TW314502B - - Google Patents
Download PDFInfo
- Publication number
- TW314502B TW314502B TW084106660A TW84106660A TW314502B TW 314502 B TW314502 B TW 314502B TW 084106660 A TW084106660 A TW 084106660A TW 84106660 A TW84106660 A TW 84106660A TW 314502 B TW314502 B TW 314502B
- Authority
- TW
- Taiwan
- Prior art keywords
- less
- weight
- composition
- glass
- patent application
- Prior art date
Description
〇145〇2 αί B7五、發明説明(1/7) 經濟部中央標準局員工消費合作社印聚 (請先閱讀背面之注意事項再填寫本頁) 可 為小玻 之璃緣 出例 物性 量 物 物 。物 因圍性 維玻絶 産術 成定 當 生 成 物生 ,範解 纖及於 以技 組安 相 是 組 成是 的其降 璃性用 ,此 雒的 有 即 維 組説 要,可 玻耐廣 性 ί 纖好 具 , 纖 維其 重圍物 且的維 工術 璃良 上 合 璃 纖 , 常範生 而維纖 加技 玻有 質。組 玻 璃物 非維的 ,纖璃 的心 的且 實決性 的 玻成 傜纖小 要璃玻 法離 α 穎、 種解特。性 : 性組 物璃大 重玻 ,。方内丨新的 一來的性解分 解維 成玻寸 常、如性知用 種性 .藉物須工降成 降纖 組徑尺 非品例濕已是 51 解 可成必加可的 可璃 維直該 性産 。耐許其74供降 · 題組成可物率 物玻 纖之是 解的是的容尤 3 提可 問維達的生分 生些 璃小但 降成亦夠須 ,20以物 該纖可好種百 種一 玻常 , 。可製性足必維 4 題生.。現璃物良一量 一 到 的非的的物所工要維纖第問為 Η 發玻成及係重 於述 性有癌性生其加需纖璃利於徵加於之組性地下 關敘 解且致癌僅或可用璃玻專基特於基物維濕目以 傺藝 降出傺致不質的應玻的國傺之易偽化纖 Μ 之於 明技 。可指者無 ,性物些 ,徑美明物且明氧璃 、明在 發前的物究米傺而熱成這且直於發成性發屬玻性發擻 本先性生研微維然及組 。而小述本組濕本金該解本特 解 種 3 纖 械雒途 有致 此耐 鹼 降 其 降 各於璃 機纖用 具如 ,或 的 可 , 本紙張尺度適用中國國家標準(CNS ) Α4規格(210Χ297公釐) ^14502 五、發明説明(2/7)
SiO 2 45 至 60 A1 0 •2 3 少於 2 CaO + MgO 10 至 16 Na 0 + K 0 15 至 23 2 2 BO 2 3 10 至 18 P 0 2 S 0 至 4 BaO 0 至 1 其它 0 至 2. 本發明之玻璃鐵維組成物可以由離心技衔所處理加工 。所得的纖維具有良好的®濕性。足令人驚異的,該玻璃 纖維組成物顏現良好的Μ濃性。平均鐵維直徑較佳傷小於 1 0微米,且特佳介於2 . 5至5間c, 本發明之玻璃缕維組成物較佳傺具有以下重量百分率 的成分:
SiO 45 至 60 2 A1 0 少於 2 2 3 CaO + MgO 10至 16 Na 0 + K 0 多於 18 2 2 BO 少於 12 2 3 P 0 0至 4 2 S BaO 0 至 1 其它 0 至 2. 經濟部中央標準局員工消費合作社印製 (請先閲讀背面之注意事項再填寫本頁) 在另一較佳實施例中,本發明之玻璃纖維組成物具有 以下重量百分率的成分:
SiO^ 45 至 60 A1 0 2 3 少於 2 CaO + MgO 10 至 16 Na Ο - l· K 0 少於 18 BO 2 多於 12 2 3 Ρ 0 0 至 4 2 S BaO 0 至 1 其它 0 至 2. 本紙張尺度適用中國國家標準(CNS ) Α4規格(210X297公釐) 經濟部中央標準局員工消費合作社印製 A7 B7 五、發明説明(3/*5 本發明玻璃鐵維組成物較佳具有少於5 7重量百分率的 二氧化矽,待別是少於5 6 . 5重量百分率。 藉添加氧化鋁,可以改良爾濕性。因此,本發明組成 饬較佳含有少於0 . 5重量百分率,且通常少於1 . 5重量百分 率的氧化鋁。 添加五氧化二遴可以增加生物可降解性。因此,本發 明較佳含有至少〇 . 1重量百分率的P2 〇5。 本發明之玻璃_維組成物的爾鏢性可由已知的標準方 法如D G G方法栗澍定、在D G G方法中,1 0克之具有粒度介於 约3 6 0至40C擻米間的細玻璃纖保持在1〇〇毫升水之漭點五 小時。在將龀饬質急冷後,將溶液過濾且將一確定量的渡 詨蒸發至乾燥。所得之乾物質的重量容許計算玻璃鐵維在 水中的溶解量。此量以毫克/每克測試玻璃表示。 本發明玻璃装證组成物乏生饬可降解性的測試傜經由 :如DGG方法所述者,將1克玻璃粉加到以下所述組成的 生理溶液(Ρ Η值為7 · 4 )中:
NaCl 6.78 NH Cl 0.535 NaHCO 3 2.268 NaH PO Η 0 2 4 2 0.166 (Na3檸檬酸鹽)2Ha0 0.059 甘胺酸: 0.450 H SO 2 4 0.049 CaCl 0.022 選擇動態的測試條件如蕭爾茲(S c h ο 1 2 e )和康拉特( ο n r. a d t )中所述者。流速為3 0 0毫升/天。測時期間為1 4天 本紙張尺度適用中國國家標準(CNS ) A4規格(210X297公釐) --------1批衣------ΐτ1.-----0 (請先閲讀背面之注意事項再填寫本頁) ^14502五、發明説明( A7 B7 4 / 。结果以在1 4天後,溶液中的S i 諜吨徽v表示乘以1 0 0 表。 以下參照實例對本發明作更詳細之説明。 奮例1 將以下重量百分率組成的玻璃熔化。 sio 2 A1 0 2 : CaO MgO Na Ο κ Ο 2 Β Ο 2 3 其它 56.01.0 9.0 4.0 18.0 1.0 10.5 0.5. 此玻璃纖組成锪可由離.心技術所處理加工 使尾上述C G G方法,丨則得4 0毫克/克之c 上述之生物可降解性的測試得到5 5 0之值c 窨微2 : ' 將以下重量百分率組成的玻璃熔化。 t..訂 # (請先閱讀背面之注意事項再填寫本頁) 經濟部中央標準局員工消費合作社印製 sio 2 55 α A1 0 2 3 0 CaO 9 0 MgO 4 0 Na Ο 2 18 0 Κ 0 2 1 0 BO 2 3 .10 5 Ρ 0 2 5 1 0 其它 0 5. 此玻璃纖組成物可由離心技術所處理加工 使用上述DGG方法,測得40毫克/克之值& - 5 本紙張尺度適用中國國家標準(CNS ) A4規格(210X297公釐) A7〇"45ϊ)ί>_Ε_五、發明説明(5/3 上述之生物可降解性的測試得到6 0 0之值。 3 例 奮 3 2ο ο ο 2 0 0 2 0 — i laga 22^、 SACMNKB 其 °3它 7 0 8 5 3 7 1 0 2 0 1 5 5 0 5 8 2 0 5 Η Π 力 理 處 所 術 技 心 離 由 可 锪 成 組 Μ 璃 玻 此 值 之 克/ 克 毫 ο 5 得 測 法 方 G G D 述 上 用 使 到 得 試 測 的 性 解 降 可¾ 生 之 述 上 值 之 ο 5 '裝-- (請先閱讀背面之注意事項再填寫本頁) 4 例 窖 *?τ )2 ο Ο 3 5 o2oo=000 {匕 iJaga 2 2 2 r SACMNKBP 其 6 0 8 5 550582005. 3 7 0 2 10 7o 2 1 1 經濟部中央標準局員工消費合作社印製 Η 加 理 處 所Ϊ/ 克 術 I 毫 技 ο ύ 5 I得 离 ] 測 由 物方 或G' L G 組 D 鐵述 璃上 玻用 此使 之 克 之 ο ο 6 到 得 試 5 測例 的奮 性 解 降 可 物 生 之 述 上 值 Μ 本紙張尺度適用中國國家橾準(CNS ) Α4規格(210X297公釐) 314502 A7 B7 五、發明説明(6/7)
SiO 57.5 2 A1 0 2 3 0.5 CaO 8.1 MgO 3.6 Na 0 17-25 K 0 0.35 2 BO 12.4 其它 0.3. 此玻璃纖組成物可由離心技術所處理加工。 使用上述D G G方法,測得3 0毫克/克之值。 上述之生物可降解性的測試得到600之值。 窨例6 ---------裝—— (請先閱讀背面之注意事項再填寫本頁) 2 A1 0 2 3 0 5 CaO 8 3 MgO 1 8 Na O 18 6 K 0 2 0 4 BO 2 3 11 5 BaO 1 0 其它 0 4.
'1T 經濟部中央標準局員工消費合作社印製 此玻璃鐵組成物可由離心技術所處理加工。 使用上述D G G方法,測得3 0毫克/克之值。 上述之生物可降解性的測試得到600之值。 管例7
SiO 57.5 2 A1 O 2 3 0.5 CaO 8.3 MgO 1-8 Na O 17.1 K 0 0.4 2 BO 2 3 13.0 BaO 1.0 其它 ^ 0·4. 本紙張尺度適用中國國家標準(CNS ) A4規格(210X297公釐) A7 B7 五、發明説明(7/7) 此玻璃纖組成物可由離心技術所處理加工。 使用上述D G G方法,測得3 0毫克/克之值。 值 之 ο ο 6 到 得 試 測 的 性 解 降 可 物 生 之 述 上 8 例 奮 3 2 ο ο 3 ο 2 0 0 No ο 它 i 1 aga==-SACMNKB 其 7 0 5 5 5 4 8 7 1 7 0 1 4 0 1 0 5 0 4 --------· 批衣—— (請先閲讀背面之注意事項再填寫本頁) 可 解 法 锪. 降 方 成 G 可 組DGiwB 0 述生 璃上之 玻罔述 此 使上 所 術 技 心 離 j的 0 由 性 克 毫 ο 3 尋 /i 測 得 試 Η D 理 處 值值 之之 克00 訂 經濟部中央標準局員工消費合作社印製 8 本紙張尺度適用中國國家標準(CNS ) A4規格(2丨Ο X 297公釐)
Claims (1)
- S14502 A8 BS C8 D8 六、申請專利範i (申請號第84106660之修正本) 1/3 —* 種 生 物可 降 解 性 之 玻 璃 纗 維 組 成 物 ,其 特 Μ 下 重 量百 分 率 的 成 分 : Sio 2 45 至 60 A1 0 2 3 少於 2 CaO + : MgO 10 至 16 Na 0 BO 2 3 丨+ K 2 0 15 10 至 至 23 18 P 0 2 5 0 至 4 BaO 0 至 1 其它 0 至 2 如 申 請 專利 範 圍 第 1 項 之 玻 璃 m 維 組成物 » 含 有 以 下重 量 百 分 率 的 成 分 • SiO 2 45 3 60 A1 0 2 3 \ 少於 2. CaO 4 MgO 10 至 16 Na 0 + K 0 多於 18 3 0 2 3 2 少於 12 P 0 2 3 0 至 4 BaO 0 1 其它 0 至 2. 如 請 專利 範 圍 第 1 項 之 玻 璃 纖 維 組成物 9 含 有 以 下重 量 百 分 率 的 成 分 In fn m· nn mi I Am —r —^ϋ am— nn mV t , ^、v*(請先閱讀背面之注意事項再填寫本頁) 經濟部中央標準局貝工消費合作社印製 SiO 2 45 至 60 A1 0 2 3 少於 2 CaO + MgO 10 至 16 Na ο + κ ο 少於 18 BO 3 2 3 多於 12 P 0 2 S 〇 至 4 BaO 〇 至 1 其它 0 至 2 本紙張尺度逋用中國國家標準(CNS ) Μ規格(210X297公釐) S14302 A8 B8 C8 D8 經濟部中央標準局負工消費合作社印装 Γ、 申請專利範圍 2 /3 - 1 1 4 如 申 請 專 利範 圍 第 1 項 之 玻 璃 雄 維 組成 物 ,其 特 激 在 於 1 1 含 有 >λ 下 重最 百 分 率 的 成 分 : 1 Sio 2 47 至 57 1 I A1 0 2 2 1 少於 2 請 1 1 CaO + HgO 12 15 閲 諸 1 Na 0 + ] K 0 16 至 20 背 1 BO 2 3 10 16 之 1 P 0 2 S 0 至 2 注 意 1 I BaO 0 1 事 項 1 I 其它 0 2. 再 填 1 1 5 如 申 請 專 利範 圍 第 1 項 之 玻 璃 纖 維 組成 物 ,其 特 激 在 於 寫 本 頁 1 含 有 Μ 下 重量 百 分 率 的 成 分 • 1 Sio 52 ?? 60 1 I A1 0 2 3 0 5 1. 5 1 I Cao ·+ MgO 1.1 12.5 1 I Na 0 3 0 + K 0 2 15 10 至 18.5 14 訂 1 P 0 2 S 0 1 1 BaO 0 1 1 其它 0 至 2. I 6 如 請 專 利範 圍 第 1 至 5 項 中 任 一 項之 玻 璃纖 維 组 成 物 1 1 » 其 特 徴 在於 二 氧 化 矽 的 含 量 少 於 57重 量 百分 率 〇 i>、 1 7 .如 申 請 專 利範 圍 第 1 至 5 項 中 任 一 項之 玻 璃纖 維 組 成 物 1 1 t 其 特 徵 在於 二 氧 化 矽 的 含 夤 少 於 56.5 重 量百 分 率 〇 1 I 8 •如 申 請 專 利範 圍 第 1 至 5 項 中 任 一 項之 玻 璃纖 維 組 成 物 1 1 I » 其 特 徵 在於 氧 化 鋁 的 含 量 至 少 為 0 . 1重量百分率 > 1 1 9 ,如 申 請 專 利範 圍 第 1 至 5 項 中 任 — 項之 玻 璃纗 維 组 成 物 1 1 9 其 特 激 在於 氧 化 鋁 的 含 量 至 少 為 0 . 5重量百分率 > 1 1 10 1 1 1 1 本紙張尺度逋用中國國家標準(CNS ) A4規格(210X297公釐) 〇14h02 ?8 D8 六、申請專利範圍3/3 10. 如申請專利範圈第1至5項中任一項之玻璃谶維姐成物 ,其特徴在於五氧化二磷的含量至少為0.1重量百分率。 11. 如申請專利範画第1至5項中任一項之玻璃纖維組成物 ,其特激在於氧化砸的含量至多於12重量百分率。 12. 如申請專利範圔第1至5項中任一項之玻璃纗維姐成物 ,其特徵在於氧化鎂的含量少於2重量百分率。 經濟部中央標準局貝工消費合作社印製 I «-1— 1=— - —^1 1^1 I 1^— — - - I -1 I! . I— HH ^1» -¾ 、-t (請先閲讀背面之注意事項再填寫本頁) -11- 本紙張X·度適用中國國家標準(CNS ) A4規格(210X297公釐)