WO1997046635A1 - Brandschutzmittel für platten aus spänen oder fasern - Google Patents
Brandschutzmittel für platten aus spänen oder fasern Download PDFInfo
- Publication number
- WO1997046635A1 WO1997046635A1 PCT/EP1997/002780 EP9702780W WO9746635A1 WO 1997046635 A1 WO1997046635 A1 WO 1997046635A1 EP 9702780 W EP9702780 W EP 9702780W WO 9746635 A1 WO9746635 A1 WO 9746635A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- parts
- weight
- fibers
- chips
- protection agent
- Prior art date
Abstract
Description
Claims