TWI824509B - 黏著片材 - Google Patents
黏著片材 Download PDFInfo
- Publication number
- TWI824509B TWI824509B TW111117102A TW111117102A TWI824509B TW I824509 B TWI824509 B TW I824509B TW 111117102 A TW111117102 A TW 111117102A TW 111117102 A TW111117102 A TW 111117102A TW I824509 B TWI824509 B TW I824509B
- Authority
- TW
- Taiwan
- Prior art keywords
- adhesive sheet
- layer
- adhesive
- gas generating
- gas
- Prior art date
Abstract
本發明提供一種黏著片材,其同時實現優異之黏著性與剝離性,且被黏著體視認性(隔著黏著片材之視認性)優異。
本發明之黏著片材具備藉由雷射光照射而產生氣體之氣體產生層,霧度值為50%以下。於一實施方式中,上述氣體產生層之厚度為0.1 μm~50 μm。於一實施方式中,上述氣體產生層為可吸收紫外線之層。於一實施方式中,上述氣體產生層含有紫外線吸收劑。
Description
本發明係關於一種黏著片材。
先前,於對電子零件進行處理(加工)時,存在進行如下操作之情形,即,於處理時將被處理體經由黏著片材而暫時固定於固定台,於處理後將被處理體自該黏著片材剝離。作為此種操作中所使用之黏著片材,存在使用如下黏著片材之情形,該黏著片材於處理時具有特定之黏著力,於處理後黏著力可下降。作為此種黏著片材之一,提出有使黏著劑層中含有熱膨脹性微小球而構成之黏著片材(例如專利文獻1)。含有熱膨脹性微小球之黏著片材具有如下特徵:具有特定之黏著力,且藉由利用加熱使熱膨脹性微小球膨脹,而於黏著面形成凹凸,從而使接觸面積減小,因此黏著力會下降或消失。此種黏著片材具有無外應力便可容易地剝離被處理體之優點。
然而,含有熱膨脹性微小球之黏著片材之透光性較低,於使用該黏著片材之情形時,產生如下問題:難以隔著黏著片材視認為了顯示電子零件之暫時固定位置而設於固定台之標記。
先前技術文獻
專利文獻
專利文獻1:日本專利特開2001-131507號公報
[發明所欲解決之問題]
本發明係為了解決上述先前之課題而完成者,其目的在於提供一種同時實現優異之黏著性與剝離性,且被黏著體視認性(隔著黏著片材之視認性)優異之黏著片材。
[解決問題之技術手段]
本發明之黏著片材具備藉由雷射光照射而產生氣體之氣體產生層,且霧度值為50%以下。
於一實施方式中,上述氣體產生層之厚度為0.1 μm~50 μm。
於一實施方式中,上述氣體產生層為可吸收紫外線之層。
於一實施方式中,上述氣體產生層含有紫外線吸收劑。
於一實施方式中,上述黏著片材之波長360 nm之紫外線透過率為30%以下。
於一實施方式中,上述黏著片材之波長500 nm之紫外線透過率為50%~100%。
於一實施方式中,上述氣體產生層為產生烴系氣體之層。
於一實施方式中,上述氣體產生層之氣化起始溫度為150℃~500℃。
於一實施方式中,上述黏著片材之10%重量減少溫度為200℃~500℃。
於一實施方式中,上述黏著片材於上述氣體產生層之至少單側進而具備黏著劑層,該黏著劑層係其表面藉由對該黏著片材照射雷射光而變形之層。
於一實施方式中,上述黏著劑層之厚度為0.1 μm~50 μm。
於一實施方式中,上述黏著劑層藉由對上述黏著片材照射雷射光而發泡。
根據本發明之其他態樣,提供一種電子零件之處理方法。該電子零件之處理方法包括:將電子零件貼附於上述黏著片材上;及對該黏著片材照射雷射光而自該黏著片材剝離該電子零件。
於一實施方式中,上述電子零件之剝離係選擇位置地進行。
於一實施方式中,上述處理方法包括:於將上述電子零件貼附於上述黏著片材後且自該黏著片材剝離該電子零件前,對該電子零件進行特定處理。
於一實施方式中,上述處理為研磨加工、切割加工、黏晶、打線接合、蝕刻、蒸鍍、成型、電路形成、檢查、產品檢驗、洗淨、轉印、排列、修復或裝置表面保護。
根據本發明之其他態樣,提供一種電子零件之處理方法。該電子零件之處理方法包括:自上述黏著片材剝離上述電子零件之後,將電子零件配置於其他片材。
[發明之效果]
根據本發明,可提供一種同時實現優異之黏著性與剝離性,且被黏著體視認性(隔著黏著片材之視認性)優異之黏著片材。
A. 黏著片材之概要圖1(a)係本發明之較佳實施方式之黏著片材之概略剖視圖。黏著片材100具備氣體產生層10。氣體產生層10藉由雷射光照射而產生氣體。更詳細而言,氣體產生層10係藉由利用雷射光照射使其成分氣化而產生氣體之層。作為雷射光,代表性而言使用UV(ultraviolet,紫外線)雷射光。氣體產生層10可具有特定之黏著力。
圖1(b)係本發明之其他實施方式之黏著片材之概略剖視圖。黏著片材100'具備氣體產生層10與配置於氣體產生層10之單面之至少一層之黏著劑層20。黏著劑層20之表面會藉由對黏著片材(實質上為氣體產生層)照射雷射光而變形。於一實施方式中,該變形會因自氣體產生層10產生之氣體,而產生於黏著劑層20之與氣體產生層10相反之側。
本發明之黏著片材可於氣體產生層或黏著劑層貼附電子零件等被處理體而使用。本發明之黏著片材具備氣體產生層,藉由雷射光照射而於微小範圍局部地產生氣體。藉由此種氣體之產生,而產生貼附面之變形,其結果,可使被黏著體良好地剝離。於黏著片材具備黏著劑層之情形時,如上所述,因該氣體之產生,而於黏著劑層產生變形,其結果,於照射過雷射光之部分表現剝離性。代表性而言,雷射光自氣體產生層之與黏著劑層相反之側照射。根據本發明,能以如上所述之方式於微小範圍產生變形,故而於對極其微細之小型電子零件進行處理(加工)時,亦可使該小型電子零件良好地剝離。又,即便於需要剝離之小型電子零件與不需要剝離之小型電子零件相鄰地暫時固定之情形時,亦可於剝離對象之部位進行剝離,於剝離對象外之部位不進行剝離,即,可僅使需要剝離之小型電子零件剝離,亦可防止小型電子零件之不需要之脫離。為使黏著劑層之變形良好地產生,較佳為以上述產生之氣體之至少一部分不自黏著片材逸出之方式阻隔,黏著劑層可作為氣體阻隔層發揮作用。
所謂黏著劑層之變形係指於黏著劑層之法線方向(厚度方向)與水平方向(與厚度方向正交之方向)產生之位移。黏著劑層之變形例如藉由如下方式產生:藉由使用波長355 nm、光束直徑約20 μm
之UV雷射光,於0.80 mW功率、40 kHz頻率下進行脈衝掃描,而自氣體產生層產生氣體。關於變形後之形狀,例如對於脈衝掃描過之任意1點,於雷射光照射結束24小時後,根據共聚聚焦雷射顯微鏡或非接觸型干涉顯微鏡(WYKO)等之測定進行觀測。其形狀可為發泡(凸)、貫通孔(凹凸)、凹陷(凹),藉由該等變形而可產生剝離性。於要沿法線方向將電子零件效率良好地剝離時,較佳為雷射光照射前後之法線方向之位移變化較大,尤其適合形成發泡形狀者。發泡(凸)係以未照射部之黏著片材表面為基準,將最高點定義為垂直位移Y,將半峰全幅值定義為水平位移X(直徑)。關於雷射光照射後形成孔之貫通孔(凹凸)與凹陷(凹),將最高點與最低點之差定義為垂直位移Y,將孔之直徑定義為水平位移X。以下,亦將藉由雷射光照射而變形之部分稱為「變形部」。
圖2係本發明之其他實施方式之黏著片材之概略剖視圖。黏著片材200於氣體產生層10與黏著劑層20之間進而具備中間層30。藉由設置中間層,可容易地控制黏著劑層之變形(詳情於後文敍述)。又,中間層可與黏著劑層協作而作為氣體阻隔層發揮作用。因此,藉由設置中間層,氣體阻隔性會提高,可獲得黏著劑層更佳地變形之黏著片材。中間層可為單層,亦可為複數層。
雖未圖示,但上述黏著片材可進而具備其他層。例如,亦可於氣體產生層之與黏著劑層為相反側之面設有基材、其他黏著劑層等。作為基材,例如使用包含任意適當之樹脂之膜。
本發明之黏著片材之特徵在於,霧度值為50%以下。本發明中,可不含有不溶性之填料等而形成氣體產生層、黏著劑層及中間層,因此可獲得霧度值較小,透光性較高,白濁得到抑制之黏著片材。上述黏著片材於雷射照射前(暫時固定時),透明性較高。若使用此種黏著片材,則例如可隔著黏著片材視認被黏著體(例如,用於暫時固定電子零件之台),從而例如可隔著該黏著片材較佳地視認為了顯示電子零件之暫時固定位置而設於固定台之標記。此種效果為利用含有不溶性之填料之黏著片材(例如,作為剝離性表現層之黏著劑層中含有熱膨脹性微小球之黏著片材)無法獲得之優異效果。
本發明之黏著片材之霧度值較佳為0%~50%,更佳為0.01%~40%,進而較佳為0.05%~30%,尤佳為0.1%~20%。若為此種範圍,則本發明之上述效果變得更顯著。
本發明之黏著片材之黏著劑層相對於SUS430之黏著力較佳為0.1 N/20 mm以上,更佳為0.2 N/20 mm~50 N/20 mm,進而較佳為0.5 N/20 mm~40 N/20 mm,尤佳為0.7 N/20 mm~20 N/20 mm,最佳為1 N/20 mm~10 N/20 mm。若為此種範圍,則可獲得例如作為電子零件之製造中所使用之暫時固定用片材而表現出良好之黏著性之黏著片材。本說明書中,所謂黏著力係指於23℃之環境下藉由依照JIS(Japanese Industrial Standards,日本工業標準) Z 0237:2000之方法(貼合條件:2 kg輥1個往返,拉伸速度:300 mm/min,剝離角度180°)而測定出之黏著力。
於一實施方式中,上述氣體產生層具有特定之黏著力。本發明之黏著片材之氣體產生層相對於SUS430之黏著力較佳為0.1 N/20 mm以上,更佳為0.5 N/20 mm~50 N/20 mm,進而較佳為1 N/20 mm~40 N/20 mm,尤佳為1.5 N/20 mm~30 N/20 mm,最佳為2 N/20 mm~20 N/20 mm。若為此種範圍,則可獲得例如作為電子零件之製造中所使用之暫時固定用片材而表現出良好之黏著性之黏著片材。
本發明之黏著片材之厚度較佳為2 μm~200 μm,更佳為3 μm~150 μm,進而較佳為5 μm~120 μm。
本發明之黏著片材之水蒸氣透過率較佳為5000 g/(m
2・day)以下,更佳為4800 g/(m
2・day)以下,進而較佳為4500 g/(m
2・day)以下,進而較佳為4200 g/(m
2・day)以下。具備具有此種範圍之水蒸氣透過率之黏著劑層(視需要進而具備中間層)之黏著片材中,防止藉由雷射光照射而產生之氣體之逸出,於黏著劑層形成優異形狀之變形部。若使用此種黏著片材,則可精度良好地使小型被黏著體(例如,電子零件)剝離。本發明之黏著片材之水蒸氣透過率越小越佳,其下限值例如為0.1 g/(m
2・day)。水蒸氣透過率可於30℃、90% RH之環境下藉由依照JIS K7129B之測定法而測定。
包含上述黏著劑層與中間層之積層體之水蒸氣透過率較佳為10000 g/(m
2・day)以下,更佳為7000 g/(m
2・day)以下,進而較佳為5000 g/(m
2・day)以下,進而較佳為4800 g/(m
2・day)以下,尤佳為4500 g/(m
2・day)以下,最佳為4200 g/(m
2・day)以下。若為此種範圍,則包含黏著劑層與中間層之積層體作為氣體阻隔層良好地發揮作用,於黏著劑層形成優異形狀之變形部。若使用此種黏著片材,則可精度良好地使小型被黏著體(例如,電子零件)剝離。包含黏著劑層與中間層之積層體之水蒸氣透過率越小越佳,其下限值例如為1 g/(m
2・day)。
包含上述黏著劑層與中間層之積層體之穿刺強度度較佳為10 mN~5000 mN,更佳為30 mN~4000 mN,進而較佳為50 mN~3000 mN,尤佳為100 mN~2000 mN。若為此種範圍,則包含黏著劑層與中間層之積層體作為氣體阻隔層良好地發揮作用,且較佳地產生藉由氣體之產生所引起之形狀變化,其結果,於黏著劑層形成優異形狀之變形部。若使用此種黏著片材,則可精度良好地使小型被黏著體(例如,電子零件)剝離。穿刺強度係如圖3所示,使用壓縮試驗機6(Kato Tech公司製造,商品名「KES-G5」),將樣品4(例如,積層體)夾於具有直徑11.28 mm之圓形開口部之試樣保持器5A、5B而測定。更詳細而言,可於23℃之測定溫度下,於該圓形開口部之圓形開口部中心,將穿刺針(曲率半徑:1 mm)對樣品穿刺(穿刺速度:0.1 mm/s),將於破裂點之最大負荷作為穿刺強度。
包含上述黏著劑層與中間層之積層體之波長360 nm之紫外線透過率較佳為50%~100%,更佳為60%~95%。
上述黏著片材之波長360 nm之紫外線透過率較佳為30%以下,更佳為20%以下,進而較佳為15%以下,尤佳為10%以下,最佳為5%以下。黏著片材之波長360 nm之紫外線透過率之下限例如為0%(較佳為0.05%,更佳為0.1%)。
上述黏著片材之波長500 nm之紫外線透過率較佳為50%~100%,更佳為60%~99%,進而較佳為70%~98%,尤佳為80%~97%。
上述黏著片材之10%重量減少溫度較佳為200℃~500℃,更佳為220℃~450℃,進而較佳為250℃~400℃,尤佳為270℃~370℃。若為此種範圍,則可獲得藉由雷射光照射而可形成更良好之變形部之黏著片材。所謂黏著片材之10%重量減少溫度係指使黏著片材升溫時之TGA分析中,相對於升溫前之重量而減少10重量%(即,黏著片材之重量相對於照射前之重量而成為90%)之時間點之溫度。
B. 氣體產生層氣體產生層可為能吸收紫外線之層。於一實施方式中,氣體產生層含有紫外線吸收劑。藉由含有紫外線吸收劑,可形成可吸收雷射光而進行氣化之氣體產生層。代表性而言,氣體產生層含有紫外線吸收劑與黏著劑A。較佳為紫外線吸收劑溶解於黏著劑A而存在。若紫外線吸收劑溶解於黏著劑A而存在,則可獲得如下黏著片材,其可於貼附面(氣體產生層表面及/或黏著劑層表面)之任意部位產生變形部(例如,凹凸部),且變形部(例如,凹凸部)之形狀之偏差較少。若使用此種黏著片材,則可於所需部位精度良好地產生變形部(例如,凹凸部),本發明之效果變得顯著。再者,本說明書中,所謂「溶解於黏著劑而存在」之狀態係指紫外線吸收劑未以粒子之形式存在於氣體產生層中。更具體而言,上述氣體產生層中,較佳為不含利用X射線CT(computer tomography,電腦斷層掃描)之氣體產生層截面內之粒子分佈測定中粒徑為10 μm以上之紫外線吸收劑。再者,氣體產生層可於黏著劑中含有不溶之成分,亦可不含有。於一實施方式中,氣體產生層中之不溶成分之有無及含量藉由氣體產生層之霧度值而評價,霧度值越小,評價為氣體產生層中之不溶成分之含量越少。較佳為氣體產生層於黏著劑中實質上不含不溶之成分。
上述氣體產生層截面之利用奈米壓痕法所得之彈性模數較佳為0.01 MPa~1000 MPa,更佳為0.05 MPa~800 MPa。若為此種範圍,則較佳地產生藉由氣體之產生所引起之氣體產生層之形狀變化,其結果,於貼附面(氣體產生層表面及/或黏著劑層表面)形成優異形狀之變形部。所謂利用奈米壓痕法所得之彈性模數係指跨及負載時、卸載時連續地測定將壓頭壓入至試樣(例如,黏著面)時對壓頭之負載負荷與壓入深度,並根據所得之負載負荷-壓入深度曲線而求出之彈性模數。利用奈米壓痕法所得之彈性模數係以如下方式獲得:對於藉由將金剛石製之Berkovich型(三角錐型)探針垂直地壓抵於測定對象層切出之截面而獲得之位移-負荷遲滯曲線,利用測定裝置附帶之軟體(triboscan)進行數值處理。本說明書中,所謂截面之利用奈米壓痕法所得之彈性模數係使用奈米壓痕儀(Hysitron Inc公司製造之Triboindenter TI-950),藉由在特定溫度(25℃)之單一壓入法,於壓入速度約500 nm/sec、拔出速度約500 nm/sec、壓入深度約1500 nm之測定條件下測定出之彈性模數。再者,氣體產生層之彈性模數可藉由該層中所含之材料之種類、構成材料之基礎聚合物之結構、添加至該層中之添加劑之種類、量等而進行調整。再者,本說明書中,於未言及截面或表面而僅記作利用奈米壓痕法所得之彈性模數時,該彈性模數係指截面之利用奈米壓痕法所得之彈性模數。
上述氣體產生層表面之利用奈米壓痕法所得之彈性模數較佳為0.01 MPa~1000 MPa,更佳為0.05 MPa~800 MPa。若為此種範圍,則較佳地產生藉由氣體之產生所引起之氣體產生層之形狀變化,其結果,於黏著劑層形成優異形狀之變形部。所謂利用奈米壓痕法所得之彈性模數係指跨及負載時、卸載時連續地測定將壓頭壓入至試樣(例如,黏著面)時對壓頭之負載負荷與壓入深度,並根據所得之負載負荷-壓入深度曲線而求出之彈性模數。利用奈米壓痕法所得之彈性模數係以如下方式獲得:對於藉由將金剛石製之Berkovich型(三角錐型)探針垂直地壓抵於測定對象層切出之截面而獲得之位移-負荷遲滯曲線,利用測定裝置附帶之軟體(triboscan)進行數值處理。本說明書中,所謂表面之利用奈米壓痕法所得之彈性模數係使用奈米壓痕儀(Hysitron Inc公司製造之Triboindenter TI-950),藉由在特定溫度(25℃)之單一壓入法,於壓入速度約500 nm/sec、拔出速度約500 nm/sec、壓入深度約3000 nm之測定條件下測定出之彈性模數。再者,氣體產生層之彈性模數可藉由該層中所含之材料之種類、構成材料之基礎聚合物之結構、添加至該層中之添加劑之種類、量等而進行調整。本發明中,將截面作為測定面藉由上述方法而測定之利用奈米壓痕法所得之彈性模數、與將表面作為測定面藉由上述方法而測定之利用奈米壓痕法所得之彈性模數並無顯著差異,於難以進行自截面之測定之情形時可採用自表面測定之值作為自截面之測定值。
上述氣體產生層之氣化起始溫度較佳為150℃~500℃,更佳為170℃~450℃,進而較佳為190℃~420℃,尤佳為200℃~400℃。若為此種範圍,則可獲得藉由雷射光照射而可形成更良好之變形部之黏著片材。再者,本說明書中,所謂氣體產生層之氣化起始溫度係指根據使黏著片材升溫時之EGA分析(evolved gas analysis,釋出氣體分析)算出之氣體產生上升溫度。所謂氣體產生上升溫度係以達到根據EGA分析所得之EGA/MS圖譜之最大氣體產生峰值之半值的溫度而定義。氣化起始溫度越低,雷射光照射時開始產生氣體之溫度越低,於利用更小功率進行雷射光照射之情形時亦會產生充分之氣體量。於一實施方式中,氣體產生層之氣化起始溫度相當於紫外線吸收劑之氣化起始溫度。
上述氣體產生層之10%重量減少溫度較佳為150℃~500℃,更佳為170℃~450℃,進而較佳為200℃~400℃。若為此種範圍,則可獲得藉由雷射光照射而可形成更良好之變形部之黏著片材。所謂氣體產生層之10%重量減少溫度係指使黏著片材升溫時(例如,藉由雷射光照射而升溫時)之TGA分析(thermogravimetric analysis,熱重量分析)中,氣體產生層之重量相對於升溫前之重量而減少10重量%(即,氣體產生層之重量相對於升溫前之重量而成為90%)之時間點的溫度。
上述氣體產生層之厚度較佳為0.1 μm~50 μm,更佳為1 μm~40 μm,進而較佳為2 μm~30 μm,尤佳為5 μm~20 μm。若為此種範圍,則可獲得藉由雷射光照射而可形成更良好之變形部之黏著片材。
上述氣體產生層之利用奈米壓痕法所得之彈性模數Er(gas)[單位:MPa]與厚度h(gas)[單位:μm]滿足下述式(1)。
Log(Er(gas)×10
6)≧8.01×h(gas)
-0.116・・・(1)
本發明中,藉由以滿足上述式(1)之方式構成氣體產生層,而防止因自氣體產生層產生之氣體所引起之過度變形,從而黏著片材藉由雷射光照射而良好地變形。藉由形成此種氣體產生層,而無需配置較厚之阻隔層(黏著劑層)作為防止過度變形之層便可產生微小範圍內之表面變形。更具體而言,可利用氣體產生層單獨體使表面變形,或柔軟地構成黏著劑層(氣體阻隔層)。
於一實施方式中,利用奈米壓痕法所得之彈性模數Er(gas)[單位:MPa]與厚度h(gas)[單位:μm]滿足下述式(2)。於一實施方式中,利用奈米壓痕法所得之彈性模數Er(gas)[單位:MPa]與厚度h(gas)[單位:μm]滿足下述式(3)。
Log(Er(gas)×10
6)≧7.66×h(gas)
-0.092・・・(2)
Log(Er(gas)×10
6)≧7.52×h(gas)
-0.081・・・(3)
若為此種範圍,則上述效果變得更顯著。
於一實施方式中,利用奈米壓痕法所得之彈性模數Er(gas)[單位:MPa]與厚度h(gas)[單位:μm]進而滿足下述式(4)。
Log(Er(gas)×10
6)≦47.675×h(gas)
-0.519・・・(4)
上述氣體產生層之波長360 nm之紫外線透過率較佳為30%以下,更佳為20%以下,進而較佳為15%以下,尤佳為10%以下,最佳為5%以下。氣體產生層之波長360 nm之紫外線透過率之下限例如為0%(較佳為0.05%,更佳為0.1%)。
上述氣體產生層之霧度值較佳為55%以下,更佳為0.1%~50%,進而較佳為0.5%~40%。該霧度值成為氣體產生層中之黏著劑(實質上為基礎聚合物)與紫外線吸收劑之相容性之指標。霧度值係根據入射可見光區域(波長:380 nm~780 nm)之光時擴散透過光相對於全光線透過光之比率而求出。於將光之波長尺寸視為最小單位,在波長尺寸以上,濃度與組成均勻之情形時,透明性較高,即,相容性較高。另一方面,於濃度與組成不均勻之情形時,產生光之散射,產生白濁,即,相容性變低。若氣體產生層之霧度為上述範圍,則可成為紫外線吸收劑無偏倚地存在而構成之黏著片材。此種黏著片材藉由雷射光照射而精度良好地表現剝離性。
B-1.紫外線吸收劑
作為紫外線吸收劑,只要獲得本發明之效果,則可使用任意適當之紫外線吸收劑。作為紫外線吸收劑,例如可例舉:二苯甲酮系紫外線吸收劑、三𠯤系紫外線吸收劑、苯并***系紫外線吸收劑、水楊酸酯系紫外線吸收劑、氰基丙烯酸酯系紫外線吸收劑等。其中較佳為三𠯤系紫外線吸收劑。尤其於使用丙烯酸系黏著劑作為黏著劑A之情形時,三𠯤系紫外線吸收劑由於與該丙烯酸系黏著劑之基礎聚合物之相容性較高,故而可較佳地使用。藉由使用三𠯤系紫外線吸收劑,可形成霧度值較小之氣體產生層。三𠯤系紫外線吸收劑更佳為包含具有羥基之化合物,尤佳為包含羥基苯基三𠯤系化合物之紫外線吸收劑(羥基苯基三𠯤系紫外線吸收劑)。
作為羥基苯基三𠯤系紫外線吸收劑,例如可例舉:2-(4,6-雙(2,4-二甲基苯基)-1,3,5-三𠯤-2-基)-5-羥基苯與[(C10-C16(主要是C12-C13)烷氧基)甲基]環氧乙烷之反應產物(商品名「TINUVIN 400」,BASF公司製造)、2-[4,6-雙(2,4-二甲基苯基)-1,3,5-三𠯤-2-基]-5-[3-(十二烷氧基)-2-羥基丙氧基]苯酚、2-(2,4-二羥基苯基)-4,6-雙-(2,4-二甲基苯基)-1,3,5-三𠯤與縮水甘油酸(2-乙基己基)酯之反應產物(商品名「TINUVIN 405」,BASF公司製造)、2,4-雙(2-羥基-4-丁氧基苯基)-6-(2,4-二丁氧基苯基)-1,3,5-三𠯤(商品名「TINUVIN 460」,BASF公司製造)、2-(4,6-二苯基-1,3,5-三𠯤-2-基)-5-[(己基)氧基]苯酚(商品名「TINUVIN 1577」,BASF公司製造)、2-(4,6-二苯基-1,3,5-三𠯤-2-基)-5-[2-(2-乙基己醯氧基)乙氧基]苯酚(商品名「Adekastab LA-46」,ADEKA股份有限公司製造)、2-(2-羥基-4-[1-辛氧基羰基乙氧基]苯基)-4,6-雙(4-苯基苯基)-1,3,5-三𠯤(商品名「TINUVIN 479」,BASF公司製造)、BASF公司製造之商品名「TINUVIN 477」等。
作為苯并***系紫外線吸收劑(苯并***系化合物),例如可例舉:2-(2-羥基-5-第三丁基苯基)-2H-苯并***(商品名「TINUVIN PS」,BASF公司製造)、苯丙酸及3-(2H-苯并***-2-基)-5-(1,1-二甲基乙基)-4-羥基(C7-9側鏈及直鏈烷基)之酯化合物(商品名「TINUVIN 384-2」,BASF公司製造)、3-[3-第三丁基-4-羥基-5-(5-氯-2H-苯并***-2-基)苯基]丙酸辛酯及3-[3-第三丁基-4-羥基-5-(5-氯-2H-苯并***-2-基)苯基]丙酸2-乙基己酯之混合物(商品名「TINUVIN 109」,BASF公司製造)、2-(2H-苯并***-2-基)-4,6-雙(1-甲基-1-苯基乙基)苯酚(商品名「TINUVIN 900」,BASF公司製造)、2-(2H-苯并***-2-基)-6-(1-甲基-1-苯基乙基)-4-(1,1,3,3-四甲基丁基)苯酚(商品名「TINUVIN 928」,BASF製造)、3-(3-(2H-苯并***-2-基)-5-第三丁基-4-羥基苯基)丙酸甲酯/聚乙二醇300之反應產物(商品名「TINUVIN 1130」,BASF公司製造)、2-(2H-苯并***-2-基)對甲酚(商品名「TINUVIN P」,BASF公司製造)、2-(2H-苯并***-2-基)-4,6-雙(1-甲基-1-苯基乙基)苯酚(商品名「TINUVIN 234」,BASF公司製造)、2-[5-氯-2H-苯并***-2-基]-4-甲基-6-(第三丁基)苯酚(商品名「TINUVIN 326」,BASF公司製造)、2-(2H-苯并***-2-基)-4,6-二-第三戊基苯酚(商品名「TINUVIN 328」,BASF公司製造)、2-(2H-苯并***-2-基)-4-(1,1,3,3-四甲基丁基)苯酚(商品名「TINUVIN 329」,BASF公司製造)、2,2'-亞甲基雙[6-(2H-苯并***-2-基)-4-(1,1,3,3-四甲基丁基)苯酚](商品名「TINUVIN 360」,BASF公司製造)、3-(3-(2H-苯并***-2-基)-5-第三丁基-4-羥基苯基)丙酸甲酯與聚乙二醇300之反應產物(商品名「TINUVIN 213」,BASF公司製造)、2-(2H-苯并***-2-基)-6-十二烷基-4-甲基苯酚(商品名「TINUVIN 571」,BASF公司製造)、2-[2-羥基-3-(3,4,5,6-四氫鄰苯二甲醯亞胺基甲基)-5-甲基苯基]苯并***(商品名「Sumisorb 250」,住友化學股份有限公司製造)、2-(3-第三丁基-2-羥基-5-甲基苯基)-5-氯-2H-苯并***(商品名「SEESORB 703」,Shipro Kasei公司製造)、2-(2H-苯并***-2-基)-4-甲基-6-(3,4,5,6-四氫鄰苯二甲醯亞胺基甲基)苯酚(商品名「SEESORB 706」,Shipro Kasei公司製造)、2-(4-苯甲醯氧基-2-羥基苯基)-5-氯-2H-苯并***(Shipro Kasei公司製造之商品名「SEESORB 7012BA」)、2-第三丁基-6-(5-氯-2H-苯并***-2-基)-4-甲基苯酚(商品名「KEMISORB 73」,Chemipro Kasei公司製造)、2,2'-亞甲基雙[6-(2H-苯并***-2-基)-4-第三辛基苯酚](商品名「Adekastab LA-31」,ADEKA股份有限公司製造)、2-(2H-苯并***-2-基)對甲酚(商品名「Adekastab LA-32」,ADEKA股份有限公司製造)、2-(5-氯-2H-苯并***-2-基)-6-第三丁基-4-甲基苯酚(商品名「Adekastab LA-36」,ADEKA股份有限公司製造)等。
於一實施方式中,使用不含鹵素原子之紫外線吸收劑。若使用此種紫外線吸收劑,則可獲得難以污染電極等被黏著體之黏著片材。
構成上述紫外線吸收劑之化合物之分子量較佳為200~1500,更佳為250~1200,進而較佳為300~1000。若為此種範圍,則可獲得藉由雷射光照射而可形成更良好之變形部之黏著片材。
上述紫外線吸收劑之最大吸收波長較佳為300 nm~450 nm,更佳為320 nm~400 nm,進而較佳為330 nm~380 nm。
相對於氣體產生層100重量份,上述紫外線吸收劑之含有比率較佳為1重量份~100重量份,更佳為1重量份~50重量份,進而較佳為5重量份~30重量份。若為此種範圍,則可獲得藉由雷射光照射而可形成更良好之變形部之黏著片材。
B-2.黏著劑A
作為上述氣體產生層中所含之黏著劑A,較佳地使用感壓黏著劑A。作為黏著劑A,例如可例舉:丙烯酸系黏著劑、橡膠系黏著劑、乙烯基烷基醚系黏著劑、矽酮系黏著劑、聚酯系黏著劑、聚醯胺系黏著劑、胺基甲酸酯系黏著劑、苯乙烯-二烯嵌段共聚物系黏著劑等。其中較佳為丙烯酸系黏著劑或橡膠系黏著劑,更佳為丙烯酸系黏著劑。再者,上述黏著劑可單獨使用或組合2種以上而使用。
作為上述丙烯酸系黏著劑,例如可例舉將使用(甲基)丙烯酸烷基酯之1種或2種以上作為單體成分之丙烯酸系聚合物(均聚物或共聚物)作為基礎聚合物之丙烯酸系黏著劑等。作為(甲基)丙烯酸烷基酯之具體例,可例舉:(甲基)丙烯酸甲酯、(甲基)丙烯酸乙酯、(甲基)丙烯酸丙酯、(甲基)丙烯酸異丙酯、(甲基)丙烯酸丁酯、(甲基)丙烯酸異丁酯、(甲基)丙烯酸第二丁酯、(甲基)丙烯酸第三丁酯、(甲基)丙烯酸戊酯、(甲基)丙烯酸己酯、(甲基)丙烯酸庚酯、(甲基)丙烯酸辛酯、(甲基)丙烯酸2-乙基己酯、(甲基)丙烯酸異辛酯、(甲基)丙烯酸壬酯、(甲基)丙烯酸異壬酯、(甲基)丙烯酸癸酯、(甲基)丙烯酸異癸酯、(甲基)丙烯酸十一烷基酯、(甲基)丙烯酸十二烷基酯、(甲基)丙烯酸十三烷基酯、(甲基)丙烯酸十四烷基酯、(甲基)丙烯酸十五烷基酯、(甲基)丙烯酸十六烷基酯、(甲基)丙烯酸十七烷基酯、(甲基)丙烯酸十八烷基酯、(甲基)丙烯酸十九烷基酯、(甲基)丙烯酸二十烷基酯等(甲基)丙烯酸C1-20烷基酯。其中,可較佳地使用具有碳數為1~20之直鏈狀或分枝狀之烷基之(甲基)丙烯酸烷基酯,可更佳地使用具有碳數為2~20之直鏈狀或分枝狀之烷基之(甲基)丙烯酸烷基酯。
於一實施方式中,使用具有碳數為4以上(較佳為4~20,更佳為4~18)之直鏈狀或分枝狀之烷基之(甲基)丙烯酸烷基酯A。使用此種單體而形成之具有較長側鏈之丙烯酸系聚合物於與紫外線吸收劑之親和性(相容性)較高之方面有利。相對於構成丙烯酸系聚合物之全部結構單元,上述(甲基)丙烯酸烷基酯A之含有比率較佳為30重量%以上,更佳為50重量%以上,進而較佳為70重量%~100重量%,尤佳為80重量%~100重量%。若為此種範圍,則可提高丙烯酸系聚合物與紫外線吸收劑之相容性。相對於丙烯酸系聚合物之總量100重量份,包含源自上述(甲基)丙烯酸烷基酯A之結構單元之丙烯酸系聚合物之含有比率較佳為30重量份~100重量份,更佳為70重量份~100重量份。
於一實施方式中,組合使用具有碳數為4以上(較佳為4~20,更佳為4~18)之直鏈狀或分枝狀之烷基之(甲基)丙烯酸烷基酯A、與三𠯤系紫外線吸收劑。(甲基)丙烯酸烷基酯A與三𠯤系紫外線吸收劑之相容性尤其優異,具備使用該等化合物而形成之氣體產生層之黏著片材之視認性顯著優異。
上述丙烯酸系聚合物亦能以凝聚力、耐熱性、交聯性等之改質為目的,視需要含有對應於可與上述(甲基)丙烯酸烷基酯共聚之其他單體成分之單元。作為此種單體成分,例如可例舉:丙烯酸、甲基丙烯酸、丙烯酸羧乙酯、丙烯酸羧戊酯、伊康酸、順丁烯二酸、反丁烯二酸、丁烯酸等含羧基之單體;順丁烯二酸酐、伊康酸酐等酸酐單體;(甲基)丙烯酸羥乙酯、(甲基)丙烯酸羥丙酯、(甲基)丙烯酸羥丁酯、(甲基)丙烯酸羥己酯、(甲基)丙烯酸羥辛酯、(甲基)丙烯酸羥癸酯、(甲基)丙烯酸羥基月桂酯、甲基丙烯酸(4-羥甲基環己基)甲酯等含羥基之單體;苯乙烯磺酸、烯丙基磺酸、2-(甲基)丙烯醯胺-2-甲基丙磺酸、(甲基)丙烯醯胺丙磺酸、(甲基)丙烯酸磺丙酯、(甲基)丙烯醯氧基萘磺酸等含磺酸基之單體;(甲基)丙烯醯胺、N,N-二甲基(甲基)丙烯醯胺、N-丁基(甲基)丙烯醯胺、N-羥甲基(甲基)丙烯醯胺、N-羥甲基丙烷(甲基)丙烯醯胺等(N-取代)醯胺系單體;(甲基)丙烯酸胺基乙酯、(甲基)丙烯酸N,N-二甲基胺基乙酯、(甲基)丙烯酸第三丁基胺基乙酯等(甲基)丙烯酸胺基烷基酯系單體;(甲基)丙烯酸甲氧基乙酯、(甲基)丙烯酸乙氧基乙酯等(甲基)丙烯酸烷氧基烷基酯系單體;N-環己基順丁烯二醯亞胺、N-異丙基順丁烯二醯亞胺、N-月桂基順丁烯二醯亞胺、N-苯基順丁烯二醯亞胺等順丁烯二醯亞胺系單體;N-甲基伊康醯亞胺、N-乙基伊康醯亞胺、N-丁基伊康醯亞胺、N-辛基伊康醯亞胺、N-2-乙基己基伊康醯亞胺、N-環己基伊康醯亞胺、N-月桂基伊康醯亞胺等伊康醯亞胺系單體;N-(甲基)丙烯醯氧基亞甲基丁二醯亞胺、N-(甲基)丙烯醯基-6-氧基六亞甲基丁二醯亞胺、N-(甲基)丙烯醯基-8-氧基八亞甲基丁二醯亞胺等丁二醯亞胺系單體;乙酸乙烯酯、丙酸乙烯酯、N-乙烯基吡咯啶酮、甲基乙烯基吡咯啶酮、乙烯基吡啶、乙烯基哌啶酮、乙烯基嘧啶、乙烯基哌𠯤、乙烯基吡𠯤、乙烯基吡咯、乙烯基咪唑、乙烯基㗁唑、乙烯基𠰌啉、N-乙烯基羧醯胺類、苯乙烯、α-甲基苯乙烯、N-乙烯基己內醯胺等乙烯基系單體;丙烯腈、甲基丙烯腈等氰基丙烯酸酯單體;(甲基)丙烯酸縮水甘油酯等含環氧基之丙烯酸系單體;(甲基)丙烯酸聚乙二醇、(甲基)丙烯酸聚丙二醇、(甲基)丙烯酸甲氧基乙二醇、(甲基)丙烯酸甲氧基聚丙二醇等二醇系丙烯酸酯單體;(甲基)丙烯酸四氫呋喃甲酯、氟(甲基)丙烯酸酯、矽酮(甲基)丙烯酸酯等具有雜環、鹵素原子、矽原子等之丙烯酸酯系單體;己二醇二(甲基)丙烯酸酯、(聚)乙二醇二(甲基)丙烯酸酯、(聚)丙二醇二(甲基)丙烯酸酯、新戊二醇二(甲基)丙烯酸酯、季戊四醇二(甲基)丙烯酸酯、三羥甲基丙烷三(甲基)丙烯酸酯、季戊四醇三(甲基)丙烯酸酯、二季戊四醇六(甲基)丙烯酸酯、環氧丙烯酸酯、丙烯酸聚酯、丙烯酸胺基甲酸酯等多官能單體;異戊二烯、丁二烯、異丁烯等烯烴系單體;乙烯醚等乙烯醚系單體等。該等單體成分可單獨使用或組合2種以上而使用。其中,尤其就與紫外線吸收劑之親和性(相容性)較高之觀點而言,較佳地使用丙烯酸、甲基丙烯酸、丙烯酸羧乙酯、丙烯酸羧戊酯、伊康酸、順丁烯二酸、反丁烯二酸、丁烯酸等含羧基之單體;順丁烯二酸酐、伊康酸酐等酸酐單體;(甲基)丙烯酸羥乙酯、(甲基)丙烯酸羥丙酯、(甲基)丙烯酸羥丁酯、(甲基)丙烯酸羥己酯、(甲基)丙烯酸羥辛酯、(甲基)丙烯酸羥癸酯、(甲基)丙烯酸羥基月桂酯、甲基丙烯酸(4-羥甲基環己基)甲酯等含羥基之單體。相對於丙烯酸系聚合物之總量100重量份,上述含羧基之單體之含有比率較佳為0.5重量份~15重量份,更佳為1重量份~10重量份,進而較佳為3重量份~9.5重量份。相對於丙烯酸系聚合物之總量100重量份,上述酸酐單體之含有比率較佳為0.5重量份~15重量份,更佳為1重量份~10重量份,進而較佳為3重量份~9.5重量份。相對於丙烯酸系聚合物之總量100重量份,上述含羥基之單體之含有比率較佳為0.5重量份~15重量份,更佳為1重量份~10重量份,進而較佳為3重量份~9.5重量份。
作為上述橡膠系黏著劑,例如可例舉將如下者作為基礎聚合物之橡膠系黏著劑:天然橡膠;聚異戊二烯橡膠、苯乙烯-丁二烯(SB)橡膠、苯乙烯-異戊二烯(SI)橡膠、苯乙烯-異戊二烯-苯乙烯嵌段共聚物(SIS)橡膠、苯乙烯-丁二烯-苯乙烯嵌段共聚物(SBS)橡膠、苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物(SEBS)橡膠、苯乙烯-乙烯-丙烯-苯乙烯嵌段共聚物(SEPS)橡膠、苯乙烯-乙烯-丙烯嵌段共聚物(SEP)橡膠、再生橡膠、丁基橡膠、聚異丁烯、該等之改性體等合成橡膠等。
自上述氣體產生層產生之氣體較佳為烴(較佳為脂肪族烴)系氣體。可產生烴系氣體之氣體產生層例如以烴系化合物為主成分而構成。氣體產生層較佳為不含有含鹵素元素之化合物。若產生之氣體為烴系氣體,則可防止作為被加工物之電子零件之腐蝕。此種效果藉由形成不含有含鹵素元素之化合物之氣體產生層而變得更顯著。自氣體產生層之產生離子式量較佳為10 m/z~800 m/z,更佳為11 m/z~700 m/z,進而較佳為12 m/z~500 m/z,尤佳為13 m/z~400 m/z。
上述黏著劑A可視需要含有任意適當之添加劑。作為該添加劑,例如可例舉:交聯劑、黏著賦予劑(例如,松香系黏著賦予劑、萜烯系黏著賦予劑、烴系黏著賦予劑等)、塑化劑(例如,偏苯三甲酸酯系塑化劑、均苯四甲酸酯系塑化劑)、顏料、染料、抗老化劑、導電材、抗靜電劑、光穩定劑、剝離調整劑、軟化劑、界面活性劑、阻燃劑、抗氧化劑等。
作為上述交聯劑,例如可例舉:異氰酸酯系交聯劑、環氧系交聯劑、三聚氰胺系交聯劑、過氧化物系交聯劑、以及脲系交聯劑、金屬烷氧化物系交聯劑、金屬螯合物系交聯劑、金屬鹽系交聯劑、碳二醯亞胺系交聯劑、㗁唑啉系交聯劑、氮丙啶系交聯劑、胺系交聯劑等。其中,較佳為異氰酸酯系交聯劑或環氧系交聯劑。
作為上述異氰酸酯系交聯劑之具體例,可例舉:伸丁基二異氰酸酯、六亞甲基二異氰酸酯等低級脂肪族聚異氰酸酯類;伸環戊基二異氰酸酯、伸環己基二異氰酸酯、異佛爾酮二異氰酸酯等脂環族異氰酸酯類;2,4-甲苯二異氰酸酯、4,4'-二苯甲烷二異氰酸酯、苯二甲基二異氰酸酯等芳香族異氰酸酯類;三羥甲基丙烷/甲苯二異氰酸酯三聚物加成物(Nippon Polyurethane Industry公司製造,商品名「Coronate L」)、三羥甲基丙烷/六亞甲基二異氰酸酯三聚物加成物(Nippon Polyurethane Industry公司製造,商品名「Coronate HL」)、六亞甲基二異氰酸酯之異氰尿酸酯體(Nippon Polyurethane Industry公司製造,商品名「Coronate HX」)等異氰酸酯加成物等。異氰酸酯系交聯劑之含量可根據所需之黏著力而設定為任意適當之量,相對於基礎聚合物100重量份,代表性而言為0.1重量份~20重量份,更佳為0.5重量份~10重量份。
作為上述環氧系交聯劑,例如可例舉:N,N,N',N'-四縮水甘油基間苯二甲胺、二縮水甘油基苯胺、1,3-雙(N,N-縮水甘油基胺基甲基)環己烷(三菱瓦斯化學公司製造,商品名「Tetrad C」)、1,6-己二醇二縮水甘油醚(共榮社化學公司製造,商品名「Epolight 1600」)、新戊二醇二縮水甘油醚(共榮社化學公司製造,商品名「Epolight 1500NP」)、乙二醇二縮水甘油醚(共榮社化學公司製造,商品名「Epolight 40E」)、丙二醇二縮水甘油醚(共榮社化學公司製造,商品名「Epolight 70P」)、聚乙二醇二縮水甘油醚(日本油脂公司製造,商品名「EPIOL E-400」)、聚丙二醇二縮水甘油醚(日本油脂公司製造,商品名「EPIOL P-200」)、山梨醇聚縮水甘油醚(Nagase chemteX公司製造,商品名「Denacol EX-611」)、甘油聚縮水甘油醚(Nagase chemteX公司製造,商品名「Denacol EX-314」)、季戊四醇聚縮水甘油醚、聚甘油聚縮水甘油醚(Nagase chemteX公司製造,商品名「Denacol EX-512」)、山梨醇酐聚縮水甘油醚、三羥甲基丙烷聚縮水甘油醚、己二酸二縮水甘油酯、鄰苯二甲酸二縮水甘油酯、三(2-羥乙基)異氰尿酸三縮水甘油酯、間苯二酚二縮水甘油醚、雙苯酚-S-二縮水甘油醚、分子內具有2個以上之環氧基之環氧系樹脂等。環氧系交聯劑之含量可根據所需之黏著力而設定為任意適當之量,相對於基礎聚合物100重量份,代表性而言為0.01重量份~10重量份,更佳為0.03重量份~5重量份。
C. 黏著劑層上述黏著劑層含有任意適當之黏著劑B。作為黏著劑B,可為感壓黏著劑B1,亦可為硬化型黏著劑B2。
上述黏著劑層之厚度較佳為0.1 μm~50 μm,更佳為0.5 μm~40 μm,進而較佳為1 μm~30 μm,尤佳為2 μm~20 μm。若為此種範圍,則可形成具有較佳黏著力,且作為氣體阻隔層良好地發揮作用之黏著劑層。
上述黏著劑層之水蒸氣透過率較佳為20000 g/(m
2・day)以下,更佳為10000 g/(m
2・day)以下,進而較佳為7000 g/(m
2・day)以下,進而較佳為5000 g/(m
2・day)以下,尤佳為4800 g/(m
2・day)以下,最佳為4500 g/(m
2・day)以下。若為此種範圍,則黏著劑層作為氣體阻隔層良好地發揮作用,形成優異形狀之變形部。若使用此種黏著片材,則可精度良好地使小型被黏著體(例如,電子零件)剝離。黏著劑層之水蒸氣透過率越小越佳,其下限值例如為100 g/(m
2・day)。
上述黏著劑層之穿刺強度較佳為10 mN~3000 mN,更佳為30 mN~2500 mN,進而較佳為50 mN~2000 mN,尤佳為100 mN~2000 mN。若為此種範圍,則黏著劑層作為氣體阻隔層良好地發揮作用,且較佳地產生藉由氣體之產生所引起之形狀變化,其結果,形成優異形狀之變形部。若使用此種黏著片材,則可精度良好地使小型被黏著體(例如,電子零件)剝離。
上述黏著劑層之波長360 nm之紫外線透過率較佳為50%~100%,更佳為60%~95%。
C-1.感壓黏著劑B1
作為上述感壓黏著劑B1,例如可例舉:丙烯酸系黏著劑、橡膠系黏著劑、乙烯基烷基醚系黏著劑、矽酮系黏著劑、聚酯系黏著劑、聚醯胺系黏著劑、胺基甲酸酯系黏著劑、苯乙烯-二烯嵌段共聚物系黏著劑等。其中較佳為丙烯酸系黏著劑或橡膠系黏著劑,更佳為丙烯酸系黏著劑。作為含有感壓黏著劑之黏著劑層所含有之黏著劑B1,可使用B-2項中說明之黏著劑。
C-2.硬化型黏著劑B2
作為硬化型黏著劑B2,例如可例舉:熱固型黏著劑、活性能量線硬化型黏著劑等。較佳為使用活性能量線硬化型黏著劑。藉由該活性能量線硬化型黏著劑而形成之上述黏著劑層為照射活性能量線而形成之黏著劑層,即,為於活性能量線照射後具有特定黏著力之黏著劑層。
作為構成上述活性能量線硬化型黏著劑之樹脂材料,例如可例舉:紫外線硬化系統(加藤清視著,綜合技術中心發行(1989))、光硬化技術(技術資訊協會編(2000))、日本專利特開2003-292916號公報、日本專利4151850號等中記載之樹脂材料。更具體而言,可例舉含有成為母劑之聚合物與活性能量線反應性化合物(單體或低聚物)之樹脂材料(B2-1)、含有活性能量線反應性聚合物之樹脂材料(B2-2)等。
作為上述成為母劑之聚合物,例如可例舉:天然橡膠、聚異丁烯橡膠、苯乙烯-丁二烯橡膠、苯乙烯-異戊二烯-苯乙烯嵌段共聚物橡膠、再生橡膠、丁基橡膠、聚異丁烯橡膠、腈橡膠(NBR(Nitrile Butadiene Rubber,丁腈橡膠))等橡膠系聚合物;矽酮系聚合物;丙烯酸系聚合物等。該等聚合物可單獨使用或組合2種以上而使用。
作為上述活性能量線反應性化合物,例如可例舉含有複數個丙烯醯基、甲基丙烯醯基、乙烯基、烯丙基、乙炔基等具有碳-碳多重鍵之官能基之光反應性之單體或低聚物。其中,較佳地使用具有乙烯性不飽和官能基之化合物,更佳地使用具有乙烯性不飽和官能基之(甲基)丙烯酸系化合物。具有乙烯性不飽和官能基之化合物藉由紫外線而容易生成自由基,因此若使用該化合物,則可形成可於短時間硬化之黏著劑層。又,若使用具有乙烯性不飽和官能基之(甲基)丙烯酸系化合物,則可形成硬化後具有適度硬度之黏著劑層。作為光反應性之單體或低聚物之具體例,可例舉:三羥甲基丙烷三(甲基)丙烯酸酯、四羥甲基甲烷四(甲基)丙烯酸酯、季戊四醇三(甲基)丙烯酸酯、季戊四醇四(甲基)丙烯酸酯、二季戊四醇單羥基五(甲基)丙烯酸酯、二季戊四醇六(甲基)丙烯酸酯、1,4-丁二醇二(甲基)丙烯酸酯、1,6-己二醇二(甲基)丙烯酸酯、聚乙二醇二(甲基)丙烯酸酯、(甲基)丙烯酸胺基甲酸酯系化合物等含(甲基)丙烯醯基之化合物;該含(甲基)丙烯醯基之化合物之二聚物~五聚物等。該等化合物可單獨使用或組合2種以上而使用。
又,作為上述活性能量線反應性化合物,可使用環氧化丁二烯、甲基丙烯酸縮水甘油酯、丙烯醯胺、乙烯基矽氧烷等單體;或由該單體構成之低聚物。含有該等化合物之樹脂材料(B2-1)可藉由紫外線、電子束等高能量線而硬化。
進而,作為上述活性能量線反應性化合物,可使用鎓鹽等有機鹽類與分子內具有複數個雜環之化合物之混合物。該混合物藉由活性能量線(例如,紫外線、電子束)之照射,有機鹽會裂解而生成離子,其成為起始種而引發雜環之開環反應,從而可形成三維網狀結構。作為上述有機鹽類,例如可例舉:錪鹽、鏻鹽、銻鹽、鋶鹽、硼酸鹽等。作為上述分子內具有複數個雜環之化合物中之雜環,可例舉:環氧乙烷、氧雜環丁烷、氧雜環戊烷、環硫乙烷、氮丙啶等。
含有上述成為母劑之聚合物與活性能量線反應性化合物之樹脂材料(B2-1)中,相對於成為母劑之聚合物100重量份,活性能量線反應性化合物之含有比率較佳為0.1重量份~500重量份,更佳為1重量份~300重量份,進而較佳為10重量份~200重量份。
作為上述活性能量線反應性聚合物,例如可例舉含有丙烯醯基、甲基丙烯醯基、乙烯基、烯丙基、乙炔基等具有碳-碳多重鍵之活性能量線反應性官能基之聚合物。較佳為使用具有乙烯性不飽和官能基之化合物(聚合物),更佳為使用具有丙烯醯基或甲基丙烯醯基之(甲基)丙烯酸系聚合物。作為具有活性能量線反應性官能基之聚合物之具體例,可例舉包含多官能(甲基)丙烯酸酯之聚合物等。該包含多官能(甲基)丙烯酸酯之聚合物較佳為於側鏈具有碳數為4以上之烷基酯,更佳為具有碳數為6以上之烷基酯,進而較佳為具有碳數為8以上之烷基酯,尤佳為具有碳數為8~20之烷基酯,最佳為具有碳數為8~18之烷基酯。
含有上述活性能量線反應性聚合物之樹脂材料(B2-2)亦可進而含有上述活性能量線反應性化合物(單體或低聚物)。
上述活性能量線硬化型黏著劑可藉由活性能量線之照射而硬化。本發明之黏著片材中,於使黏著劑硬化前貼附被黏著體之後,照射活性能量線而使黏著劑硬化,藉此可使該被黏著體密接。作為活性能量線,例如可例舉:γ射線、紫外線、可見光線、紅外線(熱線)、射頻波、α射線、β射線、電子束、電漿流、電離輻射、粒子束等。活性能量線之波長、照射量等條件可根據使用之樹脂材料之種類等而設定為任意適當之條件。例如,可照射10~1000 mJ/cm
2照射量之紫外線而使黏著劑硬化。
D. 中間層作為上述中間層之形態,例如可例舉樹脂層、具有黏著性之層等。
於一實施方式中,上述中間層含有熱塑性樹脂。此種中間層可為含有熱塑性樹脂之樹脂膜、含有包含熱塑性樹脂之黏著劑C之層等。於其他實施方式中,上述中間層含有硬化型樹脂(例如,紫外線硬化型樹脂、熱固型樹脂)。此種中間層可為含有硬化型樹脂之樹脂膜、含有硬化型黏著劑D之層等。
中間層之厚度較佳為0.1 μm~50 μm,更佳為1 μm~40 μm,進而較佳為1.5 μm~30 μm。若為此種範圍,則可形成作為氣體阻隔層良好地發揮作用之中間層。
上述中間層之水蒸氣透過率較佳為5000 g/(m
2・day)以下,更佳為4800 g/(m
2・day)以下,進而較佳為4500 g/(m
2・day)以下,進而較佳為4200 g/(m
2・day)以下。若為此種範圍,則中間層作為氣體阻隔層良好地發揮作用,形成優異形狀之變形部。若使用此種黏著片材,則可精度良好地使小型被黏著體(例如,電子零件)剝離。中間層之水蒸氣透過率越小越佳,其下限值例如為0.1 g/(m
2・day)。
上述中間層之穿刺強度較佳為300 mN~5000 mN,更佳為500 mN~4500 mN,進而較佳為1000 mN~4000 mN。若為此種範圍,則中間層作為氣體阻隔層良好地發揮作用,且較佳地產生藉由氣體之產生所引起之形狀變化,其結果,形成優異形狀之變形部。若使用此種黏著片材,則可精度良好地使小型被黏著體(例如,電子零件)剝離。
上述中間層之波長360 nm之紫外線透過率較佳為50%~100%,更佳為60%~95%。
D-1.作為樹脂層之中間層
作為樹脂層之中間層例如由樹脂膜形成。作為形成該樹脂膜之樹脂,例如可例舉:聚對苯二甲酸乙二酯系樹脂、聚烯烴系樹脂、苯乙烯系彈性體樹脂(例如SEBS等)、紫外線硬化型樹脂、熱固性樹脂、胺基甲酸酯系樹脂、環氧系樹脂等。於一實施方式中,上述樹脂膜包含熱塑性樹脂。
上述樹脂膜之厚度較佳為0.1 μm~50 μm,更佳為0.5 μm~30 μm,進而較佳為1 μm~20 μm。
D-2.作為具有黏著性之層之中間層
關於作為具有黏著性之層之中間層,可例舉:含有感壓黏著劑之中間層、含有硬化型黏著劑之中間層等。較佳為配置含有硬化型黏著劑D之中間層。尤其若作為黏著劑層而將含有感壓黏著劑A之黏著劑層與含有硬化型黏著劑D之中間層組合,則可獲得藉由雷射光照射而可形成更良好之變形部之黏著片材。作為硬化型黏著劑D,可使用C-2項中說明之黏著劑。
作為具有黏著性之層之中間層之厚度較佳為5 μm~50 μm,更佳為5 μm~30 μm。
E. 黏著片材之製造方法本發明之黏著片材可藉由任意適當之方法而製造。關於本發明之黏著片材,例如可例舉如下方法:於特定基材上直接塗佈含有黏著劑A及紫外線吸收劑之氣體產生層形成用組合物而形成氣體產生層,並於該氣體產生層上塗佈含有黏著劑B之黏著劑層形成用組合物而形成黏著劑層。於一實施方式中,於黏著片材具有中間層之情形時,在形成黏著劑層之前,將中間層形成用組合物塗佈於氣體產生層上而形成中間層,並於該中間層上塗佈黏著劑層形成用組合物而形成黏著劑層。又,亦可將各層分別形成之後進行貼合而形成黏著片材。
作為上述組合物之塗佈方法,可採用任意適當之塗佈方法。例如,可於塗佈後進行乾燥而形成各層。作為塗佈方法,例如可例舉使用多輥塗佈機、模嘴塗佈機、凹版塗佈機、敷料器等之塗佈方法。作為乾燥方法,例如可例舉:自然乾燥、加熱乾燥等。進行加熱乾燥之情形時之加熱溫度可根據成為乾燥對象之物質之特性而設定為任意適當之溫度。又,可根據各層之形態而進行活性能量線照射(例如,紫外線照射)。
F. 電子零件之處理方法本發明之電子零件之處理方法包括:將電子零件貼附於上述黏著片材;及對該黏著片材照射雷射光,而自該黏著片材剝離電子零件。作為電子零件,例如可例舉:半導體晶片、LED(Light-emitting diode,發光二極體)晶片、MLCC(Multi-layer Ceramic Capacitor,積層陶瓷電容)等。
上述電子零件之剝離可選擇位置地進行。具體而言,將複數個電子零件貼附、固定於黏著片材,能以使電子零件之一部分剝離,讓其他電子零件仍保持固定之方式進行電子零件之剝離。
於一實施方式中,本發明之電子零件之處理方法包括:於將電子零件貼附於黏著片材後且自黏著片材剝離電子零件前,對該電子零件進行特定處理。上述處理並無特別限定,例如可例舉:研磨加工、切割加工、黏晶、打線接合、蝕刻、蒸鍍、成型、電路形成、檢查、產品檢驗、洗淨、轉印、排列、修復、裝置表面保護等處理。
上述電子零件之尺寸(貼附面之面積)例如為1 μm
2~250000 μm
2。於一實施方式中,可將電子零件之尺寸(貼附面之面積)為1 μm
2~6400 μm
2之電子零件供至處理。於其他實施方式中,可將電子零件之尺寸(貼附面之面積)為1 μm
2~2500 μm
2之電子零件供至處理。
於一實施方式中,如上所述可將複數個電子零件配置於黏著片材上。電子零件之間隔例如為1 μm~500 μm。本發明中,於可縮小間隔地暫時固定被處理體之方面有利。
作為雷射光,例如可使用UV雷射光。雷射光之照射功率例如為1 μJ~1000 μJ。UV雷射光之波長例如為240 nm~380 nm。
於一實施方式中,上述電子零件之處理方法包括:於電子零件之剝離後,將該電子零件配置於其他片材(例如,黏著片材、基板等)。
實施例
以下,利用實施例對本發明進行具體說明,但本發明並不受該等實施例限定。實施例中之評價方法如下所述。再者,下述評價中,使用剝離隔離膜後之黏著片材。又,實施例中,只要無特別明確記載,則「份」及「%」為重量基準。
(1)透過率
於具有中間層之黏著片材之情形時,將黏著片材設置於分光光度計(商品名「UV-VIS紫外可見分光光度計 SolidSpec3700」,島津製作所公司製造),讓入射光向樣品之氣體阻隔層側垂直地入射,測定300 nm~800 nm之波長區域之透光率。抽選所得之透射光譜之360 nm及500 nm之波長下之透過率。於僅由黏著層構成之黏著片材之情形時,於保留單側之剝離襯墊之狀態下設置於分光光度計而進行測定,其後,測定剝離襯墊單獨體之透射光譜,藉由進行減法運算而獲得黏著層單獨體之透射光譜。抽選所得之透射光譜之360 nm與500 nm之波長下之透過率。
(2)最大氣體產生峰值溫度
將黏著片材試樣約0.5 mg設置於加熱爐型熱解器,藉由對加熱而揮發之成分進行質量分析之EGA-MS分析,而獲得質量色譜圖。利用加熱爐型熱解器(Frontier Laboratories公司製造,商品名「PY2020iD」)以10℃/min升溫速度自40℃升溫至500℃,使用GC/MS(Gas chromatography/mass spectrometry,氣相層析質譜)分析裝置(JEOL公司製造,商品名「JMS-T100GCV」),根據質量範圍m/z=10~800之質量色譜圖而算出最大氣體產生峰值溫度。
(3)氣化起始溫度
利用與上述(2)同樣之方法使黏著片材升溫,將根據EGA分析而算出之氣體產生上升溫度作為氣化起始溫度。氣體產生上升溫度係以達到根據EGA分析所得之EGA/MS色譜之最大氣體產生峰值之半值的溫度而定義。
(4)產生氣體種
將黏著片材試樣設置於自動試樣燃燒裝置(三菱化學分析技術公司製造,商品名「AQF-2100H」),捕獲以400℃加熱30分鐘而產生之氣體。藉由利用離子層析法對捕獲液進行分析,而特定出產生氣體種。
(5) 5%重量減少溫度
使用示差熱分析裝置(TA Instruments公司製造,商品名「Discovery TGA」),於10℃/min升溫溫度、N
2氛圍下,將流量設為25 ml/min,針對黏著片材測定重量減少5%之溫度。
(6) 10%重量減少溫度
使用示差熱分析裝置(TA Instruments公司製造,商品名「Discovery TGA」),於10℃/min升溫溫度、N
2氛圍下,將流量設為25 ml/min,針對黏著片材測定重量減少10%之溫度。
針對黏著片材、氣體產生層(UV吸收劑)分別測定10%重量減少溫度。
(7)水蒸氣透過率
以覆蓋具有10 mm×10 mm之開口部之Al治具之開口部的方式貼附試樣而製作測定樣品,並將測定樣品設置於水蒸氣透過度測定裝置(MOCON公司製造,商品名「PERMATRAN-W3/34G」)之第1腔室與第2腔室之間,利用MOCON測定法進行評價。溫濕度條件設為30℃/90% RH,氣體(水蒸氣)流量設為10.0±0.5 cc/min,測定時間設為20小時。
針對黏著片材、黏著劑層、中間層分別測定水蒸氣透過率。
(8)表面形狀變化
於黏著片材之氣體產生層側(與黏著劑層相反之側)貼合玻璃板(松波硝子公司製造,大型載玻片S9112(標準大型白色磨邊No.2))而獲得測定樣品。自測定樣品之玻璃板側,使用波長355 nm、光束直徑約20 μm
之UV雷射光,以0.80 mW功率、40 kHz頻率進行脈衝掃描,而使氣體自氣體產生層產生。對於與脈衝掃描過之任意1點對應之黏著劑層表面(實施例1及比較例1中為氣體產生層表面),於雷射光照射結束24小時後,利用共聚聚焦雷射顯微鏡進行觀察,而測定垂直位移Y與水平位移X(直徑;半峰全幅值)。
於位移Y為8 μm以上之情形時,剝離性顯著優異(表中,◎);於位移Y為0.6 μm以上且未達8 μm之情形時,剝離性良好(表中,〇);於位移Y未達0.6 μm之情形時,剝離性不充分(表中,×)。
(9)霧度值
於具有中間層之黏著片材之情形時,將剝離襯墊剝離後設置於霧度計,使入射光向樣品垂直地入射而測定霧度值。於僅由黏著層構成之黏著片材之情形時,於保留單側之剝離襯墊之狀態下設置於霧度計而進行測定,其後測定剝離襯墊單獨體之霧度值,藉由進行減法運算而獲得黏著層單獨體之霧度值。
於霧度值為20%以下之情形時,評價為被黏著體視認性:良(表中,〇),於霧度值為20%以上50%以下之情形時,評價為被黏著體視認性:可(表中,△),於霧度值為50%以上之情形時,評價為被黏著視認性:差(表中,×)。
(10)黏著力(氣體產生層側)
於黏著片材之黏著劑層側貼合PET#25而獲得測定樣品。對於測定樣品之氣體產生層側相對於SUS430之黏著力,藉由依照JIS Z 0237:2000之方法(貼合條件:2 kg輥1個往返,拉伸速度:300 mm/min,剝離角度180°)進行測定。
(11)黏著力(黏著劑層)
於黏著片材之氣體產生層側貼合PET#25而獲得測定樣品。對於測定樣品之黏著劑層側相對於SUS430之黏著力,藉由依照JIS Z 0237:2000之方法(貼合條件:2 kg輥1個往返,拉伸速度:300 mm/min,剝離角度180°)進行測定。
(12)變形之面內均一性
以上述(8)之方式對氣體產生層照射UV雷射光。
利用顯微鏡對隨機選擇之2 mm×2 mm範圍之變形部進行觀察,於凸部之90個%以上為相同尺寸之情形時設為良(表中,〇),於凸部之80個%以上且未達90個%為相同尺寸之情形時設為可(表中,△),於凸部之未達80個%為相同尺寸之情形時設為差(表中,×)。所謂相同尺寸係指位移X之差在±20%以內。
(13)變形之位置選擇性
以上述(8)之方式對氣體產生層照射UV雷射光。
將僅雷射光照射部單獨變形之情形設為合格(〇),將於雷射照射部周邊亦有複數處變形之情形設為不合格(×)。
(14)彈性模數
使用奈米壓痕儀(Hysitron Inc公司製造之Triboindenter TI-950),藉由在特定溫度(25℃)之單一壓入法,於壓入速度約500 nm/sec、拔出速度約500 nm/sec、壓入深度約1500 nm之測定條件下測定彈性模數。
[製造例1]氣體產生層形成用組合物a之製備
向甲苯中添加丙烯酸2-乙基己酯30重量份、丙烯酸乙酯70重量份、丙烯酸2-羥乙酯4重量份、甲基丙烯酸甲酯5重量份、及作為聚合起始劑之過氧化苯甲醯0.2重量份後,加熱至70℃而獲得丙烯酸系共聚物(聚合物A)之甲苯溶液。
將聚合物A之甲苯溶液(聚合物A:100重量份)、異氰酸酯系交聯劑(Nippon Polyurethane公司製造,商品名「Coronate L」)1.5重量份、紫外線吸收劑(BASF公司製造,商品名「Tinuvin 477」,結構:[化1])20重量份混合而製備氣體產生層形成用組合物a。將氣體產生層形成用組合物a之組成示於表1。
[化1]
[製造例2]氣體產生層形成用組合物b之製備
將UV吸收劑之調配量設為10重量份,除此以外,以與製造例1同樣之方式製備氣體產生層形成用組合物b。將氣體產生層形成用組合物b之組成示於表1。
[製造例3]氣體產生層形成用組合物c之製備
作為UV吸收劑,使用2,4-雙(2-羥基-4-丁氧基苯基)-6-(2,4-二丁氧基苯基)-1,3,5-三𠯤(商品名「TINUVIN 460」,BASF公司製造,結構:[化2])10重量份,除此以外,以與製造例1同樣之方式製備氣體產生層形成用組合物c。將氣體產生層形成用組合物c之組成示於表1。
[化2]
[製造例4]氣體產生層形成用組合物d之製備
作為UV吸收劑,使用2-(4,6-雙(2,4-二甲基苯基)-1,3,5-三𠯤-2-基)-5-羥基苯與[(C10-C16(主要為C12-C13)烷氧基)甲基]環氧乙烷之反應產物(商品名「TINUVIN 400」,BASF公司製造,結構:[化3])20重量份,除此以外,以與製造例1同樣之方式製備氣體產生層形成用組合物d。將氣體產生層形成用組合物d之組成示於表1。
[化3]
[製造例5]氣體產生層形成用組合物e之製備
向乙酸乙酯中添加丙烯酸2-乙基己酯30重量份、丙烯酸甲酯70重量份、丙烯酸10重量份、及作為聚合起始劑之過氧化苯甲醯0.2重量份後,加熱至70℃而獲得丙烯酸系共聚物(聚合物B)之乙酸乙酯溶液。
將聚合物B之乙酸乙酯溶液(聚合物B:100重量份)、異氰酸酯系交聯劑(Nippon Polyurethane公司製造,商品名「Coronate L」)1重量份、及紫外線吸收劑(BASF公司製造,商品名「Tinuvin477」)20重量份混合而製備氣體產生層形成用組合物e。將氣體產生層形成用組合物e之組成示於表1。
[製造例6]氣體產生層形成用組合物f之製備
向乙酸乙酯中添加丙烯酸2-乙基己酯95重量份、丙烯酸5重量份、及作為聚合起始劑之過氧化苯甲醯0.15重量份後,加熱至70℃而獲得丙烯酸系共聚物(聚合物C)之乙酸乙酯溶液。
將聚合物C之乙酸乙酯溶液(聚合物C:100重量份)、異氰酸酯系交聯劑(Nippon Polyurethane公司製造,商品名「Coronate L」)1重量份、及紫外線吸收劑(BASF公司製造,商品名「Tinuvin477」)20重量份混合而製備氣體產生層形成用組合物f。將氣體產生層形成用組合物f之組成示於表1。
[製造例7]氣體產生層形成用組合物g之製備
向乙酸乙酯中添加丙烯酸2-乙基己酯95重量份、丙烯酸5重量份、及作為聚合起始劑之過氧化苯甲醯0.15重量份後,加熱至70℃而獲得丙烯酸系共聚物(聚合物C)之乙酸乙酯溶液。
將聚合物C之乙酸乙酯溶液(聚合物C:100重量份)、環氧系交聯劑(三菱瓦斯化學公司製造,商品名「TETRAD-C」)0.1重量份、及紫外線吸收劑(BASF公司製造,商品名「Tinuvin 477」)20重量份混合而製備氣體產生層形成用組合物g。將氣體產生層形成用組合物g之組成示於表1。
[製造例8]氣體產生層形成用組合物h之製備
將順丁烯二酸改性苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物(SEBS:苯乙烯部位/乙烯-丁烯部位(重量比)=30/70,酸值:10(mg-CH
3ONa/g),旭化成化學公司製造,商品名「Tuftec M1913」)100重量份、環氧系交聯劑(三菱瓦斯化學公司製造,商品名「TETRAD-C」)3重量份、紫外線吸收劑(BASF公司製造,商品名「Tinuvin 477」)20重量份、及作為溶劑之甲苯混合而製備氣體產生層形成用組合物h。將氣體產生層形成用組合物h之組成示於表1。
[製造例8']氣體產生層形成用組合物i之製備
向甲苯中添加丙烯酸丁酯100重量份、丙烯酸5重量份、及作為聚合起始劑之過氧化苯甲醯0.2重量份後,加熱至70℃而獲得丙烯酸系共聚物(聚合物D)之甲苯溶液。
將聚合物D之甲苯溶液(聚合物D:100重量份)、環氧系交聯劑(三菱瓦斯化學公司製造,商品名「TETRAD-C」)0.1重量份、及紫外線吸收劑(BASF公司製造,商品名「Tinuvin 400」)20重量份混合而製備氣體產生層形成用組合物i。將氣體產生層形成用組合物i之組成示於表1。
[製造例8'']氣體產生層形成用組合物j之製備
以與製造例5同樣之方式獲得丙烯酸系共聚物(聚合物B)之乙酸乙酯溶液。
將聚合物B之乙酸乙酯溶液(聚合物B:100重量份)、環氧系交聯劑(三菱瓦斯化學公司製造,商品名「TETRAD-C」)0.1重量份、及紫外線吸收劑(BASF公司製造,商品名「Tinuvin400」)20重量份混合而製備氣體產生層形成用組合物j。將氣體產生層形成用組合物j之組成示於表1。
[製造例8''']氣體產生層形成用組合物k之製備
向甲苯中添加丙烯酸丁酯50重量份、丙烯酸乙酯50重量份、丙烯酸5重量份、丙烯酸2-羥乙酯0.1重量份、三羥甲基丙烷三丙烯酸酯0.3重量份、及作為聚合起始劑之過氧化苯甲醯0.1重量份後,加熱至70℃而獲得丙烯酸系共聚物(聚合物E)甲苯溶液。
將聚合物E之甲苯溶液(聚合物E:100重量份)、環氧系交聯劑(三菱瓦斯化學公司製造,商品名「TETRAD-C」)0.1重量份、及紫外線吸收劑(BASF公司製造,商品名「Tinuvin 400」)20重量份混合而製備氣體產生層形成用組合物k。將氣體產生層形成用組合物k之組成示於表1。
[製造例9]氣體產生層形成用組合物I之製備
作為UV吸收劑,使用2-[5-氯-2H-苯并***-2-基]-4-甲基-6-(第三丁基)苯酚(商品名「TINUVIN 326」,BASF公司製造)20重量份,除此以外,以與製造例1同樣之方式製備氣體產生層形成用組合物I。將氣體產生層形成用組合物I之組成示於表1。
[製造例10]含熱膨脹性微小球之組合物II之製備
不調配紫外線吸收劑,將交聯劑之調配量設為1.4重量份,且調配熱膨脹性微小球(松本油脂製藥公司製造,商品名「Matsumoto Microsphere F-50D」)30重量份、及萜酚系黏著賦予樹脂(住友電木公司製造,商品名「SUMILITERESIN PR51732」)10重量份,除此以外,以與製造例5同樣之方式製備含熱膨脹性微小球之組合物II。
[製造例11]含熱膨脹性微小球之組合物III之製備
代替萜酚系黏著賦予樹脂(住友電木公司製造,商品名「SUMILITERESIN PR51732」)10重量份,使用萜酚系黏著賦予樹脂(Yasuhara Chemical公司製造,商品名「YS POLYSTER T160」)20重量份,除此以外,以與製造例5同樣之方式製備含熱膨脹性微小球之組合物III。
[表1]
氣體產生層形成用組合物 | 製造例1 氣體產生層形成用組合物a | 製造例2 氣體產生層形成用組合物b | 製造例3 氣體產生層形成用組合物c | 製造例4 氣體產生層形成用組合物d | 製造例5 氣體產生層形成用組合物e | ||
基礎聚合物 | 材質 | 丙烯酸系 | 丙烯酸系 | 丙烯酸系 | 丙烯酸系 | 丙烯酸系 | |
聚合物種 | 聚合物A | 聚合物A | 聚合物A | 聚合物A | 聚合物B | ||
交聯劑 | 交聯劑種 | 異氰酸酯系 | 異氰酸酯系 | 異氰酸酯系 | 異氰酸酯系 | 異氰酸酯系 | |
交聯劑份數 | Coronate/L(1.5) | Coronate/L(1.5) | Coronate/L(1.5) | Coronate/L(1.5) | Coronate/L(1.0) | ||
UV吸收劑 | UV吸收劑種 (骨架) | 羥基苯基三𠯤系 | 羥基苯基三𠯤系 | 羥基苯基三𠯤系 | 羥基苯基三𠯤系 | 羥基苯基三𠯤系 | |
品名、份數 | Tinuvin477(20) | Tinuvin477(10) | Tinuvin460(10) | Tinuvin400(20) | Tinuvin477(20) | ||
UV吸收劑之分子量 | 958.2 | 958.2 | 629.8 | 647.8 | 958.2 | ||
TGA10%重量減少溫度[℃] | 352.8 | 352.8 | 401.5 | 391.7 | 352.8 | ||
UV吸收劑之最大吸收波長 | 356 nm | 356 nm | 349 nm | 336 nm | 356 nm | ||
備註 | |||||||
實施例1~5 | 實施例6 | 實施例7 | 實施例8 | 實施例9 | |||
氣體產生層形成用組合物 | 製造例6 氣體產生層形成用組合物f | 製造例7 氣體產生層形成用組合物g | 製造例8 氣體產生層形成用組合物h | 製造例8' 氣體產生層形成用組合物i | 製造例8" 氣體產生層形成用組合物j | 製造例8''' 氣體產生層形成用組合物k | |
基礎聚合物 | 材質 | 丙烯酸系 | 丙烯酸系 | SEBS系 | 丙烯酸系 | 丙烯酸系 | 丙烯酸系 |
聚合物種 | 聚合物C | 聚合物C | 聚合物D | 聚合物B | 聚合物E | ||
交聯劑 | 交聯劑種 | 異氰酸酯系 | 環氧系 | 環氧系 | 環氧系 | 環氧系 | 環氧系 |
交聯劑份數 | Coronate/L(1.0) | Tetrad C(0.1) | Tetrad C(3) | Tetrad C(0.1) | Tetrad C(0.1) | Tetrad C(0.1) | |
UV吸收劑 | UV吸收劑種 (骨架) | 羥基苯基三𠯤系 | 羥基苯基三𠯤系 | 羥基苯基三𠯤系 | 羥基苯基三𠯤系 | 羥基苯基三𠯤系 | 羥基苯基三𠯤系 |
品名、份數 | Tinuvin477(20) | Tinuvin477(20) | Tinuvin477(20) | Tinuvin400(20) | Tinuvin400(20) | Tinuvin400(20) | |
UV吸收劑之分子量 | 958.2 | 958.2 | 958.2 | 647.8 | 647.8 | 647.8 | |
TGA10%重量減少溫度[℃] | 352.8 | 352.8 | 352.8 | 391.7 | 391.7 | 391.7 | |
UV吸收劑之最大吸收波長 | 356 nm | 356 nm | 356 nm | 336 nm | 336 nm | 336 nm | |
備註 | |||||||
實施例10 | 實施例11 | 實施例12 | 實施例13 | 實施例14 | 實施例15 | ||
氣體產生層形成用組合物 | 製造例9 氣體產生層形成用組合物I | 製造例10 含熱膨脹性微小球之組合物II | 製造例11 含熱膨脹性微小球之組合物III | ||||
基礎聚合物 | 材質 | 丙烯酸系 | 丙烯酸系 | 丙烯酸系 | |||
聚合物種 | 聚合物A | 聚合物A | 聚合物A | ||||
交聯劑 | 交聯劑種 | 異氰酸酯系 | 異氰酸酯系 | 異氰酸酯系 | |||
交聯劑份數 | Coronate/L(1.5) | Coronate/L(1.4) | Coronate/L(1.4) | ||||
UV吸收劑 | UV吸收劑種 (骨架) | 苯并***系 | - | - | |||
品名、份數 | Tinuvin326(20) | - | - | ||||
UV吸收劑之分子量 | 315.8 | - | - | ||||
TGA10%重量減少溫度[℃] | 234.5 | - | - | ||||
UV吸收劑之最大吸收波長 | 355 nm | - | - | ||||
備註 | 含熱膨脹性微小球 | 含熱膨脹性微小球 | |||||
比較例1、2 | 比較例3 | 比較例4 |
[製造例12]黏著劑a之製備
以與製造例1同樣之方式獲得丙烯酸系共聚物(聚合物A)之甲苯溶液。
將聚合物A之甲苯溶液(聚合物A:100重量份)、異氰酸酯系交聯劑(Nippon Polyurethane公司製造,商品名「Coronate L」)3重量份、及界面活性劑(花王公司製造,商品名「EXCEPARL IPP」)5重量份混合而製備黏著劑a。將黏著劑a之組成示於表2。
[製造例12']黏著劑b之製備
以與製造例6同樣之方式獲得丙烯酸系共聚物(聚合物C)之甲苯溶液。
將聚合物C之甲苯溶液(聚合物C:100重量份)、異氰酸酯系交聯劑(Nippon Polyurethane公司製造,商品名「Coronate L」)3重量份、及環氧系交聯劑(三菱瓦斯化學公司製造,商品名「TETRAD-C」)1重量份混合而製備黏著劑b。將黏著劑b之組成示於表2。
[製造例13]黏著劑I之製備
將交聯劑之調配量設為1重量份,且不含有界面活性劑,除此以外,以與製造例12同樣之方式製備黏著劑I。將黏著劑I之組成示於表2。
[表2]
黏著劑組合物 | 製造例12 黏著劑a | 製造例12' 黏著劑b | 製造例13 黏著劑I | |
基礎聚合物 | 材質 | 丙烯酸系 | 丙烯酸系 | 丙烯酸系 |
聚合物種 | 聚合物A | 聚合物C | 聚合物A | |
交聯劑 | 交聯劑種 | 異氰酸酯系 | 異氰酸酯系 | 異氰酸酯系 |
品名、份數 | Coronate/L(3) | Coronate/L(3) | Coronate/L(1) | |
交聯劑種 | - | 環氧系 | - | |
品名、份數 | - | Tetrad C(1) | - | |
界面活性劑 | 界面活性劑種 | 脂肪酸酯系 | - | - |
品名、份數 | EXCEPARL IPP(5) | - | - | |
實施例2~10 比較例2 | 實施例13、14、15 | 比較例3~4 |
[製造例14]中間層形成用組合物a之製備
以與製造例5同樣之方式獲得丙烯酸系共聚物(聚合物B)之乙酸乙酯溶液。
將聚合物B之乙酸乙酯溶液(聚合物B:100重量份)、環氧系交聯劑(三菱瓦斯化學公司製造,商品名「Tetrad C」)1重量份、UV低聚物(三菱化學公司製造,商品名「紫光UV-1700B」)50重量份、及光聚合起始劑(BASF公司製造,商品名「Omnirad 127」)3重量份混合而製備中間層形成用組合物a。將中間層形成用組合物a之組成示於表3。
[製造例15]中間層形成用組合物b之製備
將順丁烯二酸改性苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物(SEBS:苯乙烯部位/乙烯-丁烯部位(重量比)=30/70,酸值:10(mg-CH
3ONa/g),旭化成化學公司製造,商品名「Tuftec M1913」)100重量份、環氧系交聯劑(三菱瓦斯化學公司製造,商品名「TETRAD-C」)3重量份、脂肪酸酯系界面活性劑(花王公司製造,商品名「EXCEPARL IPP」,分子量:298.5,烷基之碳數:16)3重量份、及作為溶劑之甲苯混合而獲得中間層形成用組合物b。將中間層形成用組合物b之組成示於表3。
[表3]
中間層形成用組合物 | 製造例14 中間層形成用組合物a | 製造例15 中間層形成用組合物b | |
基礎聚合物 | 材質 | 丙烯酸系 | SEBS系 |
聚合物種 | 聚合物B | ||
UV低聚物 | UV低聚物 | UV硬化型丙烯酸胺基甲酸酯 | - |
品名、份數 | UV-1700B(50) | - | |
交聯劑 | 交聯劑種 | 環氧系 | 環氧系 |
品名、份數 | Tetrad C(1) | Tetrad C(3) | |
光聚合起始劑 | 光聚合起始劑 | 苯烷酮系 | - |
品名、份數 | Irg127(3) | - | |
實施例3 | 實施例4 |
[實施例1]
將製造例1中獲得之氣體產生層形成用組合物a以溶劑揮發(乾燥)後之厚度成為7 μm之方式塗佈於帶有矽酮脫模劑處理面之聚對苯二甲酸乙二酯膜(東麗公司製造,商品名「Cerapeel」厚度:38 μm),其後進行乾燥,而獲得於該聚對苯二甲酸乙二酯膜上僅包含氣體產生層之黏著片材。
將所得之黏著片材供於上述評價(1)~(13)。將結果示於表4。
[實施例2]
將製造例12中獲得之黏著劑a以溶劑揮發(乾燥)後之厚度成為15 μm之方式塗佈於帶有矽酮脫模劑處理面之聚對苯二甲酸乙二酯膜(厚度:75 μm),其後進行乾燥,而於該聚對苯二甲酸乙二酯膜上形成黏著劑層前驅層a。
將製造例1中獲得之氣體產生層形成用組合物a以溶劑揮發(乾燥)後之厚度成為7 μm之方式塗佈於帶有矽酮脫模劑處理面之聚對苯二甲酸乙二酯膜(東麗公司製造,商品名「Cerapeel」厚度:38 μm),其後進行乾燥,而於該聚對苯二甲酸乙二酯膜上形成氣體產生層前驅層a。
將上述黏著劑層前驅層a與上述氣體產生層前驅層a於輥間層壓而貼合,獲得夾於帶有矽酮脫模劑處理面之聚對苯二甲酸乙二酯膜之間的黏著片材(黏著劑層/氣體產生層)。
將所得之黏著片材供於上述評價(1)~(13)。將結果示於表4。
[實施例3]
將製造例12中獲得之黏著劑a以溶劑揮發(乾燥)後之厚度成為15 μm之方式塗佈於帶有矽酮脫模劑處理面之聚對苯二甲酸乙二酯膜(厚度:75 μm),其後進行乾燥,而於該聚對苯二甲酸乙二酯膜上形成黏著劑層前驅層a。
將製造例14中獲得之中間層形成用組合物a以溶劑揮發(乾燥)後之厚度成為15 μm之方式塗佈於帶有矽酮脫模劑處理面之聚對苯二甲酸乙二酯膜(東麗公司製造,商品名「Cerapeel」厚度:38 μm),其後進行乾燥,而於該聚對苯二甲酸乙二酯膜上形成中間層前驅層a。
繼而,將上述黏著劑層前驅層a與上述中間層前驅層a於輥間層壓而貼合,自中間層前驅層側於500 mJ/cm
2之條件下進行UV照射,而獲得夾於帶有矽酮脫模劑處理面之聚對苯二甲酸乙二酯膜之間的積層體前驅層a。
將製造例1中獲得之氣體產生層形成用組合物a以溶劑揮發(乾燥)後之厚度成為7 μm之方式塗佈於帶有矽酮脫模劑處理面之聚對苯二甲酸乙二酯膜(東麗公司製造,商品名「Cerapeel」厚度:38 μm),其後進行乾燥,而於該聚對苯二甲酸乙二酯膜上形成氣體產生層前驅層a。
將上述積層體前驅層a之中間層前驅層a側之帶有矽酮脫模劑處理面之聚對苯二甲酸乙二酯膜剝離後,將積層體前驅層a之中間層前驅層a與上述氣體產生層前驅層a於輥間層壓而貼合,獲得夾於帶有矽酮脫模劑處理面之聚對苯二甲酸乙二酯膜之間的黏著片材(黏著劑層/中間層/氣體產生層)。
將所得之黏著片材供於上述評價(1)~(13)。將結果示於表4。
[實施例4]
將製造例12中獲得之黏著劑a以溶劑揮發(乾燥)後之厚度成為15 μm之方式塗佈於帶有矽酮脫模劑處理面之聚對苯二甲酸乙二酯膜(厚度:75 μm),其後進行乾燥,而於該聚對苯二甲酸乙二酯膜上形成黏著劑層前驅層a。
將製造例15中獲得之中間層形成用組合物b以溶劑揮發(乾燥)後之厚度成為15 μm之方式塗佈於帶有矽酮脫模劑處理面之聚對苯二甲酸乙二酯膜(東麗公司製造,商品名「Cerapeel」厚度:38 μm),其後進行乾燥,而於該聚對苯二甲酸乙二酯膜上形成中間層前驅層a。
繼而,將上述黏著劑層前驅層a與上述中間層前驅層b於輥間層壓而貼合,獲得夾於帶有矽酮脫模劑處理面之聚對苯二甲酸乙二酯膜之間的積層體前驅層b。
將製造例1中獲得之氣體產生層形成用組合物a以溶劑揮發(乾燥)後之厚度成為7 μm之方式塗佈於帶有矽酮脫模劑處理面之聚對苯二甲酸乙二酯膜(東麗公司製造,商品名「Cerapeel」厚度:38 μm),其後進行乾燥,而於該聚對苯二甲酸乙二酯膜上形成氣體產生層前驅層a。
將上述積層體前驅層b之中間層前驅層b側之帶有矽酮脫模劑處理面之聚對苯二甲酸乙二酯膜剝離後,將積層體前驅層b之中間層前驅層b與上述氣體產生層前驅層a於輥間層壓而貼合,獲得夾於帶有矽酮脫模劑處理面之聚對苯二甲酸乙二酯膜之間的黏著片材(黏著劑層/中間層/氣體產生層)。
將所得之黏著片材供於上述評價(1)~(13)。將結果示於表4。
[實施例5]
將製造例12中獲得之黏著劑a以溶劑揮發(乾燥)後之厚度成為15 μm之方式塗佈於帶有矽酮脫模劑處理面之聚對苯二甲酸乙二酯膜(厚度:75 μm),其後進行乾燥,而於該聚對苯二甲酸乙二酯膜上形成黏著劑層前驅層a。
將製造例1中獲得之氣體產生層形成用組合物a以溶劑揮發(乾燥)後之厚度成為7 μm之方式塗佈於帶有矽酮脫模劑處理面之聚對苯二甲酸乙二酯膜(東麗公司製造,商品名「Cerapeel」厚度:38 μm),其後進行乾燥,而於該聚對苯二甲酸乙二酯膜上形成氣體產生層前驅層a。
將上述黏著劑層前驅層a於輥間層壓而貼合於聚對苯二甲酸乙二酯膜(東麗公司製造,商品名「Lumirror#2F51N」厚度:2 μm)之單側。
繼而,將氣體產生層前驅層a於輥間層壓而貼合於上述聚對苯二甲酸乙二酯膜之與黏著劑層前驅層a相反之側。
以此方式獲得夾於帶有矽酮脫模劑處理面之聚對苯二甲酸乙二酯膜之間的黏著片材(黏著劑層/中間層/氣體產生層)。
將所得之黏著片材供於上述評價(1)~(13)。將結果示於表4。
[實施例6]
代替氣體產生層形成用組合物a而使用氣體產生層形成用組合物b,除此以外,以與實施例5同樣之方式獲得黏著片材。將所得之黏著片材供於上述評價(1)~(13)。將結果示於表5。
[實施例7]
代替氣體產生層形成用組合物a而使用氣體產生層形成用組合物c,除此以外,以與實施例5同樣之方式獲得黏著片材。將所得之黏著片材供於上述評價(1)~(13)。將結果示於表5。
[實施例8]
代替氣體產生層形成用組合物a而使用氣體產生層形成用組合物d,除此以外,以與實施例5同樣之方式獲得黏著片材。將所得之黏著片材供於上述評價(1)~(13)。將結果示於表5。
[實施例9]
代替氣體產生層形成用組合物a而使用氣體產生層形成用組合物e,除此以外,以與實施例5同樣之方式獲得黏著片材。將所得之黏著片材供於上述評價(1)~(13)。將結果示於表5。
[實施例10]
代替氣體產生層形成用組合物a而使用氣體產生層形成用組合物f,除此以外,以與實施例5同樣之方式獲得黏著片材。將所得之黏著片材供於上述評價(1)~(13)。將結果示於表5。
[實施例11]
代替氣體產生層形成用組合物a而使用氣體產生層形成用組合物g,除此以外,以與實施例1同樣之方式獲得黏著片材。將所得之黏著片材供於上述評價。將結果示於表6。
[實施例12]
代替氣體產生層形成用組合物a而使用氣體產生層形成用組合物h,除此以外,以與實施例1同樣之方式獲得黏著片材。將所得之黏著片材供於上述評價。將結果示於表6。
[表4]
實施例1 | 實施例2 | 實施例3 | 實施例4 | 實施例5 | ||
黏著劑層 | 黏著劑 | - | 黏著劑a | 黏著劑a | 黏著劑a | 黏著劑a |
厚度[μm] | - | 15 | 7 | 7 | 7 | |
黏著層之水蒸氣透過率[g/(m 2・day)] | - | 3435.3 | 4059.3 | 4059.3 | 4059.3 | |
中間層 | 中間層材料 | - | - | 中間層形成用組合物a | 中間層形成用組合物b | PET |
厚度[μm] | - | - | 15 | 15 | 2 | |
中間層之水蒸氣透過率[g/(m 2・day)] | - | - | 1778 | 78 | 1114.34 | |
氣體產生層 | 氣體產生層材料 | 氣體產生層形成用組合物a | 氣體產生層形成用組合物a | 氣體產生層形成用組合物a | 氣體產生層形成用組合物a | 氣體產生層形成用組合物a |
厚度[μm] | 7 | 7 | 7 | 7 | 7 | |
UV吸收劑之分子量 | 958.2 | 958.2 | 958.2 | 958.2 | 958.2 | |
TGA10%重量減少溫度[℃] | 352.8 | 352.8 | 352.8 | 352.8 | 352.8 | |
UV吸收劑之最大吸收波長 | 356 nm | 356 nm | 356 nm | 356 nm | 356 nm | |
黏著片材 | 厚度[μm] | 7 | 22 | 29 | 29 | 16 |
氣體產生特性 | 透過率@360 nm[%] | 0.05 | 0.01 | 0.02 | 0.00 | 0.01 |
透過率@500 nm[%] | 91.78 | 91.98 | 92.62 | 92.76 | 91.98 | |
最大氣體產生峰值溫度[℃] | 380 | 380 | 370 | 370 | 380 | |
氣化起始溫度[℃] | 335 | 335 | 330 | 330 | 335 | |
產生氣體種 | 烴 | 烴 | 烴 | 烴 | 烴 | |
TGA5%重量減少溫度[℃] | 310.6 | 312.6 | 306.2 | 304.5 | 312.6 | |
TGA10%重量減少溫度[℃] | 33.5 | 349.5 | 340.1 | 339.5 | 349.5 | |
氣體阻隔特性 | 水蒸氣透過率[g/(m 2・day)] | 4062.6 | 3158.9 | 1238.1 | 198.1 | 334.2 |
表面形狀變化 | 高度(Y:垂直位移)[μm] | -6.7 | 3.4 | 1.4 | 1.2 | 10.6 |
直徑(X:水平位移)[μm] | 19.1 | 23.1 | 13.2 | 10.1 | 51.2 | |
狀態 | 破裂凹 | 發泡凸 | 發泡凸 | 發泡凸 | 發泡凸 | |
霧度值 | 0.2 | 1.5 | 0.4 | 1.2 | 1.5 | |
相對於SUS430之黏著力[N/20 mm] (黏著劑層側) | 4.20 | 3.46 | 2.32 | 0.33 | ||
相對於SUS430之黏著力[N/20 mm] (氣體產生層側) | 6.02 | 5.22 | 3.86 | 2.95 | 4.74 | |
剝離性 | 〇 | 〇 | 〇 | 〇 | ◎ | |
變形之面內均一性 | 〇 | 〇 | 〇 | 〇 | 〇 | |
被黏著體視認性 | 〇 | 〇 | 〇 | 〇 | 〇 | |
位置選擇性 | 〇 | 〇 | 〇 | 〇 | 〇 |
[表5]
實施例6 | 實施例7 | 實施例8 | 實施例9 | 實施例10 | ||
黏著劑層 | 黏著劑 | 黏著劑a | 黏著劑a | 黏著劑a | 黏著劑a | 黏著劑a |
厚度[μm] | 7 | 7 | 7 | 7 | 7 | |
黏著層之水蒸氣透過率[g/(m 2・day)] | 4059.3 | 4059.3 | 4059.3 | 4059.3 | 4059.3 | |
中間層 | 中間層材料 | PET | PET | PET | PET | PET |
厚度[μm] | 2 | 2 | 2 | 2 | 2 | |
中間層之水蒸氣透過率[g/(m 2・day)] | 1114.34 | 1114.34 | 1114.34 | 1114.34 | 1114.34 | |
氣體產生層 | 氣體產生層材料 | 氣體產生層形成用組合物b | 氣體產生層形成用組合物c | 氣體產生層形成用組合物d | 氣體產生層形成用組合物e | 氣體產生層形成用組合物f |
厚度[μm] | 7 | 7 | 7 | 7 | 7 | |
UV吸收劑之分子量 | 958.2 | 629.8 | 647.8 | 958.2 | 958.2 | |
TGA10%重量減少溫度[℃] | 352.8 | 401.5 | 391.7 | 352.8 | 352.8 | |
UV吸收劑之最大吸收波長 | 356 nm | 349 nm | 336 nm | 356 nm | 356 nm | |
黏著片材 | 厚度[μm] | 16 | 16 | 16 | 16 | 16 |
氣體產生特性 | 透過率@360 nm[%] | 0.05 | 0.00 | 0.20 | 0.02 | 0.01 |
透過率@500 nm[%] | 92.2 | 92.10 | 91.93 | 90.24 | 92.17 | |
最大氣體產生峰值溫度[℃] | 380 | 390 | 395 | 380 | 380 | |
氣化起始溫度[℃] | 335 | 360 | 370 | 335 | 335 | |
產生氣體種 | 烴 | 烴 | 烴 | 烴 | 烴 | |
TGA5%重量減少溫度[℃] | 310.3 | 319.2 | 326.2 | 313.2 | 309.7 | |
TGA10%重量減少溫度[℃] | 347.2 | 359.6 | 369.9 | 351.4 | 349.7 | |
氣體阻隔特性 | 水蒸氣透過率[g/(m 2・day)] | 330.2 | 328.4 | 339.4 | 336.2 | 284.1 |
表面形狀變化 | 高度(Y:垂直位移)[μm] | 5.3 | 10.5 | 4.5 | 6.5 | 15.7 |
直徑(X:水平位移)[μm] | 42.1 | 40.6 | 41.3 | 39.3 | 41.5 | |
狀態 | 發泡凸 | 發泡凸 | 發泡凸 | 發泡凸 | 發泡凸 | |
霧度值 | 1.6 | 10.4 | 1.4 | 26 | 9 | |
相對於SUS430之黏著力[N/20 mm] (黏著劑層側) | 0.31 | 0.35 | 0.39 | 0.46 | 0.42 | |
相對於SUS430之黏著力[N/20 mm] (氣體產生層側) | 4.59 | 4.30 | 4.68 | 2.52 | 6.37 | |
剝離性 | 〇 | ◎ | 〇 | 〇 | ◎ | |
變形之面內均一性 | 〇 | △ | 〇 | △ | △ | |
被黏著體視認性 | 〇 | 〇 | 〇 | △ | 〇 | |
位置選擇性 | 〇 | 〇 | 〇 | 〇 | 〇 |
[表6]
實施例11 | 實施例12 | 實施例13 | 實施例14 | 實施例15 | ||
黏著劑層 | 黏著劑 | - | - | 黏著劑b | 黏著劑b | 黏著劑b |
厚度[μm] | - | - | 10 | 10 | 10 | |
黏著層之水蒸氣透過率[g/(m 2・day)] | - | - | 3754.3 | 3754.3 | 3754.3 | |
中間層 | 中間層材料 | - | - | - | - | - |
厚度[μm] | - | - | - | - | - | |
中間層之水蒸氣透過率[g/(m 2・day)] | - | - | - | - | - | |
氣體產生層 | 氣體產生層材料 | 氣體產生層形成用組合物g | 氣體產生層形成用組合物h | 氣體產生層形成用組合物i | 氣體產生層形成用組合物j | 氣體產生層形成用組合物k |
厚度[μm] | 20 | 20 | 20 | 20 | 20 | |
UV吸收劑之分子量 | 958.2 | 958.2 | 647.8 | 647.8 | 647.8 | |
TGA10%重量減少溫度[℃] | 352.8 | 352.8 | 391.7 | 391.7 | 391.7 | |
UV吸收劑之最大吸收波長 | 356 nm | 356 nm | 336 nm | 336 nm | 336 nm | |
厚度h(gas)[μm] | 20 | 20 | 20 | 20 | 20 | |
彈性模數Er(gas)[MPa] | 0.95 | 77.62 | 3.05 | 2.88 | 2.12 | |
LogEr(gas) | 5.98 | 7.89 | 6.48 | 6.46 | 6.33 | |
8.01×h(gas) -0.116 | 5.66 | 5.66 | 5.66 | 5.66 | 5.66 | |
根據Log(Er(gas)×10 6)≧8.01×h(gas) - 0 .116算出之氣體產生層之彈性模數之下限值[MPa] | 0.46 | 0.46 | 0.46 | 0.46 | 0.46 | |
7.66×h(gas) -0.092 | 5.81 | 5.81 | 5.81 | 5.81 | 5.81 | |
根據Log(Er(gas)×10 6)≧7.66×h(gas) -0.092算出之氣體產生層之彈性模數之下限值[MPa] | 0.65 | 0.65 | 0.65 | 0.65 | 0.65 | |
7.52×h(gas) -0.081 | 5.90 | 5.90 | 5.90 | 5.90 | 5.90 | |
根據Log(Er(gas)×10 6)≧7.52×h(gas) -0.081算出之氣體產生層之彈性模數之下限值[MPa] | 0.79 | 0.79 | 0.79 | 0.79 | 0.79 | |
47.675×h(gas) -0.519 | 10.07 | 10.07 | 10.07 | 10.07 | 10.07 | |
根據Log(Er(gas)×10 6)≦47.675×h(gas) -0.519算出之氣體產生層之彈性模數之上限值[MPa] | 11765.71 | 11765.71 | 11,765.7 | 11,765.7 | 11,765.7 | |
黏著片材 | 厚度[μm] | 20 | 20 | 30 | 30 | 30 |
氣體產生特性 | 透過率@360 nm[%] | 0.18 | 0.19 | 0.37 | 0.48 | 0.36 |
透過率@500 nm[%] | 89.11 | 90.20 | 88.43 | 83.44 | 88.30 | |
最大氣體產生峰值溫度[℃] | 380 | 380 | 390 | 395 | 395 | |
氣化起始溫度[℃] | 335 | 335 | 360 | 375 | 370 | |
產生氣體種 | 烴 | 烴 | 烴 | 烴 | 烴 | |
TGA5%重量減少溫度[℃] | 304.90 | 308.40 | 328.9 | 331.1 | 332.3 | |
TGA10%重量減少溫度[℃] | 327.80 | 329.80 | 358.0 | 360.4 | 359.6 | |
氣體阻隔特性 | 水蒸氣透過率[g/(m 2・day)] | 3113.20 | 3356.80 | 2888.1 | 3001.2 | 2791.3 |
表面形狀變化 | 高度(Y:垂直位移)[μm] | 0.9 | 0.7 | 2.4 | 1.3 | 1.9 |
直徑(X:水平位移)[μm] | 12.3 | 14.6 | 26.3 | 25.7 | 22.4 | |
狀態 | 發泡凸 | 發泡凸 | 發泡凸 | 發泡凸 | 發泡凸 | |
霧度值 | 7.3 | 8.2 | 5.8 | 47.1 | 5.8 | |
相對於SUS430之黏著力[N/20 mm] (黏著劑層側) | - | - | 0.38 | 0.28 | 0.43 | |
相對於SUS430之黏著力[N/20 mm] (氣體產生層側) | 0.40 | 0.21 | 7.50 | 8.72 | 16.20 | |
剝離性 | 〇 | 〇 | 〇 | 〇 | 〇 | |
變形之面內均一性 | 〇 | 〇 | 〇 | △ | 〇 | |
被黏著體視認性 | 〇 | 〇 | 〇 | △ | 〇 | |
位置選擇性 | 〇 | 〇 | 〇 | 〇 | 〇 |
[比較例1]
代替氣體產生層形成用組合物a而使用氣體產生層形成用組合物I,除此以外,以與實施例1同樣之方式獲得黏著片材。將所得之黏著片材供於上述評價(1)~(13)。將結果示於表7。
[比較例2]
代替氣體產生層形成用組合物a而使用氣體產生層形成用組合物I,除此以外,以與實施例5同樣之方式獲得黏著片材。將所得之黏著片材供於上述評價(1)~(13)。將結果示於表7。
[比較例3]
代替黏著劑a而使用黏著劑I,將黏著劑層之厚度設為10 μm,使用厚度188 μm之PET膜作為中間層,代替氣體產生層形成用組合物a而使用含熱膨脹性微小球之組合物II形成48 μm之氣體產生層,除此以外,以與實施例5同樣之方式獲得黏著片材。將所得之黏著片材供於上述評價(1)~(13)。將結果示於表7。
[比較例4]
代替黏著劑a而使用黏著劑I,將黏著劑層之厚度設為10 μm,使用厚度100 μm之PET膜作為中間層,代替氣體產生層形成用組合物a而使用含熱膨脹性微小球之組合物III形成48 μm之氣體產生層,除此以外,以與實施例5同樣之方式獲得黏著片材。將所得之黏著片材供於上述評價(1)~(13)。將結果示於表7。
[表7]
比較例1 | 比較例2 | 比較例3 | 比較例4 | ||
黏著劑層 | 黏著劑 | - | 黏著劑a | 黏著劑I | 黏著劑I |
厚度[μm] | - | 7 | 10 | 10 | |
黏著層之水蒸氣透過率[g/(m 2・day)] | - | 4059.3 | - | - | |
中間層 | 中間層材料 | - | PET | PET | PET |
厚度[μm] | - | 2 | 188 | 100 | |
中間層之水蒸氣透過率[g/(m 2・day)] | - | 3450 | - | - | |
氣體產生層 | 氣體產生層材料 | 氣體產生層形成用組合物I | 氣體產生層形成用組合物I | 含熱膨脹性微小球之組合物II | 含熱膨脹性微小球之組合物III |
厚度[μm] | 7 | 7 | 48 | 48 | |
UV吸收劑之分子量 | 315.8 | 315.8 | - | - | |
TGA10%重量減少溫度[℃] | 234.5 | 232.5 | - | - | |
UV吸收劑之最大吸收波長 | 355 nm | 355 nm | - | - | |
黏著片材 | 厚度[μm] | 7 | 16 | 246 | 158 |
氣體產生特性 | 透過率@360 nm[%] | 7.56 | 7.45 | 58.32 | 71.78 |
透過率@500 nm[%] | 88.74 | 86.44 | 84.01 | 84.15 | |
最大氣體產生峰值溫度[℃] | 250 | 250 | - | - | |
氣化起始溫度[℃] | 215 | 215 | - | - | |
產生氣體種 | 烴 鹵素化合物 | 烴 鹵素化合物 | 烴 | 烴 | |
TGA5%重量減少溫度[℃] | 240.6 | 245.6 | - | - | |
TGA10%重量減少溫度[℃] | 280.3 | 284.3 | - | - | |
氣體阻隔特性 | 水蒸氣透過率[g/(m 2・day)] | 4062.6 | 298.6 | - | - |
表面形狀變化 | 高度(Y:垂直位移)[μm] | -6.2 | 8.2 | ≧100 μm | ≧100 μm |
直徑(X:水平位移)[μm] | 16.1 | 36.4 | ≧200 μm | ≧200 μm | |
狀態 | 破裂凹 | 發泡凸 | 複數發泡凸 | 複數發泡凸 | |
霧度值 | 51.2 | 58.5 | 66.4 | 56.4 | |
相對於SUS430之黏著力[N/20 mm] (黏著劑層側) | 1.05 | - | - | ||
相對於SUS430之黏著力[N/20 mm] (氣體產生層側) | 0.58 | 0.58 | - | - | |
剝離性 | 〇 | ◎ | ◎ | ◎ | |
變形之面內均一性 | △ | △ | × | × | |
被黏著體視認性 | × | × | × | × | |
位置選擇性 | 〇 | 〇 | × | × |
4:樣品
5A,5B:試樣保持器
6:壓縮試驗機
10:氣體產生層
20:黏著劑層
30:中間層
100,100',200:黏著片材
圖1(a)、(b)係本發明之一實施方式之黏著片材之概略剖視圖。
圖2係本發明之其他實施方式之黏著片材之概略剖視圖。
圖3係對穿刺強度之測定方法進行說明之概略圖。
10:氣體產生層
20:黏著劑層
100,100':黏著片材
Claims (15)
- 一種黏著片材,其具備藉由雷射光照射而產生氣體之氣體產生層,且霧度值為50%以下,波長360nm之紫外線透過率為30%以下,上述氣體產生層為產生烴系氣體之層。
- 如請求項1之黏著片材,其中上述氣體產生層之厚度為0.1μm~50μm。
- 如請求項1或2之黏著片材,其中上述氣體產生層為可吸收紫外線之層。
- 如請求項3之黏著片材,其中上述氣體產生層含有紫外線吸收劑。
- 如請求項1或2之黏著片材,其波長500nm之紫外線透過率為50%~100%。
- 如請求項1或2之黏著片材,其中上述氣體產生層之氣化起始溫度為150℃~500℃,所謂氣體產生層之氣化起始溫度係指根據使黏著片材升溫時之釋出氣體分析(EGA分析)算出之氣體產生上升溫度,所謂氣體產生上升溫度係定義為達到根據EGA分析所得之釋出氣體分析/質譜(EGA/MS) 圖譜之最大氣體產生峰值之半值的溫度。
- 如請求項1或2之黏著片材,其10%重量減少溫度為200℃~500℃,所謂10%重量減少溫度係指使黏著片材升溫時之熱重量分析(TGA分析)中,氣體產生層之重量相對於升溫前之重量而減少10重量%之時間點的溫度。
- 如請求項1或2之黏著片材,其於上述氣體產生層之至少單側進而具備黏著劑層,且該黏著劑層係其表面藉由對上述黏著片材照射雷射光而變形之層。
- 如請求項8之黏著片材,其中上述黏著劑層之厚度為0.1μm~50μm。
- 如請求項8之黏著片材,其中上述黏著劑層藉由對上述黏著片材照射雷射光而發泡。
- 一種電子零件之處理方法,其包括:將電子零件貼附於如請求項1至10中任一項之黏著片材上;及對該黏著片材照射雷射光而自該黏著片材剝離該電子零件。
- 如請求項11之電子零件之處理方法,其中上述電子零件之剝離係選擇位置地進行。
- 如請求項11或12之電子零件之處理方法,其包括:於將上述電子零件貼附於上述黏著片材後且自該黏著片材剝離該電子零件前,對該電子零件進行特定處理。
- 如請求項13之電子零件之處理方法,其中上述處理為研磨加工、切割加工、黏晶、打線接合、蝕刻、蒸鍍、成型、電路形成、檢查、產品檢驗、洗淨、轉印、排列、修復或裝置表面保護。
- 如請求項11或12之電子零件之處理方法,其包括:自上述黏著片材剝離上述電子零件之後,將電子零件配置於其他片材。