KR20050079284A - A melamine resin vessel and the method thereof - Google Patents

Abstract

본 발명은 멜라민 용기 표면의 적어도 일부분에 멜라민 수지 착색층을 포함하는 멜라민 수지 착색구조체가 파묻혀 형성된 것을 그 특징으로 하는 멜라민 수지 용기 및 그 제조방법에 관한 것이다. 본 발명의 용기는 멜라민 수지에 일정한 두께의 벌크 구조를 갖는 멜라민 수지의 착색층이 바탕천에 결합된 것을 용기의 표면에 파묻음으로써 오래 사용하여도 변색되거나 벗겨지지 않는 반영구적 무늬 또는 글자를 갖는 멜라민 수지 용기를 제공할 수 있다. 나아가 용기 완성 후 별도의 공정을 추가하지 않고 용기를 몰딩 성형하는 공정을 통해 무늬나 글자를 형성하는 효과를 갖는다. The present invention relates to a melamine resin container and a method for producing the same, wherein a melamine resin colored structure including a melamine resin colored layer is embedded in at least a portion of the melamine container surface. The container of the present invention is a melamine resin has a semi-permanent pattern or letters that do not discolor or peel off even after long use by burying the colored layer of melamine resin having a bulk structure of a certain thickness and bonded to the base fabric on the surface of the container A resin container can be provided. Furthermore, after the completion of the container, there is an effect of forming a pattern or letters through the process of molding the container without adding a separate process.

Description

멜라민 수지 용기 및 그 제조방법{A melamine resin vessel and the method thereof}A melamine resin vessel and the method of manufacturing the same

본 발명은 멜라민 수지 용기에 과한 것이다. 보다 구체적으로는 착색된 멜라민 수지를 용기 제조용 멜라민 수지의 몰딩 성형 공정을 통해 용기 표면측에 박아 넣어 착색된 멜라민 수지의 두께 층을 형성시켜 무늬나 글자 도형 등을 새김으로써 장시간 사용해도 무늬 등의 훼손이 방지되는 멜라민 수지 용기에 관한 것이다. The present invention is directed to a melamine resin container. More specifically, the colored melamine resin is embedded in the surface of the container through the molding molding process of the melamine resin for manufacturing a container to form a thick layer of the colored melamine resin, and the pattern or the letters are etched, thereby damaging the pattern. This relates to a melamine resin container to be prevented.

종래에는 멜라민 수지 용기 표면에 글자나 무늬 등을 새길 때 종이에 인쇄하고 이를 완성된 용기 표면에 전사하는 방식을 사용하였다. 이런 방식으로 제조된 용기는 글자나 무늬 등이 처음에는 선명하게 표시되어 있으나 용기를 사용하다 보면 인쇄한 글자 등이 점점 벗겨지게 되고 색이 퇴색되게 된다. 따라서 글자 등을 써 넣어도 선명하게 유지되는 기간이 짧다는 단점이 있다. Conventionally, when engraving letters or patterns on the surface of the melamine resin container was printed on paper and transferred to the finished container surface was used. Containers manufactured in this way are clearly marked with letters or patterns at first, but when the container is used, printed letters are gradually peeled off and the color is faded. Therefore, even if you write letters, etc., there is a short period of time to remain clear.

본 발명은 종래의 종이 전사 방식과는 전혀 다른 방식으로 멜라민 수지 용기에 글자나 무늬의 두께 층을 형성하는 방식을 채용하여 제조된 멜라민 수지 용기를 제공함으로써 오래 사용하여도 색의 변색이 없고 벗겨지지 않는 글자, 무늬 등을 유지하는 멜라민 수지 용기를 제공하는 것을 그 목적으로 한다. The present invention provides a melamine resin container manufactured by adopting a method of forming a thickness layer of letters or patterns on the melamine resin container in a completely different manner from the conventional paper transfer method, so that there is no discoloration of color and peeling even after long use. It is an object of the present invention to provide a melamine resin container for holding letters, patterns, and the like.

본 발명은, 멜라민 용기 표면의 적어도 일부분에 멜라민 수지 착색층을 포함하는 멜라민 수지 착색구조체가 파묻혀 형성된 것을 그 특징으로 하는 멜라민 수지 용기에 관한 것이다. The present invention relates to a melamine resin container characterized in that a melamine resin colored structure including a melamine resin colored layer is buried in at least a portion of the melamine container surface.

바람직하게는 상기 멜라민 수지 착색구조체는 바탕천 상에 멜라민 수지 착색층이 결합되어 있다,Preferably, the melamine resin colored structure is a melamine resin colored layer is bonded on the base fabric,

바람직하게는 상기 멜라민 수지 착색층은 그 두께가 0.5 mm 내지 2.5 mm로 형성된다. Preferably, the melamine resin colored layer has a thickness of 0.5 mm to 2.5 mm.

바람직하게는 상기 멜라민 수지 착색층은 복수의 서로 다른 색상의 멜라민 수지 착색층이 결합되어 형성된다.Preferably, the melamine resin colored layer is formed by combining a plurality of melamine resin colored layers of different colors.

바람직하게는 상기 멜라민 수지 착색층 내에는 복수의 펄프 알갱이가 포함되어 있다. Preferably, a plurality of pulp grains are contained in the melamine resin colored layer.

한편 본 발명은, 착색된 멜라민 수지를 금형에 넣고 그 위에 바탕천을 올려놓고 몰딩 성형에 의해 멜라민 수지 착색층과 상기 바탕천이 결합된 멜라민 수지 착색 구조체를 형성하는 단계와, 상기 멜라민 수지 착색층과 상기 멜라민 수지 착색층에 직접 접촉하고 있는 부분의 바탕천을 함께 결합된 상태로 오려내는 단계와, 용기 본체 형성용 금형 상에 재치한 용기 본체 형성용 멜라민 수지 상에/하에 오려내진 멜라민 수지 착색구조체를 재치하고 금형에 의해 몰딩 성형하여 용기를 형성하는 단계를 포함하는 멜라민 수지 용기의 제조 방법에 관한 것이다. On the other hand, the present invention, by putting a colored melamine resin in a mold and placing a base fabric thereon to form a melamine resin colored structure in which the melamine resin colored layer and the base fabric are bonded by molding molding, the melamine resin colored layer and the Cutting out the base fabric of the part directly contacting the melamine resin colored layer in a bonded state, and placing the melamine resin colored structure cut out on and under the melamine resin for container body forming placed on the mold for forming the container body. And it relates to a method for producing a melamine resin container comprising the step of molding the molding by a mold.

한편 본 발명은 착색된 멜라민 수지 분말을 금형에 넣고 몰딩 성형하여 제 1 착색층 조각을 형성하는 단계와, 상기 제 1 착색층 조각 상에 제 2 착색층 형성용 착색된 멜라민 수지를 놓고 그 위에 바탕천을 올려놓고 몰딩 성형하여 제 1 착색층과 제 2 착색층의 결합된 착색층과 상기 바탕천이 결합된 구조를 형성하는 단계와,상기 멜라민 수지 착색층과 상기 멜라민 수지 착색층에 직접 접촉하고 있는 부분의 바탕천을 결합된 상태로 오려 내는 단계와, 오려낸 멜라민 수지 착색층과 바탕천의 결합 구조를 용기 본체 형성용 멜라민 수지 반죽 상에/하에 재치하고 금형에 의해 몰딩 성형하여 용기를 형성하는 단계를 포함하되, 상기 제 1 착색층은 제 2 착색층보다 그 두께가 얇은 것을 그 특징으로 하는 멜라민 수지 용기의 제조 방법에 관한 것이다. Meanwhile, the present invention provides a method of forming a first colored layer piece by inserting the colored melamine resin powder into a mold and molding, and placing a colored melamine resin for forming a second colored layer on the first colored layer piece. Forming a structure in which the combined colored layer of the first colored layer and the second colored layer and the base fabric are bonded to each other by molding the cloth, and directly contacting the melamine resin colored layer and the melamine resin colored layer. Cutting out the base fabric in a bonded state; and mounting the cut structure of the cut melamine resin colored layer and the base fabric on / under the melamine resin dough for forming the container body and molding the mold by a mold to form a container. It includes, but the first colored layer relates to a method for producing a melamine resin container, characterized in that the thickness thereof is thinner than the second colored layer.

이하 첨부도면을 참조하여 본 발명의 실시예를 상세히 설명한다. Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings.

도 1은 본 발명의 실시예를 도시한 도면이다. 도 1에 도시된 바와 같이 제 1 멜라민 수지 착색층 조각(100)을 우선 형성한다. 멜라민 수지 착색층 조각을 형성하는 방법은 자세한 설명이 필요 없을 것이다. 착색된 멜라민 수지 분말 재료를 가열된 금형틀에 붓고 몰딩 성형하여 원하는 형상을 만들 수 있다. 바람직하게는 멜라민 수지 분말 재료에 콘이라고 통상 불리는 펄프 알갱이를 포함시켜서 함께 몰딩 성형한다. 몰딩 성형시의 적정 온도는 160℃ 내지 180℃ 정도이다. 몰딩 성형한 후 냉각하면 도 1과 같은 고형의 멜라민 조각(100)을 형성할 수 있다. 펄프 알갱이는 향후 그릇에 착색층을 매설할 때 색이 번지는 것을 방지하는 작용을 하며 색감을 좋게 한다. 1 is a view showing an embodiment of the present invention. As shown in FIG. 1, the first melamine resin colored layer piece 100 is first formed. The method for forming the melamine resin colored layer pieces will not need detailed explanation. The colored melamine resin powder material can be poured into a heated mold and molded to form the desired shape. Preferably, the melamine resin powder material is molded together with pulp grains commonly called cones. The appropriate temperature at the time of molding molding is about 160 to 180 degreeC. After molding and cooling, the solid melamine fragment 100 as shown in FIG. 1 may be formed. The pulp grains prevent the color bleeding when the colored layer is embedded in the bowl in the future and improve the color.

그 후 도 2a에 도시된 바와 같이 도 1에 도시된 바와 같은 제 1 멜라민 수지 착색층(100)을 엎어서 금형(202)에 재치한다. 그 후 도 2b에 도시된 바와 같이 그 위에 다른 색깔의 착색된 멜라민 수지 분말 재료(204)를 붓고 그 위에 바탕천(206)을 올려놓고 금형에 의해 몰딩 성형한다. 바람직하게는 다른 색깔의 착색된 멜라민 수지 분말 재료에 펄프 알갱이를 첨가한다. 금형의 형틀 온도에 의해 분말이 가열되어 반죽과 같이 점성을 갖는 상태로 되면 금형을 프레스하여 일정한 형태로 성형한다. 이러한 공정을 거치면 바탕천(306) 상에 제 2 멜라민 수지 착색층(304)이 형성되고 그 위에 제 1 멜라민 수지 착색층(300)이 형성되어 있는 도 3a에 도시된 바와 같은 구조가 형성된다. 도 3b는 도 3a의 절단선 a a'를 통해 들여다본 단면도이다. 그 후 도 3a의 구조에서 착색층이 형성된 부분만 절단하여 도 3c와 같은 착색구조체를 형성한다. 그러면 절단된 영역은 크게 두 개의 영역으로 구분된다. 제 1 멜라민 수지 착색층(300)이 있는 영역과 그 외의 영역으로서 제 2 멜라민 수지 착색층(302)만 단독으로 존재하는 영역으로 구분된다. 제 1 멜라민 수지 착색층이 존재하는 영역의 층구조는 제 1 멜라민 수지 착색층 조각의 하측에 제 2 멜라민 수지 착색층이 형성되어 있고 그 하층에는 바탕천이 결합된 구조로 되어 있다. 바탕천은 사후의 공정을 통해 멜라민 수지 착색층이 부스러지지 않게 지탱하는 작용을 한다. 멜라민 수지 착색층의 크기가 그다지 크지 않다면 바탕천에 결합하지 않아도 부스러지지 않으므로 바탕천을 사용하지 않을 수도 있다. 한편 제 1 멜라민 수지 착색층이 있는 영역을 제외한 나머지 영역은 제 2 멜라민 수지 착색층만 형성되어 있다. 바람직하게는 미리 제 1 멜라민 수지 착색층은 최종적인 층 두께보다 얇게 형성시켜 둔다. 예를 들어, 제 1 멜라민 수지 착색층이 있는 영역은 0.8mm의 두께로 형성시킨 제 1 멜라민 수지 착색층과 그 아래에 형성된 0.2mm의 제 2 멜라민 수지 착색층의 2개의 층으로 형성되어 있고 제 1 멜라민 수지 착색층이 없는 영역은 1mm의 제 2 멜라민 수지 착색층의 1개의 층이 형성되어 있을 수 있다. 표면 측에서 볼 때에는 제 1 멜라민 수지 착색층이 형성된 영역은 상부에 형성된 층인 제 1 멜라민 수지 착색층의 색으로 보이고 제 1 멜라민 수지 착색층 외부의 제 2 멜라민 수지 착색층만 형성된 영역은 제 2 멜라민 수지 착색층의 색으로 보인다. 착색층 구조는 0.5 mm 내지 2.5 mm 정도의 두께로 형성할 수 있다. 바람직하게는 0.8 mm 이상의 두께로 형성하면 작업 도중에 깨지는 것을 방지할 수 있다. Thereafter, as shown in FIG. 2A, the first melamine resin colored layer 100 as shown in FIG. 1 is placed upside down and placed in the mold 202. Thereafter, colored melamine resin powder material 204 of different colors is poured on it, and the base fabric 206 is placed thereon and molded by a mold. Preferably pulp pellets are added to the colored melamine resin powder material of a different color. When the powder is heated by the mold temperature of the mold and becomes viscous like a dough, the mold is pressed to form a constant shape. Through this process, a structure as shown in FIG. 3A in which the second melamine resin colored layer 304 is formed on the base fabric 306 and the first melamine resin colored layer 300 is formed thereon is formed. FIG. 3B is a cross-sectional view taken through the cutting line a a 'of FIG. 3A. Thereafter, only the portion in which the colored layer is formed in the structure of FIG. 3A is cut to form a colored structure as illustrated in FIG. 3C. The cut region is then divided into two regions. It is divided into the area | region in which the 1st melamine resin colored layer 300 exists, and the area | region where only the 2nd melamine resin colored layer 302 exists as another area | region. As for the layer structure of the area | region in which a 1st melamine resin colored layer exists, the 2nd melamine resin colored layer is formed in the lower side of the 1st melamine resin colored layer piece, and the base fabric is bonded to the lower layer. Batang cloth supports the melamine resin colored layer not to be broken through a post process. If the size of the melamine resin colored layer is not very large, the base fabric may not be used because it does not crumble even if it is not bonded to the base fabric. On the other hand, only the 2nd melamine resin colored layer is formed in the remaining area | region except the area | region with a 1st melamine resin colored layer. Preferably, the first melamine resin colored layer is formed thinner than the final layer thickness in advance. For example, the region with the first melamine resin colored layer is formed of two layers of the first melamine resin colored layer formed to a thickness of 0.8 mm and the second melamine resin colored layer having a thickness of 0.2 mm formed thereunder. In the region without one melamine resin colored layer, one layer of the 1 mm second melamine resin colored layer may be formed. As viewed from the surface side, the region in which the first melamine resin colored layer is formed is shown as the color of the first melamine resin colored layer, which is a layer formed on the upper side, and the region in which only the second melamine resin colored layer outside the first melamine resin colored layer is formed is the second melamine. It looks with the color of a resin colored layer. The colored layer structure may be formed to a thickness of about 0.5 mm to about 2.5 mm. Preferably, the thickness of 0.8 mm or more can be prevented from breaking during work.

도 3c에 도시된 바와 같은 착색층 구조가 형성되면 도 4에 도시된 바와 같이 최종적으로 160℃ 내지 180℃ 정도의 온도로 가열한 금형(402)에 용기 본체를 형성할 재료가 되는 멜라민 수지 분말(400)을 올려 놓고 그 위에 도 3의 착색층 구조(404)를 올려 놓고 금형을 프레스하여 성형한다. 그러면 몰딩 성형 되면서 착색층 구조가 용기 본체에 찍혀져서 원하는 무늬 또는 글자가 형성된 도 5에 도시된 바와 같은 용기가 완성된다. 도 5의 f f'의 절단선의 단면을 들여다 보면 도 6과 같은 구조로 되어 있다. 용기 본체를 구성하는 멜라민 수지(400)의 일측면에 바탕천(306) 및 바탕천 상의 제 2 멜라민 착색층(304)와 제 1 멜라민 착색층(300)의 구조가 형성된다. 즉, 금형에 의해 성형되면서 착색층 구조가 표면에 묻혀진 상태가 되는 것이다. When the colored layer structure as shown in FIG. 3C is formed, as shown in FIG. 4, melamine resin powder, which is a material for forming a container body in a mold 402 heated to a temperature of about 160 ° C. to 180 ° C. ( 400 is placed, and the colored layer structure 404 of FIG. 3 is placed thereon, and the mold is pressed to form. The molding layer is then stamped onto the container body while molding, thereby completing the container as shown in FIG. 5 in which a desired pattern or letter is formed. When looking at the cross section of the cutting line of ff 'of FIG. 5, it has a structure like FIG. The base fabric 306 and the second melamine colored layer 304 and the first melamine colored layer 300 on the base fabric are formed on one side of the melamine resin 400 constituting the container body. In other words, the colored layer structure is buried in the surface while being molded by the mold.

도 4의 공정에 있어서 멜라민 착색 구조체를 본체 형성용 멜라민 수지 분말 위에 올려 놓지 않고 반대로 멜라민 착색 구조체를 엎은 형태로 먼저 금형틀에 재치한 후 그 후 본체 형성용 멜라민 수지 분말을 붓고 마찬가지로 몰딩 성형 공정을 통해 용기 본체를 형성할 수도 있다. 이 경우는 용기의 내측면에 무늬가 형성되는 것이 아니라 용기의 외측면에 무늬가 형성된다는 것은 별도의 설명이 필요 없을 것이다. In the process of Fig. 4, the melamine colored structure is not placed on the melamine resin powder for forming the body, but the melamine colored structure is placed on the mold mold in the form of a spilled form, and then the melamine resin powder for the forming of the body is poured. It is also possible to form the container body through. In this case, the pattern is not formed on the inner surface of the container, but the pattern is formed on the outer surface of the container will not need any explanation.

도 1 내지 도 6의 실시예는 2도 인쇄 즉 2가지 색상이 인접하게 결합된 무늬나 글자 등을 형성하는 실시예에 관해 예를 들은 것이다. 2도 인쇄만 예를 들었지만 이러한 실시예로부터 3가지 색상 이상의 색을 갖는 무늬나 글자 등을 형성하는 방법은 자명하므로 별도의 설명은 생략한다. 1 to 6 is an example of an embodiment in which a second degree printing, ie, a pattern or letters in which two colors are adjacently combined, is formed. Only the second-degree printing is given as an example, but a method of forming a pattern or a character having a color of three or more colors is obvious from this embodiment, and thus a separate description is omitted.

한편 단색의 멜라민 수지 착색 구조체를 우선 형성하기 위해 착색된 멜라민 수지 분말 재료를 가열된 금형틀에 붓고 그 위에는 바탕천을 올려놓고 금형에 의해 몰딩 성형한다. 바람직하게는 멜라민 수지 분말 재료에 펄프 알갱이를 첨가한다. 이를 통해 바탕천에 결합된 착색층 조각을 형성한 후 착색층 조각을 바탕천과 함께 오려내어 멜라민 수지 착색 구조체를 준비한다. 착색층 조각의 크기가 크지 않아서 부서질 염려가 없는 경우는 바탕천을 생략할 수 있음은 전술한 바와 같다. 몰딩 성형시의 적정 온도는 160℃ 내지 180℃ 정도이다. 그 후 용기 본체의 금형에 용기 본체 형성용 멜라민 수지 분말을 올려 놓고 그 위에 상기 멜라민 수지 착색구조체를 올려 놓고 형틀 온도에 의해 분말이 가열되어 반죽과 같이 점성을 갖는 상태로 되면 금형을 프레스하여 일정한 형태로 성형함으로써 단색의 무늬나 글자를 갖는 용기가 완성된다. 단색 무늬나 글자만을 갖는 멜라민 수지 용기는 도 1 내지 도 6의 실시예의 2도 인쇄보다 훨씬 간단한 공정을 통해 완성된다. Meanwhile, in order to first form a solid melamine resin colored structure, the colored melamine resin powder material is poured into a heated mold, and a base cloth is placed thereon and molded by a mold. Preferably, pulp grains are added to the melamine resin powder material. After forming the colored layer pieces bonded to the base fabric through this, the colored layer pieces are cut out together with the base fabric to prepare a melamine resin colored structure. As described above, the base fabric may be omitted when the colored layer fragment is not large and there is no fear of breaking. The appropriate temperature at the time of molding molding is about 160 to 180 degreeC. Thereafter, the melamine resin powder for forming the container body is placed on the mold of the container body, and the melamine resin colored structure is placed thereon. When the powder is heated by the mold temperature and becomes viscous like dough, the mold is pressed to form a predetermined shape. By molding with a mold, a container having a monochromatic pattern or letters is completed. The melamine resin container having only a monochromatic pattern or letters is completed through a much simpler process than the second degree printing of the embodiment of FIGS. 1 to 6.

본 발명의 용기는 멜라민 수지에 일정한 두께의 벌크 구조를 갖는 멜라민 수지의 착색층이 바탕천에 결합된 것을 용기의 표면에 파묻음으로써 오래 사용하여도 변색되거나 벗겨지지 않는 반영구적 무늬 또는 글자를 갖는 멜라민 수지 용기를 제공할 수 있다. The container of the present invention is a melamine resin has a semi-permanent pattern or letters that do not discolor or peel off even after long use by burying the colored layer of melamine resin having a bulk structure of a certain thickness and bonded to the base fabric on the surface of the container A resin container can be provided.

나아가 용기 완성 후 별도의 공정을 추가하지 않고 용기를 몰딩 성형하는 공정을 통해 무늬나 글자를 형성하는 효과를 갖는다.Furthermore, after the completion of the container, there is an effect of forming a pattern or letters through the process of molding the container without adding a separate process.

도 1 내지 도 6은 본 발명의 일실시예를 도시한 도면이다.1 to 6 are diagrams showing one embodiment of the present invention.

Claims (7)

멜라민 수지 용기에 있어서,In the melamine resin container, 상기 멜라민 용기 표면의 적어도 일부분에 멜라민 수지 착색층을 포함하는 멜라민 수지 착색구조체가 파묻혀 형성된 것을 그 특징으로 하는Characterized in that the melamine resin colored structure comprising a melamine resin colored layer is buried in at least a portion of the melamine container surface 멜라민 수지 용기Melamine resin container 제 1 항에 있어서,The method of claim 1, 상기 멜라민 수지 착색구조체는 바탕천 상에 멜라민 수지 착색층이 결합되어 있는 것을 그 특징으로 하는The melamine resin colored structure is characterized in that the melamine resin colored layer is bonded on the base fabric 멜라민 수지 용기Melamine resin container 제 1 항 또는 제 2 항에 있어서,The method according to claim 1 or 2, 상기 멜라민 수지 착색층은 그 두께가 0.5 mm 내지 2.5 mm인 것을 그 특징으로 하는The melamine resin colored layer is characterized in that the thickness is 0.5 mm to 2.5 mm 멜라민 수지 용기Melamine resin container 제 1 항 내지 제 2 항에 있어서,The method according to claim 1 or 2, 상기 멜라민 수지 착색층은 복수의 서로 다른 색상의 멜라민 수지 착색층이 결합되어 있는 것을 그 특징으로 하는The melamine resin colored layer is characterized in that the melamine resin colored layer of a plurality of different colors are combined 멜라민 수지 용기Melamine resin container 제 1 항 내지 제 2 항에 있어서,The method according to claim 1 or 2, 상기 멜라민 수지 착색층 내에는 복수의 펄프 알갱이가 포함되어 있는 것을 그 특징으로 하는A plurality of pulp grains are contained in the said melamine resin colored layer, It is characterized by the above-mentioned. 멜라민 수지 용기Melamine resin container 멜라민 수지 용기의 제조 방법에 있어서,In the manufacturing method of a melamine resin container, 착색된 멜라민 수지를 금형에 넣고 그 위에 바탕천을 올려놓고 몰딩 성형에 의해 멜라민 수지 착색층과 상기 바탕천이 결합된 멜라민 수지 착색 구조체를 형성하는 단계와,Placing a colored melamine resin in a mold and placing a base fabric thereon to form a melamine resin colored structure in which the melamine resin colored layer and the base fabric are bonded by molding; 상기 멜라민 수지 착색층과 상기 멜라민 수지 착색층에 직접 접촉하고 있는 부분의 바탕천을 함께 결합된 상태로 오려내는 단계와,Cutting out the melamine resin colored layer and the base fabric of the portion in direct contact with the melamine resin colored layer in a bonded state; 용기 본체 형성용 금형 상에 재치한 용기 본체 형성용 멜라민 수지 상에/하에 오려내진 멜라민 수지 착색구조체를 재치하고 금형에 의해 몰딩 성형하여 용기를 형성하는 단계를 포함하는And placing the melamine resin colored structure cut out on and under the melamine resin for container body forming on the mold for forming the container body, and molding molding by means of a mold to form a container. 멜라민 수지 용기의 제조 방법. Method for producing a melamine resin container. 멜라민 수지 용기의 제조 방법에 있어서,In the manufacturing method of a melamine resin container, 착색된 멜라민 수지 분말을 금형에 넣고 몰딩 성형하여 제 1 착색층 조각을 형성하는 단계와,Inserting the colored melamine resin powder into a mold and molding to form a first colored layer piece, 상기 제 1 착색층 조각 상에 제 2 착색층 형성용 착색된 멜라민 수지를 놓고 그 위에 바탕천을 올려놓고 몰딩 성형하여 제 1 착색층과 제 2 착색층의 결합된 착색층과 상기 바탕천이 결합된 구조를 형성하는 단계와,Put the colored melamine resin for forming the second colored layer on the first colored layer piece, and put the base fabric on it and molding molding to combine the combined colored layer of the first colored layer and the second colored layer and the base fabric Forming a, 상기 멜라민 수지 착색층과 상기 멜라민 수지 착색층에 직접 접촉하고 있는 부분의 바탕천을 결합된 상태로 오려 내는 단계와,Cutting out the base fabric of the portion in direct contact with the melamine resin colored layer and the melamine resin colored layer in a bonded state; 오려낸 멜라민 수지 착색층과 바탕천의 결합 구조를 용기 본체 형성용 멜라민 수지 반죽 상에/하에 재치하고 금형에 의해 몰딩 성형하여 용기를 형성하는 단계를 포함하되,Mounting the cut structure of the cut melamine resin colored layer and the base fabric on / under the melamine resin dough for forming the container body and molding the mold by a mold to form a container; 상기 제 1 착색층은 제 2 착색층보다 그 두께가 얇은 것을 그 특징으로 하는 The first colored layer is thinner than the second colored layer, characterized in that 멜라민 수지 용기의 제조 방법. Method for producing a melamine resin container.