KR20120093487A - Anode having multi-layer structure for secondary battery and lithium secondary battery including the same - Google Patents

Anode having multi-layer structure for secondary battery and lithium secondary battery including the same Download PDF

Info

Publication number
KR20120093487A
KR20120093487A KR1020110013075A KR20110013075A KR20120093487A KR 20120093487 A KR20120093487 A KR 20120093487A KR 1020110013075 A KR1020110013075 A KR 1020110013075A KR 20110013075 A KR20110013075 A KR 20110013075A KR 20120093487 A KR20120093487 A KR 20120093487A
Authority
KR
South Korea
Prior art keywords
negative electrode
active material
electrode active
secondary battery
carbon
Prior art date
Application number
KR1020110013075A
Other languages
Korean (ko)
Other versions
KR101440347B1 (en
Inventor
장성균
김성진
양인석
Original Assignee
주식회사 엘지화학
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 엘지화학 filed Critical 주식회사 엘지화학
Priority to KR1020110013075A priority Critical patent/KR101440347B1/en
Publication of KR20120093487A publication Critical patent/KR20120093487A/en
Application granted granted Critical
Publication of KR101440347B1 publication Critical patent/KR101440347B1/en

Abstract

PURPOSE: A negative electrode of a multi-layered structure for a secondary battery is provided to improve wettability, to have excellent safety and stability, while having high energy density and high output performance. CONSTITUTION: A negative electrode of a multi-layered structure for a secondary battery comprises a first negative electrode mixture layer comprising a first negative electrode active material spread in state contacted to a surface of a current collector, and a second negative electrode mixture layer comprising a second negative electrode material spread on the first negative electrode active material, having relatively higher charging/discharging voltage and relatively higher hydrophilicity than the first negative electrode active material. Hydrophobicity of the negative electrode active material to electrolyte is 20-300% higher than the first negative electrode active material.

Description

다층 구조의 이차전지용 음극 및 이를 포함하는 리튬 이차전지 {Anode Having Multi-Layer Structure for Secondary Battery and Lithium Secondary Battery Including The Same}Anode Having Multi-Layer Structure for Secondary Battery and Lithium Secondary Battery Including The Same}

본 발명은 다층 구조의 이차전지용 음극 및 이를 포함하는 리튬 이차전지에 관한 것으로, 더욱 상세하게는, 집전체의 표면에 접촉된 상태로 도포되어 있는 제 1 음극 활물질을 포함하는 제 1 음극합제 층 및 상기 제 1 음극합체 층 상에 도포되어 있고, 상기 제 1 음극 활물질보다 상대적으로 높은 충방전 전위와 상대적으로 큰 친수성을 가진제 2 음극활물질을 포함하는 제 2 음극합제 층을 포함하는 다층 구조로 이루어진 것을 특징으로 하는 이차전지용 음극 및 이를 포함하는 리튬 이차전지에 관한 것이다. The present invention relates to a negative electrode for a secondary battery having a multilayer structure and a lithium secondary battery including the same, and more particularly, a first negative electrode mixture layer comprising a first negative electrode active material applied in contact with a surface of a current collector; A multi-layer structure comprising a second negative electrode mixture layer coated on the first negative electrode mixture layer and including a second negative electrode active material having a relatively higher charge / discharge potential and a relatively higher hydrophilicity than the first negative electrode active material. It relates to a secondary battery negative electrode and a lithium secondary battery comprising the same.

화석연료의 고갈에 의한 에너지원의 가격 상승, 환경 오염의 관심이 증폭되며, 친환경 대체 에너지원에 대한 요구가 미래생활을 위한 필수 불가결한 요인이 되고 있다. 이에 원자력, 태양광, 풍력, 조력 등 다양한 전력 생산기술들에 대한 연구가 지속되고 있으며, 이렇게 생산된 에너지를 더욱 효율적으로 사 용하기 위한 전력저장장치 또한 지대한 관심이 이어지고 있다.Increasing the price of energy sources due to the depletion of fossil fuels, interest in environmental pollution is increasing, and the demand for environmentally friendly alternative energy sources is becoming an indispensable factor for future life. Accordingly, researches on various power production technologies such as nuclear power, solar energy, wind power, tidal power, etc. continue, and power storage devices for more efficient use of the generated energy are also drawing attention.

특히, 리튬 이차전지의 경우, 모바일 기기에 대한 기술 개발과 수요가 증가함에 따라 에너지원으로서의 수요가 급격히 증가하고 있고, 최근에는 전기자동차(EV), 하이브리드 전기자동차(HEV)의 동력원으로서의 사용이 실현화되고 있으며, 그리드(Grid)화를 통한 전력 보조전원 등의 용도로도 사용영역이 확대되고 있다.In particular, in the case of lithium secondary batteries, as the development and demand for mobile devices increases, the demand for energy sources is rapidly increasing, and in recent years, the use of electric vehicles (EVs) and hybrid electric vehicles (HEVs) as power sources has been realized. In addition, the use area is also being expanded for grid auxiliary.

전기자동차(EV), 하이브리드 전기자동차(HEV)의 동력원으로 사용되는 리튬 이차전지는 높은 에너지 밀도와 단시간에 큰 출력을 발휘할 수 있는 특성과 더불어, 대전류에 의한 충방전이 단시간에 반복되는 가혹한 조건 하에서 10년 이상 사용될 수 있어야 하므로, 기존의 소형 리튬 이차전지보다 월등히 우수한 안전성 및 장기 수명 특성이 필연적으로 요구된다.Lithium secondary batteries used as power sources for electric vehicles (EVs) and hybrid electric vehicles (HEVs) have high energy density and high power output in a short time, and under severe conditions where charging and discharging by a large current is repeated in a short time. Since it should be able to be used for more than 10 years, it is inevitably required to have superior safety and long life characteristics than conventional small lithium secondary batteries.

또한, 대용량 전력 저장장치로 사용되는 리튬 이차전지는 높은 에너지 밀도와 효율을 갖고 수명이 길어야 함은 물론, 고성능화 및 대용량화에 따른 시스템의 오 작동 시 발화나 폭발사고는 대형사고로 연계되므로 안전성과 신뢰성을 확보하는 것이 특히 중요한 과제이다. In addition, a lithium secondary battery used as a large-capacity power storage device has to have a high energy density and efficiency and a long lifespan, as well as safety and reliability because fire or explosion accidents are linked to large accidents when a system malfunctions due to high performance and high capacity. Ensuring that is especially important.

이와 관련하여, 종래의 리튬 이차전지의 음극은 음극 활물질로 구조적, 전기적 성질을 유지하면서 가역적인 리튬이온의 삽입(intercalation) 및 탈리가 가능한 탄소계 화합물이 주로 사용되었다.In this regard, a negative electrode of a conventional lithium secondary battery is a carbon-based compound capable of intercalation and detachment of reversible lithium ions while maintaining structural and electrical properties as a negative electrode active material.

구체적으로, 상기 탄소계 화합물은 표준 수소 전극 전위에 대해 약 -3V의 매우 낮은 방전 전위를 갖고, 흑연판 층(graphene layer)의 일축 배향성으로 인해 매우 가역적인 충방전 거동을 보이며, 그로 인해 우수한 전극 수명 특성(cycle life)을 보이며, 또한, Li 이온의 충전 시 전극전위가 0V Li/Li+로서 순수한 리튬 금속과 거의 유사한 전위를 나타낼 수있기 때문에, 산화물계 양극과 전지를 구성할 때, 더 높은 에너지를 얻을 수 있다는 장점을 갖는다.Specifically, the carbon-based compound has a very low discharge potential of about -3V with respect to the standard hydrogen electrode potential, exhibits a very reversible charge and discharge behavior due to the uniaxial orientation of the graphite layer, thereby resulting in an excellent electrode It shows higher cycle life and also shows higher potential when constructing an oxide-based anode and cell because the electrode potential during charging of Li ions can exhibit a potential similar to that of pure lithium metal as 0 V Li / Li + . It has the advantage of obtaining energy.

그러나, 이러한 탄소계 화합물로 이루어지는 음극은 하기와 같은 문제가 있다. However, the negative electrode made of such a carbon-based compound has the following problems.

첫째, 상기 탄소계 화합물은 이론적 최대 용량이 372 mAh/g(844 mAh/cc)으로 용량 증대에 한계가 있어 빠르게 변모하는 차세대 모바일 기기의 에너지원으로서의 충분한 역할을 감당하기는 어려운 실정이다.First, the carbon-based compound has a theoretical maximum capacity of 372 mAh / g (844 mAh / cc), which is limited in capacity increase, making it difficult to play a sufficient role as an energy source of a rapidly changing next-generation mobile device.

둘째, 상기 탄소계 화합물은 리튬이온의 삽입 및 탈리시 화학적 전위(chemical potential)가 금속 리튬과 비슷하므로 약간의 높은 충전전류에서도 과전압(overpotential)에 의한 리튬 석출이 발생하고, 한번 석출된 리튬은 충방전을 반복할수록 더욱 가속화되어 용량 감퇴는 물론 수지상 결정(dendrite)를 통한 단락(short)를 유발하여 안전성에 지대한 영향을 미칠 수 있는 문제가 있다. Second, since the chemical potential of the carbon-based compound is similar to that of metallic lithium in the insertion and desorption of lithium ions, lithium precipitation occurs due to overpotential even at a slight high charging current, and once deposited lithium is charged As the discharge is repeated, there is a problem that the acceleration may be further accelerated and cause short-circuit through dendrite, which may greatly affect safety.

셋째, 전지의 과충전 등에 의해서 음극에서 받을 수 있는 리튬의 양보다 많은 양의 리튬이 충전될 경우 온도가 상승하며 발열반응을 일으키게 되는데, 이는 전지 내부에서 일어나는 열역학(thermodynamic)반응 중 가장 일찍 일어나는 반응의 하나로 전지의 발화 폭발 등의 주요 트리거(trigger)가 될 수 있다. Third, when more lithium is charged than the amount of lithium that can be received from the negative electrode due to overcharging of the battery, the temperature rises and an exothermic reaction occurs. This is because of the earliest reaction among the thermodynamic reactions occurring inside the battery. One can be a major trigger, such as a battery ignition explosion.

넷째, 소수성(hydrophobic)전극 표면은 전지 생산 시 전해액의 전극 젖음성(wetting)에 지대한 영향을 미치며, 이 전극 젖음성 시간은 전지의 생산성 저하에 영향을 미치게 된다. Fourth, the surface of the hydrophobic electrode has a great influence on the electrode wetting of the electrolyte during battery production, and this electrode wetting time affects the productivity of the battery.

상기한 문제점을 해결하기 위해, 최근에는 종래의 탄소계 음극재에서 벗어나 실리콘(Si), 주석(Sn)을 이용한 Li 합금계(alloy)반응에 의한 음극재 및 Li4Ti5O12에 대한 연구가 많이 진행되고 있다. In order to solve the above problems, a recent study on the negative electrode material and Li 4 Ti 5 O 12 by the Li alloy-based reaction using silicon (Si), tin (Sn) away from the conventional carbon-based negative electrode material There is a lot going on.

그러나, 예를 들어, 실리콘은 이론적 최대 용량이 약 4020 mAh/g(9800 mAh/cc, 비중 2.23)으로서 흑연계 물질에 비해서 매우 큰 장점은 있으나. 충방전시 부피 변화가 매우 크다는 단점을 가지고 있다.However, silicon, for example, has a theoretical maximum capacity of about 4020 mAh / g (9800 mAh / cc, specific gravity 2.23), which is a significant advantage over graphite based materials. It has the disadvantage that the volume change during charge and discharge is very large.

또한, Li4Ti5O12는 충반전 동안 구조적 변화가 극히 낮아 제로 변형률(zero-strain) 물질로 수명특성이 매우 우수하고, 상대적으로 높은 전압대를 형성하며, 수지상 결정(dendrite)의 발생이 없어, 안전성(safety) 및 안정성(stability)이 매우 우수한 물질로 알려져 있으며, 또한, 수분 내에 충전이 가능한 급속 충전용 전극 특성을 가지고 있는 장점이 있으나, 용량이 매우 낮고, 음극으로 사용하기에 전압이 매우 높아 에너지 밀도가 매우 낮다는 문제가 있다. In addition, Li 4 Ti 5 O 12 has a very low structural change during charging and recharging, which is a zero-strain material having excellent life characteristics, forming a relatively high voltage range, and generating dendrite crystals. It is known as a material having excellent safety and stability, and also has the advantage of having a quick charging electrode property that can be charged within a few minutes, but has a very low capacity and a voltage for use as a negative electrode. There is a problem that the energy density is very low and very high.

또한, 특허출원공개 제2010-0008785호, 제2008-0112977호, 제2010-0086367호, 제2006-0028327호는 탄소계 음극 활물질의 표면에 티타늄 함유 산화물을 위치시키거나 코팅시킨 음극 활물질을 개시하고 있으나, 표면에 티타늄 함유 산화물을 위치시킨 음극 활물질을 제조하는 것은 두 물질이 갖는 상반되는 특성으로 인해 상호 혼합되는 것이 어렵고, 공정상의 비용상승을 수반하는 문제가 있다. In addition, Patent Application Publication Nos. 2010-0008785, 2008-0112977, 2010-0086367, and 2006-0028327 disclose a negative electrode active material in which a titanium-containing oxide is placed or coated on a surface of a carbon-based negative electrode active material. However, manufacturing a negative electrode active material having a titanium-containing oxide on the surface is difficult to be mixed with each other due to the opposite characteristics of the two materials, and there is a problem that involves a cost increase in the process.

따라서, 고용량 전원으로 사용될 수 있는 향상된 안전성 및 안정성과, 고출력 특성 및 고에너지 밀도를 갖는 음극에 대한 개발의 필요성이 절실한 실정이다.Therefore, there is an urgent need for development of a cathode having improved safety and stability, high output characteristics and high energy density that can be used as a high capacity power source.

한편, 고용량을 위해 중대형 장치 등의 대면적화가 이루어지면서 높은 젖음성(wetting) 특성은 더욱 중요해지고 있으며, 수지상 결정의 형성은 전극의 표면에서부터 일어나므로 탄소계 음극활물질과 티타늄 함유 산화물의 단순 혼합의 경우에는 젖음성을 극대화하는 것이 용이하지 않은 문제가 있다.On the other hand, high wetting properties are becoming more important as the area of medium and large devices is increased for high capacity, and since the formation of dendritic crystals occurs from the surface of the electrode, simple mixing of a carbon-based negative electrode active material and a titanium-containing oxide is performed. There is a problem that it is not easy to maximize the wettability.

본 발명은 상기와 같은 종래기술의 문제점과 과거로부터 요청되어온 기술적 과제를 해결하는 것을 목적으로 한다.SUMMARY OF THE INVENTION It is an object of the present invention to solve the above-described problems of the prior art and the technical problems required from the past.

본 출원의 발명자들은 심도 있는 연구와 다양한 실험들을 계속한 끝에, 수지상 결정(dendrite)의 형성, 전해액의 전극 젖음성(wetting) 및 전해액과의 전기화학적 반응 등이 전극의 표면반응으로부터 발생한다는 점에 착안하여, 집전체 표면에 도포된 제 1 음극합제 상에 상기 제 1 음극합제 중의 제 1 활물질에 비해 상대적으로 높은 충방전 전위와 큰 친수성을 갖는 제 2 음극 활물질을 포함한 제 2 음극합제를 코팅하는 경우. 안전성 및 안정성이 향상됨과 동시에 높은 에너지 밀도를 가짐을 발견하고, 본 발명을 완성하기에 이르렀다. The inventors of the present application, after continuing in-depth research and various experiments, notice that the formation of dendrite, the electrode wetting of the electrolyte, and the electrochemical reaction with the electrolyte arise from the surface reaction of the electrode. When the second negative electrode mixture including the second negative electrode active material having a relatively high charge and discharge potential and a large hydrophilicity compared to the first active material in the first negative electrode mixture on the first negative electrode mixture applied to the current collector surface . The present inventors have found that they have high energy density while improving safety and stability, and have completed the present invention.

따라서, 본 발명의 목적은 안전성 및 안정성이 향상되는 동시에 고 에너지 밀도, 고 출력 특성을 갖는 이차전지용 음극 및 이를 포함하는 리튬 이차전지를 제공하는 것이다. Accordingly, an object of the present invention is to provide a secondary battery negative electrode having a high energy density, high output characteristics and a lithium secondary battery including the same while improving safety and stability.

상기한 과제를 해결하기 위해 본 발명에 따른 이차전지용 음극은 집전체의 표면에 접촉된 상태로 도포되어 있는 제 1 음극활물질을 포함하는 제 1 음극합제 층; 및 상기 제 1 음극합체 층 상에 도포되어 있고, 상기 제 1 음극 활물질보다 상대적으로 높은 충방전 전위와 상대적으로 큰 친수성을 가진 제 2 음극활물질을 포함하는 제 2 음극합제 층; 을 포함하는 다층 구조로 이루어진 것을 특징으로 한다. In order to solve the above problems, a negative electrode for a secondary battery according to the present invention includes a first negative electrode mixture layer comprising a first negative electrode active material applied in contact with a surface of a current collector; And a second negative electrode mixture layer coated on the first negative electrode mixture layer and including a second negative electrode active material having a relatively higher charge / discharge potential and a relatively higher hydrophilicity than the first negative electrode active material. Characterized in that the multilayer structure comprising a.

따라서, 본 발명에 따른 이차전지용 음극은 제 1 음극합제 상에 상기 제 1 음극합제 중의 제 1 음극 활물질에 비해 상대적으로 높은 충방전 전위를 갖는 제 2 음극 활물질을 포함하는 제 2 음극합제를 도포함으로써, 수지상 결정(dendrite)의 형성을 방지하여 안전성을 향상시킨다. Accordingly, the negative electrode for secondary batteries according to the present invention is coated on the first negative electrode mixture by applying a second negative electrode mixture including a second negative electrode active material having a relatively high charge and discharge potential compared to the first negative electrode active material in the first negative electrode mixture In addition, the formation of dendrite is prevented to improve safety.

구체적으로, 전해액과 직접 반응하는 음극 표면에 형성된 제 2 음극합제는 리튬이 음극에 충전될 때 상기 제 2 음극합제에 충전되도록 함으로써, 다량의 전류 충전에 대하여 일종의 버퍼(buffer)로 작용한다. 따라서, 리튬 금속의 충방전 전위와 비슷한 제 1 음극 활물질에 비해 높은 충방전 전위를 갖는 제 2 음극 활물질의 표면에는 반복적인 충방전에 의한 수지상 결정의 형성이 방지된다.Specifically, the second negative electrode mixture formed on the surface of the negative electrode which reacts directly with the electrolyte solution is charged to the second negative electrode mixture when lithium is charged in the negative electrode, thereby acting as a kind of buffer for a large amount of current charge. Therefore, formation of dendritic crystals due to repetitive charge and discharge is prevented on the surface of the second negative electrode active material having a higher charge and discharge potential than the first negative electrode active material similar to the charge and discharge potential of lithium metal.

또한, 본 발명에 따른 이차전지용 음극은 제 1 음극합제 상에 상기 제 1 음극합제 중의 제 1 음극 활물질에 비해 상대적으로 큰 친수성을 갖는 제 2 음극 활물질을 포함하는 제 2 음극합제를 도포함으로써, 전해액의 젖음성(wetting)을 향상시킨다. In addition, the negative electrode for secondary batteries according to the present invention by applying a second negative electrode mixture comprising a second negative electrode active material having a relatively larger hydrophilicity than the first negative electrode active material in the first negative electrode mixture on the first negative electrode mixture, Improves the wetting of

구체적으로, 전해액과 직접 반응하는 음극 표면에 형성된 제 2 음극합제는 표면장력을 낮추어 전해액이 음극 표면에 쉽게 함침될 수 있도록 하는 역할을 하고, 상기 제 2 음극 활물질에 비해 상대적으로 소수성을 가진 제 1 음극 활물질에서는 침투된 전해액이 모세관 현상에 의해 음극 집전체의 표면 부위까지 침투됨으로써 전해액 젖음성이 향상되는 것이다.Specifically, the second negative electrode mixture formed on the surface of the negative electrode that reacts directly with the electrolyte serves to lower the surface tension so that the electrolyte can be easily impregnated on the surface of the negative electrode, and has a relatively hydrophobicity compared to the second negative electrode active material. In the negative electrode active material, the permeated electrolyte solution penetrates to the surface portion of the negative electrode current collector by a capillary phenomenon to improve the electrolyte wettability.

상기 제 2 음극 활물질의 전해액에 대한 친화성은 극성 물질에 대한 친화도로 표현할 때 제 1 음극 활물질보다 20 ~ 300% 클 수 있다. 극성 물질인 전해액에 대한 친화성을 평가하는 예로서 전해액 함침 속도를 비교할 때, 제 2 음극합제 층에 대한 전해액의 함침속도는 예를 들어 제 1 음극 활물질보다 30 ~ 200% 클 수 있다.The affinity for the electrolyte of the second negative electrode active material may be 20 to 300% greater than that of the first negative electrode active material when expressed as an affinity for the polar material. As an example of evaluating affinity for an electrolyte solution that is a polar material, when the electrolyte solution impregnation rate is compared, the impregnation rate of the electrolyte solution for the second negative electrode mixture layer may be, for example, 30 to 200% greater than that of the first negative electrode active material.

제 2 음극 활물질의 전해액에 대한 친화성, 예를 들어, 전해액 함침속도가 제 1 음극 활물질 대비로 상기 범위보다 크지 않을 경우에는, 앞서 설명한 바와 같은 본 발명에서 소망하는 효과들을 발휘하기 어려울 수 있으므로 바람직하지 않다.If the affinity of the second negative electrode active material for the electrolyte, for example, the electrolyte impregnation rate is not greater than the range above the first negative electrode active material, it may be difficult to achieve the desired effects in the present invention as described above Not.

상기 제 1 음극 활물질은 바람직하게는 결정성 흑연 및 저결정성 카본(carbon)으로 이루어진 군에서 선택되는 하나 이상일 수 있다. 하나의 바람직한 예에서, 인편상의 결정성 흑연탄소계 화합물과 저결정성 탄소계 화합물이 혼합된 혼합물일 수 있다. The first negative electrode active material may be at least one selected from the group consisting of crystalline graphite and low crystalline carbon. In one preferred example, the mixture may be a mixture of the flaky crystalline graphite carbon compound and the low crystalline carbon compound.

일반적으로 결정질 탄소계 화합물은 탄소의 층상 구조에 리튬이온이 삽입 및 탈리하는 경로가 대략 2차원으로 한정되어 있는 반면에, 저결정성 탄소화계 화합물은 리튬 이온이 삽입되기 위한 경로가 그와 같이 한정적이지 않고 상대적으로 많으므로, 우수한 레이트 특성을 발휘한다. 그러나, 비정질 탄소계 화합물은 비가역 용량이 20 ~ 30% 정도로서 매우 높은 단점을 갖는다. In general, crystalline carbon-based compounds have a two-dimensional path for lithium ions to be inserted and desorbed into the layered structure of carbon, whereas low-crystalline carbonated compounds have a limited path for insertion of lithium ions. Since it is relatively large, it exhibits excellent rate characteristics. However, the amorphous carbon-based compound has a very high disadvantage as the irreversible capacity is about 20 to 30%.

반면에, 상기와 같이 제 1 음극 활물질로 비정질 탄소계 화합물에 비가역 용량이 상대적으로 적은 인편상의 결정질 탄소계 화합물을 포함함으로써, 상기와 같은 단점을 보완한다. On the other hand, as described above, by including the flake-like crystalline carbon-based compound having a relatively low irreversible capacity in the amorphous carbon-based compound as the first negative electrode active material, to compensate for the above disadvantages.

경우에 따라서는, 상기 제 1 음극 활물질은 결정성 흑연 코어(core)에 저결정성 카본(carbon)이 코팅된 형태일 수 있다. In some cases, the first negative electrode active material may have a form in which low crystalline carbon is coated on a crystalline graphite core.

상기 제 1 음극 활물질은 구상이고, 상기 결정성 흑연은 천연흑연 또는 인조흑연일 수 있으며, 상기 저결정성 카본(carbon)은 탄소원자들이 무정형 결정구조를 가지며 우수한 레이트 특성을 발휘하는 것이라면 특별히 제한되는 것은 아니며, 예를 들어, 페놀수지 또는 퓨란수지를 열분해한 난흑연화 탄소(hard carbon), 코크스, 니들 코크스 또는 피치(Pitch)를 탄화한 이흑연화 탄소(soft carbon) 등이 사용될 수 있다. The first negative electrode active material is spherical, the crystalline graphite may be natural graphite or artificial graphite, the low crystalline carbon (carbon) is particularly limited as long as the carbon atoms have an amorphous crystal structure and exhibit excellent rate characteristics For example, hard carbon, coke, needle coke or pitch carbonized carbon obtained by pyrolyzing a phenol resin or a furan resin may be used.

따라서, 본 발명에 따른 이차전지용 음극은 제 1 음극 활물질로 에너지 밀도가 높은 탄소계 화합물을 사용함으로써 높은 에너지 밀도를 가질 수 있다. Therefore, the secondary battery negative electrode according to the present invention may have a high energy density by using a carbon-based compound having a high energy density as the first negative electrode active material.

한편, 상기 제 2 음극 활물질은 바람직하게는 티타늄 함유 산화물일 수 있다. 상기 티타늄 함유 산화물은, 예를 들어, 리튬 티타늄 산화물(Li4Ti5O12) 및 이산화티탄(TiO2)로 이루어진 군에서 선택되는 하나 이상일 수 있으며, 바람직하게는 리튬 티타늄 산화물(Li4Ti5O12)일 수 있다.On the other hand, the second negative electrode active material may be preferably a titanium containing oxide. The titanium-containing oxide may be, for example, at least one selected from the group consisting of lithium titanium oxide (Li 4 Ti 5 O 12 ) and titanium dioxide (TiO 2 ), preferably lithium titanium oxide (Li 4 Ti 5). O 12 ).

경우에 따라서는, 제 2 음극 활물질이 리튬티타늄 산화물(Li4Ti5O12)과 이산화티탄(TiO2)의 혼합물일 수 있고, 이 경우, 이들의 함량비는 중량비를 기준으로 10:90 내지 90:10의 범위일 수 있다.In some cases, the second negative electrode active material may be a mixture of lithium titanium oxide (Li 4 Ti 5 O 12 ) and titanium dioxide (TiO 2 ), and in this case, their content ratio is 10:90 to 10 based on the weight ratio. It may be in the range of 90:10.

따라서, 본 발명에 따른 이차전지용 음극은 제 2 음극 활물질로 티타늄 함유 산화물을 사용함으로써 반복적인 충방전 동안 구조적 안정성이 유지되므로 사이클(cycle)특성이 향상된다. Therefore, the negative electrode for secondary batteries according to the present invention improves cycle characteristics because structural stability is maintained during repeated charging and discharging by using titanium-containing oxide as the second negative electrode active material.

상기 음극은 상기 음극 활물질을 분산액에 첨가 및 교반하여 페이스트를 제조한 후 음극 집전체 상에 도포, 건조하여 제작된 제 1 음극합제 층 및 제 2 음극합제 층을 포함하고, 필요에 따라, 상기 음극합제 층들은 도전제, 바인더 및 충진제 등의 성분들이 선택적으로 더 포함될 수도 있다.The negative electrode includes a first negative electrode mixture layer and a second negative electrode mixture layer prepared by adding and stirring the negative electrode active material to a dispersion, preparing a paste, and then applying and drying the negative electrode current collector. The mixture layers may optionally further include components such as a conductive agent, a binder, and a filler.

공정상 본 발명에 따른 다층 구조의 음극합제 층은 1회의 더블 코팅(double coating) 공정으로 형성될 수 있으므로, 공정을 단순화함으로써 공정비용 등을 절감할 수 있는 효과를 발휘한다. In the process, the negative electrode mixture layer of the multilayer structure according to the present invention may be formed by a single double coating process, thereby reducing the process cost and the like by simplifying the process.

상기 음극 집전체는 일반적으로 3 내지 500 ㎛의 두께로 만들어진다. 이러한 음극 집전체는, 당해 전지에 화학적 변화를 유발하지 않으면서 도전성을 가진 것이라면 특별히 제한되는 것은 아니며, 예를 들어, 구리, 스테인리스 스틸, 알루미늄, 니켈, 티탄, 소성 탄소, 구리나 스테인리스 스틸의 표면에 카본, 니켈, 티탄, 은 등으로 표면처리한 것, 알루미늄-카드뮴 합금 등이 사용될 수 있다. 또한, 표면에 미세한 요철을 형성하여 음극 활물질의 결합력을 강화시킬 수도 있으며, 필름, 시트, 호일, 네트, 다공질체, 발포체, 부직포체 등 다양한 형태로 사용될 수 있다.The negative electrode collector is generally made to have a thickness of 3 to 500 mu m. Such an anode current collector is not particularly limited as long as it has conductivity without causing chemical change in the battery, and may be formed of a material such as copper, stainless steel, aluminum, nickel, titanium, fired carbon, surface of copper or stainless steel A surface treated with carbon, nickel, titanium, silver or the like, an aluminum-cadmium alloy, or the like can be used. In addition, fine concavities and convexities may be formed on the surface to enhance the bonding strength of the negative electrode active material, and may be used in various forms such as films, sheets, foils, nets, porous bodies, foams, and nonwoven fabrics.

상기 바인더의 예로는, 폴리테트라플루오로에틸렌(PTFE), 폴리비닐리덴플루오라이드(PVdF), 셀룰로오즈, 폴리비닐알코올, 카르복시메틸셀룰로우즈(CMC), 전분, 히드록시프로필셀룰로우즈, 재생 셀룰로우즈, 폴리비닐피롤리돈, 테트라플루오로에틸렌, 폴리에틸렌, 폴리프로필렌, 에틸렌-프로필렌-디엔 테르 폴리머(EPDM), 술폰화 EPDM, 스티렌 브티렌 고무, 불소 고무, 다양한 공중합체 등을 들 수 있다.Examples of the binder include polytetrafluoroethylene (PTFE), polyvinylidene fluoride (PVdF), cellulose, polyvinyl alcohol, carboxymethyl cellulose (CMC), starch, hydroxypropyl cellulose, regenerated cellulose Roses, polyvinylpyrrolidone, tetrafluoroethylene, polyethylene, polypropylene, ethylene-propylene-diene terpolymer (EPDM), sulfonated EPDM, styrene butylene rubber, fluorine rubber, various copolymers, and the like. .

상기 도전제는 당해 전지에 화학적 변화를 유발하지 않으면서 도전성을 가진 것이라면 특별히 제한되는 것은 아니며, 예를 들어, 천연 흑연이나 인조 흑연 등의 흑연 카본블랙, 아세틸렌 블랙, 케첸 블랙, 채널 블랙, 퍼네이스 블랙, 램프 블랙, 서머 블랙 등의 카본블랙 탄소 섬유나 금속 섬유 등의 도전성 섬유 불화 카본, 알루미늄, 니켈 분말 등의 금속 분말 산화아연, 티탄산 칼륨 등의 도전성 위스키 산화 티탄 등의 도전성 금속 산화물 폴리페닐렌 유도체 등의 도전성 소재 등이 사용될 수 있다. 시판되고 있는 도전제의 구체적인 예로는 아세틸렌 블랙 계열인 쉐브론 케미칼 컴퍼니(Chevron Chemical Company)나 덴카 블랙(Denka Singapore Private Limited), 걸프 오일 컴퍼니(Gulf Oil Company) 제품 등), 케트젠블랙(Ketjenblack), EC 계열(아르막 컴퍼니(Armak Company) 제품), 불칸(Vulcan) XC-72(캐보트 컴퍼니(Cabot Company) 제품) 및 수퍼(Super) P(Timcal 사 제품) 등이 있다.The conductive agent is not particularly limited as long as it has conductivity without causing chemical change in the battery. For example, graphite carbon black such as natural graphite or artificial graphite, acetylene black, Ketjen black, channel black, furnace, etc. Carbon black such as black, lamp black, summer black, conductive fiber such as carbon fiber or metal fiber Metal fluoride such as carbon fluoride, aluminum, nickel powder, etc. Conductive metal oxide polyphenylene, such as zinc oxide, conductive whiskey titanium oxide such as potassium titanate Conductive materials such as derivatives and the like can be used. Specific examples of commercially available conducting agents include acetylene black Chevron Chemical Company, Denka Singapore Private Limited, Gulf Oil Company, Ketjenblack, EC series (Armak Company), Vulcan XC-72 (Cabot Company), and Super P (Timcal).

경우에 따라서는, 음극의 팽창을 억제하는 성분으로서 충진제가 선택적으로 첨가될 수 있다. 이러한 충진제는 당해 전지에 화학적 변화를 유발하지 않으면서 섬유상 재료라면 특별히 제한되는 것은 아니며, 예를 들어, 폴리에틸렌, 폴리프로필렌 등의 올리핀계 중합체 유리섬유, 탄소섬유 등의 섬유상 물질이 사용된다.In some cases, a filler may be optionally added as a component to suppress the expansion of the negative electrode. The filler is not particularly limited as long as it is a fibrous material without causing chemical change in the battery. For example, fibrous materials such as olefinic polymer glass fibers such as polyethylene and polypropylene, and carbon fibers are used.

상기 분산액으로는 대표적으로 이소프로필 알코올, N-메틸피롤리돈(NMP), 아세톤 등이 사용될 수 있다.As the dispersion, isopropyl alcohol, N-methylpyrrolidone (NMP), acetone, and the like may be typically used.

전극 재료의 페이스트를 금속 재료에 고르게 도포하는 방법은 재료의 특성 등을 감안하여 공지 방법 중에서 선택하거나 새로운 적절한 방법으로 행할 수 있다. 예를 들어, 페이스트를 집전체 위에 분배시킨 후 닥터 블레이드(doctor blade) 등을 사용하여 균일하게 분산시키는 것이 바람직하다. 경우에 따라서는, 분배와 분산 과정을 하나의 공정으로 실행하는 방법을 사용할 수도 있다. 이 밖에도, 다이캐스팅(die casting), 콤마코팅(comma coating), 스크린 프린팅(screen printing) 등의 방법을 택할 수도 있으며, 또는 별도의 기재(substrate) 위에 성형한 후 프레싱 또는 라미네이션 방법에 의해 집전체와 접합시킬 수도 있다. The method of evenly applying the paste of the electrode material to the metal material can be selected from known methods or performed by a new suitable method in consideration of the properties of the material. For example, it is preferable to disperse the paste onto the current collector and then to disperse the paste uniformly using a doctor blade or the like. In some cases, a method of distributing and dispersing in one process may be used. In addition, die casting, comma coating, screen printing, or the like may be used. Alternatively, molding on a separate substrate may be performed by pressing or lamination. You may join.

금속판 위에 도포된 페이스트의 건조는 50 내지 200℃의 진공오븐에서 1 내지 3 일 동안 건조시키는 것이 바람직하다.Drying of the paste applied on the metal plate is preferably dried for 1 to 3 days in a vacuum oven at 50 to 200 ℃.

또한, 본 발명은 상기한 음극, 하기 화학식 1 및 화학식 2로 표시되는 리튬 이차전지용 양극 활물질들에서 선택되는 하나 이상을 포함하는 양극, 및 상기 음극과 양극 사이에 개재되어 있는 다공성의 분리막을 포함하는 것으로 구성되어 있는 이차전지용 전극조립체를 제공한다. In addition, the present invention includes a positive electrode including at least one selected from the above-described negative electrode, the positive electrode active material for lithium secondary batteries represented by Formula 1 and Formula 2, and a porous separator interposed between the negative electrode and the positive electrode It provides an electrode assembly for a secondary battery consisting of.

Lix(NivMnwCoyMz)O2-tAt (1)Li x (Ni v Mn w Co y M z ) O 2-t A t (1)

상기 식에서,Where

0.8<x≤1.3, 0≤v≤0.9, 0≤w≤0.9, 0≤y≤0.9, 0≤z≤0.9, x+v+w+y+z=2, 0≤t<0.2;0.8 <x ≦ 1.3, 0 ≦ v ≦ 0.9, 0 ≦ w ≦ 0.9, 0 ≦ y ≦ 0.9, 0 ≦ z ≦ 0.9, x + v + w + y + z = 2, 0 ≦ t <0.2;

M은 +2가 내지 +4가 산화수의 하나 이상의 금속 또는 전이금속 양이온이고 A는 -1 또는 -2가의 음이온이다.M is at least one metal or transition metal cation of +2 to + 4-valent oxidation number and A is -1 or -divalent anion.

LiaMn2-bM'bO4-cA'c (2)Li a Mn 2-b M ' b 0 4-c A' c (2)

상기 식에서,Where

0.8<a≤1.3, 0≤b≤0.5, 0≤c≤0.3;0.8 <a ≦ 1.3, 0 ≦ b ≦ 0.5, 0 ≦ c ≦ 0.3;

M'는 +2가 내지 +4가 산화수의 하나 이상의 금속 또는 전이금속 양이온이고 A'는 -1 또는 -2가의 음이온이다.
M 'is at least one metal or transition metal cation of +2 to + 4-valent oxidation number and A' is -1 or -divalent anion.

상기 화학식 1에서 Ni, Mn, Co 등의 전이금속은 +2가 내지 +4가 산화수의 금속 및/또는 기타 전이금속(M) 원소로 치환될 수 있는 바, 바람직하게는 Al, Mg 및 Ti로 이루어진 군에서 선택되는 하나이상으로 치환될 수 있고, 이 경우에 바람직한 치환량은 0.3≤z≤0.6일 수 있다. In Formula 1, a transition metal such as Ni, Mn, Co, etc. may be substituted with a metal of + 2-valent to + 4-valent oxidation number and / or other transition metal (M) element, preferably Al, Mg, and Ti. It may be substituted with one or more selected from the group consisting of, in this case the preferred amount of substitution may be 0.3≤z≤0.6.

상기 화학식 2에서 M'는 Co, Mn, Ni, Al, Mg 및 Ti로 이루어진 군에서 선택되는 하나 이상일 수 있다. M ′ in Formula 2 may be at least one selected from the group consisting of Co, Mn, Ni, Al, Mg, and Ti.

또한, 상기 화학식 1 및 2에서 산소이온은 소정의 범위에서 산화수 -1가 또는 -2가의 음이온(A, A')로 치환될 수 있는 바, 상기 A 및 A'는 바람직하게는 서로 독립적으로F, Cl, Br, I 과 같은 할로겐, S 및 N으로 이루어진 군에서 선택되는 하나 이상인 것일 수 있다.In addition, the oxygen ions in the general formula (1) and (2) can be replaced with anions (A, A ') of the oxidation number -1 or -divalent in a predetermined range, A and A' are preferably independently of each other F It may be one or more selected from the group consisting of halogen, such as Cl, Br, I, S and N.

이러한 음이온들의 치환에 의해 전이금속과의 결합력이 우수해지고 화합물의 구조 전이가 방지되기 때문에, 전지의 수명을 향상시킬 수 있다. 반면에, 음이온 A, A'의 치환량이 너무 많으면(t > 0.2) 불완전한 결정구조로 인해 오히려 수명 특성이 저하되므로 바람직하지 않다. By substituting these anions, the binding force with the transition metal is improved and the structural transition of the compound is prevented, so that the lifetime of the battery can be improved. On the other hand, if the amount of substitution of the anions A and A 'is too large (t> 0.2), it is not preferable because the life characteristics are lowered due to the incomplete crystal structure.

하나의 바람직한 예에서, 상기 화학식 1로 표시되는 양극 활물질은 Ni 및 Mn의 혼합 전이금속을 포함하며 리튬을 제외한 전체 전이금속의 평균 산화수가 +3가 보다 크고, 몰비 기준으로 니켈의 함량이 망간의 함량과 동일하거나 그 보다 큰 조건을 만족하는 층상 구조의 리튬 전이금속 산화물일 수 있다.In one preferred embodiment, the positive electrode active material represented by the formula (1) includes a mixed transition metal of Ni and Mn, the average oxidation number of all transition metals except lithium is greater than +3, the content of nickel on the basis of molar ratio of manganese It may be a lithium transition metal oxide of a layered structure satisfying a condition equal to or greater than the content.

또 다른 바람직한 예에서, 상기 화학식 1로 표시되는 양극 활물질은 Li(Ni0.5Mn0.3Co0.2)O2 또는 Li(Ni1/3Mn1/3Co1/3)O2 일 수 있다.In another preferred example, the cathode active material represented by Chemical Formula 1 may be Li (Ni 0.5 Mn 0.3 Co 0.2 ) O 2 or Li (Ni 1/3 Mn 1/3 Co 1/3 ) O 2 .

본 발명에 따른 양극의 제조방법은 특별히 한정되는 것은 아니며, 이하에서 하나의 예를 설명한다. The manufacturing method of the positive electrode which concerns on this invention is not specifically limited, One example is demonstrated below.

상기 복합 양극 활물질에 대해 바인더 및 도전제를 1 내지 20 중량%의 함량으로 분산액에 첨가 및 교반하여 페이스트를 제조한 후, 이를 집전체용 금속판에 도포하고 압축한 뒤 건조하여 라미네이트 형상의 전극을 제조할 수 있다.A binder and a conductive agent were added to the dispersion in an amount of 1 to 20% by weight with respect to the composite positive electrode active material and stirred to prepare a paste, and then coated on a metal plate for current collector, compressed, and dried to prepare a laminate electrode. can do.

상기 양극 집전체는 일반적으로 3 내지 500㎛의 두께로 만든다. 이러한 양극 집전체는, 당해 전지에 화학적 변화를 유발하지 않으면서 높은 도전성을 가지는 것이라면 특별히 제한되는 것은 아니며, 예를 들어, 스테인리스 스틸, 알루미늄, 니켈, 티탄, 소성 탄소, 또는 알루미늄이나 스테인리스 스틸의 표면에 카본, 니켈, 티탄, 은 등으로 표면 처리한 것 등이 사용될 수 있다. The positive electrode current collector is generally made to a thickness of 3 to 500㎛. Such a positive electrode current collector is not particularly limited as long as it has high conductivity without causing chemical change in the battery. For example, the surface of stainless steel, aluminum, nickel, titanium, calcined carbon, or aluminum or stainless steel Surface treated with carbon, nickel, titanium, silver, or the like can be used.

집전체는 음극 집전체와 마찬가지로, 그것의 표면에 미세한 요철을 형성하여 양극 활물질의 접착력을 높일 수도 있으며, 필름, 시트, 호일, 네트, 다공질체, 발포체, 부직포체 등 다양한 형태가 가능하다. Like the negative electrode current collector, the current collector may form fine irregularities on its surface to increase the adhesion of the positive electrode active material, and may be in various forms such as a film, a sheet, a foil, a net, a porous body, a foam, and a nonwoven fabric.

상기 분리막은 양극과 음극 사이에 개재되며, 높은 이온 투과도와 기계적 강도를 가지는 절연성의 얇은 박막이 사용된다. 분리막의 기공 직경은 일반적으로 0.01 ~ 10㎛이고, 두께는 일반적으로 5 ~ 300㎛이다. 이러한 분리막으로는, 예를 들어, 내화학성 및 소수성의 폴리프로필렌 등의 올레핀계 폴리머 유리섬유 또는 폴리에틸렌 등으로 만들어진 시트나 부직포 크라프트지 등이 사용된다. 현재 시판중인 대표적인 예로는 셀가드 계열(CelgardR 2400, 2300(Hoechest Celanese Corp. 제품), 폴리프로필렌 분리막(Ube Industries Ltd. 제품 또는 Pall RAI사 제품), 폴리에틸렌 계열(Tonen 또는 Entek) 등이 있다. The separator is interposed between the anode and the cathode, and an insulating thin film having high ion permeability and mechanical strength is used. The pore diameter of the separator is generally 0.01 ~ 10㎛, the thickness is generally 5 ~ 300㎛. As such a separator, for example, a sheet made of an olefin polymer glass fiber or polyethylene such as polypropylene having chemical resistance and hydrophobicity, a nonwoven kraft paper, or the like is used. Typical examples currently on the market include Celgard series (Celgard R 2400, 2300 (manufactured by Hoechest Celanese Corp.), polypropylene separator (manufactured by Ube Industries Ltd. or Pall RAI), polyethylene series (Tonen or Entek), etc.).

경우에 따라서는, 상기 분리막 위에는 전지의 안정성을 높이기 위하여 겔 폴리머 전해질이 코팅될 수 있다. 이러한 겔 폴리머의 대표적인 예로는 폴리에틸렌옥사이드, 폴리비닐리덴플루라이드, 폴리아크릴로나이트릴 등을 들 수 있다. In some cases, a gel polymer electrolyte may be coated on the separator to increase battery stability. Representative examples of such gel polymers include polyethylene oxide, polyvinylidene fluoride, polyacrylonitrile, and the like.

또한, 본 발명은 상기한 전극조립체가 전해질에 함침된 리튬 이차전지를 제공한다. 전해질로서 폴리머 등의 고체 전해질이 사용되는 경우에는 고체 전해질이 분리막을 겸할 수도 있다.The present invention also provides a lithium secondary battery in which the electrode assembly is impregnated with an electrolyte. When a solid electrolyte such as a polymer is used as an electrolyte, the solid electrolyte may also serve as a separation membrane.

상기 리튬염 함유 비수계 전해질은, 비수 전해질과 리튬으로 이루어져 있다. 비수 전해질로는 비수 전해액, 고체 전해질, 무기 고체 전해질 등이 사용된다. The said lithium salt containing non-aqueous electrolyte consists of a nonaqueous electrolyte and lithium. As the non-aqueous electrolyte, a non-aqueous electrolyte, a solid electrolyte, an inorganic solid electrolyte and the like are used.

상기 비수 전해액으로는, 예를 들어, N-메틸-2-피롤리디논, 프로필렌 카르보네이트, 에틸렌 카르보네이트, 부틸렌 카르보네이트, 디메틸 카르보네이트, 디에틸 카르보네이트, 에틸메틸 카보네이트, 감마-부틸로 락톤, 1,2-디메톡시 에탄, 1,2-디에톡시 에탄, 테트라히드록시 프랑(franc), 2-메틸 테트라하이드로푸란, 디메틸술폭시드, 1,3-디옥소런, 4-메틸-1,3-디옥센, 디에틸에테르, 포름아미드, 디메틸포름아미드, 디옥소런, 아세토니트릴, 니트로메탄, 포름산 메틸, 초산메틸, 인산 트리에스테르, 트리메톡시 메탄, 디옥소런 유도체, 설포란, 메틸 설포란, 1,3-디메틸-2-이미다졸리디논, 프로필렌 카르보네이트 유도체, 테트라하이드로푸란 유도체, 에테르, 피로피온산 메틸, 프로피온산 에틸 등의 비양자성 유기용매가 사용될 수 있다.As said non-aqueous electrolyte, N-methyl- 2-pyrrolidinone, a propylene carbonate, ethylene carbonate, butylene carbonate, dimethyl carbonate, diethyl carbonate, ethylmethyl carbonate, for example , Gamma-butylo lactone, 1,2-dimethoxy ethane, 1,2-diethoxy ethane, tetrahydroxy franc, 2-methyl tetrahydrofuran, dimethyl sulfoxide, 1,3-dioxolon, 4-methyl-1,3-dioxene, diethyl ether, formamide, dimethylformamide, dioxolon, acetonitrile, nitromethane, methyl formate, methyl acetate, phosphate triester, trimethoxy methane, dioxolon Aprotic organic solvents such as derivatives, sulfolane, methyl sulfolane, 1,3-dimethyl-2-imidazolidinone, propylene carbonate derivatives, tetrahydrofuran derivatives, ethers, methyl pyroionate and ethyl propionate can be used. Can be.

상기 유기 고체 전해질로는, 예를 들어, 폴리에틸렌 유도체, 폴리에틸렌 옥사이드 유도체, 폴리프로필렌 옥사이드 유도체, 인산 에스테르 폴리머, 폴리 에지테이션 리신(agitation lysine), 폴리에스테르 술파이드, 폴리비닐 알코올, 폴리 불화 비닐리덴, 이온성 해리기를 포함하는 중합체 등이 사용될 수 있다.Examples of the organic solid electrolyte include a polymer electrolyte such as a polyethylene derivative, a polyethylene oxide derivative, a polypropylene oxide derivative, a phosphate ester polymer, an agitation lysine, a polyester sulfide, a polyvinyl alcohol, a polyvinylidene fluoride, Polymers containing ionic dissociation groups, and the like can be used.

상기 무기 고체 전해질로는, 예를 들어, Li3N, LiI, Li5NI2, Li3N-LiI-LiOH, LiSiO4, LiSiO4-LiI-LiOH, Li2SiS3, Li4SiO4, Li4SiO4-LiI-LiOH, Li3PO4-Li2S-SiS2 등의 Li의 질화물, 할로겐화물, 황산염 등이 사용될 수 있다.As the inorganic solid electrolyte, for example, Li 3 N, LiI, Li 5 NI 2 , Li 3 N-LiI-LiOH, LiSiO 4 , LiSiO 4 -LiI-LiOH, Li 2 SiS 3 , Li 4 SiO 4 , Nitrides, halides, sulfates, and the like of Li, such as Li 4 SiO 4 -LiI-LiOH, Li 3 PO 4 -Li 2 S-SiS 2 , and the like, may be used.

상기 리튬염은 상기 비수계 전해질에 용해되기 좋은 물질로서, 예를 들어, LiCl, LiBr, LiI, LiClO4, LiBF4, LiB10Cl10, LiPF6, LiCF3SO3, LiCF3CO2, LiAsF6, LiSbF6, LiAlCl4, CH3SO3Li, CF3SO3Li, LiSCN, LiC(CF3SO2)3, (CF3SO2)2NLi, 클로로 보란 리튬, 저급 지방족 카르본산 리튬, 4 페닐 붕산 리튬, 이미드 등이 사용될 수 있다.The lithium salt is a material that is readily soluble in the non-aqueous electrolyte, for example, LiCl, LiBr, LiI, LiClO 4, LiBF 4, LiB 10 Cl 10, LiPF 6, LiCF 3 SO 3, LiCF 3 CO 2, LiAsF 6, LiSbF 6, LiAlCl 4, CH 3 SO 3 Li, CF 3 SO 3 Li, LiSCN, LiC (CF 3 SO 2) 3, (CF 3 SO 2) 2 NLi, chloroborane lithium, lower aliphatic carboxylic acid lithium, 4-phenylborate, imide, and the like can be used.

또한, 전해액에는 충방전 특성, 난연성 등의 개선을 목적으로, 예를 들어, 피리딘, 트리에틸포스파이트, 트리에탄올아민, 환상 에테르, 에틸렌 디아민, n-글라임(glyme), 헥사 인산 트리 아미드, 니트로벤젠 유도체, 유황, 퀴논 이민 염료, N-치환 옥사졸리디논, N,N-치환 이미다졸리딘, 에틸렌 글리콜 디알킬 에테르, 암모늄염, 피롤, 2-메톡시 에탄올, 삼염화 알루미늄 등이 첨가될 수도 있다. 경우에 따라서는, 불연성을 부여하기 위하여, 사염화탄소, 삼불화에틸렌 등의 할로겐 함유 용매를 더 포함시킬 수도 있고, 고온 보존 특성을 향상시키기 위하여 이산화탄소 가스를 더 포함시킬 수도 있으며, FEC(Fluoro-Ethylene Carbonate), PRS(Propene sultone) 등을 더 포함시킬 수 있다.For the purpose of improving the charge / discharge characteristics and the flame retardancy, the electrolytic solution is preferably mixed with an organic solvent such as pyridine, triethylphosphite, triethanolamine, cyclic ether, ethylenediamine, glyme, Benzene derivatives, sulfur, quinone imine dyes, N-substituted oxazolidinones, N, N-substituted imidazolidines, ethylene glycol dialkyl ethers, ammonium salts, pyrrole, 2-methoxyethanol, . In some cases, in order to impart nonflammability, a halogen-containing solvent such as carbon tetrachloride or ethylene trifluoride may be further included, and carbon dioxide gas may be further included to improve high temperature storage characteristics, and FEC (Fluoro-Ethylene Carbonate) may be further included. ), PRS (Propene sultone) may be further included.

본 발명에 따른 이차전지는 고에너지 밀도, 고출력 특성, 향상된 안전성 및 안정성을 발휘하므로, 특히 중대형 전지모듈의 구성 전지로서 바람직하게 사용될 수 있다. 따라서, 본 발명은 또한 상기와 같은 이차전지를 단위전지로 포함하는 중대형 전지모듈을 제공한다. Since the secondary battery according to the present invention exhibits high energy density, high output characteristics, improved safety and stability, it may be particularly preferably used as a constituent battery of a medium and large battery module. Accordingly, the present invention also provides a medium-large battery module including the secondary battery as a unit cell.

이러한 중대형 전지모듈은 전기자동차, 하이브리드 전기자동차, 전력저장장치 등과 같이 고출력, 대용량이 요구되는 동력원에 바람직하게 적용될 수 있다. The medium-large battery module may be preferably applied to a power source that requires high output and large capacity, such as an electric vehicle, a hybrid electric vehicle, and a power storage device.

중대형 전지모듈의 구성 및 그것의 제작 방법은 당업계에 공지되어 있으므로, 그에 대한 설명을 명세서에서는 생략한다. Since the construction of the medium-large battery module and its manufacturing method are well known in the art, a description thereof will be omitted.

본 발명에 따른 이차전지용 음극은 제 1 음극합제 상에 제 1 음극활물질에 비해 상대적으로 높은 충방전 전위를 갖는 제 2 음극 활물질을 포함하는 제 2 음극합제를 도포함으로써 수지상 결정(dendrite)의 형성 방지하여 안전성을 향상시키는 효과가 있다.The negative electrode for a secondary battery according to the present invention prevents the formation of dendritic crystals by applying a second negative electrode mixture including a second negative electrode active material having a higher charge and discharge potential on the first negative electrode mixture than the first negative electrode active material. It has the effect of improving safety.

또한, 본 발명에 따른 이차전지용 음극은 제 1 음극합제 상에 제 1 음극활물질에 비해 상대적으로 큰 친수성을 갖는 제 2 음극활물질을 포함하는 제 2 음극합제를 도포함으로써 전해액의 젖음성(wetting)을 향상시키는 효과가 있다. In addition, the negative electrode for a secondary battery according to the present invention improves the wetting of the electrolyte by applying a second negative electrode mixture including a second negative electrode active material having a relatively larger hydrophilicity than the first negative electrode active material on the first negative electrode mixture. It is effective to let.

또한, 본 발명에 따른 이차전지용 음극은 제 1 음극활물질로 탄소계 화합물을 사용하고, 제 2 음극활물질로 반복적인 충방전 동안 구조적 안정성이 유지되는 티타늄 함유 산화물을 사용함으로써 높은 에너지 밀도를 가짐과 동시에 싸이클(cycle) 특성이 향상되는 효과가 있다. In addition, the negative electrode for a secondary battery according to the present invention has a high energy density by using a carbon-based compound as the first negative electrode active material, and by using a titanium-containing oxide that maintains structural stability during repeated charge and discharge with the second negative electrode active material. There is an effect that the cycle (cycle) characteristics are improved.

본 발명이 속한 분야에서 통상의 지식을 가진 자라면 상기 내용을 바탕으로 본 발명의 범주내에서 다양한 응용 및 변형을 행하는 것이 가능할 것이다.Those skilled in the art to which the present invention pertains will be able to perform various applications and modifications within the scope of the present invention based on the above contents.

Claims (16)

집전체의 표면에 접촉된 상태로 도포되어 있는 제 1 음극 활물질을 포함하는 제 1 음극합제 층; 및
상기 제 1 음극합체 층 상에 도포되어 있고, 상기 제 1 음극 활물질보다 상대적으로 높은 충방전 전위와 상대적으로 큰 친수성을 가진 제 2 음극 활물질을 포함하는 제 2 음극합제 층;
을 포함하는 다층 구조로 이루어진 것을 특징으로 하는 이차전지용 음극.A first negative electrode mixture layer comprising a first negative electrode active material applied in contact with a surface of a current collector; And
A second negative electrode mixture layer coated on the first negative electrode mixture layer, the second negative electrode mixture layer comprising a second negative electrode active material having a relatively higher charge / discharge potential and a relatively higher hydrophilicity than the first negative electrode active material;
A secondary battery negative electrode comprising a multi-layer structure comprising a. 제 1 항에 있어서, 상기 제 2 음극 활물질의 전해액에 대한 친화성은 제 1 음극활물질보다 20 ~ 300% 큰 것을 특징으로 하는 이차전지용 음극.The negative electrode of claim 1, wherein the affinity of the second negative electrode active material for the electrolyte is 20 to 300% greater than that of the first negative electrode active material. 제 1 항에 있어서, 상기 제 2 음극합제 층에 대한 전해액의 함침속도는 제 1 음극 활물질보다 30 ~ 200% 큰 것을 특징으로 하는 이차전지용 음극.The method of claim 1, wherein the impregnation rate of the electrolyte solution to the second negative electrode mixture layer is a secondary battery negative electrode, characterized in that 30 to 200% greater than the first negative electrode active material. 제 1 항에 있어서, 상기 제 1 음극 활물질은 결정성 흑연 및 저결정성 카본(carbon)으로 이루어진 군에서 선택되는 하나 이상인 것을 특징으로 하는 이차전지용 음극.The negative electrode of claim 1, wherein the first negative electrode active material is at least one selected from the group consisting of crystalline graphite and low crystalline carbon. 제 1 항에 있어서, 상기 제 1 음극 활물질은 결정성 흑연 코어(core)에 저결정성 카본(carbon)이 코팅되어 있는 것을 특징으로 하는 이차전지용 음극.The negative electrode of claim 1, wherein the first negative electrode active material is coated with low crystalline carbon on a crystalline graphite core. 제 4 항 또는 제 5 항에 있어서, 상기제 1 음극활물질은 구상인 것을 특징으로 하는 이차전지용 음극. The negative electrode for a secondary battery according to claim 4 or 5, wherein the first negative electrode active material is spherical. 제 4 항 또는 제 5 항에 있어서, 상기 결정성 흑연은 천연흑연 또는인조흑연인 것을 특징으로 하는 이차전지용 음극.The negative electrode for a secondary battery according to claim 4 or 5, wherein the crystalline graphite is natural graphite or artificial graphite. 제 4 항 또는 제 5 항에 있어서, 상기저결정성 카본(carbon)은 난흑연화탄소(hard carbon) 또는 이흑연화탄소(soft carbon)인 것을 특징으로 하는 이차전지용 음극.The negative electrode of claim 4 or 5, wherein the low crystalline carbon is hard carbon or soft carbon. 제 1 항에 있어서, 상기 제 2 음극 활물질은 티타늄 함유 산화물인 것을특징으로 하는 이차전지용 음극.The negative electrode for a secondary battery according to claim 1, wherein the second negative electrode active material is a titanium-containing oxide. 제 9 항에 있어서, 상기티타늄 함유 산화물은 리튬 티타늄 산화물(Li4Ti5O12) 및 이산화티탄(TiO2)로 이루어진 군에서 선택되는 하나 이상인 것을 특징으로 하는 이차전지용 음극.The anode of claim 9, wherein the titanium-containing oxide is at least one selected from the group consisting of lithium titanium oxide (Li 4 Ti 5 O 12 ) and titanium dioxide (TiO 2 ). 제 10 항에 있어서, 제 2 음극활물질이 리튬 티타늄 산화물(Li4Ti5O12)과 이산화티탄(TiO2)의 혼합물로 이루어져 있을 때, 이들의 함량비는 중량비를 기준으로 10:90 내지 90:10의 범위인 것을 특징으로 하는 이차전지용 음극.The method according to claim 10, wherein when the second negative electrode active material is made of a mixture of lithium titanium oxide (Li 4 Ti 5 O 12 ) and titanium dioxide (TiO 2 ), the content ratio thereof is 10:90 to 90 based on the weight ratio. A secondary battery negative electrode, characterized in that the range of: 10. 제 1 항에 따른 음극, 하기 화학식 1 및 화학식 2로 표시되는 리튬 이차전지용 양극 활물질들에서 선택되는 하나 이상을 포함하는 양극, 및 상기 음극과 양극 사이에 개재되어 있는 다공성의 분리막을 포함하는 것으로 구성되어 있는 것을 특징으로 하는 이차전지용 전극조립체
Lix(NivMnwCoyMz)O2-tAt (1)
상기 식에서,
0.8<x≤1.3, 0≤v≤0.9, 0≤w≤0.9, 0≤y≤0.9, 0≤z≤0.9, x+v+w+y+z=2, 0≤t<0.2;
M은 +2가 내지 +4가 산화수의 하나 이상의 금속 또는 전이금속 양이온이고
A는 -1 또는 -2가의 음이온이다.
LiaMn2-bM'bO4-cA'c (2)
상기 식에서,
0.8<a≤1.3, 0≤b≤0.5, 0≤c≤0.3;
M'는 +2가 내지 +4가 산화수의 하나 이상의 금속 또는 전이금속 양이온이고 A'는 -1 또는 -2가의 음이온이다.Comprising a negative electrode according to claim 1, a positive electrode including at least one selected from the positive electrode active material for lithium secondary batteries represented by the formula (1) and formula (2), and a porous separator interposed between the negative electrode and the positive electrode Electrode assembly for secondary battery, characterized in that
Li x (Ni v Mn w Co y M z ) O 2-t A t (1)
In this formula,
0.8 <x ≦ 1.3, 0 ≦ v ≦ 0.9, 0 ≦ w ≦ 0.9, 0 ≦ y ≦ 0.9, 0 ≦ z ≦ 0.9, x + v + w + y + z = 2, 0 ≦ t <0.2;
M is at least one metal or transition metal cation of +2 to + 4-valent oxidation number
A is a -1 or -divalent anion.
Li a Mn 2-b M ' b 0 4-c A' c (2)
In this formula,
0.8 <a ≦ 1.3, 0 ≦ b ≦ 0.5, 0 ≦ c ≦ 0.3;
M 'is at least one metal or transition metal cation of +2 to + 4-valent oxidation number and A' is -1 or -divalent anion. 제 12 항의 전극조립체를 포함하는 것을 특징으로 하는 리튬 이차전지.A lithium secondary battery comprising the electrode assembly of claim 12. 제 13 항의 리튬 이차전지를 단위전지로 사용하는 것을특징으로 하는 전지모듈.A battery module comprising the lithium secondary battery of claim 13 as a unit cell. 제 14 항에 따른 전지모듈을 전원으로 사용하는 것을특징으로 하는 전기자동차 또는 하이브리드 전기자동차.An electric vehicle or a hybrid electric vehicle, characterized by using the battery module according to claim 14 as a power source. 제 14 항에 따른 전지모듈을 전원으로 사용하는 것을특징으로 하는 전력저장 장치. A power storage device characterized by using the battery module according to claim 14 as a power source.
KR1020110013075A 2011-02-15 2011-02-15 Anode Having Multi-Layer Structure for Secondary Battery and Lithium Secondary Battery Including The Same KR101440347B1 (en)