KR20030072596A - 폴리디알킬실록산 및 지방산에 의한 광물 충전제의 처리방법, 생성된 소수성 충전제 및 통기성 필름용중합체에서의 이들의 용도 - Google Patents
폴리디알킬실록산 및 지방산에 의한 광물 충전제의 처리방법, 생성된 소수성 충전제 및 통기성 필름용중합체에서의 이들의 용도 Download PDFInfo
- Publication number
- KR20030072596A KR20030072596A KR10-2003-7009349A KR20037009349A KR20030072596A KR 20030072596 A KR20030072596 A KR 20030072596A KR 20037009349 A KR20037009349 A KR 20037009349A KR 20030072596 A KR20030072596 A KR 20030072596A
- Authority
- KR
- South Korea
- Prior art keywords
- filler
- film
- treated
- weight
- polydialkylsiloxane
- Prior art date
Abstract
Description
기준 | 종래 기술 | 기준 | 종래 기술 | 기준 | 발명 | 발명 | 발명 | 발명 | 발명 | ||
테스트 N° | 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 | 10 | |
방법 | 처리 | - | 1% 스테아린 | 0.05% 실란 | 1% 스테아린 + 0.05% 실란 | 0.05% PDMS | 0.05% PDMS + 1% 스테아린 | 0.05% PDMS + 1% 스테아린(동시) | 0.03% PDMS + 0.6% 스테아린 | 0.05% PDMS + 1.3% 스테아린 | 0.05% PDMS + 1.2% 베헨산 |
충전제 | "휘징 방법":a)혼탁 지수 | 0.0 | 1.0 | 0.0 | 1.0 | 0.0 | 1.0 | 1.0 | 0.9 | 0.95 | 1.0 |
b)발포 지수 | 0.0 | 0.8 | 0.0 | 0.75 | 0.0 | 0.8 | 0.9 | 0.8 | 0.9 | 0.9 | |
습기 픽업(mg/㎡) | 0.95 | 0.45 | 0.88 | 0.43 | 0.80 | 0.39 | 0.42 | 0.42 | 0.37 | 0.40 | |
화합물 | MVR(㎤/10 분) | 5.2 | 9.3 | 6.2 | 9.5 | 6.1 | 9.2 | 9.4 | 9.7 | 9.1 | 9.2 |
열 안정성(cm) | 10 | 23 | 6 | 23 | 6 | 23 | 20 | 20 | 22 | 23 | |
필름 | 반점 지수 | 31.2 | 21.1 | 33.3 | 21.0 | 29.7 | 7.6 | 7.8 | 9.9 | 9.1 | 8.4 |
PDMS: 폴리디메틸실록산 |
Claims (33)
- 광물 충전제가 중합체에 혼입되기에 적합하게 하는 소수성 특성을 광물 충전제에 부여함으로써 소위 "통기성" 필름, 특히 폴리올레핀(들)의 필름을 제조하기 위한 광물 충전제의 처리 방법으로서, 충전제의 표면 처리를 2 단계로 수행하고, 제1 단계(예비 처리)는 1종 이상의 폴리디알킬실록산에 의한 처리를 포함하며, 제2 단계는 탄소 원자 수가 10 이상인 1종 이상의 지방산에 의한 처리를 포함하고, 이 2 단계는 동시에 수행될 수 있는 것인 방법.
- 제1항에 있어서, 상기 두 첨가를 동시에 수행할 수 있지만, 지방산이 충전제와 먼저 접촉하지 않도록 신중하게 처리하는 것인 방법.
- 제2항에 있어서, 폴리디알킬실록산을 먼저 첨가한 직후, 지방산을 첨가하는 것인 방법.
- 제1항에 있어서, 별개의 2 단계로 조작을 수행하는, 즉 폴리디알킬실록산을 첨가한 다음, 지방산을 첨가하는 것인 방법.
- 제1항 내지 제4항 중 어느 한 항에 있어서, 대리석 또는 방해석 또는 이의 혼합물과 같은 충전제를 처리하는 것인 방법.
- 제1항 내지 제4항 중 어느 한 항에 있어서, 충전제를 처리하는, 예컨대 침전된 탄산칼슘, 활석, 카올린, 수산화마그네슘, 점토, 실리카, 알루미나, 황산바륨, 운모, 산화칼슘, 산화알루미늄 및 이의 혼합물을 처리하는 것인 방법.
- 제1항 내지 제6항 중 어느 한 항에 있어서, 화학식 (R)3-Si-O-[(R)2-Si-O-]n-Si-(R)3[이때, R은 C1-C4 알킬기임]의 폴리디알킬실록산을 사용하는 것인 방법.
- 제7항에 있어서, 알킬기 R은 메틸 라디칼인 것인 방법.
- 제8항에 있어서, 폴리디메틸실록산은 동점도가 50 내지 100,000 cSt, 바람직하게는 300 내지 5,000 cSt, 보다 바람직하게는 약 1,000 cSt인 방법.
- 제1항 내지 제9항 중 어느 한 항에 있어서, 지방산으로서 탄소 원자 수가 10 이상인 임의의 지방산, 보다 바람직한 방식에서는 스테아르산, 팔미트산, 베헨산 또는 이의 혼합물을 사용할 수 있는 것인 방법.
- 제1항 내지 제10항 중 어느 한 항에 있어서, 방법의 실시를 하기 단계에 의해 수행하는 것인 방법:- 연마된 충전제를 장입한 고속 혼합기를 사용하는 단계,- 폴리디알킬실록산을 약 100℃의 온도에서 5 분에 걸쳐서 첨가하는 단계, 및 이 5 분의 말미에,- 지방산을 첨가하는 단계.
- 제1항 내지 제11항 중 어느 한 항에 있어서, 대리석 또는 방해석 또는 이의 혼합물은 충전제로서, 폴리디메틸실록산은 폴리디알킬실록산으로서, 그리고 스테아린은 탄소 원자 수가 10 이상인 지방산으로서 사용하는 것인 방법.
- 제1항 내지 제12항 중 어느 한 항에 있어서, 건조 충전제의 중량을 기준하여 폴리디알킬실록산 100 내지 2,000 ppm, 바람직하게는 200 내지 1,000 ppm, 보다 바람직한 방식에서는 약 500 ppm을 사용하는 것인 방법.
- 제1항 내지 제13항 중 어느 한 항에 있어서, 건조 충전제의 중량을 기준하여 지방산 0.6% 내지 1.4%, 바람직하게는 0.8% 내지 1.2%를 사용하는 것인 방법.
- 제1항 내지 제14항 중 어느 한 항의 방법으로 처리된 광물 충전제.
- 제15항에 있어서, 광물 충전제는 대리석, 방해석, 침전된 탄산칼슘, 활석, 카올린, 수산화마그네슘, 점토, 실리카, 알루미나, 황산바륨, 운모, 산화칼슘, 수산화칼슘, 산화알루미늄 또는 이의 혼합물 중에서 선택되고, 바람직하게는 대리석, 방해석 또는 이의 혼합물 중에서 선택되는 것인 광물 충전제.
- 제16항에 있어서, 광물 충전제는 고 유동성, 즉 "파일법(pile method)"으로 불리우는 방법에 의해 측정된 경사각률이 0.98 이하이고, 비표면적이 2 내지 6 ㎡/g이며, 그래뉼로메트리 탑 커트(granulometry top cut)가 10 ㎛ 미만, 바람직하게는 8 ㎛ 미만인 광물 충전제.
- 제16항에 있어서, 광물 충전제는 고 소수성, 즉 혼탁 지수가 0.9 내지 1이고, 발포 지수가 0.7 내지 1이며, 이 두 값이 소위 "휘징법(whizzing method)"에 의해 측정되고, 이들은 저 습기 픽업, 즉 습기 픽업법으로 공지된 방법에 의해 측정하였을 때 0.42 mg/㎡ 이하의 습기 픽업을 갖는 것인 광물 충전제.
- 임의의 공업 분야, 특히 충전제의 소수성 특성이 필요한 분야에서의 제18항에 따라 처리된 충전제의 용도.
- 소위 통기성 필름의 제조에서의 제18항에 따라 처리된 충전제의 용도.
- 전술한 유형의 1 이상의 광물 충전제를 포함하는 폴리올레핀(들)의 소위 "통기성" 필름의 제조 방법으로서, 상기 충전제는 제18항의 충전제인 방법.
- 제21항에 있어서, 중합체 매트릭스는 폴리올레핀 중에서 단독으로 또는 혼합물로 선택되고, 상기 폴리올레핀은 저밀도 선형 폴리에틸렌, 저밀도 폴리에틸렌, 고밀도 폴리에틸렌 및 폴리프로필렌 중에서 선택될 수 있는 것인 방법.
- 제21항 또는 제22항에 있어서, 총 중량에 대하여 처리된 충전제 20 중량% 내지 80 중량%, 바람직하게는 45 중량% 내지 60 중량%, 특히 약 50 중량%를 함유하는 마스터배치 또는 화합물을 생성하는 것인 방법.
- 제21항 내지 제23항 중 어느 한 항에 있어서, 상기 중합체는 필름의 형태로 하고, 상기 필름은 일축 또는 이축 연신(또는 배향)을 행하는 것인 방법.
- 제21항 내지 제24항 중 어느 한 항의 방법에 의해 비연신 상태 또는 일축 또는 이축 연신된 상태로 얻어진 필름.
- 제25항에 있어서, 필름은 "반점 뷰어법(mottling viewer method)"으로서 언급되는 방법에 따라 측정된 반점 지수가 10 미만인 필름.
- 제26항의 1 이상의 필름을 포함하는 물품으로서, 특히 1회용 기저귀 및 유사품과 같이 물 또는 수성 유체를 흡수하는 산물을 포함하는 것인 물품.
- 제1항 내지 제14항 중 어느 한 항의 방법의 실시에 의하여 얻어진 폴리올레핀(들) 및 충전제(들)의 마스터배치 또는 화합물.
- 제28항에 있어서, ISO 1133에 따라 측정하였을 때, 용융 부피-유속이 9 ㎤/10 분(온도 190℃, 하중 5 kg, 다이 직경 2.095 mm)이고, 고 열 안정성, 즉 스트립법(strip method)으로 알려진 방법에 따라 비 변색된 스트립의 길이로 표현되는 열적 안정성이 20 cm 이상인 폴리올레핀(들) 및 충전제(들)의 마스터배치 또는 화합물.
- 소위 통기성 필름의 제조에서의 제28항 또는 제29항의 마스터배치의 용도.
- 제21항 내지 제24항 중 어느 한 항에 있어서, 충전제는 제18항의 광물 충전제이고, 마스터배치는 제29항의 마스터배치인 폴리올레핀(들)의 소위 "통기성" 필름의 제조 방법.
- 제17항 또는 제18항의 1 이상의 충전제를 필름 이외의 형태로도 함유하는 폴리올레핀 물품.
- 임의의 공업 분야, 특히 충전제의 소수성 특성이 필요한 분야에서의 제25항또는 제26항의 필름 또는 제32항의 물품의 용도.