KR102376841B1 - 에칭 방법 및 반도체의 제조 방법 - Google Patents
에칭 방법 및 반도체의 제조 방법 Download PDFInfo
- Publication number
- KR102376841B1 KR102376841B1 KR1020207010772A KR20207010772A KR102376841B1 KR 102376841 B1 KR102376841 B1 KR 102376841B1 KR 1020207010772 A KR1020207010772 A KR 1020207010772A KR 20207010772 A KR20207010772 A KR 20207010772A KR 102376841 B1 KR102376841 B1 KR 102376841B1
- Authority
- KR
- South Korea
- Prior art keywords
- etching
- silicon nitride
- hole
- silicon oxide
- oxide layer
- Prior art date
Abstract
실리콘 질화물층의 에칭 속도와 실리콘 산화물층의 에칭 속도를 동일 정도로 제어할 수 있고, 또한, 고애스펙트비의 홀이어도 높은 에칭 속도에서 양호한 형상으로 형성할 수 있는 에칭 방법을 제공한다. 적층된 실리콘 산화물층(2)과 실리콘 질화물층(3)을 갖는 적층막(5)을 구비하는 피처리체를, 화학식 C2HxF(3-x)Br(화학식 중의 x는 0, 1, 또는 2임)으로 표시되는 불포화 할론을 함유하는 에칭 가스에 의해 처리한다. 그러면, 실리콘 산화물층(2)과 실리콘 질화물층(3)이 동일 정도의 에칭 속도에서 에칭된다.
Description
본 발명은 에칭 방법 및 반도체의 제조 방법에 관한 것이다.
반도체의 제조 공정에 있어서는, 레지스트나 유기막이나 카본막을 마스크로 하여, 적층된 실리콘 산화물층과 실리콘 질화물층을 갖는 적층막을, 에칭 가스를 사용하여 에칭함으로써, 콘택트 홀 등의 홀(관통 구멍)을 형성하는 공정이 있다. 이러한 홀의 형성에 있어서는, 그 홀의 입구 부분이 폐색되는 형상으로 되는 네킹이나, 홀의 길이 방향 중간부가 배럴 형상으로 되는 보잉이 생기기 쉽다.
또한, Si-N 결합은 Si-O 결합에 비하여 결합 에너지가 약하므로, 실리콘 질화물층의 에칭 속도가 실리콘 산화물층의 에칭 속도보다 커지는 경향이 있다. 그 때문에, 고애스펙트비의 홀을 형성하는 심층 에칭을 상기 적층막에 대해 실시한 경우에는, 실리콘 산화물층이 두께 방향으로 에칭되는 속도보다, 실리콘 질화물층이 두께 방향에 직교하는 면 방향으로 에칭되는 속도쪽이 커지므로, 실리콘 질화물층이 면 방향으로 과잉으로 에칭되어, 에칭 형상의 이상이 생길 우려가 있었다.
또한, 고애스펙트비의 홀에서는, 심부에 에칭 가스가 닿기 어렵기 때문에, 에칭 속도가 저하되기 쉽다.
특히 근년은, 반도체 장치의 미세화에 수반하여, 콘택트 홀의 직경은 보다 작아지고, 그 애스펙트비는 증대되는 경향이 있다. 따라서, 미세 직경, 고애스펙트비의 콘택트 홀을, 에칭 속도를 저하시키지 않고, 대략 수직으로 네킹이나 보잉이 적은 양호한 형상으로 형성하는 기술이 요구되고 있다.
예를 들어 특허문헌 1에는, 1,3,3,3-테트라플루오로프로펜(CF3CHCHF), 탄소수 2 내지 5의 불포화 퍼플루오로카본, 산화성 가스 및 불활성 가스를 포함하는 에칭 가스를 사용하여, 상기 적층막을 실리콘 질화물층과 실리콘 산화물층의 에칭 속도를 동등하게 제어하면서 에칭하는 방법이 개시되어 있다.
또한, 특허문헌 2에는, 브로모트리플루오로메탄(CF3Br)이라는, 원자 번호가 큰 할로겐 원소, 탄소 및 불소를 갖는 가스를 에칭 가스로서 사용함으로써, 이방성 에칭 가스로부터 생성된 플라스마를 홀의 저부에 도달시키는 것이 기재되어 있다.
또한, 특허문헌 3에는, 1-브로모-3,3,3-트리플루오로프로핀(CF3CCBr)이라는, 원자 번호가 큰 할로겐 원소, 탄소 및 불소와 3중 결합을 갖는 가스를 에칭 가스로서 사용하는 에칭 방법이 기재되어 있다.
또한, 특허문헌 4에는, 브로모트리플루오로에틸렌(CBrFCF2)을 실리콘 산화막의 에칭에 사용하는 방법이 기재되어 있다. 그러나, 브로모트리플루오로에틸렌을 실리콘 질화막의 에칭에 사용하였다는 보고는 없다.
그러나, 상기 종래 기술에는, 미세 직경, 고애스펙트비의 콘택트 홀을 형성하는 경우에는, 그 콘택트 홀의 심부에 있어서 에칭 속도가 저하된다고 하는 문제가 있었다. 또한, 퇴적 효과가 약하기 때문에, 홀의 길이 방향 중간부가 배럴 형상으로 되는 보잉이 생기기 쉽다는 문제가 있었다. 또한, 탄소수가 적은 불소화 프로핀류는 안정성이 낮고 취급이 어렵다는 문제가 있었다.
본 발명은 실리콘 질화물층의 에칭 속도와 실리콘 산화물층의 에칭 속도를 동일 정도로 제어할 수 있고, 또한, 고애스펙트비의 홀이어도 높은 에칭 속도에서 양호한 형상으로 형성할 수 있는 에칭 방법 및 반도체의 제조 방법을 제공하는 것을 과제로 한다.
상기 과제를 해결하기 위해, 본 발명의 일 형태는 이하의 [1] 내지 [5]와 같다.
[1] 적층된 실리콘 산화물층과 실리콘 질화물층을 갖는 적층막을 구비하는 피처리체를, 화학식 C2HxF(3-x)Br(상기 화학식 중의 x는 0, 1, 또는 2임)으로 표시되는 불포화 할론을 함유하는 에칭 가스에 의해 처리하고, 상기 실리콘 산화물층과 상기 실리콘 질화물층의 양쪽을 에칭하는 에칭 공정을 구비하는, 에칭 방법.
[2] 상기 불포화 할론이 브로모트리플루오로에틸렌, (E)-1-브로모-2-플루오로에틸렌 및 1-브로모-1-플루오로에틸렌으로 이루어지는 군으로부터 선택되는 적어도 하나인 [1]에 기재된, 에칭 방법.
[3] 상기 에칭 가스가 불활성 가스를 더 함유하는 [1] 또는 [2]에 기재된, 에칭 방법.
[4] 상기 에칭 공정에 있어서는, 상기 에칭 가스를 플라스마화하여 얻어지는 플라스마 가스를 사용하여 에칭하는 [1] 내지 [3]의 어느 하나에 기재된, 에칭 방법.
[5] [1] 내지 [4]의 어느 하나에 기재된 에칭 방법으로 에칭을 행하는 것을 포함하는, 반도체의 제조 방법.
본 발명의 에칭 방법 및 반도체의 제조 방법에 의해, 적층된 실리콘 산화물층과 실리콘 질화물층을 갖는 적층막을 구비하는 피처리체를 에칭하면, 실리콘 질화물층의 에칭 속도와 실리콘 산화물층의 에칭 속도를 동일 정도로 제어할 수 있고, 또한, 고애스펙트비의 홀이어도 높은 에칭 속도에서 양호한 형상으로 형성할 수 있다.
도 1은 본 발명의 일 실시 형태에 관한 에칭 방법을 설명하는 피처리체의 단면도이다.
도 2는 실시예 및 비교예에 사용한 시험편의 구조를 설명하는 모식도이다.
도 3은 에칭 속도의 측정 결과를 나타내는 그래프이다.
도 4는 에칭 속도비의 측정 결과를 나타내는 그래프이다.
도 5는 애스펙트비의 측정 결과를 나타내는 그래프이다.
도 6은 사이드 에치율의 측정 결과를 나타내는 그래프이다.
도 2는 실시예 및 비교예에 사용한 시험편의 구조를 설명하는 모식도이다.
도 3은 에칭 속도의 측정 결과를 나타내는 그래프이다.
도 4는 에칭 속도비의 측정 결과를 나타내는 그래프이다.
도 5는 애스펙트비의 측정 결과를 나타내는 그래프이다.
도 6은 사이드 에치율의 측정 결과를 나타내는 그래프이다.
본 발명의 일 실시 형태에 대해 이하에 설명한다. 또한, 본 실시 형태는 본 발명의 일례를 나타낸 것으로서, 본 발명은 본 실시 형태로 한정되는 것은 아니다. 또한, 본 실시 형태에는 다양한 변경 또는 개량을 가하는 것이 가능하며, 그와 같은 변경 또는 개량을 가한 형태도 본 발명에 포함될 수 있다.
본 실시 형태의 에칭 방법은, 적층된 실리콘 산화물층(SiOy층)과 실리콘 질화물층을 갖는 적층막을 구비하는 피처리체를, 화학식 C2HxF(3-x)Br(화학식 중의 x는 0, 1, 또는 2임)으로 표시되는 불포화 할론을 함유하는 에칭 가스에 의해 처리하여, 실리콘 산화물층과 실리콘 질화물층의 양쪽을 에칭하는 에칭 공정을 구비한다.
본 실시 형태의 에칭 방법에 의해, 적층된 실리콘 산화물층과 실리콘 질화물층을 갖는 적층막을 구비하는 피처리체를 에칭하면, 에칭 조건 등에 의해, 실리콘 산화물층의 에칭 속도에 대한 실리콘 질화물층의 에칭 속도의 비([실리콘 질화물층의 에칭 속도]/[실리콘 산화물층의 에칭 속도])를 0.8 이상 1.5 미만의 사이에서 임의로 제어할 수 있다. 따라서, 본 실시 형태의 에칭 방법에 의하면, 실리콘 질화물층의 에칭 속도와 실리콘 산화물층의 에칭 속도를 동일 정도로 제어하는 것이 가능하고, 실리콘 산화물층의 에칭 속도에 대한 실리콘 질화물층의 에칭 속도의 비는 0.9 이상 1.2 미만으로 하는 것이 바람직하다.
또한, 본 실시 형태의 에칭 방법에 의하면, 고애스펙트비의 홀이어도, 다음에 설명하는 퇴적 효과에 의해 높은 에칭 속도에서 양호한 형상으로 형성할 수 있다.
상세하게 설명하면, 화학식 C2HxF(3-x)Br로 표시되는 불포화 할론은, 분자 내에 이중 결합을 갖고 있으므로, 플라스마 속에서 중합하여 고분자화한다. 그리고, 생성된 고분자가 콘택트 홀 등의 홀(관통 구멍)의 측벽에 퇴적하여, 보호막을 형성한다. 이 퇴적 효과에 의해 등방적인 에칭이 억제되므로, 대략 수직으로 네킹이나 보잉이 적은 양호한 형상의 홀을 형성할 수 있다.
또한, 화학식 C2HxF(3-x)Br로 표시되는 불포화 할론은, 분자 내에 불소 원자보다 무거운 브롬 원자를 가지므로, 고애스펙트비의 홀이어도 에칭 가스가 홀의 심부까지 도달하기 쉽다. 그 때문에, 고애스펙트비의 홀이어도 에칭 속도의 저하가 일어나기 어렵고, 높은 에칭 속도에서의 에칭이 가능하다.
화학식 C2HxF(3-x)Br로 표시되는 불포화 할론의 종류는 특히 한정되는 것은 아니지만, 브로모트리플루오로에틸렌(CBrFCF2), (E)-1-브로모-2-플루오로에틸렌(CHBrCHF) 및 1-브로모-1-플루오로에틸렌(CBrFCH2)으로 이루어지는 군으로부터 선택되는 적어도 하나를 사용할 수 있다.
에칭 가스에는, 화학식 C2HxF(3-x)Br로 표시되는 불포화 할론과 함께 불활성 가스를 함유시켜도 된다. 불활성 가스를 공존시키면서 에칭을 행함으로써, 마스크에 대해 실리콘 산화물층 및 실리콘 질화물층을 선택적으로 또한 높은 에칭 속도에서 에칭할 수 있다. 불활성 가스의 종류는 특히 한정되는 것은 아니지만, 헬륨(He), 아르곤(Ar), 네온(Ne), 크립톤(Kr), 크세논(Xe), 질소(N2)를 들 수 있다. 이들 불활성 가스는 1종을 단독으로 사용해도 되고, 2종 이상을 병용해도 된다. 이들 불활성 가스 중에서는, 취급 용이성의 관점에서 아르곤이 바람직하다. 또한, 불활성 가스를 함유시켜 불포화 할론을 희석하는 경우에는, 희석 비율은, 예를 들어 체적비로, 상기 불포화 할론:불활성 가스=1:99 내지 80:20으로 할 수 있고, 바람직하게는 5:95 내지 50:50으로 할 수 있고, 더욱 바람직하게는 5:95 내지 20:80으로 할 수 있다.
또한, 에칭 공정에 있어서 채용되는 에칭 방법은 특히 한정되는 것은 아니지만, 에칭 가스를 플라스마화하여 얻어지는 플라스마 가스를 사용하여 에칭하는 플라스마 에칭법을 채용할 수 있다.
에칭에 사용되는 플라스마에는, 플라스마 용량 결합형 플라스마(CCP: Capacitively Coupled Plasma), 전자 사이클로트론 공명 플라스마(ECP: Electron Cyclotron resonance Plasma), 헬리콘파 여기 플라스마(HWP: Helicon Wave Plasma), 유도 결합형 플라스마(ICP: Inductively Coupled Plasma), 마이크로파 여기 표면파 플라스마(SWP: Surface Wave Plasma) 등이 있다.
이러한 본 실시 형태의 에칭 방법은, 예를 들어 3차원 NAND형 플래시 메모리의 제조 과정 중의 일 공정인, 실리콘 질화물층과 실리콘 산화물층이 기판 위에 교대로 다수 적층된 적층막에 대해 두께 방향으로 연장되는 관통 구멍을 형성하는 공정에 있어서 사용 가능하다.
적층된 실리콘 산화물층과 실리콘 질화물층을 갖는 적층막을 구비하는 피처리체를, 본 실시 형태의 에칭 방법에 의해 에칭하여, 적층막에 관통 구멍을 형성하는 방법의 일례를, 도 1을 참조하면서 설명한다.
도 1은, 적층막(5)에 관통 구멍(9)이 형성된 피처리체의 단면도이지만, 이 피처리체는, 실리콘 질화물층(3)과 실리콘 산화물층(2)이 교대로 다수(도 1의 예에서는 3층씩) 적층된 적층막(5)이, 반도체 기판(1) 위에 마련되어 구성되어 있다. 또한, 반도체 기판(1)의 바로 위에는 적층막(5)의 실리콘 산화물층(2)이 적층되어 있다.
적층막(5)의 최상층의 실리콘 질화물층(3)의 위에는, 패턴이 형성된 마스크(7)가 피복되어 있고, 본 실시 형태의 에칭 방법에 의해 에칭을 행하면, 마스크(7)로부터 노출되는 적층막(5)이 에칭되어 관통 구멍(9)이 형성된다.
본 실시 형태의 에칭 방법은, 실리콘 질화물층(3)의 에칭 속도와 실리콘 산화물층(2)의 에칭 속도를 동일 정도로 제어하는 것이 가능하므로, 적층막(5)에 관통 구멍(9)을 형성할 때에는, 관통 구멍(9)의 내면에 노출되는 실리콘 질화물층(3)이 면 방향(두께 방향에 직교하는 방향)으로 과잉으로 에칭되는 것이 억제된다. 따라서, 애스펙트비 20을 초과하는 고애스펙트비의 관통 구멍(9)을 형성하는 심층 에칭을 적층막(5)에 대해 실시한 경우에도, 도 1에 도시하는 바와 같이, 적층막(5)의 적층 구조 붕괴나 에칭 형상 이상을 생기게 하지 않고 관통 구멍(9)을 형성할 수 있다. 게다가, 애스펙트비 20을 초과하는 고애스펙트비의 관통 구멍(9)을 형성하는 심층 에칭을 적층막(5)에 대해 실시한 경우에도, 높은 에칭 속도를 유지하면서 양호한 형상의 관통 구멍(9)을 형성할 수 있다.
실시예
이하에 실시예 및 비교예를 제시하여, 본 발명을 보다 상세하게 설명한다.
[실시예 1]
도 2를 참조하면서 실시예 1의 시험편 제조 방법을 설명한다. 플라스마 화학 기상 성장법에 의해, 도시하지 않은 Si 기판 위에 실리콘 질화물을 포함하는 실리콘 화합물층(21)을 성막하였다. 실리콘 화합물층(21)의 막 두께는 2000㎚로 하였다. 다음에, 실리콘 화합물층(21) 위에 포토레지스트 도트 패턴 마스크(23)를 형성하여, 시험편 A를 얻었다. 도트 패턴의 개구부(23a)의 직경은 50㎚ 내지 200㎚로 하였다. 또한, 포토레지스트 도트 패턴 마스크(23)의 막 두께는 1000㎚로 하였다.
다음에, 실리콘 질화물을 포함하는 실리콘 화합물층(21) 대신에 실리콘 산화물을 포함하는 실리콘 화합물층(21)을 Si 기판 위에 성막하는 점 이외는 상기와 마찬가지로 하여, 시험편 B를 얻었다.
이들 시험편 A, B에 대해 유도 결합형 플라스마 에칭(ICP 에칭)을 실시하고, 실리콘 화합물층(21)(실리콘 질화물층 또는 실리콘 산화물층)을 에칭하여 홀을 형성하였다. 에칭 조건은 이하와 같다.
에칭 장치: 사무코 가부시키가이샤제의 ICP 에칭 장치 RIE-200iP
에칭 시간: 10분간
ICP 전력: 500W
바이어스 전력: 200W
압력: 2Pa
에칭 가스: 브로모트리플루오로에틸렌(이하 「BTFE」라고 기재함) 1체적부와 아르곤 9체적부의 혼합 가스
에칭 가스의 유량: 100SCCM
에칭이 종료되면, Si 기판, 실리콘 화합물층(21) 및 포토레지스트 도트 패턴 마스크(23)의 적층 방향을 따르는 평면에서 시험편 A, B를 각각 절단하고, 그 단면을 니혼 덴시 가부시키가이샤제의 전계 방출형 주사 전자 현미경(FE-SEM 장치)에 의해 관찰하였다. 그리고, 그 관찰 결과로부터, 실리콘 화합물층(21)(실리콘 질화물층 및 실리콘 산화물층)의 에칭 속도와, 형성된 홀의 애스펙트비 및 사이드 에치율을 각각 측정하였다.
에칭 속도는, 포토레지스트 도트 패턴 마스크(23)에 피복된 피복부와 개구부(23a)에 있어서의 실리콘 화합물층(21)의 막 두께차(즉, 도 2에서의 에칭 깊이 c)와 에칭 시간으로부터 산출하였다. 또한, 홀의 애스펙트비는, 개구부(23a)의 직경 b와 에칭 깊이 c의 비 c/b이다. 또한, 홀의 사이드 에치율은, 홀의 측벽의 절삭량 a와 개구부(23a)의 직경 b의 비 a/b이다. 또한, 홀의 측벽의 절삭량 a란, 도 2에 도시하는 바와 같이, 대략 수직으로 연장되는 홀의 측벽이 깎여서 홀의 길이 방향 중간부가 배럴 형상으로 된 경우에, 깎인 부분의 홀의 길이 방향에 직교하는 방향의 길이를 의미한다.
[실시예 2]
에칭 가스 속의 불포화 할론을 BTFE로부터 1-브로모-1-플루오로에틸렌(이하, 「1B1FE」라고 기재함)으로 대체한 점 이외는, 실시예 1과 마찬가지로 하여 에칭 및 현미경 관찰을 행하고, 실리콘 화합물층(21)(실리콘 질화물층 및 실리콘 산화물층)의 에칭 속도와, 형성된 홀의 애스펙트비 및 사이드 에치율을 각각 측정하였다.
[실시예 3]
에칭 가스 속의 불포화 할론을 BTFE로부터 (E)-1-브로모-2-플루오로에틸렌(이하, 「1B2FE」라고 기재함)으로 대체한 점 이외는, 실시예 1과 마찬가지로 하여 에칭 및 현미경 관찰을 행하고, 실리콘 화합물층(21)(실리콘 질화물층 및 실리콘 산화물층)의 에칭 속도와, 형성된 홀의 애스펙트비 및 사이드 에치율을 각각 측정하였다.
[비교예 1]
에칭 가스를 (E)-1,3,3,3-테트라플루오로프로펜(이하, 「HFO-1234ze」라고 기재함) 1체적부와 산소 가스 1체적부와 아르곤 8체적부의 혼합 가스로 대체한 점 이외는, 실시예 1과 마찬가지로 하여 에칭 및 현미경 관찰을 행하고, 실리콘 화합물층(21)(실리콘 질화물층 및 실리콘 산화물층)의 에칭 속도와, 형성된 홀의 애스펙트비 및 사이드 에치율을 각각 측정하였다.
[비교예 2]
에칭 가스를 HFO-1234ze 1체적부와 헥사플루오로프로펜(C3F6) 0.5체적부와 산소 가스 0.6체적부와 아르곤 7.9체적부의 혼합 가스로 대체한 점 이외는, 실시예 1과 마찬가지로 하여 에칭 및 현미경 관찰을 행하고, 실리콘 화합물층(21)(실리콘 질화물층 및 실리콘 산화물층)의 에칭 속도와, 형성된 홀의 애스펙트비 및 사이드 에치율을 각각 측정하였다.
[비교예 3]
에칭 가스를 브로모트리플루오로메탄(CBrF3)으로 대체한 점 이외는, 실시예 1과 마찬가지로 하여 에칭 및 현미경 관찰을 행하고, 실리콘 화합물층(21)(실리콘 질화물층 및 실리콘 산화물층)의 에칭 속도와, 형성된 홀의 애스펙트비 및 사이드 에치율을 각각 측정하였다.
[비교예 4]
에칭 가스를 사불화탄소(CF4)로 대체한 점 이외는, 실시예 1과 마찬가지로 하여 에칭 및 현미경 관찰을 행하고, 실리콘 화합물층(21)(실리콘 질화물층 및 실리콘 산화물층)의 에칭 속도와, 형성된 홀의 애스펙트비 및 사이드 에치율을 각각 측정하였다.
실시예 1 내지 3 및 비교예 1 내지 4의 결과를, 표 1 및 도 3 내지 6의 그래프에 나타낸다. 표 1 및 도 3 내지 6의 그래프로부터 명백한 바와 같이, F와 Br을 갖는 에틸렌 유도체를 함유하는 에칭 가스를 사용하여 에칭을 행한 실시예 1 내지 3은, 비교예 1 내지 4에 비하여, 고애스펙트비의 홀을 높은 에칭 속도에서 형성할 수 있으며, 또한, 사이드 에치율이 낮고 양호한 형상의 홀이 형성되어 있다. 또한, 실시예 1 내지 3은, 실리콘 질화물층의 에칭 속도와 실리콘 산화물층의 에칭 속도가 동일 정도로 제어되어 있다.
비교예 1은, 사이드 에치율이 낮기는 했지만, 고애스펙트비의 홀을 형성할 때의 에칭 속도가 충분하지는 못하였다. 또한, 실리콘 질화물층의 에칭 속도와 실리콘 산화물층의 에칭 속도의 차가 컸다.
비교예 2는, 사이드 에치율이 낮고, 비교예 1에 비교하면 실리콘 질화물층의 에칭 속도와 실리콘 산화물층의 에칭 속도가 동일 정도로 되어 있기는 하지만, 고애스펙트비의 홀을 형성할 때의 에칭 속도가 충분하지는 못하였다.
비교예 3은, 실리콘 질화물층의 에칭 속도와 실리콘 산화물층의 에칭 속도가 동일 정도로 제어되어 있고, 고애스펙트비의 홀을 형성할 때의 에칭 속도도 양호한 레벨이기는 했지만, 사이드 에치율이 높았다.
비교예 4는, 실리콘 질화물층의 에칭 속도와 실리콘 산화물층의 에칭 속도의 차가 크고, 사이드 에치율도 높았다.
1: 반도체 기판
2: 실리콘 산화물층
3: 실리콘 질화물층
5: 적층막
7: 마스크
9: 관통 구멍
21: 실리콘 화합물층
23: 포토레지스트 도트 패턴 마스크
23a: 개구부
2: 실리콘 산화물층
3: 실리콘 질화물층
5: 적층막
7: 마스크
9: 관통 구멍
21: 실리콘 화합물층
23: 포토레지스트 도트 패턴 마스크
23a: 개구부
Claims (5)
- 적층된 실리콘 산화물층과 실리콘 질화물층을 갖는 적층막을 구비하는 피처리체를, 화학식 C2HxF(3-x)Br(상기 화학식 중의 x는 0, 1, 또는 2임)으로 표시되는 불포화 할론을 함유하는 에칭 가스에 의해 처리하여, 상기 실리콘 산화물층과 상기 실리콘 질화물층의 양쪽을 에칭하는 에칭 공정을 구비하고,
상기 에칭 공정에 있어서는, 상기 에칭 가스를 플라스마화하여 얻어지는 플라스마 가스를 사용하여 에칭하는, 에칭 방법. - 제1항에 있어서, 상기 불포화 할론이 브로모트리플루오로에틸렌, (E)-1-브로모-2-플루오로에틸렌 및 1-브로모-1-플루오로에틸렌으로 이루어지는 군으로부터 선택되는 적어도 하나인, 에칭 방법.
- 제1항 또는 제2항에 있어서, 상기 에칭 가스가 불활성 가스를 더 함유하는, 에칭 방법.
- 삭제
- 제1항 또는 제2항에 기재된 에칭 방법으로 에칭을 행하는 것을 포함하는, 반도체의 제조 방법.