KR102672720B1 - 춘추절기용 인조 속눈썹 접착제 조성물 - Google Patents
춘추절기용 인조 속눈썹 접착제 조성물 Download PDFInfo
- Publication number
- KR102672720B1 KR102672720B1 KR1020230162365A KR20230162365A KR102672720B1 KR 102672720 B1 KR102672720 B1 KR 102672720B1 KR 1020230162365 A KR1020230162365 A KR 1020230162365A KR 20230162365 A KR20230162365 A KR 20230162365A KR 102672720 B1 KR102672720 B1 KR 102672720B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- adhesive composition
- styrene
- butyl
- tert
- Prior art date
Abstract
본 발명은 스티렌계 공중합체 25 내지 35 중량%, 화이트 미네랄 오일 5 내지 19 중량%, 폴리이소부틸렌 5 내지 18 중량%, 하이드로카본 수지 50 초과 내지 60 이하 중량%, 안료 0.01 내지 0.05 중량%, 및 항산화제 0.5 내지 1 중량%를 포함하는 춘추절기용 속눈썹 접착제 조성물을 제공한다.
Description
본 발명은 춘추절기용 인조 속눈썹 접착제 조성물에 관한 것이다.
인조 속눈썹은 미용을 위하여 널리 사용되는 도구로서, 속눈썹 사이에 접착하여 눈썹에 매력 포인트를 주는데 사용된다. 인조 속눈썹은 다른 사람들로 하여금 예쁜 눈을 볼 수 있도록 함은 물론 그 눈을 통해 좋은 인상을 받도록 하는 여성 미용도구의 일종이다. 인조 속눈썹은 속눈썹을 길어 보이게 하는 기능을 수행하며, 수요가 점점 증가하는 추세이다.
인조 속눈썹은 인조 모발 내지는 사람의 모발로 만들어진 속눈썹 형상의 미용 도구를 의미한다. 상기 인조 속눈썹은 접착제 또는 접착 테이프 등의 접착 부재를 이용하여 눈꺼풀 등에 직접 부착하여 사용하고 있다.
인조 속눈썹의 사용에 있어서, 사용자의 안검과 인조 속눈썹을 고정시키는 접착제의 접착능은 매우 중요한 요소이다. 인조 속눈썹을 고정하기 위한 접착제는 사용자의 피부에 직접 부착되기 때문에 독성에 따라, 피시술자의 눈가에 피로를 유발하거나 사용자의 피부에 유해한 영향을 줄 수 있다.
현재 시중에 유통중인 대부분의 속눈썹 접착제는 화장품이 아닌 일반 생활화학제품으로 분류되어 있어, 안전기준에 대한 새로운 설정이 필요하다는 요구가 지속적으로 제기되고 있다.
실제로 2017년 한국소비자원에서 시중 유통·판매 중인 '속눈썹 접착제' 20개 제품을 대상으로 유해한 제한물질인 포름알데하이드(Formaldehyde), 톨루엔(Toluene), 벤젠(Benzene)과 화장품 사용금지 물질인 메틸 메타크릴레이트(Methyl methacrylate)의 함량 시험검사와 표시실태를 조사한 결과, 조사대상 20개 중 11개(55.0%)제품에서 기준치를 초과한 유해물질이 검출되어 안전기준에 부적합했다.
포름알데하이드는 11개 제품에서 기준치(20㎎/㎏이하)의 최소 740배~ 2천180배(1만4천800㎎/㎏~4만3천600㎎/㎏)가 검출됐고, 톨루엔은 9개 제품에서 기준치(20㎎/㎏이하)의 1.9배~414.5배(38㎎/㎏~8천290㎎/㎏)가 검출됐다. 포름알데하이드와 톨루엔 중복 검출도 9개 제품에 달했다. 벤젠은 20개 제품 모두 검출되지 않았다.
또한, 화장품에 사용이 금지된 '메틸메타크릴레이트' 역시 20개 중 10개 제품(50.0%)에서 최소 0.01%~0.05%로 검출됐다. 이는 국내에서 화장품 제조에 사용이 금지되어 있으나 일반 생활화학제품인 속눈썹 접착제에 대해서는 규제되고 있지 않아 이에 대한 새로운 안전기준이 필요한 실정이다.
포름알데하이드(Formaldehyde)는 시야를 흐릿하게 하는 등 안구 자극을 유발하고, 안구나 피부에 직접 접촉 시 화학적 화상·따가움 등을 유발할 수 있고, 톨루엔(Toluene)은 안구 접촉 시 충혈과 통증을 동반한 자극을 유발할 수 있으며, 메틸메타크릴레이트(MMA, Methylmethacrylate)는 안구나 피부 접촉 시 자극, 홍반, 통증, 가려움 및 알레르기성 피부반응 등을 유발할 수 있는 물질로서, 전문가들은 이러한 속눈썹 접착제의 잦은 사용을 최대한 자제할 것을 요구하고 있다.
한편, 접착력이 약한 셀프용 접착제는 유해 성분이 적게 함유되어 전체 성분이 공개된 경우가 많은 반면에, 강한 접착력이 요구되는 전문가용 접착제는 전체 성분이 표시되지 않을 뿐 아니라, 포름알데히드 및 톨루엔 등 유해물질을 다량 함유하고 있으며, 사용금지 물질인 메틸메타크릴레이트도 다량 검출되는 등 안전성에서 문제가 심각하다.
속눈썹 연장 시술이나 인조 속눈썹 사용이 어린 학생들에게 일반화되고 있는 현 상황에서, 시중에 유통중인 속눈썹 접착제는 안구 가까이 사용하여 결막염이나 눈가 주위 피부 자극이 우려되며 암 유발 등 건강에 큰 영향을 미치는 성분들로 구성되어 있으므로, 이를 대체할 수 있는 인체에 무해한 저자극성 속눈썹 접착제의 개발이 요구되고 있는 실정이다.
본 발명은, 상술한 종래기술의 문제점을 해소하기 위해 안출된 것으로서,
포름알데히드, 톨루엔, 메틸메타크릴레이트 등의 유해성분을 포함하지 않으며; 가볍고 이물감 없이 깔끔하게 속눈썹을 부착시키며, 건조한 피부에 자극없이 속눈썹을 부착시키며, 건조한 피부에도 우수한 접착력 및 접착 유지력을 제공할 수 있는 춘추절기용 인조 속눈썹 접착제 조성물을 제공하는 것을 목적으로 한다.
상기 목적을 달성하기 위하여, 본 발명은
스티렌계 공중합체 25 내지 35 중량%, 화이트 미네랄 오일 5 내지 19 중량%, 폴리이소부틸렌 5 내지 18 중량%, 하이드로카본 수지 50 초과 내지 60 이하 중량%, 안료 0.01 내지 0.05 중량%, 및 항산화제 0.5 내지 1 중량%를 포함하는 춘추절기용 속눈썹 접착제 조성물을 제공한다.
본 발명의 춘추절기용 인조 속눈썹 접착제 조성물은 포름알데히드, 톨루엔, 메틸메타크릴레이트 등의 유해성분을 포함하지 않으며; 가볍고 이물감 없이 깔끔하게 속눈썹을 부착시키며, 건조한 피부에 자극없이 속눈썹을 부착시키며, 건조한 피부에도 우수한 접착력 및 접착 유지력을 제공하는 효과를 제공한다.
이하에서 본 발명을 상세히 설명한다.
본 발명의 춘추절기용 속눈썹 접착제 조성물은 스티렌계 공중합체 25 내지 35 중량%, 화이트 미네랄 오일 5 내지 19 중량%, 폴리이소부틸렌 5 내지 18 중량%, 하이드로카본 수지 50 초과 내지 60 이하 중량%, 안료 0.01 내지 0.05 중량%, 및 항산화제 0.5 내지 1 중량%를 포함하는 특징을 갖는다.
상기 스티렌계 공중합체로는 SIS(Styrene-Isoprene-Styrene), SBS(Styrene-Butadiene-Styrene), SEBS(Styrene-Ethylene-Butadiene-Styrene), SEPS(StyreneEthylene Propylene Styrene), 및 H-SBC(Hydrogenated SBC)로 이루어진 군으로부터 선택되는 1종 이상이 사용될 수 있다.
상기 스티렌계 공중합체는 예를 들어, 중량평균분자량이 50,000 내지 300,000, 또는 100,000 내지 300,000인 것이 사용될 수 있으나, 이에 한정되는 것은 아니다.
상기 화이트 미네랄 오일은 석유를 정제하여 얻은 오일을 의미한다. 상기 화이트 미넬랄 오일로는 이 분야에 공지된 성분이 제한없이 사용될 수 있다. 상기 화이트 미네랄 오일은 제약, 식품, 화장품 및 퍼스널 케어 제품에 사용하기에 적합한 사양을 충족시키기 위하여 정제된 것을 의미한다.
상기 폴리이소부틸렌은 부틸 고무, PIB 라고도 불리는 비닐 중합체이다. 모든 탄소가 두 개의 메틸 그룹으로 대체된다는 점을 제외하면 구조상 폴리에틸렌 및 폴리프로필렌과 매우 유사하다. 폴리이소부틸렌은 단량체 이소부틸렌으로부터 양이온성 비닐 중합을 통해 제조될 수 있다.
상기 폴리이소부틸렌은 예를 들어, 중량평균분자량이 50,000 내지 300,000, 또는 100,000 내지 300,000인 것이 사용될 수 있으나, 이에 한정되는 것은 아니다.
상기 폴리이소부틸렌 5 이상 내지 15 미만 중량%로 포함될 수도 있다.
상기 하이드로카본 수지는 석유 증류물 및 나프타 크랙커에서 유래한 분획을 포함하는 원유의 (촉매) 분해에서 전형적으로 유래하는 탄화수소 분획의 중합에 의해 생산된다. 상기 하이드로카본 수지로는 C9 석유수지, C5 석유수지, C9 방향족 탄화수소 수지 등을 들 수 있다. 상기 하이드로카본 수지는 중량평균분자량이 50,000 내지 1,000,000, 또는 100,000 내지 300,000인 것이 사용될 수 있으나, 이에 한정되는 것은 아니다.
상기 안료는 검은색 및 유색 안료 및 증량 안료를 포함하는 의미로 사용될 수 있다. 검은색 및 유색 안료가 접착제의 착색 및 부착된 부분이 고광택으로 인하여 번쩍거리지 않도록 하며 자연스러운 느낌을 갖도록 기능한다. 본 발명의 안료는, 형태(구형, 바형(bar), 니들형(needle), 판형, 무정형, 스핀들형(spindle) 등), 입자 크기(에어로졸, 미세입자, 안료 등급 입자 등) 및 그의 입자 구조(다공성, 비다공성 등)에 대한 제한은 없으며, 파우더의 평균 일차 입자 크기는 1 nm 내지 100 ㎛의 범위일 수 있다.
상기 안료로는 예를 들어, 흑색안료가 바람직하게 사용되며, 구체적으로 Manganese ferrite black spinel, 카본블랙 등이 사용될 수 있다. 특히, Manganese ferrite black spinel이 바람직하게 사용될 수 있다.
상기 항산화제는 열, 빛 또는 점착부여 수지와 같은 원료로부터 잔류하는 촉매에 의해 유도된 산소와의 반응에 의해 야기되는 분해로부터 접착제를 보호한다. 상기 항산화제로는 예를 들어, 1,3,5-트리메틸-2,4,6-트리스-(3,5-디-tert-부틸-4-히드록시벤질)-벤젠; 펜타에리트리틸 테트라키스-3(3,5-디-tert-부틸-4-히드록시페닐)-프로피오네이트; n-옥타데실-3(3,5-디-tert-부틸-4-히드록시페닐)-프로피오네이트; 4,4'-메틸렌비스 (2,6-tert-부틸-페놀); 4,4'-티오비스 (6-tert-부틸-o-크레졸); 2,6-디-tert부틸페놀; 6-(4-히드록시페녹시)-2,4-비스(n-옥틸-티오)-1,3,5 트리아진; 디-n-옥틸티오)에틸 3,5-디-tert-부틸-4-히드록시-벤조에이트; 소르비톨 헥사[3-(3,5-디-tert-부틸-4-히드록시-페닐)-프로피오네이트] 등을 들 수 있다.
본 발명의 인조 속준썹 접착제 조성물은 상기 인조 속준썹 접착제 조성물 100 중량부에 대하여, 하기 화학식 1로 표시되는 공중합체 2 내지 5 중량부를 더 포함할 수 있다.
[화학식 1]
상기 식에서, a, b 및 c는 몰분율이고,
상기 a는 0.3 내지 0.5이고, b는 0.3 내지 0.5이며, c는 0.3 내지 0.5이며, a+b+c는 1이다.
상기 공중합체에서 2-(아크릴로일옥시)에틸)트라이메틸암모늄 클로라이드(CAS No: 44992-01-0) 구조단위는 음이온과 양이온을 포함함으로써, 접착제 조성물의 각 성분들이 잘 혼합되게 하며, 특히, 안료 성분의 분산성을 향상시키는 기능을 수행한다. 상기 2-에틸헥실 아크릴레이트(CAS No: 103-11-7) 구조단위는 눈꺼플에 속눈썹의 부착력을 향상시키며, 특히, 속눈썹이 부착된 눈꺼플에 유분이 배출되도라도 부착력을 오래 유지할 수 있게 하여, 속눈썹의 부착 지속성을 향상시키는 기능을 수행한다. 또한, 상기 1,4-부탄디올 비닐에테르(1,4-butanediol vinyl ether CAS No: 17832-28-9) 구조단위는 친수성을 가지므로, 속눈썹이 부착되는 눈꺼풀면에 대한 부착력을 향상시키며, 부착 지속성을 향상시키는 기능을 수행한다. 그러므로, 상기 화학식 1로 표시되는 공중합체를 포함하는 속눈썹 접착제 조성물은 안료의 분산능력 향상에 의해 우수한 품질을 제공하며, 부착력이 향상되며, 및 부착 지속 시간이 증가한다.
상기 화학식 1의 공중합체는 랜덤 공중합체로서, 중량평균분자량이 50,000 내지 1,000,000인 것이 사용될 수 있으며, 더욱 바람직하게는 150,000 내지 350,000, 더 더욱 바람직하게는 200,000 내지 300,000인 것이 사용될 수 있다.
이하, 바람직한 실시예를 통하여 본 발명을 상세하게 설명한다. 그러나 이는 단지 당업계의 통상의 지식을 가진 자에게 발명의 실시를 명확히 하는 목적을 지니며, 본 발명의 권리범위가 이들 실시예에 의해 한정되는 것을 의미하지 않는다.
실시예 1: 춘추절기용 속눈썹 접착제 조성물의 제조
스티렌계 공중합체로서 SBS(Styrene-Butadiene-Styrene) 30 중량%, 화이트 미네랄 오일 8.27 중량%, 폴리이소부틸렌 9 중량%, 하이드로카본 수지로서 C9 석유수지 52 중량%, 안료로서 Manganese ferrite black spinel 0.03 중량%, 및 항산화제 0.7 중량%를 혼합하여 춘추절기용 속눈썹 접착제 조성물을 제조하였다.
실시예 2: 춘추절기용 속눈썹 접착제 조성물의 제조
상기 실시예 1의 접착제 조성물 100 중량부에 대하여, 하기 화학식 1로 표시되는 공중합체 3 중량부를 더 혼합하여 춘추절기용 속눈썹 접착제 조성물을 제조하였다.
<화학식 1의 공중합체의 제조>
반응용매인 에틸벤젠에 2-(아크릴로일옥시)에틸)트라이메틸암모늄 클로라이드(CAS No: 44992-01-0), 2-에틸헥실 아크릴레이트(CAS No: 103-11-7), 및 1,4-부탄디올 비닐에테르(1,4-butanediol vinyl ether CAS No: 17832-28-9)를 0.3:0.4:0.3의 몰비로 첨가하고, 전체 단량체 100 중량부에 노르말 머캡탄 0.5 중량부를 혼합하여 균일하게 만들었다. 상기에서 제조한 중합용액을 10 L/hr의 속도로 20 L 반응기에 투입하면서 100℃의 온도로 중합하고, 휘발조에서 150℃의 온도로 미반응 단량체와 반응용매을 제거하고 세척, 탈수, 건조하여 중량평균분자량이 243,000인 화학식 1의 공중합체를 얻었다.
[화학식 1]
(a=0.3, b=0.4, c=0.3)
비교예 1: 속눈썹 접착제 조성물의 제조
유리제의 반응 용기에 테트라메틸렌에테르 글리콜 78g, 트리렌지인시아네이트 35g 및 반응 촉매로서 카르복실산 비스무트 0.05g을 더하고 80℃에서 60분간 가열 반응시킨 후, 40g의 히드록시에틸아크릴레이트를 더하고 80℃에서 60분간 가열 반응시키고 폴리우레탄 아크릴레이트를 제조했다. 상기에서 얻은 폴리우레탄 아크릴레이트에 이소보로닐 아크릴레이트 120g, 디메틸(메타) 아크릴아미드 60g, 2,4,6-트리메틸벤조일 디페닐포스핀옥사이드 24g, 카본 블랙 0.5 g, 흄드실리카 6g 및 에틸알코올 l0g을 첨가하고 균일한 용액이 될 때까지 5시간, 실온에서 혼합하여 접착제를 제조하였다.
시험예 1: 경화시간 및 접착력 측정
본 발명의 실시예 및 비교예에서 제조한 속눈썹 접착제 조성물의 경화시간을 측정하였다. 또한, 초기 접착력과 접착 유지력을 FINAT 테스트 방법 중 FTM 1(FINAT TEST METHOD NO. 1 - PEEL ADHESION (180°) AT 300 MM PER MINUTE, USING 25 mm wide strips) 및 FTM 8(Resistance to shear from a standard surface)에 준하여 측정하였다. 측정장비는 TA Texture Analyzer(Stable Micro Systems) 및 Shear Tester를 이용하였으며, 25℃, 습도 55%인 조건에서 측정하였다. 측정결과를 하기 표 1에 나타내었다.
| 경화시간 (초) |
초기 접착력 (N) |
접착 유지력(시간) | |
| 비교예 1 접착제 조성물 | 41 | 10 | 57 |
| 실시예 1 접착제 조성물 | 29 | 13 | 66 |
| 실시예 2 접착제 조성물 | 26 | 16 | 76 |
시험예 2: 피부 자극성 평가
상기 본 발명의 실시예 및 비교예에서 제조한 속눈썹 접착제 조성물의 피부 자극성을 평가하기 위하여 20 내지 50대의 여성 30명을 선정하여 만족도 평가를 실시하였다.
평점은 10점 평점법을 사용하였으며, 선호도가 높을수록 높은 점수를 주도록 하였으며, 그 결과는 하기 표 2에나타내었다.
| 눈 따가움 (시술 직후) |
눈 따가움 (30분 후) |
30분 후 안구 건조 |
|
| 비교예 1 접착제 조성물 | 7.2 | 7.0 | 7.1 |
| 실시예 1 접착제 조성물 | 8.0 | 8.1 | 8.0 |
| 실시예 2 접착제 조성물 | 8.6 | 8.8 | 8.6 |
상기 본 발명의 실시예 및 비교예에서 제조한 속눈썹 접착제 조성물의 포름알데히드 방산량을 KS F 3101-2006에 따라 측정하고, 그 결과를 하기 표 3에 나타내었다.
| 포름알데히드 검출량 (ppm) 검출한계 5ppm |
|
| 비교예 1 접착제 조성물 | 1200 ppm |
| 실시예 1 접착제 조성물 | 검출한계 미만 |
| 실시예 2 접착제 조성물 | 검출한계 미만 |
Claims (5)
- 스티렌계 공중합체 25 내지 35 중량%, 화이트 미네랄 오일 5 내지 19 중량%, 폴리이소부틸렌 5 내지 18 중량%, 하이드로카본 수지 50 초과 내지 60 이하 중량%, 안료 0.01 내지 0.05 중량%, 및 항산화제 0.5 내지 1 중량%를 포함하는 인조 속눈썹 접착제 조성물로서,
상기 인조 속눈썹 접착제 조성물 100 중량부에 대하여, 하기 화학식 1로 표시되는 공중합체 2 내지 5 중량부를 더 포함하는 것을 특징으로 하는 춘추절기용 인조 속눈썹 접착제 조성물.
[화학식 1]
상기 식에서, a, b 및 c는 몰분율이고,
상기 a는 0.3 내지 0.5이고, b는 0.3 내지 0.5이며, c는 0.3 내지 0.5이며, a+b+c는 1이다. - 제1항에 있어서,
상기 스티렌계 공중합체는 SIS(Styrene-Isoprene-Styrene), SBS(Styrene-Butadiene-Styrene), SEBS(Styrene-Ethylene-Butadiene-Styrene), SEPS(StyreneEthylene Propylene Styrene), 및 H-SBC(Hydrogenated SBC)로 이루어진 군으로부터 선택되는 1종 이상인 것을 특징으로 하는 춘추절기용 인조 속눈썹 접착제 조성물. - 제1항에 있어서,
상기 항산화제는 1,3,5-트리메틸-2,4,6-트리스-(3,5-디-tert-부틸-4-히드록시벤질)-벤젠; 펜타에리트리틸 테트라키스-3(3,5-디-tert-부틸-4-히드록시페닐)-프로피오네이트; n-옥타데실-3(3,5-디-tert-부틸-4-히드록시페닐)-프로피오네이트; 4,4'-메틸렌비스 (2,6-tert-부틸-페놀); 4,4'-티오비스 (6-tert-부틸-o-크레졸); 2,6-디-tert부틸페놀; 6-(4-히드록시페녹시)-2,4-비스(n-옥틸-티오)-1,3,5 트리아진; 디-n-옥틸티오)에틸 3,5-디-tert-부틸-4-히드록시-벤조에이트; 소르비톨 헥사[3-(3,5-디-tert-부틸-4-히드록시-페닐)-프로피오네이트]로 이루어진 군으로부터 선택되는 1종 이상인 것을 특징으로 하는 춘추절기용 인조 속눈썹 접착제 조성물. - 제1항에 있어서,
상기 안료는 Manganese ferrite black spinel인 것을 특징으로 하는 춘추절기용 인조 속눈썹 접착제 조성물. - 삭제