KR102067456B1

KR102067456B1 - Arrangement Method for Manufacturing Vaobian Pottery

Info

Publication number: KR102067456B1
Application number: KR1020190050303A
Authority: KR
Inventors: 김용득
Original assignee: 김용득
Priority date: 2019-04-30
Filing date: 2019-04-30
Publication date: 2020-01-17

Abstract

The present invention relates to an arrangement method of manufacturing a vaobian pottery by using a traditional firewood kiln for firing pottery consisting of a furnace, a plurality of firing compartments to the furnace, a stack and a chimney. The flow of fire is irregularly controlled by using a plurality of barrier plates disposed between the fire and the pottery arranged in the firing compartments so that a plurality of colors and irregular patterns appear on a surface of the pottery.

Description

요변 도자기를 제조하는 재임방법{Arrangement Method for Manufacturing Vaobian Pottery}Arrangement Method for Manufacturing Vaobian Pottery

본 발명은 요변 도자기를 제조하는 재임방법에 관한 것이다.The present invention relates to a reappointment method for producing thixotropy.

이 부분에 기술된 내용은 단순히 본 발명에 대한 배경정보를 제공할 뿐 종래기술을 구성하는 것은 아니다.The contents described in this section merely provide background information on the present invention and do not constitute a prior art.

도자기를 소성하는 작업은 예로부터 전통적으로 장작불을 이용한 장작가마가 사용되어 왔으며, 종래의 장작 가마는 봉통, 다수의 칸으로 연결되는 소성 칸과 끌목(초벌) 칸으로 나뉘어 굴뚝과 연결된다. 봉통은 전체 가마의 예열을 하는 곳으로써, 가마의 예열을 위해서는 도자기 소성온도의 차이에 따라 분청사기 8 내지 10시간, 청자 10 내지 12시간, 백자 14 내지 15시간 정도가 필요하며 소성시간은 가마의 크기 등에 따라 그 차이가 있다.The work of firing pottery has traditionally been used with a firewood kiln using a wood fire, and a conventional firewood kiln is divided into a baton, a firing compartment connected to a plurality of compartments and a chisel (primary) compartment and connected to a chimney. Bongtong is a place where all the kilns are preheated. For preheating of kilns, it is necessary to use 8 ~ 10 hours of powdered dust, 10 ~ 12 hours of celadon, and 14 ~ 15 hours of white porcelain, depending on the difference in firing temperature. The difference depends on the size.

요변 도자기는 이러한 전통적인 장작가마를 이용하여 소성할 때 간혹 탄생할 수 있다. 요변 도자기는 소성하는 과정에서 예상치 못했던 여러가지 변수로 인하여 일반적이지 않은 독특한 색깔과 문양을 나타내는 도자기를 의미할 수 있다. 요변 도자기는 한 도자기에 환원작용과 산화작용이 복합적으로 함께 일어나 그 한 도자기에 나타나는 색깔이 두가지 이상일 수 있으며, 변화무쌍한 특별한 문양으로 발색될 수 있다. 보통은 소성할 때 소성 분위기를 환원 또는 산화로 설정하기 때문에, 한 도자기에 환원작용이나 산화작용 중 어느 하나만 발생할 수 있다. 그러나 요변 도자기는 이와 같이 환원과 산화작용이 함께 일어나 독특한 문양과 다채로운 색상이 표현될 수 있다. 이는 의도하여 제작할 수 없는 것이어서 다른 도자기에 비하여 그 작품성과 값어치를 높게 평가받을 수 있는 것이다.Thixotropic pottery can sometimes be born when fired using these traditional firewood kilns. Thixotropic ceramics can refer to ceramics that display unusual colors and patterns due to various unexpected variables during the firing process. Thixotropic pottery is a combination of reduction and oxidation in one pottery, so two or more colors appear in that pottery. Usually, when firing, the firing atmosphere is set to reduction or oxidation, so that only one of reduction or oxidation can occur in a ceramic. However, the thixotropic ceramics can be combined with reduction and oxidation, so that unique patterns and colorful colors can be expressed. It is not intended to be produced and can be highly evaluated for its workability and value compared to other ceramics.

이에 본 발명자는 수많은 실험과 연구를 통하여 독특하고 다채로운 문양과 색깔을 지닌 요변 도자기를 의도하여 생산할 수 있는 재임 방법을 발명하게 되어 본 발명을 제안하기에 이르렀다.Accordingly, the present inventors have invented a method of intention to produce a thixotropic ceramic having a unique and colorful pattern and color through a number of experiments and researches, and came to propose the present invention.

요변 도자기에 관한 종래기술을 검색해 본 결과 요변 도자기 제조방법(특허 제 10-1280931호)을 찾을 수 있었는데, 이는 여러 번 유약을 시유하여 소성하는 방법을 통해 문양을 표현하는 방법이 개시되어 있을 뿐, 본 발명과 같이 전통 장작가마를 이용한 자연스러운 불꽃에 의해 요변도자기를 제조하는 방법은 전혀 개시하지 않는다.As a result of searching the prior art about thixotropic pottery, we could find a thixotropic ceramic manufacturing method (Patent No. 10-1280931), which discloses a method of expressing a pattern through a method of baking by glazing several times. As described in the present invention, a method of producing thixotropic ceramics by natural flame using a traditional firewood kiln is not disclosed at all.

따라서, 본 발명의 해결하고자 하는 과제는 종래의 문제점을 보완한, 전통 장작가마를 이용하여 불꽃의 흐름을 조절하여 독특한 문양과 색깔이 표현되는 요변 도자기를 제조할 수 있는 재임 방법을 제공하는 것이다.Therefore, the problem to be solved by the present invention is to provide a reappointment method that can produce a thixotropic pottery by expressing a unique pattern and color by adjusting the flow of the flame by using a traditional firewood kiln, complementing the conventional problems.

본 발명은, 봉통과, 봉통과 연결되는 복수의 소성칸, 연돌 및 굴뚝으로 이루어진 도자기 소성용 전통 장작가마를 이용하여 요변 도자기를 제조하는 재임방법에 있어서, 불꽃과 소성칸 내부에 재임된 도자기의 사이에 복수개가 배치되는 차단격판을 이용하여 불의 흐름을 불규칙하게 조절하여 도자기 표면에 복수의 색깔과 불규칙한 무늬가 나타나도록 하는 것을 특징으로 하는 요변 도자기를 제조하는 재임방법을 제공한다.The present invention relates to a method of manufacturing a thixotropic ceramic using a fire barrel and a traditional firewood kiln for firing pottery consisting of a plurality of firing bins, stacks and chimneys connected to the barrels. Provides a method of manufacturing a thixotropic pottery, characterized in that a plurality of colors and irregular patterns appear on the surface of the ceramic by controlling the flow of fire irregularly by using a plurality of barrier plates arranged between.

본 발명의 추가적인 해결수단은 아래에서 이어지는 설명에서 일부 설명될 것이고, 그 설명으로부터 부분적으로 용이하게 확인할 수 있게 되거나, 또는 본 발명의 실시에 의해 지득될 수 있다.Additional solutions of the invention will be set forth in part in the description which follows, and in part will be readily apparent from the description, or may be learned by practice of the invention.

전술한 일반적인 설명 및 다음의 상세한 설명 모두는 단지 예시적이고 설명을 위한 것이며 청구범위에 기재된 본 발명을 제한하지 않는다.Both the foregoing general description and the following detailed description are exemplary and explanatory only and do not limit the invention described in the claims.

본 발명에 의하면 전통 장작가마를 이용하여 불꽃의 흐름을 조절하여 독특한 문양과 색깔이 표현되는 요변 도자기를 제조할 수 있다.According to the present invention it is possible to manufacture a thixotropic pottery by expressing a unique pattern and color by controlling the flow of the flame using a traditional firewood kiln.

도 1은 일반적으로 사용되는 도자기 소성용 전통 장작가마의 평면 단면도이다.
도 2는 본 발명의 실시예에 따른 요변 도자기를 제조하는 재임방법을 이용하지 않은 종래의 재임방법이 표현된 것이다.
도 3은 본 발명의 실시예에 따른 요변 도자기를 제조하는 재임방법이 적용된 것으로 차단격판이 배치된 모습이 표현된 것이다.
도 4 는 본 발명의 실시예에 따른 요변 도자기를 제조하는 재임방법이 적용된 것으로 차단격판이 배치되었을 때의 불꽃의 행동 양상이 설명된 것이다.
도 5는 본 발명의 실시예에 따른 요변 도자기를 제조하는 재임방법에 의하여 제조되는 도자기에 불꽃이 접촉함에 따라 색깔 및 무늬가 표현되는 일 예를 도시한 것이다.
도 6은 본 발명의 실시예에 따른 요변 도자기를 제조하는 재임방법에 의하여 제조되는 도자기의 몇가지 예의 도면대용 사진이다.
도 7 은 본 발명의 실시예에 따른 요변 도자기를 제조하는 재임방법에 따른 차단격판이 적용될 때의 정면도이다.
도 8 은 본 발명의 실시예에 따른 요변 도자기를 제조하는 재임방법에 따른 차단격판이 측면에도 적용될 때의 사시도이다.1 is a plan sectional view of a traditional firewood kiln for commonly used ceramic firing.
2 is a representation of a conventional reaping method that does not use a reaping method for manufacturing a thixotropic ceramic according to an embodiment of the present invention.
Figure 3 is a representation that the blocking plate is arranged to be applied to the method of manufacturing the thixotropic ceramic according to an embodiment of the present invention.
4 is a view illustrating an operation of a flame when a barrier plate is disposed by applying a method of manufacturing a thixotropic ceramic according to an embodiment of the present invention.
Figure 5 shows an example in which the color and pattern is expressed as the flame contacts the porcelain produced by the method of reconstructing the pottery prepared in accordance with an embodiment of the present invention.
FIG. 6 is a drawing substitute photograph of some examples of ceramics manufactured by a reappointing method of manufacturing a thixotropic ceramic according to an embodiment of the present invention.
7 is a front view when the barrier plate according to the reappointment method for manufacturing a thixotropic ceramic according to an embodiment of the present invention is applied.
8 is a perspective view when the barrier plate according to the reappointment method for manufacturing a thixotropic ceramic according to an embodiment of the present invention is also applied to the side.

이하, 첨부된 도면을 참조하여 본 발명의 구체적인 실시형태에 대하여 상세하게 서술하도록 한다. Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings.

다만, 본 발명의 구체적 일 실시 형태를 설명함에 있어, 관련된 공지 기능 또는 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명을 생략한다.However, in describing a specific embodiment of the present invention, if it is determined that a detailed description of a related known function or configuration may unnecessarily obscure the subject matter of the present invention, the detailed description thereof will be omitted.

도 1은 일반적으로 사용되는 도자기 소성용 전통 장작가마의 평면 단면도이다.1 is a plan sectional view of a traditional firewood kiln for commonly used ceramic firing.

도 2는 본 발명의 실시예에 따른 요변 도자기를 제조하는 재임방법을 이용하지 않은 종래의 재임방법이 표현된 것이다.2 is a representation of a conventional reaping method that does not use a reaping method for manufacturing a thixotropic ceramic according to an embodiment of the present invention.

도 1을 참조하면 일반적으로 사용되는 도자기 소성용 전통 장작가마는 봉통(Y), 복수의 소성칸(X1, X2, X3), 복수의 소성칸 각각에 구비되는 출입구(50)를 포함할 수 있다.Referring to FIG. 1, a traditional firewood kiln for commonly used ceramic firing may include a bag Y, a plurality of baking bins X1, X2, and X3, and an entrance 50 provided in each of the baking bins. .

봉통(Y)에 장작을 투입하여 불을 지피게 되면 봉통(Y)과 연결된 제1소성칸(X1)에 봉통(Y)과 제1소성칸(X1)사이에 형성되는 불의 통로인 화로를 통해 불꽃(1)이 미치게 된다. 이 때, 제1소성칸(X1)에 배치되어 있는 도자기가 이 불꽃(1)의 영향을 받아 소성되어 완제품으로 탄생한다. 이 때, 반드시 도자기가 제1소성칸(X1)에만 있는 것은 아니고, 제2소성칸(X2), 제3소성칸(X3)에도 있을 수 있다. 아래에서는 하나의 소성칸 내부에 도자기가 재임되는 구조와 방법에 대하여 서술한다.When fire is put into the barrel (Y) to make fire, the fire path is formed between the barrel (Y) and the first firing chamber (X1) in the first firing compartment (X1) connected to the barrel (Y). The flame (1) is going crazy. At this time, the ceramics arranged in the first firing compartment X1 are fired under the influence of the flame 1 and are produced as finished products. At this time, the ceramics are not necessarily in the first firing compartment X1 but may also be in the second firing compartment X2 and the third firing compartment X3. The following describes the structure and method of ceramics served in one firing chamber.

도 2를 참조하면 하나의 소성칸 내부에는 내화판(10) 및 지주(20)를 이용하여 도자기가 적재될 수 있도록 복수의 층을 가지는 적층 구조물이 구비될 수 있고, 각 층에 해당하는 내화판(10)의 상단에 도자기(30)들이 배치될 수 있다. 도면에서는 3단 구조물이 나란히 붙어 있는 것으로 도시 되었으나, 반드시 이에 한정되는 것은 아니고 구조물의 크기와 층 수는 소성칸 내부의 크기에 따라 얼마든지 변경될 수 있다. 재임이란 이와 같이 소성을 위하여 소성칸 내부에 도자기(30)들을 배치하는 것을 의미할 수 있다.Referring to FIG. 2, one firing compartment may include a laminated structure having a plurality of layers such that ceramics may be loaded using the fireproof plate 10 and the support 20, and fireproof plates corresponding to each layer. Pottery 30 may be disposed on the top of the (10). In the drawings, the three-stage structure is shown to be attached side by side, but is not necessarily limited to this, the size and number of layers of the structure can be changed as much as the size of the interior of the plastic box. Reappointment may mean disposing ceramics 30 in the baking bin for firing as described above.

이와 같이 도자기(30)가 배치되면 불꽃이 도자기 전체에 미치게 되어 도자기가 균일하게 소성이 될 수 있다. 공기를 주입하면서(문을 열어놓고) 불을 지피는 것을 산화 소성이라 하고, 공기를 차단하고(문을 닫아놓고) 불을 지피는 것을 환원 소성이라 한다. 이와 같이 도자기(30)를 배치하고 소성하면 불꽃이 재임된 도자기 전체에 고루고루 미치게 되므로, 산화나 환원 중 선택된 소성분위기에 의한 색깔만 나타내는 도자기가 완성될 수 있다. 즉, 환원분위기를 선택하여 소성하는 경우, 도자기의 표면에 도포된 유약이 환원작용에 의해 발색되는 색깔이 예를 들어 노란색이면, 도자기가 전체적으로 노란색을 띤 것으로 소성될 수 있다. 하나의 도자기만 보았을 때 도자기 전체적으로 노란빛을 띨 것이고, 열 개의 도자기가 재임된 것을 가정하여 열 개를 관찰하면 그 중 아홉 개 내지 열 개가 노란색을 띠게 될 수 있다. 또는, 불에 가깝게 배치되어 불이 직접 닿는 도자기들은 산화작용이 일어나고, 불에 멀리 배치된 도자기들은 환원작용이 일어날 수도 있다.As such, when the ceramics 30 are disposed, the flame may spread to the whole ceramics so that the ceramics may be uniformly fired. Burning fire while injecting air (opening the door) is called oxidative firing, and reducing fire when blocking air (close door) is called reducing firing. When the ceramics 30 are disposed and fired as described above, the ceramics are evenly spread over the entire ceramic pot where the flame is served, so that ceramics showing only the color due to the selected minor component crisis during oxidation or reduction can be completed. That is, when the reduction atmosphere is selected and fired, if the glaze applied to the surface of the porcelain is colored by, for example, yellow color, the porcelain may be fired to have a yellow color as a whole. When only one pottery is seen, the whole pottery will be yellowish, and assuming ten porcelains are served, ten of them can be yellow. Or, ceramics placed close to the fire and directly touching the fire may be oxidized, and ceramics placed far from the fire may be reduced.

가끔 열 개 중 하나 정도가 공기의 흐름이나 불의 흐름 등이 예상치 못하게 전개되어 표면의 일부는 환원작용에 의한 노란색이 표현되고 이에 더하여 산화작용에 의해 발색되는 예를 들어 파란색까지 같이 표현될 수도 있다. 이와 같은 것을 요변 도자기라 할 수 있다. 이는 전술한 바와 같이 하나의 도자기에 산화작용과 환원작용이 모두 일어나야 하므로 의도하여 제조할 수는 없는 것이고, 예상치 못하게 가끔 운이 좋아 생산될 수 있는 것이다.Occasionally, about one in ten may develop an unexpected flow of air or fire, such that a part of the surface may be represented by a yellow color by reduction, in addition to a blue color by oxidation. Such a thing can be called thixotropic pottery. As described above, since the oxidation and reduction must occur in one ceramic, it cannot be manufactured intentionally, and it can be unexpectedly sometimes produced with good luck.

도 3은 본 발명의 실시예에 따른 요변 도자기를 제조하는 재임방법이 적용된 것으로 차단격판이 배치된 모습이 표현된 것이다.Figure 3 is a representation that the blocking plate is arranged to be applied to the method of manufacturing the thixotropic ceramic according to an embodiment of the present invention.

도 3을 참조하면, 도자기를 재임할 수 있는 적층 구조물의 정면에 차단격판(100)이 배치된 것을 파악할 수 있다. 여기서 정면은, 불꽃(1)을 마주하는 방향을 의미할 수 있다. 자세한 사항은 후술하겠지만, 도 3에 도시된 바와 같은 구조에 의하면 전술한 운이 좋아 가끔 생산될 수 있는 요변 도자기를, 가마 소성할 때 마다 의도하여 생산할 수 있다. 즉, 종전에 비해 생산되는 빈도가 높아질 수 있다.Referring to Figure 3, it can be seen that the blocking plate 100 is disposed on the front of the laminated structure that can serve ceramic. Here, the front face may mean a direction facing the flame 1. Although details will be described later, according to the structure as shown in FIG. 3, the thixotropic ceramics, which may be occasionally produced by good luck as described above, may be intentionally produced every time the kiln is fired. That is, the frequency of production may be higher than before.

도 3을 참조하면, 차단격판(100)은 불꽃(1)과 도자기의 사이에 복수개가 일정간격(S)을 두고 설치될 수 있다. 차단격판(100)은 내열성, 내화성을 지닌 재질로 구성될 수 있으며, 전술한 내화판(10)과 동일한 재질로 구성될 수 있다.Referring to Figure 3, the blocking plate 100 may be installed with a plurality of predetermined intervals (S) between the flame (1) and ceramics. The blocking plate 100 may be made of a material having heat resistance and fire resistance, and may be made of the same material as the fire plate 10 described above.

전체적으로 환원분위기로 소성을 하는 경우를 예로 들면, 차단격판(100)을 설치하면 차단격판(100)에 의해 불꽃(1)이 직접적으로 닿지 않는 부분은 환원작용이 일어날 수 있고, 차단격판(100)과 차단격판(100)의 사이에 존재하는 틈을 통해 불꽃(1)이 들어가 도자기(30)에 직접 닿으면, 그 불꽃(1)이 직접 닿은 부분은 산화작용이 일어날 수 있다. 즉, 불꽃(1)이 차단격판(100)과 차단격판(100)의 사이의 틈을 통해 들어가 도자기의 둘레의 적어도 일부에 접촉하거나 감싸는 등의 상황을 발생시켜 전체적으로 환원분위기로 소성하여 환원작용에 의한 색깔을 나타내되 불꽃(1)이 접촉한 부분만 산화작용으로 인한 색깔을 나타내도록 할 수 있다. 이에 의하면, 하나의 도자기에 환원작용에 의한 색깔과 산화작용에 의한 색깔이 동시에 나타날 뿐만 아니라, 그 불꽃(1)이 접촉한 모양이나 시간 등에 따라서 독특한 무늬/문양이 형성될 수 있다.For example, when the firing is performed in a reducing atmosphere as a whole, when the blocking plate 100 is installed, a portion in which the flame 1 does not directly touch the blocking plate 100 may occur, and the blocking plate 100 may be reduced. When the flame 1 enters directly through the gap between the barrier plate 100 and the ceramic ware 30, the portion directly contacted by the flame 1 may be oxidized. That is, the flame 1 enters through the gap between the blocking plate 100 and the blocking plate 100 to contact or wrap at least a part of the circumference of the porcelain, and then fire in the reducing atmosphere as a whole to reduce the action. It can show the color by but only the part where the flame (1) is in contact with the color due to oxidation. According to this, not only the color due to the reduction action and the color due to the oxidation action appear at the same time, but also a unique pattern / pattern can be formed according to the shape or time of contact of the flame 1.

도 4 는 본 발명의 실시예에 따른 요변 도자기를 제조하는 재임방법이 적용된 것으로 차단격판이 배치되었을 때의 불꽃의 행동 양상이 설명된 것이다.4 is a view illustrating an operation of a flame when a barrier plate is disposed by applying a reaping method of manufacturing a thixotropic ceramic according to an embodiment of the present invention.

차단격판(100)이 없는 경우 불이 전체적으로 도자기(30)에 미치게 되어 균일한 색깔을 띠게 될 수 있다. 그러나 도4와 같이 차단격판(100)이 존재하는 경우 차단격판(100)에 의해 직접적으로 불꽃(1)이 닿지 않는 부분에 환원작용이 일어나고, 그 틈을 통해 들어와 불꽃(1)이 직접 닿는 부분은 산화작용이 일어날 수 있다. 불꽃(1)은, 틈이 좁은 곳은 공기가 흐르는 속도가 빠른 원리'에 의하여 차단격판(100) 간 사이의 틈을 통해 순간적으로 통과되어 도자기(30)의 적어도 일부에 접촉할 수 있다. 아니면, 반드시 이러한 원리가 아니더라도, 차단격판(100)은 단순히 불꽃(1) 차단의 역할을 하여, 차단격판(100)에 의해 불꽃(1)이 차단되는 부분과 틈을 통해 불꽃(1)이 직접 닿는 부분이 발생하도록 하여 위와 같은 요변 도자기를 제조할 수 있다.If there is no blocking plate 100, the fire is to reach the ceramic 30 as a whole may have a uniform color. However, in the case where the blocking plate 100 is present as shown in FIG. 4, a reduction action occurs in a portion where the flame 1 does not directly contact by the blocking plate 100, and a portion where the flame 1 directly comes in through the gap. Silver oxidation can occur. The flame 1 may be instantaneously passed through the gap between the blocking plates 100 by contacting at least a part of the ceramics 30 according to the principle that the space where the gap is narrow is a high speed through which air flows. Otherwise, even if this is not necessarily the principle, the blocking plate 100 simply serves as blocking the flame 1, so that the flame 1 directly through the part and the gap where the flame 1 is blocked by the blocking plate 100. It is possible to manufacture the thixotropic ceramics such that the touching part occurs.

도 5는 본 발명의 실시예에 따른 요변 도자기를 제조하는 재임방법에 의하여 제조되는 도자기에 불꽃이 접촉함에 따라 색깔 및 무늬가 표현되는 일 예를 도시한 것이다.Figure 5 shows an example in which the color and pattern is represented as the flame contacts the ceramics produced by the method of reconstructing the pottery prepared in accordance with an embodiment of the present invention.

도 6은 본 발명의 실시예에 따른 요변 도자기를 제조하는 재임방법에 의하여 제조되는 도자기의 몇가지 예의 도면대용 사진이다.FIG. 6 is a drawing substitute photograph of some examples of ceramics manufactured by a reappointing method of manufacturing a thixotropic ceramic according to an embodiment of the present invention.

도 5를 참조하면, 도자기에 불꽃이 접촉하여 그 작용에 따른 발색범위와 색깔 등을 파악할 수 있다.Referring to Figure 5, the flame in contact with the ceramic can grasp the color development range and color according to the action.

기본적으로 가마 내부는 환원분위기로 소성 하는 것을 전제로 하여 설명한다. 불꽃은 기본적으로 완전 연소를 전제하므로 산화분위기를 갖는다. 따라서, 불꽃이 도자기의 표면에 접촉하는 경우 그 접촉한 부분은 유약이 산화작용을 하게 된다. 따라서, 도 5에 도시된 것과 같이 A구역은 산화작용을 하여 산화작용에 의한 색깔이 표현된다. A구역 중 a구역은 불꽃이 직접적으로 닿아 매우 온도가 높게 작용된 부분으로, 발색을 일으키는 구성요소가 증발해버려 백색으로 표현될 수 있다. 또한, 불꽃이 접촉하지 않은 부분인 B구역은 가마 전체가 환원분위기로 소성되므로 환원작용에 의한 색깔이 표현된다.Basically, the inside of the kiln is explained on the premise that it is fired in a reducing atmosphere. The flame has an oxidizing atmosphere because it basically assumes complete combustion. Therefore, when the flame comes into contact with the surface of the porcelain, the glazed portion is oxidized. Therefore, as illustrated in FIG. 5, the zone A is oxidized to express the color due to the oxidation. Area a is the area where the flame is directly touched and the temperature is very high, and the color causing component may evaporate and be expressed in white. In addition, in the zone B, which is not in contact with the flame, the entire kiln is calcined in a reducing atmosphere, and thus color is expressed by the reducing action.

본 발명은 산화구리(CuO)가 포함된 진사 유약을 도자기의 표면에 도포하는 것을 일 예로 한다. 산화구리(CuO)는 진사 유약에서 발색의 역할을 하는 구성요소이다. 산화구리(CuO)는 환원분위기에서 소성하는 경우 적색 내지 자주색을 띠며 강한 환원분위기(일산화탄소(CO) 다량 유입)에서 소성하는 경우 흑적색 내지 흑색을 띠게 될 수 있다. 산화구리(CuO)는 산화분위기에서 소성하는 경우 녹색 내지 연한 녹색을 띠게 될 수 있다. 그러나, 불꽃이 직접 닿아 유약이 녹는 온도(1250℃)에 비해 높게 된 부분은 산화구리(CuO)가 증발되어 백색으로 표현될 수 있다.The present invention is an example of applying a cinnabar glaze containing copper oxide (CuO) to the surface of the ceramics. Copper oxide (CuO) is a component that plays a role in color development in cinnabar glaze. Copper oxide (CuO) may be red to purple when calcined in a reducing atmosphere and may be blackish red to black when calcined in a strong reducing atmosphere (large inflow of carbon monoxide (CO)). Copper oxide (CuO) may have a green to light green color when fired in an oxidizing atmosphere. However, copper oxide (CuO) is evaporated and may be expressed as white when the flame is directly touched and becomes higher than the melting temperature (1250 ° C.).

도 6을 참조하면 위에서 설명한 여러가지 색깔들이 표현되고 불이 접촉한 모양 등에 따라 독특한 무늬/문양이 형성되는 것을 파악할 수 있다. 이러한 다채로운 색깔과 독특한 문양을 가지는 요변 도자기는 두 번 다시 완전히 동일한 것을 제조할 수 없기에 그 가치는 더욱 높게 매겨질 수 있다.Referring to FIG. 6, it can be seen that various colors described above are expressed and a unique pattern / pattern is formed according to the shape of the fire contact. These colorful colors and unique patterns can make the pottery more valuable because it cannot be produced exactly the same again.

도 7 은 본 발명의 실시예에 따른 요변 도자기를 제조하는 재임방법에 따른 차단격판이 적용될 때의 정면도(a) 및 측면사시도(b)이다.7 is a front view (a) and a side perspective view (b) when the barrier plate according to the reappointment method for manufacturing a thixotropic ceramic according to an embodiment of the present invention is applied.

도 8 은 본 발명의 실시예에 따른 요변 도자기를 제조하는 재임방법에 따른 차단격판이 측면에도 적용될 때의 상부사시도(a) 및 측면사시도(b)이다.8 is a top perspective view (a) and a side perspective view (b) when the barrier plate according to the reappointment method for manufacturing a thixotropic ceramic according to an embodiment of the present invention is also applied to the side.

도 7 (a)를 참조하면 차단격판(100)은 적어도 재임된 도자기의 정면에 적어도 4개가 배치될 수 있다. 도면에는 도자기 재임용 적층 구조물이 5단인 것으로 도시 되었고 이에 맞추어 차단격판(100)이 4개가 배치된 것으로 도시되었다. 다만, 반드시 도 7에 도시된 것과 같이 적층 구조물과 차단격판(100)의 층 수와 개수가 이에 한정되는 것은 아니다. Referring to FIG. 7 (a), at least four blocking plates 100 may be disposed on a front surface of at least one of the pottery boards. In the drawings, the lamination structure for porcelain reaping is illustrated as having five stages, and four blocking plates 100 are arranged accordingly. However, the number and number of layers of the laminated structure and the barrier plate 100 are not necessarily limited thereto, as shown in FIG. 7.

차단격판(100)은 상단에 2개가 서로 나란히 배치되고, 그 하단에 2개가 서로 나란히 배치될 수 있다. 상단과 하단의 각 2개의 차단격판(100)은 좌우로 일정 간격(S)을 두어 배치될 수 있다. 또한, 상단의 차단격판(100)과 하단의 차단격판(100)은 위의 일정 간격(S)보다 작은 간격(T)을 두어 배치될 수 있다. 여기서, 차단격판(100)은 도 7(b)에 표현된 바와 같이 도자기 재임용 적층 구조물 쪽으로 일정 각도 기울여서 기대어 배치될 수 있다. 이는 구조적인 안정성을 강화하기 위함이다. 또한, 상단의 차단격판(100)들은 하단의 차단격판(100)에 인접한 내화판(10)중 가장 최상단의 내화판(10)을 정면 방향으로 돌출시켜 그 돌출된 내화판(10)의 상단 가장자리에 지지되도록 배치될 수 있다. 이 역시 구조적인 안정성을 강화하기 위함이다.Blocking plate 100 may be arranged side by side two to each other, the two at the bottom may be arranged side by side with each other. Each of the two blocking plates 100 at the top and the bottom may be arranged at a predetermined interval S from left and right. In addition, the upper blocking plate 100 and the lower blocking plate 100 may be disposed at a spacing (T) smaller than the predetermined interval (S) above. Here, the blocking plate 100 may be disposed leaning at an angle toward the laminated structure for porcelain reaping, as represented in Figure 7 (b). This is to enhance structural stability. In addition, the upper blocking plate 100 protrudes in front of the fireproof plate 10 of the uppermost end of the fireproof plate 10 adjacent to the lower blocking plate 100 at the upper edge of the protruding fireproof plate 10. It may be arranged to be supported on. This is also to enhance structural stability.

도 8(a)를 참조하면 차단격판(100)은 도자기 재임용 적층 구조물의 양 측면에 적어도 2개가 상하로 일정 간격(T)을 두어 배치될 수 있다. 다만, 정면에 배치되는 차단격판(100)들과 수직에 인접한 각도를 이루어 배치될 수 있다. 이 때, 측면에 배치되는 차단격판(100)은 이에 인접하는 정면에 배치되는 차단격판(100)과 일정 간격(S)보다 크거나 작은 간격(S')을 두어 배치될 수 있다. 여기서, 차단격판(100)은 도 8(b)에 표현된 바와 같이 도자기 재임용 적층 구조물 쪽으로 일정 각도 기울여서 기대어 배치될 수 있다. 이는 전술한 도 7(b)에서 언급한 정면에 배치되는 차단격판(100)에 대한 설명과 동일하다. 이는 구조적인 안정성을 강화하기 위함이다.Referring to FIG. 8 (a), at least two barrier plates 100 may be disposed at both sides of a sidewall of the laminated structure for ceramic ware at regular intervals T. However, it may be disposed at an angle adjacent to the vertical and the blocking plate 100 is disposed in the front. At this time, the blocking plate 100 is disposed on the side may be arranged with a space (S ') greater or less than a predetermined distance (S) and the blocking plate 100 disposed in the front adjacent thereto. Here, the blocking plate 100 may be disposed leaning at an angle toward the laminated structure for porcelain reaping, as represented in Figure 8 (b). This is the same as the description of the blocking plate 100 disposed in the front mentioned in FIG. 7 (b). This is to enhance structural stability.

측면에 배치되는 차단격판(100)은 도 8(b)에 표현된 바와 같이 중앙을 관통하는 가상의 축을 중심으로 일정 각도로 회전되어 비스듬하게 배치될 수도 있다. 뿐만 아니라, 앞서 도 7에서 설명하였던 정면에 배치되는 차단격판(100)들 역시 중앙을 관통하는 가상의 축을 중심으로 일정 각도로 회전되어 비스듬하게 배치될 수도 있다. 이는, 불꽃이 흐르는 통로의 모양 등을 조절하여 또 색다른 문양/무늬 등을 나타내는 도자기를 제조할 것을 목적으로 이와 같이 할 수 있다.The blocking plate 100 disposed on the side surface may be rotated at an angle with respect to an imaginary axis passing through the center and beveled as shown in FIG. 8 (b). In addition, the barrier plates 100 disposed on the front surface described above with reference to FIG. 7 may also be rotated at an angle about an imaginary axis passing through the center and arranged obliquely. This can be done in this way for the purpose of manufacturing ceramics showing different patterns / patterns and the like by adjusting the shape of the passage through which the flame flows.

도면에 도시된 바와 같이 차단 격판(100)은 도자기의 정면, 후면, 좌우측면 모두에 배치될 수도 있다. 그러나 반드시 이에 한정되는 것은 아니고, 경우에 따라 배치되는 위치가 정면과 좌우측면에만, 정면과 좌측면에만, 정면과 우측면에만 배치될 수도 있다. 또한, 그 개수가 변경될 수 있다.As shown in the figure, the blocking plate 100 may be disposed on both the front, rear, left and right sides of the porcelain. However, the present invention is not limited thereto, and in some cases, the positions may be disposed only on the front and left and right sides, only on the front and left sides, and only on the front and right sides. In addition, the number can be changed.

본 실시예는 본 발명의 기술적 사상을 예시적으로 설명한 것에 불과하고, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자라면 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 본 실시예의 다양한 수정 및 변형이 가능할 것이다. 본 실시예는 본 발명의 기술적 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 따라서 본 실시예에 의하여 본 발명의 권리범위가 한정되는 것은 아니다. 본 발명의 보호범위는 청구범위에 의하여 해석되어야 하며, 그와 동등하거나 균등하다고 인정되는 모든 기술적 사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 한다.The present embodiment is merely illustrative of the technical idea of the present invention, and those skilled in the art to which the present invention pertains various modifications and variations of the present embodiment without departing from the essential characteristics of the present invention. It will be possible. The present embodiment is not intended to limit the technical spirit of the present invention but to explain, and thus, the scope of the present invention is not limited by the present embodiment. The scope of protection of the present invention should be construed by the claims, and all technical ideas deemed equivalent or equivalent thereto should be construed as being included in the scope of the present invention.

Claims

봉통과, 봉통과 연결되는 복수의 소성칸, 연돌 및 굴뚝으로 이루어진 도자기 소성용 전통 장작가마를 이용하여 요변 도자기를 제조하는 재임방법에 있어서,
불꽃과 소성칸 내부에 재임된 도자기의 사이에 복수개가 배치되는 차단격판을 이용하여 불의 흐름을 불규칙하게 조절하여 도자기 표면에 복수의 색깔과 불규칙한 무늬가 나타나도록 하는 것으로,
상기 차단격판은,
불규칙한 불의 흐름을 유도하기 위하여 복수개가 서로 기 설정된 간격을 두고 틈을 형성하도록 배치되며,
상기 차단격판에 의하여 일부 불꽃은 차단되고 나머지 불꽃 중 적어도 일부는 상기 틈을 통과하여 상기 차단격판 후면에 위치하는 도자기의 적어도 일부에 접촉하도록 구성되며,
도자기는 산화구리(CuO)를 포함하는 진사유약이 도포되고,
상기 차단격판에 의하여 불꽃이 접촉하지 않는 부분은 환원분위기에 의하여 적색 내지 흑적색을 나타내고,
상기 복수의 차단격판 간 틈을 통하여 불꽃이 접촉한 부분은 산화분위기에 의하여 녹색을 나타내며,
상기 복수의 차단격판 간 틈을 통하여 유입된 불꽃이 접촉한 부분은 직접 접촉부분과 그 인접부분으로 구분할 수 있고,
상기 직접 접촉부분은 상기 산화구리가 증발됨에 의하여 백색을 나타내고, 상기 인접부분은 녹색을 나타내고,
상기 차단격판은,
상기 소성칸 내부에 재임된 도자기의 정면에 적어도 4개가 배치되며,
상단 및 하단 각각에 적어도 2개가 나란히 일정 간격(S)을 두어 배치되고 상단과 하단의 차단격판은 상기 일정 간격(S)보다 작은 일정 간격(T)을 두어 배치되는 것
을 특징으로 하는 요변 도자기를 제조하는 재임방법.In the reappointment method of manufacturing a thixotropic pottery by using a traditional firewood kiln for pottery firing consisting of a bong and a plurality of calcination bars, stacks and chimneys connected to the bong,
By controlling the flow of fire irregularly by using a plurality of barrier plates arranged between the flame and the pottery served inside the baking box, a plurality of colors and irregular patterns appear on the surface of the ceramic.
The blocking plate,
In order to induce an irregular fire flow, a plurality are arranged to form a gap at a predetermined interval from each other,
Some of the flame is blocked by the barrier plate and at least some of the remaining flame passes through the gap and is configured to contact at least a portion of the ceramics located at the rear of the barrier plate,
Ceramics are coated with cinnabar glaze containing copper oxide (CuO),
The part where the flame does not contact by the blocking plate shows red to black red by the reducing atmosphere,
The portion of the flame contacted through the gap between the plurality of blocking plates is green by the oxidation atmosphere,
The portion of the flame introduced through the gap between the plurality of blocking plates can be divided into a direct contact portion and its adjacent portion,
The direct contact portion is white as the copper oxide is evaporated, the adjacent portion is green,
The blocking plate,
At least four are disposed on the front of the pottery served in the baking bin,
At least two of each of the upper and lower sides are arranged side by side at a predetermined interval (S) and the upper and lower barrier plates are arranged at a predetermined interval (T) smaller than the predetermined interval (S).
Reappointment method for manufacturing a thixotropic pottery characterized in that.

삭제delete

제1항에 있어서,
상기 차단격판은,
양 측면에 적어도 2개가 상하로 일정 간격(T)를 두어 배치되되 정면에 배치되는 적어도 4개의 차단격판과 수직을 이루며 배치되는 것
을 특징으로 하는 요변 도자기를 제조하는 재임방법.The method of claim 1,
The blocking plate,
At least two on each side are arranged at a predetermined interval (T) up and down, and are arranged perpendicular to at least four blocking plates arranged in front
Reappointment method for manufacturing a thixotropic pottery characterized in that.

제6항에 있어서,
상기 측면에 배치되는 차단격판은,
상기 정면에 배치되는 차단격판과 상기 일정 간격(S)보다 크거나 작은 일정 간격(S')을 두어 배치되는 것
을 특징으로 하는 요변 도자기를 제조하는 재임방법.The method of claim 6,
Blocking plate disposed on the side,
The barrier plate disposed in the front and the predetermined interval (S ') greater than or smaller than the predetermined interval (S) is disposed
Reappointment method for manufacturing a thixotropic pottery characterized in that.

제7항에 있어서,
상기 복수의 차단격판은 서로 평행하지 않고 일정 각도를 이루며 배치되는 것
을 특징으로 하는 요변 도자기를 제조하는 재임방법.The method of claim 7, wherein
The plurality of blocking plates are arranged at an angle not parallel to each other
Reappointment method for manufacturing a thixotropic pottery characterized in that.