JPS616329A - Traveller for spinning machine - Google Patents
Traveller for spinning machineInfo
- Publication number
- JPS616329A JPS616329A JP12813984A JP12813984A JPS616329A JP S616329 A JPS616329 A JP S616329A JP 12813984 A JP12813984 A JP 12813984A JP 12813984 A JP12813984 A JP 12813984A JP S616329 A JPS616329 A JP S616329A
- Authority
- JP
- Japan
- Prior art keywords
- traveler
- steel wire
- ring
- traveller
- spinning machine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【発明の詳細な説明】
産業上の利用分野
本発明は耐摩耗性、耐熱性、耐蝕性でリングとの馴じみ
性の良好な紡機用トラベラに関するものである。DETAILED DESCRIPTION OF THE INVENTION Field of Industrial Application The present invention relates to a traveler for a spinning machine that has wear resistance, heat resistance, corrosion resistance, and good compatibility with a ring.
従来の技術及び発明が解決しようとする問題点従来の紡
機用トラベラは一般に硬鋼線又は合金鋼線材を用い、表
面硬化処理として焼入処理が行われ、その後ニッケルメ
ッキを行っているものもある。Conventional technology and problems to be solved by the invention Conventional spinning machine travelers generally use hard steel wire or alloy steel wire, are subjected to quenching treatment as a surface hardening treatment, and then nickel plating is applied in some cases. .
しかし、今日の紡績工場での過酷な操業条件の下では、
従来の紡績用トラベラでは耐摩耗性が不足し、早期に摩
耗を生じ、トラペラの走行が不安定で糸切れを多発した
9毛羽の発生が多く、トラペラが早期焼付き飛散し、更
にリングの寿命が短かくなるという欠点があった。However, under the harsh operating conditions in today's textile mills,
Conventional spinning travellers lack abrasion resistance, causing early wear, leading to unstable travel of the traveller, resulting in frequent yarn breakage, 9 fuzzing, premature seizure and scattering of the trapeller, and further shortening the lifespan of the ring. The disadvantage was that it was shorter.
このため、トラベ2の耐摩耗性を向上するため、トラペ
ラにクロムメッキを施したものが考えらnているが、ク
ロムメッキは硬度は高いがリングとの馴じみ性が悪く、
紡出初期において紡出張力が非常に高くなシ、糸切れが
多発したシ、あるいは、メッキ表面に亀裂が入シ易く、
これが剥離摩耗の原因となって、トラペ2が異常摩耗を
生じる原因となる等の欠点があった。For this reason, in order to improve the wear resistance of Trabe 2, it has been considered to chrome plate the trapella, but although chrome plating has high hardness, it does not fit well with the ring.
In the early stage of spinning, the spinning force is very high, the yarn breaks frequently, or the plating surface is prone to cracking.
This caused problems such as peeling and wear, which caused abnormal wear of the trapezoid 2.
問題点を解決するための手段
本発明は上記従来の紡機用トラベラの欠点を解消するも
のであり、硬鋼線又は合金鋼線より形成された紡機用ト
ラベラをイオン注入部と真空蒸着部とよりなるイオン蒸
着薄膜形成装置によシ、ほう素、アルミニウム、チタン
、シリコン、クローム、ニッケル等の金属を蒸気化して
リング表面に蒸着せしめると同時に窒素、炭素。Means for Solving the Problems The present invention solves the above-mentioned drawbacks of the conventional traveler for spinning machines. The ion evaporation thin film forming equipment vaporizes metals such as boron, aluminum, titanium, silicon, chromium, and nickel and deposits them on the ring surface while simultaneously vaporizing them with nitrogen and carbon.
リン等のイオンビームを照射し、窒化ほう素。Boron nitride is irradiated with an ion beam of phosphorus, etc.
債化アルミニウム、炭化ほう素、窒化チタン。Bonded aluminum, boron carbide, titanium nitride.
ニッケル、リン、炭化クローム等の均一な金属薄膜を少
なくともリングと接触するトラベラ表面に形成し、耐摩
耗性リングとの馴じみ性の向上並びに焼付き防止、トラ
ベラ飛散に寄与する紡機用トラベラを提供するものであ
る。We provide a traveler for spinning machines in which a uniform thin metal film of nickel, phosphorus, chromium carbide, etc. is formed at least on the surface of the traveler in contact with the ring, which improves compatibility with wear-resistant rings, prevents seizure, and prevents the traveler from scattering. It is something to do.
以下本発明の1実施例を図面に基づいて説明する。An embodiment of the present invention will be described below based on the drawings.
実施例1゜
硬鋼線材を第1図の如く所要形状の横形トラベラ】に形
成する。Example 1 A hard steel wire rod is formed into a horizontal traveler having a desired shape as shown in FIG.
イオン注入部と真空蒸着部とよシなるイオン蒸着薄膜形
成装置の真空容器内に装填し、電子衝撃蒸着によりチタ
ンを飛ばして該トラベラ表面に蒸着させると同時にイオ
ン注入装置より窒素イオンを照射して蒸着膜内に打込み
、リング7ランジと接触する表面に、厚さ2〜20μの
窒化チタン層gt−形成し、次に焼入れ処理後表面研摩
することによって本発明の紡機用トラベラを構成する。The ion implantation section and the vacuum evaporation section are loaded into a vacuum container of an ion evaporation thin film forming apparatus, and titanium is evaporated by electron impact evaporation and deposited on the surface of the traveler, and at the same time nitrogen ions are irradiated from the ion implantation apparatus. The traveler for a spinning machine of the present invention is constructed by implanting a titanium nitride layer gt into the deposited film, forming a titanium nitride layer gt with a thickness of 2 to 20 μm on the surface in contact with the ring 7 flange, and then hardening and polishing the surface.
なお、上記窒化チタン層2の処理層はトラベラ全表面に
施すこともできるが、ト2べ2の少なくともリングと接
触する表面に設ければよく、処理前にマスキング処理す
ることによp所要部に施すことができる。Note that the treated layer of the titanium nitride layer 2 can be applied to the entire surface of the traveler, but it is only necessary to provide it on at least the surface of the traveler 2 that comes into contact with the ring. It can be applied to
また、上記処理層は第2図に示す如く、トラベラ母材8
と処理層4の金属元素が界面近くで拡散により混在する
混合層5を形成し、金属元素が互に強力に結合して密着
性の非常にすぐれたものとなる。Further, as shown in FIG. 2, the treated layer is formed on the traveler base material 8
A mixed layer 5 is formed in which the metal elements of the treated layer 4 and the treated layer 4 are mixed together by diffusion near the interface, and the metal elements are strongly bonded to each other, resulting in extremely excellent adhesion.
本発明の紡機用トラベラは上記の如き構成よりなり、第
8図に示す如く本発明の紡機用トラベラAは表面硬度は
Hマス000〜4000 と従来の紡機用トラベラBよ
シ非常に高硬度でおるが摩擦係数は低く滑らかで、リン
グとのなじみか良好である。また、処理層と母材とは拡
散により接合し、密着性はメツΦや物理的蒸着よシより
優nたものt得ることができる。The traveler for a spinning machine according to the present invention has the above-mentioned configuration, and as shown in FIG. The friction coefficient is low and smooth, and it fits well with the ring. Further, the treated layer and the base material are bonded together by diffusion, and adhesion can be obtained that is superior to that obtained by bonding Φ or physical vapor deposition.
第4図は従来のニッケルメッキトラベラBと本発明の紡
機用トラベラAを用いて下記のテスト条件にて紡出した
場合のトラペラ焼は率の比較を示し、トラベラの焼は率
は3倍以上減少することが判る。Figure 4 shows a comparison of the trapera firing rate when spinning under the following test conditions using the conventional nickel-plated traveler B and the spinning machine traveler A of the present invention, and the traveler firing rate is more than three times as high. It can be seen that it decreases.
テスト条件
リング内径:45IIIJI
フ2/ジ巾:8.2ms
繊維;ポリエステル、綿45′8
スピンドル回転数:15000r、p、m) 5へ5
: ZS/hf 610なお、上記実施例においては
横形トラベラに適用した例を示したが、第5図の如く縦
形トラベラ6の少なくとも内面に窒化アルミニウム層7
を形成したシ、第6図の如くメタルインサートナイロン
トラベラ8のインサート部材9に窒化ほう素層10
i形成することによシ耐熱性。Test conditions Ring inner diameter: 45IIIJI Width: 8.2ms Fiber: Polyester, cotton 45'8 Spindle rotation speed: 15000r, p, m) 5 to 5
: ZS/hf 610 In the above embodiment, an example was shown in which the application was applied to a horizontal traveler, but as shown in FIG.
6, a boron nitride layer 10 is applied to the insert member 9 of the metal insert nylon traveler 8.
It is heat resistant due to its formation.
潤滑性が良好で耐摩耗性、耐寿命特性にすぐnた本発明
の紡機用トラベラを構成することが出来る。It is possible to construct a traveler for a spinning machine according to the present invention, which has good lubricity, wear resistance, and long life characteristics.
発明の効果
本発明の紡機用トラベラは硬鋼線又は合金鋼線よシ形成
された紡機用トラベラの少なくともリングと接触する表
面に母材との密着性のよい窒化チタン層を窒化ほう素層
、炭化シリコン層。Effects of the Invention The spinning machine traveler of the present invention is made of hard steel wire or alloy steel wire, and has a titanium nitride layer with good adhesion to the base material, a boron nitride layer, and a boron nitride layer on at least the surface that contacts the ring. silicon carbide layer.
窒化アルミニウム層等の処理層を形成しているため、耐
摩耗性、潤滑性、耐熱性及び耐蝕性にすぐれ長期にわた
りトラベラが安定した走行をし、リングとの馴じみ性が
良く、糸切れの多発を防止し、毛羽の発生を押えると共
にトラベラの寿命を著しく延長することが出来る。また
、窒化チタン層は耐蝕性の向上に寄与するため、難燃性
繊維の紡績に使用してもトラベラの発錆を防止すること
ができる等、優nた効果を有する発明である。Because it has a treated layer such as an aluminum nitride layer, it has excellent wear resistance, lubricity, heat resistance, and corrosion resistance, allowing the traveler to run stably over a long period of time, compatibility with the ring, and preventing thread breakage. It is possible to prevent frequent occurrence of fuzz, suppress the occurrence of fuzz, and significantly extend the life of the traveler. Furthermore, since the titanium nitride layer contributes to improving corrosion resistance, this invention has excellent effects such as being able to prevent rusting of the traveler even when used for spinning flame-retardant fibers.
第1図は本発明の1実施例を示す横形トラベラの断面図
、第2図は同金属薄膜処理層の説明断面図、第8図及び
第4図は本発明の紡機用トラベラと従来のトラベラとの
比較を示し、第8図は断面硬度分布曲線図、第4図はト
ラベラ焼は率曲線図、第5図及び第6図は各々本発明の
紡機用トラベラ他の実施例を示す断面図である。
】・・・・・・・・・横形トラベラ
2・・・・・・・・・窒化チタン層
8・・・・・・・・・母材
4・・・・・・・・処理層
5・・・・・・・・・混合層FIG. 1 is a sectional view of a horizontal traveler showing one embodiment of the present invention, FIG. 2 is an explanatory sectional view of the metal thin film treated layer, and FIGS. FIG. 8 is a cross-sectional hardness distribution curve diagram, FIG. 4 is a traveler yaki rate curve diagram, and FIGS. 5 and 6 are cross-sectional diagrams showing other embodiments of the traveler for spinning machines of the present invention. It is. ]...... Horizontal traveler 2... Titanium nitride layer 8... Base material 4... Processing layer 5.・・・・・・Mixed layer
Claims (2)
ラの少なくともリングと接触する部分の表面に、イオン
注入と真空蒸着法の併用による金属薄膜の密着層を形成
してなることを特徴とする紡機用トラベラ。(1) A traveler for a spinning machine made of hard steel wire or alloy steel wire is characterized by forming an adhesive layer of a thin metal film on the surface of at least the part that comes into contact with the ring by a combination of ion implantation and vacuum evaporation. A traveler for spinning machines.
ン、窒化チタン、炭化クロムである特許請求の範囲第1
項記載の紡機用トラベラ。(2) Claim 1, wherein the metal thin film is aluminum nitride, boron nitride, silicon carbide, titanium nitride, or chromium carbide.
A traveler for a spinning machine as described in Section 1.