MX2020012957A - Lamina de acero chapada con aleacion de al-fe para formacion en caliente, que tiene excelentes caracteristicas de soldadura twb, miembro de formacion en caliente, y metodos de fabricacion para los mismos. - Google Patents

Lamina de acero chapada con aleacion de al-fe para formacion en caliente, que tiene excelentes caracteristicas de soldadura twb, miembro de formacion en caliente, y metodos de fabricacion para los mismos.

Info

Publication number
MX2020012957A
MX2020012957A MX2020012957A MX2020012957A MX2020012957A MX 2020012957 A MX2020012957 A MX 2020012957A MX 2020012957 A MX2020012957 A MX 2020012957A MX 2020012957 A MX2020012957 A MX 2020012957A MX 2020012957 A MX2020012957 A MX 2020012957A
Authority
MX
Mexico
Prior art keywords
hot forming
steel sheet
plated steel
manufacturing methods
methods therefor
Prior art date
Application number
MX2020012957A
Other languages
English (en)
Inventor
Yeol - Rae CHO
Jin - Keun Oh
Seong - Woo Kim
Hyeon - Jeong Shin
Original Assignee
Posco
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Posco filed Critical Posco
Publication of MX2020012957A publication Critical patent/MX2020012957A/es

Abstract

Un aspecto preferido de la presente invención proporciona: una lámina de acero chapada con aleación de Al-Fe para formación en caliente, que tiene excelentes características de soldadura TWB puesto que la uniformidad de dureza excelente de una zona de soldadura TWB después de la formación en caliente se obtiene al controlar adecuadamente una condición de recocido por lotes, después del chapado con Al, tal que se forma una capa de aleación de Al-Fe; un miembro de formación en caliente; y métodos de fabricación para los mismos.
MX2020012957A 2018-05-31 2018-05-31 Lamina de acero chapada con aleacion de al-fe para formacion en caliente, que tiene excelentes caracteristicas de soldadura twb, miembro de formacion en caliente, y metodos de fabricacion para los mismos. MX2020012957A (es)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/KR2018/006244 WO2019231023A1 (ko) 2018-05-31 2018-05-31 Twb 용접 특성이 우수한 열간성형용 al-fe 합금화 도금강판, 열간성형 부재 및 그들의 제조방법

Publications (1)

Publication Number Publication Date
MX2020012957A true MX2020012957A (es) 2021-02-16

Family

ID=68697611

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2020012957A MX2020012957A (es) 2018-05-31 2018-05-31 Lamina de acero chapada con aleacion de al-fe para formacion en caliente, que tiene excelentes caracteristicas de soldadura twb, miembro de formacion en caliente, y metodos de fabricacion para los mismos.

Country Status (6)

Country Link
US (2) US11939651B2 (es)
EP (1) EP3805421A4 (es)
JP (2) JP7261822B2 (es)
CN (1) CN112218969A (es)
MX (1) MX2020012957A (es)
WO (1) WO2019231023A1 (es)

Families Citing this family (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP7167343B2 (ja) * 2018-11-30 2022-11-08 ポスコ 水素遅延破壊特性及びスポット溶接性に優れた熱間プレス用アルミニウム系めっき鋼板及びその製造方法
CN112455024B (zh) * 2021-02-03 2021-04-27 育材堂（苏州）材料科技有限公司 激光拼焊预镀层钢板及其热冲压成形构件
KR20230021319A (ko) 2021-08-05 2023-02-14 주식회사 포스코 테일러 웰디드 블랭크, 열간성형부재 및 이들의 제조방법
CN115725906B (zh) * 2021-08-30 2024-02-13 宝山钢铁股份有限公司 一种用于高压直流继电器的镀覆锌铝镁的免磁化退火电磁纯铁钢板及其制造方法
TWI788080B (zh) * 2021-11-01 2022-12-21 中國鋼鐵股份有限公司 熱成形硬化鋁基鍍覆鋼板及其製造方法
JP7425391B1 (ja) 2022-05-19 2024-01-31 日本製鉄株式会社 ホットスタンプ用重ね合わせブランク、及び、重ね合わせホットスタンプ成形体
DE102022123742A1 (de) * 2022-09-16 2024-03-21 Thyssenkrupp Steel Europe Ag Halbzeug für die Warmumformung

Family Cites Families (26)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5721931Y2 (es) 1977-10-14 1982-05-12
JP3405379B2 (ja) * 1996-01-25 2003-05-12 日新製鋼株式会社 Ｆｅ−Ａｌ−Ｓｉ合金層を形成した熱器具用鋼材およびその製造方法
FR2780984B1 (fr) 1998-07-09 2001-06-22 Lorraine Laminage Tole d'acier laminee a chaud et a froid revetue et comportant une tres haute resistance apres traitement thermique
CN100370054C (zh) * 2001-06-15 2008-02-20 新日本制铁株式会社 镀有铝合金体系的高强度钢板以及具有优异的耐热性和喷漆后耐腐蚀性的高强度汽车零件
JP4446428B2 (ja) 2003-02-17 2010-04-07 新日本製鐵株式会社 塗装後耐食性に優れた高強度自動車部品
JP4990500B2 (ja) 2005-02-14 2012-08-01 新日本製鐵株式会社 部材内硬さの均一性に優れた高強度自動車用部材およびその製造方法
WO2007118939A1 (fr) 2006-04-19 2007-10-25 Arcelor France Procede de fabrication d'une piece soudee a tres hautes caracteristiques mecaniques a partir d'une tole laminee et revetue
JP4860537B2 (ja) 2007-04-10 2012-01-25 新日本製鐵株式会社 接合部の耐食性に優れた自動車用部材
JP5463906B2 (ja) 2009-12-28 2014-04-09 新日鐵住金株式会社 ホットスタンプ用鋼板及びその製造方法
BR112013009515B1 (pt) * 2010-10-22 2018-08-07 Nippon Steel & Sumitomo Metal Corporation Método de fabricação de corpo estampado a quente que tem uma parede vertical e corpo estampado a quente que tem uma parede vertical
KR101304621B1 (ko) * 2011-06-28 2013-09-05 주식회사 포스코 영역별로 상이한 강도를 갖는 프레스 성형품의 제조방법
KR101277858B1 (ko) * 2011-09-28 2013-06-21 현대제철 주식회사 테일러 웰디드 블랭크 제조방법 및 이를 위한 용접 이음부 재도금 장치
US9540720B2 (en) 2011-09-30 2017-01-10 Nippon Steel & Sumitomo Metal Corporation High-strength hot-dip galvanized steel sheet and high-strength alloyed hot-dip galvanized steel sheet having excellent formability and small material anisotropy with ultimate tensile strength of 980 MPa or more
CA2850195C (en) 2011-09-30 2016-10-25 Nippon Steel & Sumitomo Metal Corporation High-strength hot-dip galvanized steel sheet excellent in impact resistance property and manufacturing method thereof, and high-strength alloyed hot-dip galvanized steel sheet and manufacturing method thereof
KR101601001B1 (ko) * 2011-09-30 2016-03-08 신닛테츠스미킨 카부시키카이샤 고강도 용융 아연 도금 강판
NO2839049T3 (es) 2012-04-17 2018-03-17
KR20150075277A (ko) 2013-12-25 2015-07-03 주식회사 포스코 용융 도금재 테일러드 블랭크를 이용한 차등 강도 핫 프레스 포밍 부품 제조 방법 및 그 부품
KR101614603B1 (ko) * 2014-07-10 2016-04-22 주식회사 포스코 테일러 웰디드 블랭크 용접된 Al-Si 도금 강판의 열간 프레스 성형 방법
KR101714121B1 (ko) 2014-11-21 2017-03-09 현대자동차주식회사 테일러 웰디드 블랭크 제조방법
KR101696121B1 (ko) 2015-12-23 2017-01-13 주식회사 포스코 내수소지연파괴특성, 내박리성 및 용접성이 우수한 열간성형용 알루미늄-철 합금 도금강판 및 이를 이용한 열간성형 부재
KR101746996B1 (ko) 2015-12-24 2017-06-28 주식회사 포스코 도금 밀착성이 우수한 고망간 용융 알루미늄계 도금강판
KR101879104B1 (ko) * 2016-12-23 2018-07-16 주식회사 포스코 TWB 용접 특성이 우수한 열간성형용 Al-Fe 합금화 도금강판, 열간성형 부재 및 그들의 제조방법
KR101858868B1 (ko) 2016-12-23 2018-05-16 주식회사 포스코 충격특성이 우수한 열간성형용 도금강판, 열간성형 부재 및 그들의 제조방법
CA3050646A1 (en) * 2017-02-02 2018-08-09 Nippon Steel Corporation Alloyed al plated steel sheet for hot stamping and hot stamped steel member
JP6836600B2 (ja) * 2017-06-02 2021-03-03 日本製鉄株式会社 ホットスタンプ部材
DE102017211076B4 (de) 2017-06-29 2019-03-14 Thyssenkrupp Ag Verfahren zum Herstellen eines mit einem Überzug versehenen Stahlbauteils und Stahlbauteil

Also Published As

Publication number Publication date
JP2023093564A (ja) 2023-07-04
EP3805421A1 (en) 2021-04-14
WO2019231023A1 (ko) 2019-12-05
US20240191329A1 (en) 2024-06-13
EP3805421A4 (en) 2021-04-28
JP2021524885A (ja) 2021-09-16
CN112218969A (zh) 2021-01-12
US20210222276A1 (en) 2021-07-22
US11939651B2 (en) 2024-03-26
JP7261822B2 (ja) 2023-04-20

Similar Documents

Publication Publication Date Title
MX2020012957A (es) Lamina de acero chapada con aleacion de al-fe para formacion en caliente, que tiene excelentes caracteristicas de soldadura twb, miembro de formacion en caliente, y metodos de fabricacion para los mismos.
MX2016010703A (es) Metodo para soldar por laser una o mas piezas de trabajo hechas de acero endurecible en una union a tope.
MX2019013153A (es) Un metodo para la fabricacion de lamina de acero galvanorrecocido resistente a la fragilizacion por metal liquido.
MX2016000266A (es) Lamina de acero chapado de alta resistencia que tiene propiedades superiores de chapado, capacidad de manipulacion, y resistencia a la fractura retardada, y metodo de produccion la misma.
MX2016013666A (es) Metodo para fabricar una parte de formacion por prensado en caliente y una parte de formacion por prensado en caliente.
MX2017009018A (es) Lámina de acero chapado de alta resistencia que tiene excelentes propiedades de chapado, trabajabilidad y mayor resistencia a las fracturas, y método para su producción.
MX2017009016A (es) Lámina de acero chapado de alta resistencia que tiene excelentes propiedades de chapado, trabajabilidad y mayor resistencia a las fracturas, y método para su producción.
MX2020006445A (es) Lamina de acero de alta resistencia que tiene excelentes propiedades de impacto y formabilidad y metodo para manufacturarla.
MA45115B1 (fr) Procédé de fabrication d'une tôle d'acier twip à microstructure austénitique
MX2018011688A (es) Lamina de acero y lamina de acero enchapada, metodo para producir lamina de acero laminada en caliente, metodo para producir lamina de acero de dureza completa laminada en frio, metodo para producir lamina termicamente tratada, metodo para producir lamina de acero, y metodo para producir lamina de acero enchapada.
TR201820853T4 (tr) Alümine edilmiş bir ambalaj çeliğinin üretilmesi için yöntem.
MX2020013458A (es) Lamina de acero, pieza en bruto a medida, producto estampado en caliente, tubo de acero, producto hueco estampado en caliente y metodo de fabricacion de la lamina de acero.
EP3889293A4 (en) SHEET STEEL WITH EXCELLENT TENACITY OF AREA AFFECTED BY HEAT AND ITS MANUFACTURING PROCESS
WO2016067636A8 (ja) 方向性電磁鋼板の製造方法
MA51268B1 (fr) Substrat en d'acier revêtu par immersion à chaud
MX2018014323A (es) Metodo para la fabricacion de una lamina de acero twip que tiene una matriz austenitica.
MX2019007638A (es) Miembro soldado para placa de acero enchapada excelente en resistencia a la porosidad en la zona soldada y propiedades de fatiga y método para fabricar la misma.
MA54420B1 (fr) Tôle d'acier revêtue par dépôt en bain fondu, son procédé de fabrication et son utilisation
MX2022004926A (es) Lamina de acero, elemento y metodos para producir el mismo.
MX2021006199A (es) Lamina de acero chapada en base de hierro-aluminio para formacion en prensa caliente, que tiene excelentes propiedades de fractura retardada de hidrogeno y propiedades de soldabilidad por puntos y metodo de manufactura de la misma.
MX2018014327A (es) Lamina de acero twip que tiene una matriz austenitica.
EP3889313A4 (en) ALUMINUM BASED STEEL PLATE FOR HOT PRESSING WITH EXCELLENT RESISTANCE TO HYDROGEN INDUCED BREAKAGE AND POINT WELDABILITY AND METHOD OF MANUFACTURING IT
MX2018005716A (es) Metodo para fabricar un componente de acero austenitico y uso del componente.
PL3615261T3 (pl) Metalowy przedmiot obrabiany ze znacznikami odpornymi na śrutowanie, sposób znakowania laserowego takich znaczników na metalowym przedmiocie obrabianym
EP4261316A4 (en) HIGH-STRENGTH HOT-GALVANIZED STEEL SHEET HAVING EXCELLENT PLATING QUALITY, STEEL SHEET FOR PLATING AND METHODS OF MANUFACTURING THE SAME