KR100434269B1 - Coating composition including acrylic resin - Google Patents
Coating composition including acrylic resin Download PDFInfo
- Publication number
- KR100434269B1 KR100434269B1 KR10-2001-0026106A KR20010026106A KR100434269B1 KR 100434269 B1 KR100434269 B1 KR 100434269B1 KR 20010026106 A KR20010026106 A KR 20010026106A KR 100434269 B1 KR100434269 B1 KR 100434269B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- coating composition
- molecular weight
- monomer
- coating
- Prior art date
Abstract
본 발명은 1회 도장만으로도 외관품질이 우수하고, 내수성, 내산성, 내스크래치성 및 부착성 등이 우수한 도막을 얻기 위하여, 비닐형 이중결합을 갖는 단량체를 포함하고, (a) 산가 5 내지 30 mg KOH/g, (b) 수산기 함량 3.0 내지 6.0%, (c) 유리전이온도 -22 내지 100℃, (d) 25℃에서 가드너 점도 X 내지 Z2, (e) 수평균분자량 1,000 내지 25,000, (f) 중량평균분자량 6,000 내지 50,000, (g) 분자량 분포도 3의 조건을 만족하는 고형분 55% 이상의 아크릴 합성 수지, 및 이를 포함하는 고광택 도료를 제공한다.The present invention comprises a monomer having a vinyl double bond in order to obtain a coating film excellent in appearance quality and excellent in water resistance, acid resistance, scratch resistance and adhesion even with one coating, and (a) an acid value of 5 to 30 mg. KOH / g, (b) hydroxyl content 3.0 to 6.0%, (c) glass transition temperature -22 to 100 ° C, (d) Gardner viscosity X to Z2 at 25 ° C, (e) number average molecular weight 1,000 to 25,000, (f ) A weight average molecular weight of 6,000 to 50,000, (g) an acrylic synthetic resin having a solid content of 55% or more that satisfies the conditions of molecular weight distribution 3, and a high gloss paint containing the same.
Description
본 발명은 아크릴 수지 및 이를 포함하는 고광택 도료 조성물에 관한 것으로, 상세하게는 가전기기의 내외장 재료로 사용되는 각종 플라스틱 제품 및 부품에 하도 및 상도없이 1회 도장만으로 기존과 동등하거나 그 이상의 물성을 갖는 도료용 아크릴 합성 수지 및 이를 포함하는 도료 조성물에 관한 것이다.The present invention relates to an acrylic resin and a high gloss coating composition comprising the same, and more particularly, to a variety of plastic products and components used as interior and exterior materials of home appliances. It relates to an acrylic synthetic resin for paint having and a coating composition comprising the same.
도료는 보통 수지, 용제, 안료, 첨가제, 신너(희석제) 등으로 구성되고, 주로 목재, 철재 또는 플라스틱 등의 제품 및 부품 표면에 피복되어 이를 보호하는 작용을 하며 물체 표면에 원하는 색채와 광택을 부여함으로써 외관을 변화시켜 도장된 물체를 장식하는 작용을 한다.Paint is usually composed of resins, solvents, pigments, additives, thinners, etc., and is mainly coated on the surface of products and parts such as wood, steel, or plastics to protect them and give the desired color and gloss to the surface of objects. By changing the appearance to decorate the painted object.
최근에, 많이 사용되고 있는 도료는 광택, 물성 및 작업 조건 면에서 우수한 아크릴 폴리올과 이소시아네이트(isocyanate)기를 포함하고 있는 2액형 아크릴 우레탄 도료이다.In recent years, paints widely used are two-component acrylic urethane paints containing acrylic polyols and isocyanate groups which are excellent in terms of gloss, physical properties and working conditions.
종래의 열경화성 아크릴우레탄계 금속조(펄) 도료는 표면 평활감(平滑感) 및 표면 광택 등 외관품질 향상과 금속조 도료에 함유된 금속안료의 산화에 의한 변색 등 색상 보호를 위하여 상도로서 열경화성 아크릴 우레탄계 또는 아크릴 락카계 투명도료를 도장하는 2회 도장 방식을 채택하고 있었다.Conventional thermosetting acrylic urethane-based metal paints (pearls) are thermosetting acrylic urethanes as top coats for improved surface quality such as surface smoothness and surface gloss and color protection such as discoloration by oxidation of metal pigments contained in metal paints. Or the two-time coating method which coats acrylic lacquer transparent paint was adopted.
가전기기용 플라스틱 소재로는 주로 아크릴로니트릴 부타디엔스티렌, 나일론, 폴리프로필렌, 벌크 몰딩 컴파운드, 하이임팩트스티렌, 폴리카보네이트, 폴리에틸렌테레프탈레이트, 폴리부타디엔테레프탈레이트 등의 합성수지 사출 또는 압출제품이 사용되고 있고, 그 외에도 재생가능한 플라스틱의 재활용품을 이용한 소재 등 다양한 플라스틱 소재가 사용되고 있다.As plastic materials for home appliances, synthetic resin injection or extrusion products such as acrylonitrile butadiene styrene, nylon, polypropylene, bulk molding compound, high impact styrene, polycarbonate, polyethylene terephthalate and polybutadiene terephthalate are used. In addition, various plastic materials such as materials using recycled plastics are being used.
이와 같은 각종 플라스틱 소재를 이용한 가전기기 부품 등의 제품에 밀착성 또는 부착성을 증진시키기 위해서는 각각의 플라스틱 소재별로 적합한 프라이머 도료가 적용되기도 하였다.In order to enhance adhesion or adhesion to products such as home appliance parts using various plastic materials, primer paints suitable for each plastic material have been applied.
종래의 도장시스템은, 여러 가지 방법이 있으나, 물성 및 경제적인 이유 때문에, 일반적으로 다층 도장 형식을 갖는 2코트 1베이킹(2 Coat 1 Baking) 또는 3코트 1베이킹 타입이 적용된다. 즉, 하도로서 프라이머 도료, 중도로서 금속조(펄) 색상 도료, 상도로서 투명 도료 등 3회 도장하거나, 플라스틱 소재와의 밀착성을 개선한 방법으로 하도 겸 중도로서 금속조(펄) 색상도료와 상도로서 투명도료의 2회 도장한다.Conventional coating systems have many methods, but for reasons of physical properties and economics, two coat one baking or three coat one baking types having a multilayer coating form are generally applied. In other words, the paint is applied three times, such as a primer paint as a coat, a metal paint (pearl) paint as a midway, and a transparent paint as a coat, or a metal paint (pearl) paint and a coat as a coat as a method of improving the adhesiveness with a plastic material. It is applied twice as a transparent paint.
이러한 종래의 도료를 이용한 2회 또는 3회의 도장시스템은 여러 단계를 거쳐야 하기 때문에 시간이 많이 소요될 뿐만 아니라, 도막 한 층 마다 광택을 높이기 위해서 얇게 2번 이상 뿌려야 하기 때문에 도료의 낭비가 심하였고, 2층 이상의 도막을 올림으로써 공정비/재료비가 추가되었다. 또한, 고가격의 도장 설비와 많은 도장 인력이 필요함에 따라, 운영비도 과다하게 소요되었다.2 or 3 times the coating system using the conventional paint is not only time-consuming because it has to go through several steps, but also wastes paint because it has to be sprayed thinly two or more times in order to increase the gloss per layer. The process cost / material cost was added by raising more than one layer of coating. In addition, due to the high cost of painting equipment and a large number of painting personnel, operating costs were excessively required.
특히, 최근에는 도료 내에 함유된 유기 용제의 배출에 의한 환경오염 문제가 크게 대두되고 있기 때문에, 종래의 유기 용제를 함유하는 도료 조성물 대신에 수성 코팅 조성물의 개발이 또한 요구되고 있다.In particular, in recent years, the problem of environmental pollution due to the discharge of the organic solvent contained in the paint has emerged largely, the development of an aqueous coating composition instead of the coating composition containing the conventional organic solvent is also required.
본 발명은 이와 같은 종래 문제점들을 해결하기 위하여 안출된 것으로, 우수한 외관품질과 내수성, 내산성, 내스크래치성 및 부착성 등이 우수한 합성 수지와, 이러한 합성 수지를 포함하는 도료 조성물을 제공함으로써, 하도로서 프라이머 도료와 상도로서 2액형 아크릴우레탄 투명도료 또는 아크릴락카계 등 어떠한 종류의 1액형 투명도료를 도장하지 않고 1회 도장을 가능하게 하여 그에 따라 도료의 원가 및 도장 비용이 절감되고 도장 시간이 절약됨과 동시에 고광택의 도막 표면을 얻을 수 있도록 하는 것을 그 목적으로 한다.SUMMARY OF THE INVENTION The present invention has been made to solve such conventional problems, and by providing a synthetic resin having excellent appearance quality, excellent water resistance, acid resistance, scratch resistance and adhesion, and a coating composition comprising such a synthetic resin, As a primer paint and a top coat, it is possible to apply a one-time coating without applying any one-component transparent paint such as two-component acrylic urethane transparent paint or acrylic lacquer type, thereby reducing the cost and coating cost of the paint and saving the coating time. At the same time, the purpose is to obtain a high gloss coating surface.
본 발명의 다른 목적은 베이스 도료 조성물에 아크릴 수지와 폴리에스테르 수지를 함께 첨가한 도료를 제공함으로써 기존의 아크릴우레탄 수지에 비해서 광택의 선영성을 증대시키고 경화제로 사용되는 이소시아네이트와의 가교 밀도를 높이도록 하는 것이다.Another object of the present invention is to provide a coating material by adding an acrylic resin and a polyester resin together to the base coating composition to increase the glossiness of the gloss and to increase the crosslinking density with isocyanate used as a curing agent compared to the conventional acrylic urethane resin. It is.
본 발명의 또 다른 목적은 도료에 첨가되는 안료에 마이크로셀을 적용시킴으로써 도막이 건조된 후에도 안료가 노출되지 않도록 하는 것이다.Another object of the present invention is to apply a microcell to a pigment added to the paint so that the pigment is not exposed even after the coating film is dried.
도 1은 본 발명의 도료에 마이크로셀(Microcell)이 적용된 알루미늄 안료를 사용한 경우의 도장 표면을 나타내는 SEM 사진이다.BRIEF DESCRIPTION OF THE DRAWINGS It is the SEM photograph which shows the coating surface at the time of using the aluminum pigment to which the microcell was applied to the coating material of this invention.
도 2는 종래의 도료에 마이크로셀이 적용되지 않은 알루미늄 안료를 사용한 경우의 도장 표면을 나타내는 SEM 사진이다.FIG. 2 is a SEM photograph showing a coating surface when an aluminum pigment to which a microcell is not applied is applied to a conventional paint.
상기 목적을 달성하기 위하여, 본 발명은 비닐형 이중결합을 갖는 단량체를 포함하고, (a) 산가 5 내지 30 mg KOH/g, (b) 수산기 함량 3.0 내지 6.0%, (c) 유리전이온도 -22 내지 100℃, (d) 25℃에서 가드너 점도 X 내지 Z2, (e) 수평균분자량 1,000 내지 25,000, (f) 중량평균분자량 6,000 내지 50,000, (g) 분자량 분포도 3의 조건을 만족하는 고형분 또는 불휘발분 55% 이상의 아크릴 합성 수지를 제공한다.In order to achieve the above object, the present invention comprises a monomer having a vinyl double bond, (a) acid value of 5 to 30 mg KOH / g, (b) hydroxyl group content of 3.0 to 6.0%, (c) glass transition temperature- (D) Gardner viscosity X to Z2 at 25 to 100 ° C, (e) number average molecular weight 1,000 to 25,000, (f) weight average molecular weight 6,000 to 50,000, (g) solid content satisfying the conditions of molecular weight distribution degree 3 or An acrylic synthetic resin having a nonvolatile content of at least 55% is provided.
본 발명의 합성 수지인 열경화성 아크릴 수지의 특성치로서 수산기 함량이 3.0 중량% 이하이면 가교제와 충분한 경화성을 발휘할 수 없어 건조속도가 느리고, 경화밀도가 낮아 내스크래치성, 내수성 및 내산성 등의 고기능성 경화도막을 얻을 수 없으며, 6.0% 이상이면 경화밀도가 너무 높아 도막이 부스러지기 쉬우며, 가교제의 사용량이 많아지게 되므로 도료의 가격 앙등 요인이 될 수 있다.When the hydroxyl group content is 3.0 wt% or less as a characteristic value of the thermosetting acrylic resin of the present invention, it is difficult to exhibit sufficient curing property with a crosslinking agent, and thus the drying speed is low and the curing density is low, and thus a high functional cured coating film such as scratch resistance, water resistance and acid resistance is obtained. If it is 6.0% or more, the curing density is too high, the coating film is easily brittle, and the amount of the crosslinking agent is increased, which may cause a price increase of the paint.
그리고, 산가가 5 mg KOH/g 이하이면 안료 분산성이 저하되어 고광택의 도막을 얻을 수 없으며, 30 mg KOH/g 이상이면 합성 수지 중의 극성이 너무 높아지고 분자량 증가에 의한 점도가 높아져서 고형분을 높일 수가 없으므로 도료의 작업성이 나빠지고, 표면 평활감이 저하되어 고광택의 도막을 기대할 수 없게 된다.If the acid value is 5 mg KOH / g or less, the pigment dispersibility is lowered and a high gloss coating film cannot be obtained. If the acid value is 30 mg KOH / g or more, the polarity in the synthetic resin becomes too high and the viscosity due to the increase in molecular weight increases, thereby increasing the solid content. As a result, the workability of the paint is deteriorated, the surface smoothness is lowered, and a high gloss coating cannot be expected.
고형분 또는 불휘발분이라 함은 상기 아크릴 합성 수지를 도장했을 때 아크릴 수지 안에 포함되어 있던 휘발성 물질이 휘발되고 남은 부분을 말하는 것이다.Solid content or non-volatile content means the part remaining after volatilization of the volatile material contained in the acrylic resin when the acrylic synthetic resin is coated.
한편, 유리전이온도가 -22℃ 이하에서는 경화도막의 충분한 경도를 기대할 수 없으며, 도료 도장시 수직부위에서 도료가 흐름에 따라 균일한 도막 두께를 형성하기 어렵게 되어 고광택의 도막을 기대할 수 없게 된다. 또 100℃ 이상에서는 합성수지 점도가 높아져 고형분을 높일 수 없기 때문에 도장 작업성이 나빠져 고광택의 도막을 얻을 수 없게 된다.On the other hand, when the glass transition temperature is -22 ° C or less, sufficient hardness of the cured coating film cannot be expected, and it becomes difficult to form a uniform coating thickness as the paint flows in the vertical portion during the coating of the paint, and thus a high gloss coating film cannot be expected. Moreover, since the viscosity of synthetic resin becomes high and solid content cannot be raised above 100 degreeC, coating workability worsens and a high gloss coating film is no longer obtained.
그리고 수평균분자량이 1,000 이하이면 경화도막의 물성 저하를 가져오며, 25,000이상에서는 고형분을 55% 이상으로 하는 합성 수지를 얻기가 어렵게 된다.When the number average molecular weight is 1,000 or less, the physical properties of the cured coating film are lowered, and at 25,000 or more, it is difficult to obtain a synthetic resin having a solid content of 55% or more.
본 발명에 따르는 아크릴 수지에 포함되는 비닐형 이중결합을 갖는 단량체의 예로는 유기산기 함유 단량체, 수산기 함유 단량체, 방향족계 비관능성 단량체 및 지방족계 비관능성 단량체를 들 수 있으며, 이러한 단량체들은 하나 또는 둘 이상 선택되어 사용될 수 있다.Examples of the monomer having a vinyl double bond included in the acrylic resin according to the present invention include an organic acid group-containing monomer, a hydroxyl group-containing monomer, an aromatic non-functional monomer and an aliphatic non-functional monomer, and these monomers are one or two. The above selection can be used.
상기 유기산기 함유 단량체는 예를 들어, 아크릴산, 메타크릴산, 푸마르산(fumaric acid), 이타콘산(itaconic acid), 말레인산(maleinic acid) 및 그 무수물 등을 들 수 있으며, 이들 중 1종 또는 2종 이상 사용할 수도 있다. 이러한 유기산기 함유 단량체는 1 내지 6 중량% 범위로 포함되는 것이 바람직하다.Examples of the organic acid group-containing monomer may include acrylic acid, methacrylic acid, fumaric acid, itaconic acid, maleinic acid, and anhydrides thereof, and one or two of them. You can also use the above. Such organic acid group-containing monomer is preferably included in the range of 1 to 6% by weight.
상기 수산기 함유 단량체는 예를 들어, 2-하이드록시에틸아크릴레이트, 2-하이드록시에틸메타크릴레이트, 하이드록시프로필아크릴레이트, 하이드록시프로필메타크릴레이트, 4-하이드록시부틸아크릴레이트 등을 들 수 있으며, 이들 중 1종 또는 2종을 동시에 사용할 수도 있다. 이 중에서 2-하이드록시에틸메타크릴레이트는더욱 바람직한 수산기 함유 단량체이다. 이러한 수산기 함유 단량체는 10 내지 60 중량% 범위로 포함되는 것이 바람직하다.Examples of the hydroxyl group-containing monomers include 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, hydroxypropyl acrylate, hydroxypropyl methacrylate, 4-hydroxybutyl acrylate, and the like. In addition, one or two of these may be used simultaneously. Among these, 2-hydroxyethyl methacrylate is a more preferable hydroxyl group containing monomer. Such hydroxyl group-containing monomer is preferably included in the range of 10 to 60% by weight.
상기 방향족계 비관능성 단량체는 예를 들어, 스티렌(styrene), 비닐톨루엔 또는 알파메틸스티렌다이머 등을 들 수 있다. 이러한 방향족계 단량체는 15 내지 60 중량% 범위로 포함되는 것이 바람직하다. 이 중에서 더욱 바람직한 방향족계 비관능성 단량체는 알파메틸스티렌다이머이며, 이를 필수성분으로 적어도 3%이상 사용한 열경화성 아크릴 합성수지가 고(高)고형분 합성수지로 합성 가능했으며, 뛰어난 고광택의 외관품질과 양호한 기능을 발휘할 수 있었다.Examples of the aromatic nonfunctional monomers include styrene, vinyltoluene or alphamethylstyrene dimer. Such aromatic monomers are preferably included in the range of 15 to 60% by weight. Among these, the more preferred aromatic non-functional monomer is alpha methyl styrene dimer, and the thermosetting acrylic synthetic resin using at least 3% as an essential component can be synthesized as a high solid synthetic resin, and exhibits excellent gloss appearance quality and good function. Could.
상기 지방족계 비관능성 단량체는 예를 들어, 메틸메타크릴레이트, 에틸아크릴레이트, 에틸메타크릴레이트, 프로필메타크릴레이트, 노르말부틸아크릴레이트, 노르말부틸메타크릴레이트, 이소부틸메타크릴레이트, 노르말헥실메타크릴레이트, 사이클로헥실아크릴레이트, 라우릴메타크릴레이트, 이소보닐아크릴레이트, 이소보닐메타크릴레이트, 아크릴로니트릴, 비닐아세테이트, 셀룰로오스 유도체 등을 들 수 있으며, 이외의 비닐형 이중결합을 갖는 단량체를 사용할 수 있다. 이러한 지방족계 비관능성 단량체는 15 내지 50 중량% 범위로 포함되는 것이 바람직하다.Examples of the aliphatic nonfunctional monomers include methyl methacrylate, ethyl acrylate, ethyl methacrylate, propyl methacrylate, normal butyl acrylate, normal butyl methacrylate, isobutyl methacrylate, and normal hexyl methacrylate. Acrylate, cyclohexyl acrylate, lauryl methacrylate, isobornyl acrylate, isobornyl methacrylate, acrylonitrile, vinyl acetate, cellulose derivative, and the like, and other monomers having a vinyl double bond Can be used. Such aliphatic non-functional monomers are preferably included in the range of 15 to 50% by weight.
본 발명에 따른 아크릴 합성 수지는 알파, 베타 이중결합을 갖는 단량체들의 열분해 개시제에 의한 라디칼 중합의 통상적인 용액중합법에 따라 합성할 수 있다. 따라서, 상기 열경화성 아크릴 수지를 합성하기 위해서 라디칼중합개시제가 첨가될 수 있다. 상기 라디칼 중합 개시제의 예로는 벤조일퍼옥사이드, 아조이소부틸로니트릴, 터셔리부틸퍼옥시2-에틸헥사노에이트 등을 들 수 있으며, 본 발명에 따른 아크릴 합성 수지는 이와 같은 일반적인 라디칼중합개시제를 사용하고, 크실렌, 부틸아세테이트, 톨루엔 등의 용제를 사용하여 합성온도 100 내지 130℃에서 합성하였다.The acrylic synthetic resin according to the present invention can be synthesized according to a conventional solution polymerization method of radical polymerization by thermal decomposition initiators of monomers having alpha and beta double bonds. Therefore, a radical polymerization initiator may be added to synthesize the thermosetting acrylic resin. Examples of the radical polymerization initiator include benzoyl peroxide, azoisobutylonitrile, tertiary butyl peroxy 2-ethylhexanoate, and the like, and the acrylic synthetic resin according to the present invention uses such a general radical polymerization initiator. It synthesize | combined at the synthesis | combination temperature of 100-130 degreeC using solvents, such as xylene, butyl acetate, and toluene.
한편, 본 발명은 본 발명에 따른 아크릴 합성 수지를 포함하는 도료 조성물을 제공한다.On the other hand, this invention provides the coating composition containing the acrylic synthetic resin which concerns on this invention.
또한, 본 발명은 (a) 본 발명에 따르는 아크릴 합성 수지를 포함하는 주제 도료 조성물과, (b) 상기 합성 수지를 가교 경화시키기에 충분한 양의 폴리이소시아네이트계 경화제를 포함하고, 경화 도막의 60°경면 광택이 90 이상인 2액형 고광택 도료 조성물을 제공한다. 바람직하게는 경화 도막의 60°경면 광택이 95 이상이다.In addition, the present invention comprises (a) a main coating composition comprising an acrylic synthetic resin according to the present invention, and (b) a polyisocyanate-based curing agent in an amount sufficient to crosslink and cure the synthetic resin, wherein 60 ° of the cured coating film is used. Provided is a two-component high gloss coating composition having a mirror gloss of 90 or more. Preferably, the 60 ° mirror gloss of the cured coating film is 95 or more.
이러한 도료 조성물은 하도로서 프라이머 도료와 상도로서 투명 도료를 도장하지 않고 1회 도장가능하고, 1회 도장시에도 기존의 다수 도장시의 물성을 그대로 유지하면서 경화 도막의 60°경면 광택이 90 이상이다. 이러한 점은 본 발명의 중요한 특징이다.Such a coating composition can be coated once without coating a primer paint as a top coat and a transparent paint as a top coat, and has a 60 ° mirror gloss of the cured coating film of 90 or more while maintaining the properties of the existing multiple coatings even at the time of one coating. . This is an important feature of the present invention.
상기 도료 조성물에 첨가되는 폴리이소시아네이트계 경화제의 양은 예를 들어 상기 아크릴 수지가 40 내지 60 중량%일 때, 상기 경화제는 10 내지 27 중량%가 포함되는 것이 바람직하다.The amount of the polyisocyanate-based curing agent added to the coating composition is, for example, when the acrylic resin is 40 to 60% by weight, it is preferable that the curing agent contains 10 to 27% by weight.
상기 도료 조성물은 또한 필요에 따라 다양한 첨가제를 포함할 수 있다. 상기 주제 도료 조성물에는 금속감과 색감을 주기 위해서 금속 안료 또는 착색 안료 등이 첨가될 수 있으며, 이 때 안료는 마이크로셀이 적용된 안료로서, 바람직하게는 마이크로셀이 적용된 알루미늄계 안료이다. 안료는 1 내지 6% 정도 첨가되는 것이 바람직하며, 6%가 초과하면 표면에 올라오는 안료의 밀도가 높아져서 광택이 저하될 수 있다.The paint composition may also include various additives as needed. To the subject coating composition, a metal pigment or a coloring pigment may be added to give a metallic feeling and color. At this time, the pigment is a pigment to which a microcell is applied, and preferably, an aluminum pigment to which a microcell is applied. It is preferable that the pigment is added in an amount of about 1 to 6%, and when it exceeds 6%, the density of the pigment on the surface may increase, thereby decreasing the gloss.
또한, 본 발명은 (a) (ⅰ) 본 발명에 따르는 아크릴 합성 수지와, (ⅱ) 폴리에스테르 수지를 포함하는 주제 도료 조성물과, (b) 상기 합성 수지 및 상기 폴리에스테르 수지를 가교 경화시키기에 충분한 양의 폴리이소시아네이트계 경화제를 포함하고, 경화 도막의 60°경면 광택이 90 이상인 2액형 고광택 도료 조성물을 제공한다.In addition, the present invention provides a crosslinking curing of the main coating composition comprising (a) an acrylic synthetic resin according to the present invention, (ii) a polyester resin, and (b) the synthetic resin and the polyester resin. Provided is a two-component high gloss coating composition comprising a sufficient amount of a polyisocyanate-based curing agent and having a 60 ° mirror gloss of the cured coating film of 90 or more.
폴리에스테르 수지는 기존의 아크릴 우레탄 수지에 비해 선영성 및 광택을 증가시키고 이소시아네이트와의 가교 밀도를 높이기 위해 첨가되며, 아크릴 수지가 약 40 내지 55 중량%, 폴리에스테르 수지가 약 5 내지 18 중량% 첨가되는 것이 바람직하다. 5% 이하에서는 효과가 저하되며, 18% 이상에서는 핀 홀(pin hole)등의 도막 불량을 일으킨다.Polyester resins are added to increase the lightness and gloss and to increase the crosslinking density with isocyanates compared to conventional acrylic urethane resins, and acrylic resins are added in an amount of about 40 to 55% by weight and polyester resins are added in an amount of about 5 to 18% by weight. It is preferable to be. At 5% or less, the effect is lowered, and at 18% or more, coating film defects such as pin holes are caused.
당업자라면 이러한 아크릴 수지 및 폴리에스테르 수지를 모두 포함하고 있는 2액형 고광택 도료 조성물도 아크릴 수지만을 포함하고 있는 상기 도료 조성물과 마찬가지로 1회 도장가능하며, 필요에 따라 마이크로셀이 적용된 안료 등의 첨가제가 첨가될 수 있다는 것을 알 수 있을 것이다.Those skilled in the art can apply the two-component high gloss coating composition containing both the acrylic resin and the polyester resin as well as the coating composition containing only the acrylic resin once, and if necessary, additives such as pigments to which microcells are applied It will be appreciated that it may be added.
한편, 본 명세서에서 사용되는 "마이크로셀(Microcell)이 적용된 안료"란 표현은 안료를 도료에 투입하기 전에 알루미늄 안료 내에 있는 알루미늄 박편(aluminum flake)을 1차적으로 수지로 피복한 안료를 의미한다. 일반적으로 1회 도장을 적용하면 안료가 도막 표면에 노출되어 심각하게 광택이 나빠지고 물성이 저하되었다. 본 발명은 이러한 문제점을 해결하기 위해 상기 마이크로셀을 안료에 적용함으로써 건조후에 안료가 노출되는 것을 방지하여 도막의 광택과 물성이 그대로 유지되도록 하였다.On the other hand, as used herein, the expression "pigment to which the microcell is applied" refers to a pigment in which an aluminum flake in an aluminum pigment is first coated with a resin before the pigment is added to the paint. In general, once coating is applied, the pigment is exposed to the surface of the coating film, so that the gloss is seriously degraded and the physical properties are degraded. In order to solve this problem, the microcell is applied to the pigment to prevent the pigment from being exposed after drying to maintain the gloss and physical properties of the coating film.
도 1은 본 발명에 따라 마이크로셀이 적용된 알루미늄 안료를 이용한 도료를 1회 도장하였을 때의 도장 표면을 나타내는 SEM 사진(표면 500배 확대)이다. 도 1로부터, 알루미늄 안료 입자가 수지 속에 묻혀 있는 깨끗한 도막 표면을 볼 수 있다(광택도 96%). 반면에, 도 2는 마이크로셀을 적용시키지 않은 알루미늄 안료를 이용한 기존의 도료를 1회 도장하였을 때의 도장 표면을 나타내는 SEM 사진(표면 500배 확대)이다. 도 2로부터, 도장 표면에 많은 알루미늄 입자가 돌출되어 있어서 거친 표면을 볼 수 있다(광택도 67%).1 is a SEM photograph (500 times magnification of surface) showing the coating surface when coating the coating material using the aluminum pigment to which the microcell is applied according to the present invention once. From Fig. 1, the surface of the clean coating film in which the aluminum pigment particles are embedded in the resin can be seen (96% glossiness). On the other hand, Fig. 2 is a SEM photograph (500 times magnification of surface) showing the coating surface when a conventional coating using an aluminum pigment without microcells is applied once. From Fig. 2, a large amount of aluminum particles protrude from the painted surface, so that a rough surface can be seen (67% glossiness).
상기한 바와 같이, 알루미늄계 금속안료를 적당량의 용제에 분산시킨 후 여기에 본 발명에 따른 열경화성 아크릴 합성 수지 및 안료 침강방지제, 라벨링제 등의 첨가제를 투입한 후 균일하게 혼합하여 1회 도장으로 적용 가능한 플라스틱용 고광택 주제 도료용 조성물을 제조한다.As described above, after dispersing the aluminum-based metal pigment in an appropriate amount of solvent, and added to the additives such as thermosetting acrylic synthetic resin and pigment anti-settling agent, labeling agent according to the present invention, it is uniformly mixed and applied in a single coating A composition for high gloss topical paints for plastics is prepared.
상기 주제 도료 조성물에 경화제로서 2 내지 3 관능성 이소시아네이트를 첨가하여 균일하게 혼합한 도료를 플라스틱 소재에 도막두께가 15 내지 40㎛가 되도록 스프레이 도장하여 60 내지 80℃에서 20 내지 40분간 건조시킨다.The coating material uniformly mixed by adding 2 to 3 functional isocyanates as a curing agent to the main coating composition is spray-coated to a plastic material so as to have a film thickness of 15 to 40 µm and dried at 60 to 80 ° C. for 20 to 40 minutes.
본 발명의 도료 조성물의 경화 메카니즘은 다음과 같다:The curing mechanism of the coating composition of the present invention is as follows:
R-OH (아크릴 폴리올 및/또는 에스테르 폴리올) + O=N-C-R' (경화제)R-OH (acrylic polyol and / or ester polyol) + O = N-C-R '(curing agent)
--→ R-(-NH-CO-)n-R'-→ R-(-NH-CO-) n-R '
이처럼, 본 발명자들은 종래의 도료와 도장시스템을 단순화하여 1회 도장만으로도 2 내지 3회 도장한 것과 동등하거나 또는 그 이상의 부착성, 표면 평활감, 표면 고광택, 내수성, 내산성 및 내스크래치성 등의 성능을 발휘할 수 있는 합성수지의 설계와 합성 및 도료제조 방법에 관하여 연구한 결과 표면광택이 약 90(60°경면광택측정기) 이상인 고광택의 우수한 외관품질과 내수성, 내산성 및 내스크래치성이 우수한 도막성능을 갖는 고성능 아크릴우레탄계 금속조(펄) 도료를 발명하게 되었다.As such, the present inventors have simplified the conventional paint and coating system to achieve the same or more adhesion, surface smoothness, surface high gloss, water resistance, acid resistance, scratch resistance, etc. As a result of research on the design of synthetic resin and the method of manufacturing and coating of synthetic resin, it is possible to have high gloss with surface gloss of about 90 (60 ° mirror gloss meter) and excellent appearance quality, water resistance, acid resistance and scratch resistance. Invented a high performance acrylic urethane-based metal-based (pearl) paint.
도막의 외관품질 중 중요한 요소인 광택도는 도막표면의 미세한 굴곡이나 요철의 정도에 따라 지배를 받는데, 이는 도료에 사용하는 합성수지의 성질과 유기안료, 무기안료 및 금속(펄) 안료 등의 첨가에 따른 표면요철의 정도에 따라 결정되며, 측정은 60°경면광택측정기를 사용하여 측정한다.Glossiness, which is an important factor in the appearance quality of coatings, is governed by the degree of fine bending and unevenness of the surface of coatings, which is influenced by the properties of synthetic resins used in coatings and the addition of organic pigments, inorganic pigments and metal (pearl) pigments. Depending on the degree of surface irregularities according to the measurement, the measurement is measured using a 60 ° mirror gloss meter.
본 발명의 도료에 사용한 합성수지 조성물은 우수한 외관품질과 내수성, 내산성, 내스크래치성 및 각종 플라스틱 소재와의 부착성 등의 기능성을 중요시하여 설계한 열경화성 아크릴계 합성수지로 비단 플라스틱 소재용 도료 이외의 일반 공업용 도료 분야에도 적용할 수 있는 합성수지 조성물이다.Synthetic resin composition used in the paint of the present invention is a thermosetting acrylic synthetic resin designed with an emphasis on excellent appearance quality, water resistance, acid resistance, scratch resistance and adhesion to various plastic materials, and general industrial paints other than the coating material for silk materials. It is a synthetic resin composition that can be applied to the field.
이하, 본 발명은 실시예 및 비교예를 참고로 상세히 설명될 것이나, 본 발명의 범위를 제한하려는 것은 아니다.Hereinafter, the present invention will be described in detail with reference to Examples and Comparative Examples, but is not intended to limit the scope of the present invention.
A. 아크릴 수지 공중합체 용액 합성A. Synthesis of Acrylic Resin Copolymer Solution
실시예 1Example 1
교반기와 질소가스 도입관, 온도계, 적하 깔때기가 장착된 4구 플라스크에 크실렌 25.2부를 넣고 교반하면서 110 내지 120℃까지 가열하여 크실렌 용제를 환류시킨다. 그런 다음, 반응 온도를 110 내지 120℃로 유지시키면서 여기에 방향족계 단량체로 스티렌 21.1부, 알파메틸스티렌다이머 2.0부, 지방족계 단량체로 메틸메타크릴레이트 19.9부, 노르말부틸아크릴레이트 7.5부, 수산기 함유 단량체로 2-하이드록시에틸메타크릴레이트 9.3부, 유기산기 함유 단량체로 메타크릴산 0.87부 및 라디칼중합개시제로 터셔리부틸퍼옥시2-에틸헥사노에이트 5.46부의 혼합물을 3시간에 걸쳐 균일한 속도로 적하시킨다. 적하가 완료된 다음 2시간 동안 유지반응시킨후 크실렌 용제를 8.65부를 넣어 희석시킨다.Into a four-necked flask equipped with a stirrer, a nitrogen gas introduction tube, a thermometer, and a dropping funnel, 25.2 parts of xylene was heated to 110 to 120 ° C. while stirring to reflux the xylene solvent. Then, while maintaining the reaction temperature at 110 to 120 ℃ containing 21.1 parts of styrene as an aromatic monomer, 2.0 parts of alphamethylstyrene dimer, 19.9 parts of methyl methacrylate as aliphatic monomer, 7.5 parts of normal butyl acrylate, hydroxyl group A mixture of 9.3 parts of 2-hydroxyethyl methacrylate as a monomer, 0.87 parts of methacrylic acid as an organic acid group-containing monomer and 5.46 parts of tertiary butyl peroxy 2-ethylhexanoate as a radical polymerization initiator were uniformly mixed over 3 hours. Dropwise. After dropping was completed, the reaction was carried out for 2 hours, followed by dilution of 8.65 parts of xylene solvent.
이렇게 하여 25℃ 가드너 점도 Z1, 고형분 65%, 유리전이 온도 65℃, 수산기 함량 4.0%, 산가 6mg KOH/g, 수평균분자량 5,600, 중량평균분자량 12,000, 분자량분포 2.14의 특성치를 갖는 아크릴수지 공중합체 용액을 얻었다.Thus, acrylic resin copolymer having a Gardner viscosity Z1 of 25 ° C, a solid content of 65%, a glass transition temperature of 65 ° C, a hydroxyl content of 4.0%, an acid value of 6 mg KOH / g, a number average molecular weight of 5,600, a weight average molecular weight of 12,000, and a molecular weight distribution of 2.14. A solution was obtained.
실시예 2Example 2
실시예 1과 동일한 방법으로 부틸아세테이트 17.5부, 크실렌 12.6부의 혼합용제 환류하에, 2-하이드록시에틸메타크릴레이트 12.5부, 메틸메타크릴레이트 20부, 스티렌 21.5부, 노르말 부틸아크릴레이트 7.0부, 터셔리부틸퍼옥시2-에틸헥사노에이트 4.4부의 혼합물을 적하하여 반응시킨다.17.5 parts of butyl acetate and 12.6 parts of xylene in the same manner as in Example 1, 12.5 parts of 2-hydroxyethyl methacrylate, 20 parts of methyl methacrylate, 21.5 parts of styrene, 7.0 parts of normal butyl acrylate, ter A mixture of 4.4 parts of sherlybutylperoxy 2-ethylhexanoate is added dropwise to react.
이렇게 하여 25℃ 가드너 점도 Y, 고형분 65%, 유리전이온도 79%, 수산기 함량 5.4%, 산가 5mg KOH/g, 수평균분자량 5,700, 중량평균분자량 9,000, 분자량분포 1.58의 특성치를 갖는 아크릴수지 공중합체 용액을 얻었다.Thus, acrylic resin copolymer having a Gardner viscosity of 25 ° C, a solid content of 65%, a glass transition temperature of 79%, a hydroxyl content of 5.4%, an acid value of 5 mg KOH / g, a number average molecular weight of 5,700, a weight average molecular weight of 9,000, and a molecular weight distribution of 1.58. A solution was obtained.
실시예 3Example 3
실시예 1과 동일한 방법으로 크실렌 25부 환류하에, 스티렌 25부, 노르말부틸아크릴레이트 25부, 라우릴메타크릴레이트 17부, 메타크릴산 3부, 2-하이드록시에틸아크릴레이트 15부, 2-하이드록시에틸, 메타크릴레이트 10부, 프락셀에프엠-1 10부, 아조이소부틸로니트릴 2부의 혼합물을 적하하여 반응시킨다.In the same manner as in Example 1, under 25 parts of xylene reflux, 25 parts of styrene, 25 parts of normal butyl acrylate, 17 parts of lauryl methacrylate, 3 parts of methacrylic acid, 15 parts of 2-hydroxyethyl acrylate, and 2- A mixture of hydroxyethyl, 10 parts of methacrylate, 10 parts of Fraxel FM-1 and 2 parts of azoisobutylonitrile was added dropwise to react.
이렇게 하여 25℃ 가드너 점도 Z2, 고형분 65%, 유리전이온도 8℃, 수산기 함량 4.2%, 산가 21mg KOH/g, 수평균분자량 5,700, 중량평균분자량 9,000, 분자량분포 1.58의 특성치를 갖는 아크릴수지 공중합체 용액을 얻었다.Thus, the acrylic resin copolymer having a Gardner viscosity of 25 ° C., a solid content of 65%, a glass transition temperature of 8 ° C., a hydroxyl content of 4.2%, an acid value of 21 mg KOH / g, a number average molecular weight of 5,700, a weight average molecular weight of 9,000, and a molecular weight distribution of 1.58. A solution was obtained.
비교예 1Comparative Example 1
실시예 1과 같은 방법으로, 크실렌 19부, 부틸아세테이트 15부의 혼합용제 환류하에 스티렌 15부, 메틸메타크릴레이트 3부, 노르말 부틸아크릴레이트 10부, 2-에틸헥실아크릴레이트 10부, 아크릴산 0.5부, 2-하이드록시에틸메타크릴레이트 12부, 벤조일퍼옥사이드 0.5부의 혼합물을 적하하여 반응시킨다.In the same manner as in Example 1, 15 parts of styrene, 15 parts of butyl acetate, 3 parts of methyl methacrylate, 10 parts of normal butyl acrylate, 10 parts of 2-ethylhexyl acrylate, and 0.5 parts of acrylic acid under reflux of a mixed solvent of 19 parts of xylene and 15 parts of butyl acetate And 12 parts of 2-hydroxyethyl methacrylate and 0.5 parts of benzoyl peroxide are added dropwise to react.
이렇게 하여 25℃ 가드너 점도 U, 고형분 50%, 유리전이온도 0℃, 수산기 함량 4.9%, 산가 6mg KOH/g, 수평균분자량 5,200, 중량평균분자량 8,000, 분자량분포 1.54의 특성치를 갖는 아크릴수지 공중합체 용액을 얻었다.Thus, the acrylic resin copolymer having a characteristic property of 25 ° C Gardner viscosity U, solid content 50%, glass transition temperature 0 ° C, hydroxyl content 4.9%, acid value 6mg KOH / g, number average molecular weight 5,200, weight average molecular weight 8,000, molecular weight distribution 1.54 A solution was obtained.
B. 상기 아크릴수지를 포함하는 도료의 성능 시험B. Performance Test of Paint Containing the Acrylic Resin
실시예 4Example 4
혼합 도료 제조Mixed paint manufacturers
실시예 1, 2, 3 및 비교예 1에서와 같이 합성한 아크릴수지 공중합체 용액들의 성능을 시험하기 위하여 톨루엔 3부, 코코졸-100 2부, 코코졸-150 3부의 혼합용제에 알루미늄 페이스트 1109MA(삼아알루미늄사 제품) 4.0부를 균일하게 분산시킨 후, 이것에 합성수지 57.5부, 셀룰로오스아세테이트부틸레이트(코닥사 제품) 20% 용액 7부, 에틸렌옥사이드 8.1부, 코코졸-100 5부, 크실렌 1.5부의 조성으로 투입하여 균일한 금속조(펄) 색상의 혼합 도료를 제조한다.In order to test the performance of the acrylic resin copolymer solutions synthesized as in Examples 1, 2, 3 and Comparative Example 1, aluminum paste 1109MA in a mixed solvent of 3 parts of toluene, 2 parts of cocosol-100, and 3 parts of cocosol-150 After dispersing 4.0 parts uniformly (products of Sanya Aluminum), 57.5 parts of synthetic resin, 7 parts of cellulose acetate butyrate (Kodak Corporation) 20% solution, 8.1 parts of ethylene oxide, 5 parts of cocosol-100, 1.5 parts of xylene It is added as a composition to prepare a mixed paint of a uniform metal color (pearl) color.
실시예 5Example 5
시험용 시편 제작Test Specimen Fabrication
시험용 시편 제작은 종래의 기술인 하도로서 프라이머, 상도로서 투명도료를 도장하지 않고 본 발명의 도료 1회 도장으로 제작하였다. 경화제 이소시아네이트 수지로는 데스모듈 엔-75(바이엘사 제품)를 사용하여 상기 제조한 금속조(펄) 색상도료와 데스모듈 엔-75를 4:1의 중량비율로 첨가하여 균일하게 혼합하였다. 그 후 이소부틸 알코올로 세척한 아크릴로니트릴부타디엔스틸렌 플라스틱 소재에 건조 후 도막 두께 35 내지 40 ㎛가 되도록 에어스프레이 도장한 다음 70℃에서 20분간 건조시켜 만든다.Test specimens were prepared by coating the coating of the present invention without applying a primer as a primer and a transparent coating as a coat. As a curing agent isocyanate resin, the metal-coated (pearl) color paint and Desmodul N-75 prepared above were added at a weight ratio of 4: 1 using Desmoden N-75 (manufactured by Bayer) and mixed uniformly. Thereafter, the resultant is dried on an acrylonitrile butadiene styrene plastic material washed with isobutyl alcohol, and then air sprayed to have a thickness of 35 to 40 μm, and then dried at 70 ° C. for 20 minutes.
C. 상기 아크릴수지를 포함한 도료의 성능 시험 결과C. Performance test result of the paint including the acrylic resin
본 발명의 수지합성 실시예 1, 2, 3과 비교예 1의 합성수지를 이용하여 만든 1회 도장용 플라스틱 도료의 도막 성능시험은 일반적인 도막 물성 시험방법으로 평가하였으며 그 결과는 다음 표 1과 같다.The coating performance test of the plastic coating material for one-time coating made of the synthetic resins of Examples 1, 2, 3 and Comparative Example 1 of the present invention was evaluated by a general coating property test method, and the results are shown in Table 1 below.
(◎ : 우수, △ : 보통, Ｘ : 불량)(◎: Excellent, △: Normal, Ｘ: Poor)
상기 표 1에 나타난 도막 물성에 대한 내용은 다음과 같다.Details of the coating film properties shown in Table 1 are as follows.
광택은 60° 경면광택기로 측정한 값이다.Gloss is a value measured with a 60 ° mirror polisher.
내약품성은 5% 염산수용액 및 5% 가성소다수용액에 24시간 침지 시험후 도막부풀음, 광택저하 등의 변화 여부를 관찰한 것이다.Chemical resistance was observed in the film swelling and gloss decrease after 24 hours immersion in 5% aqueous hydrochloric acid solution and 5% caustic soda solution.
부착성은 횡절단 테이프 시험법(cross cut tape test)에 따라 예리한 칼로 플라스틱 소재 표면까지 도달되도록 절단하여 1mm x 1mm 크기의 정사각형 100개를 만들고 그 위에 스카치테이프를 부착시킨 다음 떼어내어 플라스틱 소재로부터 도막이 떨어지는 정도를 측정한 것이다.Adhesiveness is cut according to the cross cut tape test with a sharp knife to reach the surface of the plastic material, making 100 1mm x 1mm squares, attaching scotch tape on it, and then peeling it off to remove the coating from the plastic material. It is a measure of accuracy.
내수성은 40℃ 항온수조에 도장시편을 240 시간 담갔다가 꺼내어 도막표면에 부풀음, 광택저하 등의 변화를 관찰한 것이다.Water resistance is to observe the change of swelling, gloss reduction, etc. on the surface of the coating film by soaking the coated specimen in a 40 ℃ constant temperature water bath for 240 hours.
내스크래치성은 도막경화후 표면을 손톱으로 긁어 상처 발생 정도를 관찰한 것이다.Scratch resistance was observed by scratching the surface with a fingernail after curing the film.
D. 아크릴 수지와 폴리에스테르 수지를 포함한 도료D. Paints containing acrylic resins and polyester resins
실시예 6Example 6
실시예 1, 2 또는 3에서와 같이 제조된 아크릴 폴리올 약 40 내지 55 중량%, 폴리에스테르 폴리올 약 5 내지 18 중량%, 상기 수지들을 용해시킬 수 있는 용제 약 21 내지 47 중량%, 마이크로셀이 적용된 안료 약 1 내지 6 중량%, 상기 아크릴폴리올과 폴리에스테르 폴리올을 가교 경화시키기에 충분한 양의 폴리이소시아네이트계 경화제, 그리고 도장 미세 물성을 조정하기 위해서 경화촉진제, 표면조정제등의 첨가제를 포함한 도료를 만들고, 건조 두께가 15 내지 30㎛정도 되도록 1회 도장한 후, 65 ±5℃로 약 30분 동안 건조시켰다.About 40 to 55% by weight of acrylic polyol prepared as in Examples 1, 2 or 3, about 5 to 18% by weight of polyester polyol, about 21 to 47% by weight of solvent capable of dissolving the resins, microcell applied About 1 to 6% by weight of a pigment, a polyisocyanate-based curing agent in an amount sufficient to cross-cure the acrylic polyol and the polyester polyol, and a paint including additives such as a curing accelerator and a surface conditioner to adjust the coating fine physical properties, The coating was once applied so that the dry thickness was about 15 to 30 μm, and then dried at 65 ± 5 ° C. for about 30 minutes.
비교예 2Comparative Example 2
기존의 아크릴 폴리올 40 내지 60%, 마이크로셀이 적용되지 않은 안료 0 내지 12%, 용제, 첨가제, 상기 아크릴 폴리올을 가교 경화시키기에 충분한 양의 이소시아네이트계 경화제를 포함한 도료를 만들고, 1회 도장시 두께가 15㎛ 정도로 2 내지 3회 도장한 후, 65 ±5℃로 약 30분 동안 건조시켰다.40 to 60% of conventional acrylic polyols, 0 to 12% of pigments without microcells applied, solvents, additives, and paints containing an amount of isocyanate-based curing agent sufficient to crosslink and cure the acrylic polyols. Was applied 2 to 3 times on the order of 15 µm and then dried at 65 ± 5 ° C for about 30 minutes.
그 후, 실시예 6과 비교예 2의 도막에 대해 광택도, 내후성, 경도 등에 대한 물성을 시험하였다. 그 결과를 하기 표 2에 나타내었다.Then, the physical properties with respect to glossiness, weather resistance, hardness, etc. were tested about the coating film of Example 6 and the comparative example 2. The results are shown in Table 2 below.
상기와 같이 도막의 물성 시험 결과를 통해 본 발명에 따른 도료를 1회 도장했을 때의 물성이 기존의 도료를 여러 번 도장했을 때의 물성과 비교하여 전혀 손색이 없다는 것을 알 수 있었다.As described above, it can be seen from the physical property test results of the coating film that the physical properties of the paint coating according to the present invention are not comparable with those of the conventional coating of paints many times.
그러나, 기존 2회 도장형 도료 수지를 1회 도장하였을 경우에는 광택이 20% 이상 저하되었으며, 기존의 도료에 광택을 높이기 위해 폴리에스테르 수지를 혼합할 경우에는 건조 온도가 상승되어 약 80℃로 30분 동안 행해야 하며, 이는 ABS 등 일부 플라스틱 수지의 변형을 초래하고, 핀 홀(pin hole) 발생을 일으키기 쉬우며, 도막 경도 등이 기존의 아크릴 우레탄에 비해 낮아지는 등의 문제가 있다.However, when one coat of the existing paint type paint resin was applied once, the gloss was reduced by 20% or more. When the polyester resin was mixed in order to increase the gloss of the existing paint, the drying temperature was increased to 30 to about 80 ° C. It has to be done for minutes, which causes deformation of some plastic resins such as ABS, is easy to cause pin holes, and the coating film hardness is lower than that of conventional acrylic urethane.
따라서, 본 발명에 따른 도료의 1회 도장(15 내지 40㎛)으로도 두꺼운 도막이 생성되므로, 기존 도료의 1회 도장(15㎛내외)으로 얻을 수 있는 도막에 비해서 고형분비의 증대로 인해 미려한 광택의 도막을 생성하여 생산량 증대 효과를 가져올 수 있도록 하였다.Therefore, since a thick coating film is produced even with a single coating (15 to 40 μm) of the paint according to the present invention, a beautiful gloss due to an increase in solid content compared to a coating obtained with a single coating (about 15 μm) of an existing paint. The film was produced to increase the yield.
이처럼, 본 발명에 따라 제조된 도료는 보통 광택을 내기 위한 상막을 베이스 부분에 포함시켜 플라스틱 등의 재료에 1회 도장가능하고, 2회 이상 도장처리 하던 종래의 도료의 도막과 동등한 내수성, 내산성 및 내스크래치성 등의 제반 물성을 가지며, 표면 평활감, 표면 광택 등이 뛰어나다. 이에 따라서, 도장 공정을 단순화시킴으로써 시간, 도장 비용 및 인건비를 절약할 수 있고, 여러 번의 도장으로 낭비되었던 도료의 사용량을 줄여 도료 원가를 대폭 절감할 수 있게 되었다.As described above, the paint prepared according to the present invention usually includes a top film for gloss in the base portion, and can be coated once on a material such as plastic, and has water resistance, acid resistance, and It has various physical properties such as scratch resistance and is excellent in surface smoothness and surface gloss. Accordingly, by simplifying the painting process, it is possible to save time, painting cost and labor costs, and it is possible to significantly reduce the paint cost by reducing the amount of paint wasted by several paintings.
Claims (12)