KR100944767B1 - Preparing method of moisture permeable waterproof-processed fabric improved in its excellent dry feel and anti-abrasion property having a pattern visually and moisture permeable waterproof garment thereby and preparing method of seam-sealing tape for making clothing - Google Patents
Preparing method of moisture permeable waterproof-processed fabric improved in its excellent dry feel and anti-abrasion property having a pattern visually and moisture permeable waterproof garment thereby and preparing method of seam-sealing tape for making clothing Download PDFInfo
- Publication number
- KR100944767B1 KR100944767B1 KR1020090028960A KR20090028960A KR100944767B1 KR 100944767 B1 KR100944767 B1 KR 100944767B1 KR 1020090028960 A KR1020090028960 A KR 1020090028960A KR 20090028960 A KR20090028960 A KR 20090028960A KR 100944767 B1 KR100944767 B1 KR 100944767B1
- Authority
- KR
- South Korea
- Prior art keywords
- fabric
- weight
- parts
- moisture
- resistant
- Prior art date
Abstract
Description
본 발명은 건조감 및 의장성이 우수한 내마모 투습방수원단의 제조방법, 그에 의해 제조된 투습방수원단, 방수의류 및 의류봉제용 심실링 테이프의 제조방법에 관한 것으로, 보다 상세하게는, 특정 조성의 표면처리제 수지조성물을 싱크로 인그레이브드 실린더 업로우딩 방식에 의해 투습방수 코팅면 또는 라미네이팅 필름면에 코팅함으로써, 피부에의 직접 접촉시 건조감, 쾌적감 및 냉감을 극대화시키고, 싱크로 인그레이브드 실린더로부터 원단 코팅면에 효과적이고 견고하게 패턴을 전사시킴으로써, 의장성이 부여되어 안감을 생략할 수 있으며, 이에 따라, 경량성과 패커블성이 개선된 투습방수원단, 그를 이용한 패커블성이 우수한 방수의류 및 의류봉제용 심실링 테이프의 제조방법에 관한 것이다. The present invention relates to a method for producing a wear-resistant moisture-proof waterproof fabric excellent in dryness and design, a method for producing a moisture-resistant waterproof fabric, waterproof clothing and sewing seam sealing tape for sewing clothes, and more specifically, The coating agent resin composition is coated on the moisture-permeable waterproof coating surface or the laminating film surface by a synchro-encoded cylinder uploading method to maximize dryness, comfort and coldness upon direct contact with the skin, and By transferring the pattern to the fabric coating surface effectively and firmly, the design is imparted and the lining can be omitted. Accordingly, the waterproof and waterproof fabric with light weight and packability is improved, waterproof clothing and garment sewing with excellent packability. The present invention relates to a method for producing a ventilated sealing tape.
투습방수 코팅원단은 스키, 골프웨어, 하이킹, 등산, 죠깅복 등 각종 액티브 스포츠웨어 및 캐쥬얼웨어에 널리 사용되고 있는 소재로서 겉감지 섬유 원단은 주로 두껍지 않은 합성섬유원단에 투습방수코팅을 하여 제조되는 것이 일반적이다. 또한, 상기 투습방수원단은 외부로부터의 수분을 배척하기 위해 통상적으로 발수가공이 적용되는데 선발수(투습방수 코팅전에 실시) 또는 후발수(투습방수코팅 후 실시)가 적용된다.The waterproof coating fabric is widely used in various active sportswear and casual wear such as skiing, golf wear, hiking, mountain climbing, jogging clothes, etc. The outer textile fabric is mainly manufactured by the waterproof coating of non-thick synthetic fiber fabric. It is common. In addition, the water-repellent waterproof fabric is usually applied to water repellent in order to reject moisture from the outside is applied to the water repellent (executed before the moisture-repellent waterproof coating) or after water repellent (after the moisture-repellent waterproof coating) is applied.
일반적으로 종래의 투습방수원단은 섬유층과 코팅층으로 구성된 2층 구조와 섬유층(겉감), 코팅층 및 섬유층(안감)으로 구성된 3층 구조로 되어 있는데, 2층 구조의 원단은 봉제시 별도로 안감지를 사용함으로써, 결국 3층 구조의 원단으로 되게 마련이다. 따라서, 안감지 부가로 인하여 그만큼 촉감이 둔탁해지고, 부피 및 중량이 커지게 되며, 제조원가도 올라가는 단점이 있어 왔다.In general, the conventional waterproof and waterproof fabric has a two-layer structure consisting of a fiber layer and a coating layer and a three-layer structure consisting of a fiber layer (outer fabric), a coating layer and a fiber layer (lining). In the end, the three-layer fabric will be made. Therefore, due to the addition of the lining paper, the touch becomes dull, the volume and weight are increased, and the manufacturing cost has been disadvantageous.
또한, 방수 방풍용으로 간헐적인 사용을 위한 휴대를 위해 접어서 패킹할 때 부피 및 중량이 커지게 되어 매우 불편하게 되는 문제점이 있어 왔다.In addition, there has been a problem that the volume and weight becomes very uncomfortable when folded and packed for portable for intermittent use for waterproof windproof.
종래에 상술한 바와 같은 목적을 위해 패커블(packable)용으로 2층 구조의 코팅원단에 그라비아 방식으로 인쇄를 하거나 음각무늬 표면처리를 한 제품들이 고안되기는 하였었으나, 이것들은 요철감이 없거나 내마모성, 내스크래치성이 약하고, 특유의 매끄럽고 건조한 감이 부족하여 목적에 충분히 부합하지 못하였다.Conventionally, for the purpose as described above, products for which the gravure printing or the intaglio pattern surface treatment were designed on the two-layer coating fabric for packable use, but these have no unevenness or wear resistance, It is not scratch-resistant and lacks the peculiar smooth and dry feeling.
또한, 요철감을 준 것이라 하더라도 내마모성이나 내스크래치성이 약하여 세탁내구성이 미흡하고, 코팅면의 항균방취 성능 등이 열악하여 운동 시, 땀 등에 의한 악취의 발생을 예방하지 못하는 단점들이 있어왔다.In addition, even if it gives a sense of unevenness, the wear resistance and scratch resistance is weak due to the poor durability of the laundry, the antibacterial deodorization performance of the coating surface, such as poor performance during exercise, there is a disadvantage that can not prevent the occurrence of odor due to sweat.
예를 들어, 대한민국 공개특허공보 제2004-0004301호에서는 요철감을 부여키 위해 표면처리 약제를 발포제로 발포시키는 방법을 사용하였으나, 표면에 발포셀이 형성됨으로 인하여 내마모성이 열악하게 되고, 스크래치시 자국을 남기게 되는 문제점을 안고 있다. 또한 요철부제로 사용하는 돌가루, 규소토, 탄산칼슘 등은 가공후 표면의 슬립성을 부여하기 곤란하며, 세탁이나 드라이크리닝에 대해서 견뢰하지 못한 단점을 지니고 있다.For example, in Korean Patent Laid-Open Publication No. 2004-0004301, a method of foaming a surface treatment agent with a foaming agent is used to give an uneven feeling, but since a foam cell is formed on the surface, wear resistance becomes poor, and scratches are scratched. I have a problem left. In addition, stone powder, silicon earth, calcium carbonate, etc., which are used as uneven subsidiary materials, are difficult to impart slipperiness after processing, and have disadvantages of being unstable against washing or dry cleaning.
제판롤러의 설계에 의한 요철감 발현 측면에서도 상기 특허에서와 같이 필름부식방법에 의해 7∼12㎛ 정도의 심도로 설계를 할 경우 표면처리제 배합물 내 고체물질의 입도 분포상 셀의 심도보다 큰 물질이 존재하기 때문에 정상적인 전사코팅이 이루어지지 않으며, 또한 통상적으로 그라비아 롤상에서 원단으로의 전이율이 70%이상을 넘기기가 현실적으로 곤란하여 표면처리 가공후 실제 코팅원단의 표면으로부터의 부착 높이는 제판상 심도의 30% 이하 수준 정도로 매우 미흡하다.In terms of the appearance of unevenness caused by the design of the plate making roller, when designing with a depth of about 7 to 12 μm by the film corrosion method as in the patent, there is a substance larger than the depth of the cell due to the particle size distribution of the solid material in the surface treatment agent formulation. Since it is not possible to perform normal transfer coating, and it is generally difficult to transfer more than 70% of the gravure roll-to-fabric, the adhesion height from the surface of the actual coating fabric after the surface treatment is 30% of the depth of the plate making. Very low level.
본 발명은 상술한 바와 같은 종래기술의 문제점을 해결하고자 안출된 것으로서, 본 발명의 목적은 건조감 및 내마모성이 우수하여 착용감이 좋을 뿐만 아니라 경량이고 접었을 때 부피가 작아 패커블성이 우수하여 봉제시 안감지를 필요로 하지 않으며 무늬에 의한 의장성을 함께 부여한 투습방수원단의 제조방법을 제공함에 있다.The present invention has been made to solve the problems of the prior art as described above, the object of the present invention is not only good wear feeling due to excellent dry feeling and wear resistance, but also light weight and small volume when folded, excellent packable properties when sewing lining paper It does not need to provide a method of producing a waterproof moisture-repellent fabric, which also gives the design by the pattern.
본 발명의 다른 목적은 상기 방법에 의해 제조되는 건조감 및 내마모성이 우수하고 세탁 내구성이 강한 투습방수원단을 제공함에 있다.Another object of the present invention is to provide a moisture-proof waterproof fabric having excellent drying feeling and abrasion resistance and strong laundry durability.
본 발명의 또 다른 목적은 상기 투습방수원단을 채용하여 봉제된 방수의류 및 의류봉제용 심실링 테이프의 제조방법을 제공함에 있다.Still another object of the present invention is to provide a method of manufacturing a waterproof garment and a garment sewing seam sealing tape by employing the moisture-permeable waterproof fabric.
본 발명은 제직 또는 편직 후 염색 가공된 원단에 투습방수 코팅가공을 수행하는 단계, 상기 투습방수 코팅가공되어 롤상으로 공급되어 온 원단 상에, 그라스 펄; 또는 가교 폴리메틸메타크릴레이트 고분자 미립자 또는 가교 폴리우레탄 고분자 미립자에서 선택되는 내열내용제성 고분자 구상입자;가 함유된 표면처리제 수지조성물을 싱크로 인그레이브드 실린더 업로우딩 방식으로 전사코팅하는 단계 및 상기 전사코팅된 원단을 건조하는 단계를 포함하는 건조감 및 의장성이 부여된 내마모 투습방수원단의 제조방법을 제공한다. The present invention is a step of performing a waterproof coating coating on the dyed fabric after weaving or knitting, on the fabric that has been supplied in a roll to the waterproof coating; Or transfer-coating the surface treating agent resin composition containing a crosslinked polymethyl methacrylate polymer fine particle or crosslinked polyurethane polymer fine particle by a synchro-enclosed cylinder uploading method and the transfer; It provides a method for producing a wear-resistant moisture-proof waterproof fabric provided with a feeling of drying and design, including the step of drying the coated fabric.
본 발명의 제조방법은 상기 투습방수 코팅가공 전 또는 후에, 발수가공 단계를 더 수행할 수 있다. The production method of the present invention may further perform a water repellent step before or after the waterproof coating coating.
본 발명에 있어서, 상기 싱크로 인그레이브드 실린더의 무늬심도는 40 내지 300㎛인 것이 바람직하다.In the present invention, the pattern depth of the synchro-engraved cylinder is preferably 40 to 300㎛.
또한, 본 발명에 있어서, 표면처리제 수지조성물의 바람직한 실시형태로는 폴리우레탄수지(고형분 기준) 100 중량부에 대하여, 혼합유기용제 30 내지 300 중량부, 그라스 펄 30 내지 300 중량부, 안료피그먼트 3 내지 6 중량부, 블록킹 방지제 1.5 내지 15중량부 및 유ㆍ무기복합화합물로 이루어진 커플링제 0.5 내지 2.0 중량부인 것이 바람직하다.In the present invention, preferred embodiments of the surface treatment agent resin composition include 30 to 300 parts by weight of mixed organic solvent, 30 to 300 parts by weight of glass pearl, pigment pigment, based on 100 parts by weight of polyurethane resin (solid content basis). It is preferable that it is 0.5-2.0 weight part of coupling agents which consist of 3-6 weight part, the blocking agent 1.5-15 weight part, and an organic / inorganic compound.
상기 표면처리제 수지조성물의 바람직한 다른 실시형태로는 폴리우레탄수지(고형분 기준) 100 중량부에 대하여, 혼합유기용제 30 내지 300 중량부, 가교 폴리메틸메타크릴레이트 고분자 미립자 또는 가교 폴리우레탄 고분자 미립자에서 선택되는 내열내용제성 고분자 구상입자 30 내지 300 중량부, 안료피그먼트 3 내지 6 중량부 및 블록킹 방지제 1.5 내지 15중량부로 이루어진 표면처리제 수지조성물을 사용하는 것이다.Another preferred embodiment of the surface treating agent resin composition is selected from 30 to 300 parts by weight of mixed organic solvent, crosslinked polymethyl methacrylate polymer particles or crosslinked polyurethane polymer particles with respect to 100 parts by weight of polyurethane resin (based on solids). It is to use a surface treatment agent resin composition consisting of 30 to 300 parts by weight of the heat-resistant solvent-resistant polymer spherical particles, 3 to 6 parts by weight of pigment pigment and 1.5 to 15 parts by weight of antiblocking agent.
상기 표면처리제 조성물에는 무기항균제 또는 바이오세라믹계 소취제가 30 중량부 이하로 더 함유되는 것이 바람직하며, 상기 무기항균제는 무기계 세라믹물질 제올라이트계인 것이 바람직하다.In the surface treating agent composition, an inorganic antimicrobial agent or a bioceramic deodorant may be further contained in an amount of 30 parts by weight or less, and the inorganic antimicrobial agent is preferably an inorganic ceramic material zeolite.
상기 표면처리제 조성물에 있어서, 상기 혼합유기용제는 톨루엔, 메틸에틸케톤, 디메틸포름아마이드, 이소프로필알콜, 크실렌, 퍼클로로에틸렌, 아세톤 및 에틸아세테이트로 이루어지는 군에서 선택되는 둘 이상인 것이다.In the surface treating agent composition, the mixed organic solvent is at least two selected from the group consisting of toluene, methyl ethyl ketone, dimethylformamide, isopropyl alcohol, xylene, perchloroethylene, acetone and ethyl acetate.
또한, 본 발명의 표면처리제 수지조성물의 점도가 2,000∼50,000 cps가 바람직하고, 표면처리제 수지조성물의 전체 고형분은 20∼50%인 것이 바람직하다.Moreover, the viscosity of the surface treating agent resin composition of the present invention is preferably 2,000 to 50,000 cps, and the total solid content of the surface treating agent resin composition is preferably 20 to 50%.
본 발명은 상기 제조방법에 의해 제조되되, 원단의 투습방수 코팅면에 싱크로 인그레이브드 실린더의 무늬심도가 40 내지 300㎛로 전사되어 건조감 및 의장성이 부여된 내마모 투습방수원단을 제공한다.The present invention is manufactured by the above production method, the pattern depth of the synchro-engraved cylinder is transferred to 40 to 300㎛ on the moisture-permeable waterproof coating surface of the fabric to provide a wear-resistant moisture-proof fabric imparting a sense of dryness and design.
또한, 상기 내마모 투습방수원단이 채용되어 봉제된 건조감 및 의장성이 부여된 방수의류를 제공한다.In addition, the wear-resistant breathable waterproof fabric is adopted to provide a waterproof garment with a sense of dryness and design.
나아가, 본 발명은 이형지, 핫멜트 접착제층 및 폴리우레탄 수지로 제조된 내열성수지 필름층이 순차 합지된 심실링테이프 제작용 원단을 제조하고, Furthermore, the present invention manufactures a fabric for fabrication of a seam sealing tape in which a release paper, a hot melt adhesive layer and a heat-resistant resin film layer made of a polyurethane resin are sequentially laminated.
상기 원단 중 내열성수지 필름층 상에, 본 발명의 표면처리제 수지조성물을 싱크로 인그레이브드 실린더 업로우딩 방식으로 전사코팅하여 패턴을 인각한 후, 슬리팅 또는 커팅하여 재단하는 의류봉제용 심실링 테이프의 제조방법을 제공한다.On the heat-resistant resin film layer of the fabric, the surface treatment agent resin composition of the present invention by a transfer coating coating by a synchro-engraved cylinder uploading method to imprint the pattern, and then sewing or cutting seam tape for cutting by cutting or cutting It provides a method of manufacturing.
이때, 상기 표면처리제 조성물에 무기항균제 또는 바이오세라믹계 소취제가 30 중량부 이하로 더 함유될 수 있다.In this case, the surface treatment agent composition may further contain 30 parts by weight or less of inorganic antibacterial or bioceramic deodorant.
또한, 본 발명의 의류봉제용 심실링 테이프는 잔류변형율이 35%이하를 충족한다.In addition, the sewing sewing seam tape of the present invention satisfies the residual strain less than 35%.
본 발명은 투습방수원단 코팅면에 특정 성분의 표면처리제 수지조성물을 싱크로 인그레이브드 실린더 업로우딩 방식에 의해 효과적으로 견고하게 전사시키는 내마모 투습방수원단의 제조방법을 제공할 수 있다.The present invention can provide a method for producing a wear-resistant moisture-proof fabric to effectively and firmly transfer the surface treatment agent resin composition of a specific component on the surface of the moisture-proof waterproof fabric coating by a synchro-engraved cylinder uploading method.
이에, 본 발명은 상기 내마모 투습방수원단의 제조방법에 의하여, 피부에의 직접 접촉시 건조감, 쾌적감 및 냉감을 극대화시키고, 싱크로 인그레이브드 실린더로부터 원단 코팅면에 효과적이고 견고하게 패턴을 전사시킴으로써, 의장성이 부여되어 안감을 생략할 수 있으며, 이에 따라, 경량성과 패커블성이 개선된 투습방수원단, 그를 이용한 방수의류 및 의류봉제용 심실링 테이프의 제조방법을 제공할 수 있다. Accordingly, the present invention maximizes the dryness, comfort and coldness when directly contacting the skin by the method of manufacturing the wear-resistant moisture-proof waterproof fabric, and transfer the pattern to the fabric coating surface from the synchro-engraved cylinder effectively and firmly By doing so, the design is imparted and the lining can be omitted. Accordingly, it is possible to provide a moisture-permeable waterproof fabric having improved light weight and packability, a method for manufacturing waterproof clothing and a seam sealing tape for sewing clothes using the same.
이하, 본 발명을 상세히 설명하고자 한다.Hereinafter, the present invention will be described in detail.
본 발명은 제직 또는 편직 후 염색 가공된 원단에 투습방수 코팅가공을 수행하는 제1단계, 상기 투습방수 코팅가공되어 롤상으로 공급되어 온 원단 상에, 그라스 펄; 또는 가교 폴리메틸메타크릴레이트 고분자 미립자 또는 가교 폴리우레탄 고분자 미립자에서 선택되는 내열내용제성 고분자 구상 입자; 단독 또는 그 혼합형태가 함유된 표면처리제 수지조성물을 싱크로 인그레이브드 실린더 업로우딩 방식으로 전사코팅하는 제2단계 및 상기 전사코팅된 원단을 건조하는 제3단계를 포함하는 건조감 및 의장성이 부여된 내마모 투습방수원단의 제조방법을 제공한다. The present invention is the first step of performing a water-permeable waterproof coating processing on the dyed fabric after weaving or knitting, on the fabric that has been supplied in a roll to the water-resistant waterproof coating, glass pearl; Or heat-resistant solvent-resistant polymer spherical particles selected from cross-linked polymethyl methacrylate polymer microparticles or cross-linked polyurethane polymer microparticles; Imparting dryness and designability, comprising a second step of transferring the surface treating agent resin composition containing a single or mixed form thereof by a synchro-engraved cylinder uploading method and a third step of drying the transfer-coated fabric. It provides a method for producing a wear-resistant waterproof waterproof fabric.
이하, 단계별로 상세히 설명하면, 상기 제1단계에서 투습방수원단은 원단을 직조 또는 편직하고 염색 및 발수 가공처리 한 후, 합성수지 코팅액으로 다이렉트 또는 트랜스퍼 코팅 방법으로 코팅처리한 다음, 롤링된 상태로 공급되거나, 원단 직조 또는 편직 염색 후에 발수가공을 생략하고, 합성수지 코팅액으로 코팅처리하여 발수가공 처리한 후(후발수) 역시 롤링된 상태로 전사코팅공정에 공급될 수 있다.Hereinafter, in detail step by step, the water-permeable waterproof fabric in the first step after weaving or knitting the fabric, dyeing and water repellent processing, coated with a synthetic resin coating solution by direct or transfer coating method, and then supplied in a rolled state Alternatively, after weaving or knitting the fabric, the water repellent may be omitted, the coating may be coated with a synthetic resin coating solution, and the water repellent treatment (post-water repellent) may also be supplied to the transfer coating process in a rolled state.
본 발명의 제조방법은 상기 투습방수 코팅가공 전공정 또는 후공정으로 발수가공 단계를 더 수행할 수 있는데, 상기 투습방수 코팅과 발수가공은 전후를 바꾸어 수행할 수 있으며, 방수원단에서 합성수지 코팅액으로 코팅 하기전에 발수가공하면 선발수, 발수가공을 합성수지 코팅액으로 코팅을 한 후에 실시하면 후발수 가공이라 한다. The manufacturing method of the present invention may further perform a water-repellent step in the previous step or the previous step of the water-permeable waterproof coating processing, the water-repellent waterproof coating and water-repellent processing can be carried out by changing the front and back, coated with a synthetic resin coating solution in a waterproofing fabric If water-repellent is processed before, it is called post-water-repellent process if it is applied after coating water-repellent and water-repellent process with synthetic resin coating solution.
본 발명에 있어서, 상기 전사코팅하는 제2단계는 도 1에 도시된 바와 같이, 싱크로 인그레이브드 실린더(음각롤)의 표면상에 상기 표면처리제 수지조성물을 공급하여 양변부를 막아 수지조성물의 변부 이탈을 막고, 스크랩퍼로 롤(실린더)표면을 균일하게 스크랩핑하여 음각이외의 부위에 있는 수지조성물을 제거한 후 방수원단의 코팅면에 소정의 두께 및 무늬로 전사코팅이 이루어지도록 수행되는 것이 바람직하다.In the present invention, the second step of the transfer coating, as shown in Figure 1 , by supplying the surface treatment agent resin composition on the surface of the synchrographed cylinder (engraved roll) to block both sides to leave the edge of the resin composition It is preferable that the coating is performed to uniformly scrape the surface of the roll (cylinder) with a scraper to remove the resin composition at the portion other than the intaglio, and then transfer coating the coating surface of the waterproof fabric to a predetermined thickness and pattern. .
상기 코팅 방식은 투습방수 코팅면 또는 라미네이팅 필름면에 싱크로 인그레이브드 실린더 상에 업로우딩 방식으로 표면처리제 수지조성물을 공급하여 처리함으로써 고점도(약 2,000∼50,000 cps)의 수지조성물을 균일하게 효과적으로 전사 고착시킬 수 있게 된다.The coating method is uniformly and effectively transfers a high viscosity (about 2,000 to 50,000 cps) resin composition by supplying and treating a surface treating agent resin composition by an up-loading method on a synchronized grooved cylinder on a moisture-permeable waterproof coating surface or a laminating film surface. I can fix it.
표면처리제의 전사 고착 원리는 싱크로 인그레이브드 실린더와 쿳션롤 사이에 피착체를 통과시키면서 압착을 해줌으로써, 싱크로 인그레이브드 실린더에 묻어있던 표면처리제 수지조성물을 피착체 쪽으로 전사시키는 원리인데, 통상 쿳션롤을 하단부에 위치시키는 경우와 상단부에 위치시키는 경우 모두 가능한 방법이지만 전사의 안정성 측면에서 쿳션롤을 하단부에 위치시키는 것이 더욱 바람직하다.The transfer fixation principle of the surface treatment agent is a principle of transferring the surface treatment agent resin composition, which is buried in the synchro-engraved cylinder, to the adherend by compressing the adherend between the synchro-engaged cylinder and the cushion roll. Although both the case where the roll is located at the lower end and the upper part is possible, it is more preferable to position the cushion roll at the lower end in view of the stability of the transfer.
이러한 전사코팅 방법으로 해야 하는 이유는 방수 원단의 코팅 표면에 요철감을 부여키 위한 것이며, 이를 위해 표면 처리제 수지조성물의 고형분을 최대한 높이는 것이 요구되고, 수지특성상 고형분의 증가에 따라 자연스럽게 표면처리제 수지조성물의 점도도 높아지게 됨은 당업자에게 있어서 용이하게 이해되어질 수 있을 것이다.The reason for the transfer coating method is to impart the unevenness to the coating surface of the waterproof fabric. For this purpose, the solid content of the surface treatment agent resin composition is required to be as high as possible. The increase in viscosity will be readily understood by those skilled in the art.
이와 같이 고점도로 하는 경우에 건조 열처리 과정에서 증발되는 양을 최소화할 수 있게 되고, 나아가 싱크로 인그레이브드 실린더에서 전사되는 수지조성물을 일정 두께로 전사 고착시킬 수 있게 되는 것이다.As such, when the high viscosity is achieved, the amount of evaporation during the dry heat treatment process can be minimized, and the resin composition transferred from the synchro-engraved cylinder can be transferred and fixed to a predetermined thickness.
본 발명에 있어서, 싱크로 인그레이브드 실린더의 무늬심도는 40 내지 300㎛인 것이 바람직하다. 상기 싱크로 인그레이브드 실린더의 심도가 40㎛보다 얕으면, 요철감 발현이 미흡하게 되고, 300㎛을 초과하여 깊게 제판할 경우는 수지조성물의 균일한 전사가 어렵게 되거나 전사무늬형태가 일그러지는 문제가 발생할 수 있다. 즉, 무늬 크기에 비해 지나치게 심도가 깊을 경우 전이율이 불량해질 우려가 있다.In the present invention, the pattern depth of the synchro-engraved cylinder is preferably 40 to 300 µm. If the depth of the synchro-engraved cylinder is shallower than 40 μm, the unevenness is insufficient, and when deeply engraved over 300 μm, uniform transfer of the resin composition becomes difficult or the transfer pattern is distorted. May occur. That is, when the depth is too deep compared to the size of the pattern, there is a fear that the transfer rate is poor.
본 발명의 전사 코팅단계에서 사용되는 표면처리제 수지조성물은 약 200℃ 온도에서 물성 변화가 없어야 하고, 톨루엔, 메틸에틸케톤, 디메틸포름아마이드, 이소프로필알콜, 크실렌, 퍼클로로에틸렌, 아세톤, 에틸아세테이트 등의 유기용제에 불용성을 충족하는 내열내용제성의 구상입자를 사용하는 것이 바람직하다. 바람직하게는 그라스 펄(glass bead) 또는 가교 폴리메틸메타크릴레이트 고분자 미립자 또는 가교 폴리우레탄 고분자 미립자에서 선택되는 내열내용제성 고분자 구상입자를 함유하는 것이며, 그 혼합형태 역시 적용될 수 있다.The surface treatment agent resin composition used in the transfer coating step of the present invention should have no physical property change at a temperature of about 200 ° C., toluene, methyl ethyl ketone, dimethylformamide, isopropyl alcohol, xylene, perchloroethylene, acetone, ethyl acetate, and the like. It is preferable to use spherical particles of heat-resistant solvent that satisfy insolubility in the organic solvent of. Preferably it contains a heat-resistant solvent-resistant polymeric spherical particles selected from glass bead or crosslinked polymethyl methacrylate polymer microparticles or crosslinked polyurethane polymer microparticles, and a mixed form thereof may also be applied.
이에, 바람직한 표면처리제 수지조성물의 실시형태로는 폴리우레탄수지(고형분 기준) 100 중량부에 대하여, 혼합유기용제 30 내지 300 중량부, 그라스 펄 30 내지 300 중량부, 안료피그먼트 3 내지 6 중량부, 블록킹 방지제 1.5 내지 15 중량부 및 유ㆍ무기 복합 화합물로 이루어진 커플링제 0.5 내지 2.0 중량부로 이루어진 표면처리제 수지조성물을 사용하는 것이다. Thus, in an embodiment of the preferred surface treatment agent resin composition, 30 to 300 parts by weight of mixed organic solvent, 30 to 300 parts by weight of glass pearl, 3 to 6 parts by weight of pigment pigment, based on 100 parts by weight of polyurethane resin (solid content basis) And a surface treating agent resin composition comprising 1.5 to 15 parts by weight of an antiblocking agent and 0.5 to 2.0 parts by weight of a coupling agent composed of an organic-inorganic composite compound.
상기 조성 중, 그라스 펄(glass pearl)은 건조감, 내마모성, 요철감 및 슬립성 등 복합 기능성을 위한 조제로 사용되며, 상기 그라스 펄의 형상은 구상(bead)인 것이 바람직한데, 표면의 돌출된 부분이 반구 또는 구상으로 되면 마찰에 의한 슬립성이 우수하게 되고, 피부에 접했을 경우 끈적임 촉감을 느낄수 없고 건조하고 쾌적한 느낌을 부여 할 수 있다. 특히, 패커블성이 우수한 방수의류는 봄여름시즌에 많이 착용하므로 쾌적성 측면에서 무기 그라스 펄의 특성상 피부에 접촉했을 경우 냉감 효과도 부여할 수 있다.In the composition, glass pearl is used as a preparation for complex functionalities such as dryness, abrasion resistance, unevenness and slipperiness, and the shape of the glass pearl is preferably a bead, which protrudes from the surface. When the hemisphere or spherical shape is formed, the slipperiness due to friction is excellent, and when the skin is in contact with the skin, it is not possible to feel a sticky touch and can give a dry and comfortable feeling. In particular, waterproof clothing having excellent packability is worn a lot in the spring and summer season, and in terms of comfort, it can also give a cooling effect when it comes in contact with the skin due to the characteristics of the inorganic glass pearl.
이때, 그라스 펄은 직경 5 내지 100㎛의 구상형태가 바람직하며, 더욱 바람직하기로는 8 내지 40㎛으로 되는 것이다. 상기 그라스 펄의 직경이 5㎛ 미만이면, 복합기능성의 효과가 미흡하고, 100㎛을 초과하면, 표면터치가 거칠어 착용감이 불량하다.At this time, the glass pearl is preferably a spherical shape having a diameter of 5 to 100 µm, more preferably 8 to 40 µm. If the diameter of the glass pearl is less than 5 µm, the effect of the compound functionality is insufficient. If the diameter of the glass pearl exceeds 100 µm, the surface touch is rough, resulting in poor fit.
그라스 펄의 조성예로서는 SiO2 70∼73중량%, Al2O3 0.8∼1.0중량%, CaO 7∼12중량%, MgO 1.0∼4.5중량%, Na2O3 및 K2O 13∼15중량%로 이루어진 그라스 펄; 또는 SiO2 52∼56중량%, Al2O3 12∼16중량%, CaO 16∼25중량%, MgO 0∼6중량%, TiO2 0∼0.5중량%, B2O3 5∼13중량%, Na2O3 및 K2O 0∼0.8중량%로 이루어진 그라스 펄; 등 제조공법이나 원료성분의 조성이 다소 다를 수 있으나, 경제성을 고려하여 공지된 그라스 펄에서 선택 사용할 수 있다. Examples The composition of the glass pearl SiO 2 70~73 wt%, Al 2 O 3 0.8~1.0 wt%, CaO 7~12 wt%, MgO 1.0~4.5% by weight, Na 2 O 3 and K 2 O 13~15% by weight Glass pearls; Or 52 to 56 wt% SiO 2 , 12 to 16 wt% Al 2 O 3, 16 to 25 wt% CaO, 0 to 6 wt% MgO, 0 to 0.5 wt% TiO 2 , 5 to 13 wt% B 2 O 3 Glass pearl consisting of 0 to 0.8 wt.%, Na 2 O 3 and K 2 O; The manufacturing method and the composition of the raw material components may be slightly different, but may be selected and used from known glass pearls in consideration of economical efficiency.
또한, 표면처리제 수지조성물에 그라스 펄을 함유할 경우, 아크릴계 일관능성 또는 다관능성 단량체와 인계 화합물로 이루어진 유ㆍ무기 복합 화합물로 이루어진 커플링제를 사용하며, 상기 커플링제는 무기 그라스 펄과 유기물인 폴리우레탄수지와의 결합력과 분산성을 높여주는 효과를 부여할 수 있다. 이때, 커플링제는 폴리우레탄수지(고형분 기준) 100 중량부에 대하여, 0.5 내지 2.0 중량부를 사용한다. In addition, when the surface treatment agent resin composition contains glass pearl, a coupling agent composed of an organic / inorganic complex compound composed of an acryl-based monofunctional or polyfunctional monomer and a phosphorus compound is used, and the coupling agent is an inorganic glass pearl and an organic poly It can give the effect of improving the binding force and dispersibility with the urethane resin. At this time, the coupling agent is 0.5 to 2.0 parts by weight based on 100 parts by weight of the polyurethane resin (solid content basis).
바람직한 표면처리제 수지조성물의 다른 실시형태로서, 폴리우레탄수지(고형분 기준) 100 중량부에 대하여, 혼합유기용제 30 내지 300 중량부, 가교 폴리메틸메타크릴레이트 고분자 미립자 또는 가교 폴리우레탄 고분자 미립자에서 선택되는 어느 하나의 내열내용제성 고분자 구상입자 30 내지 300 중량부, 안료피그먼트 3 내지 6 중량부 및 블록킹 방지제 1.5 내지 15 중량부를 함유하는 것이다.As another embodiment of a preferable surface treating agent resin composition, it is selected from 30-300 weight part of mixed organic solvents, crosslinked polymethyl methacrylate polymer microparticles | fine-particles, or crosslinked polyurethane polymer microparticles with respect to 100 weight part of polyurethane resins (solid content basis). It contains 30 to 300 parts by weight of any one heat-resistant solvent-resistant polymer spherical particles, 3 to 6 parts by weight of pigment pigment and 1.5 to 15 parts by weight of antiblocking agent.
상기 표면처리제 수지조성물의 경우, 가교 폴리메틸메타크릴레이트 고분자 미립자 또는 가교 폴리우레탄 고분자 미립자에서 선택되는 어느 하나의 내열내용제성 고분자 구상입자를 함유함으로써, 가공성 측면에서 유리하다. In the case of the surface treatment agent resin composition, it is advantageous in terms of processability by containing any heat-resistant solvent-resistant polymer spherical particles selected from crosslinked polymethylmethacrylate polymer microparticles or crosslinked polyurethane polymer microparticles.
본 발명의 표면처리제 수지조성물은 주제 수지바인더로서, 1-콤포넌트형 폴리우레탄 수지를 사용하는 것이 싱크로 인그레이브드 실린더에서의 전이성이 양호하며 건조후 표면 끈적임 현상도 없앨 수 있어서 바람직하다.The surface treatment agent resin composition of the present invention is a main resin binder, and it is preferable to use a 1-component polyurethane resin because it has good transferability in a synchro-engraved cylinder and can eliminate surface stickiness after drying.
상기 안료피그먼트는 안감지 사용을 하지 않는 관계로 심미적 관점에서 사용되는 것이다.The pigment pigment is used from the aesthetic point of view because no lining paper is used.
상기 표면처리제 수지조성물 중, 건조감의 상승 효과를 위해서 채용되는 블록킹 방지제로는 시판의 실리카계 미분말이 채용될 수 있다.In the surface treating agent resin composition, a commercially available silica-based fine powder may be employed as the blocking agent used for the synergistic effect of the drying feeling.
상기 표면처리제 조성물에는 무기항균제 또는 바이오세라믹계 소취제가 30 중량부이하로 더 함유되는 것이 바람직하다.It is preferable that the surface treatment agent composition further contain 30 parts by weight or less of an inorganic antibacterial agent or a bioceramic deodorant.
상기 무기항균제로는 무기계 세라믹물질인 제올라이트계로 은(Ag)과 아연(Zn)을 이온 형태로 담지시킨 제올라이트계 무기항균제가 인체에 무해하며 인체에서 발생하는 땀 등의 부패를 방지하는 살균력, 항균력이 뛰어나 바람직하다.The inorganic antimicrobial agent is a zeolite-based inorganic antimicrobial agent, which is an inorganic ceramic material and contains a silver (Ag) and zinc (Zn) in an ionic form. Excellent and desirable.
상기 표면처리제 조성물에는 공지의 음이온 방출을 위한 물질이 부가될 수도 있을 것이다. The surface treatment agent composition may be added with a known material for anion release.
또한, 상기 표면처리제 조성물에 있어서, 상기 표면처리제 수지조성물의 용해 및 점도 조절을 위해 사용하는 혼합유기용제로는 톨루엔, 메틸에틸케톤, 디메틸포름아마이드, 이소프로필알콜, 크실렌, 퍼클로로에틸렌, 아세톤, 에틸아세테이트 등의 단독 또는 2종 이상의 혼합용제로 사용하되, 수지등 부재료의 용해성 등을 감안하여 적의 조정 사용하는 것이 좋다.In addition, in the surface treating agent composition, mixed organic solvents used for dissolution and viscosity control of the surface treating agent resin composition may include toluene, methyl ethyl ketone, dimethylformamide, isopropyl alcohol, xylene, perchloroethylene, acetone, It may be used alone or in combination of two or more kinds of solvents such as ethyl acetate, but may be appropriately adjusted in consideration of the solubility of submaterials such as resin.
본 발명의 표면처리제 수지조성물의 점도는 2000 cps 이상인 것이 바람직하며, 더욱 바람직하게는 2,000∼50,000 cps인 것이다. 이때, 표면처리제 수지조성물의 점도가 2,000 cps 미만이면, 구상 그라스 펄의 자중에 의해 침전하는 문제가 발생하며, 이렇게 되어 구상의 그라스 펄이 침전할 경우 표면처리제 수지조성물의 처리에 의한 복합기능성의 물성이 불균일해질 가능성이 있어서 상기 수지조성물의 점도는 2,000 cps 이상인 것이 바람직하다.It is preferable that the viscosity of the surface treating agent resin composition of this invention is 2000 cps or more, More preferably, it is 2,000-50,000 cps. At this time, if the viscosity of the surface treatment agent resin composition is less than 2,000 cps, there is a problem of precipitation by spherical glass pearl self-weight, thus, when the spherical glass pearl precipitates, the physical properties of the complex functionalities by treatment of the surface treatment agent resin composition Since this may become nonuniform, the viscosity of the resin composition is preferably 2,000 cps or more.
또한, 본 발명의 제조방법에서, 코팅면에 요철감을 줄 수 있는 또 다른 효과적인 방법은 최종 배합된 수지조성물의 고형분을 작업성을 저해하지 않는 범위 내에서 높게 설계하는 것인데, 구체적으로 표면처리제 수지조성물의 전체 고형분이 20% 이상, 더욱 바람직하게는 30∼50%일 경우, 효과 발현에 유용할 것이다. In addition, in the production method of the present invention, another effective method for giving unevenness to the coated surface is to design a solid content of the final blended resin composition within a range that does not impair workability, specifically, the surface treatment agent resin composition If the total solid content of is 20% or more, more preferably 30-50%, it will be useful for expressing the effect.
요철감 부여를 위해 상기 배합약제의 고형분 조정과 더불어 롤제판시 조각의 심도에 의해 그 효과의 상승을 기대할 수 있을 것이다.In addition to adjusting the solid content of the formulation to give a sense of unevenness it may be expected to increase the effect by the depth of the engraving during the roll plate.
통상 롤무늬 제판 방법은 필름부식제판과 조각제판으로 구분될 수 있는데, 필름부식제판은 동을 도금한 실린더에 감광액을 도포한 후, 필름을 현상하는 방식으로 약 5∼20㎛ 심도로 부식이 되어 음각 무늬를 표현하는 방식이고 일반적으로 낮은 심도의 무늬형성이 가능하다. Usually, the rolled plate making method may be classified into a film corrosion plate and a engraving plate, and the film corrosion plate is corroded to a depth of about 5 to 20 μm by applying a photoresist to a copper plated cylinder and then developing the film. It is a way of expressing the intaglio pattern, and generally low depth pattern formation is possible.
한편, 조각제판 방식은 밀을 사용하여 음각 무늬를 롤실린더에 표현하며, 통상 40∼500㎛의 심도 표현이 가능하여, 표면처리제 수지조성물의 도포 전이량을 극대화 하기가 용이할 것이다. 물론 무늬의 크기 즉, 목(目)수에 따른 적도의 심도를 조정해야 함은 당업자에게 용이하게 이해될 것이다.On the other hand, engraving engraving method using the mill to express the intaglio pattern on the roll cylinder, it is possible to express the depth of 40 ~ 500㎛ usually, it will be easy to maximize the amount of coating transfer of the surface treatment agent resin composition. Of course, it will be easily understood by those skilled in the art to adjust the depth of the equator according to the size of the pattern, ie the number of necks.
본 발명에 있어서, 상기 제3단계의 건조 공정은 상기 싱크로 인그레이브드 실린더 업로우딩 방식에 의해 전사 코팅한 후에, 표면처리제 수지조성물의 건조 과정이 포함되는데, 이것은 열풍이 공급되는 챔버안에서 이루어진다. In the present invention, the drying process of the third step includes a drying process of the surface treating agent resin composition after the transfer coating by the synchro-engraved cylinder uploading method, which is performed in a chamber to which hot air is supplied.
상세하게는, 상기 표면처리제 수지조성물을 싱크로 인그레이브드 실린더 업로우딩 방식으로 표면 처리한 후, 반드시 열처리 챔버를 통과시켜 사용한 용제를 증발시키고 수지바인더를 경화시켜 원단에 고착시키는 공정에 있어서, 열처리 챔버는 간접열풍식 또는 직접 복사열 방식으로 해도 무관할 것이다. 그러나 직접 열복사 방식은 화재 등의 관점에서 각별한 주의가 요망되는 바, 바람직하기로는 간접 열풍 방식이 좋다.In detail, the surface treatment agent resin composition is subjected to a surface treatment by a synchro-engraved cylinder uploading method, and then passes through a heat treatment chamber to evaporate the used solvent, hardens the resin binder and adheres to the fabric. The chamber may be indirect hot air or direct radiant heat. However, the direct heat radiation method requires special attention from the viewpoint of fire and the like, and preferably an indirect hot air method.
한편, 표면처리제 수지조성물의 처리시 피처리 원단에는 표면장력을 떨어뜨리는 물질, 예를 들면, 발수제, 유연제, 왁스류 등의 사용은 수지조성물의 전이율을 떨어뜨릴 뿐만 아니라 불균일도를 증가시키는 원인이 되므로 피하는 것이 좋다.On the other hand, when the surface treatment agent resin composition is treated, the use of a material that lowers the surface tension, for example, a water repellent agent, a softening agent, a wax, etc., causes not only the transfer rate of the resin composition but also an increase in unevenness. This is good to avoid.
본 발명은 상기 내마모 투습방수원단의 제조방법에 의해 제조되되, 원단의 투습방수 코팅면에 싱크로 인그레이브드 실린더의 무늬 심도가 40 내지 300㎛로 전사되어 건조감 및 의장성이 부여된 내마모 투습방수원단을 제공한다.The present invention is manufactured by the method of manufacturing the wear-resistant moisture-proof waterproof fabric, the depth of the pattern of the synchro-engraved cylinder is transferred to 40 to 300㎛ on the moisture-proof waterproof coating surface of the fabric wear resistance and moisture resistance to the design endowed Provide waterproof fabric.
특히, 본 발명의 투습방수원단은 100회 내마모성 실험 결과, 마모전후의 중량변화 가 거의 없었으며, 마모손상에 따른 외관변화없는 우수한 내마모성을 확인할 수 있다[도 2a 내지 도 2c].In particular, the moisture-permeable waterproof fabric of the present invention has a result of 100 times the wear resistance test, there was almost no weight change before and after wear, it can be confirmed excellent wear resistance without a change in appearance due to wear damage [ Fig. 2a to 2c ].
또한, 상기 내마모 투습방수원단이 채용되어 봉제된 건조감 및 의장성이 부여된 방수의류를 제공한다.In addition, the wear-resistant breathable waterproof fabric is adopted to provide a waterproof garment with a sense of dryness and design.
본 발명의 방수의류는 투습방수 코팅면 또는 라미네이팅 필름면에 특정 조성의 표면처리제 수지조성물이 싱크로 인그레이브드 실린더 업로우딩 방식(synchro engraved cylinder up-loading coating method)에 의해 코팅함으로써[도 1], 피부에의 직접 접촉시 건조감, 쾌적감 및 냉감을 극대화시킬 수 있다. 또한, 싱크로 인그레이브드 실린더로부터 원단 코팅면에 효과적이고 견고하게 패턴을 전사시킴으로써, 의장성이 부여되어 안감을 생략할 수 있다. 이에, 경량성, 건조감 및 의장성이 부여된 방수의류를 제공할 수 있다.The waterproof garment of the present invention is coated with a surface treatment agent resin composition having a specific composition on a moisture-permeable waterproof coating surface or a laminating film surface by a synchro engraved cylinder up-loading coating method [FIG. 1]. Direct contact with the skin can maximize dryness, comfort and coldness. In addition, by transferring the pattern from the synchro-encoded cylinder to the original coating surface effectively and firmly, design is imparted and the lining can be omitted. Accordingly, it is possible to provide a waterproof garment provided with lightness, dryness and design.
나아가, 본 발명은 안감지 대용의 표면처리된 코팅원단을 봉제할 경우, 특히 방수 또는 투습방수 원단의 경우 심미적 관점에서 심실링 테이프에도 본 원단과 같은 무늬로 표면처리 해주거나 특정 로고 등을 표현해 주어야 함은 당연하다.Furthermore, in the present invention, when sewing the surface-treated coating fabric substitutes for lining paper, in particular, in the case of waterproof or breathable waterproof fabric, in the aesthetic point of view, the surface should be surfaced with the same pattern as the fabric, or a specific logo should be expressed. Of course.
구체적으로, 본 발명은 이형지, 핫멜트 접착제층 및 폴리우레탄 수지로 제조된 내열성수지 필름층이 순차 합지된 심실링테이프 제작용 원단을 제조하고, 상기 원단 중 내열성수지 필름층 상에, 표면처리제 수지조성물을 싱크로 인그레이브드 실린더 업로우딩 방식으로 전사코팅하여 패턴을 인각한 후, 슬리팅 또는 커팅하여 재단하는 의류봉제용 심실링 테이프의 제조방법을 제공한다.Specifically, the present invention manufactures a fabric for fabricating a seam sealing tape in which a heat-resistant resin film layer made of a release paper, a hot melt adhesive layer and a polyurethane resin are sequentially laminated, and on the heat-resistant resin film layer of the fabric, a surface treatment agent resin composition After the transfer coating in a synchro-engraved cylinder uploading method to imprint the pattern, it provides a method for manufacturing a garment sewing seam tape for cutting by cutting or cutting.
이때, 상기 표면처리제 수지조성물 및 인그레이브드 실린더 업로우딩 방식은 상기에서 구체적으로 설명한 바와 동일하며, 본 발명의 표면처리제 조성물에서, 폴리우레탄수지(고형분 기준) 100 중량부에 대하여, 무기항균제 또는 바이오세라믹계 소취제가 30 중량부 이하로 더 함유될 수 있음도 당연히 이해될 것이다.At this time, the surface treatment agent resin composition and the engraved cylinder uploading method is the same as described above in detail, in the surface treatment agent composition of the present invention, based on 100 parts by weight of polyurethane resin (solid content), an inorganic antibacterial agent or It will of course be appreciated that the bioceramic deodorant may further contain up to 30 parts by weight.
본 발명의 심실링 테이프는 방수가공원단의 봉제선 실링에 사용하는 것으로서, 먼저 이형지상에 친환경성 핫멜트 접착층을 압출방식으로 30∼80㎛ 두께로 성형한다. 내열성수지 필름층은 캐스팅방식 또는 압출방식으로 20∼70㎛ 두께로 성형하고, 상기 핫멜트 접착층과 열합지하여 라미네이션시킨 후, 내열성수지 필름층 상에 본 발명에 의한 특정 조성의 표면처리제 조성물을 이용한 인그레이브드 실린더 업로우딩 방식으로 전사코팅한다. 이후, 이형지를 박리하고, 요구되는 폭으로 슬리팅 또는 컷팅하여 신축 회복특성, 요철감, 의장성 및 건조감이 우수한 심실링테이프를 얻을 수 있다[표 7]. 또한, 본 발명의 심실링 테이프는 잔류변형율이 35% 이하를 충족한다.The seam sealing tape of the present invention is used to seal the seam of the waterproof garment end, and first, an eco-friendly hot melt adhesive layer is molded to a thickness of 30 to 80 μm by extrusion on a release paper. The heat-resistant resin film layer is molded to a thickness of 20 to 70 μm by a casting method or an extrusion method, thermally laminated with the hot melt adhesive layer, and then laminated on a heat-resistant resin film layer using a surface treating agent composition having a specific composition according to the present invention. Transfer-coated using a graduated cylinder uploading method. Thereafter, the release paper is peeled off and slitting or cutting to a desired width to obtain a ventilating tape having excellent stretch recovery characteristics, irregularities, design and dryness [ Table 7 ]. In addition, the shim sealing tape of the present invention satisfies a residual strain of 35% or less.
이하, 실시예를 통하여 본 발명을 보다 상세히 설명하고자 한다. Hereinafter, the present invention will be described in more detail with reference to Examples.
본 실시예는 본 발명을 보다 구체적으로 설명하기 위한 것이며, 본 발명의 범위가 이들 실시예에 한정되는 것은 아니다. This embodiment is intended to illustrate the present invention in more detail, and the scope of the present invention is not limited to these examples.
<실시예 1> 투습방수원단 제조 1<Example 1> moisture-proof waterproof fabric 1
1. 표면처리제 수지조성물 제조1. Preparation of surface treatment resin composition
수지 고형분 30% 함유 액상 폴리우레탄수지 100kg, 그라스 펄 40kg, 안료피그먼트 토너(안료고형분 2%) 20kg, 제올라이트계 무기항균제 5kg, 유ㆍ무기 복합화합물 커플링제 0.5kg [(주)마이크로폴사의 MC-502 제품] 및 실리카 분말 2kg을 25kg의 혼합유기용제(디메틸포름아마이드:톨루엔:메틸에틸케톤=1:5:2 중량비로 혼합한 혼합유기용제)에 넣고, 분말이 완전히 혼합될 때까지 교반하고, 100 메쉬의 거름망으로 필터링하여 준비하였다. 이때, 그라스 펄은 구상(球狀)의 입경분포가 8∼30㎛인 것을 사용하였다.Liquid Polyurethane Resin 100kg with 30% Resin Solid Content, Glass Pearl 40kg, Pigment Pigment Toner (2% Pigment Solid Content) 20kg, 5kg Zeolite Inorganic Antimicrobial Agent, 0.5kg Organic / Inorganic Compound Coupling Agent [Micropole Co., Ltd.] -502 products] and 2 kg of silica powder in a mixed organic solvent (dimethylformamide: toluene: methylethylketone = 1: 5: 2 weight ratio mixed organic solvent) of 25 kg, and stirred until the powder is completely mixed. It was prepared by filtering with a strainer of 100 mesh. At this time, the glass pearl used the spherical particle size distribution of 8-30 micrometers.
2. 싱크로 인그레이브드 실린더에 의한 표면처리제 수지조성물의 전사코팅2. Transfer coating of resin composition of surface treatment agent by synchro-engraved cylinder
70 데니어 나이론 원사를 립스탑 조직으로 제직 및 염색후, 투습방수 기능성 폴리우레탄수지로 코팅처리된 방수원단을 원단 페이스면에 편면 발수 가공한 후, 벳칭기 롤에 감긴 상태로 준비하였으며, 이것을 싱크로 인그레이브드 실린더 롤코팅기에 걸고, 전자조각 제판(심도80㎛, 선수30, 격자형 4각 무늬)의 음각롤에 의한 전사코팅 작업을 수행하였다.After weaving and dyeing 70 denier nylon yarns with a lipstop structure, the waterproof fabric coated with a moisture-permeable waterproof polyurethane resin was treated with water repellent on one side of the fabric face, and then wrapped in a betting machine roll, which was then synchro-engraved. The transfer coating operation was carried out by engraving a roll of an electronic engraving plate (depth 80 μm, bow 30, lattice square pattern) on a roll cylinder roll coater.
언와인더롤에서 풀린 방수원단이 싱크로 인그레이브드 실린더의 코팅헤드부를 통과하면서 방수원단의 투습방수 기능성 폴리우레탄수지가 코팅된 필름면에 상기 단계 1에서 제조된 표면처리제 수지조성물이 전사되도록 하였다. As the waterproofing fabric released from the unwinder roll passes through the coating head of the synchro-engraved cylinder, the surface-treatment resin composition prepared in Step 1 is transferred onto the film surface coated with the waterproofing waterproof functional polyurethane resin.
이후, 표면처리된 방수원단을 열풍에 의한 건조챔버를 통과시켜 표면처리제를 건조시켰다. 챔버의 열풍 온도는 120℃로 하였고, 챔버를 통과하는 속도는 10m/min. 이었다.Thereafter, the surface-treated waterproof fabric was passed through a drying chamber by hot air to dry the surface treatment agent. The hot air temperature of the chamber was 120 ° C., and the rate of passage through the chamber was 10 m / min. It was.
<실시예 2> 투습방수원단 제조 2 Example 2 Preparation of moisture-proof waterproof fabric 2
실시예 1에서 전자조각제판 싱크로 인그레이브드 실린더 대신 필름부식제판에 의한 심도 30㎛의 싱크로 인그레이브드 실린더로 전사코팅 작업을 수행하는 것을 제외하 고는, 실시예 1과 동일한 방법으로 방수원단의 표면처리 작업을 하였다.The surface of the waterproof fabric in the same manner as in Example 1, except that the transfer coating operation was performed with a synchronized grooved cylinder having a depth of 30 μm by a film corrosion plate instead of the electronic engraving plated synchronized cylinder in Example 1. Treatment work was done.
<실시예 3> 투습방수원단 제조 3 Example 3 Preparation of moisture-permeable waterproof fabric 3
실시예 1의 표면처리제 수지조성물에, 알루미노실리케이트계 소취제 10kg을 추가하는 것을 제외하고는, 상기 실시예 1과 동일한 방법으로 전사코팅을 수행하였다.Transfer coating was carried out in the same manner as in Example 1, except that 10 kg of the aluminosilicate-based deodorant was added to the surface treatment agent resin composition of Example 1.
<실시예 4> 투습방수원단 제조 4Example 4 Fabrication of Waterproofing Fabric 4
수지 고형분 30% 함유 액상 폴리우레탄수지 100kg, 주성분이 폴리메틸메타크릴레이트로 구성된 내열내용제성 고분자미립자 30kg, 안료피그먼트 토너(안료고형분 2%) 20kg, 제올라이트계 무기항균제 5kg 및 실리카 분말 2kg을 25kg의 혼합유기용제(디메틸포름아마이드:톨루엔:메틸에틸케톤=1:5:2 중량비로 혼합한 혼합유기용제)에 넣고 분말이 완전히 혼합될 때까지 교반하고, 100메쉬의 거름망으로 필터링하여 준비하였다. 이때, 폴리메틸메타크릴레이트를 주성분으로 구성된 내열내용제성 고분자미립자는 구상(球狀)의 입경분포가 8∼30㎛인 것을 사용하였다.100kg of liquid polyurethane resin containing 30% of resin solids, 30kg of heat-resistant solvent-resistant polymer fine particles composed of polymethylmethacrylate, 20kg of pigment pigment toner (2% of pigment solids), 5kg of zeolite inorganic antimicrobial agent and 25kg of 2kg of silica powder Was prepared into a mixed organic solvent (dimethylformamide: toluene: methylethylketone = 1: 5: 2 mixed organic solvent mixed in a weight ratio) and stirred until the powder was completely mixed, followed by filtering with a 100 mesh sieve. At this time, the heat-resistant solvent-resistant polymer fine particles composed of polymethyl methacrylate as the main component was used having a spherical particle size distribution of 8 ~ 30㎛.
<비교예 1>Comparative Example 1
실시예 1의 표면처리제 수지조성물에 함유된 그라스 펄 대신에 탄산칼슘을 넣는 것을 제외하고는, 실시예 1과 동일한 방법으로 방수원단의 전사코팅 작업을 수행하였다. The transfer coating of the waterproof fabric was carried out in the same manner as in Example 1, except that calcium carbonate was added instead of the glass pearl contained in the surface treating agent resin composition of Example 1.
<비교예 2>Comparative Example 2
실시예 1의 표면처리제 수지조성물에 그라스 펄이 함유되지 않은 것을 제외하고는, 상기 실시예1 과 동일한 방법으로 방수원단의 전사코팅 작업을 수행하였다.The transfer coating of the waterproof fabric was carried out in the same manner as in Example 1, except that glass pearl was not contained in the surface treating agent resin composition of Example 1.
<비교예 3>Comparative Example 3
상기 실시예 4의 표면처리제 수지조성물에서, 폴리메틸메타크릴레이트를 주성분으로 구성된 내열내용제성 고분자미립자의 입경분포가 50∼100㎛인 것을 제외하고는, 상기 실시예 4와 동일한 방법으로 방수원단의 전사코팅 작업을 수행하였다.In the surface treatment agent resin composition of Example 4, the particle size distribution of the heat-resistant solvent-resistant polymer fine particles composed of polymethyl methacrylate as a main component is 50-100㎛, Transfer coating work was performed.
<실시예 5> 심실링 테이프 제조 1Example 5 Preparation of Shim Sealing Tape
유동개시점이 95℃인 저융점 폴리우레탄 핫멜트 접착제를 크라프트 이형지에 두께50㎛, 폭 54 인치로 압출 성형시켜 접착제층을 제조하였다. A low melting point polyurethane hot melt adhesive having a flow start point of 95 ° C. was extruded onto a kraft release paper with a thickness of 50 μm and a width of 54 inches to prepare an adhesive layer.
폴리에스터폴리올 및 디이소시아네이트가 주성분인 용액형 폴리우레탄(CYTEC사제UCECOAT-775) 1액형 스킨 수지(고형분 30% 함유) 100 중량부에 대하여, 메틸에틸케톤 20 중량부, 실리카 파우더(DAEGUSA제 OK-412) 5 중량부를 처방하여, 두께 40㎛, 폭 57인치로 RP(Release Paper) 상에 콤마 코팅하여 80℃에서 건조 및 120℃에서 20m/min의 속도로 열처리하는 연속공정으로 두께 40㎛, 폭 57인치로 캐스팅 필름을 제조하고, 박리하여 110℃의 열실린더에서 상기 준비한 핫멜트 접착제층과 열합지하여 심실링테이프 제작용 원단 시트를 제조하였다. 20 parts by weight of methyl ethyl ketone and silica powder (OK- made by DAEGUSA) to 100 parts by weight of a solution-type polyurethane (UCECOAT-775 manufactured by CYTEC) containing 30% solids content of polyester polyol and diisocyanate as main components 412) Prescribe 5 parts by weight, a comma-coated on RP (Release Paper) with a thickness of 40 ㎛, 57 inches in width and drying at 80 ℃ and heat treatment at a speed of 20 m / min at 120 ℃ 40 ㎛ thickness A cast film was prepared at 57 inches, peeled off, and thermally laminated with the prepared hot melt adhesive layer in a thermal cylinder at 110 ° C. to prepare a fabric sheet for fabricating a seam sealing tape.
상기 제작된 이형지가 합지된 원단 시트를 실시예 1의 단계 2의 싱크로 인그레이브드 실린더에 의한 표면처리제 수지조성물의 전사코팅 공정을 수행하여 사각도트로 연결된 사각격자 패턴 무늬를 인각시킨 후, 크라프트 이형지를 제거하고 롤 상으로 권취한 후, 롤 컷팅기에서 20mm 폭으로 재단하여 심실링테이프를 제조하였다.After the fabric sheet on which the release paper is laminated is subjected to the transfer coating process of the surface treatment agent resin composition by the synchro-engraved cylinder of Step 2 of Example 1, the square grid pattern is connected to the square dots, and then the kraft release paper After removing and winding up on a roll, cut to 20mm width in a roll cutting machine to prepare a seam sealing tape.
<실시예 6><Example 6>
상기 실시예 5에서 내열층용 1액형 스킨수지를 R/P 캐스팅 공법이 아닌 무용제형 압출 열가소성 폴리우레탄 필름을 사용하는 것을 제외하고는, 상기 실시예 5와 동 일하게 수행하여, 심실링 테이프를 제조하였다.In Example 5, except that the one-component skin resin for the heat-resistant layer using a solvent-free extruded thermoplastic polyurethane film other than the R / P casting method, the same as in Example 5, to produce a seam sealing tape It was.
<비교예 4><Comparative Example 4>
내열 R/P상에 콤마 코팅으로 용액형 핫멜트형 폴리우레탄 접착제(SAMHO CHEMICAL CO., LTD 제 SPU-10710,고형분30%) 100 중량부에 대하여, 메틸에틸케톤 25 중량부의 처방으로 5M/MIN.의 속도로 코팅하고, 연속하여 폴리에스터폴리올 및 디이소시아네이트가 주성분인 용액형 폴리우레탄(CYTEC사제 UCECOAT-775) 1액형 스킨 수지(고형분 30% 함유) 100 중량부에 대하여, 메틸에틸케톤 20 중량부, 실리카 파우더(DAEGUSA제 OK-412) 5 중량부로 내열 스킨층을 코팅하여 80℃ 건조 및 120℃ 열처리를 수행하여 심실링테이프용 시트원단을 제조하는 것을 제외하고는, 상기 실시예5와 동일한 방법으로 수행하여 심실링 테이프를 제조하였다.5M / MIN by prescription of 25 parts by weight of methyl ethyl ketone based on 100 parts by weight of a solution-type hot melt type polyurethane adhesive (SPU-10710 manufactured by SAMHO CHEMICAL CO., LTD., 30% solids) by a comma coating on a heat-resistant R / P. 20 parts by weight of methyl ethyl ketone based on 100 parts by weight of a solution-type polyurethane (UCECOAT-775 manufactured by CYTEC) containing 30% solids of a solution type polyurethane (CYTEC Co.) In the same manner as in Example 5, except that the heat-resistant skin layer was coated with 5 parts by weight of silica powder (OK-412 made by DAEGUSA) to perform 80 ° C. drying and 120 ° C. heat treatment to prepare a sheet fabric for a ventilating tape. Was performed to prepare a ventilating tape.
<실험예 1>Experimental Example 1
상기 실시예 1∼4 및 비교예 1∼3에서 제조된 투습방수원단에 대하여, 촉감, 내마모성, 착용감, 항균방취 성능 및 소취성능의 물성을 시험하여 하기 표 1 내지 표 5에 나타내었다.About the moisture-permeable waterproof fabrics prepared in Examples 1 to 4 and Comparative Examples 1 to 3, the physical properties of touch, abrasion resistance, wearing comfort, antibacterial deodorization performance, and deodorizing performance are shown in Tables 1 to 5 below.
1. 촉감 : 손에 의한 촉감 테스트(hand feel test)1. Tactile: Hand feel test
상기 실시예 1∼4 및 비교예 1∼2에서 제조된 투습방수원단에 대하여, 30명의 섬유 기술분야 당업자 및 30명의 일반 소비자가 참여하여, 손에 의한 촉감 중, 원단의 요철감, 슬립성, 건조감 및 냉감에 대한 관능검사를 수행하고, 그 결과를 하기 표 1에 기재하였다.For the moisture-permeable waterproof fabrics prepared in Examples 1 to 4 and Comparative Examples 1 to 2, 30 persons skilled in the textile art field and 30 general consumers participated, and the unevenness of the fabric, slip properties, Sensory tests were carried out for dry and cold feelings, and the results are shown in Table 1 below.
이때, 상기 촉감이 요철감이 매우 두드러지고, 표면처리된 원단면끼리 마주보고 비 빌 경우 슬립이 매우 잘 이루어지고, 손등으로 문질렀을 경우 건조감이 매우 우수하고, 손등으로 만졌을 경우, 차가운 감이 매우 느껴질 경우를 매우 우수(◎),At this time, the touch is very noticeable, unevenness, the surface treated fabric faces face each other, the slip is very good, when rubbed with the back of the hand is very good dry feeling, if touched with the back of the hand, very cold feeling If you feel very good (◎),
상기 촉감이 요철감이 두드러지고, 표면처리된 원단면끼리 마주보고 비빌 경우 슬립이 잘 이루어지고, 손등으로 문질렀을 경우 건조감이 우수하고, 손등으로 만졌을경우 차가운 감이 우수한 경우, 우수(○), The feel is concave and convex, the surface treated fabric faces face each other, the slip is well done, when rubbed with the back of the hand is excellent dry feeling, when touched with the back of the hand, excellent cold feeling, excellent (○),
상기 촉감이 요철감이 다소 있고, 표면처리된 원단면끼리 마주보고 비빌 경우 다소슬립이 이루어지며, 손등으로 문질렀을 경우 건조감이 약하게 느껴지며, 손등으로 만졌을 경우 차가운 감이 약간 느껴지는 경우 보통(△) 및 If the touch is a little uneven, the surface treated fabric faces face each other, if you rub a little slip, if you rub with the back of the hand feels dry, if you touch with the back of the hand feels a little cold usually (△) And
상기 촉감이 요철감이 전혀없고, 표면처리된 원단면끼리 마주보고 비빌 경우 슬립이 잘 이루어지지 않고, 손등으로 문질렀을 경우 건조감이 매우 약하며, 손등으로 만졌을 경우 차가운 감이 느껴지지 않는 경우, 불량(×)으로 판정하였다. If the touch does not have any unevenness, and the surface treated fabric faces face each other, the slip does not work well, when rubbed with the back of the hand is very dry, if touched with the back of the hand does not feel cold, poor ( X).
상기 손에 의한 촉감 테스트 결과, 본 발명의 표면처리제 수지조성물을 이용하여 전사코팅한 경우, 그라스 펄 또는 내열내용제성 고분자 구상입자를 함유하지 않고 제조된 원단보다 우수한 결과를 보였다. 특히, 그라스 펄을 함유한 표면처리제 수 지조성물을 이용하여 전사코팅하여 제조된 원단의 경우, 요철감, 슬립성, 건조감 및 냉감에 대한 물성을 최적화시켰으며, 제판공정 시, 전자조각제판 싱크로 인그레이브드 실린더를 이용한 경우(실시예 1), 필름부식제판 싱크로 인그레이브드 실린더로 전사코팅한 경우(실시예 2)보다 우수한 촉감을 나타내었다.As a result of the tactile test by the hand, when the transfer coating using the surface treatment agent resin composition of the present invention, it was superior to the fabric prepared without containing glass pearl or heat-resistant solvent-resistant polymer spherical particles. In particular, in the case of the fabric prepared by transfer coating using the surface treatment resin resin composition containing glass pearl, the properties of the unevenness, slip, dryness and coldness were optimized. In the case of using a graduated cylinder (Example 1), it showed a better feel than the case of transfer coating in a film corrosion plated synchro-engraved cylinder (Example 2).
2. 내마모성 시험2. Wear resistance test
상기 실시예 1, 4 및 비교예 1에서 제조된 투습방수원단에 대하여, 마모측정기(TABER Abrasion Tester)를 이용하여, 마모정도를 비교 평가하였다.Prepared in Examples 1, 4 and Comparative Example 1 For the moisture-permeable waterproof fabric, the degree of wear was compared and evaluated using a TABER Abrasion Tester.
직경 10cm 원판에 상기 투습방수원단을 장착하고, 미국(TABER Industries)의 표준마모시험법 NO. CS-10으로 100 회 실시하여, 시험 전후의 중량감소 및 마모외관 상태를 육안 관찰하였다.Mounting the moisture-proof waterproof fabric on a 10cm diameter disc, standard wear test method NO. The test was carried out 100 times with CS-10 to visually observe the weight loss and abrasion appearance before and after the test.
이때, 시험편이 마모손상이 육안으로 거의 없을 경우 ◎, 시험편 마모손상이 약간 보일 경우 ○ 및 시험편 마모손상이 현저할 경우를 ×로 판정하였다.At this time, when the test piece had almost no abrasion damage visually, (circle), when the test piece abrasion damage was seen a little, (circle), and when the test piece abrasion damage was remarkable, it determined with x.
또한, 도 2a 내지 도 2c는 상기 실시예 1, 4 및 비교예 1에서 제조된 투습방수원단을 이용한 시험편을 100회 마모시험 후 사진결과를 나타낸다.2A to 2C show photographic results after 100 times of abrasion tests on test pieces using the moisture-permeable waterproof fabrics prepared in Examples 1 and 4 and Comparative Example 1. FIG.
상기 내마모성 실험 결과, 그라스 펄 또는 내열내용제성 고분자 구상입자를 함유한 표면처리제 수지조성물을 이용하여 전사코팅한 경우(실시예 1 및 4), 100회 마모조건 하에서도 마모전후의 중량감소가 현저히 감소하였으며, 특히, 그라스 펄을 함유한 경우, 마모손상 정도의 외관변화가 거의 없을 정도로 우수한 내마모성을 보였다. As a result of the above abrasion resistance test, when the transfer coating was performed using a surface treatment resin resin composition containing glass pearl or heat resistant polymer spherical particles (Examples 1 and 4), the weight loss before and after abrasion was significantly reduced even under 100 abrasion conditions. Particularly, when glass pearl was contained, the wear resistance was excellent enough that there was almost no change in the appearance of wear damage.
3. 착용감3. fit
상기 실시예 1∼4 및 비교예 1∼2에서 제조된 투습방수원단으로 의류를 제작한 후, 착용감을 비교 시험하였다. 이때, 상기 투습방수원단에 별도의 안감지를 대지 않고 제작하였다. After the garments were manufactured from the moisture-permeable waterproof fabrics prepared in Examples 1 to 4 and Comparative Examples 1 and 2, the fit was tested. At this time, it was produced without attaching a separate lining paper to the waterproof breathable fabric.
착용감은 착용자가 피부에 닿는 면을 중심으로 관능검사를 실시하였으며, 쾌적(○), 보통(△) 및 불쾌감(×)으로 분류하였다.The fit was performed by sensory test centered on the surface where the wearer touches the skin, and classified into comfort (○), normal (△), and discomfort (×).
4. 항균 방취 성능4. Antibacterial deodorization performance
상기 실시예 1∼4 및 비교예 1∼2에서 제조된 투습방수원단에 대한 항균 방취시험을 하기 조건 하에서 수행하였다. The antimicrobial deodorization test for the moisture-permeable waterproof fabrics prepared in Examples 1 to 4 and Comparative Examples 1 to 2 was performed under the following conditions.
사용한 균주로는 식중독의 주원인균인 황색포도상 구균(Staphylcoccus aureus ATCC 6538) 및 폐렴균인 폐렴막대균(Klebsiella pneumoniae ATCC 4352)을 0.05% 비이온 계 계면활성제(Snogen) 상에 접종하여 37℃에서 24시간 배양한 균을 접종원으로 사용하였다. 표준포는 KS K 0905 염색견뢰도용 면소재 백포를 사용하였으며, 상기 항균성 실험 결과를 하기 표 4에 기재하였다. The strains used were inoculated on Staphylcoccus aureus ATCC 6538, the main cause of food poisoning, and Klebsiella pneumoniae ATCC 4352, a pneumococcal strain, on 0.05% nonionic surfactant (Snogen) for 24 hours at 37 ° C. The cultured bacteria were used as inoculum. KS K 0905 dyed color fastness cotton fabric was used as the standard cloth, the antimicrobial test results are described in Table 4 below.
5. 탈취 성능5. Deodorization performance
상기 실시예 1∼4 및 비교예 1∼2에서 제조된 투습방수원단을 암모니아가스가 들어있는 용기 내에 노출시켜 흡수되고 남은 양을 시간의 경과에 따라 측정하였으며, 하기 조건 하에서 수행하였다. The moisture-permeable waterproof fabrics prepared in Examples 1 to 4 and Comparative Examples 1 to 2 were exposed to a container containing ammonia gas, and the amount of water remaining after absorption was measured over time.
시험편 : 10 × 10 ㎠Test piece: 10 × 10 ㎠
가스백 : 5LGas Bag: 5L
가스백 내 가스량 : 3LGas volume in gas bag: 3L
측정시간 : 2시간 경과 후Measurement time: After 2 hours
초기농도 :암모니아(100 ppm)Initial concentration: Ammonia (100 ppm)
탈취율 % = (Cb - Cs)/ Cb)×100Deodorization% = (C b -C s ) / C b ) × 100
(상기에서, Cb; blank, 2시간 경과 후 시험용기 안에 남아있는 시험가스의 농도이고, Cs; sample, 2시간 경과 후 시험용기 안에 남아있는 시험가스의 농도이다.)(Cb; blank, the concentration of the test gas remaining in the test container after 2 hours, Cs; sample, the concentration of the test gas remaining in the test container after 2 hours.)
6. 내세탁성6. Laundry resistance
상기 실시예 1, 4 및 비교예 1에서 제조된 투습방수원단을 10회 세탁시험한 후, 그라스 펄 또는 내열내용제성 고분자 구상입자의 탈락에 의한 표면촉감 변화를 분석 평가하였다.Prepared in Examples 1, 4 and Comparative Example 1 Breathable waterproof fabric After 10 wash tests, the surface touch change due to the dropping of glass pearl or heat-resistant solvent-resistant polymer spherical particles was analyzed.
◎; 요철감, 건조감, 냉감, 슬립감 등 감성 지수가 매우 훌륭함.◎; Excellent sensitivity index such as unevenness, dryness, coldness and slippery feeling.
○; 요철감, 건조감, 냉감, 슬립감 등 감성 지수가 다소 좋은 편임.○; The sensitivity index, such as unevenness, dryness, coldness and slipperiness, is rather good.
△; 요철감, 건조감, 냉감, 슬립감 등 감성 지수가 그다지 좋지 못함.△; The sensitivity index, such as unevenness, dryness, coldness, and slippage, is not very good.
상기 결과로부터, 실시예 1 및 4에서 제조된 투습방수원단의 경우, 10회 세탁이후에도 그라스 펄 또는 내열내용제성 고분자 구상입자의 탈락없이 우수한 촉감을 유지하였다. From the above results, in the case of the moisture-permeable waterproof fabrics prepared in Examples 1 and 4, even after 10 washes, excellent touch was maintained without dropping of glass pearl or heat-resistant solvent-resistant polymer spherical particles.
<실험예 2> 심실링 테이프의 물성측정<Experimental Example 2> Measurement of the physical properties of the ventilating tape
실시예 5∼6 및 비교예 4에서 제조된 심실링 테이프에 대하여, 인장실험 이후, 인장이전의 상태로 회복되기까지의 변형정도를 나타내는 잔류변형율, 인장강도 및 신도에 관한 물성을 측정하여 하기 표 7에 나타내었다. For the shimling tapes prepared in Examples 5 to 6 and Comparative Example 4, the physical properties of the residual strain, tensile strength and elongation indicating the degree of deformation from the tensile test to the state before the tension was restored to the following table were measured. 7 is shown.
그 결과, 본 발명의 심실링 테이프는 본 발명의 제조방법인 싱크로 인그레이브드 실린더 업로우딩 방식으로 투습방수원단 코팅면에 직접 전사코팅함으로써, 원단과 같은 패턴 무늬로 표면처리할 수 있다. As a result, the shim sealing tape of the present invention can be surface-treated in a pattern pattern such as fabric by directly transferring a coating on the moisture-permeable waterproof fabric coating surface by a synchro-enclosed cylinder uploading method, which is the manufacturing method of the present invention.
또한, 본 발명의 심실링 테이프는 우수한 잔류변형율, 인장강도 및 신도에 관한 물성전반을 보임으로써, 안감지 대용의 투습방수원단의 봉제용도에 적합하다.In addition, the seam sealing tape of the present invention exhibits excellent properties of properties related to residual strain, tensile strength, and elongation, and is suitable for sewing of the moisture-permeable waterproof fabric instead of lining paper.
본 발명의 내마모 투습방수원단의 제조방법에 따라, 특정 성분의 표면처리제 수지조성물을 싱크로 인그레이브드 실린더 업로우딩 방식에 의해 투습방수원단 코팅면에 효과적으로 견고하게 전사시킴으로써 요철감, 건조감, 의장성 및 내마모성을 극대화시키는 효과가 있다.According to the manufacturing method of the wear-resistant moisture-proof waterproof fabric of the present invention, the surface treatment agent resin composition of the specific component is effectively and firmly transferred to the surface of the moisture-proof waterproof fabric by the synchro-engraved cylinder uploading method, thereby feeling the unevenness, dryness, and design. It has the effect of maximizing the wear resistance and wear resistance.
또한, 본 발명의 제조방법에 의해 제조된 투습방수원단은 가볍고, 부피가 작아 일 반 캐주얼, 스포츠용, 방수 방풍용의 방수의류에 매우 유용하게 채용될 수 있다.In addition, the moisture-permeable waterproof fabric produced by the manufacturing method of the present invention is light and small in volume can be very usefully employed in waterproof clothing for general casual, sports, waterproof windproof.
또한, 본 발명의 투습방수원단을 채용하여 봉제된 의류제품은 별도의 안감지가 필요하지 않게 되어 의류제품이 경량화되고 부피감이 작아지며, 잘 접어지므로 패커블(Packable)하게 되는 효과가 있다. 또한, 본 발명의 패커블성이 우수한 방수의류는 코팅면의 내구성이 강하여 의복의 착의 탈의시 또는 피부와 접촉시 내스크래치성이 좋고, 건조감, 냉감이 우수하여 쾌적한 착용감을 부여하는 효과가 있어서 더운 날씨에도 시원한 감이 부여되는 효과가 있다.In addition, the garment product sewn by employing the moisture-permeable waterproof fabric of the present invention does not need a separate lining paper, the clothing product is lighter and less bulky, and because it is folded well, there is an effect that can be packable (Packable). In addition, the waterproof clothing having excellent packability of the present invention has a strong durability of the coated surface, has good scratch resistance when detaching clothes or comes into contact with the skin, and has a good feeling of dryness and coldness, providing a comfortable fit and hot weather. Edo cool effect is given.
본 발명의 내마모 투습방수원단의 제조방법을 심실링 테이프에 적용하여, 안감지 대용의 표면처리된 코팅원단을 봉제할 경우, 특히 방수 또는 투습방수원단의 심미적 관점에서 심실링 테이프에도 본 원단과 같은 무늬로 표면처리할 수 있다.When the method of manufacturing the wear-resistant moisture-proof waterproof fabric of the present invention is applied to a seam sealing tape to sew a surface-treated coating fabric instead of a lining paper, the fabric and the fabric may also be used in a ventilating tape, especially from the aesthetic point of view of the waterproof or waterproof waterproof fabric. The surface can be treated with the same pattern.
이상에서 본 발명은 기재된 구체예에 대해서만 상세히 설명되었지만 본 발명의 기술사상 범위 내에서 다양한 변형 및 수정이 가능함은 당업자에게 있어서 명백한 것이며, 이러한 변형 및 수정이 첨부된 특허청구범위에 속함은 당연한 것이다. Although the present invention has been described in detail only with respect to the described embodiments, it will be apparent to those skilled in the art that various modifications and variations are possible within the technical scope of the present invention, and such modifications and modifications are within the scope of the appended claims.
도 1은 본 발명의 제조방법 중, 전사코팅 공정에 사용되는 싱크로 인그레이브드 실린더 업로우딩 방식의 모식도이고, 1 In the manufacturing method of the present invention, it is a schematic diagram of a synchro-engraved cylinder uploading method used in the transfer coating process,
도 2a는 본 발명의 실시예 1에서 제조된 투습방수원단의 100회 마모시험 후 결과이고, Figure 2a is a result after 100 times the wear test of the moisture-permeable waterproof fabric prepared in Example 1 of the present invention,
도 2b는 본 발명의 실시예 4에서 제조된 투습방수원단의 100회 마모시험 후 결과이고, Figure 2b is the result after 100 times the wear test of the moisture-permeable waterproof fabric prepared in Example 4 of the present invention,
도 2c는 본 발명의 비교예 1에서 제조된 투습방수원단의 100회 마모시험 후 결과이다. Figure 2c is the result after 100 times the wear test of the moisture-permeable waterproof fabric prepared in Comparative Example 1 of the present invention.
Claims (12)