KR20080064890A - 탄소 마찰재 - Google Patents
탄소 마찰재 Download PDFInfo
- Publication number
- KR20080064890A KR20080064890A KR1020087012560A KR20087012560A KR20080064890A KR 20080064890 A KR20080064890 A KR 20080064890A KR 1020087012560 A KR1020087012560 A KR 1020087012560A KR 20087012560 A KR20087012560 A KR 20087012560A KR 20080064890 A KR20080064890 A KR 20080064890A
- Authority
- KR
- South Korea
- Prior art keywords
- sintered
- friction material
- fiber
- carbon
- friction
- Prior art date
Abstract
소결된 탄소 마찰재가 소결 전에 수지에 함침된 섬유 재료로 제조된다. 바람직하게는, 부직포 섬유 재료가 페놀 수지에 함침된 후 400 ~ 800°C에서 소결된다. 그 생성물은 50체적% 이상의 열린 기공률을 가진다.
마찰재, 소결, 다공성, 기공, 공극, 페놀 수지, 섬유
Description
본 발명은 소결(sintering)처리에 의해 제조된 탄소 마찰재에 관한 것이다. 보다 상세하게는, 수지 함침 섬유재료를 소결함으로써 제조되는 소결 탄소 마찰재에 관한 것이다.
연속 슬립 토크 컨버터(continuous slip torque converter)와 시프팅 클러치 시스템(shifting clutch system)을 갖춘 새롭고 진보된 연속 토크 트랜스미션 시스템(continuous torque transmission system)이 자동차 산업에 의해 개발되어지고 있다. 이들 새로운 시스템은 흔히 고 에너지의 요구사항들을 포함한다. 따라서, 또한 마찰재 기술은 이러한 진보된 시스템에 있어서의 증가하는 에너지 요구사항들을 충족하도록 개발되어야 한다.
특히, 새로운 고성능의 내구성을 갖춘 마찰재가 요구된다. 이러한 새로운 마찰재는 표면속도가 약 65m/s 까지 달하는 고속에 견딜 수 있어야 한다. 또한, 이러한 마찰재는 약 1500psi에까지 달하는 높은 페이싱 라이닝 압력(facing lining pressure)을 견딜 수 있어야 한다. 그리고, 이러한 마찰재가 제한된 윤활 조건 하 에서 유용하다는 점이 중요하다.
마찰재가 상기 진보된 시스템에 사용되기 위해서는 내구성과 고 내열성을 가져야 한다. 또한, 마찰재는 고온 하에서도 안정적으로 유지되어야 할 뿐만 아니라, 작동 상태 동안에 발생되는 고열을 신속히 발산시킬 수 있어야 한다.
상기 새로운 시스템의 연결 및 분리 중에 발생되는 높은 속도는 마찰재가 상기 연결 중에 비교적 일정한 마찰을 유지할 수 있어야 한다는 점을 의미한다. 제동하는 동안 또는 트랜스미션 시스템 있어서 일단의 기어로부터 타단의 기어로 변속하는 동안 재료의 "떨림(shuddering)"을 최소화하기 위해 넓은 범위의 속도 및 온도에 걸쳐서 마찰 연결이 비교적 일정해야 한다는 점은 중요하다. 또한, 마찰재가 바람직한 토크 곡선 형상을 가짐으로써 마찰 연결 중에 마찰재에 노이즈나 "스쿼크(squawk)"가 없어야 한다는 점도 중요하다.
종래에는, 습식 클러치 어플리케이션(wet clutch application)용 습식 마찰재에서 함침제로서 페놀 수지가 사용되었지만, 이 페놀 수지는 많은 제한을 가진다. 페놀수지 마찰재는 상기의 새로운 고 에너지 트랜스미션 시스템에 사용되기 위해 필요한 고 내열성을 가지고 있지 않다. 특히, 페놀수지는 고 에너지 어플리케이션에 사용되기에는 너무 낮은 온도인 약 300°C 온도에서 분해된다. 게다가, 페놀수지는 강성(剛性)을 가진 재료이며, 페놀수지가 마찰재에 사용될 경우 만약 균일한 접촉이 이루어지지 않으면 불균일한 라이닝 마모와 세퍼레이터판 "열점"(separator plate "hot spots")이 더욱 더 야기되기 쉽다.
더욱 향상된 마찰재에 대한 요구에 부응한 광범위한 연구의 결과로서, 진보 된 특성을 갖는 마찰재가 본 발명에 의해 개발되었다. 본 발명의 습식 마찰재는 사용 중에 마찰재가 "젖어" 있거나 브레이크액 또는 자동 변속기액과 같은 액체에 함침(impregnated)되어있는 "습식" 어플리케이션에 유용하다. 상기 "습식" 마찰재가 사용되는 동안, 상기 액체가 궁극적으로 짜내어지거나 상기 액체에 마찰재를 함침시킨다. 습식 마찰재는 그 구성과 물리적 특성면에서 "건식" 마찰재와 크게 다르다.
"습식" 마찰재의 증가된 기공률(porosity)에 대한 조사를 계속할 필요가 있다. 종이 제조공정을 통해 제조된 기존의 "습식" 마찰재의 열린 공극(open pore)은 대략 50 체적%이다. 압축 성형으로 제조된 것과 같은 다른 "습식" 마찰재의 기공률은 50 체적% 미만이다.
독특한 탄소 마찰재가 400°C ~ 800°C의 온도 범위에서 섬유 재료들의 소결에 의해 제조된다. 상기 섬유 재료들은 충전제(filler)와 입자들(particles)을 함유하거나 함유하지 않은 수많은 섬유들로 구성될 수 있다. 상기 재료들은 소결 전에 먼저 수지에 침지된다. 그 결과물이 소결된 다공성 탄소체(sintered, porous carbon body)이다. 상기 섬유 재료들은 종이와 부직포형 섬유 재료가 바람직하고, 상기 수지는 페놀 수지가 바람직하다.
본 발명의 소결된 탄소 마찰재는 거의 50 체적% 이상의 열린 기공률(open porosity)을 가진다. 섬유(fiber)/충전제(filler) 타입 마찰재가 550°C 이하에서 처리될 때, 그 재료는 충분한 가요성과 강도를 유지한다. 처리 온도가 높아지면 공극의 크기는 증가하고, 표면도 더욱 개방된다. 처리 온도가 높아지면 마찰 계수는 커지고, 마찰-속도 곡선은 더욱 긍정적/바람직해진다.
도 1은 본 발명에 의한 탄화된 샘플들의 측면도이다.
도 2는 본 발명의 탄화가 압축성(compressibility)을 증대시키는 것을 보여주는 그래프이다.
도 3은 기공 크기에 대한 증대된 탄화의 효과를 나타내는 그래프이다.
도 4는 내열성에 대한 향상된 탄화의 효과를 나타내는 그래프이다.
바람직한 실시예에 관한 아래의 상세한 설명과 첨부 도면을 검토해보면 본 발명의 다른 목적들과 이점이 당업자에게 명백해질 것이다.
본 발명에 유용한 다양한 수지는 페놀 수지와 페놀계 수지를 포함한다. 에폭시, 부타디엔, 실리콘, 동유(tung oil), 벤젠, 캐슈넛 오일(cashew nut oil) 등과 같은 다른 개질 성분을 수지 혼합물에 포함시키는 다양한 페놀계 수지가 본 발명에 유용할 수 있는 것으로서 고려된다는 점을 이해해야 한다. 페놀 개질 수지(phenolic modified resin)에 있어서, 일반적으로 페놀 수지는 수지 혼합물(존재하는 용매는 제외함)의 대략 50 중량% 이상 존재한다. 그러나, 함침제 수지 혼합물 이 실리콘-페놀 혼합물(용매와 다른 가공 조제들은 제외함)의 중량을 기준으로 하여 약 5~80중량%, 어떤 목적을 위해서는 약 15~55중량%, 및 다른 실시예들에서 15~25중량%의 실리콘 수지를 함유할 경우에 마찰재가 개선될 수 있다는 것이 발견되었다.
일반적으로, 소결된 다공질체는 큰 비표면적을 가진다. 또한, 상기 소결된 다공질체는 기공 공극(pore voids)을 가지며 큰 체적의 상기 기공 공극들을 갖는다. 이는 열린 기공 구조를 갖는 독특한 소결된 다공질체를 제공한다.
본 발명에 의하면, 마찰재는 베이스 재료 전체에 걸쳐서 균일하게 분포된 수지를 가진다. 어떤 실시예들에 있어서, 상기 수지 재료는 마찰재의 100중량파트 당 대략 45~65중량파트를 포함한다.
어떤 실시예들에 있어서, 수지 재료가 베이스 재료에 적용되고 상기 베이스 재료가 수지 혼합물에 함침된 후, 함침된 베이스 재료가 소정 시간 동안 원하는 온도로 가열되어 마찰재를 형성한다. 그 후, 경화된 마찰재가 적당한 수단에 의해 원하는 기재(substrate)에 부착된다.
도 1은 본 발명에 의한 탄화된 샘플들의 측면도이다. 상기 측면도는 샘플들의 탄화 전과 탄화 후를 나타낸다.
도 2는 본 발명의 탄화가 압축성을 증대시키는 것을 보여주는 그래프이다. 탄화된 섬유 베이스 재료가 증대된 압축성을 가지게 되고, 이는 열점 저항성과 마찰 특성을 향상시킨다.
도 3은 기공 크기에 대한 증대된 탄화의 효과를 나타내는 그래프이다. 이 그 래프는 탄화가 기공 크기를 증가시킨다는 것을 보여준다. 또한, 이 그래프는 탄화 온도가 높아질수록 구조도 더욱 개방된다는 것을 보여준다.
도 4는 내열성에 대한 향상된 탄화의 효과를 나타내는 그래프이다. 탄화된 재료가 최초 탄화되지 않은 재료보다 더 큰 에너지 용량을 가진다.
어떤 실시예들에서는, 베이스 재료에 의한 수지의 목표 픽업은 전체 페놀 수지 재료의 대략 25 ~ 120중량% 범위인 것이 바람직하고, 다른 실시예에서는 대략 40 ~ 100중량%, 또 다른 실시예에서는 60 ~ 적어도 80중량%인 것이 바람직하다. 베이스 재료에 수지가 스며든 후, 상기 수지 재료를 경화하여 마찰재를 형성하기 위해 상기 베이스 재료가 160~250°C 범위의 온도 하에서 일정 시간 동안(일 실시예에서는 대략 30분 동안) 경화된다. 마찰재의 최종 두께는 베이스 재료의 최초 두께에 의존한다.
또한, 수지 혼합물과 섬유 베이스 재료를 제조하는데에 유용한 것으로 알려진 다른 성분과 가공조제가 포함될 수 있다는 점이 고려되고, 이것은 본 발명의 고려 범위 내에 있는 것이다.
일반적으로, 소결은 질소와 수소의 화합물 또는 일산화탄소(CO)를 함유한 가스 혼합물 등과 같은 비활성 또는 환원 분위기 하에서 실시된다. 그후에 소결 부품들은 가열상태(heating phase)에 처하게 되며 가열상태에서 미세구조의 변형이 일어난다. 10중량%의 수소를 가진 질소 혼합물과 같은, 그 자체에 탄소 화합물을 포함하지 않는 환원 가스 하에서도 소결은 실시될 수 있다.
본 발명에 있어서의 공정은 자체 지지 소결체, 예컨대 자체 지지 골격 (self-supporting skeleton)을 가진 소결체의 제조에도 사용될 수 있다.
베이스 재료(base materials)
예를 들면, 천(fabric) 재료, 직포 및/또는 부직포 재료를 포함하는 비석면계 섬유 베이스 재료를 포함하는 다양한 베이스 재료가 본 발명의 마찰재에 유용하다. 적합한 섬유 베이스 재료는, 예컨대 섬유와 충전제(filler)를 포함한다. 상기 섬유는 유기 섬유, 무기 섬유 및 탄소 섬유일 수 있다. 상기 유기 섬유는 아라미드 섬유, 폴리에스테르 섬유, 나일론 섬유, 폴리아미드 섬유, 면(cotton)/셀룰로스(cellulose) 섬유 등일 수 있다. 상기 충전제는, 예를 들면 실리카(silica), 규조토, 흑연, 알루미나, 및 캐슈 더스트(cashew dust) 등일 수 있다.
다른 실시예들에서, 상기 베이스 재료는 섬유 직물 재료, 섬유 부직포 재료, 및 종이 재료를 포함할 수 있다. 또한, 본 발명에 유용한 다양한 형태의 섬유 베이스 재료의 예는 보르그워너(BorgWarner)사의 많은 미국 특허들에 개시되어 있다. 그러나, 본 발명의 다른 실시예는 다른 섬유 베이스 재료를 포함할 수 있다는 점을 이해해야 한다.
예를 들면, 어떤 실시예들에서는, 상기 섬유 베이스 재료는 마찰재에 원하는 기공 구조를 제공하기 위해 적게 피브릴화된 섬유(fibrillated fiber)와 탄소 섬유가 사용된 섬유 베이스 재료를 포함한다. 상기 섬유 구조는 향상된 내열성을 제공할 뿐만 아니라 내박리성(delamination resistance) 및 내잡음성(squeal or noise resistance)를 제공한다. 또한, 어떤 실시예들에 있어서는, 탄소 섬유와 탄소 입자의 존재는 섬유 베이스 재료에 있어서 내열성을 증가시키고, 마찰계수를 안정적으 로 유지시키며, 내잡음성을 증가시키는 것을 돕는다. 마찰재의 클러치 "브레이크-인(break-in)" 특성을 개선시키기 위해 섬유 베이스 재료에 비교적 적은 양의 면섬유가 포함될 수 있다.
다양한 충전제가 본 발명의 섬유 베이스 재료의 일차 층(primary layer)에 유용하다. 특히, 규조토 같은 실리카 충전제가 유용하다. 그러나, 다른 타입의 충전제가 본 발명으로의 사용에 적합할 수 있고, 충전제의 선택은 마찰재에 대한 특유의 요구조건에 의존한다.
바람직한 실시예에서, 소결된 마찰재는 아라미드 섬유로 제조된다. 그러나, 상기 소결된 마찰재는 아크릴 섬유만으로 이루어지거나 아라미드 섬유와의 조합으로도 이루어질 수 있다.
어떤 실시예들에 있어서, 섬유 재료에 더 큰 마찰계수를 제공하기 위해 면섬유가 본 발명의 섬유 베이스 재료에 첨가된다. 어떤 실시예들에서는 대략 5 ~ 20%, 다른 실시예들에서는 대략 10%의 면(cotton)이 섬유 베이스 재료에 첨가될 수도 있다.
상기 섬유 베이스 재료의 일차 층에 대한 조성의 일 예는 대략 75중량% ~ 85중량%의 적게 피브릴화된 아라미드 섬유와, 대략 15중량% ~ 25중량%의 충전제 재료를 포함한다.
어떤 실시예들에서, 유용한 것으로 알려진 하나의 특유한 조성은 대략 35 ~ 45중량%의 적게 피브릴화된 아라미드 섬유, 대략 5 ~ 15중량%의 면섬유, 대략 2 ~ 20중량%의 탄소 섬유, 및 대략 25 ~ 35중량%의 충전제를 포함한다.
또 어떤 실시예들에서, 상기 베이스 재료는 약 15 ~ 25%의 면, 약 40 ~50%의 아라미드 섬유, 약 10 ~ 20%의 탄소 섬유, 및 약 5 ~ 15%의 세라이트(celite)와 선택적으로 약 1 ~ 3%의 라텍스 첨가물(latex add-on)을 포함하는 마찰 개질 입자들을 포함한다.
섬유 베이스 재료가 더 큰 평균 기공 직경과 액체 투과성을 가질 경우, 마찰재의 다공성 구조를 통하여 자동 변속기액의 유동이 더욱 양호해지기 때문에 마찰재는 더 온도가 낮거나 트랜스미션에서 생성된 열을 더 적게하여 사용된다. 트랜스미션 시스템이 작동하는 동안, 유체는 시간이 경과함에 따라 특히 높은 온도에서 파괴되어 "오일 침전물(oil deposits)" 형성하는 경향이 있다. 상기 "오일 침전물(oil deposits)"은 기공 구멍을 감소시킨다. 따라서, 마찰재가 최초에 큰 기공 상태에서 시작될 경우 마찰재의 내용연수 동안에 개방 공극이 더 많이 남아있게 된다.
섬유 베이스 재료의 상단 표면 상의 마찰 개질 입자들은 생성된 마찰재에 향상된 3차원 구조를 제공한다.
상기 상단 마찰 개질 입자층 상의 오일층 또는 유체층이 표면상에 유막을 유지하므로, 오일 또는 유체가 초기에 마찰재 내로 침투하는 것을 더욱 어렵게 한다. 상기 상단 마찰 개질 재료층은 표면상에 유체 윤활제를 유지하여 마찰재의 오일 보유 능력을 증가시킨다. 따라서, 본 발명의 마찰재는 유막이 마찰재 표면상에 잔류하도록 한다. 또한, 이것은 양호한 마찰 계수 특성과 우수한 슬립 내구성(slip durability) 특성을 제공한다.
어떤 실시예들에 있어서, 상부층을 형성하는 마찰 개질 입자들의 평균 커버(coverage)영역은 표면적의 대략 80 ~ 100% 범위 내에 있다. 또 다른 실시예에서, 평균 커버영역은 대략 90 ~ 100% 범위이다. 마찰 개질 입자는 대략 35 ~ 200㎛의 바람직한 평균 두께로 베이스 재료의 상부면에 실제로 남아있다. 어떤 실시들에 있어서, 상기 상부층은 대략 60 ~ 100 μ 의 바람직한 평균 두께를 가진다.
직경이 대략 1 ~ 80μ, 어떤 실시예들에서는 1 ~50μ, 다른 실시예들에서는 1 ~ 20μ 범위일 수 있는 입자의 크기를 사용함으로써 마찰 개질 입자의 침전층(deposited layer)이 섬유 베이스 재료의 표면상에 균일하게 형성된다. 어떤 실시예들에 있어서, 상기 입자는 대략 12㎛의 평균 입경(particle diameter)을 가진다. 어떤 실시예들에서, 만약 마찰 개질 입자의 크기가 너무 크거나 너무 작다면 원하는 최적의 3차원 구조가 달성되지 않으며, 결과적으로 열 분산과 떨림 방지(anti-shudder) 특성이 최적 조건으로 되지 못한다는 것을 발견했다.
섬유 베이스 재료 상의 마찰 개질 입자들의 커버 량은 충분히 두꺼워서 마찰 개질 입자층은 마찰 개질재의 개별 입자들과 이들 개별 입자 사이의 공간 또는 틈새로 이루어진 3차원 구조를 가진다. 어떤 실시예들에 있어서, (마찰 개질 입자의) 상부층은 (섬유 베이스 재료의) 하부층보다 공극의 수가 더 적다.
다양한 형태의 마찰 개질 입자가 마찰재에서 유용하다. 일 실시예에서, 유용한 마찰 개질 입자는 실리카 입자를 포함한다. 다른 실시예는 페놀 수지, 실리콘 수지, 에폭시 수지, 및 이들 혼합물 등의 수지 분말과 같은 마찰 개질 입자를 가질 수 있다. 또 다른 실시예는 부분적 및/또는 전체적으로 탄화된 탄소 분말 및/또는 입자 및 이들 혼합물, 그리고 이러한 마찰 개질 입자들의 혼합물을 포함할 수 있다. 어떤 실시예들에서, 규조토, Celite®, Celatom®, 및/또는 이산화규소와 같은 실리카 입자가 특히 유용하다. 상기 실리카 입자는 베이스 재료에 접착되는 저렴한 무기질 재료이다. 상기 실리카 입자는 마찰재에 높은 마찰 계수를 제공한다. 또한, 상기 실리카 입자는 베이스 재료에 매끄러운(smooth) 마찰면을 제공하며 상기 마찰재에 양호한 "변속감(shift feel)" 과 마찰 특성을 제공하므로 "떨림" 이 최소화된다.
어떤 실시예들에서, 본 발명의 마찰재의 상부층을 이루는 마찰 개질재는 불규칙한 형상을 가질 수 있다. 불규칙한 모양의 마찰 개질 입자의 표면 상에 있는 수많은 함입부(invagination)의 모세관 현상에 의하여 불규칙한 형상의 마찰 개질 입자는 섬유 베이스 재료의 표면에 원하는 양의 윤활제를 유지하도록 기능한다. 어떤 실시예들에서, 세라이트는 불규칙하거나 거친(rough) 표면을 가지므로 세라이트와 같은 실리카 재료가 마찰 개질재로서 유용하다.
어떤 실시예들에서, 상기 마찰재는 그 내부에 다수의 공극 또는 틈새를 가지는 섬유 베이스 재료로 이루어진다. 상기 섬유 베이스 재료 내의 공극의 크기는 대략 0.5μ ~ 20㎛ 범위일 수 있다.
어떤 실시예들에서, 바람직하게는 상기 섬유 베이스 재료가 대략 50 ~ 60%의 공극용량을 가짐으로써 "다공성" 직물과 비교해서 상기 섬유 베이스 재료가 "조밀한(dense)" 것으로 간주된다. 어떤 실시예들에서, 수지 재료가 상기 섬유 베이스 재료 내의 공극을 적어도 부분적으로 채운다. 상기 수지 재료는 베이스 재료의 전 체 두께에 걸쳐서 매우 균일하게 분포된다.
실시예
아래의 실시예들은 본 발명의 마찰재가 종래의 마찰재보다 개선이 되었다는 추가적인 증거를 제공한다.
내부에 공극을 구비한 개방형 3차원 구조를 가지는 소결된 다공성 탄소가 아래와 같이 제조된다. 상기 소결된 탄소 마찰재의 제조 방법은 소결 전에 수지에 섬유 재료를 함침시키는 단계, 상기 수지 함침된 섬유 재료를 소결하는 단계, 및 소결된 탄소 마찰재를 제조하는 단계를 포함한다. 상기 함침 단계는 페놀 수지로 실시되고, 상기 소결 단계는 600°C 온도에서 실시된다. 상기 섬유 재료는 부직포형 아라미드 섬유이다.
그 후, 상기 소결된 다공성 탄소가 베이스 재료로 사용된다. 일반적으로, 상기 베이스 재료는 약 5 ~ 75중량%의 아라미드 섬유, 약 5 ~ 75중량%의 면섬유, 약 5 ~ 75중량%의 탄소 섬유, 및 약 5 ~ 75중량%의 충전제 재료를 포함한다.
상기 소결 공정은 더욱 우수한 강도를 위해 조밀한 시트를 형성하도록 원료 종이 시트를 압축하는 단계, 더욱 우수한 강도를 확보하기 위해 경화처리 동안 또는 그 이후에 상기 종이를 압축하는 단계, 및 더욱 우수한 강도를 확보하기 위해 높은 수지 픽업(60 - 150%)을 사용하는 단계를 포함한다. 상기 수지는 페놀, 개질 페놀, 에폭시, 기타 형태의 유기 수지, 세라믹 수지 등을 포함한다. 바람직하게는, 400 ~ 800°C의 온도에서 질소 가스, 아르곤, 수증기, 암모니아, 및 아민 등의 분 위기 하에서 재료를 소결한다.
본 발명의 탄소 마찰재의 적용들은 고 압력(20㎫까지)과 고 에너지 시스템들을 포함한다. 기타 적용들은 낮고 제한된 오일 유동 또는 건조 상태 시스템들을 포함한다.
표 1은 탄화된 샘플들에 대한 재료 가공을 나타낸다.
파이럿 시험 ID | A | B |
캘리퍼(caliper) | 0.031" | 0.031" |
가공 1 | 0.025"의 크기로 됨 | 0.025"의 크기로 됨 |
가공 2 | 60% PU | 60% PU |
소결 후 캘리퍼 | 0.0245" | 0.0285" |
소결 후 중량 손실(%) | 12% | 9% |
시험된 판 두께(측정치) | 0.023" | 0.023" |
시험된 판 밀도(g/㎤) | 0.73 | 0.77 |
표 2는 습식 오일, 반 건식 내구성 테스트에서의 소결된 재료의 결과값을 나타낸다.
샘플 | 제어(control:C) | 소결 후 C |
라이닝 두께 변화 & 라이닝 상태 | 0.001mm (0.2%) OK | 0.000mm (0.7% 이득(gain)) OK |
세퍼레이터 상태 | 검은 얼룩 | 열 얼룩 |
마찰 수준 변화 | 0.143-0.106-->26% | 0.121-0.139-->+13% |
총 사이클 | 1377 | 2226 |
상기 결과들은 아래 사실들을 보여준다.
1. 소결처리된 C는 소결처리되지 않은 것보다 더욱 하강하는 곡선을 가진다.
2. 소결된 C의 mu 레벨은 테스트 사이클과 함께 증가했다.
3. 가공되지 않은 순수한 C는 다른 재료들보다 더 많은 마찰 페이드(friction fade)를 가진다.
알 수 있는 바와 같이, 본 발명의 소결된 탄소 마찰재는 비교대상 재료보다 우수한 기능을 일관되게 수행한다. 따라서, 본 발명의 상기 섬유 베이스 재료는 더 높은 속도에서 비교대상 재료보다 더욱 양호한 효과를 달성한다.
4. 소결된 C는 제어C 샘플보다 더 우수한 내구성을 가진다.
본 발명은 클러치판, 트랜스미션 밴드, 브레이크 슈(brake shoe), 싱크로나이저 링(synchronizer ring), 마찰 디스크 또는 시스템 플레이트에 사용되는 고 에너지 마찰재로서 유용하다. 본 발명의 바람직하고 대안적인 실시예들에 관한 상기 설명은 예시적인 의도로 설명된 것이며, 아래의 청구항의 범위와 내용을 제한할 의도로 설명되지는 않았다.
본 발명의 상기 상세한 설명은 설명의 편의를 목적으로 기재된다. 본 발명의 범위를 벗어나는 일 없이 다양한 변경과 변형이 가능하다는 것은 당업자에게 자명할 것이다. 따라서, 상기 상세한 설명의 전체는 제한적인 의미가 아닌 예시적인 의미로서 해석되어야 하고, 본 발명의 범위는 첨부된 청구항에 의해서만 정의된다.
Claims (32)
- 소결 전에 수지에 함침된 섬유 재료들로 제조되고, 소결된 재료는 원재료보다 더 많은 열린 기공률을 가지는 것을 특징으로 하는 소결된 탄소 마찰재.
- 제 1 항에 있어서,상기 소결된 재료는 적어도 50체적%의 열린 기공률을 갖는 소결된 다공질 탄소체인 것을 특징으로 하는 소결된 탄소 마찰재.
- 제 2 항에 있어서,상기 소결된 다공질 탄소체는 상당한 비표면적을 가지는 것을 특징으로 하는 소결된 탄소 마찰재.
- 제 2 항에 있어서,상기 소결된 다공질 탄소체는 아라미드 섬유로 제조되는 것을 특징으로 하는 소결된 탄소 마찰재.
- 제 2 항에 있어서,상기 소결된 다공질 탄소체는 기공 공극을 가지며, 상당한 체적의 상기 기공 공극을 가지는 것을 특징으로 하는 소결된 탄소 마찰재.
- 제 2 항에 있어서,상기 소결된 다공질 탄소체는 열린 기공 구조를 가지는 것을 특징으로 하는 소결된 탄소 마찰재.
- 제 1 항에 있어서,상기 섬유 재료는 아라미드 섬유, 셀룰로스 섬유, 유기 섬유, 유리 섬유, 탄소 섬유 또는 아크릴 섬유 또는 다른 합성 섬유들인 것을 특징으로 하는 소결된 탄소 마찰재.
- 제 1 항에 있어서,40% 이상의 증가된 수지 픽업을 가지는 것을 특징으로 하는 소결된 탄소 마찰재.
- 제 1 항에 있어서,60% 이상의 증가된 수지 픽업을 가지는 것을 특징으로 하는 소결된 탄소 마찰재.
- 제 7 항에 있어서,실리카, 규조토, 흑연, 알루미나, 캐슈 더스트, 마찰 입자들, 탄소 입자들, 니트릴, 캐슈 넛 오일 입자들, 고형 윤활제, 테프론 및 이황화 몰리브덴으로 이루어진 그룹으로부터 선택된 하나 이상의 충전제를 포함하는 것을 특징으로 하는 소결된 탄소 마찰재.
- 제 1 항에 있어서,상기 소결된 섬유 재료들은 아라미드 섬유들, 아크릴 섬유들 또는 이들 조합물인 것을 특징으로 하는 소결된 탄소 마찰재.
- 제 1 항에 있어서,상기 섬유 재료들은 직물형, 종이형, 및 부직포형 섬유 재료들인 것을 특징으로 하는 소결된 탄소 마찰재.
- 제 1 항에 있어서,상기 섬유 재료들은 부직포형 섬유 재료들인 것을 특징으로 하는 소결된 탄소 마찰재.
- 제 1 항에 있어서,상기 수지는 페놀 수지인 것을 특징으로 하는 소결된 탄소 마찰재.
- 제 2 항에 있어서,상기 소결된 다공질 탄소체는 그 내부에 공극을 갖는 개방형 3차원 구조인 것을 특징으로 하는 소결된 탄소 마찰재.
- 소결 전에 수지에 함침된 섬유 재료로 제조되는 소결된 탄소 마찰재로서, 상기 소결된 탄소 마찰재는 큰 기공률을 가진 소결된 다공질 탄소체인 것을 특징으로 하는 소결된 탄소 마찰재.
- 제 16 항에 있어서,상기 소결된 다공질 탄소체는 50체적% ~ 85체적%의 범위의 평균 공극 체적을 가지고, 평균 직경 크기가 약 5μ ~ 100μ 의 범위인 기공들을 가지는 것을 특징으로 하는 소결된 탄소 마찰재.
- 제 16 항에 있어서,상기 소결된 다공질 탄소체는 60체적% ~ 85체적% 의 범위의 평균 공극 체적을 가지고, 평균 직경 크기가 5μ ~ 50μ 의 범위인 기공들을 가지는 것을 특징으로 하는 소결된 탄소 마찰재.
- 제 16 항에 있어서,상기 소결된 다공질 탄소체는 65체적% ~ 85체적%의 범위의 평균 공극 체적을 가지고, 평균 직경 크기가 5μ ~ 25μ의 범위인 기공들을 가지는 것을 특징으로 하 는 소결된 탄소 마찰재.
- 제 1 항에 있어서,약 5 ~ 75중량%의 아라미드 섬유, 약 5 ~ 75중량%의 셀룰로스 섬유, 약 5 ~ 75중량%의 탄소 섬유, 및 약 5 ~ 75중량%의 충전제 재료를 포함하는 베이스 재료가 사용되는 것을 특징으로 하는 소결된 탄소 마찰재.
- 제 20 항에 있어서,트랜스미션 밴드의 형태로 된 것을 특징으로 하는 소결된 탄소 마찰재.
- 제 20 항에 있어서,클러치 페이싱의 형태로 된 것을 특징으로 하는 소결된 탄소 마찰재.
- 제 20 항에 있어서,브레이크 슈 라이닝의 형태로 된 것을 특징으로 하는 소결된 탄소 마찰재.
- 제 20 항에 있어서,싱크로나이저의 형태로 된 것을 특징으로 하는 소결된 탄소 마찰재.
- 소결 전에 섬유 재료를 수지에 함침시키는 단계;상기 수지가 함침된 섬유 재료를 400~800°C 범위의 온도에서 소결시키는 단계; 및50체적% 이상의 열린 기공률을 가진 소결된 탄소 마찰재를 제조하는 단계;를 포함하는 것을 특징으로 하는 소결된 탄소 마찰재 제조 방법.
- 제 25 항에 있어서,제조된 상기 소결된 탄소 마찰재는 소결된 다공질 탄소체인 것을 특징으로 하는 소결된 탄소 마찰재 제조 방법.
- 제 25 항에 있어서,상기 함침은 페놀 수지로 실시되는 것을 특징으로 하는 소결된 탄소 마찰재 제조 방법.
- 제 25 항에 있어서,상기 소결은 400 ~ 600°C 범위의 온도에서 실시되는 것을 특징으로 하는 소결된 탄소 마찰재 제조 방법.
- 제 25 항에 있어서,상기 섬유 재료들은 부직포, 직물 또는 종이 섬유 재료들인 것을 특징으로 하는 소결된 탄소 마찰재 제조 방법.
- 제 25 항에 있어서,상기 소결된 다공질 탄소체는 그 내부에 공극을 갖는 개방형 3차원 구조인 것을 특징으로 하는 소결된 탄소 마찰재 제조 방법.
- 제 25 항에 있어서,상기 소결된 다공질 탄소체는 자체 지지 골격인 것을 특징으로 하는 소결된 탄소 마찰재 제조 방법.
- 제 25 항에 있어서,상기 소결은 400 ~ 550°C 범위의 온도에서 실시되는 것을 특징으로 하는 소결된 탄소 마찰재 제조 방법.