JPS5894406A - Manufacture of aggregate decorative veneer - Google Patents

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.

Description

【発明の詳細な説明】 （１）発明の目的 集成化粧単板、特に杉杢のような孤立島杢を表現する化
粧単板を製造する場合の接着不良を無くし、孤立島杢を
忠実に表現することを目的とする。Detailed Description of the Invention (1) Purpose of the Invention To eliminate adhesion defects when manufacturing laminated decorative veneers, especially decorative veneers that express isolated island heather such as Japanese cedar, and faithfully express isolated island heather. The purpose is to

（２）背景技術 集成化粧単板の製造において、たとえば杉杢における型
形状の概略は、第１図のようであった。(2) Background Art In the production of decorative veneers, for example, the outline of the mold shape for cedar wood is as shown in FIG.

第１図ビ）は雄型１の斜視図、（ロ）は前面図、ｆ’Ｍ
は側面図である＠これらの図の示すよう番と型の略中央
部２が特に盛り上った凸状を示す３次元形状の雄型を用
いる。勿論この雄型に対応する雌型と対になって７リツ
チ成形用型版をなしている。Figure 1 B) is a perspective view of male type 1, (B) is a front view, f'M
1 is a side view. As shown in these figures, a three-dimensional male mold is used in which the substantially central portion 2 of the mold has a particularly raised convex shape. Of course, this male die is paired with a corresponding female die to form a 7-rich molding die.

ところで、従来前記のような型版を用いて、フリッチを
得ようとしても、型周囲にほとんどの圧力が加わり、型
中央部には圧力がかからず、その結果接着不良が発生し
ていた。また前記型の中央部において孤島杢を表現しよ
うとしても、充分忠実性ある杢が得られないのであった
。By the way, conventionally, when trying to obtain a flitch using the above-mentioned mold plate, most of the pressure was applied to the periphery of the mold, and no pressure was applied to the center of the mold, resulting in poor adhesion. Furthermore, even if an attempt was made to express isolated island heather in the center of the mold, a sufficiently faithful heather could not be obtained.

〔発明の開示〕[Disclosure of the invention]

本発明は積層圧締に供する単板を、その周囲を予め圧縮
処理を施こして用い、かつ化粧単板の島杢部分に対応す
る部分に孔を穿けた単板を適当枚数挾んで積層圧締する
ことを特徴とする。以下杉を例に挙げて詳しく説明する
。The present invention uses veneers to be subjected to lamination pressing, the periphery of which has been compressed in advance, and an appropriate number of veneers with holes drilled in the areas corresponding to the island areas of the decorative veneer are sandwiched and laminated. It is characterized by tightening. This will be explained in detail below using cedar as an example.

一般に杉の集成単板は、原木丸太からロータリーレスに
よりロータリー単板を得て、これを脱色、ついで染色、
以下乾燥、色１転写、積層圧締（フリッチ化）、スライ
スの工程を順次経て製造されている。し−し、この積層
圧締工程−こより、型の形状によりフリッチ内部へ応力
分布が発生し、特に２次元形状に３いてさえ、型中央部
に圧力不足が発生し、それがスライスしたときの接着不
足につながっていた。また、第２図番こ示すような杉杢
の孤立島杢（第２図の３）表現に右いてはその部分に特
に圧力不足が生じ易い。そこで本発明においては、全て
の原料単板の周囲を予め圧縮して座屈させて使用するよ
うｋしたのである。これは第３図の斜線を施こした部分
で示されている。また、ξれら単板について、例えば１
０枚に１枚の割合で中央部に、すなわち集成化粧単板の
孤立島杢相当部分に孔５をあけておくのである。このよ
うにしてフリッチを造ると、中央部に充分圧力がかかり
接着不良のないフリッチが得られ、かつ杉孤立島杢表現
が可能となったのである。In general, laminated cedar veneers are obtained by obtaining rotary veneers from raw wood logs using a rotaryless process, which is then bleached and then dyed.
The product is manufactured through the following steps: drying, color 1 transfer, lamination pressing (flitching), and slicing. However, due to this lamination pressing process, stress distribution occurs inside the flitch due to the shape of the mold, and in particular, even in a two-dimensional shape, a lack of pressure occurs in the center of the mold, which causes problems when slicing. This led to insufficient adhesion. Furthermore, in the case of an isolated island of cedar heather (3 in Fig. 2) as shown in Fig. 2, a lack of pressure is particularly likely to occur in that part. Therefore, in the present invention, the periphery of all raw material veneers is compressed and buckled in advance before use. This is shown by the shaded area in FIG. In addition, for ξ these veneers, for example, 1
A hole 5 is drilled in the center of every 0 sheets, that is, in a portion corresponding to an isolated island of the laminated decorative veneer. By making the flitch in this way, sufficient pressure was applied to the center, making it possible to obtain a flitch without any adhesion defects, and also to make it possible to express isolated cedar islands and heather.

【図面の簡単な説明】[Brief explanation of drawings]

第１図は従来より用いられている３次元型板の雄型を示
す図であり、（イ）は斜視図、（０）は正面図−ＨＧ！
側面図であり、第２図は杉孤立島杢を例示する平面図、
第３図は本発明で用いる単板の平面図である。 ３・・・・・・・・・・・孤立島杢 ４・・・・・・・・・・・圧縮麩理部 ５・・・・・・・・・・・孔 特許出動人 松下電工株式会社 代理人弁理士　　竹　元　敏　丸 （ほか２名） 第１図 （ロ） （７す 第２図　　　　　　　゛ 第３図FIG. 1 is a diagram showing a male mold of a conventionally used three-dimensional template, where (A) is a perspective view and (0) is a front view - HG!
It is a side view, and FIG. 2 is a plan view illustrating isolated cedar island heather.
FIG. 3 is a plan view of the veneer used in the present invention. 3・・・・・・・・・・・Isolated island heather 4・・・・・・・・・・・Compression processing department 5・・・・・・・・・・・Pentee patent dispatcher Matsushita Electric Works Co., Ltd. Company Representative Patent Attorney Toshimaru Takemoto (and 2 others) Figure 1 (B) (7th Figure 2 Figure 3)

Claims (1)

【特許請求の範囲】[Claims] （１）三次元凸形状の型面を有する雄型、およびこれに
対応する雌型を用いて単板を積層圧締してフリッチを造
り、ついてこれをスライスして板目島杢を表現する集成
化粧単板の製法であって、積層圧締に供する単板をその
周囲を予め圧縮処理を施こして用い、かつ化粧単板の島
杢部分に対応する部分に孔を穿けた単板を適当枚数挾ん
で積層圧締することを特徴とする集成化粧単板の製法。(1) Using a male mold with a three-dimensional convex mold surface and a corresponding female mold, veneers are laminated and pressed to create a flitch, which is then sliced to express the Itamejima heather. A method for producing laminated decorative veneer, in which the veneer to be laminated and pressed is compressed around the periphery of the veneer in advance, and holes are drilled in the areas corresponding to the island areas of the decorative veneer. A method for producing laminated decorative veneer, which is characterized by sandwiching an appropriate number of sheets and laminating them and pressing them together.