RU2013127126A - Мультиполимерные композитные структуры и способы их получения - Google Patents

Мультиполимерные композитные структуры и способы их получения Download PDF

Info

Publication number
RU2013127126A
RU2013127126A RU2013127126/05A RU2013127126A RU2013127126A RU 2013127126 A RU2013127126 A RU 2013127126A RU 2013127126/05 A RU2013127126/05 A RU 2013127126/05A RU 2013127126 A RU2013127126 A RU 2013127126A RU 2013127126 A RU2013127126 A RU 2013127126A
Authority
RU
Russia
Prior art keywords
pore diameter
polymer
threshold
fibers
textile
Prior art date
Application number
RU2013127126/05A
Other languages
English (en)
Other versions
RU2628607C2 (ru
Inventor
Кристофер П. ХЕНРИ
Original Assignee
Дзе Боинг Компани
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Дзе Боинг Компани filed Critical Дзе Боинг Компани
Publication of RU2013127126A publication Critical patent/RU2013127126A/ru
Application granted granted Critical
Publication of RU2628607C2 publication Critical patent/RU2628607C2/ru

Abstract

1. Композитная структура (10), содержащая:текстильную конструкцию (12) по меньшей мере из одного текстильного слоя (22), состоящего из текстильных волокон (20) и имеющую распределение пор (30) в нем, где распределение пор (30) включает множество пор внутри волокон (30) в отдельных текстильных волокнах (20) и множество пор между волокнами (30) между текстильными волокнами (20);первый полимер (14), заполняющий поры внутри волокон (30) и также те поры между волокнами (30), которые имеют диаметр пор, равный или меньше порога диаметра пор; ивторой полимер (16), связанный с первым полимером (14) и практически заполняющий поры между волокнами (30), которые имеют диаметр пор больше порога диаметра пор.2. Композитная структура (10) по п.1, где первый полимер (14) является более жестким, чем второй полимер (16); и где первый полимер (14) имеет модуль упругости более 1 ГПа, и где второй полимер (16) имеет модуль упругости менее 1 ГПа.3. Композитная структура (10) по п.2, где первый полимер (14) включает термореактивный материал и где второй полимер (16) включает эластомер.4. Композитная структура (10) по п.2, где первый полимер (14) включает эпоксид и где второй полимер (16) включает силикон.5. Композитная структура (10) по п.1,где по меньшей мере один текстильный слой (22) включает одну или более насыщенных волокнами областей (36), в которых все поры между волокнами имеют диаметр пор, равный или меньше порога диаметра пор, и одну или более не насыщенных волокнами областей (38), в которых некоторые поры между волокнами имеют диаметр пор, равный или меньше порога диаметра пор, и некоторые имеют диаметр пор больше порога диаметра пор;где одна или более насыщенных волокнами областей (36) перемежают

Claims (16)

1. Композитная структура (10), содержащая:
текстильную конструкцию (12) по меньшей мере из одного текстильного слоя (22), состоящего из текстильных волокон (20) и имеющую распределение пор (30) в нем, где распределение пор (30) включает множество пор внутри волокон (30) в отдельных текстильных волокнах (20) и множество пор между волокнами (30) между текстильными волокнами (20);
первый полимер (14), заполняющий поры внутри волокон (30) и также те поры между волокнами (30), которые имеют диаметр пор, равный или меньше порога диаметра пор; и
второй полимер (16), связанный с первым полимером (14) и практически заполняющий поры между волокнами (30), которые имеют диаметр пор больше порога диаметра пор.
2. Композитная структура (10) по п.1, где первый полимер (14) является более жестким, чем второй полимер (16); и где первый полимер (14) имеет модуль упругости более 1 ГПа, и где второй полимер (16) имеет модуль упругости менее 1 ГПа.
3. Композитная структура (10) по п.2, где первый полимер (14) включает термореактивный материал и где второй полимер (16) включает эластомер.
4. Композитная структура (10) по п.2, где первый полимер (14) включает эпоксид и где второй полимер (16) включает силикон.
5. Композитная структура (10) по п.1,
где по меньшей мере один текстильный слой (22) включает одну или более насыщенных волокнами областей (36), в которых все поры между волокнами имеют диаметр пор, равный или меньше порога диаметра пор, и одну или более не насыщенных волокнами областей (38), в которых некоторые поры между волокнами имеют диаметр пор, равный или меньше порога диаметра пор, и некоторые имеют диаметр пор больше порога диаметра пор;
где одна или более насыщенных волокнами областей (36) перемежаются с одной или более не насыщенными волокнами областями (38); и где одна или более насыщенных волокнами областей (36) и одна или более не насыщенных волокнами областей (38) перемежаются по шаблону.
6. Композитная структура (10) по п.5,
где текстильная конструкция (12) содержит два или более сложенных текстильных слоев (22), каждый из которых включает одну или более насыщенных волокнами областей (36), перемежающихся с одной или более не насыщенными волокнами областями (38);
где по меньшей мере на одну насыщенную волокнами область (36) по меньшей мере одного текстильного слоя (22) наложена одна или более не насыщенных волокнами областей (38) по меньшей мере одного другого текстильного слоя (22), в направлении, в общем, перпендикулярном слоям; и где сложенные текстильные слои (22) по меньшей мере частично связаны друг с другом первым (14) и вторым (16) полимерами.
7. Композитная структура (10) по п.1, где отношение диаметра пор между волокнами, имеющими диаметр равный или меньше порога диаметра пор, к диаметру пор между волокнами, имеющими диаметр больше порога диаметра пор, составляет 1:10.
8. Композитная структура (10) по п.1, где порог диаметра пор составляет от 0,01 мм до 5,0 мм.
9. Композитная структура по п.8, где порог диаметра пор составляет 1,0 мм.
10. Композитная структура по п.8, где порог диаметра пор соответствует порогу смачивания текстильных волокон по меньшей мере одного текстильного слоя с первым полимером.
11. Способ получения композитной структуры (10); где способ включает:
селективное заполнение в текстильном слое (22), имеющем множество пор (30) в нем, только тех пор (30), которые имеют диаметр пор, равный и меньше порога диаметра пор, первым полимером (14); и
по существу, заполнение оставшихся пор (30) в текстильном слое (22) вторым полимером (16).
12. Способ по п.11, также включающий:
формирование текстильного слоя (22) из текстильных волокон (20) так, чтобы перемежать одну или более насыщенных волокнами областей (36), в которых все поры (30) имеют диаметр пор, равный или меньше порога диаметра пор, с одной или более не насыщенными волокнами областями (36), в которых некоторые поры (30) имеют диаметр пор, равный или меньше порога диаметра пор, и некоторые имеют диаметр пор больше порога диаметра пор.
13. Способ по п.11,
где по меньшей мере один текстильный слой (22) включает одну или более насыщенных волокнами областей (36), в которых все поры (30) имеют диаметр пор, равный или меньше порога диаметра пор, и одну или более не насыщенных волокнами областей (36), в которых некоторые поры (30) имеют диаметр пор, равный или меньше порога диаметра пор, и некоторые имеют диаметр пор больше порога диаметра пор;
где способ также включает складывание двух или более текстильных слоев (22) так, чтобы по меньшей мере на одну не насыщенную волокнами область (36) по меньшей мере одного текстильного слоя (22) накладывалась одна или более насыщенных волокнами областей (36) по меньшей мере одного другого текстильного слоя (22), в направлении, в основном, перпендикулярном слоям.
14. Способ по п.11,
где первый полимер (14) имеет определенный порог смачивания в отношении текстильных волокон (20) текстильного слоя (22), который ограничивает первый полимер (14) заполнением только тех пор (30), которые имеют диаметр пор, равный или меньше порога диаметра пор; и
где селективное заполнение включает не селективное нанесение первого полимера (14) на текстильный слой (22).
15. Способ по п.14, также включающий:
выбор первого полимера (14) на основе определенного порога смачивания по отношению к текстильным волокнам (20) текстильного слоя (22).
16. Способ по любому из пп.11-15, также включающий:
получение первого полимера (14) для связывания со вторым полимером (16) посредством обработки первого полимера (14) агентом, улучшающим совместимость.
RU2013127126A 2012-06-15 2013-06-14 Мультиполимерные композитные структуры и способы их получения RU2628607C2 (ru)