KR870006106A - 친수성 폴리우레탄/폴리우레아 스폰지의 제조방법 - Google Patents

친수성 폴리우레탄/폴리우레아 스폰지의 제조방법 Download PDF

Info

Publication number
KR870006106A
KR870006106A KR860010518A KR860010518A KR870006106A KR 870006106 A KR870006106 A KR 870006106A KR 860010518 A KR860010518 A KR 860010518A KR 860010518 A KR860010518 A KR 860010518A KR 870006106 A KR870006106 A KR 870006106A
Authority
KR
South Korea
Prior art keywords
group
carbon atoms
sponge
linear
groups
Prior art date
Application number
KR860010518A
Other languages
English (en)
Other versions
KR910004899B1 (ko
Inventor
키쓰 라슨 웨인
토마스 헤드릭 스티븐
Original Assignee
도날드 밀러 셀
미네소타 마이닝 앤드 매뉴팩츄어링 컴패니
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US06/806,758 external-priority patent/US4638017A/en
Application filed by 도날드 밀러 셀, 미네소타 마이닝 앤드 매뉴팩츄어링 컴패니 filed Critical 도날드 밀러 셀
Publication of KR870006106A publication Critical patent/KR870006106A/ko
Application granted granted Critical
Publication of KR910004899B1 publication Critical patent/KR910004899B1/ko

Abstract

내용 없음

Description

친수성 폴리우레탄/폴리우레아 스폰지의 제조방법
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음

Claims (16)

  1. 폴리우레아와 폴리우레탄을 함유하는 최소한 하나의 설폰기와 20,000 분자량 단위에 해당되는 최소한 하나의 설포네이트를 함유하는 중합체로 구성된 물-흡착성 스폰지.
  2. 제1항에 있어서, 하기식의 다수의 단위로 구성된 스폰지.
    상기식에서
    R은 2,3 또는 3가의 갖는 유기기로서 2-12 탄소원자의 선형 또는 측쇄 지방족기, 또는 5-50 탄소원자를 함유하는 5-내지 6-원의 지방족과 방향족 카르보시 클릭기;
    R1은 독립적으로 (b+1)의 원자가를 갖는 직쇄 또는 측쇄 지방족기인데 n이 2-12인 CnH2n과 CnH2n-2의 선형기, 5- 또는 6-원의 카르보시클릭기, 각각의 산소원자에 의해 분리된 5-20 탄소원자의 방향족기, 분자량 2000까지의 지방족기에서 선택된 단위의 110 탄소원자의 사슬로 구성되었으며 b는 1,2 또는 3;
    R2는 (d+2)의 원자를 가지며 6-20 탄소원자의 아텐폴리일기 (다가아렌기) 또는 2-20 탄소원자의 알칸 폴리일 (다가의 알칸)인데 d는 1,2 또는 3;
    X는 독립적으로 -O- 또는 -NH-
    M은 양이온
  3. 제2항에 있어서, 다음의 기에서 선택된 다수의 단위로 구성된 스폰지.
    상기식에서, R3은 2-50 탄소원자의 선형 또는 측쇄 지방족 또는 c가 2-5인, c의 원자가를 갖는 5-50 탄소원자의 방향족기, 1-20의 비과산화성 산소원자,를 함유하는 기, 또는 R3은 5- 또는 6-원의 시클로지방족기 또는 5-20 탄소원자의 방향족기.
  4. a) 1) 지방족, 시클로지방족 또는 방향족기와 2) 지방족, 시클로지방족 또는 방향족에 스테르기와 이소시아네이트로 앤드 캐핑된 1-3 펜던트기를 함유하는 중심 아렌폴리일 또는 알칸폴리일기로 구성된 군에서 선택된 선형 또는 측쇄 유기기의 백본으로 구성된 이소시아네이트-종단된 설포 폴리우레타/우레아와 b) 다음 중 최소한 하나의 1) 물, 2) 폴리올과 블로잉제 3) 폴리아민과 블로잉제의 반응 생성물로 구성된 스폰지.
  5. 제4항에 있어서, 이소시아네이트-종단된 설포폴리우레탄/우레아가 하기식(Ⅴ)와 하기식(Ⅳ)와 (Ⅴa')를 구성하는 스폰지.
    상기식에서
    R은 선형 또는 측쇄인 2-12탄소원자, 5-50 탄소원자를 갖는 5-와 6-원자의카르보시클릭기로부터 선택된 (a+1)가의 유기기;
    a는 1,2 또는 3;
    R1은 선형 CnH2n과 CnH2n-2(n은 2-12)에서 선택된 110 탄소원자의 포화된 또는 비포화된 사슬, 5-20 탄소원자의 방향족, 각각의 산소원자,로 인하여 분리된 5- 또는 6-원의 카르보시클릭기, 2000까지의 분자량을 갖는 유기기로 구성된 (b+1)가의 선형 또는 측쇄 유기기로부터 독립적으로 선택되며 b는 1,2 또는 3의 정수;
    R2는 d+2가이며 6-20 탄소원자의 아렌 폴리인기(다가아렌기) 또는 2-20 탄소원자의 알칸 폴리일기(다가알칸)이며 d는 1,2 또는 3의 수;
    X는 독립적으로 -O- 또는 -NH-
    M은 양이온
  6. a) 최소한 하나의 하기식(V)의 이소시아네이트-종단된 설포폴리우레탄/우레아,
    b) 식(OCNR(NCO)a)의 폴리이소시아네이트와
    c) 하기식(Va)'의 이소시아네이트-종단된 폴리우레탄/우레아,
    d) (1) 물과 (2) 폴리올 또는 폴리아민과 블로잉제로 구성된 군에서 선택된 화합물의 반응 생성물로 구성된 스폰지.
    상기식에서
    R은 선형 또는 측쇄인 2-12 탄소원자, 5-50 탄소원자를 I 갖는 5-와 6-원자의 카르보시클릭기로부터 선택된 (a+1)가의 유기기 ;
    a는 1, 2 또는 3 ;
    R1은 선형 CnH2n과 CnH2n-2(n은 2-12)에서 선택된 110탄소원자의 포화된 또는 비포화된 사슬, 5-20 탄소원자의 방향족, 각각의 산소원자,로 인하여 분리된 5- 또는 6-원자의 카르보시클릭기, 2000까지의 분자량을 갖는 유기기로 구성된 (b+1)가의 선형 또는 측쇄 유기기로부터 독립적으로 선택되며 b는 1, 2 또는 3의 정수 ;
    R2은 d+2가이며 6-20 탄소원자의 아렌 폴리일기(다가 아렌기)또는 2-20 탄소원자의 알칸폴리일기(다가알칸)이며 d는 1, 2 또는 3의 수 ;
  7. 제1항에 있어서, 1g의 건조스폰지의 흡수용량이 물 10∼50g인 스폰지.
  8. 제1항에 있어서, 물 흡수율이 0.001∼0.4g/cm2/5초인 스폰지.
  9. 제1항에 있어서, 밀도가 0.01-0.4g/cm2인 스폰지.
  10. 제1항에 있어서, 수중에서의 퍼센트 부피팽창이 25∼50%인 스폰지.
  11. 제1항에 있어서, 수중에서의 퍼센트 부피팽창이 30% 이하인 스폰지.
  12. 제2항에 있어서, M이 H, 알칼리 또는 알칼리 토금속 양이온 또는 1차, 2차, 3차 또는 4차 암모늄 양이온인 스폰지.
  13. 제1항에 있어서, 섬유, 충진제, 향료, 의약품, 살충제, 살진균제, 살균제, 보습제 염료 또는 안료로부터 선택된 보조제로 구성된 스폰지.
  14. 제1항에 있어서, 중합체가 3,000-10,000 분자량 단위에 대하여 하나의 설포네이트 등가량을 함유하는 스폰지.
  15. a) 하기식(Ⅴ)와 하기식(Ⅳ) 또는 (Ⅴa)'중 최소한 하나로 구성된 이소시아네이트-종단된 설포폴리우레탄/우레아를 산출한 뒤
    b) 상기 설폰 폴리우레탄/우레아를
    (a) 물,
    (b) 폴리올 또는 폴리아민 중 최소한 하나와 블로잉제 중 최소한 하나와 반응시키고
    c) 생성된 스폰지를 분리하는 것으로 구성된 스폰지의 제조방법.
    상기식에서
    R은 선형 또는 측쇄인 2-12탄소원자, 5-50 탄소원자를 갖는 5-와 6-원자의카르보시클릭기로부터 선택된 (a+1)가의 유기기;
    a는 1,2 또는 3;
    R1은 선형 CnH2n과 CnH2n-2(n은 2-12)에서 선택된 110 탄소원자의 포화된 또는 비포화된 사슬, 5-20 탄소원자의 방향족, 각각의 산소원자, -OC-와 -NHC-로 인하여 분리된 5- 또는 6-원의 카르보시클릭기, 2000까지의 분자량을 갖는 유기기로 구성된 (b+1)가의 선형 또는 측쇄 유기기로부터 독립적으로 선택되며 b는 1,2 또는 3의 정수;
    R2는 d+2가이며 6-20탄소원자의 아렌 폴리인기(다가아렌기) 또는 2-20 탄소원자의 알칸 폴리일기(다가알칸)이며 d는 1,2 또는 3의 수;
  16. 제15항에 있어서, 폴리올 또는 폴리아민이 하기식들인 스폰지의 제조방법.
    R3(OH)c
    R3(OH2)c
    상기식에서, R3은 2-50 탄소원자의 선형 또는 측쇄의 지방족기로서 c는 2-5의 값을 갖는 원자가, R3은 1-20의 비관산화성 산소원자기를 함유할 수 있거나, R3은 5- 또는 6- 원자의 시클로 지방족기 또는 5-20 탄소원자의 방향족기.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019860010518A 1985-12-09 1986-12-08 친수성 폴리우레탄/폴리우레아 스폰지의 제조방법 KR910004899B1 (ko)