JPS6011740B2 - ポリフツ化ビニリデンを硬質基体に接着させるための改良方法 - Google Patents
ポリフツ化ビニリデンを硬質基体に接着させるための改良方法Info
- Publication number
- JPS6011740B2 JPS6011740B2 JP52044176A JP4417677A JPS6011740B2 JP S6011740 B2 JPS6011740 B2 JP S6011740B2 JP 52044176 A JP52044176 A JP 52044176A JP 4417677 A JP4417677 A JP 4417677A JP S6011740 B2 JPS6011740 B2 JP S6011740B2
- Authority
- JP
- Japan
- Prior art keywords
- mastic
- adhering
- polyvinylidene fluoride
- pvf2
- hard substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
本発明はポリフッ化ビニリデン（以下、ＰＶＦ２と称す
る）の硬質基体への接着を改善する方法に関する。
る）の硬質基体への接着を改善する方法に関する。
ＰＶＦ２を硬質基体に接着させることが困難であること
は知られている。
は知られている。
ＰＶＦ２は、処理を施さない状態では、いかなる種類の
硬質基体にも接着させることが困難であり、特殊な処理
を施さない限り、接着剤はＰＶＦ２に接着しない。この
欠点を除去するために種々の解決方法が提案されている
が、特に、繊維のあるいはプラスチックフィルムの形の
中間層材料をＰＶＦ２に接着させて、この中間層材料に
よりＰＶＦ２と硬質基体とを接着させることが行われて
いる。この種の方法により多くの場合満足すべき結果が
得られるが、上記接着層は薄いフィルムの形で施されし
かも乾燥した状態では多かれ少かれ脆弱であり、また、
その伸張性は多くの場合少さいために、熱衝撃を反復し
て受けた場合、ＰＶＦ２が１℃当り１５〜１０×１０‐
５の大きな膨張率を有するので、上記方法においてはＰ
ＶＦ２が硬質基体から剥離する現象が認められる。本発
明は上記したごとにＰＶＦ２と硬質基体の剥離を防止し
、両者の接着をあらゆる点で完全なものにすることを目
的とする。本発明は、ＰＶＦ２を硬質基体に接着させる
ための中間層材料と該硬質基体との間に、膨張率の相違
により生ずる弊害を防止するのに十分な程度の可榛性を
有するマスチツク（ｍａｓｔｉｃ）を設けることからな
る。このマスチックは、その場で重合させる物質であっ
てかつ、ＰＶＦ２を硬質基体に接着させるための中間層
材料と該硬質基体の両方に接着する物質からなることを
特徴とする。その場で重合させる物質は、重合後に下記
の物理的性質を有するものであることが好ましい三ショ
アーＡ硬度 ２０〜９０引張強さ
４〜７０ｋｇノの破断伸び
１〜１０００％上記物質を重合させる前に、２６０
において１０００センチポィズから、加圧下での押出加
工を必要とする揺変性ペーストの鋼度までの粘度を有し
得る、その構成成分からなる複合物質を、ＰＶＦ２接着
用中間層材料と、場合により予備処理された硬質基体の
間に施す。
硬質基体にも接着させることが困難であり、特殊な処理
を施さない限り、接着剤はＰＶＦ２に接着しない。この
欠点を除去するために種々の解決方法が提案されている
が、特に、繊維のあるいはプラスチックフィルムの形の
中間層材料をＰＶＦ２に接着させて、この中間層材料に
よりＰＶＦ２と硬質基体とを接着させることが行われて
いる。この種の方法により多くの場合満足すべき結果が
得られるが、上記接着層は薄いフィルムの形で施されし
かも乾燥した状態では多かれ少かれ脆弱であり、また、
その伸張性は多くの場合少さいために、熱衝撃を反復し
て受けた場合、ＰＶＦ２が１℃当り１５〜１０×１０‐
５の大きな膨張率を有するので、上記方法においてはＰ
ＶＦ２が硬質基体から剥離する現象が認められる。本発
明は上記したごとにＰＶＦ２と硬質基体の剥離を防止し
、両者の接着をあらゆる点で完全なものにすることを目
的とする。本発明は、ＰＶＦ２を硬質基体に接着させる
ための中間層材料と該硬質基体との間に、膨張率の相違
により生ずる弊害を防止するのに十分な程度の可榛性を
有するマスチツク（ｍａｓｔｉｃ）を設けることからな
る。このマスチックは、その場で重合させる物質であっ
てかつ、ＰＶＦ２を硬質基体に接着させるための中間層
材料と該硬質基体の両方に接着する物質からなることを
特徴とする。その場で重合させる物質は、重合後に下記
の物理的性質を有するものであることが好ましい三ショ
アーＡ硬度 ２０〜９０引張強さ
４〜７０ｋｇノの破断伸び
１〜１０００％上記物質を重合させる前に、２６０
において１０００センチポィズから、加圧下での押出加
工を必要とする揺変性ペーストの鋼度までの粘度を有し
得る、その構成成分からなる複合物質を、ＰＶＦ２接着
用中間層材料と、場合により予備処理された硬質基体の
間に施す。
ついでその場で重合反応を行わせる；加熱操作がＰＶＦ
２の膨張率と硬質基体の膨張率の相違と両立するという
条件で、重合反応を促進するために、場合により、前記
複合物質を加熱し得る。複合物質は任意既知の方法によ
り接着されるべき面の間に導入される。複合物質は、そ
の粘度が注入可能な程度である場合には単に注入するこ
とができ、また加圧して注入することができる。重合性
物質の量は「マスチツクの最終の厚さが１肋〜２０伽と
なるような量であることが好ましい。
２の膨張率と硬質基体の膨張率の相違と両立するという
条件で、重合反応を促進するために、場合により、前記
複合物質を加熱し得る。複合物質は任意既知の方法によ
り接着されるべき面の間に導入される。複合物質は、そ
の粘度が注入可能な程度である場合には単に注入するこ
とができ、また加圧して注入することができる。重合性
物質の量は「マスチツクの最終の厚さが１肋〜２０伽と
なるような量であることが好ましい。
本発明において使用し得るマスチックとしては、ポリウ
レタンが好ましい。
レタンが好ましい。
この種の物質は当業者には周知のものであり、ポリィソ
シアネートとポリオールとを触媒の存在下または不存在
下で反応させることにより得られる。本発明においては
、空気または水分の不存在下でも重合する多成分系原料
から得られたポリウレタンを使用することが特に好まし
い。これらのポリウレタンは、ワン‐ショット法により
、すなわちポリィソシアネートとポリオールをその場で
反応させることにより、あるいはポリイソシアネートと
ポリオールとを反応させて得られる、遊離のィソシアネ
ート官能基を含有するプレボリマーと、ポリオールとを
反応させることにより得られる。トルェンジィソシアネ
ートおよびジフエニルメタンジイソシアネートが特に適
当なポリィソシアネ−トである。ポリウレタンを製造す
るのに通常使用されるポリオールとしては、エチレンオ
キシドおよび／またはプロピレンオキシドから誘導され
る、２〜６、好ましくは２〜３の官能性（血ｎｃｔｉｏ
ｎａｌｉツ）と４００〜６０００、好ましくは２０００
〜４５００の分子量を有するポリアルコールが特に興味
のあるものである。触媒、発泡剤、充填剤、顔料のごと
きポリウレタン用の慣用の種々の助剤を既知の条件下で
原料成分に添加することができる。本発明は、ＰＶＦ２
と、膨張率がＰＶＦ２と実質的に異る硬質基体との接着
性を強化するのに特に興味のある方法である：硬質基体
は、金属またはプラスチック基体あるいはコンクリート
、場合によっては木材でもあり得る。本発明の方法は、
形状が多少不規則であるために、慣用の方法によっては
その表面の全ての点においてはＰＶＦ２を完全に接着さ
せることのできないタンク内にＰＶＦ２を内張りするの
に特に適している。後記本発明の実施例において使用さ
れるポリウレタンマスチックの原料成分の、ポリオール
に基づく組成を下表に示す。
シアネートとポリオールとを触媒の存在下または不存在
下で反応させることにより得られる。本発明においては
、空気または水分の不存在下でも重合する多成分系原料
から得られたポリウレタンを使用することが特に好まし
い。これらのポリウレタンは、ワン‐ショット法により
、すなわちポリィソシアネートとポリオールをその場で
反応させることにより、あるいはポリイソシアネートと
ポリオールとを反応させて得られる、遊離のィソシアネ
ート官能基を含有するプレボリマーと、ポリオールとを
反応させることにより得られる。トルェンジィソシアネ
ートおよびジフエニルメタンジイソシアネートが特に適
当なポリィソシアネ−トである。ポリウレタンを製造す
るのに通常使用されるポリオールとしては、エチレンオ
キシドおよび／またはプロピレンオキシドから誘導され
る、２〜６、好ましくは２〜３の官能性（血ｎｃｔｉｏ
ｎａｌｉツ）と４００〜６０００、好ましくは２０００
〜４５００の分子量を有するポリアルコールが特に興味
のあるものである。触媒、発泡剤、充填剤、顔料のごと
きポリウレタン用の慣用の種々の助剤を既知の条件下で
原料成分に添加することができる。本発明は、ＰＶＦ２
と、膨張率がＰＶＦ２と実質的に異る硬質基体との接着
性を強化するのに特に興味のある方法である：硬質基体
は、金属またはプラスチック基体あるいはコンクリート
、場合によっては木材でもあり得る。本発明の方法は、
形状が多少不規則であるために、慣用の方法によっては
その表面の全ての点においてはＰＶＦ２を完全に接着さ
せることのできないタンク内にＰＶＦ２を内張りするの
に特に適している。後記本発明の実施例において使用さ
れるポリウレタンマスチックの原料成分の、ポリオール
に基づく組成を下表に示す。
表中の数字は重量部である。実施例 １
分子量２５００のポリオキシプロピレングリコールとト
ルェンジイソシアネートとを９０午○で３時間反応させ
て得られた、ＮＣＯ末端基を有するかつＮＣＯ／ＯＨ比
が約２．２のプレポリマーと前記成分Ａとを混合した。
ルェンジイソシアネートとを９０午○で３時間反応させ
て得られた、ＮＣＯ末端基を有するかつＮＣＯ／ＯＨ比
が約２．２のプレポリマーと前記成分Ａとを混合した。
上記２種の成分は、プレポリマーのＮＣＯ／成分ＡのＯ
Ｈ＝１．２０となる割合で混合した。上記混合物を、直
径１．２ｈ、長さ３ｈで半球形の底部を有する鋼製タン
クの壁面と、該鋼製タンクの形状と全く同−であるが該
タンクより寸法が僅かに小さい、深なべ形容器の形状を
有する、厚さ４帆のＰＶＦ２の内張の表面との間に注入
した。鋼製タンクは、予めその内面をシランプライマリ
イ（ＡＰ１３４，ＵＮＩＯＮＣＡＲＢＩＤＥ社製）で被
覆した。ＰＶＦ２表面に、ジメチルホルムアミド中にＰ
ＶＦ２を溶解させた２０％溶液を２０ｏｏで塗布し、塗
布されたＰＶＦ２表面にガラスマットを施しついでこの
複合体を１５０午０で２０分間暁付けることにより、Ｐ
ＶＦ２に予めガラスマットを被覆した。鋼製タンクの内
壁とＰＶＦ２の外面との間隙は、平均１物肋であるが、
ある部分では２仇肌を越えており、また他の部分ではわ
ずか１伽程度である。
Ｈ＝１．２０となる割合で混合した。上記混合物を、直
径１．２ｈ、長さ３ｈで半球形の底部を有する鋼製タン
クの壁面と、該鋼製タンクの形状と全く同−であるが該
タンクより寸法が僅かに小さい、深なべ形容器の形状を
有する、厚さ４帆のＰＶＦ２の内張の表面との間に注入
した。鋼製タンクは、予めその内面をシランプライマリ
イ（ＡＰ１３４，ＵＮＩＯＮＣＡＲＢＩＤＥ社製）で被
覆した。ＰＶＦ２表面に、ジメチルホルムアミド中にＰ
ＶＦ２を溶解させた２０％溶液を２０ｏｏで塗布し、塗
布されたＰＶＦ２表面にガラスマットを施しついでこの
複合体を１５０午０で２０分間暁付けることにより、Ｐ
ＶＦ２に予めガラスマットを被覆した。鋼製タンクの内
壁とＰＶＦ２の外面との間隙は、平均１物肋であるが、
ある部分では２仇肌を越えており、また他の部分ではわ
ずか１伽程度である。
ＰＶＦ２からなる内部容器は重合を行う間、加圧した袋
により所定の位置に保持した。重合反応は約２０００で
２少時間行った。実施例 ２実施例１と同一のタンクの
内側に、前記成分Ｂと実施例１のプレポリマ−をＮＣＯ
／ＯＨ比が１．２０となるような割合で混合して得られ
る髭変性混合物を、ヘラにより、約１０〜２０肋の厚さ
に被覆した。
により所定の位置に保持した。重合反応は約２０００で
２少時間行った。実施例 ２実施例１と同一のタンクの
内側に、前記成分Ｂと実施例１のプレポリマ−をＮＣＯ
／ＯＨ比が１．２０となるような割合で混合して得られ
る髭変性混合物を、ヘラにより、約１０〜２０肋の厚さ
に被覆した。
１時間後、全体が鋼製タンクと同一の形状を有するが、
それより僅かに寸法の小さい深なべ形の、厚さ３肌のＰ
ＶＦ２の内張をタンク内に挿入した。
それより僅かに寸法の小さい深なべ形の、厚さ３肌のＰ
ＶＦ２の内張をタンク内に挿入した。
このＰＶＦ２の内張は重合を行う間、加圧した袋により
所定の位置に保持した。重合は、約２０午○で２独特間
行った。ＰＶＦ２製内張は、タンク内に挿入する前に、
中性極性溶剤中のポリウレタンの溶液を塗布しついで溶
剤を除去することにより、その外面をポリウレタンで被
覆した。
所定の位置に保持した。重合は、約２０午○で２独特間
行った。ＰＶＦ２製内張は、タンク内に挿入する前に、
中性極性溶剤中のポリウレタンの溶液を塗布しついで溶
剤を除去することにより、その外面をポリウレタンで被
覆した。
この予備処理により、ＰＶＦ２とマスチツクの接着がよ
り良好になった。実施例 ３ 前記成分Ｃと実施例１のプレポリマーとをＮＣＯ／ＯＨ
比が１．２０となる割合で混合した。
り良好になった。実施例 ３ 前記成分Ｃと実施例１のプレポリマーとをＮＣＯ／ＯＨ
比が１．２０となる割合で混合した。
Claims (1)
- 【特許請求の範囲】 １ ポリフツ化ビニリデンを硬質基体に接着させるため
の中間層材料と上記硬質基体との間に、下記のマスチツ
ク、すなわち、その場で重合させる物質からなり、かつ
、ポリフツ化ビニリデンを硬質基体に接着させるための
前記中間層材料と該硬質基体の両者に接着ししかも膨張
率の相違により生ずる弊害を防止するのに十分な程度の
可撓性を有するマスチツクを設けることを特徴とする、
ポリフツ化ビニリデンを硬質基体に接着させるための改
良方法。 ２ マスチツクが、つぎの物理的性質、すなわち、 ２
０〜９０のシヨアーＡ硬度 ４〜７０ｋｇ／ｃｍ＾２の引張強さ １〜１０００％の破断点伸び を有する、特許請求の範囲第１項記載の方法。 ３ マスチツクの厚さが１ｍｍ〜２０ｃｍである特許請
求の範囲第１項記載の方法。 ４ マスチツクがポリウレタンである、特許請求の範囲
第１項記載の方法。 ５ ポリウレタンを、ポリイソシアネートと、エチレン
オキシドおよび（または）プロピレンオキシドから誘導
された、２〜６の官能性と４００〜６０００の分子量と
を有するポリアルコールとをその場で反応させることに
よって製造する、特許請求の範囲第４項記載の方法。 ６ ポリイソシアネートがトルエンジイソシアネートで
ある特許請求の範囲第５項記載の方法。 ７ ポリイソシアネートが、誘離のイソシアネート官能
基を有するかつポリイソシアネートとポリオールとを反
応させて得られたプレポリマーである、特許請求の範囲
第５項記載の方法。