KR100663839B1 - Multifunctional cellulose textile and preparation for preparing the same - Google Patents
Multifunctional cellulose textile and preparation for preparing the same Download PDFInfo
- Publication number
- KR100663839B1 KR100663839B1 KR1020050049849A KR20050049849A KR100663839B1 KR 100663839 B1 KR100663839 B1 KR 100663839B1 KR 1020050049849 A KR1020050049849 A KR 1020050049849A KR 20050049849 A KR20050049849 A KR 20050049849A KR 100663839 B1 KR100663839 B1 KR 100663839B1
- Authority
- KR
- South Korea
- Prior art keywords
- multifunctional
- processing agent
- cellulose fiber
- acid
- processing
- Prior art date
Abstract
본 발명은 항균방취성, 소취성, 흡수성, 속건성, 흡습발열성 및 자외선 차단성 등이 우수한 다기능 셀룰로오스 섬유제품에 관한 것으로, 더욱 상세하게는 다기능성을 발현하는 카르복실계 화합물을 셀룰로오스계 섬유와 화학적 결합이 가능한 에폭시계 화합물, 트리아진계 화합물, 피리미딘계 화합물 등과 반응시켜 다기능 가공제를 합성하는 단계, 합성한 다기능 가공제를 섬유, 슬라이버, 조사, 실 및 직·편성물 등에 처리하는 단계를 거쳐 제조되는 항균방취성, 소취성, 흡수성, 속건성, 흡습발열성 및 자외선 차단성 등이 우수하고, 이들 기능성의 내세탁성이 영구적인 셀룰로오스 섬유제품 및 그의 제조 방법에 관한 것이다.The present invention relates to a multifunctional cellulose fiber product excellent in antimicrobial deodorization, deodorization, absorbency, quick drying, hygroscopic and sun protection, and more particularly, a carboxyl compound expressing multi-functionality may be combined with a cellulose fiber. Synthesizing a multifunctional processing agent by reacting with an epoxy compound, a triazine compound, a pyrimidine compound, etc., which are capable of chemical bonding, and treating the synthesized multifunctional processing agent with fibers, slivers, irradiation, yarns, and knit fabrics. The present invention relates to a cellulose fiber product which is excellent in antibacterial deodorization, deodorizing property, absorbency, quick drying, hygroscopic pyrogenic property and ultraviolet ray blocking property, and has a launder resistance of these functional properties and a method for producing the same.
셀룰로오스 섬유, 다기능성, 항균방취성, 소취성, 흡수성, 속건성, 흡습발열성, 자외선 차단성 Cellulose Fiber, Multifunctional, Antibacterial Deodorant, Deodorant, Absorbent, Quick Dry, Moisture Absorption, UV Blocking
Description
본 발명은 항균방취성, 소취성, 흡수성, 속건성, 흡습발열성 및 자외선 차단성 등이 우수한 다기능 셀룰로오스 섬유제품에 관한 것으로, 더욱 상세하게는 셀룰로오스계 섬유와 화학적 결합이 가능한 에폭시계 화합물, 트리아진계 화합물, 피리미딘계 화합물 등과 항균방취성, 소취성, 흡수성, 속건성, 흡습발열성 및 자외선 차단성 등의 기능성 발현이 가능한 카르복실계 화합물 등을 반응시켜 다기능 가공제를 합성하는 단계, 흡진법 또는 패드 드라이 큐어법을 이용하여 합성 가공제를 섬유, 슬라이버, 조사, 실 및 직·편성물 등에 처리하는 단계를 거쳐 제조되는 항균방취성, 소취성, 흡수성, 속건성, 흡습발열성 및 자외선 차단성 등이 우수하고, 이들 기능성의 내세탁성이 영구적인 셀룰로오스 섬유제품 및 그의 제조 방법에 관한 것이다.The present invention relates to a multifunctional cellulose fiber product excellent in antimicrobial deodorization, deodorization, absorbency, quick drying, hygroscopic and sun protection, and more specifically, an epoxy compound and a triazine-based chemical compound capable of chemically bonding with cellulose fibers. Synthesizing a multifunctional processing agent by reacting a compound or a pyrimidine compound with a carboxyl compound capable of expressing functionalities such as antibacterial deodorization, deodorization, absorption, quick drying, hygroscopicity and UV blocking, etc. Antibacterial deodorant, deodorant, absorbent, quick-drying, hygroscopic heat-generating and UV-blocking, etc., which are manufactured through the process of treating synthetic processing agents to fibers, slivers, irradiation, yarn, and knitted fabrics using the pad dry cure method. The present invention relates to a cellulosic fiber product having excellent excellent washing resistance of these functionalities and a method for producing the same.
섬유의 기능성 가공이란 기존 섬유제품이 가지고 있지 않은 기능을 새로이 부여하는 것으로, 대표적인 가공으로는 항균방취가공, 소취가공, 흡한속건가공, 흡 습발열가공, 자외선 차단가공, 형태안정가공, 발수 및 발유가공 등이 있다. 이 중에서 특히 항균방취가공, 소취가공, 흡한속건가공, 자외선 차단가공 등은 사람들의 생활수준 향상에 따라 점차 건강과 쾌적함을 추구하려는 경향이 높아져 다수의 섬유제품에 대해 행해지고 있다.The functional processing of the fiber is to give a new function that the existing textile products do not have. Representative processing includes antibacterial deodorization processing, deodorization processing, quick drying process, moisture absorption heat treatment, UV protection processing, shape stability processing, water repellent and water repellent Dairy processing. Among them, in particular, antibacterial deodorization processing, deodorization processing, sweat absorption quick drying processing, UV protection processing and the like have been increasingly performed to a large number of textile products in accordance with the increasing tendency to seek health and comfort as people's living standards are improved.
항균방취가공은 악취의 원인인 미생물의 증식을 억제하기 위한 것으로, 구리, 은, 아연 등의 금속 화합물, 제4급 암모늄염계 화합물, 카르복실계 화합물 등이 사용된다. 소취가공은 각종 악취물질을 화학적으로 변화시키거나 흡착하여 냄새를 제거하는 것으로 금속 프탈로시아닌, 광촉매, 카르복실계 화합물, 활성탄 등이 사용된다. 흡한속건가공은 땀 등의 수분을 빠르게 흡수, 확산, 건조되도록 한 것으로 물이 빠르게 확산되도록 섬유의 단면형태를 변화시킨 것이 주로 사용되고 있다. 자외선 차단가공은 자외선을 흡수하거나 산란하는 물질을 섬유에 부여하여 인체에 유해한 자외선을 차단하는 것으로 방향족 유기화합물, 산화티타늄 등이 사용된다. Antibacterial and deodorant processing is for suppressing the growth of microorganisms that cause malodor, and metal compounds such as copper, silver and zinc, quaternary ammonium salt compounds and carboxyl compounds are used. Deodorization is to remove odor by chemically changing or adsorbing various odorous substances. Metal phthalocyanine, photocatalyst, carboxyl compound, activated carbon and the like are used. Absorption quick-drying processing is used to quickly absorb, diffuse, and dry the moisture, such as sweat, and is mainly used to change the cross-sectional shape of the fiber so that the water diffuses quickly. Ultraviolet ray blocking processing is to block ultraviolet rays harmful to the human body by imparting substances to absorb or scatter ultraviolet rays to the fiber, aromatic organic compounds, titanium oxide and the like are used.
기존의 기능성 가공제품은 주로 하나의 기능성만을 부여한 단일 가공 제품이었으나 최근에는 2종류 이상의 기능성을 부여한 제품, 즉 항균방취성과 소취성이 동시에 발현되거나 항균방취성과 흡한속건성이 동시에 발현되도록 한 다기능 제품들이 제조되고 있다. 통상 이들 다기능 제품은 2종류 이상의 기능성 가공제를 사용하여 2회 이상 가공을 하거나 여러 종류의 기능성 가공제를 혼합하는 방법으로 제조된다. 그러나 2회 이상 가공을 행할 경우 생산성 저하 및 제조비용 증가 등의 단점이 있고, 여러 종류의 기능성 가공제를 혼합하여 처리할 경우 가공제간 특성 차이로 응집을 일으켜 가공제가 침전하거나 상호작용에 의해 서로간의 성능을 저하시 키는 등 실제 사용에 있어 많은 제약이 따르는 단점이 있다. Existing functional processed products were mainly single processed products that gave only one functionality, but recently, products that have been given two or more types of functionalities, such as antibacterial and deodorant at the same time, or antibacterial and sweat absorbent quick drying are simultaneously produced. It is becoming. Usually these multifunctional products are produced by the process of two or more times using two or more types of functional processing agents, or by mixing several types of functional processing agents. However, when processing more than two times, there are disadvantages such as lower productivity and increased manufacturing cost.When mixing and processing various kinds of functional processing agents, the processing agent precipitates due to the difference in characteristics between processing agents and precipitates or interacts with each other. There are many disadvantages in actual use, such as degrading performance.
상기한 기능성 가공제들은 대부분 섬유와 화학적 결합을 하지 못하기 때문에 세탁에 대한 내구성이 매우 약하다. 따라서 내구성 향상을 위해 바인더를 사용하여 직물 또는 편성물에 가공제를 부착시켜주는데, 이 경우에도 반복 세탁에 의해 가공제가 탈락하기 때문에 세탁 내구성 향상에 한계가 있다는 단점이 있다.Most of the functional processing agents described above do not chemically bond with the fiber, and thus have very low durability against washing. Therefore, in order to improve durability, a binder is used to attach the processing agent to a fabric or knitted fabric. In this case, the processing agent is dropped by repeated washing.
또한 상기 기능성 가공제들은 주로 바인더를 사용하여 섬유 제품에 부착시켜주기 때문에 흡진법으로는 처리가 곤란하여 패드 드라이 큐어법을 이용하여 처리를 한다. 그러나 패드 드라이 큐어법은 주로 직물 및 편성물에 한해 적용이 가능하기 때문에 섬유, 슬라이버, 조사, 실 등에는 적용이 어려워 제품 다양화 측면에서도 한계가 있다. In addition, since the functional processing agents are mainly attached to the fiber products using a binder, it is difficult to process by the dust-absorbing method, so the treatment is performed using the pad dry cure method. However, since the pad dry cure method is mainly applicable to fabrics and knitted fabrics, it is difficult to apply to fibers, slivers, yarns, and yarns, and thus there is a limit in terms of product diversification.
본 발명은 상기한 바와 같은 선행기술의 제반 문제점을 해소하기 위한 것으로, 항균방취성, 소취성, 흡수성, 속건성, 흡습발열성 및 자외선 차단성 등의 다기능성을 가지며, 섬유와 화학적으로 결합이 가능한 가공제를 합성하는 방법과 이를 이용하여 합성한 다기능 가공제로 셀룰로오스 섬유, 슬라이버, 조사, 실 및 직·편성물에 처리함으로써 영구적인 내세탁성을 갖는 다기능 셀룰로오스 섬유제품을 제조하는 것을 목적으로 한다.The present invention is to solve all the problems of the prior art as described above, has a multi-functionality such as antibacterial deodorant, deodorant, absorbent, quick-drying, hygroscopic pyrogenic and UV-blocking, and can be chemically combined with the fiber A method of synthesizing a processing agent and a multifunctional processing agent synthesized by using the same, and the object of the present invention is to produce a multifunctional cellulose fiber product having permanent washing resistance by treating it with cellulose fibers, slivers, irradiation, yarns, and knitted fabrics.
이와 같은 목적은 셀룰로오스 섬유와 공유결합이 가능한 반응성기와 항균방취성, 소취성, 흡수성, 속건성, 흡습발열성 및 자외선 차단성 등의 다기능성을 발 현하는 기능성기로 구성되는 가공제를 합성하고, 합성한 가공제가 포함된 가공제 수용액으로 섬유, 슬라이버, 조사, 실 및 직·편성물 등을 흡진법 또는 패드 드라이 큐어법으로 처리하는 것에 의해 달성된다.This purpose is to synthesize and synthesize a processing agent composed of a functional group that exhibits multifunctional properties such as a reactive group capable of covalent bonding with cellulose fibers and antibacterial deodorant, deodorant, absorbent, quick-drying, hygroscopic pyrogenicity and UV protection. It is achieved by treating fibers, slivers, irradiation, yarns, knitted fabrics and the like with a dust reduction method or a pad dry cure method with an aqueous solution of a processing agent containing a processing agent.
본 발명은, 에폭시계 화합물, 트리아진계 화합물 및 피리미딘계 화합물로 이루어진 그룹에서 선택된 1종의 화합물과 카르복실계 화합물을 반응시켜 다기능 가공제를 합성하고, 상기 다기능성 가공제를 셀룰로오스 섬유, 슬라이버, 조사, 실 또는 직·편성물에 화학적 결합시키는 것을 특징으로 한다. 상기 다기능성 가공제는 히드록시기 또는 아민기와 반응할 수 있는 반응기를 2개 이상 갖는 트리아진계 화합물로 이루어진 그룹에서 선택된 1종의 화합물과 히드록시기 또는 아민기를 가지고 있는 카르복실계 화합물을 반응시켜 다기능 가공제를 합성하는 것이 바람직하다.The present invention synthesizes a multifunctional processing agent by reacting one compound selected from the group consisting of an epoxy compound, a triazine compound, and a pyrimidine compound with a carboxyl compound, and converting the multifunctional processing agent into a cellulose fiber, a slice It is characterized by chemically bonding to burrs, irradiation, yarns, or knitted fabrics. The multifunctional processing agent reacts a carboxyl compound having a hydroxy group or an amine group with a compound selected from the group consisting of triazine compounds having two or more reactors capable of reacting with a hydroxyl group or an amine group to form a multifunctional processing agent. It is preferable to synthesize.
또한, 상기 다기능성 가공제는 섬유제품 중량대비 0.1 내지 5% o.w.f.(on the weight of fiber) 포함시키는 것이 바람직하다.In addition, the multifunctional processing agent is preferably included 0.1 to 5% o.w.f. (on the weight of fiber) relative to the weight of the fiber product.
또한, 상기 셀룰로오스 섬유, 슬라이버, 조사, 실 또는 직·편성물에 은, 아연 및 구리로 이루어진 그룹에서 선택된 1종의 금속화합물을 섬유제품 중량대비 20 내지 10,000ppm 더 포함할 수 있다. In addition, the cellulose fibers, slivers, irradiation, yarn or knitted fabrics may further comprise 20 to 10,000 ppm by weight of the fiber product of one metal compound selected from the group consisting of silver, zinc and copper.
또한, 상기 카르복실계 화합물은 히드록시아세트산, 히드록시벤조산, 히드록시벤젠디카르복실산, 아미노아세트산, 아미노벤조산, 및 아미노벤젠디카르복실산으로 이루어진 그룹에서 선택된 1종의 화합물인 것이 바람직하다. In addition, the carboxyl compound is preferably one compound selected from the group consisting of hydroxyacetic acid, hydroxybenzoic acid, hydroxybenzenedicarboxylic acid, aminoacetic acid, aminobenzoic acid, and aminobenzenedicarboxylic acid. .
본 발명의 다기능 셀룰로오스 섬유제품은 하기 단계를 거쳐 제조되는 것을 특징으로 한다. Multifunctional cellulose fiber product of the present invention is characterized in that it is produced through the following steps.
(A) 셀룰로오스 섬유와 화학적 결합이 가능한 에폭시계 화합물, 트리아진계 화합물, 피리미딘계 화합물 중 한가지와 카르복실계 화합물인 히드록시아세트산, 히드록시벤조산, 히드록시벤젠디카르복실산, 아미노아세트산, 아미노벤조산, 아미노벤젠디카르복실산 등을 반응시켜 다기능 가공제를 합성하는 단계;(A) hydroxyacetic acid, hydroxybenzoic acid, hydroxybenzenedicarboxylic acid, aminoacetic acid, amino Reacting benzoic acid, aminobenzenedicarboxylic acid or the like to synthesize a multifunctional processing agent;
(B) 합성한 다기능 가공제를 이용하여 셀룰로오스 섬유, 슬라이버, 조사, 실 및 직·편성물을 가공하는 단계; 및(B) processing the cellulose fibers, slivers, yarns, yarns, and knitted fabrics using the synthesized multifunctional processing agent; And
(C) 상기 가공된 셀룰로오스 섬유, 슬라이버, 조사, 실 및 직·편성물에 구리, 은, 아연 등의 금속 성분을 도입하는 단계.(C) introducing metal components such as copper, silver, zinc into the processed cellulose fibers, slivers, irradiation, yarns and knitted fabrics.
본 발명의 다기능 셀룰로오스 섬유제품 제조에 있어서 (A)단계는 다기능 가공제를 합성하는 단계로, 다기능 가공제는 2개 이상의 화합물을 화학적으로 반응시켜 합성한 화합물(즉, R + F = RF(다기능 가공제))이다. R은 다기능 가공제를 셀룰로오스 섬유에 결합시키기 위한 반응성 그룹이고, F는 기능성을 발현하는 기능성 그룹에 해당된다. 반응성 그룹인 R에 해당되는 화합물로는 에폭시계 화합물, 트리아진계 화합물, 피리미딘계 화합물 등이 있다. 에폭시계 화합물로는 에피클로로히드린 등이 있으며, 트리아진계 화합물로는 트리클로로트리아진 등이 있고, 피리미딘계 화합물로는 테트라클로로피리미딘 등이 있는데 특별히 이들로 한정하는 것은 아니다. 기능성 그룹(F)에 해당되는 화합물로는 카르복실계 화합물인 히드록시아세트산, 히드록시벤조산, 히드록시벤젠디카르복실산, 아미노아세트산, 아미노벤조산, 아미노벤젠디카르복실산 등이 있다. In the production of the multifunctional cellulose fiber product of the present invention, step (A) is a step of synthesizing a multifunctional processing agent, and the multifunctional processing agent is a compound synthesized by chemically reacting two or more compounds (that is, R + F = RF (multifunctional) Processing agent)). R is a reactive group for binding the multifunctional processing agent to the cellulose fiber, and F corresponds to a functional group expressing functionality. Examples of the compound corresponding to R, which is a reactive group, include an epoxy compound, a triazine compound, a pyrimidine compound, and the like. Examples of the epoxy compound include epichlorohydrin, triazine triazine and the like, and pyrimidine compounds include tetrachloropyrimidine and the like, but are not particularly limited thereto. Examples of the compound corresponding to the functional group (F) include hydroxyacetic acid, hydroxybenzoic acid, hydroxybenzenedicarboxylic acid, aminoacetic acid, aminobenzoic acid and aminobenzenedicarboxylic acid, which are carboxyl compounds.
본 발명의 다기능 가공제 합성에 있어서, 반응성 그룹(R)에 해당되는 화합물의 종류에 따라 그 합성방법이 달라질 수 있다.In the synthesis of the multifunctional processing agent of the present invention, the synthesis method may vary depending on the kind of the compound corresponding to the reactive group (R).
반응성 그룹(R)으로 에피클로로히드린을 사용하여 기능성 그룹(F)에 해당되는 화합물과 반응시켜 다기능 가공제를 합성하는 경우;Using epichlorohydrin as the reactive group (R) to react with the compound corresponding to the functional group (F) to synthesize a multifunctional processing agent;
에피클로로히드린 20～200g/l를 물/에탄올(80/20) 혼합액에 10～20분간 교반하여 분산시키고, 50～90℃에서 에피클로로히드린과 같은 몰수에 해당되는 아미노벤젠디카르복실산을 30～60분간에 걸쳐 5～10회 분할 투입한 후 1～4시간 동안 교반하여 다기능 가공제를 합성하는 것을 특징으로 한다. 이때 기능성 그룹(F)으로 아미노벤젠디카르복실산 대신에 히드록시아세트산, 히드록시벤조산, 히드록시벤젠디카르복실산, 아미노아세트산, 아미노벤조산 등을 사용할 수도 있고, 이들을 혼합하여 사용해도 무방하다. 20-200 g / l of epichlorohydrin was dispersed by stirring in water / ethanol (80/20) mixture for 10-20 minutes, and aminobenzenedicarboxylic acid corresponding to the number of moles such as epichlorohydrin at 50-90 ° C. It is characterized by synthesizing the multifunctional processing agent by adding 5 to 10 times divided into 30 to 60 minutes and stirred for 1 to 4 hours. In this case, hydroxyacetic acid, hydroxybenzoic acid, hydroxybenzenedicarboxylic acid, aminoacetic acid, aminobenzoic acid, etc. may be used instead of aminobenzenedicarboxylic acid as functional group (F), and these may be mixed and used.
반응성 그룹(R)으로 트리클로로트리아진을 사용하여 기능성 그룹(F)에 해당되는 화합물과 반응시켜 다기능 가공제를 합성하는 경우;Using trichlorotriazine as the reactive group (R) to react with the compound corresponding to the functional group (F) to synthesize a multifunctional processing agent;
트리클로로트리아진 20～300g/l를 비이온계 계면활성제 1～5g/l를 이용하여 10～20분간 0～5℃의 물에 균일하게 분산시키고, 트리클로로트리아진과 같은 몰수에 해당되는 히드록시아세트산, 히드록시벤조산, 히드록시벤젠디카르복실산, 아미노아세트산, 아미노벤조산, 아미노벤젠디카르복실산 중의 한가지 화합물 또는 이들의 혼합물을 1～2시간에 걸쳐 5～10회 분할 투입한 후 0～60℃에서 30분～3시간 동안 교반하여 다기능 가공제를 합성하는 것을 특징으로 한다. 20 to 300 g / l of trichlorotriazine is uniformly dispersed in water of 0 to 5 ° C. for 10 to 20 minutes using 1 to 5 g / l of nonionic surfactant, and hydroxyacetic acid corresponding to the number of moles such as trichlorotriazine. , A compound of hydroxybenzoic acid, hydroxybenzenedicarboxylic acid, aminoacetic acid, aminobenzoic acid, aminobenzenedicarboxylic acid, or a mixture thereof in 5 to 10 times over 1 to 2 hours, followed by 0 to 60 It is characterized by synthesizing a multifunctional processing agent by stirring for 30 minutes to 3 hours at ℃.
반응성 그룹(R)으로 테트라클로로피리미딘을 사용하여 기능성 그룹(F)에 해 당되는 화합물과 반응시켜 다기능 가공제를 합성하는 경우;Using tetrachloropyrimidine as the reactive group (R) to react with the compound corresponding to the functional group (F) to synthesize a multifunctional processing agent;
테트라클로로피리미딘 20～300g/l를 비이온계 계면활성제 1～5g/l를 이용하여 10～20분간 20～40℃의 물에 균일하게 분산시키고, 테트라클로로피리미딘과 같은 몰수에 해당되는 히드록시아세트산, 히드록시벤조산, 히드록시벤젠디카르복실산, 아미노아세트산, 아미노벤조산, 아미노벤젠디카르복실산 중의 한가지 화합물 또는 이들의 혼합물을 30～60분간에 걸쳐 5～10회 분할 투입한 후 20～60℃에서 1～6시간 동안 교반하여 다기능 가공제를 합성하는 것을 특징으로 한다.20 to 300 g / l of tetrachloropyrimidine is uniformly dispersed in water of 20 to 40 ° C. for 10 to 20 minutes using 1 to 5 g / l of nonionic surfactant, and a hydrate corresponding to the number of moles such as tetrachloropyrimidine. One or a mixture of hydroxyacetic acid, hydroxybenzoic acid, hydroxybenzenedicarboxylic acid, aminoacetic acid, aminobenzoic acid, and aminobenzenedicarboxylic acid, or a mixture thereof, is added in portions of 5 to 10 times over 30 to 60 minutes. It is characterized by synthesizing a multifunctional processing agent by stirring for 1-6 hours at ~ 60 ℃.
상기한 다기능 가공제의 합성에 있어서 에피클로로히드린은 부가반응에 의해, 트리아진계 및 피리미딘계 화합물은 치환반응에 의해 F에 해당하는 화합물과 반응한다. 이때 알칼리는 촉매로 작용하므로 반응시 탄산나트륨 등의 알칼리를 첨가함으로써 반응을 촉진시킬 수 있다. 사용 가능한 알칼리로는 가성소다, 탄산나트륨, 과탄산나트륨, 아세트산나트륨 등이 있고, 알칼리를 첨가할 경우에는 기능성 그룹(F)에 해당되는 아미노벤젠디카르복실산 등의 0.5～1몰비에 해당하는 양을 0.5～2시간에 걸쳐 반응성 그룹(R) 분산액에 분할 투입한다. In the synthesis of the above-mentioned multifunctional processing agent, epichlorohydrin reacts with the compound corresponding to F by addition reaction and triazine-based and pyrimidine-based compounds by substitution reaction. In this case, since the alkali acts as a catalyst, the reaction may be promoted by adding an alkali such as sodium carbonate during the reaction. Examples of alkalis that can be used include caustic soda, sodium carbonate, sodium percarbonate, and sodium acetate. When alkali is added, an amount corresponding to 0.5 to 1 molar ratio of aminobenzene dicarboxylic acid, etc., corresponding to the functional group (F) is used. Split into reactive group (R) dispersion over 0.5 to 2 hours.
본 발명의 (A)단계에서 합성한 가공제는 합성액 그대로를 희석하여 섬유처리에 사용하거나 합성액을 침전, 여과, 건조, 분쇄 등의 과정을 거쳐 분말 상태로 만든 후 필요시 물에 다시 용해시켜 사용할 수 있다.The processing agent synthesized in step (A) of the present invention is diluted with a synthetic liquid and used for fiber treatment, or the synthetic liquid is made into a powder state through a process such as precipitation, filtration, drying and grinding, and then dissolved again in water if necessary. Can be used.
본 발명의 (A)단계에서 합성된 가공제는 반응성 그룹(R)과 기능성 그룹(F)으로 구성되어 있는데 기능성 그룹(F)에 의해 항균방취성, 소취성, 흡수성, 속건성, 흡습발열성, 자외선 차단성 등의 기능성이 발현된다. 기능성 그룹(F)은 친수성의 카르복실기와 강한 소수성 부분으로 되어있는데, 항균방취성, 소취성, 흡수성, 흡습발열성은 친수성의 카르복실기에 의해 발현되며, 속건성은 카르복실기에 의해 흡수된 물이 강한 소수성부분에 의해 섬유내부로 침투하지 못하고 섬유 표면을 따라 빠르게 확산됨으로써 발현된다. 또한 기능성 그룹(F)에 해당되는 아미노벤젠디카르복실산 등은 자외선 흡수가 가능한 공명구조로 되어 있기 때문에 자외선 차단성을 나타낸다. The processing agent synthesized in step (A) of the present invention is composed of a reactive group (R) and a functional group (F), but functional antibacterial, deodorant, absorbent, quick-drying, hygroscopic pyrogenic, Functionalities such as ultraviolet ray blocking properties are expressed. The functional group (F) is composed of a hydrophilic carboxyl group and a strong hydrophobic moiety. The antibacterial, deodorant, absorbent and hygroscopic exothermic properties are expressed by the hydrophilic carboxyl group, and the quick-drying property is a strong hydrophobic moiety in the water absorbed by the carboxyl group. It does not penetrate into the fiber and is rapidly diffused along the fiber surface. Moreover, since aminobenzene dicarboxylic acid etc. which correspond to a functional group (F) have a resonance structure which can absorb an ultraviolet-ray, it exhibits ultraviolet blocking property.
본 발명의 다기능 셀룰로오스 섬유제품의 제조에 있어서 (B)단계는 셀룰로오스 섬유, 슬라이버, 조사, 실, 직·편성물을 (A)단계에서 합성한 다기능 가공제로 처리하는 단계로, (A)단계에서 합성한 다기능 가공제 1～10% o.w.f., 탄산나트륨 5～20g/ℓ, 황산나트륨 50～200g/ℓ를 첨가하고, 40～80℃에서 액비 1:5～50으로 20～60분간 셀룰로오스 섬유를 처리한다.In the production of the multifunctional cellulose fiber product of the present invention, step (B) is a step of treating cellulose fibers, slivers, irradiation, yarns, and knitted fabrics with the multifunctional processing agent synthesized in step (A), and in step (A) 1-10% owf of the synthesized multifunctional processing agent, 5-20 g / l sodium carbonate, 50-200 g / l sodium sulfate are added, and the cellulose fiber is treated for 20 to 60 minutes at a liquid ratio of 1: 5 to 50 at 40 to 80 ° C.
또한 다기능제 10～100g/ℓ, 탄산나트륨 50～100g/ℓ, 황산나트륨 10～100g/ℓ로 구성된 패딩욕에서 직물 또는 편성물 등을 패딩하고 100～130℃에서 스팀 또는 건열처리하는 패드 드라이 큐어법을 사용해도 무방하다.In addition, the pad dry cure method is used to pad fabrics or knitted fabrics in a padding bath consisting of 10-100 g / l multifunctional agent, 50-100 g / l sodium carbonate and 10-100 g / l sodium sulfate and steam or dry heat at 100-130 ° C. It is okay.
또한, 본 발명의 다기능성 가공제는 섬유제품 중량대비 0.1 내지 5% o.w.f. 포함시키는 것이 바람직하다. 이때 다기능성 가공제의 함량이 0.1% o.w.f. 미만이면 효과가 미미하고 5% o.w.f. 이상이면 경제적인 측면에서 불리하다.In addition, the multifunctional processing agent of the present invention is 0.1 to 5% o.w.f. It is preferable to include. At this time, the content of the multifunctional processing agent is 0.1% o.w.f. Less than 5% o.w.f. The above is disadvantageous from an economic point of view.
본 발명의 다기능 셀룰로오스 섬유제품의 제조에 있어서 (C)단계는 다기능 가공제가 처리된 셀룰로오스 섬유에 금속을 도입하는 단계로 금속화합물을 30～60℃에서 처리하는 것에 의해 섬유제품 중량대비 20～10,000ppm의 금속을 다기능 가공제 처리 셀룰로오스 섬유에 도입하는 것이 가능하다. 이때 금속화합물의 함량이 20ppm 미만이면 효과가 미미하고 10,000ppm 이상이면 색상 및 경제적인 측면에서 불리하다. 금속 화합물로는 질산은, 황산아연, 황산구리 등을 사용할 수 있는데 이들 금속 화합물은 수용액 중에서 금속 이온으로 해리되어 다기능 셀룰로오스 섬유의 카르복실기에 의해 흡착된다. 흡착된 금속은 다기능 가공제와 착염을 형성하여 불용성이 되기 때문에 세탁 등에 의해서도 쉽게 탈락하지 않는다. In the production of the multifunctional cellulose fiber product of the present invention, step (C) is a step of introducing a metal into the cellulose fiber treated with the multifunctional processing agent by treating the metal compound at 30 to 60 ° C. to 20 to 10,000 ppm relative to the weight of the fiber product. It is possible to introduce the metal into the multifunctional processing agent treated cellulose fiber. In this case, if the content of the metal compound is less than 20ppm, the effect is insignificant, and if it is 10,000ppm or more, it is disadvantageous in terms of color and economics. As a metal compound, silver nitrate, zinc sulfate, copper sulfate, etc. can be used, These metal compounds dissociate with metal ion in aqueous solution, and are adsorbed by the carboxyl group of a multifunctional cellulose fiber. The adsorbed metal forms a complex salt with the multifunctional processing agent and becomes insoluble so that it is not easily eliminated by washing or the like.
본 발명의 다기능 셀룰로오스 섬유제품의 제조에 있어서 (C)단계는 항균방취성 및 소취성을 더욱 향상시키기 위한 것이므로 (C)단계를 거치지 않아도 무방하다.In the production of the multifunctional cellulose fiber product of the present invention, step (C) is to further improve the antibacterial and deodorizing properties, so it is not necessary to go through step (C).
본 발명의 다기능 셀룰로오스 섬유제품은 섬유, 슬라이버, 조사, 실, 직·편성물 등 어떤 형태로든 제조가 가능하며, 타 섬유와 혼용할 경우, 혼용하는 섬유의 종류, 혼용방법, 혼용률에 따라 여러 용도의 제품으로 응용할 수 있다.Multifunctional cellulose fiber products of the present invention can be manufactured in any form, such as fibers, slivers, irradiation, yarns, woven and knitted fabrics, and when mixed with other fibers, various uses depending on the type of mixed fibers, mixing method, mixing rate It can be applied as a product of.
본 발명의 다기능성 셀룰로오스 섬유제품은 하기 성능을 가지는 것을 특징으로 한다:The multifunctional cellulose fiber product of the present invention is characterized by having the following performance:
(1) 균감소율 90～100%(1) Germination reduction rate 90-100%
(2) 염기성 취기에 대한 소취율 90～100%(2) 90-100% deodorization rate for basic odor
(3) 흡수성 5～30% 향상(3) 5-30% improvement in absorbency
(4) 건조 시간 10～40% 단축(4) Reduced drying time by 10-40%
(5) 흡습발열성 0.5～2.0℃(RH 90%, 20℃)(5) Hygroscopic heat generation 0.5 ~ 2.0 ℃ (RH 90%, 20 ℃)
(6) 자외선 차단율 80～100%(6) UV protection rate 80 ~ 100%
상기에서 알 수 있는 바와 같이, 본 발명의 다기능 셀룰로오스 섬유제품의 항균성은 포도상구균 등에 대해 90～100%의 균감소율, 암모니아가스 등의 염기성 취기에 대해 90～100%의 소취율을 나타낸다. 흡수성은 미처리 면섬유에 비해 약 5～30% 증가하고 건조시간은 미처리 면섬유가 대략 80분인데 반해 45～70분으로 약 10～40% 정도 빠른 시간에 건조된다. 흡습발열성은 섬유가 수분을 흡수하면서 열을 발생하는 것으로 미처리 시료에 비해 0.5～2.0℃ 더 높다. 자외선 차단율은 미처리 면섬유가 약 60～75%인데 반해 다기능 셀룰로오스 섬유제품은 80～100% 이다. 상기한 다기능성 셀룰로오스 섬유제품의 기능성은 다기능 가공제의 처리 농도에 따라 성능에 차이가 나며 섬유나 슬라이버, 조사 등에 처리할 경우 다른 섬유와 혼용하여 사용할 수 있고, 이때 혼용율에 따라 성능에 차이가 나므로 최종 용도에 적합하도록 가공제 농도와 혼용률을 조절하여 사용할 수 있다.As can be seen from the above, the antimicrobial activity of the multifunctional cellulose fiber product of the present invention exhibits a reduction of 90 to 100% against Staphylococcus and the like, and a deodorization rate of 90 to 100% against basic odors such as ammonia gas. Absorbency is increased about 5 ~ 30% compared to untreated cotton fiber, and drying time is about 80 minutes while untreated cotton fiber is 45 ~ 70 minutes and dried about 10 ~ 40% faster. Hygroscopic pyrogenicity generates heat while the fiber absorbs moisture, which is 0.5 ~ 2.0 ℃ higher than untreated samples. UV protection rate is about 60-75% of untreated cotton fiber, whereas multi-functional cellulose fiber products are 80-100%. The functionality of the multifunctional cellulose fiber products varies in performance depending on the processing concentration of the multifunctional processing agent, and can be used in combination with other fibers when treating fibers, slivers, irradiation, etc., and the performance varies depending on the mixing ratio. Therefore, it is possible to adjust the processing agent concentration and mixing ratio to suit the end use.
또한, 본 발명의 셀룰로오스 섬유는 면 섬유 및 재생 셀룰로오스 섬유(레이온 및 라이오셀)등을 포함한다.The cellulose fibers of the present invention also include cotton fibers and regenerated cellulose fibers (rayon and lyocell).
이하, 구체적인 실시예 및 비교예를 가지고 본 발명의 구성 및 효과를 보다 상세히 설명한다. Hereinafter, the configuration and effects of the present invention will be described in more detail with specific examples and comparative examples.
[실시예 1～6 및 비교예 1][Examples 1 to 6 and Comparative Example 1]
비이온 계면활성제(Triton X-100) 0.5g이 들어 있는 5℃의 물 200ml에 트리클로로트리아진 7.38g을 넣고 10분간 교반하여 분산시켰다. 이 분산액에 아미노벤조산 5.49g과 가성소다 1.6g으로 구성된 50ml 수용액을 30분에 걸쳐 투입하고, 20℃로 승온하여 90분간 교반하는 방법으로 다기능 가공제를 합성하였다. 합성액에 염화나트륨 37.5g을 첨가하여 침전을 형성시킨 후 필터링한 다음 아세톤으로 수회 세척하여 미반응물을 제거하고 건조 및 분쇄하여 다기능 가공제 분말을 얻었다. 7.38 g of trichlorotriazine was added to 200 ml of 5 ° C. water containing 0.5 g of a nonionic surfactant (Triton X-100), followed by stirring for 10 minutes to disperse. A 50 ml aqueous solution composed of 5.49 g of aminobenzoic acid and 1.6 g of caustic soda was added to the dispersion over 30 minutes, and the multifunctional processing agent was synthesized by heating at 20 ° C. and stirring for 90 minutes. 37.5 g of sodium chloride was added to the synthetic solution to form a precipitate, which was then filtered and washed several times with acetone to remove unreacted material, and dried and pulverized to obtain a multifunctional processing powder.
정련한 면 편성물(Ne 30, 싱글저지)에 대해, 상기 다기능 가공제 2～5% o.w.f., 탄산나트륨 15g/l, 황산나트륨 50g/l를 첨가하고 40℃에서 액비 1:10으로 30분간 처리하여 실시예 1～5를 제조하였다. 이들 중 실시예 5에 대해서는 질산은 0.03g/l를 40℃에서 30분간 처리하여 은 200ppm을 도입하였다. 이들 시료에 대해 항균성, 소취성, 흡수성, 건조성, 흡습발열성을 시험하였으며 미처리 정련 면 편성물을 비교예로 표 1에 함께 나타내었다.To the refined cotton knitted fabric (Ne 30, single jersey), the above-mentioned multifunctional processing agent 2-5% owf, sodium carbonate 15g / l, sodium sulfate 50g / l was added and treated for 30 minutes at 40 ℃ liquid ratio 1:10 Example 1 to 5 were prepared. In Example 5, 200 ppm of silver was introduced by treating 0.03 g / l of silver nitric acid at 40 ° C for 30 minutes. These samples were tested for antimicrobial, deodorizing, absorbent, dry, and hygroscopic pyrogenic properties, and the untreated refined cotton knit was shown in Table 1 together as a comparative example.
항균성은 JIS 1902에 따라 포도상구균을 공시균으로 하여 시험하였으며 균감소율(%)로 나타내었다. The antimicrobial activity was tested according to JIS 1902 with Staphylococcus aureus and expressed as percentage reduction.
소취성은 암모니아 가스에 대해 검지관법으로 시험하였으며 2시간 뒤의 암모니아 가스 소취율(%)로 나타내었다.Deodorization was tested by a detection tube method for ammonia gas and expressed as ammonia gas deodorization rate (%) after 2 hours.
흡수성은 JIS L 1907의 바이렉법에 따라 측정하였다. Absorbency was measured according to the Bylek method of JIS L 1907.
건조성은 시료에 일정량의 수분을 가한 후 시간에 따른 확산성 잔류수분율(%)을 측정하여 잔류 수분량이 10% 미만일 때의 시간으로 나타내었다. The dryness was expressed as the time when the residual moisture content was less than 10% by measuring the diffusible residual water content (%) with time after adding a certain amount of water to the sample.
발열성은 RH 5%, 21℃의 조건하에 시료를 3시간 방치 후 RH 90%, 21℃의 조건에 노출시켜 흡습에 따른 시료 표면의 발열온도를 측정하였으며 미처리 시료와의 온도차로 나타내었다.The exothermicity of the sample was left for 3 hours under conditions of RH 5% and 21 ° C., and then exposed to conditions of RH 90% and 21 ° C. to determine the exothermic temperature of the sample surface due to moisture absorption.
자외선 차단성은 AATCC 183에 따라 시험하였으며 자외선 차단율로 나타내었다. UV protection was tested according to AATCC 183 and expressed as UV protection.
상기 표 1의 실시예 1～5 및 비교예 1의 결과에서 알 수 있듯이, 다기능 가공제 처리 면 편성물은 다기능 가공제 농도 및 은 함유 여부에 따라 다소 성능에 차이가 있으나, 균감소율 95～99.9%, 소취율 90～100%를 나타내었다. 또한 흡수성은 비교예 1에 비해 10～25% 더 향상되었고, 건조시간은 5～15분 더 빠른 것으로 나타났다. 흡습발열성은 0.4～1.2℃, 자외선 차단율은 80～99%인 것으로 나타났다. As can be seen from the results of Examples 1 to 5 and Comparative Example 1 of Table 1, the multifunctional processing agent-treated cotton knitted fabric has a difference in performance depending on the multifunctional processing agent concentration and silver content, but has a reduction ratio of 95 to 99.9%. The deodorization rate was 90 to 100%. In addition, the water absorption was improved by 10-25% more than in Comparative Example 1, the drying time was found to be 5-15 minutes faster. Hygroscopic heat generation was 0.4 ~ 1.2 ℃, UV blocking rate was 80 ~ 99%.
[실시예 6～10][Examples 6-10]
상기 실시예 1～5와 동일한 방법으로 합성한 다기능 가공제를 면섬유에 대해 다기능 가공제 5% o.w.f., 탄산나트륨 15g/l, 황산나트륨 50g/l을 첨가하고, 액비 1:10으로 40℃에서 30분간 처리하여 다기능 면섬유를 제조하였다. 제조한 다기능 면섬유를 미처리 면섬유(정련면)와 혼용하여 다기능 면/미처리면 혼방사(Ne 20)를 제조하였다(실시예 6～10). 이들의 항균성, 소취성, 흡수성, 건조성, 흡습발열성을 시험하여 표 2에 나타내었다. 이때 미처리면 100% 면사를 비교예 2로 함께 나타내었다. The multifunctional processing agent synthesized in the same manner as in Examples 1 to 5 was added to the cotton fiber 5% owf of the multifunctional processing agent, 15 g / l sodium carbonate, 50 g / l sodium sulfate, and treated at 40 ° C. for 30 minutes at a liquid ratio of 1:10. To prepare a multifunctional cotton fiber. A multifunctional cotton / untreated cotton blended yarn (Ne 20) was prepared by mixing the prepared multifunctional cotton fiber with an untreated cotton fiber (refined cotton) (Examples 6 to 10). Their antibacterial, deodorant, absorbent, dry, and hygroscopic pyrogenic properties were tested and shown in Table 2. The untreated cotton 100% cotton yarn is shown in Comparative Example 2.
상기 표 2의 실시예 6～10의 결과에서 알 수 있듯이, 다기능 면/미처리면 혼방사는 다기능 면섬유의 혼용률이 증가할 수록 기능성이 향상되었으며, 다기능면 함유율 40%에서 균감소율 95% 이상, 소취율 90% 이상, 흡수성 10% 이상 향상, 건조시간 10분 이상 단축, 흡습발열성 0.5 이상의 기능성을 나타내었다.As can be seen from the results of Examples 6 to 10 of Table 2, the multi-functional cotton / untreated cotton blended yarn improved functionality as the blending ratio of the multi-functional cotton fiber increased, the reduction rate of 95% or more at 40% of the multi-functional cotton content, deodorization rate At least 90%, absorbency improved by at least 10%, drying time is reduced by at least 10 minutes, hygroscopic exothermic ability of 0.5 or more.
이상에서 설명한 바와 같이, 본 발명에 의하면 셀룰로오스 섬유와 화학적 결합이 가능하며 항균방취성, 소취성, 흡수성, 속건성, 흡습발열성 및 자외선 차단성 등의 기능성이 우수한 다기능 가공제를 합성할 수 있고, 이 가공제를 흡진법 또는 패드 드라이 큐어법으로 처리하여 영구적인 내세탁성을 갖는 다기능 셀룰로오스 섬유제품을 제조할 수 있다.As described above, according to the present invention, it is possible to synthesize a multifunctional processing agent capable of chemically bonding with cellulose fibers and having excellent functionalities such as antibacterial deodorization, deodorization, absorbency, quick drying, hygroscopic pyrogenicity, and UV protection, This processing agent can be processed by the dust reduction method or the pad dry cure method to produce a multifunctional cellulose fiber product having permanent washing resistance.
또한 본 발명의 다기능 가공제는 섬유, 슬라이버, 조사, 실, 직·편성물 등 모든 형태의 셀룰로로스 섬유에 처리가 가능하기 때문에 다기능 셀룰로오스 섬유제품의 응용범위가 매우 넓다. In addition, the multifunctional processing agent of the present invention is capable of treating all types of cellulose fibers such as fibers, slivers, irradiation, yarns, woven fabrics, and knitted fabrics, so that the application range of the multifunctional cellulose fiber products is very wide.
위에서 본 발명이 실시 예로 상세하게 기술되었지만, 본 발명이 속하는 기술분야에 있어서 통상의 지식을 가진 사람이라면 첨부된 청구 범위에 정의된 본 발명의 정신 및 범위를 벗어나지 않으면서 본 발명을 여러 가지로 변형하여 실시할 수 있을 것이다. 상기와 같은 본 발명의 실시 예에 대한 변형에 의하여 본 발명의 범위가 제한되는 것은 아니다. Although the invention has been described above in detail by way of example, it will be understood that various modifications of the invention may be made by those of ordinary skill in the art without departing from the spirit and scope of the invention as defined in the appended claims. It can be done by. The scope of the present invention is not limited by the modifications to the embodiments of the present invention as described above.
Claims (5)