KR101189156B1 - Electromagnetic Wave Absorbing Fabric Article - Google Patents
Electromagnetic Wave Absorbing Fabric Article Download PDFInfo
- Publication number
- KR101189156B1 KR101189156B1 KR1020110007754A KR20110007754A KR101189156B1 KR 101189156 B1 KR101189156 B1 KR 101189156B1 KR 1020110007754 A KR1020110007754 A KR 1020110007754A KR 20110007754 A KR20110007754 A KR 20110007754A KR 101189156 B1 KR101189156 B1 KR 101189156B1
- Authority
- KR
- South Korea
- Prior art keywords
- synthetic
- electromagnetic wave
- fabric layer
- fabric
- conductive
- Prior art date
Abstract
본 발명은 전기전도도를 가진 전도성 섬유와 합성섬유를 혼합 연사하여 제작한 전도성 혼합섬유를 위사/경사로 사용하여 직물형태로 제작함으로써 특정 표면저항을 갖는 전도성 혼합직물층; 섬유 고유의 유전율을 갖는 합성섬유를 위사/경사로 사용하여 직물형태로 제작한 제 1 합성직물층; 상기 전도성 혼합직물을 외부환경으로부터 보호하기 위한, 합성섬유를 위사/경사로 사용하여 직물형태로 제작한 제 2 합성직물층; 및 입사된 전자파를 반사하는 기능의 금속 배면층을 포함하는 직물형 전자파 흡수체에 관한 것으로, 본 발명의 직물형 전자파 흡수체에 전자파가 입사되는 경우, 상기 전자파는 본 발명의 직물형 전자파 흡수체를 구성하는 직물들의 도전손실과 유전손실에 의해 흡수된다. The present invention is a conductive mixed fabric layer having a specific surface resistance by producing a fabric form using a conductive mixed fiber produced by mixing and twisting the conductive fiber and the synthetic fiber having electrical conductivity as a weft / inclination; A first synthetic fabric layer made of a woven fabric using a synthetic fiber having a dielectric constant inherent to the fiber as a weft / tilt; A second synthetic fabric layer fabricated in the form of a fabric using a synthetic fiber as a weft / tilt to protect the conductive mixed fabric from an external environment; And a metal backing layer having a function of reflecting incident electromagnetic waves. When the electromagnetic wave is incident on the textile type electromagnetic wave absorber of the present invention, the electromagnetic wave constitutes the textile type electromagnetic wave absorber of the present invention. Absorbed by the conductive and dielectric losses of the fabrics.
Description
본 발명은 입사되는 전자파를 직물 내 섬유의 도전 및 유전손실에 의해 흡수하는 직물형태의 전자파 흡수체에 관한 것이다.The present invention relates to an electromagnetic wave absorber in the form of a fabric that absorbs incident electromagnetic waves by conduction and dielectric loss of the fibers in the fabric.
본 발명의 전자파 흡수체는 직물구조 조직 형태를 이용하여 전자파 흡수성능이 구현되도록 함으로써, 전자파 흡수의 임의 조절이 가능하다. 또한 흡수체 기본조직을 유연한 형태의 섬유 및 직물구조를 사용함으로써, 기존 평판 형태의 전자파 흡수체에 비하여 장착성이 매우 우수하며, 대량생산에 용이한 직물구조를 사용하여 제작시 경제성도 우수하다.
The electromagnetic wave absorber of the present invention by using the fabric structure tissue form to implement the electromagnetic wave absorption performance, it is possible to arbitrarily control the electromagnetic wave absorption. In addition, by using a flexible fiber and fabric structure of the absorber basic structure, it is very easy to install compared to the conventional electromagnetic wave absorber of the flat plate type, and economical when manufacturing using a fabric structure that is easy to mass production.
과학기술의 발달에 따라 일상 생활에서 전자파를 사용하는 전자 및 통신기기는 날로 증대되고 있으며, 특히 무기체계의 전자파를 사용하는 통신 및 탐지장비는 첨단기술로 고도화되고 있는 실정이다. 즉, 민간 및 군 분야에 걸쳐서 사람들은 현재 복잡한 전자파 환경에 노출되어 있다고 할 수 있다. 따라서, 민간 및 군사 등 특정목적으로 전자파 환경을 임의로 제어할 필요가 있다.BACKGROUND With the development of science and technology, electronic and communication devices that use electromagnetic waves in everyday life are increasing day by day, and in particular, communication and detection equipment using electromagnetic waves of weapon systems are being advanced with high technology. In other words, people in civilian and military fields are currently exposed to complex electromagnetic environment. Therefore, there is a need to arbitrarily control the electromagnetic environment for specific purposes such as civilian and military.
특히 군 분야에서, 군사 목적으로 입사된 전자파의 특정 주파수를 흡수하여 적으로부터 탐지되지 않도록 하는 전자파 흡수체의 경우, 전자파 흡수성능 뿐만 아니라 장착성 및 경제성까지 고려되어야 한다.
Particularly in the military field, in the case of an electromagnetic wave absorber that absorbs a specific frequency of electromagnetic wave incident for military purposes so that it is not detected from the enemy, not only the electromagnetic wave absorbing performance but also the mounting and economical efficiency should be considered.
본 발명의 목적은 전도성 섬유와 합성섬유를 혼합 연사하여 제작한 전도성 혼합섬유와 합성섬유로 제작한 혼합직물층의 도전손실, 합성섬유층의 유전손실을 이용하여 전자파를 흡수할 수 있는 직물형태의 전자파 흡수체를 제공하는 것이다.
An object of the present invention is a fabric type electromagnetic wave that can absorb the electromagnetic waves by using the conductive loss of the mixed composite fabric made of the mixed and twisted conductive fibers and synthetic fibers, the dielectric loss of the synthetic fiber layer It is to provide an absorbent body.
본 발명의 직물형 전자파 흡수체는, 전기전도도를 가진 전도성 섬유와 합성섬유를 혼합 연사하여 제작한 전도성 혼합섬유를 위사 및 경사로 사용하여 직조한 전도성 혼합직물층; 섬유 고유의 유전율을 갖는 합성섬유를 위사 및 경사로 사용하여 직조한 제 1 합성직물층; 상기 전도성 혼합직물층을 외부환경으로부터 보호하기 위한, 합성섬유를 위사 및 경사로 사용하여 직조한 제 2 합성직물층; 및 입사된 전자파를 반사하는 기능의 금속 배면층을 포함하는 것을 특징으로 한다.
Fabric-type electromagnetic wave absorber of the present invention, the conductive mixed fabric layer woven using a conductive blended fiber produced by mixing and twisting the conductive fiber and the synthetic fiber having electrical conductivity with a weft and warp; A first synthetic fabric layer woven using a weft and warp yarn of synthetic fibers having a dielectric constant inherent to the fiber; A second synthetic fabric layer woven using synthetic fibers in a weft and warp yarn for protecting the conductive mixed fabric layer from an external environment; And a metal back layer having a function of reflecting incident electromagnetic waves.
본 발명에 따른 직물형 전자파 흡수체는, 전자파 흡수 효과를 나타내기 위하여, 전도성 혼합직물층의 보호목적을 갖는 제 2 합성직물층이 외부환경과 접촉하는 최외측에 위치하고, 그 아래로 전도성 혼합직물층, 제 1 합성직물층 및 금속 배면층의 순서로 적층된 구성을 갖는 것을 특징으로 한다.
In the fabric type electromagnetic wave absorber according to the present invention, in order to exhibit the electromagnetic wave absorbing effect, the second synthetic fabric layer having a protective purpose of the conductive mixed fabric layer is located at the outermost side in contact with the external environment, and the conductive mixed fabric layer thereunder. , Characterized in that it has a configuration laminated in the order of the first synthetic fabric layer and the metal back layer.
본 발명의 직물형 전자파 흡수체에 사용되는 상기 전도성 혼합직물층은 전도성 섬유와 합성섬유를 혼합 연사하여 제작된 전도성 혼합섬유를 위사 및 경사로 사용하여 평직, 능직 또는 사문직 등을 포함하는 일반적인 직조방법에 의해 직물형태로 제작될 수 있다.The conductive mixed fabric layer used in the fabric-type electromagnetic wave absorber of the present invention is formed by weaving and inclining the conductive mixed fiber produced by mixing and twisting the conductive fiber and the synthetic fiber by a general weaving method including plain weave, twill or serpentine weave. It can be manufactured in the form of a fabric.
상기 전도성 혼합섬유에 사용되는 상기 전도성 섬유는 합성섬유 표면에 코팅된 구리, 금 또는 은과 같은 전도성 금속을 포함하여 이루어진다. 상기 전도성 혼합섬유는 상기와 같이 고유한 전기전도도를 갖는 전도성 섬유와 합성섬유를 혼합 연사하여 제조될 수 있다. 상기 전도성 섬유 및 전도성 혼합섬유의 제조에 사용가능한 합성섬유로는 특별한 제한없이 일반적인 합성섬유가 사용될 수 있으며, 예로서 폴리에스테르, 아크릴, 나일론 또는 케블라 등으로부터 선택될 수 있다.The conductive fiber used in the conductive mixed fiber comprises a conductive metal such as copper, gold or silver coated on the surface of the synthetic fiber. The conductive mixed fiber may be prepared by mixing and twisting a conductive fiber and a synthetic fiber having a unique electrical conductivity as described above. As the synthetic fibers usable in the production of the conductive fibers and the conductive mixed fibers, general synthetic fibers may be used without particular limitation, and for example, may be selected from polyester, acrylic, nylon or kevlar.
상기 전도성 혼합직물층은 직조시 선택적으로 일반적인 합성섬유와 함께 직조될 수 있으며, 이러한 합성섬유들로는 폴리에스테르, 아크릴, 나일론 또는 케블라로부터 선택되는 것들이 사용될 수 있다.The conductive blend fabric layer may optionally be woven together with common synthetic fibers when woven, and those selected from polyester, acrylic, nylon or kevlar may be used.
상기 전도성 혼합직물층은 직조시 위사 및 경사의 간격, 합성섬유의 직물구조의 형태 등과 같은 파라미터들에 따라 그 전기전도도 및 표면저항을 필요에 따라 변화시켜 전자파 흡수성능을 조절할 수 있다.
The conductive mixed fabric layer can control the electromagnetic wave absorbing performance by changing the electrical conductivity and surface resistance as necessary according to parameters such as weft and warp spacing, the shape of the fabric structure of synthetic fibers, and the like when weaving.
본 발명의 직물형 전자파 흡수체에 사용되는 상기 제 1 합성직물층 및 제 2 합성직물층은 합성섬유를 위사 및 경사로 사용하여 평직, 능직 또는 사문직 등을 포함하는 일반적인 직조방법에 위해 직물형태로 제작될 수 있으며, 사용된 섬유종류에 따라 특정 유전율 및 두께를 갖는다. 본 발명에서 제 1 합성직물층은 유전손실특성을 갖는 합성섬유로 직조되어 입사되는 전자기파의 유전손실을 일으키며, 전자파 흡수성능의 조절을 위해 합성섬유의 두께 또는 그 종류는 변화될 수 있다.The first synthetic fabric layer and the second synthetic fabric layer used in the woven electromagnetic wave absorber of the present invention may be manufactured in the form of a fabric for a general weaving method including plain weave, twill or serpentine using synthetic fibers as weft and warp yarns. It may have a specific permittivity and thickness depending on the type of fiber used. In the present invention, the first synthetic fabric layer is woven into a synthetic fiber having a dielectric loss characteristic to cause a dielectric loss of incident electromagnetic waves, and the thickness or type of the synthetic fibers may be changed to control the electromagnetic wave absorption performance.
상기 제 1 합성직물층 및 제 2 합성직물층에 사용되는 합성섬유는 특별히 제한되지는 않지만, 폴리에스테르, 아크릴, 나일론 또는 케블라 등으로부터 선택될 수 있다. 특히, 상기 제 2 합성직물층은 전도성 혼합직물을 보호하기 위한 것으로, 전도성 혼합직물의 외측에 사용되며, 제 1 합성직물층에 사용된 것과 동일한 합성섬유가 사용될 수 있으나 제 1 합성직물층에 비해 염색성이 양호한 것들이 사용될 수 있다.Synthetic fibers used in the first synthetic fabric layer and the second synthetic fabric layer is not particularly limited, but may be selected from polyester, acrylic, nylon or kevlar. In particular, the second synthetic fabric layer is to protect the conductive blended fabric, which is used on the outside of the conductive blended fabric, the same synthetic fibers used in the first synthetic fabric layer can be used, but compared to the first synthetic fabric layer Those with good dyeability can be used.
본 발명의 전자파 흡수체에 사용되는 상기 금속배면층은 전자파를 반사할 수 있는 알루미늄, 철, 구리 또는 카본으로부터 선택되는 전도성 금속성 성분을 포함한 층인 것을 특징으로 한다. 상기 금속 배면층은 장착되는 부분의 형태 및 목적에 따라, 금속판 또는 금속성분이 포함된 직물층의 형태일 수 있다.The metal backing layer used in the electromagnetic wave absorber of the present invention is characterized by being a layer containing a conductive metallic component selected from aluminum, iron, copper or carbon capable of reflecting electromagnetic waves. The metal backing layer may be in the form of a metal layer or a fabric layer containing a metal component, depending on the shape and purpose of the mounting portion.
본 발명의 전자파 흡수체의 전자파 흡수성능은 전도성 혼합섬유의 간격 및 전기전도도, 제 1 합성직물층 및 제 2 합성직물층의 유전율 및 두께에 따라 조절가능하다. 본 발명의 전자파 흡수체는 전자기파, 일반적으로 1cm~1mm의 파장을 갖는 밀리미터파(Millimeter Wave: MMW)의 차단에 적용되며, 특히 군사목적의 밀리미터파인 3~95GHz 대역의 밀리미터파를 효과적으로 흡수하는데 사용될 수 있으며, 전자파에 대한 반사손실로서 적어도 -10dB 이상의 반사 손실을 달성한다.
The electromagnetic wave absorbing performance of the electromagnetic wave absorber of the present invention can be adjusted according to the spacing and electrical conductivity of the conductive mixed fiber, the dielectric constant and the thickness of the first synthetic fabric layer and the second synthetic fabric layer. The electromagnetic wave absorber of the present invention is applied to the blocking of electromagnetic waves, in general, millimeter wave (MWW) having a wavelength of 1 cm to 1 mm, and particularly can be used to effectively absorb millimeter waves in the band of 3 to 95 GHz, which are military millimeter waves. And return loss of at least -10 dB as return loss to electromagnetic waves.
본 발명에 따른 직물형 전자파 흡수체는 전도성 혼합직물층을 구성하는 전도성 혼합섬유의 전기전도도와 경사/위사의 간격, 합성직물의 두께 및 유전율과 같은 섬유의 전기 및 물리적 특성만을 이용하여 전자파 손실을 발생하는 메커니즘을 구현함으로써, 별도의 전자파 흡수를 위한 구성품이 필요하지 않다. 또한, 본 발명에 따른 직물형 전자파 흡수체는 유연한 섬유 및 직물 형태를 가져, 기존의 평판 형태의 전자파 흡수체에 비하여 복잡한 형상의 몸체 또는 부위에의 장착성이 매우 우수하며, 대량 생산 및 제작비 절감 효과가 뛰어나 경제적이다.The fabric type electromagnetic wave absorber according to the present invention generates an electromagnetic wave loss using only the electrical and physical properties of the fiber, such as the electrical conductivity of the conductive mixed fiber constituting the conductive mixed fabric layer, the interval between the warp / weft, the thickness and the dielectric constant of the composite fabric. By implementing a mechanism, a separate component for absorbing electromagnetic waves is not required. In addition, the fabric-type electromagnetic wave absorber according to the present invention has a flexible fiber and fabric form, and compared to the conventional electromagnetic wave absorber of the flat plate type is very excellent in mounting to a complex body or part, excellent in mass production and manufacturing cost reduction effect It is economical.
특히 본 발명에 따른 직물형 전자파 흡수체는 군용 목적으로 많이 사용되는 35GHz의 주파수에서 -10dB의 반사 손실을 달성할 수 있다.
In particular, the fabric type electromagnetic wave absorber according to the present invention can achieve a return loss of -10 dB at a frequency of 35 GHz which is widely used for military purposes.
도 1은 본 발명의 일 실시예에 따른 직물형 전자파 흡수체(10)의 상세도이다.
도 2a 및 도 2b는 각각 본 발명에 따른 직물형 전자파 흡수체의 사용예를 나타낸다.
도 3은 본 발명에 따른 직물형 전자파 흡수체(10)의 분해 사시도로, 제 2 합성직물층(300), 전도성 혼합직물층(100), 제 1 합성직물층(200) 및 금속 배면층(400)으로 구성된 예를 나타낸다.
도 4a 및 도 4b는 본 발명에 따른 직물형 전자파 흡수체의 전도성 혼합직물층(100)의 각각 상이한 직조구조의 예시적인 구성을 나타낸다.
도 5는 본 발명에 따른 직물형 전자파 흡수체에서, 전도성 섬유(120) 및 합성섬유(220)를 연사하여 제조된 전도성 혼합섬유(110)의 한 예를 나타낸다.
도 6은 본 발명에 따른 직물형 전자파 흡수체에서, 제 1 합성직물층의 구성의 한 예를 나타낸다.
도 7은 본 발명에 따른 직물형 전자파 흡수체에서, 제 2 합성직물층의 구성의 한 예를 나타낸다.
도 8은 본 발명에 따른 직물형 전자파 흡수체의 금속 배면층(400)의 한 예를 나타낸다.1 is a detailed view of the fabric-type electromagnetic wave absorber 10 according to an embodiment of the present invention.
2A and 2B show an example of use of the fabric type electromagnetic wave absorber according to the present invention.
3 is an exploded perspective view of the fabric type electromagnetic wave absorber 10 according to the present invention, wherein the second synthetic fabric layer 300, the conductive mixed
4A and 4B show exemplary configurations of different weave structures of the conductive mixed
5 shows an example of the conductive mixed
6 shows an example of the configuration of the first synthetic fabric layer in the fabric type electromagnetic wave absorber according to the present invention.
7 shows an example of the configuration of the second synthetic fabric layer in the fabric type electromagnetic wave absorber according to the present invention.
8 shows an example of the metal backing layer 400 of the fabric type electromagnetic wave absorber according to the present invention.
이하에서, 본 발명에 따른 직물형 전자파 흡수체를 도면을 참조하여 보다 상세하게 설명한다. 본 명세서에서는 서로 다른 실시예라도 동일?유사한 구성에 대해 동일?유사한 번호를 부여하였으며, 상기 번호에 대한 설명은 최초 설명된 내용과 동일한 것으로 갈음한다. 본 명세서에서 사용되는 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현도 포함한다.Hereinafter, a fabric type electromagnetic wave absorber according to the present invention will be described in more detail with reference to the accompanying drawings. In the present specification, different embodiments are given the same or similar numbers for the same or similar components, and the description of the numbers is replaced with the same as the first description. As used herein, the singular forms "a", "an" and "the" are intended to include the plural forms as well, unless the context clearly indicates otherwise.
본 발명의 일 실시예에 따른 직물형 전자파 흡수체(10)를 도 1에 나타내었으며, 이는 전도성 혼합직물층(100), 제 1 합성직물층(200), 제 2 합성직물층(300), 금속 배면층(400)을 포함하여 이루어진다.A fabricated electromagnetic wave absorber 10 according to an embodiment of the present invention is shown in FIG. 1, which is a conductive mixed
상기 도 1의 전도성 혼합직물층(100)은 폴리에스테르, 아크릴 및 나일론 등으로부터 선택되는 합성섬유(210)에 구리, 금, 은 또는 카본 등의 금속성분이 코팅된 전도성 섬유(120), 및 폴리에스테르, 아크릴, 나일론 및 케블라 등으로부터 선택되는 특정 유전율을 갖는 합성섬유(220)를 혼합 연사하여 제조된 전도성 혼합섬유(110)를 전도성 혼합직물층(100)의 경사 및 위사로 사용하여 직조하여 제조된다. 전도성 혼합섬유(110)는 경사 및 위사에 모두 사용되며, 합성섬유(230)가 선택적으로 경사 및/또는 위사에 함께 사용되어 전도성 혼합직물층을 제조할 수도 있다.The conductive mixed
도 1의 제 1 합성직물층(200) 및 제 2 합성직물층(300)은 폴리에스테르, 아크릴, 나일론 및 케블라 등 특정 유전율을 갖는 합성섬유(240)를 경사 및 위사로 사용하여 직조하여 제조된다.The first synthetic fabric layer 200 and the second synthetic fabric layer 300 of FIG. 1 are manufactured by weaving using synthetic fibers 240 having a specific dielectric constant such as polyester, acrylic, nylon, and kevlar as warp and weft yarns. .
도 1의 금속 배면층(400)은 구리, 금, 은 또는 카본 등으로부터 선택된 금속의 박판 또는 시트일 수 있다.The metal backing layer 400 of FIG. 1 may be a thin plate or sheet of metal selected from copper, gold, silver, carbon, or the like.
도 2a 및 도 2b는 본 발명에 따른 직물형 전자파 흡수체의 사용한 예를 나타내는 것으로, 본 발명에 따른 직물형 전자파 흡수체(10)가 레이더 탐지센서가 부착된 항공기나 지능형 포탄으로부터 전자파 흡수를 통해 은폐가능한 위장막으로 사용가능하며, 또한 적의 레이더에 의한 탐지 및 사격을 제어함으로써 생존성을 향상시킬 수 있는 위장망으로 사용될 수 있음을 보여준다.2A and 2B show an example of using the fabric type electromagnetic wave absorber according to the present invention, wherein the fabric type electromagnetic wave absorber 10 according to the present invention is concealable through electromagnetic wave absorption from an aircraft or an intelligent shell equipped with a radar detection sensor. It can be used as a gastrointestinal membrane, and it can also be used as a gastrointestinal network that can improve survivability by controlling detection and shooting by enemy radar.
도 3은 본 발명에 따른 직물형 전자파 흡수체(10)의 분해사시도로서, 흡수체 성능유지를 위하여 제 2 합성직물층(300), 전도성 혼합직물층(100), 제 1 합성직물층(200), 금속배면층(400)의 순서로 적층, 조립되어 있다.3 is an exploded perspective view of the fabric type electromagnetic wave absorber 10 according to the present invention, the second synthetic fabric layer 300, the conductive mixed
도 4a는 본 발명에 따른 직물형 전자파 흡수체(10)의 전도성 혼합직물층(100)을 평직으로 직조한 예를 나타내는 구성도이다. 상기 전도성 혼합직물층(100)은 폴리에스테르, 아크릴 및 나일론 등으로부터 선택되는 합성섬유(210)에 구리, 금, 은 및 카본 등으로부터 선택된 금속성분이 코팅된 전도성 섬유(120), 및 폴리에스테르, 아크릴, 나일론, 케블라 등으로부터 선택되는 합성섬유(220)를 혼합 연사하여 제조된 전도성 혼합섬유(110)를 경사/위사로 사용하여 직조된다. 특히 전자파 흡수 성능과 관련하여 경사 및 위사로 공급되는 전도성 혼합섬유(110)의 간격과 패턴의 영향이 크므로, 이의 고정을 위하여 전도성 혼합섬유(110) 사이에 합성섬유(230)를 함께 위치시켜, 간격의 균일성과 직물 촉감의 향상을 꾀하고 있다.Figure 4a is a block diagram showing an example of weaving the conductive mixed
도 4b는 본 발명에 따른 직물형 전자파 흡수체(10)의 전도성 혼합직물층(100)의 다른 예로서, 전도성 혼합섬유(110)와 합성섬유(230)를 직물에 따라 경사 및 위사로 사용하여 서로 다른 직물 패턴으로 구현한 전도성 혼합직물층(100)의 예들을 나타낸다.Figure 4b is another example of the conductive mixed
도 5는 본 발명에 따른 직물형 전자파 흡수체(10)에서, 전도성 혼합직물층에 사용된 전도성 혼합섬유(110)의 예를 나타내며, 기본 섬유인 폴리에스테르, 아크릴, 나일론, 케블라 등의 합성섬유(220) 및 폴리에스테르, 아크릴, 나일론 등의 기반 합성섬유(210)에 구리, 금, 은, 카본 등의 금속성분이 코팅된 전도성 섬유(120)가 혼합 연사되어 있는 형태를 나타낸다.5 shows an example of the conductive mixed
도 6 및 도 7은 본 발명에 따른 직물형 전자파 흡수체(10)에서, 제 1 합성직물층(200) 및 제 2 합성직물층(300)의 구성도로서, 폴리에스테르, 아크릴, 나일론, 케블라 등 고유 유전율을 가진 일반 합성섬유(240)를 경사와 위사로 사용하여 직조하여 제조한 예를 나타낸다.6 and 7 are schematic diagrams of the first synthetic fabric layer 200 and the second synthetic fabric layer 300 in the fabric type electromagnetic wave absorber 10 according to the present invention, such as polyester, acrylic, nylon, Kevlar, and the like. It shows an example manufactured by weaving using a general synthetic fiber 240 having an intrinsic dielectric constant as a warp and weft.
도 8은 본 발명에 따른 직물형 전자파 흡수체(10)의 금속 배면층(400)으로 구리, 금, 은, 카본 등의 금속의 박판 또는 시트의 형태이다.
8 is a metal backing layer 400 of the fabric type electromagnetic wave absorber 10 according to the present invention in the form of a thin plate or sheet of metal such as copper, gold, silver, and carbon.
실시예Example
전도성 섬유로서 구리성분이 도금된 아크릴 섬유(75데니어, 단면적 4347.82㎛2, 전도성 4347.82)와 100데니어 굵기의 폴리에스테르 섬유를 혼합 연사하여 전도성 혼합섬유를 제조하였다. 제조된 전도성 혼합섬유를 경사 및 위사로 사용하여 평직구조로 전도성 혼합직물층을 제조하였다(경사굵기: 100데니어, 위사굵기: 150데니어, 표면 저항성: 200Ω/m2).Copper conductive plated acrylic fiber (75 denier, cross-sectional area 4347.82㎛ 2, conductive 4347.82) and 100 denier thick polyester fiber as a conductive fiber was mixed and twisted to prepare a conductive mixed fiber. Using the prepared conductive mixed fibers as warp and weft yarn, a conductive mixed fabric layer was prepared in a plain weave structure (incline thickness: 100 denier, weft thickness: 150 denier, surface resistance: 200 Ω / m 2 ).
직물 특유의 유연성, 제작성 및 경제성을 고려하여 폴리에스테르 합성섬유를 사용하여 평직구조의 제 1 합성직물층을 제조하였다(경사굵기: 300데니어, 위사굵기: 100데니어, 밀도: 0.298g/cm3). 구형 도파관을 이용하여 34GHz~36GHz 영역에서 제 1 합성직물층의 유전율을 측정시, 유전율은 약 1.5로 측정되었다. In consideration of the fabric's unique flexibility, manufacturability and economy, a first synthetic fabric layer having a plain weave structure was prepared using polyester synthetic fibers (incline thickness: 300 denier, weft thickness: 100 denier, density: 0.298 g / cm 3). ). When measuring the dielectric constant of the first composite fabric layer in the 34GHz ~ 36GHz region using a rectangular waveguide, the dielectric constant was measured to be about 1.5.
폴리에스테르 합성섬유를 이용하여 보호층인 제 2 합성직물층을 제조하였으며, 금속 배면층으로서 알루미늄판을 이용하였다.A second synthetic fabric layer was used as a protective layer using polyester synthetic fibers, and an aluminum plate was used as the metal backing layer.
상기 준비된 각 층을 이용하여 시편을 제작하였다. 600mm×600mm 크기의 알루미늄 판재인 금속 배면층 위에 상기 제 1 합성직물층, 전도성 혼합직물층, 보호층인 제 2 합성직물층을 접착제를 이용하여 순서대로 적층하여 전자파 흡수체 시편을 제작하였다. 상기 제 1합성직물층의 두께는 1.60mm, 전도성 혼합직물층의 두께는 0.49mm, 제 2합성직물층의 두께는 0.81mm로, 알루미늄 두께를 제외한 상기 제작된 흡수체 시편의 총 두께는 2.90mm였다. Specimens were prepared using the prepared layers. The first synthetic fabric layer, the conductive mixed fabric layer, and the second synthetic fabric layer, which is a protective layer, were sequentially laminated on the metal backing layer of 600 mm × 600 mm aluminum plate by using an adhesive to fabricate an electromagnetic wave absorber specimen. The thickness of the first composite fabric layer was 1.60 mm, the thickness of the conductive mixed fabric layer was 0.49 mm, the thickness of the second composite fabric layer was 0.81 mm, and the total thickness of the fabricated absorbent specimen except for the aluminum thickness was 2.90 mm. .
근거리 전자파 시험(표준과학연구원(KRISS) 시설)에 의해 상기 흡수체 시편의 전자파 흡수성능을 확인하였으며, 26.5GHz~40GHz 대역에 대한 반사손실을 측정하였다.The electromagnetic wave absorbing performance of the absorber specimens was confirmed by a near field test (KRISS facility), and the return loss was measured in the 26.5GHz ~ 40GHz band.
반사손실 측정 결과, 군용목적에 많이 사용되는 주파수인 35GHz에서 -11.48dB의 반사손실을 나타내었다.
As a result of return loss measurement, it showed return loss of -11.48dB at 35GHz, which is used for military purpose.
10...직물형 전자파 흡수체
100...전도성 혼합직물층
200...제 1 합성직물층
300...제 2 합성직물층
400...금속 배면층
110...전도성 혼합섬유
120...전도성 섬유
210, 220, 230, 240...합성섬유10 ... fabric electromagnetic wave absorber
100 ... conductive blended fabric layer
200 ... First Synthetic Fabric Layer
300 ... Second synthetic fabric layer
400 ... metal backing layer
110 ... conductive blended fiber
120 ... conductive fiber
210, 220, 230, 240 ... synthetic fiber
Claims (6)
A conductive mixed fabric layer 100 woven using the conductive mixed fiber prepared by mixing and twisting the conductive fiber and the synthetic fiber with a weft and a warp yarn; A first synthetic fabric layer 200 woven using synthetic fibers as weft and warp yarns; A second synthetic fabric layer 300 for protecting the conductive mixed fabric layer 100, which is woven using synthetic fibers in a weft and warp yarn; And a metal backing layer 400 reflecting incident electromagnetic waves, wherein each of the layers includes a second composite fabric layer 300, a conductive mixed fabric layer 100, a first synthetic fabric layer 200, and a metal backing layer. Woven electromagnetic wave absorber is laminated in the order of (400).
The woven electromagnetic wave absorber of claim 1, wherein the conductive mixed fabric layer (100) further comprises synthetic fibers between the woven conductive mixed fibers.
According to claim 1 or 2, wherein the fabric type electromagnetic wave absorber is located on the outermost side where the second synthetic fabric layer 300 is in contact with the external environment, the conductive mixed fabric layer 100, the first synthetic Fabric type electromagnetic wave absorber, characterized in that laminated in the order of the fabric layer 200 and the metal back layer (400).
[Claim 3] The electromagnetic wave of claim 1, wherein the conductive fiber is coated with a metal selected from copper, gold, silver or carbon on the surface of the synthetic fiber selected from polyester, acrylic, nylon or kevlar. Absorber.
The fabric type electromagnetic wave absorber according to claim 1 or 2, wherein the synthetic fiber is a synthetic fiber selected from polyester, acrylic, nylon or kevlar.