KR20010110285A - Process for preparing aluminum decorative elements with thermal adhesive type - Google Patents

Process for preparing aluminum decorative elements with thermal adhesive type Download PDF

Info

Publication number
KR20010110285A
KR20010110285A KR1020010073315A KR20010073315A KR20010110285A KR 20010110285 A KR20010110285 A KR 20010110285A KR 1020010073315 A KR1020010073315 A KR 1020010073315A KR 20010073315 A KR20010073315 A KR 20010073315A KR 20010110285 A KR20010110285 A KR 20010110285A
Authority
KR
South Korea
Prior art keywords
aluminum
applying
heat
coating
baking
Prior art date
Application number
KR1020010073315A
Other languages
Korean (ko)
Inventor
염근창
Original Assignee
염근창
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 염근창 filed Critical 염근창
Priority to KR1020010073315A priority Critical patent/KR20010110285A/en
Publication of KR20010110285A publication Critical patent/KR20010110285A/en

Abstract

본 발명은 기존에 시판되고 있는 금속 스터드 보다도 펄 색상이 발현되고, 아름답고, 심미감이 있는 색상을 발현할 수 있는 열 부착형 알루미늄 장식물 소재의 제조방법에 관한 것이다.The present invention relates to a method for producing a heat-attached aluminum decorative material capable of expressing a pearl color and expressing a beautiful and aesthetic color than a conventional metal stud.

본 발명의 방법은 옵셋 인쇄 방식과 도료 스프레이 방식을 결합하여 장식물 제품의 광택, 색상, 부착력 등을 한층 향상시킨 효과가 있다.The method of the present invention has an effect of further improving the gloss, color, adhesion, etc. of the decorative product by combining the offset printing method and the paint spray method.

본 발명에 따른 열 부착형 알루미늄 장식물 소재는 그 모양에 있어서 지름이 2 내지 10 mm 크기의 위로 볼록한 원형 형태, 직사각형 형태, 별 모양 형태, 인조 다이아몬드 형태, 정사각형 등 여러 모양으로 금형 속에서 프레스의 펀칭에 의해 제조되어 사용할 수 있다.The heat-attachable aluminum decorative material according to the present invention is punched in the mold in various shapes, such as a convex circular shape, a rectangular shape, a star shape, an artificial diamond shape, a square shape having a diameter of 2 to 10 mm in shape, and the like. It is manufactured by and can be used.

Description

열 부착형 알루미늄 장식물 소재의 제조방법{Process for preparing aluminum decorative elements with thermal adhesive type}Process for preparing aluminum decorative elements with thermal adhesive type

본 발명은 열 부착형 알루미늄 장식물 소재의 제조방법에 관한 것이다. 더욱 상세하게는, 기존에 시판되고 있는 금속 스터드(metal stud) 보다도 펄 색상이 발현되고, 아름답고, 심미감이 있는 색상을 발현할 수 있는 열 부착형 알루미늄 장식물 소재의 제조방법에 관한 것이다.The present invention relates to a method for producing a heat-attach aluminum decorative material. More specifically, the present invention relates to a method for producing a heat-attached aluminum decorative material capable of expressing a pearl color and expressing a beautiful and aesthetic color than a conventional metal stud.

종래 알루미늄 금속을 기본 재질로 하여 하면에 고열 용융형 접착제를 부착시키고, 상면에는 보통 양극 산화(anodizing) 도금 처리 또는 옵셋 인쇄로 잉크를 도포하여 반짝이는 색상을 발현시켜서 알루미늄 표면의 광택과 옵셋 잉크의 반투명한 색상이 조화된 재료를 여러 가지 모양으로 새겨진 금형에 넣고 프레스(일명 power press)로 타공하여 제조하여 왔다.A high-temperature melting adhesive is attached to the lower surface by using aluminum metal as a base material, and the upper surface is usually coated with anodizing plating or offset printing to express shiny colors by applying the shiny color of the aluminum surface. Translucent color harmonized materials have been manufactured in various molds and punched with a press (aka power press).

그러나, 이러한 종래의 방법은 알루미늄 금속의 광택을 활용할 수는 있으나, 색상이 표면에서만 발현되어 색감이 단조롭고, 세탁시 부착성이 탈락되거나 표면의 색상이 변색되는 등의 여러 문제점이 있었다.However, this conventional method can utilize the gloss of aluminum metal, but the color is expressed only on the surface, the color is monotonous, there are a number of problems such as dropping the adhesion when washing or discoloration of the surface.

따라서, 본 발명자는 종래의 이와 같은 문제점을 해소하기 위하여 예의 연구를 거듭한 결과, 종래 기술의 옵셋 인쇄 방식과 도료 스프레이 방식을 결합하게 되면 장식물 제품의 광택, 색상, 부착력 등이 한층 향상될 수 있음을 알게 되어 본 발명을 완성하게 된 것이다.Accordingly, the present inventors have made intensive studies to solve such problems in the related art, and when the offset printing method and the paint spray method of the prior art are combined, the gloss, color, and adhesion of the decorative product may be further improved. The present invention is to complete the present invention.

즉, 본 발명은 종래의 금속 스터드 제품보다도 펄 색상이 발현되고 아름답고 심미감이 있는 색상으로, 보는 각도에 따라서 표면에서 이중으로 색상이 발현되는 특성이 있으며, 세탁 시에도 본래의 색상과 부착력에 결함이 나타나지 않는 열 부착형 장식물 소재를 제조하는 방법을 제공하는데 그 목적이 있는 것이다.In other words, the present invention is a color of pearl color is expressed more beautiful and aesthetic than conventional metal stud products, there is a characteristic that the color is expressed on the surface according to the viewing angle, the defect in the original color and adhesion even when washing It is an object of the present invention to provide a method for manufacturing a heat-resistant decorative material that does not appear.

이와 같은 목적을 달성하기 위한 수단은 다음과 같다. 즉, 본 발명에 따른 열 부착형 알루미늄 장식물 소재를 제조하는 방법은,Means for achieving this purpose are as follows. That is, the method of manufacturing a heat-attach aluminum decorative material according to the present invention,

알루미늄 금속 표면 상면에 비닐 수지, 메틸이소부틸케논 또는 이소포론을 주성분으로 하는 알루미늄 금속 전용 프라이머를 도포하는 단계;Applying an exclusive primer for aluminum metal mainly composed of vinyl resin, methyl isobutyl kenone or isophorone on the upper surface of the aluminum metal surface;

상기 프라이머 상면에 아크릴계를 주성분으로 하는 내열성 바탕 도료를 옵셋 방식에 의해 도포하는 단계;Applying a heat-resistant base paint mainly composed of acryl based on the upper surface of the primer by an offset method;

상기 바탕 도료 상면에 아크릴 수지와 멜라민 수지를 주성분으로 하는 1액형 열 경화형 혼합수지에 펄이 함유된 도료를 분사 방식에 의해 균일하게 도포하는 단계;Uniformly applying a paint containing pearl on the upper surface of the base paint to a one-component thermosetting mixed resin mainly containing an acrylic resin and a melamine resin by a spray method;

상기 펄 도료 상면에 아크릴 수지와 멜라민 수지를 주성분으로 하는 1액형 열 경화형 투명도료를 분사 방식에 의해 도포하는 단계;Applying a one-part type thermosetting transparent coating containing acrylic resin and melamine resin as a main component on the upper surface of the pearl paint by a spray method;

상기 알루미늄 금속 표면의 하면에 프라이머를 도포한 후 통상의 방식으로 열 용융형 접착제를 부착시키는 단계; 및Applying a primer to a lower surface of the aluminum metal surface and then attaching the hot melt adhesive in a conventional manner; And

이로부터 얻어진 알루미늄 금속 제품을 금형 안에 넣고 프레스에 의해 여러 가지 모양으로 타공에 의해 성형하는 것으로 이루어짐을 특징으로 한다.The aluminum metal product thus obtained is put into a mold, and is formed by punching into various shapes by pressing.

이하 본 발명을 더욱 상세히 설명하면 다음과 같다.Hereinafter, the present invention will be described in more detail.

본 발명에 의하면, 알루미늄 금속 표면 상면에 해당 알루미늄 소재 및 펄 도료와의 부착성을 향상시키기 위하여 비닐 수지, 메틸이소부틸케톤 또는 이소포론을 주성분으로 하는 알루미늄 금속 전용 프라이머를 롤러 등을 이용하여 2 내지 5 ㎛의 두께로 도포한다. 그리고, 150 내지 180℃에서 20 내지 30분 동안 소부 건조를 실시한다.According to the present invention, in order to improve the adhesion between the aluminum material and the pearl paint on the upper surface of the aluminum metal surface, a primer for exclusive use of an aluminum metal mainly composed of vinyl resin, methyl isobutyl ketone or isophorone is used, using a roller or the like. Apply to a thickness of 5 μm. Then, bake drying is performed at 150 to 180 ° C. for 20 to 30 minutes.

여기서, 온도는 상기 범위 내에서 열을 가해 주어야 열 경화형 수지가 경화되어 강도가 발현되며, 층과 층이 서로 결합력이 유지되나, 온도 및 시간이 상기 범위를 벗어날 경우에는 수지 자체가 열화되어 오히려 부착력 및 강도가 약해지게 된다.Here, the temperature should be heated within the above range, the heat-curable resin is cured to express strength, and the bonding strength between the layers and layers is maintained, but when the temperature and time are out of the range, the resin itself is deteriorated and the adhesion force rather than And strength is weakened.

상기 알루미늄 금속 전용 프라이머 도막 상면에 내열성이 양호한 아크릴계를 주성분으로 하는 불투명성의 바탕 도료를 옵셋 방식에 의해 3 내지 5 ㎛의 두께로 도포하고, 150 내지 180℃에서 10 내지 30분간 소부 건조시킨다.An opaque base paint mainly composed of acrylic having good heat resistance on the upper surface of the primer coating film exclusively for aluminum metal is applied by a thickness of 3 to 5 μm by an offset method, and baked at 150 to 180 ° C. for 10 to 30 minutes.

이어서, 상기 바탕 도막 상면에 아크릴 수지와 멜라민 수지를 주성분으로 하는 1액형 열 경화형 혼합 수지에 펄을 첨가한 도료를 스프레이 건(spray gun)을 이용해서 분사 방식에 의해 10 내지 20㎛의 두께로 도포한 후, 150 내지 180℃에서 5내지 10분 동안 소부 건조를 실시한다.Subsequently, a coating material in which pearl was added to the one-component thermosetting mixed resin containing acrylic resin and melamine resin as a main component was applied to the base coating film by spraying using a spray gun to a thickness of 10 to 20 μm. After that, the baking is carried out at 150 to 180 ° C. for 5 to 10 minutes.

이때, 온도는 가급적 상기 범위에서 열을 가해 주는 것이 좋으며, 유기 용제가 제거되고 완전경화가 되지 않는 상태로 층과 층이 서로 결합력이 유지되도록 하며, 온도 및 시간이 상기 범위를 벗어나게 할 경우에는 수지 자체가 열화되어 오히려 부착력 및 강도가 약해지게 된다.At this time, it is preferable to apply heat in the above-mentioned range as much as possible, and to maintain the bonding strength between the layers in a state in which the organic solvent is removed and not completely cured, and when the temperature and time are out of the range, It degrades itself, but rather weakens adhesion and strength.

그리고, 상기 펄 도막 상면에 아크릴 수지와 멜라민 수지를 주성분으로 하는 1액형 열 경화형 투명 도료를 스프레이 건으로 10 내지 20㎛의 두께로 도포한 후, 150 내지 180℃의 온도 범위에서 20 내지 30분 동안 최종적으로 소부 건조를 실시한다.Then, a one-component thermosetting transparent paint mainly containing an acrylic resin and a melamine resin on the upper surface of the pearl coating film was applied with a spray gun at a thickness of 10 to 20 μm, and finally, at a temperature range of 150 to 180 ° C. for 20 to 30 minutes. Baking is carried out.

한편, 상기 알루미늄 금속 표면의 하면은 고열 용융형 접착제를 부착시키게 되는데 이 접착제가 잘 부착되도록 폴리비닐부탄올을 주성분으로 하는 프라이머 또는 페인트 하도료인 워시-프라이머를 약 10㎛의 두께로 칠한 후, 폴리아미드 또는 폴리우레탄을 주성분으로 하는 열 용융형 접착제를 150 내지 180℃의 온도 범위에서 열을 가하여 100 내지 200㎛의 두께로 접착시킨다.On the other hand, the lower surface of the aluminum metal surface is attached to a high-temperature melting adhesive, the paint-primer, which is a primer or a paint undercoat mainly containing polyvinyl butanol to a thickness of about 10㎛ so that the adhesive is attached well, and then A hot melt adhesive mainly composed of amide or polyurethane is bonded to a thickness of 100 to 200 mu m by applying heat in a temperature range of 150 to 180 deg.

이렇게 하여 얻어진 소재를 여러 가지 모양으로 새겨진 금형에 넣고, 파우더 프레스로 타공하면 본 발명에 따른 열 부착형의 알루미늄 장식물 소재가 제조되게 된다.The material thus obtained is placed in a mold engraved in various shapes, and punched with a powder press to produce a heat-attached aluminum decorative material according to the present invention.

이와 같은 방법으로 펄을 이용한 소재를 제조할 경우에는 알루미늄 소재 표면 상면의 도막 두께를 얇게 할 수 있고, 도막의 부착력도 크게 향상시킬 수 있으며, 금형에 넣고 프레스로 타공시 도막 표면이 깨지지 않고 세탁 40회 후에도 도막표면이 본래의 색상과 형태를 그대로 유지하는 양호한 부착성을 갖게 된다.When manufacturing materials using pearl in this way, it is possible to reduce the thickness of the coating film on the upper surface of the aluminum material, and to greatly improve the adhesion of the coating film. Even after the coating, the surface of the coating film has good adhesion that retains its original color and shape.

이하 본 발명을 실시예를 들어 더욱 구체적으로 설명하면 다음과 같다.Hereinafter, the present invention will be described in more detail with reference to Examples.

실시예Example

알루미늄 금속 소재 표면상에 해당 알루미늄 소재와의 부착성을 높이기 위하여 비닐 수지를 주성분으로 하는 알루미늄 금속 전용 프라이머(삼영잉크사제 프라이머 801제품)를 롤러를 이용해서 3 ㎛의 두께로 칠하고, 170℃의 온도에서 20분간 소부 건조시켰다.In order to increase the adhesion with the aluminum material on the surface of the aluminum metal material, an exclusive primer for aluminum metal (primary 801 manufactured by Samyoung Ink), which contains vinyl resin as a main component, is coated with a roller to a thickness of 3 μm, Baked for 20 minutes at the temperature.

다음에 상기 알루미늄 금속 전용 프라이머 상면에 내열성이 양호한 아크릴계를 주성분으로 하는 불투명성의 바탕 잉크를 4 ㎛의 두께로 도포하고, 170℃에서 20분 동안 소부 건조를 실시하였다.Subsequently, an opaque base ink mainly composed of an acrylic system having good heat resistance on the upper surface of the aluminum metal primer was applied at a thickness of 4 μm, followed by baking for 20 minutes at 170 ° C.

상기 바탕 도막 상면에 아크릴 수지와 멜라민 수지를 주성분으로 하는 1액형 열 경화성 혼합수지에 펄을 첨가한 도료를 스프레이 건을 이용해서 10㎛의 두께로 도포한 후, 160℃에서 10분 동안 소부 건조를 실시하였다.Applying paint with pearl added to the one-component thermosetting mixed resin containing acrylic resin and melamine resin as a main component on the upper surface of the base coating film using a spray gun, and then baking the baking at 160 ° C. for 10 minutes. Was carried out.

상기 펄 도막 상에 아크릴 수지와 멜라민 수지를 주성분으로 하는 1액형 열 경화형 투명 도료를 스프레이 건을 이용해서 10㎛의 두께로 도포하고, 170℃의 온도 범위에서 20분 동안 소부 건조를 실시하였다.On the pearl coating film, a one-component thermosetting transparent coating containing acrylic resin and melamine resin as a main component was applied at a thickness of 10 μm using a spray gun, and baked baking was carried out for 20 minutes at a temperature range of 170 ° C.

알루미늄 금속 소재의 하면은 프라이머를 10㎛, 열 용융형 접착제를 170℃의 온도에서 열을 가하여 100㎛의 두께로 접착시켰다.The lower surface of the aluminum metal material was bonded to a thickness of 100 μm by applying a primer to 10 μm and heat-melting adhesive at a temperature of 170 ° C.

이렇게 하여 얻어진 소재를 금형에 넣고 파워 프레스로 타공하여 알루미늄 장식물 소재를 얻었다.The material thus obtained was placed in a mold and perforated with a power press to obtain an aluminum decorative material.

상기 소재에 대한 세탁 시간을 1시간을 1회 기준으로 세제를 첨가하여 물세탁 건조를 40회 반복실험 후에도 알루미늄의 펄 도막 표면이 본 색상과 형태를 그대로 유지하는 양호한 부착성을 나타내었다. 섬유 부착물의 제품 규격인 세탁 20회 기준을 2배 이상 유지하는 양호한 특성을 나타내었으며, 종래 방법으로 실시한 제품은 세탁 10회에서부터 알루미늄 위의 도막의 이탈 현상이 발생되었다.The washing time for the material showed a good adhesion that the pearl coating film surface of aluminum maintains the present color and shape even after 40 times of repeated washing with water by adding a detergent on a one-hour basis. A good property of maintaining the standard of 20 times of washing, which is the product standard of the fiber adherend, was exhibited, and the product carried out by the conventional method had a peeling phenomenon of the coating on aluminum from 10 times of washing.

본 발명의 방법에 의해 제조된 열 부착형 알루미늄 장식물 소재는 주로 의복에 사용되며, 내열성과 내마모성, 특히 섬유와의 부착성이 요구되는 특성을 가지며, 본 발명에서 사용하는 방법은 옵셋 잉크가 알루미늄 소재 표면과 잘 부착되도록 하는 금속 프라이머의 사용과 바탕 도료가 얇게 도포되는 특성을 잘 활용한 것이고, 도료 표면의 광택이 잘나고 아크릴계 등의 내열성 및 내마모도가 양호한 도료를 선택하여 내열성과 표면 부착성 내마모도를 획기적으로 향상시킨 것이다.The heat-attachable aluminum decorative material produced by the method of the present invention is mainly used in garments, and has properties that require heat resistance and abrasion resistance, especially adhesion to fibers, and the method used in the present invention is that the offset ink is an aluminum material. It utilizes the use of metal primer to adhere well to the surface and the thin coating of the base paint, and selects a paint with good gloss on the surface of the paint and good heat resistance and abrasion resistance such as acrylic. It is a significant improvement.

열 부착형 알루미늄 장식물 소재는 그 모양에 있어서 지름이 2 내지 10 mm 크기의 위로 볼록한 원형 형태, 직사각형 형태, 별 모양 형태, 인조 다이아몬드 형태, 정사각형 등 여러 모양으로 금형 안에서 프레스의 펀칭에 의해 제조가 가능하다.Heat attachable aluminum decorative material can be manufactured by punching in the mold in various shapes such as round shape, rectangular shape, star shape, artificial diamond shape and square shape with diameter of 2 to 10 mm in shape. Do.

Claims (5)

알루미늄 금속 표면 상면에 비닐 수지, 메틸이소부틸케톤, 이소포론 등을 주성분으로 하는 알루미늄 금속 전용 프라이머를 도포하는 단계;Applying an exclusive primer for aluminum metal mainly composed of vinyl resin, methyl isobutyl ketone, isophorone, etc. on the upper surface of the aluminum metal surface; 상기 프라이머 상면에 내열성이 양호한 아크릴계를 주성분으로 하는 불투명성의 바탕 잉크를 옵셋 방식에 의해 도포하는 단계;Applying an opaque base ink mainly composed of acrylic having good heat resistance on the upper surface of the primer by an offset method; 상기 바탕 도료 위에 아크릴 수지와 멜라민 수지를 주성분으로 하는 1액형 열 경화형 혼합수지에 펄을 첨가한 도료를 분사 방식에 의해 도포하는 단계;Applying, by spraying, a paint on which the pearl is added to the one-component thermosetting mixed resin mainly containing an acrylic resin and a melamine resin on the base paint; 상기 펄 도료 상면에 아크릴 수지와 멜라민 수지를 주성분으로 하는 1액형 열 경화형 투명도료를 분사 방식에 의해 도포하는 단계;Applying a one-part type thermosetting transparent coating containing acrylic resin and melamine resin as a main component on the upper surface of the pearl paint by a spray method; 상기 알루미늄 금속 표면의 하면에 프라이머를 도포한 후 통상의 방식으로 열 용융형 접착제를 부착시키는 단계; 및Applying a primer to a lower surface of the aluminum metal surface and then attaching the hot melt adhesive in a conventional manner; And 이로부터 얻어진 알루미늄 금속 제품을 금형 안에 넣고 프레스에 의해 여러 가지 모양으로 타공에 의해 성형하는 것으로 이루어짐을 특징으로 하는 열 부착형 알루미늄 장식물 소재의 제조방법.A method of producing a heat-attached aluminum decorative material, comprising: forming an aluminum metal product obtained therefrom into a mold and molding the same into various shapes by pressing. 제 1항에 있어서, 상기 알루미늄 금속 전용 프라이머의 도포 과정은 그 도막의 두께를 2 내지 5 ㎛로 하고, 150 내지 180℃에서 20 내지 30분 동안 소부 건조를 실시하여서 되는 것을 특징으로 하는 열 부착형 알루미늄 장식물 소재의 제조방법.The heat attaching type according to claim 1, wherein the coating process of the aluminum metal primer is performed by baking the coating film at a thickness of 2 to 5 µm and performing baking for 20 to 30 minutes at 150 to 180 ° C. Manufacturing method of aluminum decoration material. 제 1항에 있어서, 상기 바탕 도료의 도포 과정은 그 도막을 3 내지 5 ㎛의 두께로 도포하고, 150 내지 180℃에서 10 내지 30분간 소부 건조시켜서 됨을 특징으로 하는 열 부착형 알루미늄 장식물 소재의 제조방법.The method of claim 1, wherein the coating process of the base paint is applied to a thickness of 3 to 5 ㎛, the baking by baking for 10 to 30 minutes at 150 to 180 ℃ manufacturing of the heat-attached aluminum decorative material, characterized in that Way. 제 1항에 있어서, 상기 펄 도료의 도포 과정은 그 도막을 10 내지 20㎛의 두께로 도포한 후, 150 내지 180℃에서 5 내지 10분 동안 소부 건조를 실시하여서 됨을 특징으로 하는 열 부착형 알루미늄 장식물 소재의 제조방법.The method of claim 1, wherein the coating process of the pearl paint is heat-attached aluminum, characterized in that by applying the coating to a thickness of 10 to 20㎛, followed by baking for 5 to 10 minutes at 150 to 180 ℃ Manufacturing method of decorative material. 제 1항에 있어서, 상기 투명 도료의 도포 과정은 그 도막을 10 내지 20㎛의 두께로 도포한 후, 150 내지 180℃의 온도 범위에서 20 내지 30분 동안 소부 건조하여서 됨을 특징으로 하는 열 부착형 알루미늄 장식물 소재의 제조방법.The method of claim 1, wherein the coating process of the transparent coating is characterized in that the coating is applied to a thickness of 10 to 20㎛, and then baked for 20 to 30 minutes in a temperature range of 150 to 180 ℃ Manufacturing method of aluminum decoration material.
KR1020010073315A 2001-11-23 2001-11-23 Process for preparing aluminum decorative elements with thermal adhesive type KR20010110285A (en)