US20210121951A1 - Three-dimensional printing - Google Patents
Three-dimensional printing Download PDFInfo
- Publication number
- US20210121951A1 US20210121951A1 US16/604,384 US201816604384A US2021121951A1 US 20210121951 A1 US20210121951 A1 US 20210121951A1 US 201816604384 A US201816604384 A US 201816604384A US 2021121951 A1 US2021121951 A1 US 2021121951A1
- Authority
- US
- United States
- Prior art keywords
- flow additive
- metal
- build material
- material composition
- aggregates
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- This application claims priority to International Patent Application Number PCT/US2018/028341, filed Apr. 19, 2018; which itself claims priority to International Patent Application Number PCT/US2018/022684, filed Mar. 15, 2018, and to International Patent Application Number PCT/US2018/027286, filed Apr. 12, 2018, which claims priority to International Patent Application Number PCT/US2018/022684, filed Mar. 15, 2018; the disclosure of each of which is incorporated by reference herein in its entirety.
- Three-dimensional (3D) printing may be an additive printing process used to make three-dimensional solid parts from a digital model. 3D printing is often used in rapid product prototyping, mold generation, mold master generation, and short run manufacturing. Some 3D printing techniques are considered additive processes because they involve the application of successive layers of material (which, in some examples, may include build material, binder and/or other printing liquid(s), or combinations thereof). This is unlike traditional machining processes, which often rely upon the removal of material to create the final part. Some 3D printing methods use chemical binders or adhesives to bind build materials together. Other 3D printing methods involve at least partial curing, thermal merging/fusing, melting, sintering, etc. of the build material, and the mechanism for material coalescence may depend upon the type of build material used. For some materials, at least partial melting may be accomplished using heat-assisted extrusion, and for some other materials (e.g., polymerizable materials), curing or fusing may be accomplished using, for example, ultra-violet light or infrared light.
- Features of examples of the present disclosure will become apparent by reference to the following detailed description and drawings, in which like reference numerals correspond to similar, though perhaps not identical, components. For the sake of brevity, reference numerals or features having a previously described function may or may not be described in connection with other drawings in which they appear.
-
FIG. 1 depicts a graph of Hausner Ratio as a function of flow additive weight percentage for a mixture of a comparative fumed silica flow aid in 316L stainless steel powder; -
FIG. 2 is a schematic diagram depicting an example method for forming example fumed flow additive aggregates; -
FIG. 3 is a flow diagram depicting an example of a method for making a build material composition according to the present disclosure; -
FIG. 4 is a flow diagram depicting another example of a method for making a build material composition according to the present disclosure; -
FIG. 5 is a block diagram that depicts components of a build material composition and a three-dimensional (3D) printing kit as disclosed herein; -
FIG. 6 is a schematic diagram depicting effects of processing on examples of the composition disclosed herein; -
FIG. 7 is a flow diagram depicting an example of a 3D printing method; -
FIG. 8 depicts semi-schematic, partially cross-sectional views illustrating an example of a 3D printing method applying an example of the composition disclosed herein; -
FIG. 9 is a block diagram illustrating a portion of a 3D printing system that can use an example of the composition disclosed herein; -
FIG. 10 is a column graph depicting Hausner Ratio test results of a comparative example build material composition and example build material compositions as disclosed herein; -
FIG. 11 depicts a graph of Hausner Ratio as a function of flow additive weight percentage for comparative example build material compositions and example build material compositions as disclosed herein; -
FIG. 12 is a scanning electron microscope (SEM) image (at 250,000 times magnification), with a scale bar of 500 nm, of an example fumed flow additive aggregate disclosed herein; and -
FIG. 13 is a SEM image (at 250,000 times magnification), with a scale bar of 1 μm, of a comparative example flow additive aggregate. - Disclosed herein is a method for making a build material composition, which includes a custom flow additive. The custom flow additive is formed by liquid-feed flame spray pyrolysis. During this process, a precursor liquid is sprayed into a combustion chamber, where it is introduced into an external flame or is ignited to form a flame. The flame decomposes a precursor in the precursor liquid to form flow additive nanoparticles. The flow additive nanoparticles are primary particles, which aggregate to form fumed flow additive aggregates. The fumed flow additive aggregates include the flow additive nanoparticles and partially fused necks between at least some of the flow additive nanoparticles. The partially fused necks weakly attach the flow additive nanoparticles, and thus the fumed flow additive aggregates are easily broken. When combined with host build materials, the fumed aggregates readily break apart into individual flow additive nanoparticles and/or aggregate fragments that stick to surfaces of the host build material. This improves the flowability and spreadability of the host build material.
- The flow additive nanoparticles consist of a metal containing compound that is reducible to an elemental metal in a reducing environment at a reducing temperature less than or equal to a sintering temperature of the host metal. As used herein, the term “elemental metal” means one or more metals obtained from the reduction, decomposition, or decomposition and reduction of a metal containing compound. The number of elemental metals obtained will depend upon the metal containing compound and the reaction(s) it undergoes. For examples, a transition metal oxide may reduce to a single elemental metal (that corresponds to the transition metal cation), while mixed transition metal oxides may reduce to two or more elemental metals (that correspond to the transition metal cations). Unlike the elemental metal, the metal containing compound contains a non-metal component, such as oxygen, or oxygen and hydrogen (for hydroxides), etc. in accordance with the examples disclosed herein. The elemental metal produced can be integrated into a 3D object being formed without deleteriously affecting the mechanical properties of the 3D object. As such, the custom flow additive is suitable for a 3D printing process.
- In some examples, the 3D printing process may include patterning of uniformly spread layers of the build material composition with liquid binder agent applied by means of an inkjet printhead. Each patterned layer of the composition forms an individual cross-section of the final metal object. Stacking of the binder-patterned layers produces an intermediate part which can be extracted from the powderbed (or other build surface) after the patterning has been finished. The extracted intermediate part may be subjected to post-printing processing (e.g., heating via sintering), leading to consolidation of the particles of the composition into a mechanically stronger final metal object.
- In other examples, the 3D printing process may include Selective Laser Melting (SLM). In these examples, uniformly spread layers of the build material composition are individually exposed to a laser beam of high energy density. The laser spot scans the spread metal powder surface, heats the metal particles, melts the metal particles and fuses the molten metal into continuous layers. During a SLM printing process, stacked fused layers (each layer representing a portion of the printed part) produce the final metal part (i.e., each subsequent laser-patterned layer is fused on top of the previous one). With SLM, the final metal part is produced without printing an intermediate part and without sintering the intermediate part. Therefore the sintering-related advantages of smaller particles size are not applicable to SLM; however, the flow additives disclosed herein enable non-classified, lower cost metal powders with wide particle size distribution to be used with SLM.
- Examples of the build material composition disclosed herein may be used in a 3D printing kit, a 3D printing system, and a 3D printing method. While some of the examples provided herein relate to 3D printing, it is to be understood that the flow additives disclosed herein and the compositions including the flow additives may also be used in other methods and applications. When the custom flow additives disclosed herein are used in applications other than 3D printing, it is to be understood that the metal containing compound may be suitable for the particular application (i.e., the flow additive does not deleteriously affect the host material or any aspect of the application).
- As used herein, “material set” or “kit” is understood to be synonymous with “composition.” Further, “material set” and “kit” are understood to be compositions comprising one or more components where the different components in the compositions are each contained in one or more containers, separately or in any combination, prior to and during printing but these components can be combined together during printing. The containers can be any type of a vessel, box, or receptacle made of any material.
- Throughout this disclosure, a weight percentage that is referred to as “wt % active” refers to the loading of an active component of a dispersion or other formulation that is present in the precursor liquid, and/or binder agent. For example, binder polymer particles may be present in a water-based formulation (e.g., a stock solution or dispersion) before being incorporated into the binder agent. In this example, the wt % actives of the binder polymer particles accounts for the loading (as a weight percent) of the binder polymer particles solids that are present in the binder agent, and does not account for the weight of the other components (e.g., water, etc.) that are present in the stock solution or dispersion with the binder polymer particles. The term “wt %,” without the term actives, refers to either i) the loading (in the precursor liquid, or binder agent) of a 100% active component that does not include other non-active components therein, or ii) the loading (in the precursor liquid or binder agent) of a material or component that is used “as is” and thus the wt % accounts for both active and non-active components.
- The build material compositions include the host metal and the custom flow additive formed by flame spray pyrolysis. In example compositions, the host metal is present in an amount of at least 99 wt % based on a total weight of the build material composition; and the individual flow additive nanoparticles, the aggregate fragments, or the combination thereof is present in an amount of less than 1 wt % based on the total weight of the build material composition. In an example, the individual flow additive nanoparticles, the aggregate fragments, or the combination thereof is/are present in an amount ranging from about 0.02 wt % to about 1 wt % based on the total weight of the build material composition. In another example, the individual flow additive nanoparticles, the aggregate fragments, or the combination thereof is/are present in an amount ranging from about 0.02 wt % to about 0.1 wt % based on the total weight of the build material composition. In still another example, the individual flow additive nanoparticles, the aggregate fragments, or the combination thereof is/are present in an amount of about 0.1 wt % based on the total weight of the build material composition. In yet another example, the individual flow additive nanoparticles, the aggregate fragments, or the combination thereof is/are present in an amount of about 0.02 wt % based on the total weight of the build material composition.
- As such, in examples of the present disclosure, the composition is mainly the host metal. The host metal may be in powder form, i.e., particles. In the present disclosure, the term “particles” means discrete solid pieces of components of the build material composition. As used herein, the term “particles” does not convey a limitation on the shape of the particles. As examples, particles may be spherical beads or irregularly shaped beads of lower aspect ratio.
- Sintering of the host metal particles usually happens below a melting temperature of the host metal. The sintering temperature of the host metal particles may be dependent, in part, on the size of the host metal particles. A host metal with a smaller average particle size will experience a faster sintering rate than a host metal having a larger average particle size. The rate of sintering of solid crystalline powders obeys Herring scaling law and is inversely proportional to the particle size by a power of between 2 and 4. Therefore, reducing a metal particle size may allow faster sintering at a lower sintering temperature. Both the speed of sintering and the sintering temperature may beneficially alter a structure of the sintered part. For example, a fast sintering rate at a lower temperature may prevent large grain growth. The prevention of large grain growth may improve ultimate tensile strength, yield strength, ductility and other mechanical properties of the final metal objects.
- Thus, it may be desirable to use metal powders with the smallest particle size possible in 3D printing processes involving sintering. However, spreading of a powder into uniform thin layers of well-controlled thickness becomes increasingly difficult with decreased particle size. Without being held bound to any theory, it is believed that the reduced spreadability with decreasing particle size is due to inter-particle forces (i.e., van der Waals, electrostatic attraction, etc.) becoming significantly stronger than gravitational pull. Therefore, in general, powders become increasingly cohesive when a particle size of the powder is well below 100 μm. As such, smaller particles agglomerate together and the powders lose flowability. In the case of metals, even powders with spherical particles become non-spreadable into thin layers when the average particle size of the metal particles is within or below the range of about 12 μm to about 20 μm; especially when a fraction of particles present in the powder is within or smaller than the range of about 7 μm to about 10 μm. It is possible to remove the small particles from a metal powder by classification; however, classification is an additional process that adds to cost and removes the beneficial effects of small particles discussed above.
- Comparative flow additives include fumed silica or alumina powders, which have been used to decrease the inter-particle cohesive forces in difficult-to-flow powders. It is believed that many, if not all, current commercially available comparative flow additives are based on different grades of fumed silica and, in some cases, fumed aluminum oxides. In some cases, precipitated colloidal silica powders have been used as comparative flow additives after surface modification.
- These comparative flow additives are very low density powders made of loosely aggregated nano-particles. A typical primary particle size for the comparative flow additives ranges from about 1.5 to about 3 orders of magnitude smaller than the particle size of the cohesive powders to which the comparative flow additives are added. When added and mixed with cohesive host powders, these comparative flow additive nano-particles or their small aggregates stick to surfaces of the host particles. The host particle surfaces are coated with flow additive nano-spacers, thereby preventing agglomeration of the cohesive powder particles. Thus, formerly cohesive powders treated with an effective amount of the comparative flow additive (about 0.01 weight percent to 1.0 weight percent of the host powder) may be made flowable, with the potential of being spread in thin uniform layers. As used herein, better flowability of a composition means that the composition has better spreadability.
-
FIG. 1 depicts a graph of Hausner Ratio as a function of weight percentage for a mixture of a fumed silica flow aid in 316L stainless steel powder. The 316L stainless steel powder had an “as is” Hausner Ratio of about 1.37. Hausner Ratio (H[n]) is a powder flowability metric that can be measured by a tap density test. More specifically, the Hausner Ratio is a ratio of powder densities after and before compaction by tapping. A lower H[n] correlates to better flowability. Metal powders with a spherical particle shape and a Hausner Ratio of less than or equal to about 1.20 may be suitable for 3D printing applications with. In some cases, suitable flowability may be found with a Hausner Ratio up to about 1.25. The function depicted inFIG. 1 was determined from laboratory test results. The stainless steel powder was SAE 316L, grade −22 μm (80%) powder from “Sandvik”, (average particle diameter is approximately 11 μm). The fumed silica flow aid was Aerosil R812, available from Evonik. - It has been found that the comparative flow additives based on fumed oxides of silicon and aluminum discussed above cannot be used to improve flowability of metal powders used in certain additive manufacturing processes (e.g., those involving sintering) without negatively affecting strength-related structural properties of the final metal objects produced during the sintering process. Silica and alumina are not reduced during sintering processes with or without a reducing atmosphere. As such, both silica and alumina flow additive nano-particles become part of the structure of the final metal object. More particularly, the silica and alumina flow additive nano-particles get incorporated into grain boundary space of the final metal object structure. The presence of silica and/or alumina inclusions in a metal object structure diminishes the mechanical strength and ductility of the metal object. Thus, although comparative flow additives may improve flowability of certain metal powders, the comparative flow additives deleteriously affect mechanical properties of 3D objects formed therefrom.
- The examples of the method disclosed herein generate low density, loosely aggregated flow additive aggregates, which have a structure similar to comparative flow additives based on fumed oxides of silicon and aluminum. The fumed flow additive aggregates disclosed herein include flow additive nanoparticles (primary particles), at least some of which are connected by partially fused necks. The partially fused necks between the flow additive nanoparticles are sufficiently fused so that the primary particles are held together in the form of rigid secondary aggregates having a fractal structure. The partial fusing, however, enables the secondary aggregates to be easily broken. In some examples, the flow additive (secondary) aggregates can agglomerate into even larger loose agglomerates (up to 1000 μm), where the flow additive (secondary) aggregates are held together by weak Van der Waals forces. These loose agglomerates are multi-level, highly structured materials, that can be easily broken apart when mixed with the host metal. The Van der Waals forces of the loose agglomerates can be easily broken, resulting in the flow additive (secondary) aggregates, and the partially fused necks between the flow additive nanoparticles are not completely fused so that the secondary aggregates can be easily broken, resulting in the primary particles. As such, the fumed flow additive aggregates disclosed herein, whether present as secondary aggregates or larger agglomerates of the secondary aggregates, can easily break down to flow additive nanoparticles (the primary particles) when mixed with a host metal, and thus improve host metal flowability in a manner similar to or better than comparative flow additives based on fumed oxides of silicon and aluminum. For example, the build material composition disclosed herein is spreadable, having a Hausner Ratio less than 1.25. In some examples, the build material composition has a Hausner Ratio less than 1.2.
- Moreover, unlike the comparative flow additives based on fumed oxides of silicon and aluminum, the flow additive formed by the method disclosed herein is a metal containing compound that is reducible to an elemental metal in a reducing environment at a reducing temperature less than or equal to a sintering temperature of the host metal. In some examples, the metal containing compound is selected from the group consisting of vanadium oxides, chromium oxides, iron oxides, cobalt oxides, nickel oxides, manganese oxides, copper oxides, and mixed transition metal oxides. As such, the elemental metal(s) is/are capable of being incorporated into a bulk metal phase of the host metal in a final metal object. It is to be understood that incorporation into a bulk metal phase may include dissolution into the bulk metal phase, and/or alloying with a bulk metal phase. Further, incorporation into a grain boundary space, as occurs with comparative silica and alumina flow additive nano-particles, is not a form of incorporation into a bulk metal phase. Thus, unlike the build compositions that have the comparative flow additives discussed above, the build composition of the present disclosure has better spreadability/flowability and is able to be incorporated into the bulk metal phase. Further, final metal objects made from the build composition of the present disclosure have comparable strength properties to parts made from sintered powdered metal without flow additives. Therefore, the flow additives formed by the methods disclosed herein include metallurgy-friendly flow additives based on reducible metal oxide nano-powders that enable using small particle metal powder with low inherent flowability in additive manufacturing processes to yield final metal objects with comparable strength properties to parts made from sintered powdered metal without flow additives.
- Referring now to
FIG. 2 , an example of a method for making the fumed flow additive aggregates 21′ is depicted. - At the outset of the method, a precursor liquid 58 (which is shown at the bottom of
FIG. 2 ) is prepared or purchased. Theprecursor liquid 58 includes a solvent and a precursor of the metal containing compound. Because the metal containing compound is a transition metal oxide or a mixed transition metal oxide, the precursor liquid includes, in some examples, a solvent and i) a precursor of a transition metal oxide selected from the group consisting of vanadium oxides, chromium oxides, iron oxides, cobalt oxides, nickel oxides, manganese oxides, and copper oxides, or ii) a precursor of mixed transition metal oxide. - The solvent may be water, an organic solvent, or a combination thereof. Examples of suitable organic solvents include alcohols (e.g., primary aliphatic alcohols, secondary aliphatic alcohols, aromatic alcohols, 1,2-alcohols, 1,3-alcohols, 1,5-alcohols, etc.) and aromatic hydrocarbons. Suitable aromatic hydrocarbons are commercially available as part of the SOLVESSO® Series from ExxonMobile.
- In some examples, the solvent includes a combination of water and an organic solvent. In these examples, the solvent may be a water-based solvent mixture (e.g., 50 wt % or more of the solvent mixture is water) or an organic solvent-based solvent mixture (e.g., 50 wt % or more of the solvent mixture is an organic solvent). When the solvent is a water-based solvent mixture, the organic solvent may be selected so that it is miscible with water and so that the precursor is not precipitated.
- The precursor may be any component that is i) able to form the
flow additive nanoparticles 21 when exposed to the flame 60, and ii) soluble in the solvent of theprecursor liquid 58. - Each of the
flow additive nanoparticles 21 consists of a metal containing compound that is reducible to an elemental metal in a reducing environment at a reducing temperature less than or equal to a sintering temperature of ahost metal 15, and thus any component that is a precursor of the metal containing compound may be used. In some examples, the metal containing compound is selected from the group consisting of vanadium oxide nanoparticles, chromium oxide nanoparticles, iron oxide nanoparticles, cobalt oxide nanoparticles, nickel oxide nanoparticles, manganese oxide nanoparticles, copper oxide nanoparticles, and mixed transition metal oxide nanoparticles. In examples, the iron oxide may be selected from the group consisting of ferrous oxide (FeO), ferric oxide (Fe2O3), and magnetite (Fe3O4). The mixed transition metal oxide may be a spinel, i.e., A2+B2 3+O4 2−, where A and B are independently selected from the group consisting of chromium, cobalt, iron, manganese, nickel, copper, vanadium and zinc, or many other mixed oxides of the ferrite type not necessarily limited to the spinel structure. In an example, the mixed transition metal oxide is nickel iron oxide. As such, any precursor of the listed transition metal oxides or mixed transition metal oxides may be used in theprecursor liquid 58. - In some examples, the precursor is a metal salt that is soluble in the solvent. In some of these examples, the precursor has a high enough solubility in the solvent that it may be fully dissolved.
- The cation of the metal salt may be selected from the group consisting of vanadium, chromium, iron, cobalt, nickel, manganese, and copper. The anion of the metal salt may be selected from the group consisting of nitrate, sulfate, a halide (e.g., chloride, bromide, fluoride, iodide), an organic carboxylate (e.g., propionate, acetate, ethylhexanoate, etc.), and an alkoxide (e.g., methoxide, ethoxide, etc.). The anion of the metal salt may be selected so that the metal salt is/are soluble in the solvent. For example, when the solvent is water or a water-based solvent mixture (e.g., 50 wt % or more of the solvent mixture is water), the anion may be nitrate, sulfate, or chloride. For another example, when the solvent is an organic solvent or an organic solvent-based solvent mixture (e.g., 50 wt % or more of the solvent mixture is an organic solvent), the anion may be an organic carboxylate or an alkoxide. Examples of suitable metal salts include Ni(NO3)2 (nickel (II) nitrate), NiSO4 (nickel (II) sulfate), Co(NO3)2 (cobalt (II) nitrate), CoSO4 (cobalt (II) sulfate), Cr(NO3)3 (chromium (III) nitrate), CrSO4 (chromium (II) sulfate), VSO4 (vanadium (II) sulfate), C40H75O10V (vanadium 2-ethylhexanoate), CuCl2 (copper (II) chloride), CuSO4 (copper (II) sulfate), Cu(NO3)2 (copper (II) nitrate), Mn(CH3CO2)2 (manganese (II) acetate), C2H6MnO2 (manganese (II) methoxide), C6H10FeO4 (iron propionate), [Fe3O(OAc)6(H2O)3]OAc (OAc− is CH3CO2 −) (iron (III) acetate), etc.
- In some examples, the precursor is present in the
precursor liquid 58 in an amount ranging from about 0.1 wt % to about 5 wt %, based on the total weight of theprecursor liquid 58. - In one specific example, the
precursor liquid 58 includes a solvent and a transition metal salt precursor having: a cation selected from the group consisting of vanadium, chromium, iron, cobalt, nickel, manganese, and copper; and an anion selected from the group consisting of nitrate, sulfate, halide, an organic carboxylate, and an alkoxide; and the precursor is present in the precursor liquid in an amount ranging from about 0.1 wt % to about 5 wt %, based on a total weight of the precursor liquid. - Still referring to
FIG. 2 , after theprecursor liquid 58 is prepared or purchased, theprecursor liquid 58 is atomized so that it can be sprayed into acombustion chamber 36. Theprecursor liquid 58 may be atomized by an aerosol generator, such as an ultrasonic nebulizer (using high-frequency vibration to form a mist of the precursor liquid 58), a two-fluid nozzle (using an atomizing gas, such as oxygen gas, to disperse the precursor liquid 58), or an electro-sprayer (using high voltage to convert theprecursor liquid 58 into an aerosol). The mist/spray/aerosol is introduced into thecombustion chamber 36 where it can be introduced into an external flame 60, or where it can be ignited to form a flame 60′. Aprecursor liquid 58 containing water or an aqueous-based mixture as the solvent cannot form a self-sustaining flame due to the low combustion enthalpy (<50% of total energy of combustion) of the solution. In these instances, an external flame source (e.g., an oxy-hydrogen or oxyhydrocarbon) may be used to generate the external flame 60 to support the combustion of theprecursor liquid 58. In contrast, aprecursor liquid 58 containing an organic solvent or an organic-based mixture as the solvent can form a self-sustaining flame 60′ due to the high combustion enthalpy (>50% of total energy of combustion) of the solution. In these instances, pilot torches orflamelets 38 may be used to ignite the mist/spray/aerosol, which generates the self-sustaining flame 60′. - The flame 60 or 60′ may have any temperature suitable for the conversion of the precursor to the primary
flow additive nanoparticles 21, and ultimately to the fumed flow additive aggregates 21′. In an example, the flame 60 or 60′ has a temperature ranging from about 1000° C. to about 3000° C. - Within the external flame 60 or the self-sustaining flame 60′, the primary
flow additive nanoparticles 21, and ultimately to the fumed flow additive aggregates 21′, are formed. The mechanism for particle formation taking place in the flame 60 or 60′ may depend upon the components of theprecursor liquid 58. With someprecursor liquids 58, the solvent evaporates and the precursor is dispersed. The dispersed precursor reacts with a carrier gas (e.g., oxygen, air, or a mixture of an oxidizing and reducing gas) to form particles (e.g., metal oxide particles). With other precursor liquids 58 (e.g., organometallic salts), the precursor evaporates and decomposes to form metal vapor and gaseous oxyanion species, which co-react to nucleate as a result of supersaturation. This forms sub-nano-size proto-particles. Growth continues to form clusters of metal oxide bonds by coalescence and sintering processes taking place in the high temperature environment of the flame 60, 60′ (which forms the primary flow additive nanoparticles 21). Theseparticles 21 can then aggregate or fuse to form necks between the particles (i.e., the fumed flow additive (secondary) aggregates 21′). With either mechanism, the oxygen abundance in the system and the high temperature of the flame 60, 60′ may result in fully oxidized andcrystalline nanoparticles 21 and aggregates 21′. - The
aggregates 21′ formed have low density, fractal structures that are easily broken when mixed with thehost metal 15. The low density, fractal structures or fumed flow additive aggregates 21′ are shown at the top ofFIG. 2 . - The fumed flow additive aggregates 21′ may be collected using a suitable filtering system place above the flame 60, 60′. The fumed flow additive aggregates 21′ are ready to use, and thus no additional post-processing is used.
- The
flow additive nanoparticles 21 may have an average flow additive particle size (i.e., a primary particle size) ranging from about 3 nanometers to about 200 nanometers. As used herein, the term “particle size” or “average particle size” refers to the volume-weighted mean diameter (i.e., the average diameter of particles in a distribution normalized by the volume of the particles). The size of thenanoparticles 21 formed through flame spray pyrolysis may be affected by various parameters, such as the composition of theprecursor liquid 58, the fuel used to generate the flame 60, the mist/spray/aerosol and/or oxidant flow rates, the size of the mist/spray/aerosol droplets, and the temperature of flame 60, or 60′. In an example, theflow additive nanoparticles 21 may have an average flow additive particle size ranging from about 3 nm to about 15 nm. In another example, theflow additive nanoparticles 21 may have an average flow additive particle size ranging from about 3 nm to about 10 nm. In still another example, theflow additive nanoparticles 21 may have an average flow additive particle size of about 10 nm. In yet another example, theflow additive nanoparticles 21 may have an average flow additive particle size ranging of about 7 nm. - The fumed flow additive aggregates 21′ are highly structured aggregates of the
flow additive nanoparticles 21. The fumed flow additive aggregates 21′ have a relatively high porosity. As such, the fumed flow additive aggregates 21′ may have a surface area greater than 50 m2/g. In another example, the fumed flow additive aggregates 21′ have a surface area greater than 70 m2/g. In still another example, the fumed flow additive aggregates 21′ have a surface area greater than 100 m2/g. In yet another example, the fumed flow additive aggregates 21′ have a surface area of about 150 m2/g. - The fumed flow additive (secondary) aggregates 21′ have a relatively low density ranging from about 0.1% to 20% of a bulk density of the material of the
flow additive nanoparticles 21. In another example, the fumed flow additive aggregates 21′ have a relatively low density ranging from about 0.5% to 20% of a bulk density of the material of theflow additive nanoparticles 21. In some examples, the highly structured fumed flow additive aggregates 21′ may have an average flow additive aggregate particle size ranging from about 50 nm to about 1000 μm, or 100 nm to about 300 μm, or from about 1 μm to about 300 μm, or from about 1 μm to about 200 μm. At the higher end of these ranges (e.g., 300 μm or more), it is to be understood that the fumed flow additive (secondary) aggregates 21′ may be agglomerated together as described herein. The secondary aggregates 21′ are composed from primary particles (i.e., the flow additive nanoparticles 21) having a primary particle size in the nano-range, as mentioned hereinabove. Theaggregates 21′ also have meso-sized pores. These mesopores may range in size from about 10 nm to about 1 μm, and are present between the loosely aggregatedflow additive nanoparticles 21. In some examples, at least one of: the fumed flow additive aggregates 21′ have an average flow additive aggregate particle size ranging from about 50 nm to about 1000 μm; or the fumed flow additive aggregates 21′ have meso-sized pores; or the fumed flow additive aggregates have a density ranging from about 0.1% to 20% of a bulk density of a material of the flow additive nanoparticles. In a container of the flow additive formed by this method, the primaryflow additive nanoparticles 21 may be encountered as low density, often fractal structures or aggregates 21′ and/or as loose agglomerates of theaggregates 21′. - The fumed flow additive aggregates 21′ (whether present as secondary aggregates and/or as larger agglomerates of the secondary aggregates), when mixed with the
host metal 15, break into individualflow additive nanoparticles 21, aggregate fragments, or a combination thereof; and the individualflow additive nanoparticles 21, the aggregate fragments, or the combination thereof become disposed on a surface of particles of thehost metal 15. The relatively high porosity and the relatively low density of the fumed flow additive aggregates 21′ may contribute to the ability of the fumed flow additive aggregates 21′ to break into individualflow additive nanoparticles 21, aggregate fragments, or a combination thereof when mixed with thehost metal 15. - The method described in reference to
FIG. 2 may be accomplished in an environment including an oxidizing gas (e.g., oxygen gas (O2) or air). The oxidizing gas may oxidize the precursor in the presence of the flame 60, 60′ to form the metal oxide. The oxidizing gas may also participate in the combustion to form the self-sustaining flame 60′. In some examples, the method may be accomplished in an air environment (i.e., an environment including at least 20 vol. % oxygen gas (O2)). In other examples, the method may be accomplished in an environment that includes a reducing component (e.g., hydrogen gas (H2)), in addition to the oxidizing gas. In these examples, the reducing component may convert the precursor into an oxide. As an example, when the precursor is a halide, a reducing component may convert the halide into an oxide. - The method described in reference to
FIG. 2 may be used in a method for making a build material composition for 3D printing, examples of which are depicted inFIGS. 3 and 4 . - In the example shown in
FIG. 3 , themethod 200 for making abuild material composition 12 for three-dimensional (3D) printing comprises: spraying aprecursor liquid 58 into acombustion chamber 36, wherein theprecursor liquid 58 is exposed to an external flame 60 or is ignited to generate a flame 60′, whereby fumed flow additive aggregates 21′ are formed, the fumed flow additive aggregates 21′ includingflow additive nanoparticles 21 and partially fused necks between at least some of the flow additive nanoparticles, each of theflow additive nanoparticles 21 consisting of a metal containing compound that is reducible to an elemental metal in a reducing environment at a reducing temperature less than or equal to a sintering temperature of a host metal 15 (as shown at reference numeral 210); and mixing the flow additive aggregates 21′ with the host metal 15 (shown inFIGS. 5 and 6 ); wherein the fumedflow additive nanoparticles 21 have an average flow additive particle size ranging from about 1 to about 3 orders of magnitude smaller than an average host metal particle size of the host metal 15 (as shown at reference numeral 212). - The formation of the fumed flow additive aggregates 21′ may be performed as described in reference to
FIG. 2 . Any of the materials, amounts of materials, conditions (for the flame 60, 60′), etc. may be used in themethod 200. - Once the fumed flow additive aggregates 21′ are formed, they may be mixed with the
host metal 15. In an example, thehost metal 15 may be a single phase metallic material composed of one element. In this example, the sintering temperature of thebuild material composition 12 may be below the melting point of the single element. In another example, thehost metal 15 may be composed of two or more elements, which may be in the form of a single phase metallic alloy or a multiple phase metallic alloy. In these other examples, sintering generally occurs over a range of temperatures. - Some examples of the
host metal 15 include steels, stainless steel, bronzes, titanium (Ti) and alloys thereof, aluminum (Al) and alloys thereof, nickel (Ni) and alloys thereof, cobalt (Co) and alloys thereof, iron (Fe) and alloys thereof, nickel cobalt (NiCo) alloys, gold (Au) and alloys thereof, silver (Ag) and alloys thereof, platinum (Pt) and alloys thereof, tungsten (W) and alloys thereof, and copper (Cu) and alloys thereof. Some specific examples include AlSi10Mg, 2xxx series aluminum, 4xxx series aluminum, CoCr MP1, CoCr SP2, MaragingSteel MS1, Hastelloy C, Hastelloy X, NickelAlloy HX, Inconel IN625, Inconel IN718, SS GP1, SS 17-4PH, SS 316L, SS 430L, Ti6Al4V, and Ti-6Al-4V ELI7. While several example alloys have been provided, it is to be understood that other alloys may be used. - In some examples, the particles of the
host metal 15 may have an average host metal particle size less than 20 μm. In some examples, some host metal particles in a mixture of host metal particles may be as small as about 1 μm. Theflow additive nanoparticles 21 have an average flow additive particle size ranging from about 1 to about 3 orders of magnitude smaller than the average host metal particle size. In some examples, the average host metal particle size is less than 20 μm; and the average flow additive particle size may range from about 3 nm to about 200 nm. In other examples, the average host metal particle size is less than 20 μm, and the average flow additive primary particle size is 50 nm or less. - Any suitable conditions may be used to mix the
host metal 15 with the fumed flow additive aggregates 21′. As examples, mixing may be accomplished in a rotating container, using a mechanical mixer, or using a hand mixer. Mixing may also be accomplished at ambient temperatures, which may range from about 18° C. to about 25° C. In some examples (as described further in reference toFIG. 4 ), mixing may be accomplished for a suitable time period, which may depend, at least in part, upon how long it takes for the mixture to obtain a desirable Hausner Ratio (which indicates good flowability). As such, some examples of themethod 200 include stopping mixing when thebuild material composition 12 has a Hausner Ratio less than 1.25. Other examples, of themethod 200 include stopping mixing when thebuild material composition 12 has a Hausner Ratio less than 1.2. - The mixing breaks the fumed flow additive aggregates 21′ into either individual
flow additive nanoparticles 21, aggregate fragments, or combinations thereof; the individualflow additive nanoparticles 21, the aggregate fragments, or the combination thereof become disposed on a surface of the particles of thehost metal 15; and the mixing forms thebuild material composition 12 including: thehost metal 15 present in an amount of at least 99 wt % based on a total weight of thebuild material composition 12; and the individualflow additive nanoparticles 21, the aggregate fragments, or the combination thereof present in an amount of less than 1 wt % based on the total weight of thebuild material composition 12. As used herein, the term “aggregate fragments” refers to a fewflow additive nanoparticles 21 that are stuck together, but are smaller than the fumed flow additive aggregates 21′. Theflow additive nanoparticles 21 and/or the aggregate fragments stick to a surface of thehost metal 15 particles and improve the flowability of thehost metal 15. - Referring now to
FIG. 4 , another example of the method, shown as 300, is depicted. In this example, themethod 300 for making a build material composition for three-dimensional (3D) printing comprises: spraying aprecursor liquid 58 intocombustion chamber 36, wherein theprecursor liquid 58 is exposed to an external flame 60 or is ignited to generate a flame 60′, whereby fumed flow additive aggregates 21′ are formed, the flow additive aggregates 21′ includingflow additive nanoparticles 21 and partially fused necks between at least some of the flow additive nanoparticles, each of theflow additive nanoparticles 21 consisting of a metal containing compound that is reducible to an elemental metal in a reducing environment at a reducing temperature less than or equal to a sintering temperature of a host metal 15 (as shown at reference numeral 310); mixing the fumed flow additive aggregates 21′ with thehost metal 15 to form a build material mixture (as shown at reference numeral 312); during mixing, monitoring a Hausner Ratio of the build material mixture (as shown at reference numeral 314); and stopping mixing when abuild material composition 12 having a Hausner Ratio less than 1.25 is formed (as shown at reference numeral 316). - The formation of the fumed flow additive aggregates 21′ may be performed as described in reference to
FIG. 2 . Any of the materials, amounts of materials, conditions (for the flame 60, 60′), etc. may be used in themethod 300. - The mixing of the
host metal 15 and the fumed flow additive aggregates 21′ may be performed as described in reference toFIG. 3 . - In examples of the
method 300, the Hausner Ratio may be monitored throughout the mixing process to determine when the desirable Hausner Ratio has been obtained. Monitoring the Hausner Ratio may be accomplished by periodically testing the Hausner Ratio of the mixture throughout the mixing process. In an example, simple mixing of thehost metal 15 with the fumed flow additive aggregates 21′ in a rotating container for about 1 hour to about 2 hours may be sufficient mixing to obtain a uniform Hausner Ratio throughout the mixture. Very long mixing, (e.g., 2 days or more) may result in flowability degradation (i.e., an increase in the Hausner Ratio over the Hausner Ratio that is achieved by an amount of mixing that has a duration at a threshold of sufficiency to be effective). - In some examples, the fumed flow additive aggregates 21′ (which may or may not agglomerate into larger loose agglomerate) are included in a 3D printing kit, such as the build material composition kit 13 shown in
FIG. 5 . In an example, the kit 13 includes thehost metal 15 and the fumed flow additive aggregates 21′ (formed by the method described in reference toFIG. 2 ) that are to be mixed with thehost metal 15. In one example, the kit for three-dimensional (3D) printing, comprises: thehost metal 15 and the fumed flow additive aggregates 21′ to be mixed with thehost metal 15, the fumed flow additive aggregates 21′ includingflow additive nanoparticles 21 and partially fused necks between at least some of theflow additive nanoparticles 21, each of theflow additive nanoparticles 21 consisting of a metal containing compound that is reducible to an elemental metal in a reducing environment at a reducing temperature less than or equal to a sintering temperature of thehost metal 15. - The
components build material composition 12 for use in 3D printing, or to form another composition that is to be used in an application that involves spreading of thecomposition 12. The components of the build material composition kit 13 may be maintained separately until used together in examples of the 3D printing method disclosed herein. - In some examples, the kit 13 may consist of the fumed flow additive aggregates 21′ and the
metal host 15 with no other components. In other examples, the build material composition kit 13 may further include abinder agent 14 to be applied, via an inkjet printhead, to at least a portion of a layer of abuild material composition 12 formed from mixing the fumed flow additive aggregates 21′ with thehost metal 15. - As shown in
FIG. 5 , the fumed flow additive aggregates 21′ and themetal host 15 are mixed together to form thebuild material composition 12. Thebuild material composition 12 may be included in another example of a3D printing kit 23. In this example, thekit 23 includes thebuild material composition 12 and abinder agent 14 to be applied to at least a portion of a layer of thebuild material composition 12 via an inkjet printhead to pattern a cross-section of an intermediate part. Thekit 23 may consist of thebuild material composition 12 and thebinder agent 14 with no other components. The components of thekit 23 may be maintained separately until used together in examples of the 3D printing method disclosed herein. - As mentioned herein, the fumed flow additive aggregates 21′ and the
host metal 15 are mixed to form abuild material composition 12 for an additive manufacturing process.FIG. 6 is a diagram depicting the components (15, 21′, 21) of thebuild material composition 12 going through certain steps of an example of an additive manufacturing process.FIG. 6 begins with thehost metal particles 15 being mixed with the fumed flow additive aggregates 21′. As a result of mixing, the fumed flow additive aggregates 21′ (or larger agglomerates thereof) break up to form individualflow additive nanoparticles 21 and/or aggregate fragments that stick to thehost metal 15. This forms thebuild material composition 12. Thebuild material composition 12 may be spread into a layer and patterned with a binder fluid 14 (not shown inFIG. 6 ) to form a portion of anintermediate part 31. During initial heating stages after patterning, theexample flow aid 21 decomposes (e.g., by reduction), and is removed from theintermediate part 31. Thevapor cloud 19 shown inFIG. 6 represents theflow additive nanoparticles 21 being removed from thebuild material composition 12. The remainingintermediate part 31′ is then sintered to form the final 3D object orpart 35. - An example of a
printing method 400 that utilizes thebuild material composition 12 disclosed herein is shown inFIG. 7 . In this example, themethod 400 for three-dimensional (3D) printing comprises: applying abuild material composition 12 including: ahost metal 15 present in an amount of at least 99 wt %, based on a total weight of thebuild material composition 12; and a flow additive present in an amount of less than 1 wt % based on the total weight of thebuild material composition 12, the flow additive including flow additiveprimary particles 21 that: have an average flow additive primary particle size ranging from about 1 to about 3 orders of magnitude smaller than an average host metal particle size; and are metal oxide particles that are reducible to at least one elemental metal in a reducing environment at a reducing temperature less than or equal to a sintering temperature of thehost metal 15, wherein the at least one elemental metal is capable of being incorporated into a bulk metal phase of thehost metal 15 in a final metal object; wherein thebuild material composition 12 is spreadable, having a Hausner Ratio less than 1.25; and selectively applying abinder agent 14 on at least a portion of thebuild material composition 12. - In some examples of the
method 400, prior to the applying of thebuild material composition 12, the method further comprises: spraying aprecursor liquid 58 into acombustion chamber 36, wherein theprecursor liquid 58 is exposed to an external flame 60 or is ignited to generate a flame 60′, whereby fumed flow additive aggregates 21′ are formed, the flow additive aggregates 21′ including theflow additive 21; and mixing the flow additive aggregates 21′ with thehost metal 15 to form thebuild material composition 12. - In the examples of the
printing method 400 disclosed herein, thebinder agent 14 may include a binder and a liquid vehicle. - Examples of suitable binders include latexes (i.e., an aqueous dispersion of polymer particles), polyvinyl alcohol, polyvinylpyrrolidone, and combinations thereof.
- Examples of polyvinyl alcohol include low weight average molecular weight polyvinyl alcohols (e.g., from about 13,000 to about 50,000), such as SELVOL™ PVOH 17 from Sekisui. Examples of polyvinylpyrrolidones include low weight average molecular weight polyvinylpyrrolidones (e.g., from about 15,000 to about 19,000), such as LUVITEC™ K 17 from BASF Corp.
- The binder polymer particles may be any latex polymer (i.e., polymer that is capable of being dispersed in an aqueous medium) that is jettable via inkjet printing (e.g., thermal inkjet printing or piezoelectric inkjet printing). In some examples disclosed herein, the binder polymer particles are heteropolymers or co-polymers. The heteropolymers may include a more hydrophobic component and a more hydrophilic component. In these examples, the hydrophilic component renders the particles dispersible in the
binder agent 14, while the hydrophobic component is capable of coalescing upon exposure to heat in order to temporarily bind thehost metal particles 15. - The binder polymer particles of the latex may have several different morphologies. The binder polymer particles may include two different copolymer compositions, which may be fully separated core-shell polymers, partially occluded mixtures, or intimately comingled as a polymer solution. In an example, the polymer particles may be individual spherical particles containing polymer compositions of hydrophilic (hard) component(s) and/or hydrophobic (soft) component(s) that may be interdispersed according to IPN (interpenetrating networks), although it is contemplated that the hydrophilic and hydrophobic components may be interdispersed in other ways. For another example, the polymer particles may be made of a hydrophobic core surrounded by a continuous or discontinuous hydrophilic shell. This may lead to good water dispersibility and jetting reliability. For another example, the polymer particle morphology may resemble a raspberry, in which a hydrophobic core is surrounded by several smaller hydrophilic particles that are attached to the core. For still another example, the polymer particles may include 2, 3, or 4 or more relatively large particles (i.e., lobes) that are at least partially attached to one another or that surround a smaller polymer core. The latex polymer particles may have a single phase morphology, may be partially occluded, may be multiple-lobed, or may include any combination of the morphologies disclosed herein.
- The latex polymer particles may have a weight average molecular weight ranging from about 5,000 to about 500,000. As examples, the weight average molecular weight of the latex particles may range from about 10,000 to about 500,000, from about 100,000 to about 500,000, or from about 150,000 to about 300,000.
- Latex particles may include a heteropolymer including a hydrophobic component that makes up from about 65% to about 99.9% (by weight) of the heteropolymer, and a hydrophilic component that makes up from about 0.1% to about 35% (by weight) of the heteropolymer, where the hydrophobic component may have a lower glass transition temperature than the hydrophilic component. In general, a lower content of the hydrophilic component is associated with easier use of the latex particles under typical ambient conditions. The glass transition temperature of the latex particles may range from about −20° C. to about 130° C., or in a specific example, from about 60° C. to about 105° C. The particle size of the latex particles may range from about 10 nm to about 300 nm.
- Examples of monomers that may be used to form the hydrophobic component of the binder polymer particles may include C4 to C8 alkyl acrylates or methacrylates, styrene, substituted methyl styrenes, polyol acrylates or methacrylates, vinyl monomers, vinyl esters, ethylene, maleate esters, fumarate esters, itaconate esters, or the like. Some specific examples include methyl methacrylate, butyl acrylate, butyl methacrylate, hexyl acrylate, hexyl methacrylate, ethyl acrylate, ethyl methacrylate, propyl acrylate, propyl methacrylate, 2-ethylhexyl acrylate, 2-ethylhexy methacrylate, hydroxyethyl acrylate, lauryl acrylate, lauryl methacrylate, octadecyl acrylate, octadecyl methacrylate, isobornyl acrylate, isobornyl methacrylate, stearyl methacrylate, ethylene glycol dimethacrylate, diethylene glycol dimethacrylate, triethylene glycol dimethacrylate, tetrahydrofurfuryl acrylate, alkoxylated tetrahydrofurfuryl acrylate, 2-phenoxyethyl methacrylate, benzyl acrylate, ethoxylated nonyl phenol methacrylate, cyclohexyl methacrylate, trimethyl cyclohexyl methacrylate, t-butyl methacrylate, n-octyl methacrylate, tridecyl methacrylate, isodecyl acrylate, dimethyl maleate, dioctyl maleate, acetoacetoxyethyl methacrylate, diacetone acrylamide, pentaerythritol tri-acrylate, pentaerythritol tetra-acrylate, pentaerythritol tri-methacrylate, pentaerythritol tetra-methacrylate, divinylbenzene, styrene, methylstyrenes (e.g., α-methyl styrene, p-methyl styrene), 1,3-butadiene, vinyl chloride, vinylidene chloride, vinylbenzyl chloride, acrylonitrile, methacrylonitrile, N-vinyl imidazole, N-vinylcarbazole, N-vinyl-caprolactam, combinations thereof, derivatives thereof, or mixtures thereof.
- The heteropolymer may be formed of at least two of the previously listed monomers, or at least one of the previously listed monomers and a higher Tg hydrophilic monomer, such as an acidic monomer. Examples of acidic monomers that can be polymerized in forming the latex polymer particles include acrylic acid, methacrylic acid, ethacrylic acid, dimethylacrylic acid, maleic anhydride, maleic acid, vinylsulfonate, cyanoacrylic acid, vinylacetic acid, allylacetic acid, ethylidineacetic acid, propylidineacetic acid, crotonoic acid, fumaric acid, itaconic acid, sorbic acid, angelic acid, cinnamic acid, styrylacrylic acid, citraconic acid, glutaconic acid, aconitic acid, phenylacrylic acid, acryloxypropionic acid, aconitic acid, phenylacrylic acid, acryloxypropionic acid, vinylbenzoic acid, N-vinylsuccinamidic acid, mesaconic acid, methacroylalanine, acryloylhydroxyglycine, sulfoethyl methacrylic acid, sulfopropyl acrylic acid, styrene sulfonic acid, sulfoethylacrylic acid, 2-methacryloyloxymethane-1-sulfonic acid, 3-methacryoyloxypropane-1-sulfonic acid, 3-(vinyloxy)propane-1-sulfonic acid, ethylenesulfonic acid, vinyl sulfuric acid, 4-vinylphenyl sulfuric acid, ethylene phosphonic acid, vinyl phosphoric acid, vinyl benzoic acid, 2 acrylamido-2-methyl-1-propanesulfonic acid, combinations thereof, derivatives thereof, or mixtures thereof. Other examples of high Tg hydrophilic monomers include acrylamide, methacrylamide, monohydroxylated monomers, monoethoxylated monomers, polyhydroxylated monomers, or polyethoxylated monomers.
- In an example, the selected monomer(s) is/are polymerized to form a polymer, heteropolymer, or copolymer. In some examples, the monomer(s) are polymerized with a co-polymerizable surfactant. In some examples, the co-polymerizable surfactant can be a polyoxyethylene compound. In some examples, the co-polymerizable surfactant can be a HITENOL® compound e.g., polyoxyethylene alkylphenyl ether ammonium sulfate, sodium polyoxyethylene alkylether sulfuric ester, polyoxyethylene styrenated phenyl ether ammonium sulfate, or mixtures thereof.
- The binder polymer particles may have a particle size that can be jetted via thermal inkjet printing or piezoelectric printing or continuous inkjet printing. In an example, the particle size of the binder polymer particles ranges from about 10 nm to about 300 nm.
- Any suitable polymerization process may be used to prepare the binder polymer particles. In examples, the aqueous dispersion of polymer particles (latexes) may be produced by emulsion polymerization or co-polymerization of any of the previously listed monomers.
- In an example, the polymer particles may be prepared by polymerizing hydrophilic monomers to form the hydrophilic component and attaching the hydrophilic component onto the surface of the hydrophobic component.
- In another example, each of the polymer particles may be prepared by polymerizing the hydrophobic monomers and the hydrophilic monomers at a ratio of the hydrophobic monomers to the hydrophilic monomers that ranges from 5:95 to 30:70. In this example, the hydrophobic monomers may dissolve in the hydrophilic monomers.
- In still another example, each of the binder polymer particles may be prepared by starting the polymerization process with the hydrophobic monomers, then adding the hydrophilic monomers, and then finishing the polymerization process. In this example, the polymerization process may cause a higher concentration of the hydrophilic monomers to polymerize at or near the surface of the hydrophobic component.
- In still another example, each of the polymer particles may be prepared by starting a copolymerization process with the hydrophobic monomers and the hydrophilic monomers, then adding additional hydrophilic monomers, and then finishing the copolymerization process. In this example, the copolymerization process may cause a higher concentration of the hydrophilic monomers to copolymerize at or near the surface of the hydrophobic component.
- Other suitable techniques, specifically for generating a core-shell structure, may be used, such as: i) grafting a hydrophilic shell onto the surface of a hydrophobic core, ii) copolymerizing hydrophobic and hydrophilic monomers using ratios that lead to a more hydrophilic shell, iii) adding hydrophilic monomer (or excess hydrophilic monomer) toward the end of the copolymerization process so there is a higher concentration of hydrophilic monomer copolymerized at or near the surface, or iv) any other method known in the art to generate a more hydrophilic shell relative to the core.
- The hydrophobic monomers and/or the hydrophilic monomers used in any of these example methods may be any of the hydrophobic monomers and/or the hydrophilic monomers (respectively) listed above. In an example, the hydrophobic monomers are selected from the group consisting of C4 to C8 alkyl acrylate monomers, C4 to C8 alkyl methacrylate monomers, styrene monomers, substituted methyl styrene monomers, vinyl monomers, vinyl ester monomers, and combinations thereof; and the hydrophilic monomers are selected from the group consisting of acidic monomers, unsubstituted amide monomers, alcoholic acrylate monomers, alcoholic methacrylate monomers, C1 to C2 alkyl acrylate monomers, C1 to C2 alkyl methacrylate monomers, and combinations thereof.
- The resulting binder polymer particles may exhibit a core-shell structure, a mixed or intermingled polymeric structure, or some other morphology.
- In some examples, the binder polymer particles have a MFFT or a glass transition temperature (Tg) that is greater (e.g., >) than ambient temperature. In other examples, the binder polymer particles have a MFFT or Tg that is much greater (e.g., >>) than ambient temperature (i.e., at least 15° higher than ambient). As mentioned herein, “ambient temperature” may refer to room temperature (e.g., ranging about 18° C. to about 22° C.), or to the temperature of the environment in which the 3D printing method is performed. Examples of the 3D printing environment ambient temperature may range from about 40° C. to about 50° C. The MFFT or the Tg of the bulk material (e.g., the more hydrophobic portion) of the polymer particles may range from 25° C. to about 125° C. In an example, the MFFT or the Tg of the bulk material (e.g., the more hydrophobic portion) of the polymer particles is about 40° C. or higher. The MFFT or the Tg of the bulk material may be any temperature that enables the polymer particles to be inkjet printed without becoming too soft at the printer operating temperatures.
- The binder polymer particles may have a MFFT or Tg ranging from about 125° C. to about 200° C. In an example, the binder polymer particles may have a MFFT or Tg of about 160° C.
- In an example, the binder is present in the
binder agent 14 in an amount ranging from about 1 wt % active to about 40 wt % active based on a total weight of the binder agent. In another example, the binder is present in thebinder agent 14 in an amount ranging from about 2 wt % active to about 30 wt % active based on the total weight ofbinder agent 14. - In addition to the binder, the
binder agent 14 may also include water, co-solvent(s), surfactant(s) and/or dispersing aid(s), antimicrobial agent(s), and/or anti-kogation agent(s). - The co-solvent may be an organic co-solvent present in an amount ranging from about 0.5 wt % to about 40 wt % (based on the total weight of the binder agent 14). It is to be understood that other amounts outside of this range may also be used depending, at least in part, on the jetting architecture used to dispense the
binder agent 14. The organic co-solvent may be any water miscible, high-boiling point solvent, which has a boiling point of at least 120° C. Classes of organic co-solvents that may be used include aliphatic alcohols, aromatic alcohols, diols, glycol ethers, polyglycol ethers, 2-pyrrolidones/pyrrolidinones, caprolactams, formamides, acetamides, glycols, and long chain alcohols. Examples of these co-solvents include primary aliphatic alcohols, secondary aliphatic alcohols, 1,2-alcohols, 1,3-alcohols, 1,5-alcohols, ethylene glycol alkyl ethers, propylene glycol alkyl ethers, higher homologs (C6-C12) of polyethylene glycol alkyl ethers, N-alkyl caprolactams, unsubstituted caprolactams, both substituted and unsubstituted formamides, both substituted and unsubstituted acetamides, and the like. In some examples, the gas generating liquid functional agent may include 2-pyrrolidone, 2-methyl-1,3-propanediol, 1-(2-hydroxyethyl)-2-pyrrolidone, 1,2-butanediol, or combinations thereof. - The
binder agent 14 may also include surfactant(s) and/or dispersing aid(s). Surfactant(s) and/or dispersing aid(s) may be used to improve the wetting properties and the jettability of thebinder agent 14. Examples of suitable surfactants and dispersing aids include those that are non-ionic, cationic, or anionic. Examples of suitable surfactants/wetting agents include a self-emulsifiable, non-ionic wetting agent based on acetylenic diol chemistry (e.g., SURFYNOL® SEF from Evonik Degussa), a non-ionic fluorosurfactant (e.g., CAPSTONE® fluorosurfactants from DuPont, previously known as ZONYL FSO), and combinations thereof. In a specific example, the surfactant is a non-ionic, ethoxylated acetylenic diol (e.g., SURFYNOL® 465 from Evonik Degussa). In other examples, the surfactant is an ethoxylated low-foam wetting agent (e.g., SURFYNOL® 440 or SURFYNOL® CT-111 from Evonik Degussa) or an ethoxylated wetting agent and molecular defoamer (e.g., SURFYNOL® 420 from Evonik Degussa). Still other suitable surfactants include non-ionic wetting agents and molecular defoamers (e.g., SURFYNOL® 104E from Evonik Degussa) or secondary alcohol ethoxylates (commercially available as TERGITOL® TMN-6, TERGITOL® 15-S-7, TERGITOL® 15-S-9, etc. from The Dow Chemical Co.). In some examples, it may be desirable to utilize a surfactant having a hydrophilic-lipophilic balance (HLB) less than 10. Examples of suitable dispersing aid(s) include those of the SILQUEST™ series from Momentive, including SILQUEST™ A-1230. Whether a single surfactant or dispersing aid is used or a combination of surfactants and/or dispersing aids is used, the total amount of surfactant(s) and/or dispersing aid(s) may range from about 0.01 wt % active to about 6 wt % active based on the total weight of thebinder agent 14. - The
binder agent 14 may also include antimicrobial agent(s). Suitable antimicrobial agents include biocides and fungicides. Example antimicrobial agents may include the NUOSEPT® (Ashland Inc.), UCARCIDE™ or KORDEK™ or ROCIMA™ (Dow Chemical Co.), PROXEL® (Arch Chemicals) series, ACTICIDE® B20 and ACTICIDE® M20 and ACTICIDE® MBL (blends of 2-methyl-4-isothiazolin-3-one (MIT), 1,2-benzisothiazolin-3-one (BIT), and Bronopol) (Thor Chemicals), AXIDE™ (Planet Chemical), NIPACIDE™ (Clariant), blends of 5-chloro-2-methyl-4-isothiazolin-3-one (CIT or CMIT) and MIT under the tradename KATHON™ (Dow Chemical Co.), and combinations thereof. In an example, thebinder agent 14 may include a total amount of antimicrobial agents that ranges from about 0.1 wt % active to about 1 wt % active. - An anti-kogation agent may also be included in the
binder agent 14. Kogation refers to the deposit of dried solids on a heating element of a thermal inkjet printhead. Anti-kogation agent(s) is/are included to assist in preventing the buildup of kogation, and thus may be included when thebinder agent 14 is to be dispensed using a thermal inkjet printhead. Examples of suitable anti-kogation agents include oleth-3-phosphate (e.g., commercially available as CRODAFOS® O3A or CRODAFOS® N-3 acid from Croda), dextran 500k, CRODAFOS™ HCE (phosphate-ester from Croda Int.), CRODAFOS® N10 (oleth-10-phosphate from Croda Int.), DISPERSOGEN® LFH (polymeric dispersing agent with aromatic anchoring groups, acid form, anionic, from Clariant), or a combination of oleth-3-phosphate and a low molecular weight (e.g., <5,000) acrylic acid polymer (e.g., commercially available as CARBOSPERSE™ K-7028 Polyacrylate from Lubrizol). The anti-kogation agent may be present in thebinder agent 14 in an amount ranging from about 0.1 wt % active to about 1 wt % active, based on the total weight of thebinder agent 14. - The balance of the
binder agent 14 is water (e.g., deionized water). As such, the amount of water may vary depending upon the weight percent of theother binder agent 14 components. - Examples of a
printing method 100 andsystem 10, which include thebuild material composition 12 and thebinder agent 14 are shown inFIG. 8 . - As depicted in
FIG. 8 atreference numeral 102, the3D printing system 10 may include aninkjet applicator 16, a supply bed 20 (including a supply of build material composition 12), adelivery piston 26, aspreader 24, afabrication bed 22, and afabrication piston 28. Thedelivery piston 26 and thefabrication piston 28 may be the same type of piston, but are programmed to move in opposite directions. In an example, when a layer of the3D part 35 is to be formed, thedelivery piston 26 may be programmed to push a predetermined amount of thebuild material composition 12 out of the opening in thesupply bed 20 and thefabrication piston 28 may be programmed to move in the opposite direction of thedelivery piston 26 in order to increase the depth of thefabrication bed 22. Thedelivery piston 26 will advance enough so that when thespreader 24 pushes thebuild material composition 12 into thefabrication bed 22 and onto thebuild surface 18 or the previously formed layer, the depth of thefabrication bed 22 is sufficient so that alayer 34 of thebuild material composition 12 and thebinder agent 14 may be formed in thefabrication bed 22. Thespreader 24 is capable of spreading thebuild material composition 12 into thefabrication bed 22 to form thebuild material layer 34, which is relatively uniform in thickness. - In an example, the thickness of the
build material layer 34 ranges from about 10 μm to about 70 μm, although thinner or thicker layers may also be used. For example, the thickness of the layer may range from about 20 μm to about 1000 μm. Depending upon the desired thickness for thelayer 34 and the particle size(s) within thebuild material composition 12, thelayer 34 that is formed in a single build material application may be made up of a single row of thebuild material composition 12 or several rows ofbuild material composition 12. - While the
system 10 is depicted, it is to be understood thatother printing systems 10 may also be used. For example, another support member, such as a build area platform, a platen, a glass plate, or another build surface may be used instead of thefabrication bed 22. Thebuild material composition 12 may be delivered from another source, such as a hopper, an auger conveyer, or the like. It is to be understood that thespreader 24 may be a rigid or flexible blade, which is a more common spreader for metal/metal alloy build materials. However, the spreader may also be replaced by other tools, such as a roller, or a combination of a roller and a blade. - Each of these physical elements of the
3D printing system 10 may be operatively connected to a central processing unit 46 (seeFIG. 9 ) of the3D printing system 10. The central processing unit 46 (e.g., running computerreadable instructions 48 stored on a non-transitory, tangible computer readable storage medium) manipulates and transforms data represented as physical (electronic) quantities within the printer's registers andmemories 50 in order to control the physical elements to create the3D part 35. The data for the selective delivery of thebinder agent 14, thebuild material composition 12, etc. may be derived from a 3D model of the3D part 35 to be formed. For example, theinstructions 48 may cause the controller to utilize an applicator (e.g., an inkjet applicator 16) to selectively dispense thebinder agent 14, and to utilize a build material distributor (spreader 24) to dispense thebuild material composition 12. Thecentral processing unit 46 controls the selective delivery (i.e. dispensing) of thebinder agent 14 in accordance withdelivery control data 52. - The
binder agent 14 may be dispensed from any suitable applicator. As illustrated inFIG. 8 atreference number 102, thebinder agent 14 may be dispensed from an inkjet applicator, such as a thermal inkjet printhead or a piezoelectric inkjet printhead. The printhead may be a drop-on-demand printhead or a continuous drop printhead. Theinkjet applicator 16 may be selected to deliver drops ofbinder agent 14 at a resolution ranging from about 300 dots per inch (DPI) to about 1200 DPI. In other examples, theinkjet applicator 16 may be selected to be able to deliver drops of thebinder agent 14 at a higher or lower resolution. The drop velocity may range from about 5 m/s to about 24 m/s and the firing frequency may range from about 1 kHz to about 100 kHz. Theinkjet applicator 16 may include an array of nozzles through which it is able to selectively eject drops of fluid. In one example, each drop may be in the order of about 5 ng per drop, although it is contemplated that a higher (e.g., 100 ng) or lower (e.g., 1 ng) drop size may be used. In some examples,inkjet applicator 16 is able to deliver variable size drops of thebinder agent 14. - The inkjet applicator(s) 16 may be attached to a moving XY stage or a translational carriage (neither of which is shown) that moves the inkjet applicator(s) 16 adjacent to the
build surface 18 in order to deposit thebinder agent 14 in desirable area(s) 30. In other examples, the applicator(s) 16 may be fixed while a support member (supporting the build surface 18) is configured to move relative thereto. - The inkjet applicator(s) 16 may be programmed to receive commands from the
central processing unit 46 and to deposit thebinder agent 14 according to a pattern of thelayer 34 to be achieved. In an example, a computer model of thepart 35 to be printed is generated using a computer aided design (CAD) program. The computer model of the3D part 35 is sliced into N layers, which are then divided into voxels. The printing parameters for each voxel are computed based on the desired composition and physical properties of thepart 35 to be printed. The printing parameters for each voxel may include the X, Y, and Z coordinates that define its location and the amount of the binder agent 14 (if any) that is to be received. Thecentral processing unit 46 may then use this information to instruct the inkjet applicator(s) 16 as to how much (if any) of thebinder agent 14 should be jetted into each voxel. - The
inkjet applicator 16 selectively applies thebinder agent 14 on those portions 30 of thelayer 34 of thebuild material composition 12 that is to form the intermediate part, and ultimately thefinal 3D part 35. Thebinder agent 14 may not be applied on theentire layer 34, as shown at theportions 32. - After the
binder agent 14 is selectively applied in a pattern on the desired portion(s) 30 of thelayer 34 ofbuild material composition 12, another layer of thebuild material composition 12 is applied, as shown atreference numeral 104 inFIG. 5 , and patterned with thebinder agent 14, as shown atreference numeral 106. The formation and patterning of additional layers may be repeated in order to form theintermediate part 31. - During and/or after formation of the
intermediate part 31, liquid components of thebinder agent 14 may be evaporated. At least substantially evaporation (with or without the application of heat) activates the binder, and the activated binder provides enough adhesive strength to hold theintermediate part 31 together with enough mechanical stability to survive removal from any non-patternedbuild material composition 12. - The
intermediate part 31 may be extracted or separated from the non-patterned build material composition 12 (e.g., in portion(s) 32) by any suitable means. In an example, theintermediate part 31 may be extracted by lifting theintermediate part 31 from the non-patternedbuild material composition 12. Any suitable extraction tool may be used. In some examples, theintermediate part 31 may be cleaned to remove non-patternedbuild material composition 12 from its surface. In an example, theintermediate part 31 may be cleaned with a brush and/or an air jet, may be exposed to mechanical shaking, or may be exposed to other techniques that can remove the non-patternedbuild material composition 12. - The
intermediate part 31 may then be placed in a heating mechanism (not shown). Examples of the heating mechanism include a conventional furnace or oven, a microwave, or devices capable of hybrid heating (i.e., conventional heating and microwave heating). - The heating mechanism may be used to perform a heating sequence, which involves exposing the
intermediate part 31 to a decomposition/reduction temperature or a pyrolysis temperature that decomposes theflow additive 21. The heating sequence may form the 3D object 35 (seeFIG. 6 ). In some examples, heating involves exposure to a series of temperatures. - The series of temperatures may involve heating the
intermediate structure 31 to the decomposition/reduction or pyrolysis temperature, a de-binding temperature, and then to the sintering temperature. Briefly, the decomposition/reduction temperature decomposes/reduces theflow additive nanoparticle 21 to the elemental metal or the pyrolysis temperature removes theflow additive nanoparticle 21, and the de-binding temperature removes the binder, from theintermediate structure 31 to produce a binder-freeintermediate structure 31′, and thestructure 31′ may be sintered to form thefinal 3D object 35. Heating to decompose/pyrolyze, de-bind, and sinter may take place at several different temperatures, where the temperatures for decomposing/pyrolyzing and de-binding are lower than the temperature(s) for sintering. In some instances, heating to de-bind and heating to decompose/pyrolyze may take place at the same temperature or within the same temperature range (e.g., from about 300° C. to about 500° C.). - Heating to decompose/reduce is accomplished at a reducing temperature that is sufficient to thermally decompose/reduce the
flow additive 21. As such, the reducing temperature depends upon theflow additive 21 used. In an example, the reducing temperature ranges from about 250° C. to about 600° C. In another example, the reducing temperature ranges from about 300° C. to about 550° C. - Heating to pyrolyze is accomplished at a thermal decomposition temperature that is sufficient to thermally decompose the
flow additive 21. As such, the temperature for pyrolysis depends upon theflow additive 21 used. In an example, the thermal decomposition temperature ranges from about 250° C. to about 600° C. In another example, the pyrolysis temperature ranges from about 300° C. to about 550° C. Theflow additive 21 may have a clean thermal decomposition mechanism (e.g., leaves non-volatile residue in an amount <5 wt % of the initial binder, and in some instances non-volatile residue in an amount <<1 wt % of the initial binder). Since the amount offlow additive 21 in thebuild material composition 12 is low, any carbon residue that is formed and remains in the part is in a very small amount that does not deleteriously affect the part. - Heating to de-bind is accomplished at a thermal decomposition temperature that is sufficient to thermally decompose the binder. As such, the temperature for de-binding depends upon the binder in the
agent 14. In an example, the thermal decomposition temperature ranges from about 250° C. to about 600° C. In another example, the thermal decomposition temperature ranges from about 300° C. to about 550° C. The binder may have a clean thermal decomposition mechanism (e.g., leaves non-volatile residue in an amount <5 wt % of the initial binder, and in some instances non-volatile residue in an amount <<1 wt % of the initial binder). The smaller residue percentage (e.g., close to 0%) is more desirable. - While not being bound to any theory, it is believed that the binder-free
intermediate structure 31′ may maintain its shape due, for example, to one or more of: i) the low amount of stress experience by thepart 31′ due to it not being physically handled, and/or ii) low level necking occurring between thehost metal particles 15 at the decomposition/reducing temperature or the pyrolysis temperature and at the thermal decomposition temperature of the binder. The at least substantially flow additive and binder-freeintermediate structure 31′ may maintain its shape although the binder is at least substantially removed and thehost metal particles 15 are not yet sintered. - The temperature may be raised to sinter the binder-free
intermediate structure 31′, which can result in the formation of weak bonds that are strengthened throughout sintering. During sintering, thehost metal particles 15 coalesce to form the3D object 35, and so that a desired density of the3D object 35 is achieved. The sintering temperature is a temperature that is sufficient to sinter the remaininghost metal particles 15. The sintering temperature is highly depending upon the composition of thehost metal particles 15. During sintering, the at least substantially flow additive and binder-freeintermediate structure 31′ may be heated to a temperature ranging from about 80% to about 99.9% of the melting point of thehost metal particles 15. In another example, the at least substantially flow additive and binder-freeintermediate structure 31′ may be heated to a temperature ranging from about 90% to about 95% of the melting point of thehost metal particles 15. In still another example, the at least substantially flow additive and binder-freeintermediate structure 31′ may be heated to a temperature ranging from about 60% to about 90% of the melting point of thehost metal particles 15. In still another example, the sintering temperature may range from about 50° C. below the melting temperature ofhost metal particles 15 to about 200° C. below the melting temperature of thehost metal particles 15. The sintering temperature may also depend upon the particle size and time for sintering (i.e., high temperature exposure time). As an example, the sintering temperature may range from about 500° C. to about 1800° C. In another example, the sintering temperature is at least 900° C. An example of a sintering temperature for bronze is about 850° C., and an example of a sintering temperature for stainless steel is between about 1300° C. and about 1400° C. While these temperatures are provided as sintering temperature examples, it is to be understood that the sintering temperature depends upon thehost metal particles 15 that are utilized, and may be higher or lower than the provided examples. Heating at a suitable sintering temperature sinters and coalesces thehost metal particles 15 to form a completed3D object 35. As a result of final sintering, the density may go from 50% density to over 90%, and in some cases very close to 100% of the theoretical density. - The length of time at which the heat (for each of decomposition/reduction or pyrolysis, de-binding, and sintering) is applied and the rate at which the
structure flow additive 21 and binder, characteristics of the host metal particles 15 (e.g., metal type, particle size, etc.), and/or the characteristics of the 3D object/part 46 (e.g., wall thickness). - Heating, respectively, at the decomposition/reduction or pyrolysis temperature and de-binding temperature may occur for a time period ranging from about 10 minutes to about 72 hours. When the
structure 31 contains open porosity to vent out binder and/or flowaid 21 pyrolysis, and/or the amount of the binder and/or flowaid 21 is low, and/or the wall thickness of thestructure 31 is relatively thin, the time period for de-binding and decomposition/reduction or pyrolysis may be 3 hours (180 minutes) or less. Longer times may be used if thestructure 31 has less open porosity, if thestructure 31 has thicker walls, and/or if thestructure 31 has a higher concentration of binder. In an example, the decomposition/reduction or pyrolysis and de-binding time period is about 60 minutes. In another example, the de-binding time period is about 180 minutes. Theintermediate part 31 may be heated to the decomposition/reduction or pyrolysis and/or de-binding temperatures at a heating rate ranging from about 0.5° C./minute to about 20° C./minute. The heating rate (i.e. temperature rise rate) may depend, in part, on one or more of: the amount of the flow additive and/or binder and/or the porosity of theintermediate part 31. - The binder-free
intermediate structure 31′ may be heated at the sintering temperature for a time period ranging from about 20 minutes to about 15 hours. In an example, the sintering time period is 60 minutes. In another example, the sintering time period is 90 minutes. In still another example, the sintering time period is less than or equal to 3 hours. The at least substantially flow additive and binder-freeintermediate structure 31′ may be heated to the sintering temperature at a heating rate ranging from about 1° C./minute to about 20° C./minute. - While
FIGS. 7 and 8 illustrate example 3D printing processes, it is to be understood that thebuild material composition 12 may be used in other additive manufacturing processes. An example of another additive manufacturing process is direct metal laser sintering (DMLS). During DMLS, an energy beam is aimed at a selected region (in some instances less than the entire layer) of a layer of thebuild material composition 12. The energy beam may first applied to cause theflow additive 21 in thebuild material composition 12 to decompose, and then the intensity may be increased to raise the temperature so that the remaininghost metal particles 15, which are exposed to the energy beam, sinter to form the layer of the 3D part. The application of additionalbuild material composition 12 layers and the selective energy beam exposure may be repeated to build up the 3D part layer by layer. In examples that use DMLS, abinder agent 14 may be omitted from the process. - To further illustrate the present disclosure, examples are given herein. It is to be understood that these examples are provided for illustrative purposes and are not to be construed as limiting the scope of the present disclosure.
- Four examples of the build material composition were prepared according to examples of the methods disclosed herein. One comparative build material composition was also prepared according to a comparative method. The host metal used in each of the build material compositions was stainless steel, 316L, grade −22 μm (80%) powder from “Sandvik”, (average particle diameter was about 11 μm).
- The comparative build material composition was a baseline build material composition, which included the stainless steel host particles without any flow additive.
- Iron oxide flow additives prepared according to different examples of the methods disclosed here were used as the example flow additives in the example build material compositions.
- To prepare the first example build material composition, fumed flow additive aggregates including iron oxide nanoparticles that had an average flow additive primary particle size of about 30 nm were obtained.
- The iron oxide flow additive aggregates were mixed with the stainless steel host particles via rolling the powder mix in a plastic container for about 2 hours. Mixing broke the iron oxide flow additive aggregates into individual nanoparticles and aggregate fragments, and disposed the individual nanoparticles and aggregate fragments on the stainless steel host metal particles. The first example build material composition included 0.1 wt % of the first example iron oxide flow additive.
- To prepare the second example build material composition, fumed flow additive aggregates including iron oxide nanoparticles that had an average flow additive primary particle size of about 20 nm were obtained.
- The iron oxide flow additive aggregates were mixed with the stainless steel host particles via rolling the powder mix in a plastic container for about 2 hours. Mixing broke the iron oxide flow additive aggregates into individual nanoparticles and aggregate fragments, and disposed the individual nanoparticles and aggregate fragments on the stainless steel host metal particles. The second example build material composition included 0.1 wt % of the second example iron oxide flow additive.
- To prepare the third example build material composition, fumed flow additive aggregates including iron oxide nanoparticles that had an average flow additive primary particle size of about 10 nm were obtained.
- The iron oxide flow additive aggregates were mixed with the stainless steel host particles via rolling the powder mix in a plastic container for about 2 hours. Mixing broke the iron oxide flow additive aggregates into individual nanoparticles and aggregate fragments, and disposed the individual nanoparticles and aggregate fragments on the stainless steel host metal particles. The third example build material composition included 0.1 wt % of the third example iron oxide flow additive.
- To prepare the fourth example build material composition, fumed flow additive aggregates included iron oxide nanoparticles that had an average flow additive primary particle size of about 7 nm.
- The iron oxide flow additive aggregates were mixed with the stainless steel host particles via rolling the powder mix in a plastic container for about 2 hours. Mixing broke the iron oxide flow additive aggregates into individual nanoparticles and aggregate fragments, and disposed the individual nanoparticles and aggregate fragments on the stainless steel host metal particles. The fourth example build material composition included 0.1 wt % of the fourth example iron oxide flow additive.
- The flowability of each of the build material compositions was evaluated using a Granupack density tester tap (available from Granutools, www.granutools.com). The results of flowability tests are shown in
FIG. 10 . InFIG. 10 , the Hausner Ratio values are shown on the y-axis, and the build material compositions are identified on the x-axis. - The comparative build material composition (labeled “Control” in
FIG. 10 ) demonstrated poor flowability and thus poor spreadability, with a Hausner ratio of about 1.29. The first example build material (labeled “30 nm” inFIG. 10 ) had a Hausner Ratio of about 1.25. The first example build material had a lower Hausner Ratio than the baseline (comparative) build material composition. It is believed that including a larger amount of the first example iron oxide flow additive may result in a lower Hausner ratio and a greater spreadability. The second example build material (labeled “20 nm” inFIG. 10 ) had a Hausner Ratio of about 1.27. The second example build material had a lower Hausner Ratio than the baseline (comparative) build material composition. It is believed that including a larger amount of the second example iron oxide flow additive may result in a lower Hausner ratio and a greater spreadability. The third example build material (labeled “10 nm” inFIG. 10 ) had a Hausner Ratio of about 1.165. The third example build material had a lower Hausner Ratio than the baseline (comparative) build material composition, and was considered spreadable. The fourth example build material (labeled “7 nm” inFIG. 10 ) had a Hausner Ratio of about 1.145. The fourth example build material had a lower Hausner Ratio than the baseline (comparative) build material composition, and was considered spreadable. - As shown in
FIG. 10 , the addition of example iron oxide flow additives that were prepared according to examples of the methods disclosed herein lowered the Hausner Ratio of the example build material compositions compared to the host metal particles without any flow additive (the comparative build material composition). These results indicate that method of making the build material composition (and in particular the method of making the flow additive) impacts the flowability/speadability of the build material composition. - Four additional examples of the build material composition were prepared according to examples of the methods disclosed herein. The host metal used in each of the additional example build material compositions was stainless steel, 316L, grade −22 μm (80%) powder from “Sandvik”, (average particle diameter was about 11 μm). The fourth example iron oxide flow additive used in the fourth example build material composition (in Example 1) was also used in each of the additional example build material compositions.
- To prepare the fifth example build material composition, the fourth example iron oxide flow aggregates were mixed with the stainless steel host particles via rolling the powder mix in a plastic container for about 2 hours. Mixing broke the iron oxide flow additive aggregates into individual nanoparticles and aggregate fragments, and disposed the individual nanoparticles and aggregate fragments on the stainless steel host metal particles. The fifth example build material composition included 0.05 wt % of the fourth example iron oxide flow additive.
- To prepare the sixth example build material composition, the fourth example iron oxide flow aggregates were mixed with the stainless steel host particles via rolling the powder mix in a plastic container for about 2 hours. Mixing broke the iron oxide flow additive aggregates into individual nanoparticles and aggregate fragments, and disposed the individual nanoparticles and aggregate fragments on the stainless steel host metal particles. The sixth example build material composition included 0.03 wt % of the fourth example iron oxide flow additive.
- To prepare the seventh example build material composition, the fourth example iron oxide flow aggregates were mixed with the stainless steel host particles via rolling the powder mix in a plastic container for about 2 hours. Mixing broke the iron oxide flow additive aggregates into individual nanoparticles and aggregate fragments, and disposed the individual nanoparticles and aggregate fragments on the stainless steel host metal particles. The seventh example build material composition included 0.02 wt % of the fourth example iron oxide flow additive.
- The flowability of each of the additional build material compositions was evaluated using a Granupack density tester tap. The results of flowability tests are shown in
FIG. 11 . Also shown inFIG. 11 are the results of flowability tests of the fourth example build material composition (including 0.1 wt % of the flow additive, from Example 1), the comparative build material composition (including 0 wt % of a flow additive, from Example 1), and the host metal with different amounts of a fumed silica flow aid (also shown inFIG. 1 ). InFIG. 11 , the Hausner Ratio values are shown on the y-axis, and amounts (in wt %) of flow additive present in the build material compositions are shown on the x-axis. - Again, the comparative build material composition (corresponding with “0.00%” in
FIG. 11 ) demonstrated poor flowability, with a Hausner ratio of about 1.29. The fourth example build material (corresponding with “0.10%” of “Fumed FeOx 7 nm” inFIG. 11 ) had a Hausner Ratio of about 1.145. The fourth example build material had a lower Hausner Ratio than the baseline (comparative) build material composition, had a lower Hausner Ratio than the build material including the same amount of the silica flow aid, and was considered spreadable. The fifth example build material (corresponding with “0.05%” of “Fumed FeOx 7 nm” inFIG. 11 ) had a Hausner Ratio of about 1.142. The fifth example build material had a lower Hausner Ratio than the baseline (comparative) build material composition, had a lower Hausner Ratio than the build material including the same amount of the silica flow aid, and was considered spreadable. The sixth example build material (corresponding with “0.03%” of “Fumed FeOx 7 nm” inFIG. 11 ) had a Hausner Ratio of about 1.15. The sixth example build material had a lower Hausner Ratio than the baseline (comparative) build material composition, had a lower Hausner Ratio than the build materials including the similar amounts of the silica flow aid, and was considered spreadable. The seventh example build material (corresponding with “0.02%” of “Fumed FeOx 7 nm” inFIG. 11 ) had a Hausner Ratio of about 1.155. The seventh example build material had a lower Hausner Ratio than the baseline (comparative) build material composition, had a lower Hausner Ratio than the build material including the same amount of the silica flow aid, and was considered spreadable. - As shown in
FIG. 11 , the addition of example iron oxide flow additives that were prepared according to examples of the methods disclosed herein lowered the Hausner Ratio of the example build material compositions compared to the host metal particles without any flow additive (the comparative build material composition). As also shown inFIG. 11 , the addition of example iron oxide flow additives also lowered the Hausner Ratio of the example build material compositions compared to the host metal particles with a comparative fumed silica flow aid. These results indicate that method of making the build material composition (and in particular the method of making the flow additive) impacts the flowability/speadability of the build material composition. - Further, the seventh example build material was used in an example of a 3D printing method disclosed herein. The seventh example build material composition was able to be spread into substantially uniform build material layers. Thus, the seventh example build material composition was shown to be a suitable build material composition for the 3D printing methods disclosed herein.
- The structure of the fourth example iron oxide flow additive was compared to the structure of a comparative iron oxide flow additive using SEM imaging. The comparative iron oxide flow additive was obtained by freezing a dispersion of iron oxide nanoparticles and lyophilizing the frozen dispersion.
- The fourth example iron oxide flow additive is shown in
FIG. 12 . The comparative iron oxide flow additive is shown inFIG. 13 . ComparingFIGS. 12 and 13 , it is shown that an iron oxide flow additive prepared according to the method disclosed herein (FIG. 12 ) has a less dense structure with a higher porosity that is more easily broken into smaller fragments than an iron oxide flow additive prepared according to a comparative freeze-drying method (FIG. 13 ). - The fourth example iron oxide flow additive and the comparative freeze-dried flow additive were mixed with the 316L stainless steel powder, and the build material composition with the fourth example iron oxide flow additive was 3 to 5 times more spreadable than the comparative build material composition.
- It is to be understood that the ranges provided herein include the stated range and any value or sub-range within the stated range, as if the value(s) or sub-range(s) within the stated range were explicitly recited. For example, a range from about 0.1 wt % to about 5 wt % should be interpreted to include the explicitly recited limits of about 0.1 wt % to about 5 wt %, as well as individual values, such as 0.73 wt %, 2.6 wt %, 4.2 wt %, etc., and sub-ranges, such as from about 0.25 wt % to about 3.25 wt %, from about 1.5 wt % to about 3.85 wt %, from about 2.0 wt % to about 4.95 wt %, etc. Furthermore, when “about” is utilized to describe a value, this is meant to encompass minor variations (up to +/−10%) from the stated value. As used herein, the term “few” means about three.
- Reference throughout the specification to “one example”, “another example”, “an example”, and so forth, means that a particular element (e.g., feature, structure, and/or characteristic) described in connection with the example is included in at least one example described herein, and may or may not be present in other examples. In addition, it is to be understood that the described elements for any example may be combined in any suitable manner in the various examples unless the context clearly dictates otherwise.
- In describing and claiming the examples disclosed herein, the singular forms “a”, “an”, and “the” include plural referents unless the context clearly dictates otherwise.
- While several examples have been described in detail, it is to be understood that the disclosed examples may be modified. Therefore, the foregoing description is to be considered non-limiting.
Claims (15)