KR880000615A - 조절된 기계적 성질과 조절된 절삭성을 갖는 냉간 인발 쾌삭 재황화 및 재인화 강봉 - Google Patents
조절된 기계적 성질과 조절된 절삭성을 갖는 냉간 인발 쾌삭 재황화 및 재인화 강봉 Download PDFInfo
- Publication number
- KR880000615A KR880000615A KR870005837A KR870005837A KR880000615A KR 880000615 A KR880000615 A KR 880000615A KR 870005837 A KR870005837 A KR 870005837A KR 870005837 A KR870005837 A KR 870005837A KR 880000615 A KR880000615 A KR 880000615A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- cold drawn
- less
- amount
- steel bar
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (15)
- 하기와 같은 조성을 갖는 냉간 인발 재황화 및 재인화 쾌삭 강봉 :C 0.08중량% 이하Mn 0.6중량% 내지 1.4중량%Si 0.1중량% 이하P 최소한 0.03중량%S 0.25중량% 내지 0.50중량%Cb 0.01중량% 내지 0.10중량%V 0.1중량% 이하Ni, Cr, Mo 및 Cu의 총량 0.15중량% 이하, 잔여량 만큼의 철 ;중량% Mn/중량% S의 비율은 1.6 내지 4.0, (중량% Mn-1.62×중량% S)/중량% Cb의 비율은 2 내지 50.
- 제1항에 있어서, 0.03중량% 내지 0.35중량%의 양으로 Pb를 함유하는 냉간 인발 강봉.
- 제1항에 있어서, 0.005중량% 내지 0.05중량%의 양으로 Zr을 함유하는 냉간 인발 강봉.
- 제1항에 있어서, 0.05중량% 내지 0.25중량%의 양으로 Bi를 함유하는 냉간 인발 강봉.
- 제1항에 있어서, 0.03중량% 내지 0.15중량%의 양으로 Pb를, 그리고 0.05중량% 내지 0.15중량%의 양으로 Bi를 함유하는 냉간 인발 강봉.
- 제1항에 있어서, 0.006중량% 내지 0.012중량%의 양으로 N을 함유하는 냉간 인발 강봉.
- 제1항에 있어서, 0.05중량% 내지 0.25중량%의 양으로 Bi를, 그리고 0.005중량% 내지 0.05중량%의 양으로 Te를 함유하는 냉간 인발 강봉.
- 제1항에 있어서, Cb의 양이 0.01중량% 내지 0.04중량%이고 봉이 대략 60ksi의 항복 강도를 갖는 것을 특징으로 하는 냉간 인발 강봉.
- 제1항에 있어서, Cb의 양이 0.02중량% 내지 0.06중량%이고 봉이 대략 65ksi의 항복 강도를 갖는 것을 특징으로 하는 냉간 인발 강봉.
- 제1항에 있어서, Cb의 양이 0.02중량% 내지 0.07중량%이고 봉이 대략 70ksi의 항복 강도를 갖는 것을 특징으로 하는 냉간 인발 강봉.
- 제1항에 있어서, Cb의 양이 0.06중량% 내지 0.1중량%이고 봉이 대략 80ksi의 항복 강도를 갖는 것을 특징으로 하는 냉간 인발 강봉.
- 아래와 같은 조성을 갖는 열간 압연 강철 코일로부터 성형된 냉간 인발 재인화 및 재황화 쾌삭강봉 :C 0.06중량% 이하Mn 0.6중량% 내지 1.15중량%Si 0.1중량% 이하P 0.03중량% 내지 0.06중량%S 0.25중량% 내지 0.40중량%Cb 0.01중량% 내지 0.07중량%Ni, Cr, Mo 및 Cu의 총량 0.15중량% 이하, 잔여량 만큼의 철 ;중량% Mn/중량% S의 비율은 2.0 내지 3.5, (중량% Mn-1.62×중량% S)/중량% Cu의 비율은 2 내지 50, 중량% S=(0.0042-0.0054)×원하는 항복강도(ksi).
- 제1항에 있어서, 냉각 인발시의 면적 감소가 항복강도 60 내지 80ksi를 갖는 열간 압연봉의 15% 내지 30%인 것을 특징으로 하는 냉각 인발 강봉.
- 단면적이 5.08cm(2in) 이하인 봉을 열간 압연시킴으로써 성형된, 다음과 같은 조성을 갖는 냉간 인발 재인화 및 재황화 쾌삭 강봉 :C 0.08중량% 이하Mn 0.7중량% 내지 1.30중량%Si 0.1중량% 이하P 0.03중량% 내지 0.09중량%S 0.28중량% 내지 0.50중량%Cb 0.02중량% 내지 0.08중량%V 0.1중량% 이하Ni, Cr Mo 및 Cu의 총량 0.15중량% 이하, 잔여량 만큼의 철 ;중량% Mn/중량% S의 비율은 2.0 내지 3.2, (중량% Mn-1.62×중량% S)/중량% Cb의 비율은 4 내지 51, 중량% S=(0.0045-0.0058)×원하는 항복강도(ksi).
- 단면적이 최소한 5.08cm(2in)인 열간 압연 봉으로 성형된 다음과 같은 조성을 갖는 냉간 인발 재인화 및 재황화 쾌삭 강봉 :C 0.08중량% 이하Mn 0.8중량% 내지 1.4중량%Si 0.1중량% 이하P 0.03중량% 내지 0.9중량%S 0.30중량% 내지 0.50중량%Cb 0.02중량% 내지 0.10중량%V 0.1중량% 이하Nr, Cr, Mo 및 Cu의 총량 0.15중량% 이하, 잔여량 만큼의 철 ;중량% Mn/중량% S의 비율은 2.0 내지 3.5, (중량% Mn-1.62×중량% S)/중량% Cb의 비율은 5 내지 25, 중량% S=(0.0045-0.0063)×원하는 강항복도(ksi).※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.