酯瓶用树脂及其制备方法
RU2450035C2 (ru) Способ получения полимеров сложных сополиэфиров для прозрачных однослойных контейнеров, демонстрирующих улучшенные характеристики газонепроницаемости
EP0105826B1 (fr) Mélanges de polyester à l'état fondu, ayant une haute imperméabilité aux gaz
US4340721A (en) Novel polyester for the packaging of comestibles
EP0934351B1 (fr) Procede de production d'articles pour animaux familiers a faible teneur en acetaldehyde
US6500506B1 (en) Aromatic polyester composition and articles therefrom
RU2440894C2 (ru) Смолы на основе сложных сополиэфиров для производства упаковки, полученные без использования твердофазной полимеризации, способ переработки смол на основе сложных сополиэфиров с изменением приведенной вязкости и контейнеры и другие изделия, полученные данным способом
EP3153310B1 (fr) Procede de fabrication de resines de co-polyester formant une barriere sans polymerisation a l'etat solide, resines de co-polyester fabriquees par ce procede et contenants transparents monocouches fabriques a partir de ces resines de co-polyester
EP0698631A2 (fr) Résine de copolyester, mélange de polymères et matériau d'emballage le contenant
KR930002416B1 (ko) 고분자량 폴리에스테르 수지의 제조방법
EP0492999B1 (fr) Copolyester et récipient creux et film orienté ainsi obtenu
WO1998055529A1 (fr) Polyester, technique de production et recipient etanche aux gaz fabrique a l'aide de ce polyester
MXPA02009572A (es) Composiciones a base de poliester que tienen propiedades termomecanicas mejoradas y procedimiento para producir las mismas.
CN110964339B (zh) 一种气密性良好的生物基复合材料薄膜制备方法
KR101405871B1 (ko) 고분자량을 가지는 폴리에스테르 블렌드의 제조방법 및 이를 이용하여 제조된 폴리에스테르 블렌드
JP2863570B2 (ja) 共重合ポリエチレンテレフタレートおよびその用途
JP4929615B2 (ja) ポリエステル組成物及びそれからなるポリエステル成形体
CN111019100B (zh) 一种蒙脱土改性的阻隔聚酯及其制备方法
RU2430939C2 (ru) Нанокомпозит и способ его производства
JP2000510177A (ja) ポリエステル組成物
WO2023118409A1 (fr) Procédé de production d'un (co)polymère de polyester
US20110263812A1 (en) Ethylene terephthalate type polyester resin for forming containers and process for producing the same
KR101405866B1 (ko) 고분자량을 가지는 폴리에스테르/폴리카보네이트 블렌드의 제조방법 및 이를 이용하여 제조된 폴리에스테르/폴리카보네이트 블렌드
JP2002114892A (ja) ポリエステル樹脂組成物
JPH11123717A (ja) ポリエステル樹脂成形体

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AU JP US

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 09445257

Country of ref document: US

122 Ep: pct application non-entry in european phase