SU614043A1 - Glaze - Google Patents
GlazeInfo
- Publication number
- SU614043A1 SU614043A1 SU772439600A SU2439600A SU614043A1 SU 614043 A1 SU614043 A1 SU 614043A1 SU 772439600 A SU772439600 A SU 772439600A SU 2439600 A SU2439600 A SU 2439600A SU 614043 A1 SU614043 A1 SU 614043A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- glaze
- bao
- poured
- cao
- ratio
- Prior art date
Description
Изобретение относитс к составам глазурей, примен емых дл облицовочных и фасадных плиток и плиток дл полов из низкоспекающихс керамических масс. Известен состав стекловидного покрыти содержащего, вес.%: Si О 50-80 0,5-12; MgO 4-25; NajO 8-18 и, кроме того по крайней мере один окисел из группы: 6fO, ZfOf . z-S CrjOj.WO, MoO,,, CoO, NiO и из группы CaO, , BeO, BaO, 83.05 , Ti 0 , ff O , FejO. в количествах соответственно О, 1-3,0 и О, 1-10,0 .l . Наиболее близким к изобретению вл етс состав глазури, включающей, вес.%: 640 40-44; ,, 4-7; BjO 1015; CaO 4-7; 2.«О 7-10; 2-5; К2,О 0,5-2, 5; Z.i-Oj 8-14; 2-4; ВаО 5-7; и, кроме того, 1-3 2 . Недостатком указанных глазурей вл етс недостаточна заглушенность и повышенный блеск глазури. Цель изобретени - повьаиение заглу шенности и снижение блеска глазури. Поставленна цель достигаетс тем, чго rJia;iypb лп.полнительно содержит Р и -у. - соотношении к с; м VI о не;; , о и , Bt с . : Дл приготовлени глазури исходные сырьевые материалы отвешивали в заданных соотношени х, тщательно перемешивали полученную шихту и в количестве 300 г высыпали в шамотные тигли, предварительно нагретые до температуры 1000-1050с. Варку шихты осуществл ли в силитовой печи в окисл11тельной среде при 1300+20 0. Врем варки 1,52 час, выдержка при максимальной температуре 40-60 мин. После полного провара расплав фритты сливали в холодную воду, что обеспечивает хорошую гранул цию готовой фритты. Мокрый помол фритты производили совместно с Лружковскок ГЛИНОЙ ЛН-1 в соотношении 9Ь% и 4% в luapOBOvi мельнице. ВлажностьThe invention relates to compositions of glazes used for facing and facade tiles and floor tiles of low-caking ceramic masses. The known composition of the vitreous coating contains, wt%: Si O 50-80 0.5-12; MgO 4-25; NajO 8-18 and, in addition, at least one oxide from the group: 6fO, ZfOf. z-S CrjOj.WO, MoO ,,, CoO, NiO and from the group CaO,, BeO, BaO, 83.05, Ti 0, ff O, FejO. in amounts of O, 1-3.0 and O, respectively, 1-10.0 .l. Closest to the invention is the composition of the glaze, including, wt.%: 640 40-44; ,, 4-7; BjO 1015; CaO 4-7; 2. “About 7-10; 2-5; K2, O 0.5-2, 5; Z.i-Oj 8-14; 2-4; BAO 5-7; and besides, 1-3 2. The disadvantage of these glazes is insufficient obtrusiveness and increased gloss of the glaze. The purpose of the invention is to increase the roughness and reduce the glare of the glaze. The goal is achieved by the fact that rJia; iypb lp contains p and -y. - ratio to; m VI o not ;; oh and bt c. : To prepare the glaze, the raw materials were weighed out in predetermined ratios, the resulting mixture was thoroughly mixed and in an amount of 300 g was poured into chamotte crucibles, preheated to a temperature of 1000-1050s. The charge was cooked in a silicon silicate furnace in an oxidizing medium at 1300 + 20 0. The cooking time was 1.52 hours, the exposure at a maximum temperature of 40-60 minutes. After complete penetration, the frit melt was poured into cold water, which ensures good granulation of the finished frit. Wet grinding of frits was carried out jointly with Lruzhkovsk CLAY LN-1 in the ratio of 9% and 4% in a luapOBOvi mill. Humidity