KR102273973B1 - Easily-peelability coating composition - Google Patents
Easily-peelability coating composition Download PDFInfo
- Publication number
- KR102273973B1 KR102273973B1 KR1020200093206A KR20200093206A KR102273973B1 KR 102273973 B1 KR102273973 B1 KR 102273973B1 KR 1020200093206 A KR1020200093206 A KR 1020200093206A KR 20200093206 A KR20200093206 A KR 20200093206A KR 102273973 B1 KR102273973 B1 KR 102273973B1
- Authority
- KR
- South Korea
- Prior art keywords
- composition
- weight
- easy
- parts
- paint
- Prior art date
Abstract
Description
본 발명은 박리 용이성 도료 조성물에 관한 것으로서, 보다 상세하게는 색상 및 디자인 기호에 변화를 주거나 원래의 제품으로 다시 사용하고 싶을 경우 손쉽게 도막층을 박리하여 원상 복구가 가능한 박리 용이성 도료 조성물에 관한 것이다.The present invention relates to an easy-to-peel coating composition, and more particularly, to an easy-to-peel coating composition that can be restored to its original state by easily peeling the coating layer when changing color and design preferences or wanting to use it again as an original product.
일반적으로 페인트는 유동성의 물질로 물체의 표면에 넓게 도포되어 얇은 피막 층을 형성하고 시간의 경과에 따라 건조, 경화됨으로써 물체의 표면을 보호할 뿐만 아니라 미감을 증대시키는 기능을 갖는다. 이러한 페인트는 특히 건축물 등과 같은 각종 구조물에 도포되어 구조물의 외관을 미려하게 할 뿐만 아니라 부식 등과 같은 손상을 방지하여 내구성을 향상시키는데 많이 이용된다.In general, paint is a fluid material that is widely applied to the surface of an object to form a thin film layer and dries and hardens over time to protect the surface of the object as well as increase the aesthetics. In particular, such paint is applied to various structures such as buildings to make the appearance of the structure beautiful, and is often used to improve durability by preventing damage such as corrosion.
건축물과 같은 구조물의 보호를 위해 주로 사용되고 있는 페인트로는 유성페인트, 에나멜페인트 및 수성페인트 등이 있다. 이러한 페인트들은 건축물과 소재(재료)의 보호뿐만 아니라 미관을 증대시키고 단열성 및 난열성 등을 향상시키는 효과를 갖는다.As paints mainly used for the protection of structures such as buildings, there are oil-based paints, enamel paints, and water-based paints. These paints have the effect of not only protecting buildings and materials (materials), but also increasing aesthetics and improving insulation and heat resistance.
일반적인 페인트 등의 도료는 내구성 향상을 위해 소재와의 부착력 향상을 주요 목적으로 개발되고 있는 실정으로 피작물에 도포 후 건조/경화 후 박리가 용이하지 않는 특성을 가진다. 특히 벽지와 같은 종이 소재에 도포할 경우 박리를 전혀 할 수 없거나 억지로 박리할 경우 종이가 뜯어지는 문제점이 발생한다. 상기와 같이 일반적인 페인트 등의 도료는 원상 복구가 전혀 불가능한 실정이다.Paints such as general paints are being developed for the main purpose of improving adhesion to materials to improve durability, and have a characteristic that it is not easy to peel off after drying/curing after application to a work piece. In particular, when applied to a paper material such as wallpaper, there is a problem that the peeling cannot be done at all or the paper is torn when peeled forcibly. As described above, it is impossible to restore the original state of paints such as general paints.
한편, 박리 가능한 형태의 페인트는 차량의 적용 용도로 일부 사용되고 있다. 차량 용도의 경우 유성타입으로 유기 용제를 함유하므로 악취가 심하고 인체에 유해하므로 실내용으로 사용하기에는 어려운 문제가 있다. 또한, 차량 용도 이외 원목 가구의 보호용으로 사용되고 있으나 페인팅 개념으로는 적용되고 있지 않은 실정이다. 상기의 페인트를 벽지와 같은 종이 소재에 코팅(도포)할 경우 추후 박리가 용이하지 않아 박리 시 종이가 뜯어지는 문제가 발생하므로 완전하게 박리가 되지 않고 소재를 원상 복구하기가 용이하지 않아 실질적인 도움을 주지 못하고 있다.On the other hand, a peelable type of paint is partially used for vehicle application. In the case of vehicle use, since it is an oil-based type and contains an organic solvent, it has a strong odor and is harmful to the human body, so it is difficult to use it for indoor use. In addition, although it is used for protection of wooden furniture other than for vehicle use, it is not applied as a painting concept. When the above paint is coated (applied) on a paper material such as wallpaper, it is not easy to peel off later, causing a problem of tearing the paper during peeling, so it is not completely peeled off and it is not easy to restore the material to its original state. can't give
특히, 합지 벽지(종이)와 같은 많은 기공(포러스)과 재료 간의 내부 응집력이 약해 층간 분리가 발생할 수 있는 소재의 경우, 페인트가 상기와 같은 요인으로 높은 부착력을 가져 도막층이 소재와의 박리가 어렵고 심지어 박리 시 벽지(종이)가 뜯어지는 경우가 발생하므로 박리 가능한 페인트는 실내 인테리어용으로 아직 적용되지 않고 있다. In particular, in the case of a material that can cause separation between layers due to the weak internal cohesion between the many pores (porous) and the material, such as laminated wallpaper (paper), the paint has high adhesion due to the above factors, so that the coating layer may not be peeled from the material. Peelable paint has not yet been applied for interior use because it is difficult and even the wallpaper (paper) may tear during peeling.
이에, 빠른 기호의 변화, 자신만의 아이템/공간에 요구 및 손쉬운 DIY 접근 등을 위하여 장소와 시간에 구애받지 않고 도포된 소재에서 박리가 가능하고, 박리 시 원 소재로 원상 복구가 가능한 페인트 또는 도료가 필요한 실정이다.Therefore, it is possible to peel off the applied material regardless of place and time for quick change of preference, request for one's own item/space, easy DIY access, etc., and a paint or paint that can be restored to its original state when peeled off is needed.
본 발명의 목적은 도료가 도포된 소재에서 박리가 용이하여 원상 복구 효과를 극대화함과 동시에 수성타입으로 설계하여 실내 인테리어, 인체와 접촉할 수 있는 용도로 개발하여 장소와 용도에 구애받지 아니하며 소재를 보호하고 내구성이 우수한 박리 용이성 도료 조성물을 제공하는데 있다.The object of the present invention is to maximize the effect of restoring the original state by easy peeling from the material to which the paint is applied, and at the same time to design the water-based type and develop it for use in indoor interiors and in contact with the human body, regardless of the location and use of the material. An object of the present invention is to provide an easy-to-peel coating composition having excellent protection and durability.
본 발명의 다른 목적 및 기술적 특징은 이하의 발명의 설명, 청구범위 및 도면에 의해 보다 구체적으로 제시된다.Other objects and technical features of the present invention are presented in more detail by the following description of the invention, claims and drawings.
상기 과제를 해결하기 위하여, 본 발명은 In order to solve the above problems, the present invention
폴리 비닐계 수지 30 내지 80 중량부; 증점제 0.2 내지 2 중량부; 안료 5 내지 30 중량부; 소포제를 포함하는 첨가제 1 내지 5 중량부; 및 용제 5 내지 30 중량부를 포함하는, 대상체로부터 박리가 용이한 도료 조성물로서, 상기 조성물은 이형성 첨가제 및 무기소재 중 어느 하나 이상을 포함하는 것을 특징으로 한다.30 to 80 parts by weight of a polyvinyl-based resin; 0.2 to 2 parts by weight of a thickener; 5 to 30 parts by weight of a pigment; 1 to 5 parts by weight of an additive containing an antifoaming agent; and 5 to 30 parts by weight of a solvent, wherein the composition is easily peelable from an object, wherein the composition includes at least one of a release agent and an inorganic material.
상기 폴리 비닐계 수지는 염화 비닐 수지, 비닐계 단량체로 변성된 염화 비닐 수지, 폴리 비닐 부티랄 또는 이들의 혼합물을 포함하는 것일 수 있으며, 바람직하게 상기 폴리 비닐계 수지는 폴리부티랄일 수 있다.The polyvinyl-based resin may include a vinyl chloride resin, a vinyl chloride resin modified with a vinyl-based monomer, polyvinyl butyral, or a mixture thereof, and preferably, the polyvinyl-based resin may be polybutyral.
상기 이형성 첨가제는 실리콘 오일, 실리콜 폴리머, 실리콘 에멀젼, 변성 실리콘 오일 또는 폴리머, 실록산 및 변성 실록산, 실리콘 고무, 왁스타입 첨가제, 계면 활성제, 오일 및 실란으로 이루어진 군에서 선택되는 어느 하나 이상을 포함하는 것일 수 있다.The release additive includes at least one selected from the group consisting of silicone oil, silicone polymer, silicone emulsion, modified silicone oil or polymer, siloxane and modified siloxane, silicone rubber, wax-type additive, surfactant, oil, and silane it could be
상기 무기소재는 SiO2, CaCO3, BaSO4, Talc, Al(OH)3, Al2O3 및 TiO2 로 이루어진 군에서 선택되는 어느 하나 이상을 포함하는 것일 수 있다.The inorganic material may include any one or more selected from the group consisting of SiO 2 , CaCO 3 , BaSO 4 , Talc, Al(OH) 3 , Al 2 O 3 and TiO 2 .
상기 이형성 첨가제는 1 내지 20 중량부일 수 있다.The releasability additive may be 1 to 20 parts by weight.
상기 무기소재는 5 내지 40 중량부일 수 있다.The inorganic material may be 5 to 40 parts by weight.
상기 용제는 물, 알코올류, 셀로솔부류 및 카비톨류 중 어느 하나 이상일 수 있다. 구체적으로 상기 용제는 전체 용제 기준으로 물을 90% 이상 함유하고, 기능성 향상을 목적으로 알코올류, 셀로솔부류 및 카비톨류 중 어느 하나 이상을 첨가할 수 있다.The solvent may be any one or more of water, alcohols, cellosols, and carbitols. Specifically, the solvent contains 90% or more of water based on the total solvent, and any one or more of alcohols, cellosols, and carbitols may be added for the purpose of improving functionality.
상기 대상체는 상기 조성물이 도포된 후, 박리가 가능한 어느 재질에도 적용이 가능하다. 구체적으로, 상기 대상체는 종이 재질 소재일 수 있다.The object can be applied to any material that can be peeled off after the composition is applied. Specifically, the object may be a paper material.
본 발명은 박리 용이성 도료 조성물에 관한 것으로서, 도료가 도포된 소재에서 박리가 용이하여 원상 복구 효과를 극대화함과 동시에 소재를 보호하고 내구성이 우수한 기능성 도료로 사용될 수 있다.The present invention relates to an easy-to-peel paint composition, which can be easily peeled off from a material to which the paint is applied, thereby maximizing an original restoration effect, protecting the material, and being used as a functional paint with excellent durability.
본 발명의 박리 용이성 도료 조성물은 수성 타입의 친환경적으로 설계되어, 인체와 접촉 시에도 안전하게 사용할 수 있어 실내 인테리어에 적용이 가능하고 이 경우 장소와 용도에 구애받지 아니한 이점이 존재한다.The easy-to-peel paint composition of the present invention is designed to be water-based and eco-friendly, so it can be safely used even when in contact with the human body, so it can be applied to indoor interiors, and in this case, there is an advantage regardless of location and use.
본 발명의 박리 용이성 도료가 도포되어 건조/경화된 도막은 박리가 가능하고, 박리된 도막은 알코올류에 용해되어 재활용이 가능하므로 무독성 소재로 친환경적인 특성을 갖는 이점도 존재한다.The easily peelable paint of the present invention is applied and the dried/cured coating film can be peeled off, and the peeled coating film is dissolved in alcohol and can be recycled, so it is a non-toxic material and has the advantage of having eco-friendly properties.
또한, 본 발명의 박리 용이성 도료에 단열 소재를 혼합 또는 분산하여 외부 창에 도포 시 방한, 보온효과를 얻을 수 있다.In addition, when the heat insulating material is mixed or dispersed in the easy-to-peel paint of the present invention and applied to an external window, cold protection and thermal insulation effects can be obtained.
도 1은 수지단독 첨가된 도료(A) 및 본 발명에 따른 도료(B 및 C)를 도포 후 박리 전의 비교를 나타낸 사진이다.
도 2는 수지단독 첨가된 도료(A`) 및 본 발명에 따른 도료(B` 및 C`)를 도포 후 박리 후의 비교를 나타낸 사진이다.1 is a photograph showing a comparison before peeling after applying a paint (A) to which a resin is added alone and a paint (B and C) according to the present invention.
2 is a photograph showing a comparison after peeling after applying the paint (A') and the paints (B' and C') according to the present invention to which the resin is added alone.
이하, 본 발명의 바람직한 실시형태들을 설명한다. 그러나, 본 발명의 실시형태는 여러 가지 다른 형태로 변형될 수 있으며, 본 발명의 범위가 이하 설명하는 실시 형태로 한정되는 것은 아니다. 또한, 본 발명의 실시형태는 당해 기술분야에서 평균적인 지식을 가진 자에게 본 발명을 더욱 완전하게 설명하기 위해서 제공되는 것이다.Hereinafter, preferred embodiments of the present invention will be described. However, the embodiment of the present invention may be modified in various other forms, and the scope of the present invention is not limited to the embodiments described below. Further, the embodiments of the present invention are provided in order to more completely explain the present invention to those of ordinary skill in the art.
본 발명은 폴리 비닐계 수지, 증점제, 안료, 소포제를 포함하는 첨가제 및 물을 포함하는 조성물에 이형성 첨가제 또는 무기소재를 추가로 더 포함하는 박리 용이성 도료 조성물이다. 상기 박리 용이성 도료 조성물은 박리가 가능한 일반적인 도료와 대비하여 도포된 소재를 보호하고 내구성이 우수하며, 종이 소재인 벽지에서도 박리가 용이하므로 소재의 원상 복구 효과를 극대화하며, 수성타입으로서 인체와 접촉 가능성이 존재하는 실내 인테리어에 사용되어 장소와 용도에 구애받지 않고 안전하게 사용할 수 있는 이점이 존재한다.The present invention provides an easy-to-peel coating composition further comprising a release agent or an inorganic material to a composition including an additive including a polyvinyl-based resin, a thickener, a pigment, and an antifoaming agent, and water. The easy-to-peel paint composition protects the applied material and has excellent durability compared to general paints that can be peeled off, and it is easy to peel even from wallpaper, which is a paper material, so it maximizes the restoration effect of the material, and as a water-based type, contact with the human body There is an advantage that it can be safely used regardless of place and purpose as it is used in the existing indoor interior.
상기 폴리 비닐계 수지는 상기 물에 용해되어 소재 표면에 도장되며 용제가 건조된 후 표면을 보호하는 역할을 하며, 소재 건조가 완료되어 도막의 박리가 필요할 때 쉽게 박리가 일어날 수 있는 특성을 갖는 것이 바람직하다. 본 발명의 박리 용이성 도료 조성물에 적용될 수 있는 폴리 비닐계 수지의 예로서는 폴리 비닐 수지, 비닐계 단량체로 변성된 폴리 비닐 수지 등을 들 수 있다. 이들은 단독 또는 둘 이상을 혼합하여 사용할 수 있다. 상기 폴리 비닐 수지는 수분산 형태로 유연성, 인장력 및 인성이 우수한 수지로서 박리 용이성 도료 조성물을 소재로부터 쉽게 박리가 가능하게 하는 이점이 있다. 바람직하게, 상기 폴리 비닐계 수지는 폴리 비닐 부티랄(poly vinyl butyral), 폴리 비닐 아세테이트(PVaC), 폴리 비닐 알코올(PVA) 등 일 수 있다.The polyvinyl-based resin is dissolved in the water and painted on the surface of the material, and serves to protect the surface after the solvent is dried. desirable. Examples of the polyvinyl-based resin applicable to the easily peelable coating composition of the present invention include a polyvinyl resin, a polyvinyl resin modified with a vinyl-based monomer, and the like. These may be used alone or in combination of two or more. The polyvinyl resin is a resin having excellent flexibility, tensile strength and toughness in the form of water dispersion, and has the advantage of enabling easy peeling of the easily peelable paint composition from the material. Preferably, the polyvinyl-based resin may be polyvinyl butyral, polyvinyl acetate (PVaC), polyvinyl alcohol (PVA), or the like.
상기 박리 용이성 도료 조성물에 포함된 폴리 비닐계 수지의 함량이 전체 중량부에 대하여 30 중량부 미만이면, 코팅액 안정성이 떨어지고 도포성이 나빠 도막 형성이 잘 되지 않는 어려움이 있으며, 80 중량부 초과할 경우 안료가 포함된 페인트를 제조할 수 없는 어려움이 발생된다. 따라서, 상기 박리 용이성 도료 조성물은 상기 폴리 비닐계 수지를 20 내지 80 중량부 포함하고, 바람직하게는 35 내지 65 중량부 포함한다.If the content of the polyvinyl-based resin contained in the easy-to-peel coating composition is less than 30 parts by weight based on the total weight, the coating solution stability is poor and there is a difficulty in forming a coating film due to poor applicability, and when it exceeds 80 parts by weight A difficulty arises in that paints containing pigments cannot be produced. Accordingly, the easily peelable paint composition contains 20 to 80 parts by weight of the polyvinyl-based resin, preferably 35 to 65 parts by weight.
상기 증점제는 조성물의 저장 안정성 및 점도를 개선하여 도포성을 향상시키는 것 역할을 한다. 상기 증점제의 예로서는 셀롤로오스, 아크릴 증점제, 우레탄 증점제, 왁스, Clay 계 등을 들 수 있다. 이들은 단독 또는 둘 이상을 혼합하여 사용할 수 있다.The thickener serves to improve the coating properties by improving the storage stability and viscosity of the composition. Examples of the thickener include cellulose, acrylic thickener, urethane thickener, wax, and clay. These may be used alone or in combination of two or more.
상기 증점제의 함량이 2 중량부 이상이면 점도와 칙소성이 너무 높아 도막을 형성하지 못하는 문제점이 발생한다. 반면, 0.2 중량부 미만일 경우 점도가 너무 낮아 물처럼 흘러내려 도포가 되지 않는 문제점이 발생한다. 따라서, 상기 박리 용이성 도료 조성물은 증점제를 0.2 내지 2 중량부 포함하고, 바람직하게는 0.3 내지 1.5 중량부 포함한다.If the content of the thickener is 2 parts by weight or more, the viscosity and thixotropic properties are too high, and thus a coating film cannot be formed. On the other hand, when the amount is less than 0.2 parts by weight, the viscosity is too low and it flows down like water, which causes a problem in that it is not applied. Therefore, the easy-to-peel paint composition contains 0.2 to 2 parts by weight of the thickener, preferably 0.3 to 1.5 parts by weight.
상기 첨가제는 레벨링제, 습윤 분산제, 방부제, 동결방지제, 소포제 및 기능성을 가지는 첨가제 등을 포함할 수 있다. 이들은 단독 또는 둘 이상을 혼합하여 사용할 수 있다. 상기 첨가제는 박리 용이성 도료 조성물의 작업성 및 물성을 균일하게 유지시키 위해 일반적으로 사용되는 것이다.The additive may include a leveling agent, a wetting and dispersing agent, a preservative, an anti-freezing agent, an antifoaming agent, and an additive having functionality. These may be used alone or in combination of two or more. The additive is generally used to uniformly maintain workability and physical properties of the easily peelable coating composition.
또한, 본 발명의 박리 용이성 도료 조성물은 이형성 첨가제를 추가로 포함할 수 있다. 상기 이형성 첨가제는 본 발명의 박리 용이성 도료 조성물에 포함되어 박리 용이성 도료 조성물을 도포된 소재로부터 쉽게 박리가 가능하게 함에 따라 박리성을 개선할 수 있다. In addition, the easily peelable paint composition of the present invention may further include a releasability additive. The releasability additive may be included in the easily peelable coating composition of the present invention to enable easy peeling of the easily peelable coating composition from the applied material, thereby improving peelability.
상기 이형성 첨가제는 도막의 박리성 향상을 확보하기 위한 것으로 이형성을 높이거나 수지의 응집력을 향상시켜 도료와 소재 표면과의 부착력을 낮추어 박리 효과를 높일 수 있다. 바람직하게, 상기 이형성 첨가제는 실리콘 오일, 실리콘 폴리머, 실리콘 에멀젼, 변성 실리콘 오일 또는 폴리머, 실록산 및 변성 실록산, 실리콘 고무, 왁스타입 첨가제, 계면 활성제, 오일 및 실란 등 일 수 있다. 다만, 박리성을 개선하기 위하여 이형성 첨가제로서 실리콘 오일 및 폴리머 외의 이형성 첨가제는 과량을 사용해야 하며, 박리 가능한 도료는 내구성, 도막 두께 및 도막 강도 등의 문제점이 발생하므로 본 발명의 박리 용이성 도료 조성물에 포함되는 이형성 첨가제는 실리콘 폴리머 또는 오일 (변성 실리콘 오일 및 폴리머)이 적합하다. 상기 박리 용이성 도료 조성물은 이형성 첨가제를 1 내지 20 중량부 포함하고, 바람직하게는 3 내지 15 중량부 포함한다.The releasability additive is for securing the improvement of peelability of the coating film, and may increase the peeling effect by increasing the releasability or improving the cohesive force of the resin to lower the adhesion between the paint and the material surface. Preferably, the release agent additive may be silicone oil, silicone polymer, silicone emulsion, modified silicone oil or polymer, siloxane and modified siloxane, silicone rubber, wax-type additive, surfactant, oil, silane, or the like. However, in order to improve releasability, an excessive amount of releasable additives other than silicone oil and polymer must be used as releasable additives, and peelable paints have problems such as durability, film thickness, and film strength, so they are included in the easy-to-peel paint composition of the present invention Suitable mold release additives are silicone polymers or oils (modified silicone oils and polymers). The easy-to-peel paint composition contains 1 to 20 parts by weight of the releasability additive, preferably 3 to 15 parts by weight.
또한, 본 발명의 박리 용이성 도료 조성물은 무기소재를 추가로 포함할 수 있다. 상기 무기소재는 본 발명의 박리 용이성 도료 조성물에 포함되어 박리 용이성 도료 조성물을 도포된 소재로부터 쉽게 박리가 가능하게 함에 따라 박리성을 개선할 수 있다.In addition, the easily peelable paint composition of the present invention may further include an inorganic material. The inorganic material is included in the easily peelable coating composition of the present invention to enable easy peeling of the easily peelable coating composition from the applied material, thereby improving peelability.
상기 무기소재는 도막의 박리성을 확보하기 위한 것으로 박리 용이성 도료 조성물의 이형성을 높여 페인트와 소재 표면과의 부착력을 낮추어 박리 효과를 높일 수 있다. 또한, 상기 무기소재는 박리 효과 이외에 페인트 증량 효과 및 도포성을 개선하는 역할과 도막의 강도를 향상시키는 역할을 할 수 있다. 바람직하게, 상기 무기소재는 SiO2, CaCO3, BaSO4 및 Talc, Al(OH)3, TiO2 로 이루어진 군에서 선택되는 어느 하나 이상을 포함하거나 혼합하여 사용할 수 있다.The inorganic material is for securing the releasability of the coating film, and by increasing the releasability of the easily peelable coating composition, the adhesion between the paint and the surface of the material is lowered, thereby enhancing the peeling effect. In addition, the inorganic material may serve to improve the paint increase effect and applicability in addition to the peeling effect, and to improve the strength of the coating film. Preferably, the inorganic material may include or mix any one or more selected from the group consisting of SiO 2 , CaCO 3 , BaSO 4 and Talc, Al(OH) 3 and TiO 2 .
상기 무기소재 입자의 크기(㎛)를 조절하여 지지 효과를 높이고 침투성을 억제할 수 있고 수지/무기소재 비율 조절을 통해 내구성, 도막 강도, 도막 두께 등의 기존 물성을 유지하면서 박리성을 개선할 수 있다. 상기 박리 용이성 도료 조성물은 상기 무기소재를 5 내지 40 중량부 포함하고, 바람직하게는 10 내지 30 중량부 포함한다.By controlling the size (㎛) of the inorganic material particles, the support effect can be increased and permeability can be suppressed, and the exfoliation property can be improved while maintaining the existing physical properties such as durability, coating film strength, and coating film thickness by adjusting the resin/inorganic material ratio. have. The easily peelable paint composition contains 5 to 40 parts by weight of the inorganic material, preferably 10 to 30 parts by weight.
또한, 상기 박리 용이성 도료 조성물은 도장부분의 식별을 위하여 안료를 더 포함할 수 있다. 상기 안료의 예로서는 체질안료, 유색안료 및 이들의 혼합 안료들을 들 수 있다. 상기 박리 용이성 도료 조성물에 안료가 포함될 경우 포함되는 안료의 함량이 30 중량부 초과할 경우 페인트의 안정성이 떨어져 페인트의 역할을 하지 못하여 도막 박리가 불량해지는 문제점이 발생된다. 따라서, 상기 박리 용이성 도료 조성물은 상기 안료를 5 내지 30 중량부 포함하고, 바람직하게는 5 내지 20 중량부 포함할 수 있다.In addition, the easy-to-peel paint composition may further include a pigment to identify the painted portion. Examples of the pigment include extender pigments, colored pigments, and mixed pigments thereof. When the pigment is included in the easy-to-peel paint composition, when the content of the pigment exceeds 30 parts by weight, the stability of the paint is lowered and the paint film does not play a role, thereby causing a problem in that the peeling of the coating film is poor. Accordingly, the easily peelable paint composition may contain 5 to 30 parts by weight of the pigment, preferably 5 to 20 parts by weight.
상기 박리 용이성 도료 조성물에 포함되는 용제는 박리 용이성 도료 조성물의 도장의 작업성 확보를 위해 사용된다. 바람직하게, 상기 용제는 물, 셀로솔부류 및 카비톨류 중 어느 하나 이상 일 수 있다. 이들은 단독 또는 둘 이상을 혼합하여 사용할 수 있다. 더욱 바람직하게, 물 및 셀로솔부류 및 카비톨류 중 어느 하나의 혼합물 일 수 있다. 상기 도료에 적용되는 용제의 사용량이 작을 경우 건조 시간이 빠를 수 있으며, 상기 도료에 적용되는 용제의 사용량이 많을 경우 건조 시간이 늦어질 수 있다.The solvent contained in the easily peelable coating composition is used to secure workability of the coating of the easily peelable coating composition. Preferably, the solvent may be any one or more of water, cellosol, and carbitol. These may be used alone or in combination of two or more. More preferably, it may be a mixture of any one of water and cellosols and carbitols. When the amount of the solvent applied to the paint is small, the drying time may be fast, and when the amount of the solvent applied to the paint is large, the drying time may be delayed.
[실시예] [Example]
1. 이형성 첨가제가 포함된 박리 용이성 도료 조성물 제조1. Preparation of easy-to-peel paint composition containing releasable additives
실시예 1Example 1
소재에서 박리와 표면 보호가 가능한 PVB 수분산 수지 PC-2(Shark-Solutions) 60 g을 교반하면서 색상 및 무기 소재의 특성을 발휘시킬 수 있는 수분산 백색 안료(우신피크먼트) 15 g을 첨가하였다. 이 후, 물 11 g을 첨가하고 10분 동안 혼합이 잘 되게 하였다. 계속 교반하면서 증점제인 TT-935D(Dow chemical) 5.5 g을 첨가하면서 도료의 점도가 상승하면 교반기의 rpm을 상승시켜 혼합을 용이하게 하였다. 30~60분 이상 고속으로 교반 후 박리성을 향상시킬 수 있는 실리콘 이형성 첨가제 PMX200F(새한실리켐) 7.5 g 및 기포 억제 및 발생된 기포를 파포시키는 소포제 F-810(Tego) 1 g을 혼합한 후, 30분 이상 고속 교반함으로써 본 발명에 따른 박리 용이성 도료 조성물을 제조하였다.60 g of PVB water-dispersed resin PC-2 (Shark-Solutions), which can be peeled off and surface protected from the material, was added while stirring, and 15 g of water-dispersed white pigment (Wooshin Pigment) capable of exhibiting the properties of color and inorganic materials was added. . After this, 11 g of water was added and mixed well for 10 minutes. When the viscosity of the paint increased while adding 5.5 g of TT-935D (Dow chemical) as a thickener while stirring continuously, the rpm of the stirrer was increased to facilitate mixing. After mixing 7.5 g of PMX200F (Saehan Silicone Chem), a silicone releasable additive that can improve peelability after stirring at high speed for 30 to 60 minutes or more, and 1 g of F-810 (Tego), an antifoaming agent that suppresses bubbles and breaks the generated bubbles, , an easy-to-peel coating composition according to the present invention was prepared by high-speed stirring for at least 30 minutes.
실시예 2Example 2
상기 실시예 1과 동일한 방법으로 박리 용이성 도료 조성물을 제조하되, 상기 이형성 첨가제인 PMX200F 7.5 g 대신에 MEM3345(새한실리켐) 7.5 g를 사용하여 박리 용이성 도료 조성물을 제조하였다.An easy-to-peel coating composition was prepared in the same manner as in Example 1, except that 7.5 g of MEM3345 (Saehan Silicam) was used instead of 7.5 g of PMX200F, which is the release agent, to prepare an easy-to-peel coating composition.
실시예 3Example 3
상기 실시예 1과 동일한 방법으로 박리 용이성 도료 조성물을 제조하되, 상기 이형성 첨가제인 PMX200F 7.5 g 대신에 MEM3345(새한실리켐) 20 g 사용하여 박리 용이성 도료 조성물을 제조하였다.An easy-to-peel paint composition was prepared in the same manner as in Example 1, except that 20 g of MEM3345 (Saehan Silichem) was used instead of 7.5 g of PMX200F, which is the release agent, to prepare an easy-to-peel paint composition.
실시예 4Example 4
상기 실시예 1과 동일한 방법으로 박리 용이성 도료 조성물을 제조하되, 상기 이형성 첨가제인 PMX200F 7.5 g 대신에 MEM3345(새한실리켐) 25 g 사용하여 박리 용이성 도료 조성물을 제조하였다.An easy-to-peel paint composition was prepared in the same manner as in Example 1, except that 25 g of MEM3345 (Saehan Silicam) was used instead of 7.5 g of PMX200F, which is the release additive, to prepare an easy-to-peel paint composition.
실시예 5Example 5
상기 실시예 1과 동일한 방법으로 박리 용이성 도료 조성물을 제조하되, 상기 이형성 첨가제인 PMX200F 7.5 g 대신에 PMX50(새한실리켐) 10 g 사용하여 박리 용이성 도료 조성물을 제조하였다.An easy-to-peel paint composition was prepared in the same manner as in Example 1, except that 10 g of PMX50 (Saehan Silicam) was used instead of 7.5 g of PMX200F, which is the releasability additive, to prepare an easy-to-peel paint composition.
실시예 6Example 6
상기 실시예 1과 동일한 방법으로 박리 용이성 도료 조성물을 제조하되, 상기 이형성 첨가제인 PMX200F 7.5 g 대신에 HV495(새한실리켐) 10 g 사용하여 박리 용이성 도료 조성물을 제조하였다.An easy-to-peel paint composition was prepared in the same manner as in Example 1, except that 10 g of HV495 (Saehan Silicam) was used instead of 7.5 g of PMX200F, which is the releasability additive, to prepare an easy-to-peel paint composition.
실시예 7Example 7
상기 실시예 1과 동일한 방법으로 박리 용이성 도료 조성물을 제조하되, 상기 이형성 첨가제인 PMX200F 7.5 g 대신에 PMX 0345(새한실리켐) 10 g 사용하여 박리 용이성 도료 조성물을 제조하였다.An easy-to-peel paint composition was prepared in the same manner as in Example 1, except that 10 g of PMX 0345 (Saehan Silichem) was used instead of 7.5 g of PMX200F, which is the release additive, to prepare an easy-to-peel paint composition.
실시예 8Example 8
상기 실시예 1과 동일한 방법으로 박리 용이성 도료 조성물을 제조하되, 상기 이형성 첨가제인 PMX200F 7.5 g 대신에 PMX 0245(새한실리켐) 10 g 사용하여 박리 용이성 도료 조성물을 제조하였다.An easy-to-peel paint composition was prepared in the same manner as in Example 1, except that 10 g of PMX0245 (Saehan Silicam) was used instead of 7.5 g of PMX200F, which is the release additive, to prepare an easy-to-peel paint composition.
2. 무기소재가 포함된 박리 용이성 도료 조성물 제조2. Manufacture of easy-to-peel paint composition containing inorganic materials
실시예 9Example 9
소재에서 박리와 표면 보호가 가능한 PVB 수분산 수지 PC-2(Shark-Solutions) 60 g을 교반하면서 색상 및 무기 소재의 특성을 발휘시킬 수 수분산 백색 안료(우신피크먼트) 20 g을 첨가하였다. 이 후, 물 14 g을 첨가하고 10분 동안 혼합이 잘 되게 하였다. 계속 교반하면서 증점제인 TT-935D(Dow chemical) 3 g을 첨가하면서 도료의 점도가 상승하면 교반기의 rpm을 상승시켜 혼합을 용이하게 하였다. 30~60분 이상 고속으로 교반 후 박리성을 향상시키고 도료의 도포성 개선할 수 있는 무기소재 SiO2(5μm)(SOLVAY) 2 g을 첨가하여 고속으로 60분 이상 교반한 후, 기포 억제 및 발생된 기포를 파포시키는 소포제(Tego) F-810 1 g을 혼합한 후, 30분 이상 고속 교반함으로써 본 발명에 따른 박리 용이성 도료 조성물을 제조하였다.While stirring 60 g of PVB water-dispersed resin PC-2 (Shark-Solutions), which can be peeled off and surface protected from the material, 20 g of water-dispersed white pigment (Wooshin Pigment) that can exhibit color and inorganic material properties was added. After this, 14 g of water was added and mixed well for 10 minutes. While stirring, 3 g of TT-935D (Dow chemical), a thickener, was added, and when the viscosity of the paint increased, the rpm of the stirrer was increased to facilitate mixing. After stirring at high speed for 30 to 60 minutes or more , 2 g of inorganic material SiO 2 (5 μm) (SOLVAY), which can improve peelability and improve paint applicability, is added and stirred at high speed for more than 60 minutes, and bubbles are suppressed and generated After mixing 1 g of an antifoaming agent (Tego) F-810 for breaking the old air bubbles, the easy-to-peel paint composition according to the present invention was prepared by high-speed stirring for at least 30 minutes.
실시예 10Example 10
상기 실시예 1과 동일한 방법으로 박리 용이성 도료 조성물을 제조하되, 상기 증점제인 TT-935D 3 g 대신에 TT-935D 2 g 사용하여 박리 용이성 도료 조성물을 제조하였다.An easy-to-peel coating composition was prepared in the same manner as in Example 1, but an easy-to-peel coating composition was prepared using 2 g of TT-935D instead of 3 g of TT-935D as the thickener.
실시예 11Example 11
상기 실시예 1과 동일한 방법으로 박리 용이성 도료 조성물을 제조하되, 상기 무기소재인 SiO2(5μm) 3 g 대신에 CaCO3(5μm)(오미야코리아) 7.5 g 사용하여 박리 용이성 도료 조성물을 제조하였다.An easy-to-peel coating composition was prepared in the same manner as in Example 1, except that 7.5 g of CaCO 3 (5 μm) (Omiya Korea) was used instead of 3 g of the inorganic material SiO 2 (5 μm) to prepare an easy-to-peel coating composition.
실시예 12Example 12
상기 실시예 1과 동일한 방법으로 박리 용이성 도료 조성물을 제조하되, 상기 무기소재인 SiO2(5μm) 3 g 대신에 CaCO3(20μm)(오미야코리아) 7.5 g 사용하여 박리 용이성 도료 조성물을 제조하였다.An easy-to-peel coating composition was prepared in the same manner as in Example 1, except that 7.5 g of CaCO 3 (20 μm) (Omiya Korea) was used instead of 3 g of the inorganic material SiO 2 (5 μm) to prepare an easy-to-peel coating composition.
실시예 13Example 13
상기 실시예 1과 동일한 방법으로 박리 용이성 도료 조성물을 제조하되, 상기 무기소재인 SiO2(5μm) 3 g 대신에 CaCO3(5μm)(오미야코리아) 10 g 사용하여 박리 용이성 도료 조성물을 제조하였다.An easy-to-peel coating composition was prepared in the same manner as in Example 1, but instead of 3 g of the inorganic material SiO 2 (5 μm), 10 g of CaCO 3 (5 μm) (Omiya Korea) was used to prepare an easy-to-peel coating composition.
실시예 14Example 14
상기 실시예 1과 동일한 방법으로 박리 용이성 도료 조성물을 제조하되, 상기 무기소재인 SiO2(5μm) 3 g 대신에 BaSO4(2μm)(대정화금(시약), 코츠) 10 g 사용하여 박리 용이성 도료 조성물을 제조하였다.An easy-to-peel paint composition was prepared in the same manner as in Example 1, but instead of 3 g of SiO 2 (5 μm), which is the inorganic material, 10 g of BaSO 4 (2 μm) (Daejeong Hwaeum (reagent), coat) was used to facilitate peeling A paint composition was prepared.
실시예 15Example 15
상기 실시예 1과 동일한 방법으로 박리 용이성 도료 조성물을 제조하되, 상기 무기소재인 SiO2(5μm) 3 g 대신에 CaCO3(10μm) 10 g 사용하여 박리 용이성 도료 조성물을 제조하였다.An easy-to-peel coating composition was prepared in the same manner as in Example 1, except that 10 g of CaCO 3 (10 μm) was used instead of 3 g of the inorganic material SiO 2 (5 μm) to prepare an easy-to-peel coating composition.
실시예 16Example 16
상기 실시예 1과 동일한 방법으로 박리 용이성 도료 조성물을 제조하되, 상기 무기소재인 SiO2(5μm) 3 g 대신에 Talc 10 g 사용하여 박리 용이성 도료 조성물을 제조하였다.An easy-to-peel paint composition was prepared in the same manner as in Example 1, except that 10 g of Talc was used instead of 3 g of the inorganic material SiO 2 (5 μm) to prepare an easy-to-peel paint composition.
상기 본 발명에 따른 실시예 1 내지 16의 박리 용이성 도료 조성물에 따른 각각의 성분 및 함량을 하기 표 1 및 표 2에 정리하였다.Each of the components and contents according to the easily peelable paint compositions of Examples 1 to 16 according to the present invention are summarized in Tables 1 and 2 below.
(5μm)SiO 2
(5μm)
(5μm)CaCO 3
(5μm)
(20μm)CaCO 3
(20μm)
(2μm)BaSO 4
(2μm)
(10μm)BaSO 4
(10μm)
비교예comparative example
소재에서 박리와 표면 보호가 가능한 PVB 수분산 수지 PC-2 70 g을 교반하면서 색상을 발휘시킬 수 수분산 백색 안료 10 g을 첨가하였다. 이 후, 물 15 g을 첨가하고 10분 동안 혼합이 잘 되게 하였다. 계속 교반하면서 증점제인 TT-935D 4 g을 첨가하면서 도료의 점도가 상승하면 교반기의 rpm을 상승시켜 혼합을 용이하게 하였다. 30~60분 이상 고속으로 교반 후 기포 억제 및 발생된 기포를 파포시키는 소포제 F-810 1 g을 혼합한 후, 30분 이상 고속 교반하여 비교예 1의 도료를 제조하였다.70 g of PVB water-dispersed resin PC-2, which can be peeled off and surface protected from the material, was stirred while 10 g of water-dispersed white pigment was added. After this, 15 g of water was added and mixed well for 10 minutes. When the viscosity of the paint increased while adding 4 g of TT-935D as a thickener while stirring continuously, the rpm of the stirrer was increased to facilitate mixing. After stirring at high speed for 30-60 minutes or more, 1 g of an antifoaming agent F-810 for suppressing bubbles and breaking generated bubbles was mixed, followed by high-speed stirring for 30 minutes or more to prepare the paint of Comparative Example 1.
[실험 결과][Experiment result]
종이 시편 위에 실시예 1 내지 8 및 실시예 9 내지 16, 비교예의 도료를 에어리스 스프레이나 롤러(붓) 등으로 50~100㎛ 두께로 도장한 후 건조한다. 이후 1개월간 방치하여 형성된 도막의 박리성과 물성을 확인하였다. 상기 물성의 평가는 하기와 같은 평가 방법에 의해 평가되었고, 그 평가 결과가 표 3 및 표 4에 개시되어 있다.On a paper specimen, the paints of Examples 1 to 8, Examples 9 to 16, and Comparative Examples are coated with an airless spray or roller (brush) to a thickness of 50 to 100 μm, and then dried. After that, it was allowed to stand for 1 month to confirm the peelability and physical properties of the formed coating film. The evaluation of the physical properties was evaluated by the following evaluation method, and the evaluation results are disclosed in Tables 3 and 4.
1. 이형성 첨가제가 포함된 박리 용이성 도료 조성물의 평가1. Evaluation of easy-to-peel paint composition containing releasable additives
(숫자가 높을수록 박리성 및 도막강도가 우수함: 1~5점)(The higher the number, the better the peelability and film strength: 1 to 5 points)
2. 무기소재가 포함된 박리 용이성 도료 조성물의 평가2. Evaluation of Easy Peelable Paint Compositions Containing Inorganic Materials
(숫자가 높을수록 박리성 및 도막강도가 우수함: 1~5점)(The higher the number, the better the peelability and film strength: 1 to 5 points)
3. 이형성 첨가제 또는 무기소재가 미포함된 도료 조성물의 평가3. Evaluation of paint composition that does not contain mold release additives or inorganic materials
상기 표 3 내지 표 5를 참조하면, 본 발명에 따른 실시예 1 내지 16의 박리 용이성 도료 조성물이 이형성 첨가제 또는 무기소재를 포함하지 않는 비교예의 도료에 비해 우수한 박리성을 가짐을 확인할 수 있다. Referring to Tables 3 to 5, it can be seen that the easily peelable paint compositions of Examples 1 to 16 according to the present invention have superior peelability compared to the paints of Comparative Examples that do not include a release additive or an inorganic material.
한편, 도 1 및 도 2는 대상체에 비교예 및 본 발명의 도료를 도포에 의한 박리성을 테스트한 것으로, 이형성 첨가제를 포함한 도료(도 1의 B 및 도 2의 B`) 및 무기소재를 포함한 도료(도 1의 C 및 도 2의 C`)가 이형성 첨가제 및 무기소재를 포함하지 아니한 비교예(도 1의 A 및 도 2의 A`)와 대비하여 박리성이 우수한 것을 확인할 수 있었다.On the other hand, FIGS. 1 and 2 are tests for peelability by applying the paints of the comparative example and the present invention to the object, and include a paint including a release agent (B and 2B in FIGS. 1B and 2B ') and an inorganic material. It was confirmed that the paint (C' in FIG. 1 and C' in FIG. 2) had excellent peelability compared to the comparative examples (A in FIG. 1 and A' in FIG. 2) that did not include a release additive and an inorganic material.
Claims (8)
증점제 0.2 내지 2 중량부;
안료 5 내지 30 중량부;
소포제를 포함하는 첨가제 1 내지 5 중량부; 및
용제 5 내지 30 중량부를 포함하는, 대상체로부터 박리가 용이한 도료 조성물로서,
상기 조성물은 이형성 첨가제 및 무기소재 중 어느 하나 이상을 포함하고,
상기 용제는 물을 포함하며,
상기 이형성 첨가제는 1 내지 20 중량부이며,
상기 무기소재는 5 내지 40 중량부인 것을 특징으로 하는 박리 용이성 도료 조성물.30 to 80 parts by weight of a polyvinyl-based resin;
0.2 to 2 parts by weight of a thickener;
5 to 30 parts by weight of a pigment;
1 to 5 parts by weight of an additive containing an antifoaming agent; and
A paint composition comprising 5 to 30 parts by weight of a solvent, which is easily peeled off from an object,
The composition includes any one or more of a mold release additive and an inorganic material,
The solvent includes water,
The releasability additive is 1 to 20 parts by weight,
The easily peelable paint composition, characterized in that the inorganic material is 5 to 40 parts by weight.