KR100923254B1 - Paint For Forming The Peeling Layer And Method Of Forming The Peeling Layer - Google Patents
Paint For Forming The Peeling Layer And Method Of Forming The Peeling Layer Download PDFInfo
- Publication number
- KR100923254B1 KR100923254B1 KR1020070136308A KR20070136308A KR100923254B1 KR 100923254 B1 KR100923254 B1 KR 100923254B1 KR 1020070136308 A KR1020070136308 A KR 1020070136308A KR 20070136308 A KR20070136308 A KR 20070136308A KR 100923254 B1 KR100923254 B1 KR 100923254B1
- Authority
- KR
- South Korea
- Prior art keywords
- coating film
- weight
- paint
- forming
- peeling
- Prior art date
Abstract
금속 표면에 도장되어 도막을 보호하고 일정한 기간이 경과한 후에 쉽게 박리될 수 있는 박리 도막 형성용 도료 및 도막 형성방법에 관한 것이다. 상기 도료는 염화 비닐계 수지 15 내지 35중량%, 도막의 유연성을 유지하기 위한 가소제 8 내지 15중량%, 도막의 박리성을 확보하기 위한 알콜계 또는 에스테르계 이형제 2 내지 5중량%, 분산제, 유동성 조절제 및 소포제를 포함하는 첨가제 3 내지 8 중량%, 색상을 부여하기 위한 안료 1 내지 5 중량% 및 여분의 혼합유기 용제를 포함한다. 상기 도료는 대상체를 일시적으로 보호한 후 제거될 수 있는 도막을 형성하기 위해 사용된다. 상기 도료는 금속 표면에 도장된 도막 보호 능력이 뛰어나고, 작업성이 우수하며, 도막 박리가 용이한 특징을 가는 도막을 형성할 수 있다.The present invention relates to a peeling coating film-forming paint and a method for forming a coating film which are coated on a metal surface to protect the coating film and that can be easily peeled off after a certain period of time has passed. The paint is 15 to 35% by weight of the vinyl chloride resin, 8 to 15% by weight plasticizer to maintain the flexibility of the coating film, 2 to 5% by weight alcohol- or ester-based release agent to ensure the peelability of the coating film, dispersant, fluidity 3 to 8% by weight of an additive comprising a regulator and an antifoaming agent, 1 to 5% by weight of a pigment for imparting color and an extra mixed organic solvent. The paint is used to form a coating that can be removed after temporarily protecting the subject. The paint can form a coating film having excellent coating film protection ability coated on a metal surface, excellent workability, and easy peeling of the coating film.
박리 도막, 이형제 Peeling Film, Release Agent
Description
본 발명은 박리 도막 형성용 도료 및 박리 도막 형성 방법에 관한 것으로서 금속의 표면이나 금속 표면에 도장된 도막을 보호하고 일정한 기간이 경과한 후에 쉽게 박리될 수 있는 박리 도막 형성용 도료 및 박리 도막 형성 방법에 관한 것이다.The present invention relates to a coating film for forming a peeling coating film and a method for forming a peeling coating film, the method for forming a peeling coating film and a peeling coating film that can be easily peeled off after a certain period of time, protecting the surface of the metal or the coating film coated on the metal surface. It is about.
선박의 제조시 선박 또는 도장 공정이 수행된 선박의 표면을 보호하기 위해 코팅되어 도장된 도막을 보호하고 일정한 기간이 경과한 후에 쉽게 박리(剝離)될 수 있는 박리 도막 형성용 도료를 사용하고 있다. 일반적으로 선박을 건조하는 과정을 개략적으로 설명하면, 먼저 선체의 블록을 제작하여 선체에 조립시 필용한 용접부를 제외한 부분에 도장을 하고, 이 제작된 블록을 도크(dock)에서 용접하여 선체의 외부 및 내부의 도장(塗裝)과 기본적인 내부설비와 엔진설치, 전기장치 설치, 배관설치 등의 실질적인 내부공사를 수행하게 된다.In the manufacture of ships, to protect the surface of the vessel or the vessel in which the painting process is carried out, a coating film for forming a peeling coating film which protects the coated film and is easily peeled off after a certain period of time is used. In general, the process of drying the ship is described schematically, first, to produce a block of the hull and to paint the parts except the weld required when assembling the hull, and to weld the produced block in the dock (dock) to the outside of the hull And inside the painting (기본적인) and basic internal equipment and engine installation, electrical installation, piping installation, etc. Substantial internal construction will be carried out.
상기의 선박 건조과정 중에서 선체의 블록을 제작하는 과정은 금속의 산화하여 부식되는 것을 방지하기 위하여 도장을 실시하고 2 내지 3개월 동안 실외에 노 출되어 대기한 후에 선체에 조립되어 용접작업이 진행된다. 상기 선체의 블록을 제작하는 공정은 통상 야외에 노출되어 작업이 진행되며 도장 표면이 먼지 및 해풍으로 인한 오염 발생이 심하며, 용접작업을 통하여 선체에 조립되는데 이 때 용접에 의한 불티로 인하여 도장된 표면에 손상을 입게 되어 선체 조립 완료 후 다시 재 도장을 실시함으로 인한 많은 비용 및 시간이 추가되는 문제점이 발생된다.The process of manufacturing the block of the hull during the ship construction process is painted to prevent oxidation and corrosion of the metal, exposed to the outdoors for 2 to 3 months, then assembled to the hull is welded progress . The process of manufacturing the hull block is usually exposed to the outdoors and the work is progressed, the surface of the painting is heavily polluted due to dust and sea wind, and is assembled to the hull through welding work, the surface painted due to the sparking by welding It causes a problem that adds a lot of cost and time due to repainting after the hull assembly is completed.
또한 선체에 조립된 후에도 엔진설치, 전기장치 설치, 배관설치 등의 내부공사 기간이 3개월 내지 1년 이상 장기간 소요되므로 건조 완료하여 선주에게 인계되기 전에 이미 많은 먼지 및 해수로 인한 오염으로 미관상 좋지 않은 문제점이 발생된다. 따라서 이러한 문제점을 해소하기 위해 블록을 제작한 다음 도장을 실시하고 제거가 용이한 박리(剝離) 페인트를 도장하여 선체 조립이 완료된 후에 박리 페인트 도막을 제거함으로써 선체조립 후 재도장하는 비용 및 시간을 절약할 수 있고 깨끗한 상태로 선주에게 인도할 수 있다.In addition, since the internal construction period such as engine installation, electric equipment installation, and piping installation takes 3 months to 1 year or more even after being assembled to the hull, it is not aesthetically pleasing due to the pollution caused by a lot of dust and seawater before it is completed and handed over to the owner. Problems arise. Therefore, in order to solve this problem, the block is manufactured and then coated, and the peeling paint is easily applied and the peeling paint is removed after the hull assembly is completed, thereby saving the cost and time of repainting after hull assembly. I can do it and lead it to the owner in a clean state.
이러한 종래의 유성 박리 페인트는 내구성이 불량하여 선체 제작 완료 후 박리 페인트 도막 제거에 어려움이 있으며, 수성의 박리 페인트 제품은 온도가 5℃ 이하에서는 균일한 도막이 형성되지 않아 박리에 문제가 있어 겨울에는 사용할 수 없는 계절적 한계를 가지고 있다.These conventional oil-based peeling paints are difficult to remove the peeling paint film after completion of the hull production due to poor durability, water-based peeling paint products are used in winter because there is a problem in peeling because a uniform coating film is not formed at a temperature below 5 ℃. There is no seasonal limit.
상술한 문제점을 해결하기 위한 본 발명의 목적은 알콜계 또는 에스테르계 이형제를 포함함으로서 광택성과 상온 박리성이 용이한 도막을 형성할 수 있는 박리 도막 형성용 도료를 제공하는데 있다.SUMMARY OF THE INVENTION An object of the present invention for solving the above problems is to provide a release coating film-forming paint which can form a coating film having excellent glossiness and room temperature peelability by including an alcohol-based or ester-based release agent.
또한, 상술한 문제점을 해결하기 위한 본 발명의 다른 목적은 알콜계 또는 에스테르계 이형제를 포함함으로서 광택성과 상온 박리성이 용이한 도막을 형성할 수 있는 박리 도막 형성용 도료를 이용하여 박리 도막을 형성할 수 있는 방법을 제공하는데 있다.In addition, another object of the present invention for solving the above-mentioned problems is to form a peeling coating film using a paint for forming a peeling coating film that can form a coating film having a gloss and easy to peel at room temperature by including an alcohol- or ester-based release agent To provide a way to do it.
상기 목적을 달성하기 위한 본 발명의 일 실시예에 따른 박리 도막 형성용 도료는 염화 비닐계 수지 15 내지 35중량%, 도막의 유연성을 유지하기 위한 가소제 8 내지 15중량%, 알콜계 또는 에스테르계 이형제 2 내지 5중량%, 분산제, 유동성 조절제 및 소포제를 포함하는 첨가제 3 내지 8 중량%, 색상을 부여하기 위한 안료 1 내지 5 중량% 및 여분의 혼합유기 용제를 포함한다. 상기 박리 도막 형성용 도료는 대상체를 일시적으로 보호한 후 제거될 수 있는 도막을 형성하기 위해 사용된다.Peeling film forming paint according to an embodiment of the present invention for achieving the above object is 15 to 35% by weight of vinyl chloride resin, 8 to 15% by weight plasticizer for maintaining the flexibility of the coating film, alcohol or ester-based release agent 2 to 5% by weight, 3 to 8% by weight of additives including dispersant, flow control agent and antifoaming agent, 1 to 5% by weight of pigment for imparting color and extra mixed organic solvent. The release coating film-forming paint is used to form a coating film that can be removed after temporarily protecting the object.
또한, 상기 다른 목적을 달성하기 위한 본 발명의 일 실시예에 따른 박리 도막을 형성하기 위해서는 먼저, 도료 도장 공정이 수행된 대상체에 염화 비닐계 수지 15 내지 35중량%, 도막의 유연성을 유지하기 위한 가소제 8 내지 15중량%, 알콜 계 또는 에스테르계 이형제 2 내지 5중량%, 분산제, 유동성 조절제 및 소포제를 포함하는 첨가제 3 내지 8 중량%, 색상을 부여하기 위한 안료 1 내지 5 중량% 및 여분의 혼합유기 용제를 포함하는 박리 도막 형성용 도료를 도장한다. 이어서, 상기 대상체에 도장된 상기 박리 도막 형성용 도료를 건조시킨다. 그 결과 상기 대상체의 표면에는 박리 도막이 형성된다.In addition, in order to form a peeling coating film according to an embodiment of the present invention for achieving the above another object, 15 to 35% by weight of the vinyl chloride-based resin to the object, the coating coating process is performed, for maintaining the flexibility of the coating film 8 to 15% by weight plasticizer, 2 to 5% by weight alcoholic or ester release agent, 3 to 8% by weight additives including dispersant, rheology control agent and antifoaming agent, 1 to 5% by weight pigment to impart color and extra mixing The coating material for peeling coating film formation containing an organic solvent is coated. Subsequently, the release coating film-forming paint coated on the object is dried. As a result, a peeling coating film is formed on the surface of the object.
일 예로서, 상기 염화 비닐계 수지의 예로서는 염화 비닐 수지, 비닐계 단량체로 변성된 염화비닐 수지 등을 들 수 있다.As one example, examples of the vinyl chloride-based resin include vinyl chloride resin, vinyl chloride resin modified with vinyl monomer, and the like.
상술한 조성을 갖는 박리 도막 형성용 도료는 알콜계 또는 에스테르계 이형제를 포함하고 있어 유기수지의 특성인 유연성(신율)과 강한 인장력을 갖는 동시에 제거가 용이하여 기존 소지의 도장상태와 관계없이 코팅이 가능하다. 이에 따라 건조 후 바로 다음 공정이 가능하게 되어 작업공기 및 생산성을 향상시킬 수 있다.The coating material for forming a release coating film having the above-described composition includes an alcohol-based or ester-based release agent, which has flexibility (elongation) and strong tensile force, which are characteristics of organic resins, and can be easily removed, so that coating can be performed regardless of the existing coating state. Do. Accordingly, the next process is possible immediately after drying, thereby improving work air and productivity.
이하, 본 발명의 바람직한 실시예들에 따른 박리 도막 형성용 도료 및 이를 이용한 박리 도막 형성방법을 상세히 설명하지만, 본 발명은 하기의 실시예들에 한정되지 않고 다른 형태로 구현될 수도 있다. 또한, 상기 중량%와 중량부는 상호 교환적으로 사용될 수 있으며 여기서 소개되는 실시예들은 개시된 내용이 보다 완전해질 수 있도록 그리고 당업자에게 본 발명의 사상과 특징이 충분히 전달될 수 있도록 하기 위해 제공된다.Hereinafter, the peeling coating film-forming paint and the peeling coating film forming method using the same according to preferred embodiments of the present invention will be described in detail, but the present invention is not limited to the following embodiments and may be implemented in other forms. In addition, the weight percent and weight portion may be used interchangeably and the embodiments introduced herein are provided to make the disclosure more complete and to fully convey the spirit and features of the invention to those skilled in the art.
박리 도막 형성용 도료 및 박리 도막 형성방법Peeling film forming paint and peeling film forming method
박리 도막 형성용 도료는 도장공정이 수행된 선박 등과 같은 대상체에 도장되어 상기 대상체를 일시적으로 보호한 후 제거될 수 있는 도막을 형성하는데 적용된다. 상기 박리 도막 형성용 도료는 염화 비닐계 수지, 가소제, 이형제, 분산제, 유동성 조절제 및 소포제를 포함하는 첨가제, 안료 및 유기 용제를 포함한다.The paint for forming a release coating film is applied to an object such as a vessel on which a painting process is performed, and is applied to form a coating film which can be removed after temporarily protecting the object. The peeling coating film-forming coating material includes a vinyl chloride-based resin, a plasticizer, a mold releasing agent, a dispersant, an additive including a flow control agent and an antifoaming agent, a pigment, and an organic solvent.
구체적으로 본 발명의 박리 도막 형성용 도료는 염화 비닐계 수지 15 내지 35중량%와 도막의 유연성을 유지하기 위한 가소제 8 내지 15중량%, 도막의 박리성을 확보하기 위한 알콜계 또는 에스테르계 이형제 2 내지 5중량%와, 분산제, 유동성 조절제 및 소포제를 포함하는 첨가제 3 내지 8중량%와. 안료 1 내지 5중량% 및 여분의 혼합 유기용제를 포함할 수 있다. Specifically, the paint for forming a release coating film of the present invention is 15 to 35% by weight of vinyl chloride resin and 8 to 15% by weight of a plasticizer for maintaining the flexibility of the coating film, alcohol or ester release agent 2 to secure the peelability of the coating film. To 5% by weight, and 3 to 8% by weight of an additive comprising a dispersant, a flow control agent and an antifoaming agent. It may include 1 to 5% by weight of the pigment and the extra mixed organic solvent.
상기 염화 비닐계 수지는 상기 유기 용제에 용해되어 표면에 도장되며 용제가 건조된 후 표면을 보호하는 역할을 하며, 선박 건조가 완료되어 도막을 박리가 필요할 때 쉽게 박리가 일어날 수 있는 특성을 갖는 것이 바람직하다. 상기 박리 도막을 형성용 도료에 적용될 수 있는 염화 비닐계 수지의 예로서는 염화 비닐 수지, 비닐계 단량체로 변성된 염화비닐 수지 등을 들 수 있다. 이들은 단독 또는 둘 이상을 혼합하여 사용할 수 있다.The vinyl chloride-based resin is dissolved in the organic solvent and coated on the surface, and serves to protect the surface after the solvent is dried. The vinyl chloride-based resin has a property of easily peeling off when the ship drying is completed and the coating film needs to be peeled off. desirable. Examples of the vinyl chloride resin that can be applied to the paint for forming the release coating film include a vinyl chloride resin, a vinyl chloride resin modified with a vinyl monomer, and the like. These can be used individually or in mixture of 2 or more.
상기 박리 도막 형성용 도료에 포함된 염화 비닐계 수지의 함량이 전체 중량% 에 대하여 15중량% 미만이면, 형성되는 도막의 박리성이 불량하여 도막의 제거에 어려움이 있으며, 35중량%를 초과할 경우 금속이나 도장면과의 부착성이 뛰어나 도막이 박리되지 않는 어려움이 발생된다. 따라서, 상기 박리 도막 형성용 도료는 상기 염화 비닐계 수지를 약 15 내지 35중량% 포함하고, 바람직하게는 약 18 내지 30중량%를 포함한다.When the content of the vinyl chloride-based resin contained in the release coating film-forming paint is less than 15% by weight based on the total weight%, there is difficulty in removing the coating film due to poor peelability of the formed coating film, and may exceed 35% by weight. In this case, it is difficult to prevent the coating film from peeling off due to excellent adhesion to metal or painted surface. Therefore, the release coating film-forming paint contains about 15 to 35% by weight of the vinyl chloride resin, and preferably about 18 to 30% by weight.
상기 가소제는 상기 박리 도막 형성용 도료로 형성되는 도막의 유연성을 유지하기 위한 사용된다. 상기 가소제의 예로서는 디부틸프탈레이트, 디옥틸프탈레이트, 디부틸아디페이트, 디옥틸아디페이트, 디이소노닐 아디페이트, 디이소데실 아디페이트, 트리메틸올프로판 변성계, 네오펜틸글리콜 변성계 등을 들 수 있다. 이들은 단독 또는 둘 이상을 혼합하여 사용할 수 있다. The plasticizer is used to maintain the flexibility of the coating film formed of the coating film for forming the release coating film. Examples of the plasticizer include dibutyl phthalate, dioctyl phthalate, dibutyl adipate, dioctyl adipate, diisononyl adipate, diisodecyl adipate, trimethylolpropane modified system, neopentyl glycol modified system and the like. . These can be used individually or in mixture of 2 or more.
상기 가소제의 함량이 8 중량% 미만이면 형성되는 박리 도막의 유연성이 부족하여 형성되는 도막을 박리하는데 어려움이 있으며 특히 동절기 낮은 온도에서 형성되는 박리 도막에 제거가 일어나지 않고 도막이 끊어지는 현상이 발생한다. 반면에 15중량%를 초과할 경우 장시간 야외에 노출되면서 가소제가 이형되어 선체 보호를 위하여 도장해 놓은 도막으로 침투하는 문제점이 발생된다. 따라서, 상기 박리 도막 형성용 도료는 가소제를 약 8 내지 15중량%포함하고, 바람직하게는 약 10 내지 14중량%를 포함한다.If the content of the plasticizer is less than 8% by weight, it is difficult to peel off the coating film formed due to the lack of flexibility of the peeling coating film formed, and in particular, a phenomenon in which the coating film is broken without removal occurs in the peeling coating film formed at a low temperature in winter. On the other hand, if the content exceeds 15% by weight, the plasticizer is released after prolonged exposure to the open air for a long time, thereby causing a problem of penetrating into the coated film for protecting the hull. Thus, the release coating film-forming paint contains about 8 to 15% by weight of plasticizer, preferably about 10 to 14% by weight.
상기 도료에 적용되는 이형제의 예로서는 알콜계 이형제, 에스테르계 이형제등을 들 수 있다. 이들은 단독 또는 둘 이상을 혼합하여 사용할 수 있다. 특히 본 실시예에 적용되는 알콜계 이형제의 예로서는 폴리 글리세롤 등을 들 수 있고, 에스테르계 이형제의 예로서는 폴리글리세롤 지방산 에스테르 등을 들 수 있다. As an example of the mold release agent applied to the said coating agent, an alcohol type mold release agent, an ester type mold release agent, etc. are mentioned. These can be used individually or in mixture of 2 or more. In particular, examples of the alcohol releasing agent to be applied to this embodiment include polyglycerol and the like, and examples of the ester releasing agent include polyglycerol fatty acid esters and the like.
상기 박리 도막 형성용 도료에 포함되는 이형제 함량이 2 중량% 미만일 경우 박리 도막을 박리하는데 어려움이 발생되고, 반면에 5중량%를 초과할 경우 박리 도 막의 박리 후에도 박리 도막의 잔여물이 잔존하여 먼지 등으로 인한 오염을 촉진한다. 따라서, 상기 박리 도막 형성용 도료는 상기 이형제를 약 2 내지 5중량%포함하고, 바람직하게는 약 3 내지 5중량%를 포함한다.When the release agent content in the release coating film is less than 2% by weight, it is difficult to peel off the release coating film. On the other hand, when the release agent is more than 5% by weight, the residue of the release coating film remains after peeling off the release coating film. Promotes contamination due to Accordingly, the release coating film-forming paint contains about 2 to 5% by weight of the release agent, preferably about 3 to 5% by weight.
상기 박리 도막 형성용 도료에 적용되는 첨가제의 예로서는 소포제, 평활제, 유동성 조절제 등을 들 수 있다. 상기 박리 도막 형성용 도료는 상기 첨가제를 약 3 내지 8중량%포함하고, 바람직하게는 약 4 내지 7중량%를 포함한다. 상기 첨가제는 박리 도막 형성용 도료의 작업성 및 물성을 균일하게 유지하기 위해 일반적으로 사용되는 것이기 때문에 본 발명에서는 이를 구체적으로 설명하지 않고 생략한다.As an example of the additive applied to the said coating material for peeling film formation, an antifoamer, a smoothing agent, a fluidity regulator, etc. are mentioned. The release coating film-forming paint contains about 3 to 8 wt% of the additive, and preferably about 4 to 7 wt%. Since the additive is generally used to maintain the workability and physical properties of the paint for forming a release coating film uniformly, the present invention will not be described without specific description thereof.
또한, 상기 박리 도막 형성용 도료는 도장부분의 식별을 위한 색상을 부여하는 안료를 포함한다. 상기 안료의 예로서는 체질안료, 유색안료 및 이들의 혼합 안료들을 들 수 있다. 상기 박리 도막 형성용 도료에 안료가 포함될 경우 포함되는 안료의 함량이 5중량%를 초과할 경우 도막 박리가 불량해지는 문제점이 발생된다. 따라서, 상기 박리 도막 형성용 도료는 상기 안료 약 1 내지 5중량%를 포함하고, 바람직하게는 약 1 내지 3중량%를 포함할 수 있다.In addition, the paint for forming a release coating film includes a pigment that gives a color for identification of a coating portion. Examples of the pigments include extender pigments, colored pigments and mixed pigments thereof. When the pigment is included in the paint for forming the release coating film, when the content of the pigment included exceeds 5% by weight, there is a problem that the peeling of the coating film becomes poor. Therefore, the paint for forming the release coating film may include about 1 to 5% by weight of the pigment, and preferably about 1 to 3% by weight.
상기 박리 도막 형성용 도료에 포함되는 혼합 유기용제는 박리 도막 형성용 도료의 도장의 작업성 확보를 위해 사용된다. 상기 유기용제의 예로서는 메틸알콜, 에틸알콜, 프로필알콜, 부틸알콜과, 아세톤, 메틸에틸케톤, 메틸이소부틸케톤, 메틸아밀케톤, 벤젠, 톨루엔, 크실렌, 에틸아세테이트, 부틸아세테이트, 셀로솔부아세테이트, 부틸셀로솔부, 부틸카르비톨 등을 들 수 있다. 이들은 둘 이상을 혼합하여 사용할 수 있다. 본 실시예에의 혼합 유기용제는 메틸이소부틸케톤 및 크실렌을 포함할 수 있다.The mixed organic solvent contained in the release coating film-forming paint is used to ensure the workability of the coating of the release coating film-forming paint. Examples of the organic solvent include methyl alcohol, ethyl alcohol, propyl alcohol, butyl alcohol, acetone, methyl ethyl ketone, methyl isobutyl ketone, methyl amyl ketone, benzene, toluene, xylene, ethyl acetate, butyl acetate, cellosolbuacetate, butyl Cellosol part, butyl carbitol, etc. are mentioned. These can mix and use two or more. The mixed organic solvent in this embodiment may include methyl isobutyl ketone and xylene.
상기 도료에 적용되는 유기 용제의 사용량이 작을 경우 도료의 점도가 높아 도장 작업성이 불량해지고, 상기 도료에 적용되는 유기 용제의 사용량이 많을 경우 도막 두께가 얇아져 한 번의 작업으로 마무리하는데 어려움이 있다. When the amount of the organic solvent applied to the paint is small, the viscosity of the paint is high and the painting workability is poor. When the amount of the organic solvent to be applied to the paint is large, the thickness of the coating film becomes thin, which makes it difficult to finish in one operation.
이하, 상기 박리 도막 형성용 도료를 이용하여 박리 도막을 형성하는 방법을 설명한다. 상기 박리 도막 형성용 도료의 구체적인 설명은 위에서 설명한 바와 같기 때문에 생략한다. Hereinafter, the method of forming a peeling coating film using the said coating film for peeling film formation is demonstrated. The detailed description of the paint for forming a release coating film is omitted because it is as described above.
도장이 공정이 수행된 선박 등의 대상체에 박리 도막을 형성하기 위해서는 먼저, 염화 비닐계 수지 15 내지 35중량%, 도막의 유연성을 유지하기 위한 가소제 8 내지 15중량%, 알콜계 또는 에스테르계 이형제 2 내지 5중량%, 분산제, 유동성 조절제 및 소포제를 포함하는 첨가제 3 내지 8 중량%, 색상을 부여하기 위한 안료 1 내지 5 중량% 및 여분의 혼합유기 용제를 포함하는 박리 도막 형성용 도료를 준비한다. In order to form a peeling coating film on an object such as a vessel on which a painting process is performed, first, 15 to 35% by weight of a vinyl chloride resin, 8 to 15% by weight of a plasticizer to maintain the flexibility of the coating film, an alcoholic or ester type release agent 2 A paint for forming a peeling coating film is prepared, which includes from 5% by weight to 3% by weight of an additive including a dispersant, a flow control agent and an antifoaming agent, 1 to 5% by weight of a pigment for imparting color and an extra mixed organic solvent.
이어서, 상기 박리 도막 형성용 도료를 상기 대상체에 에어리스 스프레이를 이용하여 도장한다. 일 예로서, 상기 박리 도막 형성용 도료는 건조 도막이 약 60 내지 180㎛의 두께를 갖도록 도장하고, 바람직하게는 약 80 내지 150㎛의 두께를 갖도록 도장한다.Subsequently, the release coating film-forming paint is applied to the object using an airless spray. As an example, the release coating film-forming paint may be coated such that the dry coating film has a thickness of about 60 to 180 μm, and preferably has a thickness of about 80 to 150 μm.
이어서, 상기 대상체에 표면에 도장된 박리 도막 형성용 도료를 건조시켜 박리 도막을 형성한다.Subsequently, the peeling coating film-forming paint coated on the surface of the object is dried to form a peeling coating film.
박리 도막 형성용 도료 제조Paint production for release coating film formation
실시예 1Example 1
메틸이소부틸케톤 36중량%, 크실렌 21중량%, 염화비닐수지 21중량%, TMP 변성계가소제(LGflex BET, LG화학) 10중량%, 알콜계 이형제(Hexaglycerol)3중량%, 안료인 티타늄디옥사이드 2중량%, 분산제 2.5중량%, 유동성조절제 4중량%, 소포제(EFKA-2040) 0.5중량%를 혼합하여 박리 도막 형성용 도료를 제조하였다.36% by weight of methyl isobutyl ketone, 21% by weight of xylene, 21% by weight of vinyl chloride resin, 10% by weight of TMP modified plasticizer (LGflex BET, LG Chemical), 3% by weight of alcohol-based release agent (Hexaglycerol), pigment titanium dioxide 2 By weight, 2.5% by weight of dispersant, 4% by weight of flow control agent, 0.5% by weight of antifoaming agent (EFKA-2040) was mixed to prepare a paint for forming a peeling coating film.
실시예 2Example 2
상기 실시예 1과 동일한 방법으로 박리 도막 형성용 도료를 제조하되, 상기 알콜계 이형제(Hexaglycerol)3중량%대신에 에스테르계 이형제(폴리글리세린 지방산 에스테르) 3중량%를 사용하여 박리 도막 형성용 도료를 제조하였다.A paint for forming a peeling coating film was prepared in the same manner as in Example 1, except that 3% by weight of an ester release agent (polyglycerin fatty acid ester) was used instead of 3% by weight of an alcoholic release agent (Hexaglycerol). Prepared.
비교예 1Comparative Example 1
상기 실시예 1과 동일한 방법으로 박리 도막 형성용 도료를 제조하되, 상기 TMP 변성계가소제 10중량% 및 알콜계 이형제(Hexaglycerol)3중량% 대신에 메톡사이디즈드 소이빈오일 10중량%과 오일 변성계 이형제(Additol VXL 1105, Solutia Inc) 3중량%를 사용하여 박리 도막 형성용 도료를 제조하였다.A paint for forming a release coating film was prepared in the same manner as in Example 1, except that 10% by weight of the TMP modified plasticizer and 3% by weight of alcohol-based mold release agent (Hexaglycerol), 10% by weight of methoxide synthesized soybean oil and oil modification 3 wt% of a system release agent (Additol VXL 1105, Solutia Inc) was used to prepare a paint for forming a release coating film.
비교예 2Comparative Example 2
상기 실시예 1과 동일한 방법으로 박리 도막 형성용 도료를 제조하되, 상기 실시예 1과 동일한 방법으로 박리 도막 형성용 도료를 제조하되, 상기 TMP 변성계가소제 10중량% 및 알콜계 이형제(Hexaglycerol)3중량% 대신에 디옥틸프탈레이트 10중량% 및 오일 변성계 이형제(Additol VXL 1105, Solutia Inc) 3중량%를 사용하여 박리 도막 형성용 도료를 제조하였다.A paint for forming a peeling coating film was prepared in the same manner as in Example 1, but a paint for forming a peeling coating film was prepared in the same manner as in Example 1, except that 10% by weight of the TMP modified plasticizer and an alcohol-based mold release agent (Hexaglycerol) 3 Instead of the weight percent, 10% by weight of dioctylphthalate and 3% by weight of an oil-modifying mold release agent (Additol VXL 1105, Solutia Inc) were used to prepare a paint for forming a peeling coating film.
비교예 3Comparative Example 3
상기 실시예 1과 동일한 방법으로 박리 도막 형성용 도료를 제조하되, 상기 TMP 변성계가소제 10중량% 및 알콜계 이형제(Hexaglycerol)3중량% 대신에 디프로필렌글리콜디벤조에이트가소제 10중량% 및 오일 변성계 이형제(Additol VXL 1105, Solutia Inc) 3중량%를 사용하여 박리 도막 형성용 도료를 제조하였다.A paint for forming a release coating film was prepared in the same manner as in Example 1, except that 10% by weight of the TMP modified plasticizer and 3% by weight of alcohol-based mold release agent (Hexaglycerol), 10% by weight of dipropylene glycol dibenzoate plasticizer and oil modification. 3 wt% of a system release agent (Additol VXL 1105, Solutia Inc) was used to prepare a paint for forming a release coating film.
비교예 4Comparative Example 4
상기 실시예 1과 동일한 방법으로 박리 도막 형성용 도료를 제조하되, 상기상기 염화비닐수지 21중량%과 알콜계 이형제(Hexaglycerol)3중량% 대신에 염화비닐수지 17중량%와 우레탄수지 4중량%와 오일 변성계 이형제(Additol VXL 1105, Solutia Inc) 3중량%를 사용하여 박리 도막 형성용 도료를 제조하였다.A paint for forming a release coating film was prepared in the same manner as in Example 1, but instead of 21% by weight of the vinyl chloride resin and 3% by weight of alcohol-based mold release agent (Hexaglycerol), 17% by weight of vinyl chloride resin and 4% by weight of urethane resin 3% by weight of an oil-modifying agent (Additol VXL 1105, Solutia Inc) was used to prepare a paint for forming a peeling coating film.
상기 실시예 1 내지 2 및 비교예 1 내지 4의 박리 도막 형성용 도료에 따른 각각의 성분 및 함량을 하기 표 1에 나타내었다.Table 1 shows the components and the contents according to the paints for forming the release coating films of Examples 1 to 2 and Comparative Examples 1 to 4, respectively.
[표 1] 도막 박리용 도료[Table 1] Paint for peeling coating film
박리 도막 형성용 도료의 평가Evaluation of paint for release coating film formation
먼저, 가로× 세로 200× 300mm 인 스틸 시편 위에 선박용 에폭시 도료를 도장하여 완전히 경화시킨 후 각 시편 위에 실시예 1 내지 2과 비교예1 내지 4 도료를 에어리스 스프레이로 건조도막두께 100㎛로 도장한 후 건조한다. 이후 실외에 3개월간 방치하여 형성된 도막의 박리성과 물성을 확인하였다. 상기 물성의 평가는 하기와 같은 평가 방법에 의해 평가되었고, 그 평가 결과가 표 2에 개시되어 있다.First, paint the epoxy coating for ships on steel specimens of width × length 200 × 300 mm and completely harden them, and then apply Examples 1 to 2 and Comparative Examples 1 to 4 on each specimen with airless spray to a dry coating thickness of 100 μm. To dry. After that, the peeling properties and physical properties of the coating film formed after being left for 3 months were checked. Evaluation of the said physical property was evaluated by the following evaluation method, The evaluation result is shown in Table 2.
[표 2]TABLE 2
상기 표 2를 참조하면, 실시예 1 내지 2의 박리 도막 형성용 도료는 비교예의 도료에 비해 비교적 높은 광택성을 갖는 동시에 우수한 박리성을 갖는 도막을 형성할 수 있음을 확인할 수 있다. 특히, 에스테르계 이형제를 포함하는 실시예 2의 도료는 모든 면에서 우수한 특성을 갖는 박리 도막을 형성할 수 있음을 확인할 수 있었다.Referring to Table 2, it can be seen that the paint for forming a release coating film of Examples 1 to 2 can form a coating film having a relatively high glossiness and excellent peelability compared to the paint of the comparative example. In particular, it was confirmed that the coating material of Example 2 containing an ester release agent can form a peeling coating film having excellent properties in all respects.
1) 상온 박리성 : 각시편을 상기의 조건으로 건조한 후 상온 25 ~ 30 ℃에서 박리하여 박리력과 인장강도, 신율을 아래 기준에 의거하여 평가 하였다.1) Room temperature peelability: Each specimen was dried under the above conditions, and then peeled at room temperature 25 ~ 30 ℃ to evaluate the peel force, tensile strength and elongation based on the following criteria.
◎ : 연속적으로 박리되며, 적정 인장강도와 신율을 갖고 박리력 0.04 kgf/2cm 미만.(Double-circle): It peels continuously, has moderate tensile strength and elongation, and peels less than 0.04 kgf / 2cm.
△ : 연속적으로 박리되며, 적정 인장강도와 신율을 갖고 있으나 박리력 0.04 kgf/2cm 이상.(Triangle | delta): It peels continuously and has moderate tensile strength and elongation, but peeling force is 0.04 kgf / 2cm or more.
× : 연속적으로 박리되나, 낮은 인장강도와 신율을 갖고 박리력 또한 0.04 kgf/2cm 이상.X: It is continuously peeled off, but has a low tensile strength and elongation, and the peeling force is also 0.04 kgf / 2 cm or more.
2) 선박도료 도막 변색2) Discoloration of ship paint film
◎ : 박리도료의 도막을 제거한 후 선박용 에폭시 도막과 박리도료의 도막을 형성하기 전 선박용 에폭시 도막과의 색상 차이가 없음.(Double-circle): There is no color difference between a ship's epoxy coating film and a ship's epoxy coating film after removing a peeling paint film and before forming a peeling paint film.
× : 박리도료의 도막을 제거한 후 선박용 에폭시 도막과 박리도료의 도막을 형성하기 전 선박용 에폭시 도막과의 색상 차이가 있음.X: After removing the coating film of the peeling paint, there is a color difference between the epoxy coating for ship and the epoxy coating for ship before forming the coating film of the peeling paint.
3) 선박도료 도막 광택3) Marine paint coating gloss
◎ : 박리도료의 도막을 제거한 후 선박용 에폭시 도막과 박리도료의 도막을 형성하기 전 선박용 에폭시 도막을 광택계로 60ㅀ 광택을 측정한 값의 차이가 -5 이상.(Double-circle): The difference of the value which measured the glossiness of 60 degrees with the glossmeter of the ship's epoxy coating film and the ship's epoxy coating film after forming the coating film of a peeling paint before forming a coating film of a peeling paint is -5 or more.
△ : 박리도료의 도막을 제거한 후 선박용 에폭시 도막과 박리도료의 도막을 형성하기 전 선박용 에폭시 도막을 광택계로 60ㅀ 광택을 측정한 값의 차이가 -5 ~ -25.(Triangle | delta): The difference of the value which measured the glossiness of 60 degree | times with the glossmeter of the ship epoxy coating film and the ship epoxy coating film after forming the coating film of a peeling paint before forming the coating film of a peeling paint is -5--25.
× : 박리도료의 도막을 제거한 후 선박용 에폭시 도막과 박리도료의 도막을 형성하기 전 선박용 에폭시 도막을 광택계로 60ㅀ 광택을 측정한 값의 차이가 -25 미만.X: After removing the coating film of the peeling paint, and before forming the ship epoxy coating film and the coating film of the peeling paint, the difference of the value which measured the glossiness of 60 degrees with a gloss meter with a glossmeter is less than -25.
4) 재도장성 : 박리 도료 도막을 제거한 후 선박용 에폭시 도료를 붓으로 터치 업하여 25℃에서 48시간 동안 경화시킨 도막을 1mm 간격으로 가로 세로 11줄씩 그어 100칸을 만든 후 점착 테이프를 이용하여 밀착성을 측정하였고, 다음 기준에 의해 평가하였다.4) Repainting: After removing the peeling paint film, touch up the epoxy paint for ships with a brush and draw hardened coating film at 25 ℃ for 48 hours at 11mm width by 11 lines to make 100 spaces, and then use adhesive tape for adhesiveness. It was measured and evaluated by the following criteria.
◎ : 도막 잔존율이 100%, △ : 도막잔존율이 95% 이상, × : 도막잔존율 90% 이상◎: coating film remaining rate is 100%, △: coating film remaining rate is 95% or more, ×: coating film remaining rate is 90% or more
이상에서 살펴본 바와 같이, 본 발명의 박리도막 형성용 도료는 유기수지의 특성인 유연성과 강한 인장력으로 제거가 용이하나, 선박용 에폭시 등의 기존 소지에 대한 영향과 보다 완벽한 박리를 위한 알콜계 또는 에스테르계 이형제를 포함한다. 따라서, 상술한 이형제를 포함하는 박리도막 형성용 도료는 기존 소지의 도장상태와 관계없이 코팅이 가능한과 동시에 건조 후 바로 다음 공정이 가능하게 되어 작업공기 및 생산성을 향상시킬 수 있다. 또한 이러한 특성을 통해 선박, 항공기, 자동차 등의 공정상에 이용될 수 있을 뿐만 아니라 가구 및 건물의 리모델링 등의 다양한 분야에 부분, 전체 기존 소지를 보호하기 위해 사용될 수 있다.As described above, the paint for forming a peeling coating of the present invention is easy to remove due to the flexibility and strong tensile strength of the organic resin, but the effect on the existing base such as ship epoxy and alcohol or ester based for more perfect peeling Release agents. Therefore, the paint for forming a release coating film including the above-described release agent can be coated regardless of the existing coating state and at the same time, the next step immediately after drying can improve work air and productivity. In addition, this property can be used not only in the process of ships, aircraft, automobiles, etc., but also to protect parts and entire existing possession in various fields such as remodeling of furniture and buildings.
이상, 본 발명의 바람직한 실시예를 참조하여 설명하였지만 해당 기술 분야의 통상의 지식을 가진 자라면 하기의 특허 청구의 범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 이해할 수 있을 것이다.The present invention has been described above with reference to preferred embodiments of the present invention, but those skilled in the art may variously modify the present invention without departing from the spirit and scope of the present invention as set forth in the claims below. And can be changed.
Claims (5)