KR100944680B1 - Pen-input device surface member, and pen-input device - Google Patents
Pen-input device surface member, and pen-input device Download PDFInfo
- Publication number
- KR100944680B1 KR100944680B1 KR1020047012050A KR20047012050A KR100944680B1 KR 100944680 B1 KR100944680 B1 KR 100944680B1 KR 1020047012050 A KR1020047012050 A KR 1020047012050A KR 20047012050 A KR20047012050 A KR 20047012050A KR 100944680 B1 KR100944680 B1 KR 100944680B1
- Authority
- KR
- South Korea
- Prior art keywords
- pen
- input device
- friction coefficient
- surface layer
- surface material
- Prior art date
Abstract
본 발명은 입력 장치의 표시면에 부착되는 표면재를 제공한다. 표면재는 기재와, 기재 상에 설치된 표면층을 포함한다. 표면층은 조정되는 동마찰계수 및 정마찰계수를 갖는다. 조정되는 동마찰계수와 정마찰계수는 20℃, 50% 상대습도의 분위기하에서 입력 펜을 하중 200g으로 표면층의 표면과 접촉시키면서 입력 펜을 10 cm/sec이 속도로 이동시킴으로써 측정하는데, 그 값은 각각 0.02~0.5 및 0.4~1.5 이다.
The present invention provides a surface material attached to the display surface of the input device. The surface material includes a substrate and a surface layer provided on the substrate. The surface layer has a dynamic friction coefficient and a static friction coefficient to be adjusted. The dynamic friction coefficient and the static friction coefficient to be adjusted are measured by moving the input pen at a speed of 10 cm / sec while the input pen is in contact with the surface of the surface layer at a load of 200 g in an atmosphere of 20 ° C. and 50% relative humidity. 0.02-0.5 and 0.4-1.5, respectively.
펜 입력 장치, 표면재, 미끄러운감, 패인감, 까칠까칠감Pen input device, surface material, slippery, hollow, rough
Description
본 발명은 필기감이 우수한 펜 입력 장치용 표면재 및 이를 이용한 펜 입력 장치에 관한 것이다.
The present invention relates to a surface material for a pen input device excellent in writing feeling and a pen input device using the same.
일반적으로, 펜 입력 장치는 액정 디스플레이 등의 각종 디스플레이의 전면에 설치되고, 그 표면을 입력 펜으로 접촉하는 것에 따라 검출되는 접촉위치신호에 의하여 정보의 입력조작을 행한다. 펜 입력 장치에 의하면, 입력 펜으로 곡선이나 직선 등의 연속한 선상 도형 입력과 같은 상세한 조작이 용이하고, 비교적 작은 화면에 있어서도 많은 정보의 입력이 가능하다. 입력 펜으로 디스플레이 상에 문자를 쓰는 입력 조작에 쉽게 친숙해지기 때문에, 펜 입력장치의 이용범위는 전자 수첩과 같은 휴대정보 단말기 및 멀티미디어 기기 등 그 이용 범위가 급속도로 확대되고 있다.
In general, a pen input device is provided in front of various displays such as a liquid crystal display, and performs input operation of information by a contact position signal detected by touching the surface with an input pen. According to the pen input device, a detailed operation such as continuous linear graphic input such as a curve or a straight line is easy with the input pen, and much information can be input even on a relatively small screen. Since the input pen is easily familiar with an input operation for writing characters on a display, the use range of the pen input device is rapidly expanding its use range such as portable information terminals and multimedia devices such as electronic notebooks.
종래, 펜 입력 장치에 사용되고 있는 표면재로는, 유리판이나 그 표면에 하 드 코팅층을 형성한 플라스틱 판이었다. 그러나, 표면재에 대한 필기감이 통상의 종이에 대한 것보다 매우 나빴다.Conventionally, the surface material used for the pen input device was a glass plate or a plastic plate with a hard coating layer formed on the surface thereof. However, the writing feeling on the surface material was much worse than that on ordinary paper.
표면재의 필기감을 개선하기 위하여, 몇몇 제안이 이루어졌다.In order to improve the writing feeling of the surface material, several proposals have been made.
예를 들면, 기재의 표면에 설치된 하드 코팅제와, 기재의 표면에 설치된 탄성 변형성을 갖는 점착층을 갖는 패널(panel) 표면재가 알려져 있다(특허 문헌 1 : 특개평 6-309990호 공보 (제 2 쪽 및 제 3 쪽) 참조). 또한, 아크릴 수지의 미립자를 표면층에 첨가함으로써, 그 표면에 요철을 형성한 전리 방사선 경화성 수지로 만든 표면재가 알려져 있다(특허 문헌 2 : 특개평 7-244552호 공보 (제 2 쪽) 참조). 또한, 자기 수복성 및 내찰상성을 갖는 투명한 연질 합성 수지를 구비한 펜 입력 장치용 보호 필름이 알려져 있다(특허 문헌 3 : 특개평 6-180628호 공보 (제 2 쪽) 참조).For example, a panel surface material having a hard coating agent provided on the surface of a substrate and an adhesive layer having elastic deformation property provided on the surface of the substrate is known (Patent Document 1: Japanese Patent Laid-Open No. 6-309990 (Second Page)). And page 3)). Moreover, the surface material made from the ionizing radiation curable resin which provided the unevenness | corrugation on the surface by adding microparticles | fine-particles of an acrylic resin to the surface layer is known (refer patent document 2: Unexamined-Japanese-Patent No. 7-244552 (the 2nd page)). Moreover, the protective film for pen input devices provided with the transparent soft synthetic resin which has self-recoverability and abrasion resistance is known (refer patent document 3: Unexamined-Japanese-Patent No. 6-180628 (the 2nd page)).
일반적으로, 펜 입력 장치는 입력 펜에 의하여 패널의 표면에 묘화(描畵)하는 동작에 따라 정보를 입력하기 때문에, 입력 펜에 의한 필기감이 특히 중요하다. 그 필기감을 미끄러운감, 패인감(탄력감) 및 까칠까칠감(거친감)의 세 개의 감각으로 나누어 고려할 수 있고, 이러한 세 개의 감각을 균형있게 충족시키는 것이 가장 바람직하다. 이 중에서 미끄러운감이 특히 중요하고, 입력 펜 선단과 패널 등의 펜 입력 장치 표면과의 마찰 저항을 측정하는 것에 의해 미끄러운감을 평가할 수 있다. 이 마찰 저항은 묘화 동작 중의 미끄러운감에 상당하는 동마찰저항과 쓰기 시작할 때의 미끄러운감에 상당하는 정마찰 저항의 2 개로 구분할 수 있다. 그 양쪽의 마찰 저항을 제어하는 것이 중요하다. 또한, 이 미끄러운감과 합쳐서 종이의 부드러운 느낌에 패인감을 갖게 함으로써 필기감을 보다 양호하게 된다. 또한, 연필로 종이에 쓰는 때와 같은 까칠까칠감을 갖게 함으로써 필기감이 더욱더 양호해 진다.
In general, since the pen input device inputs information in accordance with an operation of drawing on the surface of the panel by the input pen, writing feeling by the input pen is particularly important. The writing can be considered divided into three senses of slippery feeling, stiffness (elasticity), and roughness (roughness), and it is most desirable to satisfy these three senses in a balanced manner. Of these, slipperiness is particularly important, and the slipperiness can be evaluated by measuring the frictional resistance between the tip of the input pen and the surface of a pen input device such as a panel. This frictional resistance can be classified into two types: dynamic frictional resistance corresponding to slipperiness during drawing operation and static frictional resistance corresponding to slipperiness at the start of writing. It is important to control the frictional resistance on both sides. Also, in combination with the slippery feeling, the soft feeling of the paper is made to have a dent, thereby making the writing feeling better. In addition, the feeling of writing becomes even better by giving the same rough feeling as when writing on paper with a pencil.
그러나, 종래 기술에서는, 이들 세 개의 감각에 근거하는 평가가 이루어 지지 않아 필기감이 만족스럽지 못하였다. 특허 문헌 1의 표면재에서는, 최표면이 하드 코팅 층으로 형성되어 있기 때문에 미끄러운감이 적절하지 못했다. 또한, 그 표면이 종이와 같은 요철(텍스처; texture)이 없고, 까칠까칠감이 부족하다는 문제점이 있었다. 특허문헌 2의 표면재에서는, 표면의 요철에 의하여 까칠까칠감은 있으나, 미끄러운감이 적절하지 못했고, 패인감이 부족하다는 문제점이 있었다. 특허 문헌 3의 표면재에서는, 연질 합성 수지에 의하여 패인감은 있으나, 미끄러운감은 적절하지 못했다. 또한, 표면 텍스처가 형성되어 있지 않기 때문에 까칠까칠감이 부족하다는 문제점이 있었다.
However, in the prior art, evaluation based on these three sensations was not made and the writing feeling was not satisfactory. In the surface material of patent document 1, since the outermost surface was formed by the hard-coat layer, slipperiness was not appropriate. In addition, there is a problem that the surface does not have a texture (texture), such as paper, the lack of roughness. In the surface material of patent document 2, although there exists a feeling of roughness by the surface unevenness, slipperiness was inadequate and there existed a problem that lack of a feeling of indentation. In the surface material of patent document 3, although there exists a feeling of dent by soft synthetic resin, slipperiness was not appropriate. In addition, there is a problem that the lack of roughness because the surface texture is not formed.
따라서, 미끄러운감, 패인감 및 까칠까칠감의 세 개의 감각을 균형있게 충족시킨 양호한 필기감을 갖는 표면재가 바람직하지만, 특히 미끄러운감을 충분히 만족시킬 수 있는 표면재가 없는 것이 현실이다.
Therefore, a surface material having a good writing feeling that balances three senses of slipperiness, dents, and roughness is desirable, but in reality there is no surface material that can sufficiently satisfy the slipperiness.
본 발명의 목적은 필기감이 우수한 펜 입력 장치용 표면재 및 이를 이용한 펜 입력 장치를 제공하기 위한 것이다.
An object of the present invention is to provide a surface material for a pen input device excellent in writing feeling and a pen input device using the same.
본 발명자들은 상기한 목적을 달성하기 위하여 연구한 결과, 펜 입력 장치용 표면재의 표면층의 동마찰계수 및 정마찰계수의 양쪽이 특정의 범위 내에 있는 경우에 상기 3 개의 감각이 양호하게 되고, 특히 미끄러운감이 양호하게 되고, 필기감이 우수하다는 것을 발견하게 되어 본 발명을 완성하게 되었다.
The present inventors have studied to achieve the above object, and as a result, the three sensations become good when both the dynamic friction coefficient and the static friction coefficient of the surface layer of the surface material for a pen input device are within a specific range, and are particularly slippery. A feeling becomes good, It has been found that the writing feeling is excellent, thus completing the present invention.
본 발명의 일태양은, 기재 및 상기 기재를 지지하는 표면층으로 된 펜 입력 장치용 표면재를 제공한다. 20℃, 50% 상대습도의 분위기하에서 입력 펜을 하중 200g으로 상기 표면층에 접촉시키면서 입력 펜을 10cm/sec의 속도로 이동시킨 때의 동마찰계수가 0.02~0.5이고, 또한 정마찰계수가 0.4~1.5이다.
An aspect of the present invention provides a surface material for a pen input device comprising a substrate and a surface layer supporting the substrate. The coefficient of dynamic friction is 0.02 to 0.5 when the input pen is moved at a speed of 10 cm / sec while the input pen is brought into contact with the surface layer at a load of 200 g under an atmosphere of 20% and 50% relative humidity, and the coefficient of static friction is 0.4 to 1.5.
이하, 본 발명의 일실시태양에 대하여 상세히 설명한다. Hereinafter, one embodiment of the present invention will be described in detail.
일실시태양의 펜 입력 장치는 패널의 표면에 연필이나 볼펜의 형상과 유사한 펜형 기구를 이용하고 묘화하는 동작에 따라 정보의 입력 조작을 행하는 장치이고, 패널 및 펜형 기구의 적어도 한 편에 전기나 전자파 등에 의한 신호 출력 회로 또는 신호 기록 회로를 구비한 장치라면 특별히 한정되지 않는다. 예를 들면, 각종 디스플레이의 전면에 설치되는 펜 입력 터치 패널 장치나, 디스플레이의 전면에 설치되지 않고 컴퓨터에 접속되고 사용되는 펜 입력 장치나, 전자 페이퍼 등을 들 수 있다.
A pen input device according to one embodiment is a device for inputting information according to an operation of drawing and using a pen-type mechanism similar to the shape of a pencil or ballpoint pen on the surface of a panel, and at least one of the panel and the pen-type mechanism for electric or electromagnetic waves. The device is not particularly limited as long as it is a device having a signal output circuit or a signal recording circuit. For example, a pen input touch panel device provided on the front of various displays, a pen input device connected to a computer and used without being provided on the front of the display, electronic paper, and the like can be given.
펜 입력 터치 패널 장치는 액정 디스플레이, 플라즈마 디스플레이(PDP), 전자 형광(EL) 디스플레이, 브라운관(CRT) 디스플레이 등의 표시장치에 터치 패널이 배치되고, 그 표면을 입력 펜으로 접촉하는 것에 따라 검출되는 접촉 위치 신호로 입력 조작을 행하는 장치이다. 터치 패널은 상기와 같은 각종 디스플레이에 조립된 일체형과, 각종 디스플레이 장치 표시 면상에 배치되는 분리형이 있다. 터치 패널 방식으로는 공지의 방식이 모두 사용 가능하고, 특별히 한정되지 않는다. 예를 들면, 초음파 방식, 저항막 방식, 정전 용량 방식, 전기 왜곡 방식, 자기 변형 방식 및 적외선 방식 등의 터치 패널을 들 수 있다.
The pen input touch panel device includes a touch panel disposed on a display device such as a liquid crystal display, a plasma display (PDP), an electroluminescent (EL) display, a CRT display, and the like. It is an apparatus which performs input operation by a contact position signal. The touch panel includes an integrated type assembled on the various displays as described above and a detachable type disposed on various display device display surfaces. As a touch panel system, all well-known methods can be used and it is not specifically limited. For example, touch panels, such as an ultrasonic system, a resistive film system, a capacitive system, an electric distortion system, a magnetostrictive system, and an infrared system, are mentioned.
이와 같은 펜 입력 장치의 입력 펜과 직접 접촉하는 면에 펜 입력 장치용 표면재가 사용된다. 본 발명의 펜 입력 장치용 표면재는 수지로 된 기재와, 입력 펜과 접촉하는 표면층으로 된다. 표면층은 단층이어도 좋고, 복수의 층으로 형성되어 있어도 좋다. 입력 펜은, 펜 입력 장치에서의 입력 조작에 사용될 수 있는 펜이라면 특별히 한정되지 않는다. 공지의 입력펜으로는, 예를 들면, 폴리아세탈 수지를 주성분으로 하는 재질로 형성된, 펜 선단의 직경이 1.6mm 정도의 것이다.
The surface material for pen input devices is used for the surface which directly contacts an input pen of such a pen input device. The surface material for pen input devices of this invention consists of a base material made of resin, and the surface layer which contacts an input pen. The surface layer may be a single layer or may be formed of a plurality of layers. The input pen is not particularly limited as long as it is a pen that can be used for input operation in the pen input device. As a well-known input pen, the diameter of the pen tip formed with the material which has a polyacetal resin as a main component is about 1.6 mm, for example.
일실시태양의 펜 입력 장치용 표면재는, 입력 펜에 대한 마찰 저항을 표면성 시험기(신동 과학(주)제, 상품명: 토라이보기아, 타입: 14DR)에 의해 측정한 값이 특정 범위에 있는 것이다. 즉, 20℃, 50% 상대습도 분위기하에서 입력 펜을 하중 200g로 펜 입력 장치용 표면재에 접촉시켜, 표면재 위를 10cm/sec의 속도로 이동시킨 때, 동마찰계수가 0.02~0.5, 바람직하게는 0.1~0.4이며, 동시에 정마찰계수가 0.4~1.5, 바람직하게는 0.5~1.0이 되는 펜 입력 장치용 표면재이다.
In the surface material for pen input devices of one embodiment, the value which measured the frictional resistance with respect to an input pen by the surface tester (made by Shin-Dong Scientific Co., Ltd., brand name: Toraiboa, type: 14DR) exists in a specific range. . That is, when the input pen is brought into contact with the pen input device surface material under a load of 200 g under 20 ° C. and 50% relative humidity atmosphere, and the surface friction material is moved at a speed of 10 cm / sec, the coefficient of dynamic friction is preferably 0.02 to 0.5, preferably It is 0.1-0.4, and is a surface material for pen input apparatuses whose static friction coefficient is 0.4-1.5, Preferably it is 0.5-1.0.
동마찰계수가 0.02 미만인 경우 또는 정마찰계수가 0.4 미만인 경우, 입력펜이 지나치게 미끄러져서, 필기감이 나쁘다. 한편, 동마찰계수가 0.5를 초과하는 경우 또는 정마찰계수가 1.5를 초과하는 경우, 입력 펜의 미끄러짐이 나쁘고, 입력 펜의 조작시 무겁게 느껴지게 되어 필기감이 나쁘다.
When the dynamic friction coefficient is less than 0.02 or the static friction coefficient is less than 0.4, the input pen slides excessively, resulting in a poor writing feeling. On the other hand, when the dynamic friction coefficient exceeds 0.5 or when the static friction coefficient exceeds 1.5, the slip of the input pen is bad, and the feeling of writing is bad because the input pen feels heavy when the input pen is operated.
표면재의 패인감을 보다 향상시킨다는 관점으로부터, 다음과 같은 펜 입력 장치용 표면재가 보다 바람직하다. 즉, 20℃, 50% 상대습도의 분위기하에서 선단경 0.75mm의 초경 재료제 가상체를 이용하고 펜 입력 장치용 표면재의 표면층을 10cm/sec의 속도로 긁을 때, 가상체로 향하여 복원하는 하중이 바람직하게는 10~1000g이고, 보다 바람직하게는 20~1000g으로 복원하는 펜 입력 장치용 표면재이다. 복원하는 하중이 10g 미만인 경우, 입력 펜에 의한 입력시에 표면재에 패인곳(필적)이 장시간 잔존하게 되고, 그 패인곳이 시인성을 저해하는 것에 더하여 필기감을 나쁘게 하는 경향이 있다. 한편, 복원하는 하중이 1000g을 초과하는 경우, 표면층이 너무 부드럽고 필기감이 저하된다. 여기에서, 복원성은 한번 생긴 패인곳이 경시적으로 소실하는 성질을 의미한다. 일시적으로 생기는 패인곳은 표면재 에 적절한 정도로 패인감을 부여한다. 또한, 패인곳의 생성에 의하여 압축력이 흡수되기 때문에 적절한 정도의 패인감을 갖는 표면재에 상처를 내기가 어렵다.
From the viewpoint of further improving the feeling of dent of the surface material, the following surface material for a pen input device is more preferable. In other words, when using a cemented carbide material having a tip diameter of 0.75 mm at a temperature of 20 ° C. and 50% relative humidity and scraping the surface layer of the surface material for pen input device at a speed of 10 cm / sec, a load for restoring toward the virtual body is preferable. Preferably it is 10-1000g, More preferably, it is the surface material for pen input apparatuses restored to 20-1000g. If the load to be restored is less than 10 g, the indentation (handwriting) remains in the surface material for a long time during input by the input pen, and the indentation tends to worsen the writing feeling in addition to impairing visibility. On the other hand, when the load to restore exceeds 1000 g, the surface layer is too soft and the writing feeling is lowered. Here, the resilience once occurred This means that the cutout is lost over time. Temporarily created indentations give the surface material an adequate degree of indentation. In addition, since the compressive force is absorbed by the creation of the pits, it is difficult to wound the surface material having a proper degree of pitting feeling.
표면재의 내구성을 보다 향상시킨다는 관점으로부터, 다음과 같은 펜 입력 장치용 표면재가 보다 바람직하다. 즉, 20℃, 50% 상대습도의 분위기하에서 직경 20mm의 원형 면포를 이용하여 하중 200g으로 펜 입력 장치용 표면재의 표면층을 10cm/sec의 속도로 1000회 왕복시켜서 닦았을 때의 헤이즈값의 증가가 바람직하게는 10% 이하이고, 보다 바람직하게는 9% 이하인 펜 입력 장치용 표면재이다. 헤이즈값의 증가가 10%를 초과하는 경우, 펜 입력 장치용 표면재는 입력 펜과의 접촉에 대하여 내구성이 낮고, 장시간의 사용에 의하여 시인성과 필기감이 악화하는 경향이 있다.
From the viewpoint of further improving the durability of the surface material, the following surface material for pen input devices is more preferable. That is, the haze value increases when the surface layer of the surface material for pen input device is reciprocated 1000 times at a speed of 10 cm / sec using a circular cotton cloth having a diameter of 20 mm in an atmosphere of 20 ° C. and 50% relative humidity at a rate of 10 cm / sec. Preferably it is 10% or less, More preferably, it is 9% or less, the surface material for pen input devices. When the increase in haze value exceeds 10%, the surface material for pen input device is low in durability against contact with the input pen, and the visibility and writing feeling tend to be deteriorated by long time use.
본 발명의 펜 입력 장치용 표면재는, 기재와 표면층가의 사이에, 또는 표면층이 형성되어 있는 기재의 표면과는 반대측의 표면에 필요에 따라 반사 방지층, 투과광 제어층, 도전성층 및 대전 방지층 등의 기능층을 갖는 단층을 형성해도 좋다. 또한, 복수의 적층을 갖는 기재를 사용해도 좋다.
The surface material for pen input devices of this invention functions as an antireflection layer, a transmission light control layer, an electroconductive layer, and an antistatic layer as needed between the base material and the surface layer value, or on the surface on the opposite side to the surface of the base material in which the surface layer is formed. You may form a single layer which has a layer. Moreover, you may use the base material which has several laminated | multilayer.
표면재의 기재의 재질로는, 예를 들면 폴리에틸렌 테레프탈레이트 등의 폴리에스테르, 폴리카보네이트, 폴리메틸메타크릴레이트, 폴리스티렌, 재생 셀룰로오스, 지아세칠셀룰로오스, 트리아세틸셀룰로오스, 아크릴로니트릴/스티렌/부타디엔 3원 공중합체, 폴리 염화 비닐, 폴리 염화 비닐리덴, 폴리 비닐 알코올, 나일론, 폴리에틸렌, 셀룰로오스 아세테이트, 폴리프로필렌, 폴리아미드, 폴리이미드, 폴리술폰, 폴리 에테르 술폰, 노르보르넨계 수지 등을 들 수 있다. 상기 중에서, 트리아세틸셀룰로오스, 폴리에틸렌 테레프탈레이트, 폴리카보네이트 등의 투명성이 있는 기재가 바람직하다.
As the material of the base material of the surface material, for example, polyester such as polyethylene terephthalate, polycarbonate, polymethyl methacrylate, polystyrene, regenerated cellulose, geoacetic cellulose, triacetyl cellulose, acrylonitrile / styrene / butadiene Copolymers, polyvinyl chloride, polyvinylidene chloride, polyvinyl alcohol, nylon, polyethylene, cellulose acetate, polypropylene, polyamide, polyimide, polysulfone, polyether sulfone, norbornene-based resin, and the like. Among the above, base materials having transparency such as triacetyl cellulose, polyethylene terephthalate, and polycarbonate are preferable.
표면층은, 기재의 표면 또는 기재에 적층된 기능층 위에, 표면층 형성용 조성물을 도포하고 경화시키는 것에 의해 형성된다. 이러한 표면층 형성용 조성물은, 자외선 경화형 또는 열경화형의 불포화 아크릴 수지 조성물, 우레탄 변성 (메타)아크릴레이트 등의 불포화 폴리우레탄 수지 조성물, 불포화 폴리에스테르 수지 조성물, 폴리아미드 수지 조성물, 열 경화형의 실리콘계, 멜라민계 및 에폭시계의 수지 조성물을 포함된다. 예를 들면, 다가 알코올과 (메타)아크릴산과의 에스테르화물 등의 아크릴로일기, 메타아크릴로일기를 2 개 이상 포함한 다관능 중합성 화합물을 포함하는 수지 조성물이나 우레탄 변성 (메타)아크릴레이트를 포함하는 수지 조성물, 그리고 실리콘계, 멜라민계 또는 에폭시계의 다관능 중합성 화합물을 포함하는 수지 조성물을 들 수 있다. 상기 중에서, 내구성이나 취급용이성 면에서, 자외선, 전자선 또는 가열에 의하여 경화할 수 있는 다가 알코올과 (메타)아크릴산과의 에스테르화물이나 우레탄 변성 (메타)아크릴레이트와 같은 (메타)아크릴기 함유 화합물을 주성분으로 포함하는 수지 조성물이 우수하다.
A surface layer is formed by apply | coating and hardening the composition for surface layer formation on the surface of a base material, or the functional layer laminated | stacked on the base material. Such a surface layer-forming composition may be an ultraviolet curable or thermosetting unsaturated acrylic resin composition, an unsaturated polyurethane resin composition such as urethane-modified (meth) acrylate, an unsaturated polyester resin composition, a polyamide resin composition, a thermosetting silicone type, or melamine. And epoxy resin compositions. For example, the resin composition and urethane modified (meth) acrylate containing the polyfunctional polymerizable compound containing two or more acryloyl groups and methacryloyl groups, such as esterified products of a polyhydric alcohol and (meth) acrylic acid, are included. And a resin composition containing a polyfunctional polymerizable compound of a silicone-based, melamine-based or epoxy-based resin composition. Among the above, (meth) acrylic group-containing compounds such as esterified products of polyhydric alcohols and (meth) acrylic acids and urethane-modified (meth) acrylates that can be cured by ultraviolet rays, electron beams, or heating in view of durability and ease of handling. The resin composition contained as a main component is excellent.
상기 다가 알코올로는, 예를 들면, 에틸렌 글리콜, 폴리에틸렌 글리콜, 프로필렌 글리콜, 폴리프로필렌 글리콜, 프로판디올, 부탄디올, 펜탄디올, 헥산디올, 네오펜틸 글리콜, 2-에틸-1,3-헥산디올, 2,2'-티오디에탄올, 1,4-시클로헥산 디메탄올 등의 2가 알코올; 트리메티롤프로판, 펜타글리세롤, 글리세롤, 펜타에리스리톨, 지글리세롤, 제펜타글리세롤 등의 3가 이상의 알코올을 들 수 있다.
Examples of the polyhydric alcohols include ethylene glycol, polyethylene glycol, propylene glycol, polypropylene glycol, propanediol, butanediol, pentanediol, hexanediol, neopentyl glycol, 2-ethyl-1,3-hexanediol, 2 Dihydric alcohols such as 2'-thiodiethanol and 1,4-cyclohexane dimethanol; Trihydric alcohol, such as a trimetholol propane, pentaglycerol, glycerol, pentaerythritol, giglycerol, zepentaglycerol, is mentioned.
상기 우레탄 변성 (메타)아크릴레이트는, 말단 이소시아네이트 폴리우레탄과 수산기를 갖는 (메타)아크릴산 유도체와의 우레탄화 반응에 따라 얻을 수 있다. 말단 이소시아네이트 폴리우레탄은, 헥사메틸렌 디이소시아네이트나 이소홀론디이소시아네이트 등의 폴리이소시아네이트와 폴리카프로락톤디올이나 폴리테트라메틸렌디올 등의 복수의 수산기를 갖는 올리고머와의 반응에 따라 제조된다. 수산기를 갖는 (메타)아크릴산 유도체로는, 예를 들면, (메타)아크릴산2-히드록시에틸, (메타)아크릴산2-히드록시프로필 등을 들 수 있다. 이러한 성분은 단독으로 이용해도 좋고, 2 종류 이상 병용해도 좋다. 표면재의 패인감과 내구성을 향상시키기 위해 상기 각종 수지 중의 장쇄 성분을 많이 포함하는 수지가 바람직하다.
The urethane-modified (meth) acrylate can be obtained by a urethanization reaction of a terminal isocyanate polyurethane with a (meth) acrylic acid derivative having a hydroxyl group. Terminal isocyanate polyurethane is manufactured by reaction with polyisocyanate, such as hexamethylene diisocyanate and isoholone diisocyanate, and the oligomer which has several hydroxyl groups, such as polycaprolactone diol and polytetramethylene diol. As a (meth) acrylic-acid derivative which has a hydroxyl group, (meth) acrylic acid 2-hydroxyethyl, (meth) acrylic acid 2-hydroxypropyl, etc. are mentioned, for example. These components may be used independently and may be used together 2 or more types. In order to improve the dent feeling and durability of a surface material, resin containing many long-chain components in the said various resin is preferable.
반응성 희석재로서 단관능 성분을 병용해도 좋다. 이들은 주성분으로 사용하는 수지와의 상용성이 좋은 단량체라면 특별히 한정되지 않는다. 예를 들면, 에틸 (메타)아크릴레이트, 2-에틸헥실 (메타)아크릴레이트, 라우릴아크릴레이트, 스티렌, 메틸스티렌, N-비닐피롤리돈, 디메틸아크릴아미드를 들 수 있다. 이것들은 단독으로 사용해도 좋고, 2 종류 이상 병용해도 좋다.
You may use together a monofunctional component as a reactive diluent. These will not be specifically limited if it is a monomer with good compatibility with resin used as a main component. For example, ethyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, lauryl acrylate, styrene, methyl styrene, N-vinylpyrrolidone, and dimethyl acrylamide are mentioned. These may be used independently and may use two or more types together.
표면층 형성용 조성물의 점도를 조정하기 위해, 희석용매를 이용해도 좋다. 상기 희석용매는 비중합성의 것이라면 특별히 한정되지 않고, 예를 들면, 톨루엔, 크실렌, 초산에틸, 초산부틸, 메틸셀솔부(에틸렌 글리콜 모노메틸 에테르), 에틸셀솔부(에틸렌 글리콜 모노에틸 에테르), 에틸셀솔부아세테이트(에틸렌 글리콜 모노에틸 에테르 아세테이트 ), 이소프로필 알코올, 메틸에틸케톤 등을 들 수 있다. 희석 용매는 단독으로 사용해도 좋고, 2 종류 이상 병용해도 좋다.
In order to adjust the viscosity of the composition for surface layer formation, you may use a dilution solvent. The diluent solvent is not particularly limited as long as it is non-polymerizable. For example, toluene, xylene, ethyl acetate, butyl acetate, methyl celsol portion (ethylene glycol monomethyl ether), ethyl celsol portion (ethylene glycol monoethyl ether), ethyl Celsol butylacetate (ethylene glycol monoethyl ether acetate), isopropyl alcohol, methyl ethyl ketone, etc. are mentioned. A dilution solvent may be used independently and may be used together two or more types.
까칠까칠감을 보다 향상시키기 위해, 표면층에 중심선 평균 거칠기(Ra)는 0.1~5.0 ㎛이 바람직하고, 보다 바람직하게는 1.0~4.0 ㎛인 미세한 텍스처를 형성시키는 것이 보다 바람직하다. 중심선 평균 거칠기(Ra)가 0.1 ㎛ 미만이라면 표면재의 까칠까칠감이 부족하며, 5.0 ㎛를 초과하는 경우에는 표면재의 광학 특성이 나빠진다. 표면층에 텍스처를 형성시키는 방법으로서는, 엠보싱 가공, 샌드블라스트 가공, 에칭 가공 등의 조면화 처리가 적절히 채용된다.
In order to further improve the roughness, the centerline average roughness Ra is preferably 0.1 to 5.0 µm, more preferably 1.0 to 4.0 µm, on the surface layer. If the centerline average roughness Ra is less than 0.1 µm, the roughness of the surface material is insufficient, and if it exceeds 5.0 µm, the optical properties of the surface material become worse. As a method of forming a texture in a surface layer, roughening processes, such as embossing, sandblasting, and etching, are employ | adopted suitably.
또한, 표면층에 미세한 텍스처를 형성시키기 위해 미립자 물질을 표면층 형성용 조성물에 첨가해도 좋다. 미립자 물질로, 예를 들면, 실리카, 산화 칼슘, 알루미나, 이산화티타늄, 산화 지르코늄, 산화 주석, 산화 인듐, 산화 카드뮴, 및 산화 아티몬 등의 무기계 미립자 물질이나, 폴리메틸메타크릴레이트, 폴리우레탄 및 폴리스티렌 등의 가교 또는 미가교 폴리머로 된 유기계 미립자 물질을 사용할 수 있다. 미립자 물질의 평균 입경은 100 ㎛ 이하인 것이 바람직하고, 보다 바람직하게는 0.1~50 ㎛이며, 보다 더 바람직하게는 0.5~20 ㎛이다. 또한, 조면화 처리와 미립자의 첨가를 병용해도 좋다.
Moreover, in order to form a fine texture in a surface layer, you may add a particulate matter to the composition for surface layer formation. As the particulate matter, for example, inorganic particulate matter such as silica, calcium oxide, alumina, titanium dioxide, zirconium oxide, tin oxide, indium oxide, cadmium oxide, and attimon oxide, polymethyl methacrylate, polyurethane, and Organic particulate materials made of crosslinked or uncrosslinked polymers such as polystyrene can be used. It is preferable that the average particle diameter of a particulate matter is 100 micrometers or less, More preferably, it is 0.1-50 micrometers, More preferably, it is 0.5-20 micrometers. Moreover, you may use together a roughening process and addition of microparticles | fine-particles.
표면재의 미끄러운감을 보다 적절히 하기 위해, 표면층 형성 조성물 중에 폴리실록산계 화합물을 함유시킬 수 있다. 폴리실록산계 화합물로는 직쇄상 또는 분기상의 폴리디오르가노실록산계 화합물 및 폴리오르가노실록산기 함유 공중합체가 바람직하다. 또한, 주쇄나 측쇄의 말단에 비닐기나 (메타)아크릴로일기 등의 반응성기를 갖는 폴리실록산계 화합물도 바람직하다. 폴리디오르가노실록산계 화합물의 예로는 폴리디메틸실록산이다. 폴리디메틸실록산의 메틸기의 일부 내지 전부가 다른 유기치환기로 치환되어도 좋다. 치환되는 메틸기의 위치는 말단이나 연쇄내라도 좋다.
In order to make the slipperiness of the surface material more appropriate, the polysiloxane compound may be contained in the surface layer forming composition. As the polysiloxane compound, a linear or branched polydiorganosiloxane compound and a polyorganosiloxane group-containing copolymer are preferable. Moreover, the polysiloxane type compound which has reactive groups, such as a vinyl group and a (meth) acryloyl group, at the terminal of a main chain or a side chain is also preferable. An example of the polydiorganosiloxane compound is polydimethylsiloxane. Some or all of the methyl groups of the polydimethylsiloxane may be substituted with other organic substituents. The position of the substituted methyl group may be in terminal or chain.
다른 유기치환기로, 예를들면, 메틸기 이외의 알킬기, 아릴기, 시클로알킬기 및 폴리옥시알킬렌 고리나 폴리에스테르 고리 등이 반복되는 단위를 갖는 연쇄 고리가 있다. 유기치환기의 수산기, 아민기, 에폭시기, 아실기, 아실옥시기, 카르복실기, 그 밖의 관능기를 가질 수 있다. 상기 반복 단위를 가지는 연쇄 고리로, 예를 들면, 폴리옥시에틸렌 고리, 폴리옥시 프로필렌 고리, 폴리옥시테트라메틸렌 고리, 폴리(옥시에틸렌옥시프로필렌) 고리 등의 폴리옥시알킬렌 고리나, 폴리카프로 락톤 고리나 폴리에틸렌세바케토 고리, 폴리에틸렌아디페이트 고리 등의 폴리에스테르 고리를 들 수 있다.
As another organic substituent, there exists a chain ring which has a unit which repeats alkyl groups other than a methyl group, an aryl group, a cycloalkyl group, and a polyoxyalkylene ring, a polyester ring, etc., for example. It may have a hydroxyl group, an amine group, an epoxy group, an acyl group, an acyloxy group, a carboxyl group, and other functional groups of an organic substituent. As a chain ring which has the said repeating unit, For example, polyoxyalkylene ring, such as a polyoxyethylene ring, a polyoxypropylene ring, a polyoxytetramethylene ring, a poly (oxyethyleneoxypropylene) ring, and a polycaprolactone ring And polyester rings such as polyethylene sebaketo ring and polyethylene adipate ring.
상기 연쇄 고리의 말단이 수산기, 카르복실기, (메타)아크릴기 또는 비닐기인 경우, 그 말단을 예를 둘면, 알킬에테르화나 알킬에스테르화해서 유기기로 봉쇄해도 좋다. 또한, 이 연쇄 고리는 통상 디메틸렌기나 트리메틸렌기 등의 알킬렌기를 통해서 규소 원자와 결합하고 있지만, 이것에 한정되는 것은 아니다.
When the terminal of the chain ring is a hydroxyl group, a carboxyl group, a (meth) acryl group or a vinyl group, the terminal may be, for example, alkylated or alkylesterized to be sealed with an organic group. In addition, although this chain ring couple | bonds with the silicon atom normally through alkylene groups, such as a dimethylene group and trimethylene group, it is not limited to this.
폴리오르가노실록산기 함유 공중합체는, 폴리오르가노실록산기 함유 화합물과 비닐계 화합물로부터 형성되는 폴리오르가노실록산기 함유 그라프트 공중합체 세그멘트 A와 비닐계 화합물로부터 형성되는 폴리오르가노실록산기를 함유하지 않은 중합체 세그멘트 B로 되는 A-B형 블록 공중합체가 바람직하다. 상기 화합물로, 예를 들면, 시판품으로서 입수할 수 있는 모디파-FS700, FS710, FS720, FS730(모두 일본유지(주)제, 상품명)등이 있다. 폴리실록산계 화합물의 표면층 형성용 조성물 중에 0.01~10 중량%을 함유한다. 상기 함유량으로는 0.01~5 중량%인 것이 더 바람직하다.
The polyorganosiloxane group-containing copolymer does not contain a polyorganosiloxane group formed from a polyorganosiloxane group-containing graft copolymer segment A formed from a polyorganosiloxane group-containing compound and a vinyl compound and a vinyl-based compound. Preferred are AB type block copolymers which are polymer segment B. Examples of the compound include Modifa-FS700, FS710, FS720, and FS730 (all manufactured by Nippon Oil Holding Co., Ltd., trade names) available as commercial products. 0.01-10 weight% is contained in the composition for surface layer formation of a polysiloxane compound. As said content, it is more preferable that it is 0.01-5 weight%.
표면층 형성 조성물을 기재에 직접 또는 기재에 적층된 기능층 위에 도포하는 방법으로는, 롤코팅법, 딥코팅법, 솔칠도법, 스프레이코팅법, 바코팅법, 나이프코팅법, 다이코팅법, 그라비아 코팅법, 커튼 플로우 코팅법, 리버스 코팅법, 키스 코팅법, 콤마 코팅법 등의 공지된 어떠한 방법이라도 좋다. 또한, 도포하는데 있어서는 필요에 따라 기재와 표면층(피막)과의 밀착성을 향상시키기 위해, 미리 코로나 방전 등의 전처리를 하여도 좋다.
As a method of applying the surface layer-forming composition directly to the substrate or on the functional layer laminated on the substrate, a roll coating method, a dip coating method, a brush painting method, a spray coating method, a bar coating method, a knife coating method, a die coating method, and a gravure coating method Any known method such as a method, a curtain flow coating method, a reverse coating method, a kiss coating method, or a comma coating method may be used. In application, pretreatment such as corona discharge may be performed in advance in order to improve the adhesion between the substrate and the surface layer (film) as necessary.
상기와 같이 기재에 직접 또는 기재에 적층된 기능층 위에 도포되고, 건조된 표면층 형성용 조성물을 경화하는 방법으로는, 특별히 한정하지 않고, 공지의 방법으로 행할 수 있다. 자외선 조사에 의하여 경화시키는 경우에는, 종래 공지의 광중합 개시제를 표면층 형성용 조성물 중에 첨가한 후에 경화시킨다. 광중합 개시제로, 예를 들면, 2,2-디메톡시-2-페닐아세토페논, 아세토페논, 벤조페논, 크산톤, 3-메틸아세토페논, 4-클로로벤조페논, 4,4'-디메톡시벤조페논, 벤조인푸로필에테르, 벤질디메틸개타르, N,N,N',N'-테트라메틸-4,4'-디아미노벤조페논, 1-(4-이소프로필 페닐)-2-히드록시-2-메틸프로판-1-온, 2-히드록시-2-메틸-1-페닐-프로판-1-온, 기타 치오키산토계 화합물 등을 들 수 있다.
It does not specifically limit as a method of apply | coating directly to the base material or the functional layer laminated | stacked on the base material as mentioned above, and hardening the dried composition for surface layer formation, It can carry out by a well-known method. When hardening by ultraviolet irradiation, it hardens after adding a conventionally well-known photoinitiator in the composition for surface layer formation. As the photoinitiator, for example, 2,2-dimethoxy-2-phenylacetophenone, acetophenone, benzophenone, xanthone, 3-methylacetophenone, 4-chlorobenzophenone, 4,4'-dimethoxybenzo Phenone, benzoin furopropyl ether, benzyldimethylgatar, N, N, N ', N'-tetramethyl-4,4'-diaminobenzophenone, 1- (4-isopropyl phenyl) -2-hydroxy 2-methyl-propan- 1-one, 2-hydroxy- 2-methyl- 1-phenyl- propane- 1-one, the other chiokisanto type compound, etc. are mentioned.
경화에 사용되는 에너지선원으로는, 예를 들면, 고압수은 램프, 할로겐 램프, 크세논 램프, 질소 레이저, 전자선 가속장치, 방사성 원소 등의 선원이 사용된다. 에너지 선원의 조사량은, 자외선 파장 365nm에서 적산노광량으로서, 50~5000mJ/cm2인 것이 바람직하다. 조사량이 50mJ/cm2 미만인 경우, 경화가 충분하게 되지 않기 때문에, 표면층의 내마모성이나 경도가 저하된다. 한편, 조사량이 5000mJ/cm2을 초과하는 경우, 표면층이 착색되고 투명성이 저하된다.
As an energy source used for curing, for example, a source of high pressure mercury lamp, halogen lamp, xenon lamp, nitrogen laser, electron beam accelerator, radioactive element or the like is used. It is preferable that the irradiation amount of an energy source is 50-5000mJ / cm <2> as an integrated exposure amount in an ultraviolet-ray wavelength 365nm. When irradiation amount is less than 50mJ / cm <2> , since hardening does not become enough, the abrasion resistance and hardness of a surface layer fall. On the other hand, when irradiation amount exceeds 5000 mJ / cm < 2 >, a surface layer will color and transparency will fall.
가열에 의한 경화를 행하는 경우, 종래의 열중합 개시제를 표면층 형성용 조성물 중에 첨가한 후에 당해 조성물을 경화시킨다. 열중합 개시제로, 예를 들면, 케톤퍼록사이드, 파옥시개타르, 하이드로퍼록사이드, 디알킬퍼록사이드, 지아실파오키사이도, 파옥시디카보네이트 등을 들 수 있다. 상기 열중합 개시제는 단독으로 사용해도 좋고, 2 종류 이상 병용해도 좋다.
When hardening by heating, after adding a conventional thermal-polymerization initiator in the composition for surface layer formation, the said composition is hardened. As a thermal polymerization initiator, a ketone peroxide, paoxygatar, hydroperoxide, dialkyl peroxide, a giacyl paokicydo, a paoxydicarbonate, etc. are mentioned, for example. The said thermal polymerization initiator may be used independently and may be used together two or more types.
상기 표면층 형성용 조성물 중에는, 성능을 손상시키지 않는 범위에서, 필요에 따라, 안료, 충전제, 계면활성제, 분산제, 가소제, 자외선 흡수제, 산화 방지제 를 첨가할 수 있다. 이들을 단독으로 사용해도 좋고, 2 종류 이상 병용해도 좋다.
In the said surface layer forming composition, a pigment, a filler, surfactant, a dispersing agent, a plasticizer, a ultraviolet absorber, and antioxidant can be added as needed in the range which does not impair performance. These may be used independently and may be used together two or more types.
또한, 표면층이 형성되어 있는 기재의 반대 면에 점착층을 형성할 수 있고, 그에 의해 필기감 중 패인감을 보다 개선할 수 있다. 상기와 같은 점착층으로, 예를 들면, 아크릴계 점착제나 고무계 점착제를 이용할 수 있지만, 투명성의 면에서 아크릴계 점착제를 이용하는 것이 보다 바람직하다. 이들 점착제 중에는, 점착성 폴리머 성분외에, 가소제, 점착 부여 성분을 포함시킬 수 있지만, 투명성을 손상시키지 않는 첨가제를 사용하는 것이 보다 바람직하다.
Moreover, an adhesion layer can be formed in the opposite surface of the base material in which the surface layer is formed, and it can improve the dent feeling among writing feelings by this. As the above-mentioned pressure-sensitive adhesive layer, for example, an acrylic pressure-sensitive adhesive or a rubber pressure-sensitive adhesive can be used, but it is more preferable to use an acrylic pressure-sensitive adhesive in terms of transparency. In these adhesives, although a plasticizer and a tackifying component can be included in addition to an adhesive polymer component, it is more preferable to use the additive which does not impair transparency.
아크릴계 점착제의 주성분인 점착성 폴리머로는, 아크릴산2-에틸헥실, 아크릴산부틸, 아크릴산이소옥틸, 메타크릴산부틸, 메타크릴산프로필 등의 알킬기의 탄소수가 1~10의 알코올과 (메타)아크릴산과의 알킬에스테르와 아크릴산, 메타크릴산, 말레인산, 푸마르산, 아크릴산 히드록시에틸, 메타크릴산 히드록시에틸 등의 관능기 함유 불포화 단량체와의 공중합체를 사용하는 것이 바람직하다.
As an adhesive polymer which is a main component of an acrylic adhesive, C1-C10 alcohol and alkyl (meth) acrylic acid of alkyl groups, such as 2-ethylhexyl acrylate, butyl acrylate, isooctyl acrylate, butyl methacrylate, and propyl methacrylate, It is preferable to use a copolymer of an alkyl ester with a functional group-containing unsaturated monomer such as acrylic acid, methacrylic acid, maleic acid, fumaric acid, hydroxyethyl acrylate and hydroxyethyl methacrylate.
고무계 점착제의 주성분인 점착성 폴리머로는, 스티렌-부타디엔 랜덤 공중합체, 스티렌-이소프렌계 부로츠쿠 공중합체, 천연 고무 등을 사용하는 것이 바람직하다. 상기한 성분에 의한 점착층을 5~100 ㎛의 두께로 형성하는 것이 바람직하다.
As an adhesive polymer which is a main component of a rubber-based adhesive agent, it is preferable to use a styrene-butadiene random copolymer, a styrene-isoprene-based butotsuk copolymer, natural rubber, etc. It is preferable to form the adhesion layer by said component in thickness of 5-100 micrometers.
표면층이 형성되어 있는 기재의 반대 면에 형성되는 도전성층으로는, 산화주석(SnO2 등), 산화 인듐, 산화 안티몬, 산화 아연(ZnO), 산화 카드뮴, 인듐석 산화물(ITO) 등의 금속 산화물이나, 금, 은, 동, 알루미늄, 주석, 니켈 등의 금속막을 들 수 있다. 상기한 것 중에서, 산화 아연, 산화 주석 등의 단일 금속으로 된 산화물이 화학량론비에 의한 제어가 용이하여 고성능인 얇은 막을 얻을 수 있는 점에서 바람직하다. 상기 도전성층의 적층 방법으로는 특별히 한정되지 않고, 스퍼터링법, 진공 증착법, 이온 도금법, 저압 플라즈마법, 도공법 및 상압 플라즈마 화학 증착(CVD)법 등을 들 수 있다. 상기 도전성층의 두께는, 도전성능이나 적외선 및 전자파의 감소 성능이 발현되고, 또한 투명성이 유지되는 두께, 즉 가시광 투과율이 60% 이상이기 위해서는, 도전성층의 두께는 30~200nm 인 것이 바람직하다.
Examples of the conductive layer formed on the opposite side of the substrate on which the surface layer is formed include metal oxides such as tin oxide (SnO 2, etc.), indium oxide, antimony oxide, zinc oxide (ZnO), cadmium oxide, and indium tin oxide (ITO). And metal films such as gold, silver, copper, aluminum, tin, and nickel. Among the above, oxides made of a single metal such as zinc oxide or tin oxide are preferable in terms of easy control by stoichiometric ratio and a high performance thin film. It does not specifically limit as a lamination method of the said conductive layer, A sputtering method, a vacuum vapor deposition method, an ion plating method, a low pressure plasma method, a coating method, an atmospheric pressure plasma chemical vapor deposition (CVD) method, etc. are mentioned. The thickness of the conductive layer is preferably 30 to 200 nm in order for the thickness of the conductive ability, the infrared ray and the electromagnetic wave reduction performance to be expressed and the transparency to be maintained, that is, the visible light transmittance is 60% or more.
이하, 본 실시태양에 따른 이점를 설명한다.Hereinafter, the advantages according to the present embodiment will be described.
본 실시 태양의 펜 입력 장치용 표면재는, 동마찰계수가 0.02~0.5이고, 정마찰계수가 0.4~1.5로 설정된 표면층을 갖는데, 입력 펜을 조작면에 접촉시킬 때의 감촉, 및 입력 펜으로 입력 조작을 할 때의 필기감이 우수하다.
The surface material for a pen input device of this embodiment has a surface layer whose dynamic friction coefficient is 0.02-0.5, and the static friction coefficient is 0.4-1.5, The touch when an input pen contacts an operation surface, and inputs with an input pen Excellent handwriting when operating.
상기 소정의 조건하에서 표면층의 복원은 하중 10~1000g에서 복원되는 경우, 표면층의 패인감은 적절하게 되고, 펜 입력할 때에 종이의 부드러운 느낌을 얻을 수 있다. 표면층을 반복해서 닦은 후의 헤이즈값의 증가가 10% 이하인 경우, 표면층의 내구성이 높아진다. 표면층의 중심선 평균 거칠기(Ra)가 0.1~5.0 ㎛인 경우, 표면층의 까칠까칠감은 적절한 정도로 된다. 따라서, 본 실시태양의 표면재를 사용한 펜 입력 장치에 있어서, 입력 조작이 쾌적하고, 펜 조작자는 쉽게 피로하지 않게 된다.
When the restoration of the surface layer under the predetermined conditions is restored under a load of 10 to 1000 g, the sensation of the surface layer becomes appropriate, and a soft feeling of paper can be obtained at the time of pen input. When the increase in haze value after repeated wiping of the surface layer is 10% or less, the durability of the surface layer is increased. When center line average roughness Ra of a surface layer is 0.1-5.0 micrometers, the roughness of a surface layer becomes an appropriate grade. Therefore, in the pen input device using the surface material of the present embodiment, the input operation is comfortable, and the pen operator is not easily tired.
이하, 본 발명의 실시예를 상세히 설명한다. Hereinafter, embodiments of the present invention will be described in detail.
펜 입력 장치용 표면재에 관해서, 정마찰계수, 동마찰계수, 도막복원성, 헤이즈값, 중심선 평균 거칠기(Ra), 전광선 투과율 및 필기감을 아래와 같은 방법으로 평가하였다.
The surface materials for pen input devices were evaluated by the following methods: static friction coefficient, dynamic friction coefficient, coating film resilience, haze value, center line average roughness (Ra), total light transmittance and writing feeling.
1) 정마찰계수 및 동마찰계수1) static friction coefficient and dynamic friction coefficient
20℃, 50% 상대습도의 분위기하에서 입력 펜을 이용하여 하중 200g로 펜 입력 장치용 표면재의 표면층을 10cm/sec의 속도로 이동시킬 때의 동마찰계수(㎲, 단위 없음) 및 정마찰계수(μK, 단위 없음)를 표면성 시험기기로 측정했다. 또한, 입력 펜은 팜(palm)사제, 상품명: 스타이라스를 사용하고, 표면성 시험기기는 신동 과학제, 상품명: 토라이보기아, 타입: 14DR을 사용했다.
Dynamic friction coefficient (㎲, no unit) and static friction coefficient when the surface layer of the surface material for pen input device is moved at a speed of 10 cm / sec with a load of 200 g using an input pen in an atmosphere of 20 ° C. and 50% relative humidity ( μK, no units) was measured with a surface tester. In addition, the input pen used the palm company make, brand name: Stylas, and the surface test apparatus used the Shinto Scientific make, brand name: Toraiboa, type: 14DR.
2) 도막 복원성2) film resilience
20℃, 50% 상대습도의 분위기하에서 선단경 0.75mm의 초경재료제 가상체를 사용하고 펜 입력 장치용 표면재의 표면층을 10cm/sec의 속도로 긁을 때에 복원되는 가상체에 대한 하중(g)을 도막 복원성으로 해서 긁기식 경도계(독일 에리쿠센사제, 상품명: 긁기식 경도계, 모델 318)로 측정했다.
Using a cemented carbide material with a tip diameter of 0.75 mm in an atmosphere of 20 ° C. and 50% relative humidity, the load (g) on the virtual body restored when the surface layer of the surface material for pen input device is scraped at a speed of 10 cm / sec It measured by the scratch-type hardness tester (Erikusen Co., Ltd. make, brand name: scratch-type hardness meter, model 318) as coating film recoverability.
3) 헤이즈값3) haze value
20℃, 50% 상대습도의 분위기하에서 면포(직경 20mm의 원형)을 이용하고, 하중 200g으로 펜 입력 장치용 표면재의 표면층을 10cm/sec의 속도로 1000회 왕복시켜서 닦았을 때의 헤이즈값(%)의 증가량을 표면성 시험기기와 직독 헤이즈미터로 측정했다. 또한, 증가량은 표면재를 1000회 닦은 후의 헤이즈값(%) - 초기의 헤이즈값(%)으로 산출했다. 또한, 표면성 시험기기는 신동 과학(주)제, 상품명: 토라 아보기아, 타입: 14DR을 이용하고, 직독 헤이즈미터는 동양정밀 기계 제작소사제, 상품명: 직독 헤이즈미터(No. 206)을 이용했다.
Haze value (%) when wiped by reciprocating the surface layer of the surface material for pen input device 1000 times at a speed of 10 cm / sec using a cotton cloth (circle having a diameter of 20 mm) under an atmosphere of 20 ° C. and 50% relative humidity at a load of 200 g. ) Was measured with a surface tester and a direct reading haze meter. In addition, the increase amount computed the haze value (%)-initial stage haze value (%) after wiping the surface material 1000 times. In addition, the surface test apparatus used by Shin-Dong Science Co., Ltd., brand name: Tora Abogia, type: 14DR, and the direct reading haze meter used by Dongyang Precision Machinery Co., Ltd., brand name: direct reading haze meter (No. 206). .
4) 중심선 평균 거칠기(Ra)4) Center Line Average Roughness Ra
JIS B0601-1982에 따르고, 절단(cutoff)치 0.8mm, 세로 배율 5000 배로 촉침식 표면 거칠기 형상 측정기(동경정밀사제, 상품명: 서프콤 550A)를 사용하고 펜 입력 장치용 표면재의 표면층에 있어서의 중심선 평균 거칠기(Ra, 단위: ㎛)을 측정했다.
According to JIS B0601-1982, the center line in the surface layer of the surface material for pen input devices, using a stylus surface roughness shape measuring instrument (trade name: SURFCOM 550A) at a cutoff value of 0.8 mm and a vertical magnification of 5000 times. Average roughness Ra (unit: micrometer) was measured.
5) 전광선 투과율5) total light transmittance
직독 헤이즈미터(동양정기제작소사제, 상품명: 직독 헤이즈미터(No. 206)을 사용하고, 광학 특성으로서의 전광선 투과율(%)을 측정했다.
The total light transmittance (%) as an optical characteristic was measured using the direct reading haze meter (Dongyang Seiki Co., Ltd. make, brand name: a direct reading haze meter (No. 206).
6) 필기감6) writing
10 인의 시험인이 입력 펜을 사용하고 표면층 위에 실제로 필기하고, 필기감을 미끄러운감, 패인감 및 까칠까칠감에 관해서 평가했다. 10인 중 6인 이상의 시험인이 연필을 사용하여 종이에 쓸 때처럼 필기감이 양호하다고 판단한 경우를 ○ 으로 평가하였고, 10 인 중 3~5 명이 필기감이 양호하다고 판단한 경우를 △ 으로 평가하였으며, 그리고 10 인 중 2 명 이하가 필기감이 양호하다고 판단한 경우를 × 로 분류하여 평가하였다.
Ten test subjects used an input pen to actually write on the surface layer and evaluated the feeling of writing in terms of slipperiness, dents, and roughness. 6 or more of 10 test subjects judged that writing feeling was good as when writing on paper using pencil, and 3-5 of 10 people judged that writing feeling was good as △, and Two or less of the ten people judged the case where it was judged that the writing feeling was favorable by classifying as x.
<< 실시예Example 1> 1>
우레탄 아크릴레이트(신나카무라 화학공업(주)제, 상품명: NK 올리고 U-108A) 80 중량부와 펜타에리스리톨트리아크릴레이트 10 중량부와 아크릴산 20 중량부와 폴리실록산계 화합물(빅 케미(Byk-chemie)사제, 상품명: BYK-300) 0.1 중량부로 된 혼합액에 평균 입경 10 ㎛의 폴리스티렌계 미립자 5 중량부를 첨가하여 충분히 교반함으로써 표면층용 수지액을 제조하였다.
80 parts by weight of urethane acrylate (manufactured by Shin-Nakamura Chemical Co., Ltd., trade name: NK oligo U-108A), 10 parts by weight of pentaerythritol triacrylate, 20 parts by weight of acrylic acid, and a polysiloxane compound (Byk-chemie) (Trade name: BYK-300) 5 weight part of polystyrene microparticles | fine-particles of 10 micrometers of average particle diameters were added to the liquid mixture of 0.1 weight part, and the resin liquid for surface layers was prepared by fully stirring.
수지액을 롤코타로, 두께 100 ㎛의 기재(폴리아세틸셀룰로오스 필름) 위에 도포하여 20 ㎛의 균일한 두께를 갖는 수지도막을 형성하였다. 전자 커튼형 EB장치(ESI 사제)에 의해 전자선을 조사(150keV, 5 Mrad)하고 수지도막을 경화시켰다. 다음에, 기재의 반대측의 면에 아크릴계 점착제를 포함하는 용액을 도공, 건조시켜, 점착층을 형성함으로써 실시예 1의 펜 입력 장치용 표면재를 작성했다. 이 펜 입력 장치용 표면재를 터치 입력 장치를 가진 액정 디스플레이 표면에 상온하에서 압착·첨부하여 펜 입력 장치를 작성했다. 이를 사용하여 정마찰계수, 동마찰계수, 도막복원성, 헤이즈값, 중심선 평균 거칠기(Ra), 전광선 투과율 및 필기감에 관한 평가를 행하였다. 그 결과를 표 1에 나타냈다.
The resin solution was applied by roll coat on a substrate (polyacetyl cellulose film) having a thickness of 100 µm to form a resin coating film having a uniform thickness of 20 µm. The electron beam was irradiated (150 keV, 5 Mrad) by the electron curtain type EB apparatus (made by ESI), and the resin coating film was hardened. Next, the surface material for pen input devices of Example 1 was created by coating and drying the solution containing an acrylic adhesive on the surface on the opposite side of a base material, and forming an adhesion layer. The surface material for pen input devices was crimped | bonded and attached to the liquid crystal display surface which has a touch input device at normal temperature, and the pen input device was created. Using this, static friction coefficient, dynamic friction coefficient, coating film resilience, haze value, center line average roughness (Ra), total light transmittance, and writing feeling were evaluated. The results are shown in Table 1.
<< 실시예Example 2> 2>
폴리에틸렌 글리콜 #600 디아크릴레이트 40 중량부와 트리메티롤프로판트리 아크릴레이트 10 중량부와 디메틸아크릴아미드 50 중량부와 폴리실록산계 화합물(신에쯔화학공업(주)제, 상품명: KF-351A) 0.1 중량부와 2-히드록시-2-메틸-1-페닐-프로판-1-온(광중합 개시제) 5 중량부로 된 혼합액에 평균 입경 14 ㎛의 아크릴계 미립자 5 중량부를 첨가후, 충분히 교반함으로써 표면층용 수지액을 제조하였다.
40 parts by weight of polyethylene glycol # 600 diacrylate, 10 parts by weight of trimetholpropane triacrylate, 50 parts by weight of dimethyl acrylamide and a polysiloxane compound (manufactured by Shin-Etsu Chemical Co., Ltd., brand name: KF-351A) 0.1 5 parts by weight of acryl-based fine particles having an average particle diameter of 14 μm were added to a mixed solution of 5 parts by weight of 2-hydroxy-2-methyl-1-phenyl-propane-1-one (photopolymerization initiator), followed by sufficiently stirring to obtain a resin for the surface layer. Liquid was prepared.
상기 수지액을 롤코타로 두께 100 ㎛의 기재(폴리에틸렌 테레프탈레이트 필름) 위에 도포하여, 20 ㎛의 균일한 두께를 갖는 수지도막을 형성하였다. 질소 분위기하에서 120W 고압 수은등(일본전지(주)제)에 의해 자외선을 조사(3J/cm2)하고 수지도막을 경화시켰다. 다음에, 기재의 반대측의 면에 아크릴계 점착제를 포함하는 용액을 도공, 건조하여 점착층을 형성함으로써 실시예 2의 펜 입력 장치용 표면재를 작성하였다. 이 펜 입력 장치용 표면재를 터치 입력 장치를 가진 액정 디스플레이 표면에 상온하에서 압착·첨부함으로써 펜 입력 장치를 작성하였다. 이를 사용하여 실시예 1과 마찬가지로 각종 평가를 행하였다. 그 결과를 표 1에 나타내었다.
The resin liquid was applied onto a substrate (polyethylene terephthalate film) having a thickness of 100 μm with a roll coater to form a resin coating film having a uniform thickness of 20 μm. Under a nitrogen atmosphere, ultraviolet rays were irradiated (3 J / cm 2 ) with a 120 W high-pressure mercury lamp (manufactured by Nippon Battery Co., Ltd.) to cure the resin coating film. Next, the surface material for pen input devices of Example 2 was created by coating and drying the solution containing an acrylic adhesive on the surface on the opposite side of a base material, and forming an adhesion layer. The pen input device was created by crimping | bonding and attaching the surface material for pen input devices to the liquid crystal display surface which has a touch input device at normal temperature. Various evaluation was performed similarly to Example 1 using this. The results are shown in Table 1.
<< 실시예Example 3> 3>
수산기가 50의 아크릴 폴리올 100 중량부와 헥사메틸렌디이소시아네이트 20 중량부와 실리카계 미립자 7 중량부로 된 혼합액을 충분히 교반하여 표면층용 수지액을 조정하였다. 상기 수지액을 롤코타로 두께 100 ㎛의 기재(폴리에틸렌테레프 탈레이트 필름) 위에 30 ㎛의 균일한 두께로 수지도막을 형성하였다. 100℃에서 10 분간 건조시키고, 점착층을 형성함으로써 실시예 3의 펜 입력 장치용 표면제를 작성하였다. 이 펜 입력장치용 표면재를 터치 입력 장치를 가진 액정 디스플레이 표면에 상온하에서 압착·첨부하여 펜 입력 장치를 작성하였다. 이를 이용하여 실시예 1과 마찬가지로 각종 평가를 행하였다. 그 결과를 표 1에 나타내었다.
The resin liquid for surface layer was adjusted by fully stirring the liquid mixture which the hydroxyl value of 100 weight part of 50 acrylic polyols, 20 weight part of hexamethylene diisocyanate, and 7 weight part of silica type microparticles | fine-particles was stirred. The resin solution was roll coated to form a resin coating film with a uniform thickness of 30 μm on a substrate (polyethylene terephthalate film) having a thickness of 100 μm. It dried at 100 degreeC for 10 minutes, and formed the adhesive agent, and the surface agent for pen input devices of Example 3 was created. The surface material for pen input devices was crimped | bonded and attached to the liquid crystal display surface which has a touch input device at normal temperature, and the pen input device was created. Various evaluation was performed similarly to Example 1 using this. The results are shown in Table 1.
<< 실시예Example 4> 4>
폴리에틸렌 글리콜 #1000 디아크릴레이트 60 중량부와 에틸렌 옥사이드 변성 트리메티롤프로판트리아크릴레이트 10 중량부와 라우릴아크릴레이트 30 중량부와 디-2-에틸헤키실펠오키시디카보네토 5 중량부로 된 혼합액에 입경 10 ㎛의 아크릴계 미립자를 3 중량부 첨가한 후, 충분히 교반하여 표면층용 수지액을 제조하였다. 이 수지액을 롤코타로 두께 100 ㎛의 기재(폴리에틸렌 테레프탈레이트 필름) 위에 도포하고, 20 ㎛의 균일한 두께를 갖는 수지도막을 형성하였다. 100℃에서 10분간 건조시키고, 수지도막을 경화시켰다. 다음에, 기재의 반대측의 면에 아크릴계 점착제를 포함하는 용액을 도공, 건조하여, 점착층을 형성함으로써 실시예 4의 펜 입력 장치용 표면제를 작성하였다. 이 펜 입력 장치 표면재를 터치 입력 장치를 갖는 액정 디스플레이 표면에 상온하에서 압착·첨부하여 펜 입력 장치를 작성하였다. 이를 이용하여 실시예 1과 마찬가지로 각종 평가를 행하였다. 그 결과를 표 1에 나타내었다.
60 parts by weight of polyethylene glycol # 1000 diacrylate, 10 parts by weight of ethylene oxide-modified trimetholpropane triacrylate, 30 parts by weight of lauryl acrylate, and 5 parts by weight of di-2-ethylhexyl feloxysicicarbonone After adding 3 weight part of acryl-type microparticles | fine-particles of 10 micrometers of particle diameters to it, it fully stirred, and manufactured the resin liquid for surface layers. This resin liquid was apply | coated on the 100-micrometer-thick base material (polyethylene terephthalate film) by roll coat, and the resin coating film which has a uniform thickness of 20 micrometers was formed. It dried at 100 degreeC for 10 minutes, and hardened the resin film. Next, the surface agent for pen input devices of Example 4 was created by coating and drying the solution containing an acrylic adhesive on the surface on the opposite side of a base material, and forming an adhesive layer. This pen input device surface material was crimped and attached to a liquid crystal display surface having a touch input device at room temperature to create a pen input device. Various evaluation was performed similarly to Example 1 using this. The results are shown in Table 1.
<< 실시예Example 5> 5>
트리에틸렌 디이소시아네이트 유도체(다케다약품공업(주)제, 상품명: 타케네토 D-212) 40 중량부와 폴리카프로락톤 변성 히드록시에틸아크릴레이트(다이세르 화학공업(주)제, 상품명: 플레이크 셀 FA3) 60 중량부로 된 우레탄 아클릴레이트 77 중량부와 폴리디메틸시로키산마쿠로모노마(칫소(주)제, 상품명: FM0721) 15 중량부와 메틸메타크릴레이트 25 중량부와 부틸메타크릴레이트 25 중량부와 이소시아네이트에틸메타크릴레이트(소화전공(주)제, 상품명: 커런츠 MOI) 15 중량부와 펜타에리스리톨트리아크릴레이트(동아합성(주)제, 상품명: 아로닉스 M305) 20 중량부로 된 자외선 경화성 실리콘 공중합체 20 중량부와 1-히드록시-시쿠로헤키실 페닐-케톤(광개시제) 3 중량부로 된 표면층용 수지액을 제조하였다. 이 수지액을 롤코타로 두께 100 ㎛의 기재(폴리에틸렌 테레프탈레이트 필름) 위에 도포하여, 20 ㎛의 균일한 두께를 갖는 수지도막을 형성하였다. 질소 분위기하에서 120W 고압 수은등(일본전지(주)제)에 의해 자외선을 조사(1J/cm2)하여 수지도막을 경화시켰다. 다음에, 기재의 반대측의 면에 아크릴계 점착제를 포함하는 용액을 도공, 건조하여, 점착층을 형성함으로써 실시예 5의 펜 입력 장치용 표면재를 작성하였다. 이 펜 입력 장치용 표면재를 터치 입력 장치를 갖는 액정 디스플레이 표면에 상온하에서 압착·첨부함으로써 펜 입력 장치를 작성하였다. 이것을 이용하여 실시예 1과 마찬가지로 각종 평가를 행하였다. 그 결과를 표 1에 나타내었다.
40 parts by weight of triethylene diisocyanate derivative (manufactured by Takeda Pharmaceutical Co., Ltd., trade name: Takeneto D-212) and polycaprolactone-modified hydroxyethyl acrylate (manufactured by Dieser Chemical Industry Co., Ltd., trade name: Flake Cell FA3 ) 60 parts by weight of urethane acrylate 77 parts by weight and polydimethylshirokisan Makuromonoma (manufactured by Chisso Corporation, trade name: FM0721) 15 parts by weight, 25 parts by weight of methyl methacrylate and 25 parts by weight of butyl methacrylate Ultraviolet curable silicone consisting of 15 parts by weight of buta isocyanate ethyl methacrylate (manufactured by Digestion Electric Co., Ltd., brand name: Currants MOI) and 20 parts by weight of pentaerythritol triacrylate (manufactured by Dong-A Synthetic Co., Ltd., brand name: Aronix M305) The resin liquid for surface layers which consisted of 20 weight part of copolymers and 3 weight part of 1-hydroxy-cyclohekisyl phenyl- ketones (photoinitiator) was prepared. This resin liquid was applied onto a substrate (polyethylene terephthalate film) having a thickness of 100 µm with a roll coater to form a resin coating film having a uniform thickness of 20 µm. In a nitrogen atmosphere, ultraviolet rays were irradiated (1 J / cm 2 ) with a 120 W high-pressure mercury lamp (manufactured by Nippon Battery Co., Ltd.) to cure the resin coating film. Next, the surface material for pen input devices of Example 5 was created by coating and drying the solution containing an acrylic adhesive on the surface on the opposite side of a base material, and forming an adhesion layer. The pen input device was created by crimping | bonding and attaching the surface material for pen input devices to the liquid crystal display surface which has a touch input device at normal temperature. Various evaluation was performed similarly to Example 1 using this. The results are shown in Table 1.
<< 실시예Example 6> 6>
우레탄 아크릴레이트 72 중량부와 자외선 경화성 실리콘 공중합체 20 중량부와 폴리오르가노실록산기 함유 공중합체(일본 유지(주)제, 상품명: 모디파 FS710) 5 중량부와 1-히드록시-시쿠로헤키실-페닐-케톤 3 중량부로 이루어진 표면층용 수지액을 제조하였다. 상기 우레탄 아크릴레이트는 트리에틸렌 디이소시아네이트 유도체(다케다약품공업(주)제, 상품명: 타케네토 D-212) 30 중량부와 폴리카프로락톤 변성 히드록시에틸아크릴레이트(다이세르 화학공업(주)제, 상품명: 플레이크 셀 FA3) 70 중량부를 반응시켜 얻은 것이다. 자외선 경화성 실리콘 공중합체는, 폴리디메틸시로키산마쿠로모노마(칫소(주)제, 상품명: FM0721) 10 중량부와 부틸메타크릴레이트 30 중량부와 이소시아네이트에틸메타크릴레이트(소화전공(주)제, 상품명: 커런츠 MOI) 15 중량부와 펜타에리스리톨 아크릴레이트(동아합성(주)제, 상품명: 아로닉스 M305) 20 중량부와 메틸메타크릴레이트 25 중량부를 반응시켜 얻은 것이다. 1-히드록시-시클로헥실-페닐-케톤은 광중합 개시제이다. 표면층용 수지액을 두께 100 ㎛의 기재(폴리에틸렌 테레프탈레이트 필름) 위에 롤코터로 균일하게 도포하여 30 ㎛의 균일한 두께를 갖는 수지도막을 형성하였다. 질소 분위기하에서 120W 고압 수은등(일본전지(주)제)에 의해 자외선을 조사(1J/cm2)하고 수지도막을 경화시켰다. 그 다음, 기재의 반대측의 면에 아크릴계 점착제를 포함하는 용액을 도공하고, 건조하여 점착층을 형성함으로써 펜 입력 장치용 표면재를 제작하였다. 이 펜 입력 장치용 표면재를 터치 입력 장치를 가진 액정 디스플레이 표면에 상온 하에서 압착하고 첨부하여 펜 입력 장치를 제작하였다. 이를 이용하여 실시예 1과 마찬가지로 각종 평가를 행하였다. 그 결과를 표 1에 나타내었다.
72 parts by weight of urethane acrylate, 20 parts by weight of an ultraviolet curable silicone copolymer, and 5 parts by weight of a polyorganosiloxane group-containing copolymer (manufactured by Nippon Oil and Fats Co., Ltd., trade name: Modifa FS710) and 1-hydroxy-shikurohe A resin solution for a surface layer consisting of 3 parts by weight of a keyyl-phenyl-ketone was prepared. The urethane acrylate is 30 parts by weight of triethylene diisocyanate derivative (manufactured by Takeda Pharmaceutical Co., Ltd., trade name: Takeneto D-212) and polycaprolactone modified hydroxyethyl acrylate (manufactured by Dieser Chemical Industry Co., Ltd., Product name: Flakes Cell FA3) 70 parts by weight of a reaction was obtained. The ultraviolet curable silicone copolymer is 10 parts by weight of polydimethylshirokisan makuromonoma (manufactured by Chisso Co., Ltd., brand name: FM0721), 30 parts by weight of butyl methacrylate and isocyanate ethyl methacrylate (digestion major) And 15 parts by weight of Currants MOI), 20 parts by weight of pentaerythritol acrylate (manufactured by Dong-A Synthetic Co., Ltd., product name: Aronix M305) and 25 parts by weight of methyl methacrylate. 1-hydroxy-cyclohexyl-phenyl-ketone is a photopolymerization initiator. The resin liquid for surface layer was apply | coated uniformly by the roll coater on the base material (polyethylene terephthalate film) of thickness 100micrometer, and the resin coating film which has a uniform thickness of 30micrometer was formed. Under a nitrogen atmosphere, ultraviolet rays were irradiated (1 J / cm 2 ) with a 120 W high-pressure mercury lamp (manufactured by Nippon Battery Co., Ltd.) to cure the resin coating film. Next, the surface material for pen input devices was produced by coating the solution containing an acrylic adhesive on the surface on the opposite side of a base material, drying, and forming an adhesion layer. The surface material for pen input devices was crimped | bonded and attached to the liquid crystal display surface which has a touch input device at normal temperature, and the pen input device was produced. Various evaluation was performed similarly to Example 1 using this. The results are shown in Table 1.
<< 비교예Comparative example 1> 1>
두께 125 ㎛의 기재(폴리에틸렌 테레프탈레이트 필름)에 아크릴계 하드 코팅 수지를 도공하고 경화하여 두께 5 ㎛의 하드코팅층을 형성하였다. 기재의 반대 면에 아크릴산2-에틸헥실 100 중량부와 아크릴산 10 중량부와의 공중합체를 주성분으로 하는 아크릴계 점착제를 도공하여 40 ㎛의 균일한 두께의 투명 점착제층을 형성하여 건조함으로써 표면재를 작성하였다.
An acrylic hard coating resin was coated on the substrate (polyethylene terephthalate film) having a thickness of 125 μm and cured to form a hard coating layer having a thickness of 5 μm. On the opposite side of the substrate, an acrylic pressure sensitive adhesive having a copolymer of 100 parts by weight of 2-ethylhexyl acrylate and 10 parts by weight of acrylic acid as a main component was coated to form a transparent adhesive layer having a uniform thickness of 40 µm and dried to prepare a surface material. .
이 표면재를 터치 입력 장치를 가진 액정 디스플레이 표면에 상온하에서 압착·첨부하여 펜 입력 장치를 작성하였다. 이를 이용하여 실시예 1과 마찬가지로 각종 평가를 행하였다. 그 결과를 표 1에 나타내었다.
This surface material was crimped | bonded and attached to the liquid crystal display surface which has a touch input device at normal temperature, and the pen input device was created. Various evaluation was performed similarly to Example 1 using this. The results are shown in Table 1.
<< 비교예Comparative example 2> 2>
자외선 경화형 아크릴계 수지 100 중량부와 입경 5~10 ㎛의 아크릴 수지계 비즈 2 중량부와 미량의 실리콘 수지를 함유하는 수지액을 제조하였다. 이 수지액을 100 ㎛ 두께의 투명한 폴리에틸렌테레프탈레이트 필름의 한쪽 면에 도포하고, 자외선 조사에 의하여 경하시켜 두께 5 ㎛의 수지층을 형성하였다. 이 폴리에틸렌테레프탈레이트 필름의 반대 면에 아크릴계 점착제 용액을 도공하고 건조하여 표면 재를 작성하였다. 이 표면재를 터치 입력 장치를 가진 액정 디스플레이 표면에 상온하에서 압착·첨부함으로써 펜 입력 장치를 작성하였다. 이를 이용하여 실시예 1과 마찬가지로 각종 평가를 행하였다. 그 결과를 표 1에 나타내었다.
A resin liquid containing 100 parts by weight of an ultraviolet curable acrylic resin, 2 parts by weight of an acrylic resin beads having a particle diameter of 5 to 10 µm, and a small amount of a silicone resin was prepared. This resin liquid was apply | coated to one side of the 100-micrometer-thick transparent polyethylene terephthalate film, and it was lightened by ultraviolet irradiation, and the resin layer of thickness 5micrometer was formed. An acrylic pressure-sensitive adhesive solution was coated on the opposite side of the polyethylene terephthalate film and dried to prepare a surface material. The pen input device was created by crimping | bonding and attaching this surface material to the liquid crystal display surface which has a touch input device at normal temperature. Various evaluation was performed similarly to Example 1 using this. The results are shown in Table 1.
<< 비교예Comparative example 3> 3>
두께 100 ㎛의 폴리에틸렌테레프탈레이트 필름의 편면에, 폴리카프로락톤트리올과 폴리실록산계 화합물을 주성분으로 하는 폴리올액(100 중량부)과 헥사메틸렌이소시아네이트를 주성분으로 하는 이소시아네이트액(90 중량부)을 혼합해서 도공하여 두께 300 ㎛의 수지층을 형성하였다. 이 수지층을 120℃에서 20분 가열한 후, 폴리에틸렌테레프탈레이트 필름에서 박리하고, 연질 수지 필름을 작성하였다. 이 연질 수지 필름의 표면에 아크릴계 점착제 용액을 도공하고 건조하여 표면재를 작성하였다. 이 표면재를 터치 입력 장치를 가진 액정 디스플레이 표면에 상온하에서 압착·첨부함으로써 펜 입력 장치를 작성하였다. 이를 이용하여 실시예 1과 마찬가지로 각종 평가를 행하였다. 그 결과를 표 1에 나타내었다.
On one side of a 100-micrometer-thick polyethylene terephthalate film, a polyol liquid (100 parts by weight) containing polycaprolactone triol and a polysiloxane compound as a main component and an isocyanate solution (90 parts by weight) containing hexamethylene isocyanate as a main component It coated and formed the resin layer of 300 micrometers in thickness. After heating this resin layer at 120 degreeC for 20 minutes, it peeled from the polyethylene terephthalate film and created the soft resin film. An acrylic adhesive solution was coated on the surface of this soft resin film, and it dried and created the surface material. The pen input device was created by crimping | bonding and attaching this surface material to the liquid crystal display surface which has a touch input device at normal temperature. Various evaluation was performed similarly to Example 1 using this. The results are shown in Table 1.
실시예 1~4의 표면재로는, 모두 미끄러운감, 패인감, 까칠까칠감의 필기감을 얻을 수 있고, 종합적인 필기감의 평가에 있어서도 양호하였다. 실시예 5 및 6에있어서는, 까칠까칠감이 부족하지만 패인감이 있고, 또 미끄러운감이 적절하기 때문에 종합적인 필기감은 양호하였다.
As the surface material of Examples 1-4, the writing feeling of slippery feeling, a dent feeling, and a feeling of roughness were all acquired, and also it was favorable also in evaluation of a comprehensive writing feeling. In Examples 5 and 6, the feeling of roughness was insufficient, but the overall feeling of writing was good because there was a feeling of indentation and slipperiness was appropriate.
이에 대해 비교예는 모두, 미끄러운감이 적절치 않고, 또한 비교예 1에서는 특히 까칠까칠감이 부족하고, 양호한 필기감을 얻을 수 없었다. 또한, 비교예 2에서는 특히 패인감이 부족하고, 양호한 필기감을 얻을 수 없었다. 또한, 비교예 3에서는 특히 까칠까칠감이 부족하고, 양호한 필기감을 얻을 수 없었다.
On the other hand, in all the comparative examples, slipperiness was inadequate, and in Comparative Example 1, in particular, the roughness was insufficient, and a good writing feeling could not be obtained. Moreover, in Comparative Example 2, the feeling of inferiority was particularly insufficient, and a good writing feeling could not be obtained. Moreover, in the comparative example 3, in particular, the rough feeling lacked, and the favorable writing feeling was not acquired.
상기 실시 태양을 다음과 같이 변경할 수도 있다.The above embodiment may be changed as follows.
미끄러운감을 향상시키기 위해, 폴리실록산계 화합물에 대신하는 불소계 화합물을 표면층 형성용 조성물에 함유시켜도 좋다. In order to improve the slippery feeling, a fluorine compound instead of the polysiloxane compound may be included in the surface layer-forming composition.
기재 면에 점착층을 설치하지 않고, 적절한 접착제에 의하여 표면재를 디스플레이의 전면에 접착시켜도 좋다.
The surface material may be adhere | attached on the front surface of a display by a suitable adhesive agent, without providing an adhesion layer in the surface of a base material.
본 발명은 필기감이 우수한 펜 입력 장치용 표면재 및 이를 이용한 펜 입력 장치에 이용 가능하다.
INDUSTRIAL APPLICABILITY The present invention can be used for a pen input device surface material having excellent writing feeling and a pen input device using the same.
Claims (14)