JPH09291224A - Pigment-dispersed resin solution composition, its production and color filter - Google Patents
Pigment-dispersed resin solution composition, its production and color filterInfo
- Publication number
- JPH09291224A JPH09291224A JP10513196A JP10513196A JPH09291224A JP H09291224 A JPH09291224 A JP H09291224A JP 10513196 A JP10513196 A JP 10513196A JP 10513196 A JP10513196 A JP 10513196A JP H09291224 A JPH09291224 A JP H09291224A
- Authority
- JP
- Japan
- Prior art keywords
- pigment
- component
- resin solution
- acid
- dispersed resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、カラーペースト、
樹脂ブラック・マトリクス用ペーストなどに用いられる
顔料分散樹脂溶液組成物およびカラーフィルターに関す
るものであり、さらに詳しくは、ポリアミック酸を使用
した顔料分散樹脂溶液組成物および、該顔料分散樹脂溶
液組成物を使用した液晶表示素子や撮像素子のカラーフ
ィルタに関するものである。TECHNICAL FIELD The present invention relates to a color paste,
The present invention relates to a pigment-dispersed resin solution composition and a color filter used for a resin black matrix paste, and more specifically, to a pigment-dispersed resin solution composition using a polyamic acid and the pigment-dispersed resin solution composition. The present invention relates to a color filter of the liquid crystal display device or the image pickup device.
【０００２】[0002]
【従来の技術】耐熱性、耐光性に優れたカラーフィルタ
ーを形成することのできるカラーペーストとして、ポリ
アミック酸の溶液に顔料を分散したカラーぺーストが知
られている（たとえば特開昭６０―１８４２０２号公
報、特開昭６０―１８４２０３号公報、特開昭６１―１
８０２０３号公報）。2. Description of the Related Art As a color paste capable of forming a color filter having excellent heat resistance and light resistance, a color paste in which a pigment is dispersed in a solution of polyamic acid is known (for example, JP-A-60-184202). JP, JP-A-60-184203, JP-A-61-1
No. 80203).
【０００３】また、ポリアミック酸の溶液に顔料を分散
したカラーぺーストを使用したカラーフィルターの製造
は、たとえば特開昭６０―２４７６０３号公報や特開昭
６１―７７８０４号公報に示されているように、次のよ
うな工程により行なわれる。The production of a color filter using a color paste in which a pigment is dispersed in a solution of polyamic acid is disclosed, for example, in JP-A-60-247603 and JP-A-61-77804. Then, the following steps are performed.
【０００４】まず、カラーぺースト（たとえば緑色）を
基板上に塗布した後、乾燥してポリイミド前駆体着色被
膜を形成する。ポリイミド前駆体着色被膜上にポジ型フ
ォトレジストを塗布し、フォトレジスト被膜を形成す
る。該フォトレジスト被膜上にマスクを置き、露光装置
を用いて紫外線を照射する。露光後、ポジ型フォトレジ
スト用アルカリ現像液により、フォトレジスト被膜とポ
リイミド前駆体着色被膜のエッチングを同時に行う。エ
ッチング後、不要となったフォトレジスト被膜を剥離す
る。その後、加熱処理することによって、ポリイミド前
駆体をポリイミドに変換する。このようにして、１色の
ポリイミド着色被膜のパターンを基板上に形成した後、
その上に別な色（たとえば赤色）のカラーぺーストを塗
布し、同様の工程を経て、２色のポリイミド着色被膜の
パターンを基板上に形成する。これをもう一度繰り返す
と、赤、青、緑の３色のポリイミド着色被膜のパターン
が得られる。First, a color paste (green, for example) is applied on a substrate and then dried to form a polyimide precursor colored film. A positive photoresist is applied on the polyimide precursor colored film to form a photoresist film. A mask is placed on the photoresist film and irradiated with ultraviolet light using an exposure device. After the exposure, the photoresist coating and the polyimide precursor colored coating are simultaneously etched with an alkaline developer for a positive photoresist. After the etching, the unnecessary photoresist film is removed. After that, the polyimide precursor is converted into polyimide by heat treatment. In this way, after forming the pattern of the polyimide colored coating film of one color on the substrate,
A color paste of another color (for example, red) is applied thereon, and a pattern of a two-color polyimide colored coating film is formed on the substrate through the same steps. When this is repeated once again, a pattern of three colored polyimide coatings of red, blue and green is obtained.
【０００５】以上のような工程によりカラーフィルター
の形成に用いられるポリアミック酸の溶液に顔料を分散
したカラーペーストにおいては、顔料の分散性がカラー
フィルターの性能に大きな影響を与える。しかしなが
ら、該カラーペーストにおいては、顔料を安定に分散さ
せることが非常に難しく、顔料の凝集を生じやすい。そ
のため、該カラーペーストを用いたカラーフィルターに
おいては、顔料の凝集に起因する基板上への塗布膜の平
滑性低下、顔料粒子の光散乱に起因する画素のコントラ
スト比低下などカラーフィルターの性能上の問題があっ
た。In the color paste in which the pigment is dispersed in the solution of polyamic acid used for forming the color filter by the above steps, the dispersibility of the pigment has a great influence on the performance of the color filter. However, in the color paste, it is very difficult to stably disperse the pigment, and the pigment easily aggregates. Therefore, in the color filter using the color paste, the smoothness of the coating film on the substrate is reduced due to the aggregation of the pigment, and the contrast ratio of the pixel is reduced due to the light scattering of the pigment particles. There was a problem.
【０００６】[0006]
【発明が解決しようとする課題】本発明は、かかる従来
技術の欠点に鑑み創案されたもので、その目的とすると
ころは、カラーペーストや樹脂ブラック・マトリクス用
ペーストなどに用いられる顔料分散樹脂溶液組成物にお
いて、無機酸成分を含有させることにより、顔料の分散
安定性の向上した顔料分散樹脂溶液組成物とその製造方
法および液晶表示素子や撮像素子などに使用され得る該
顔料分散樹脂溶液組成物を使用したカラーフィルターを
提供せんとすることである。SUMMARY OF THE INVENTION The present invention was devised in view of the above-mentioned drawbacks of the prior art. The object of the present invention is to provide a pigment-dispersed resin solution used for color paste, resin black matrix paste, etc. In the composition, by containing an inorganic acid component, a pigment-dispersed resin solution composition having improved pigment dispersion stability, a method for producing the same, and a pigment-dispersed resin solution composition that can be used in a liquid crystal display device, an imaging device, or the like Is to provide a color filter using.
【０００７】[0007]
【課題を解決するための手段】かかる本発明の目的は、
顔料成分、ポリアミック酸成分、溶媒成分および酸成分
を含有してなる顔料分散樹脂溶液組成物において、酸成
分として無機酸を含有することを特徴とする顔料分散樹
脂溶液組成物により達成される。SUMMARY OF THE INVENTION The object of the present invention is as follows.
A pigment-dispersed resin solution composition comprising a pigment component, a polyamic acid component, a solvent component and an acid component, which is characterized by containing an inorganic acid as an acid component.
【０００８】[0008]
【発明の実施の形態】以下、本発明を詳細に説明する。BEST MODE FOR CARRYING OUT THE INVENTION The present invention will be described in detail below.
【０００９】本発明におけるポリアミック酸としては、
テトラカルボン酸とジアミンを選択的に組み合わせ、こ
れらを溶媒中で反応させたものを挙げることができる。
この時、ジアミンとテトラカルボン酸二無水物の混合比
により、得られるポリアミック酸の重合度を調節するこ
とができる。As the polyamic acid in the present invention,
An example is one in which tetracarboxylic acid and diamine are selectively combined and reacted in a solvent.
At this time, the degree of polymerization of the resulting polyamic acid can be adjusted by the mixing ratio of the diamine and the tetracarboxylic dianhydride.
【００１０】このほか、テトラカルボン酸ジクロライド
とジアミンを溶媒中で反応させて、その後、塩酸と溶媒
を除去することによってポリアミック酸を得るなど、ポ
リアミック酸を得るには種々の方法がある。しかし、本
発明はその合成法によらず、全てのポリアミック酸に対
して適用が可能である。In addition to this, there are various methods for obtaining a polyamic acid, such as reacting a tetracarboxylic acid dichloride with a diamine in a solvent and then removing hydrochloric acid and the solvent to obtain a polyamic acid. However, the present invention can be applied to all polyamic acids regardless of the synthetic method.
【００１１】本発明のペーストに使用するポリアミック
酸は、膜となった場合、ポリイミドに変換される。ポリ
イミド膜の力学的特性は、分子量が大きいほど良好であ
る。The polyamic acid used in the paste of the present invention is converted into polyimide when it is formed into a film. The higher the molecular weight, the better the mechanical properties of the polyimide film.
【００１２】このため、ポリイミド前駆体であるポリア
ミック酸の分子量も大きいことが望まれる。一方、ポリ
イミド前駆体膜を湿式エッチングによりパターン加工を
行う場合、ポリアミック酸の分子量が大きすぎると、現
像に要する時間が長くなりすぎるという問題がある。し
たがって、構造単位の繰り返し数の好ましい範囲は１０
〜１０００、より好ましくは１２〜４００、さらに好ま
しくは１５〜１００である。なお、ポリアミック酸の分
子量には一般にばらつきがあるため、ここでいう構造単
位の繰り返し数の好ましい範囲とは、この範囲の中に全
ポリアミック酸の５０モル％以上、好ましくは７０モル
％以上、さらに好ましくは９０モル％以上が入っている
ことを意味する。Therefore, it is desired that the polyamic acid, which is a polyimide precursor, also has a large molecular weight. On the other hand, when performing pattern processing on the polyimide precursor film by wet etching, if the molecular weight of the polyamic acid is too large, there is a problem that the time required for development becomes too long. Therefore, the preferred range of the number of repeating structural units is 10
To 1000, more preferably 12 to 400, and still more preferably 15 to 100. Since the molecular weight of the polyamic acid generally varies, the preferable range of the number of repeating structural units here is 50 mol% or more, preferably 70 mol% or more of the total polyamic acid within this range, and It preferably means that 90 mol% or more is contained.
【００１３】ポリアミック酸の原料として一般的に使用
し得るテトラカルボン酸の例としては、たとえばピロメ
リット酸二無水物、３，３´，４，４´―ベンゾフェノ
ンテトラカルボン酸二無水物、３，４，９，１０―ペリ
レンテトラカルボン酸二無水物、３，３´，４，４´―
ジフェニルスルホンテトラカルボン酸二無水物、４，４
´―オキシジフタル酸無水物、３，３´，４，４´―ビ
フェニルテトラカルボン酸二無水物、１，２，５，６―
ナフタレンテトラカルボン酸二無水物、３，３´，４，
４´―パラターフェニルテトラカルボン酸二無水物、
３，３´，４，４´―メタ―フェニルテトラカルボン酸
二無水物、１，２，３，４―シクロブタンテトラカルボ
ン酸二無水物、１，２，３，４―シクロペンタンテトラ
カルボン酸二無水物、１，２，３，５―シクロペンタン
テトラカルボン酸二無水物、１，２，４，５―ビシクロ
ヘキセンテトラカルボン酸二無水物、１，２，４，５―
シクロヘキサンテトラカルボン酸二無水物、１，３，３
ａ，４，５，９ｂ―ヘキサヒドロ―５―（テトラヒドロ
―２，５―ジオキソ―３―フラニル）―ナフト［１，２
―Ｃ］フラン―１，３―ジオンなどを挙げることができ
る。なお、本発明は、これらに限定されずテトラカルボ
ン酸二無水物が２種以上用いられても構わない。Examples of the tetracarboxylic acid that can be generally used as a raw material for the polyamic acid include, for example, pyromellitic dianhydride, 3,3 ', 4,4'-benzophenone tetracarboxylic dianhydride, 3,3'. 4,9,10-perylenetetracarboxylic dianhydride, 3,3 ', 4,4'-
Diphenyl sulfone tetracarboxylic acid dianhydride, 4,4
′ -Oxydiphthalic anhydride, 3,3 ′, 4,4′-biphenyltetracarboxylic dianhydride, 1,2,5,6-
Naphthalenetetracarboxylic dianhydride, 3,3 ', 4
4'-paraterphenyltetracarboxylic dianhydride,
3,3 ′, 4,4′-meta-phenyltetracarboxylic dianhydride, 1,2,3,4-cyclobutanetetracarboxylic dianhydride, 1,2,3,4-cyclopentanetetracarboxylic dianhydride Anhydride, 1,2,3,5-cyclopentanetetracarboxylic dianhydride, 1,2,4,5-bicyclohexenetetracarboxylic dianhydride, 1,2,4,5-
Cyclohexane tetracarboxylic dianhydride, 1,3,3
a, 4,5,9b-Hexahydro-5- (tetrahydro-2,5-dioxo-3-furanyl) -naphtho [1,2
-C] Furan-1,3-dione and the like can be mentioned. The present invention is not limited to these, and two or more tetracarboxylic dianhydrides may be used.
【００１４】また一般に使用できるジアミンの具体的な
例として例えば、エチレンジアミン、１，３―ジアミノ
シクロヘキサン、１，４―ジアミノシクロヘキサン、
４，４´―ジアミノ―３，３´―ジメチルジシクロヘキ
シルメタン、４，４´―ジアミノ―３，３´―ジメチル
ジシクロヘキシル、４，４´―ジアミノジフェニルエー
テル、４，４´―ジアミノジフェニルメタン、３，３´
―ジアミノジフェニルメタン、４，４´―ジアミノジフ
ェニルサルファイド、ｐ―フェニレンジアミン、２，４
―ジアミノトルエン、２，５―ジアミノトルエン、２，
６―ジアミノトルエン、ベンジジン、３，３´―ジメチ
ルベンジジン、３，３´―ジメトキシベンジジン、ｏ―
トリジン、４，４´―ジアミノターフェニル、１，５―
ジアミノナフタレン、３，３´―ジメチル―４，４´―
ジアミノジフェニルメタン、４，４´―ビス （４―ア
ミノフェノキシ）ビフェニル、２，２―ビス［４―（４
―アミノフェノキシ）フェニル］プロパン、ビス［４―
（４―アミノフェノキシ）フェニル］エーテルなどを挙
げることができる。なお、本発明は、これらに限定され
ずジアミンが２種以上用いられても構わない。Specific examples of diamines that can be generally used include ethylenediamine, 1,3-diaminocyclohexane, 1,4-diaminocyclohexane,
4,4'-diamino-3,3'-dimethyldicyclohexylmethane, 4,4'-diamino-3,3'-dimethyldicyclohexyl, 4,4'-diaminodiphenyl ether, 4,4'-diaminodiphenylmethane, 3,3 ´
-Diaminodiphenylmethane, 4,4'-diaminodiphenyl sulfide, p-phenylenediamine, 2,4
-Diaminotoluene, 2,5-diaminotoluene, 2,
6-diaminotoluene, benzidine, 3,3'-dimethylbenzidine, 3,3'-dimethoxybenzidine, o-
Trisine, 4,4'-diaminoterphenyl, 1,5-
Diaminonaphthalene, 3,3'-dimethyl-4,4'-
Diaminodiphenylmethane, 4,4'-bis (4-aminophenoxy) biphenyl, 2,2-bis [4- (4
-Aminophenoxy) phenyl] propane, bis [4-
(4-aminophenoxy) phenyl] ether and the like can be mentioned. The present invention is not limited to these, and two or more diamines may be used.
【００１５】本発明におけるポリアミック酸とは、ポリ
アミック酸の脱水反応が進行し生じたポリイミドを含有
するものも含む。The polyamic acid in the present invention also includes those containing a polyimide produced by the progress of the dehydration reaction of the polyamic acid.
【００１６】本発明における溶媒成分として用いられる
溶媒には、特に限定はしないが、樹脂成分が溶解する溶
媒が好ましい。また溶媒成分は１種類の溶媒から成ると
は限らず、多種類の溶媒が混合されていても構わない。
好ましい溶媒成分としては、例えば非プロトン性極性溶
媒を挙げることができる。非プロトン性極性溶媒の具体
的な例としては、例えばＮ―メチル―２―ピロリドン、
Ｎ，Ｎ―ジメチルアセトアミド、Ｎ，Ｎ―ジメチルホル
ムアミド、β―プロピオラクトン、γ―ブチロラクト
ン、γ―バレロラクトン、δ―バレロラクトン、γ―カ
プロラクトン、ε―カプロラクトンなどを挙げることが
でき、さらに好ましくはＮ―メチル―２―ピロリドン、
Ｎ，Ｎ―ジメチルアセトアミド、Ｎ，Ｎ―ジメチルホル
ムアミド、γ―ブチロラクトンなどを挙げることができ
る。さらに好ましくはＮ―メチル―２―ピロリドン、γ
―ブチロラクトンを挙げることができる。また、これら
の溶媒とともに、エタノール、メタノール、プロパノー
ル、ブタノール、３―メチル―３―メトキシブタノール
などのアルコール類、メチルセロソルブ、エチルセロソ
ルブ、メチルカルビトール、エチルカルビトール、プロ
ピレングリコールモノエチルエーテルなどのエチレング
リコールあるいはプロピレングリコール誘導体、あるい
は、プロピレングリコールモノエチルエーテルアセテー
ト、アセト酢酸エチル、メチル―３―メトキシプロピオ
ネート、３―メチル―３―メトキシブチルアセテートな
どの脂肪族エステル類などを副溶媒として添加すること
も可能である。The solvent used as the solvent component in the present invention is not particularly limited, but a solvent in which the resin component is dissolved is preferable. Further, the solvent component is not limited to be composed of one kind of solvent, and a plurality of kinds of solvents may be mixed.
Examples of preferable solvent components include aprotic polar solvents. Specific examples of the aprotic polar solvent include, for example, N-methyl-2-pyrrolidone,
Examples thereof include N, N-dimethylacetamide, N, N-dimethylformamide, β-propiolactone, γ-butyrolactone, γ-valerolactone, δ-valerolactone, γ-caprolactone and ε-caprolactone, and more preferred. Is N-methyl-2-pyrrolidone,
Examples thereof include N, N-dimethylacetamide, N, N-dimethylformamide and γ-butyrolactone. More preferably N-methyl-2-pyrrolidone, γ
-Butyrolactone can be mentioned. In addition to these solvents, alcohols such as ethanol, methanol, propanol, butanol, 3-methyl-3-methoxybutanol and the like, ethylene such as methyl cellosolve, ethyl cellosolve, methyl carbitol, ethyl carbitol and propylene glycol monoethyl ether. Glycol or propylene glycol derivative, or aliphatic ester such as propylene glycol monoethyl ether acetate, ethyl acetoacetate, methyl-3-methoxypropionate, and 3-methyl-3-methoxybutylacetate is added as a sub solvent. It is also possible.
【００１７】本発明における顔料成分として用いられる
顔料には特に制限はないが、耐光性、耐熱性、耐薬品性
に優れたものが好ましい。本発明において使用し得る顔
料の具体的な例をカラーインデックス（ＣＩ）ナンバー
で示す。黄色顔料の例としてはピグメントイエロー２
０、２４、８３、８６、９３、９４、１０９、１１０、
１１７、１２５、１３７、１３８、１３９、１４７、１
４８、１５３、１５４、１６６、１７３などが挙げられ
る。橙色顔料の例としてはピグメントオレンジ１３、３
１、３６、３８、４０、４２、４３、５１、５５、５
９、６１、６４、６５などが挙げられる。赤色顔料の例
としてはピグメントレッド９、９７、１２２、１２３、
１４４、１４９、１６６、１６８、１７７、１８０、１
９２、２１５、２１６、２２４などが挙げられる。紫色
顔料の例としてはピグメントバイオレット１９、２３、
２９、３２、３３、３６、３７、３８などが挙げられ
る。青色顔料の例としてはピグメントブルー１５（１
５：３、１５：４、１５：６など）、２１、２２、６
０、６４などが挙げられる。緑色顔料の例としてはピグ
メントグリーン７、１０、３６、４７などが挙げられ
る。黒色顔料の代表的な例としてはピグメントブラック
７などが挙げられる。なお本発明における黒色顔料に
は、カーボンブラックや、酸化チタン、四酸化鉄などの
金属酸化物粉、および金属硫化物粉や、金属粉なども含
む。とくにカーボンブラックは、遮光性に優れ遮光剤と
して樹脂ブラック・マトリックス用ペーストに使用でき
る。カーボンブラックは、チャネルブラック、ローラー
ブラック、ディスクブラックと呼ばれているコンタクト
法で製造されたもの、ガスファーネストブラック、オイ
ルファーネストブラックと呼ばれているファーネスト法
で製造されたもの、サーマルブラック、アセチレンブラ
ックと呼ばれているサーマル法で製造されたものなどを
用いることができるが、とくに、チャネルブラック、ガ
スファーネストブラック、オイルファーネストブラック
が好ましい。遮光剤としてカーボンブラックを使用する
場合、色調を無彩色とするため、カーボンブラックの補
色の顔料を混合することが好ましい。補色用の顔料とし
ては、青色顔料、および、紫色顔料を、それぞれ単独
で、あるいは、両者を混合して使用することができる。The pigment used as the pigment component in the present invention is not particularly limited, but those having excellent light resistance, heat resistance and chemical resistance are preferable. Specific examples of pigments that can be used in the present invention are shown by color index (CI) numbers. Pigment Yellow 2 is an example of a yellow pigment.
0, 24, 83, 86, 93, 94, 109, 110,
117, 125, 137, 138, 139, 147, 1
48, 153, 154, 166, 173 and the like. Pigment Orange 13 and 3 are examples of orange pigments.
1, 36, 38, 40, 42, 43, 51, 55, 5
9, 61, 64, 65 and the like. Examples of red pigments include Pigment Red 9, 97, 122, 123,
144, 149, 166, 168, 177, 180, 1
92, 215, 216, 224 and the like. Examples of purple pigments include pigment violet 19, 23,
29, 32, 33, 36, 37, 38 and the like. Examples of blue pigments include Pigment Blue 15 (1
5: 3, 15: 4, 15: 6, etc.), 21, 22, 6
0, 64 and the like. Pigment green 7, 10, 36, 47 etc. are mentioned as an example of a green pigment. Pigment Black 7 is a typical example of the black pigment. The black pigment in the present invention includes carbon black, metal oxide powder such as titanium oxide and iron tetroxide, metal sulfide powder, and metal powder. In particular, carbon black has excellent light-shielding properties and can be used as a light-shielding agent in resin black matrix pastes. Carbon black is produced by the contact method called channel black, roller black, disc black, gas farnested black, farnested oil called farnested black, and thermal black. , Those produced by a thermal method called acetylene black, and the like can be used, and channel black, gas furnace nest black, and oil furnace nest black are particularly preferable. When carbon black is used as the light-shielding agent, it is preferable to mix a pigment having a complementary color of carbon black in order to make the color tone achromatic. As the complementary color pigment, a blue pigment and a purple pigment may be used alone or in combination of both.
【００１８】本発明における顔料成分としてはこれらの
顔料に限定されずに種々の顔料を混合して使用すること
ができる。なお、顔料は必要に応じて、ロジン処理、酸
性基処理、塩基性基処理などの表面処理が施されている
ものを使用してもよい。The pigment component in the present invention is not limited to these pigments, and various pigments can be mixed and used. The pigment may be subjected to surface treatment such as rosin treatment, acidic group treatment and basic group treatment, if necessary.
【００１９】また、本発明の顔料分散樹脂溶液組成物を
カラーフィルターに使用する場合、カラーフィルターの
Ｒ（レッド）、Ｇ（グリーン）、Ｂ（ブルー）の３色の
画素は、ＣＲＴ蛍光体の色度特性に類似させる必要があ
るため、顔料をバックライトと液晶表示素子の光線透過
特性に合うよう、数色組み合わせて調色されて用いられ
る。たとえば、Ｒ（レッド）は赤色顔料と黄色顔料また
は橙色顔料、Ｇ（グリーン）は緑色顔料と黄色顔料また
は橙色顔料、Ｂ（ブルー）は青色顔料と紫色顔料の組み
合わせなどにより調色される。When the pigment-dispersed resin solution composition of the present invention is used for a color filter, the three color pixels of R (red), G (green) and B (blue) of the color filter are CRT phosphors. Since it is necessary to make the pigments have similar chromaticity characteristics, the pigments are combined and used in several colors so as to match the light transmission characteristics of the backlight and the liquid crystal display element. For example, R (red) is toned by a combination of a red pigment and a yellow pigment or an orange pigment, G (green) is toned by a combination of a green pigment and a yellow pigment or an orange pigment, and B (blue) is toned by a combination of a blue pigment and a violet pigment.
【００２０】本発明における無機酸とは、炭素以外の非
金属元素、または炭素を含まない酸基が水素と結合して
できた酸および炭酸のことをいう。The inorganic acid in the present invention means an acid and carbonic acid formed by bonding a non-metal element other than carbon or a carbon-free acid group with hydrogen.
【００２１】本発明における無機酸としては特に限定は
しないが、その具体的な例を挙げると、硫酸、亜硫酸、
チオ硫酸、塩酸、トリチオ炭酸、硝酸、亜硝酸、炭酸、
過塩素酸、次亜塩素酸、亜塩素酸、リン酸、亜リン酸、
次亜リン酸、ピロリン酸、トリリン酸、テトラリン酸、
トリメタリン酸、テトラメタリン酸、次リン酸、ペルオ
キシモノリン酸、セレン酸、亜セレン酸、シアン酸、フ
ッ酸、、よう化水素酸、過よう素酸、ホウ酸、次ホウ酸
などを挙げることができる。好ましくはリン原子を含有
するものでありその具体例としてリン酸、亜リン酸、次
亜リン酸、ピロリン酸、トリリン酸、テトラリン酸、ト
リメタリン酸、テトラメタリン酸、次リン酸、ペルオキ
シモノリン酸を挙げることができ、より好ましくはリン
酸である。The inorganic acid in the present invention is not particularly limited, but specific examples thereof include sulfuric acid, sulfurous acid,
Thiosulfate, hydrochloric acid, trithiocarbonate, nitric acid, nitrous acid, carbonic acid,
Perchloric acid, hypochlorous acid, chlorous acid, phosphoric acid, phosphorous acid,
Hypophosphorous acid, pyrophosphoric acid, triphosphoric acid, tetraphosphoric acid,
Examples include trimetaphosphoric acid, tetrametaphosphoric acid, hypophosphoric acid, peroxymonophosphoric acid, selenic acid, selenious acid, cyanic acid, hydrofluoric acid, hydroiodic acid, periodic acid, boric acid, hypoboric acid, and the like. it can. Phosphoric acid, phosphorous acid, hypophosphorous acid, pyrophosphoric acid, triphosphoric acid, tetraphosphoric acid, trimetaphosphoric acid, tetrametaphosphoric acid, hypophosphoric acid, peroxymonophosphoric acid as a specific example preferably containing a phosphorus atom. Of these, phosphoric acid is more preferable.
【００２２】本発明における無機酸の添加量としては特
に限定はしないが、好ましくはポリマ重量に対し０．０
５〜１０重量％であり、より好ましくは０．０５〜５重
量％であり、さらに好ましくは０．１〜３重量％であ
る。なお添加量は、添加する酸の種類、ペースト中の溶
媒、ポリマの種類などにより異なり、その系に適した量
だけ添加するのが望ましい。必要以上に多量に添加する
と、ペースト中で顔料が凝集したり、カラーフィルター
などに加工した際に、含有不純物としてカラーディスプ
レーに悪影響をもたらす可能性がある。また少なすぎる
と効果がない。The amount of the inorganic acid added in the present invention is not particularly limited, but is preferably 0.0 based on the weight of the polymer.
It is 5 to 10% by weight, more preferably 0.05 to 5% by weight, and further preferably 0.1 to 3% by weight. The addition amount varies depending on the type of acid to be added, the solvent in the paste, the type of polymer, etc., and it is desirable to add only an amount suitable for the system. If added in an excessively large amount, the pigment may agglomerate in the paste, or when processed into a color filter or the like, it may adversely affect the color display as a contained impurity. If it is too small, it has no effect.
【００２３】無機酸の添加方法としては特に限定はしな
いが、好ましくはその系の溶媒の一つで希釈し酸溶液を
作った後に添加するのが好ましい。The method of adding the inorganic acid is not particularly limited, but it is preferable to add it after diluting it with one of the solvents of the system to prepare an acid solution.
【００２４】本発明の顔料分散樹脂組成物の製造として
は特に限定はしないが、好ましい例を次に述べる。例え
ば顔料成分、ポリアミック酸成分および溶媒成分を含有
してなる顔料分散樹脂溶液に、無機酸または無機酸およ
び溶媒成分を含有する酸溶液を添加する方法、顔料成分
および溶媒成分を含有してなる顔料分散液に、無機酸、
ポリアミック酸成分および溶媒成分を含有してなる樹脂
溶液を添加する方法、顔料成分、ポリアミック酸成分お
よび溶媒成分を含有してなる顔料分散樹脂溶液に、無機
酸成分、ポリアミック酸成分および溶媒成分を含有して
なる樹脂溶液を添加する方法などである。これら製造方
法の選択については、顔料成分、溶媒成分、酸成分の種
類により、適宜、適当なものを選ぶことが好ましい。The production of the pigment-dispersed resin composition of the present invention is not particularly limited, but preferable examples will be described below. For example, a method of adding an inorganic acid or an acid solution containing an inorganic acid and a solvent component to a pigment dispersion resin solution containing a pigment component, a polyamic acid component and a solvent component, a pigment containing the pigment component and a solvent component Inorganic acid,
Method of adding a resin solution containing a polyamic acid component and a solvent component, a pigment component, a pigment dispersion resin solution containing a polyamic acid component and a solvent component, containing an inorganic acid component, a polyamic acid component and a solvent component And a method of adding a resin solution obtained by Regarding the selection of these production methods, it is preferable to select an appropriate one depending on the types of the pigment component, the solvent component and the acid component.
【００２５】本発明においては、樹脂溶液や溶媒中へ顔
料の分散方法は特に限定せず、ボールミル、サンドグラ
インダー、３本ロールミル、高速度衝撃ミルなど、種々
の方法がとり得る。In the present invention, the method of dispersing the pigment in the resin solution or the solvent is not particularly limited, and various methods such as a ball mill, a sand grinder, a three roll mill and a high speed impact mill can be used.
【００２６】本発明の顔料分散樹脂組成物には、塗布
性、着色被膜の乾燥性の改良、あるいは、顔料の分散性
を良好にする目的で界面活性剤を添加することもでき
る。界面活性剤の添加量は通常、顔料分散樹脂組成物全
重量の０．００５〜１重量％、好ましくは０．０１〜
０．５重量％である。界面活性剤の具体例としては、ラ
ウリル硫酸アンモニウム、ポリオキシエチレンアルキル
エーテル硫酸トリエタノールアミンなどの陰イオン界面
活性剤、ステアリルアミンアセテート、ラウリルトリメ
チルアンモニウムクロライドなどの陽イオン界面活性
剤、ラウリルジメチルアミンオキサイド、ラウリルカル
ボキシメチルヒドロキシエチルイミダゾリウムベタイン
などの両性界面活性剤、ポリオキシエチレンラウリルエ
ーテル、ポリオキシエチレンステアリルエーテル、ソル
ビタンモノステアレートなどの非イオン界面活性剤など
が挙げられ、フッ素化炭化水素を有する非イオン界面活
性剤が特に好ましい。また界面活性剤は２種以上を混合
しても良い。界面活性剤の添加は、顔料の分散工程中ま
たはその工程の前後のどの時点でも行うことができる。
しかし、添加の時点により顔料の分散性が変わる場合が
あるので、注意を要する。A surfactant may be added to the pigment-dispersed resin composition of the present invention for the purpose of improving coatability, drying property of a colored film, or improving pigment dispersibility. The addition amount of the surfactant is usually 0.005 to 1% by weight, preferably 0.01 to 1% by weight based on the total weight of the pigment-dispersed resin composition.
0.5% by weight. Specific examples of the surfactant, ammonium lauryl sulfate, anionic surfactants such as polyoxyethylene alkyl ether sulfate triethanolamine, stearylamine acetate, cationic surfactants such as lauryltrimethylammonium chloride, lauryldimethylamine oxide, Amphoteric surfactants such as lauryl carboxymethyl hydroxyethyl imidazolium betaine, nonionic surfactants such as polyoxyethylene lauryl ether, polyoxyethylene stearyl ether, sorbitan monostearate, etc., and non-ionic surfactants having fluorinated hydrocarbons. Ionic surfactants are particularly preferred. Further, two or more kinds of surfactants may be mixed. The surfactant can be added at any point during or before or after the pigment dispersion step.
However, care must be taken since the dispersibility of the pigment may change depending on the time of addition.
【００２７】本発明におけるカラーフィルターは、任意
の色数向で各色別に所望のパターン状に設けられた着色
層からなる画素を有するカラーフィルタにおいて、該着
色層が本発明の顔料分散樹脂組成物から得られるポリマ
着色被膜であることを特徴とするものである。The color filter of the present invention is a color filter having pixels each having a colored layer provided in a desired pattern for each color in an arbitrary number of colors, wherein the colored layer comprises the pigment-dispersed resin composition of the present invention. It is characterized in that it is a polymer colored coating film obtained.
【００２８】本発明の顔料分散樹脂組成物を基板上に塗
布する方法としては、スピンコーター、バーコーター、
ブレードコーター、ロールコーター、ダイコーター、ス
クリーン印刷法などで基板に塗布する方法、基板を溶液
中に浸漬する方法、溶液を基板に噴霧するなどの種々の
方法を用いることができる。基板としては通常、ソーダ
ガラス、無アルカリガラス、ホウケイ酸ガラス、石英ガ
ラスなどの透明基板や、シリコン、ガリウム―ひ素など
の半導体基板などが用いられるが、特にこれらに限定さ
れない。As a method for applying the pigment-dispersed resin composition of the present invention onto a substrate, a spin coater, a bar coater,
Various methods such as a blade coater, a roll coater, a die coater, a method of coating the substrate by a screen printing method, a method of immersing the substrate in a solution, and a method of spraying the solution on the substrate can be used. As the substrate, a transparent substrate such as soda glass, non-alkali glass, borosilicate glass, or quartz glass, or a semiconductor substrate such as silicon or gallium-arsenic is usually used, but the substrate is not particularly limited thereto.
【００２９】なお、基板上に顔料樹脂溶液組成物を塗布
する場合、シランカップリング剤、アルミニウムキレー
ト剤、チタニウムキレート剤などの接着助剤で基板表面
を処理しておくと、着色被膜と基板の接着力を向上させ
ることができる。When the pigment resin solution composition is applied on the substrate, if the surface of the substrate is treated with an adhesion aid such as a silane coupling agent, an aluminum chelating agent, or a titanium chelating agent, the colored film and the substrate can be treated. The adhesive strength can be improved.
【００３０】本発明の顔料樹脂溶液組成物は、液晶ディ
スプレイや撮像素子のカラーフィルターのほか、光学素
子の遮光膜、光ファイバーの被覆膜などに用いられる。
たとえば、光ファイバーを顔料樹脂溶液組成物を用いて
着色被膜で被覆したものは、高温下での光学センサーと
して利用することができる。The pigment resin solution composition of the present invention is used for a color filter of a liquid crystal display or an image pickup device, a light-shielding film of an optical element, a coating film of an optical fiber and the like.
For example, an optical fiber coated with a colored film using a pigment resin solution composition can be used as an optical sensor under high temperature.
【００３１】次に本発明の顔料樹脂溶液組成物を用いた
カラーフィルターの製造方法の一例を説明する。Next, an example of a method for producing a color filter using the pigment resin solution composition of the present invention will be described.
【００３２】顔料樹脂溶液組成物を、前記のような方法
で透明基板上に塗布した後、風乾、加熱乾燥、真空乾燥
などにより、ポリイミド前駆体着色被膜を形成する。加
熱乾燥の場合、オーブン、ホットプレートなどを使用
し、５０〜１８０℃の範囲で１分〜３時間行うのが好ま
しい。次に、このようにして得られたポリイミド前駆体
着色被膜に、通常の湿式エッチングによりパターンを形
成する。まず、ポリイミド前駆体着色被膜上にポジ型フ
ォトレジストを塗布し、フォトレジスト被膜を形成す
る。続いて該フォトレジスト被膜上にマスクを置き、露
光装置を用いて紫外線を照射する。露光後、ポジ型フォ
トレジスト用アルカリ現像液により、フォトレジスト被
膜とポリイミド前駆体着色被膜のエッチングを同時に行
う。エッチング後、不要となったフォトレジスト被膜を
剥離する。The pigment resin solution composition is applied onto the transparent substrate by the method described above, and then the polyimide precursor colored film is formed by air drying, heat drying, vacuum drying or the like. In the case of heat drying, it is preferable to use an oven, a hot plate or the like, and to perform the heating in the range of 50 to 180 ° C. for 1 minute to 3 hours. Next, a pattern is formed on the thus obtained polyimide precursor colored film by ordinary wet etching. First, a positive photoresist is applied on the polyimide precursor colored film to form a photoresist film. Subsequently, a mask is placed on the photoresist film, and ultraviolet rays are irradiated using an exposure device. After the exposure, the photoresist coating and the polyimide precursor colored coating are simultaneously etched with an alkaline developer for a positive photoresist. After the etching, the unnecessary photoresist film is removed.
【００３３】ポリイミド前駆体着色被膜は、その後、加
熱処理することによって、ポリイミド着色被膜に変換さ
れる。加熱処理は通常、空気中、窒素雰囲気中、あるい
は、真空中などで、１５０〜４５０℃、好ましくは１８
０〜３５０℃の温度のもとで、０．５〜５時間、連続的
または段階的に行われる。The polyimide precursor colored film is then converted into a polyimide colored film by heat treatment. The heat treatment is usually performed at 150 to 450 ° C., preferably at 18 ° C. in air, nitrogen atmosphere, or vacuum.
It is performed continuously or stepwise at a temperature of 0 to 350 ° C. for 0.5 to 5 hours.
【００３４】以上の工程をＲ（レッド）、Ｇ（グリー
ン）、Ｂ（ブルー）の３色の顔料樹脂溶液組成物および
必要に応じて樹脂ブラック・マトリクス用黒色顔料樹脂
溶液組成物について行うと、カラーフィルターが作製で
きる。When the above steps are carried out for a pigment resin solution composition of three colors of R (red), G (green) and B (blue) and, if necessary, a black pigment resin solution composition for resin black matrix, A color filter can be produced.
【００３５】[0035]
【実施例】実施例におけるポリアミック酸の原料および
溶媒の略称は以下の通りである。EXAMPLES Abbreviations of raw materials and solvents for polyamic acid in Examples are as follows.
【００３６】ＢＰＤＡ: ３，３´，４，４´―ビフェニ
ルテトラカルボン酸二無水物 ＤＤＳ: ３，３´―ジアミノジフェニルスルホン ＤＡＥ: ４，４´―ジアミノジフェニルエーテル ＮＭＰ: Ｎ―メチル―２―ピロリドン γＢＬ: γ―ブチロラクトン また実施例における測定法は以下の通りである。BPDA: 3,3 ', 4,4'-biphenyltetracarboxylic dianhydride DDS: 3,3'-diaminodiphenyl sulfone DAE: 4,4'-diaminodiphenyl ether NMP: N-methyl-2-pyrrolidone γBL: γ-butyrolactone The measuring method in the examples is as follows.
【００３７】・コントラスト比 バックライト（明拓システム）上で色彩輝度計（トプコ
ンＢＭ―５Ａ）にて、２度視野で試料の平行ニコル状態
と直交ニコル状態での輝度を測定し、両状態での輝度の
比をコントラスト比とした。[Contrast ratio] The brightness of the sample in the parallel Nicols state and the crossed Nicols state was measured with a color luminance meter (Topcon BM-5A) on the backlight (Meikaku system), and in both states. The ratio of the brightness of the was defined as the contrast ratio.
【００３８】・表面粗さ 東京精密（株）製サーフコム１５００Ａにて測定した。Surface roughness: Measured with Surfcom 1500A manufactured by Tokyo Seimitsu Co., Ltd.
【００３９】実施例１ ５Ｌのフラスコに、ＮＭＰ４００ｇ、γＢＬ３０００
ｇ、ＤＡＥ９６．１ｇ（０．４８０ｍｏｌ）、ＤＤＳ２
９．８ｇ（０．１２０ｍｏｌ）、を投入し、釜を３０℃
に加熱した。３０分後、ＢＰＤＡ１７６．５ｇ（０．６
００ｍｏｌ）を投入し、釜を６０℃で３時間加熱するこ
とにより、ポリアミック酸溶液を得た。Example 1 A 5 L flask was charged with 400 g of NMP and γBL3000.
g, DAE 96.1 g (0.480 mol), DDS2
Add 9.8g (0.120mol), and put the kettle at 30 ° C.
Heated. After 30 minutes, 176.5 g of BPDA (0.6
(00 mol) was charged and the kettle was heated at 60 ° C. for 3 hours to obtain a polyamic acid solution.
【００４０】一方ピグメントレッド１７７ ５．４ｇ、
γＢＬ８４ｇをガラスビーズ９０ｇとともにホモジナイ
ザーを用い、７０００ｒｐｍで３０分間分散処理後、ガ
ラスビーズを濾過により除去し、顔料分散液を得た。On the other hand, 5.4 g of Pigment Red 177,
84 g of γBL was dispersed with 90 g of glass beads using a homogenizer at 7,000 rpm for 30 minutes, and then the glass beads were removed by filtration to obtain a pigment dispersion liquid.
【００４１】得られた顔料分散液１０ｇに、ポリアミッ
ク酸溶液３０ｇを添加し、顔料分散樹脂溶液を得た。得
られた顔料分散樹脂溶液に、γＢＬの１％リン酸溶液
２．２ｇを添加後攪拌を行った。To 10 g of the obtained pigment dispersion liquid, 30 g of a polyamic acid solution was added to obtain a pigment dispersion resin solution. To the obtained pigment-dispersed resin solution, 2.2 g of a 1% phosphoric acid solution of γBL was added and then stirred.
【００４２】得られた顔料分散樹脂溶液組成物をスライ
ドガラス上に落とし、カバーガラスを被せ２０分間放置
した後、光学顕微鏡により観察した結果、分散性は良好
であった。The obtained pigment-dispersed resin solution composition was dropped on a slide glass, covered with a cover glass and allowed to stand for 20 minutes, and then observed with an optical microscope. As a result, the dispersibility was good.
【００４３】実施例２ 実施例１においてピグメントレッド１７７を添加した代
わりに、ピグメントブルー１５を５．４ｇを添加したこ
と以外は全く実施例１と同様に顔料分散樹脂溶液組成物
を調製した。Example 2 A pigment-dispersed resin solution composition was prepared in the same manner as in Example 1 except that 5.4 g of Pigment Blue 15 was added instead of the addition of Pigment Red 177 in Example 1.
【００４４】得られた顔料分散樹脂溶液組成物をスライ
ドガラス上に落とし、カバーガラスを被せ２０分間放置
した後、光学顕微鏡により観察した結果、分散性は良好
であった。The obtained pigment-dispersed resin solution composition was dropped on a slide glass, covered with a cover glass and left for 20 minutes, and then observed with an optical microscope. As a result, the dispersibility was good.
【００４５】実施例３ 実施例１で調製した顔料分散樹脂溶液組成物を無アルカ
リガラス基板上にスピンコートし、５０℃で１０分間、
９０℃で１０分間、１１０℃で２０分間オーブンを用い
て空気中で加熱乾燥して、膜厚１．６μｍのポリイミド
前駆体着色膜を得た。この膜上にポジ型フォトレジスト
（東京応化社製ＯＦＰＲ―８００）を塗布し、８０℃で
２０分間加熱乾燥して膜厚１μｍのレジスト膜を得た。
キャノン社製紫外線露光機ＰＬＡ―５０１Ｆを用い、ク
ロム製のフォトマスクを介して、波長３６５ｎｍでの強
度が５０ｍＪ／ｃｍ2 の紫外線を照射した。露光後、テ
トラメチルアンモニウムハイドロオキサイドの２．３８
ｗｔ％の水溶液からなる現像液に浸漬し、フォトレジス
トおよびポリイミド前駆体着色被膜の現像を同時に行っ
た。エッチング後、不要となったフォトレジスト層をメ
チルセロソルブアセテートで剥離した。さらにこのよう
にして得られたポリイミド前駆体着色被膜を窒素雰囲気
中で３００℃で３０分間熱処理し、膜厚１．２μｍのポ
リイミド着色被膜を得た。Example 3 The pigment-dispersed resin solution composition prepared in Example 1 was spin-coated on a non-alkali glass substrate, and the mixture was heated at 50 ° C. for 10 minutes.
The polyimide precursor colored film having a thickness of 1.6 μm was obtained by heating and drying in air using an oven at 90 ° C. for 10 minutes and 110 ° C. for 20 minutes. A positive photoresist (OFPR-800 manufactured by Tokyo Ohka Kogyo Co., Ltd.) was applied on this film, and dried by heating at 80 ° C. for 20 minutes to obtain a resist film having a film thickness of 1 μm.
Using an ultraviolet exposure device PLA-501F manufactured by Canon Inc., an ultraviolet ray having an intensity of 50 mJ / cm @ 2 at a wavelength of 365 nm was irradiated through a photomask made of chromium. 2.38 of tetramethylammonium hydroxide after exposure
The photoresist and the polyimide precursor colored film were simultaneously developed by immersing them in a developing solution composed of a wt% aqueous solution. After the etching, the unnecessary photoresist layer was stripped with methyl cellosolve acetate. Further, the polyimide precursor colored film thus obtained was heat-treated at 300 ° C. for 30 minutes in a nitrogen atmosphere to obtain a polyimide colored film having a thickness of 1.2 μm.
【００４６】このようにして得られたポリイミド着色被
膜のコントラスト比を測定した結果約６００と高い値を
有することが分かった。また、表面粗さを測定した結
果、０．００８μｍと平坦性に優れていることがわかっ
た。As a result of measuring the contrast ratio of the thus obtained polyimide colored coating, it was found to have a high value of about 600. In addition, as a result of measuring the surface roughness, it was found to be excellent in flatness of 0.008 μm.
【００４７】比較例１ 実施例１においてリン酸を添加した代わりに、γＢＬを
２．２ｇ添加したこと以外は全く実施例１と同様に顔料
分散樹脂溶液組成物を調製した。Comparative Example 1 A pigment-dispersed resin solution composition was prepared in the same manner as in Example 1 except that 2.2 g of γBL was added instead of phosphoric acid in Example 1.
【００４８】得られた顔料分散樹脂溶液組成物をスライ
ドガラス上に落とし、カバーガラスを被せ２０分間放置
した後、光学顕微鏡により観察した結果、顔料の凝集が
観察された。The obtained pigment-dispersed resin solution composition was dropped on a slide glass, covered with a cover glass and allowed to stand for 20 minutes, and then observed with an optical microscope. As a result, pigment aggregation was observed.
【００４９】比較例２ 実施例２においてリン酸を添加した代わりγＢＬを２．
２ｇ添加したことを添加しなかったこと以外は全く実施
例２と同様にカラーペーストを調製した。Comparative Example 2 Instead of adding phosphoric acid in Example 2, γBL was changed to 2.
A color paste was prepared exactly as in Example 2 except that 2 g was added and not added.
【００５０】得られたカラーペーストをスライドガラス
上に落とし、カバーガラスを被せ２０分間放置した後、
光学顕微鏡により観察した結果、顔料の凝集が観察され
た。The resulting color paste was dropped on a slide glass, covered with a cover glass and left for 20 minutes,
As a result of observation with an optical microscope, aggregation of the pigment was observed.
【００５１】比較例３ 実施例３で実施例１で調製した顔料分散樹脂溶液組成物
を用いポリイミド着色被膜を得た代わりに、比較例１で
調製した酸が添加されていない顔料分散樹脂溶液組成物
を用いポリイミド着色被膜を得たこと以外は全く実施例
３と同様に、ポリイミド着色被膜を得た。Comparative Example 3 Instead of using the pigment-dispersed resin solution composition prepared in Example 1 in Example 3 to obtain a polyimide colored coating, the acid-prepared pigment-dispersed resin solution composition prepared in Comparative Example 1 was used. A polyimide colored coating was obtained in the same manner as in Example 3 except that the polyimide colored coating was used.
【００５２】このようにして得られたポリイミド着色被
膜のコントラスト比を測定した結果約４５０と低い値を
有することが分かった。また、表面粗さを測定した結
果、０．０１６μｍと平坦性が悪いことがわかった。As a result of measuring the contrast ratio of the thus obtained polyimide colored coating, it was found to have a low value of about 450. Further, as a result of measuring the surface roughness, it was found that the flatness was poor at 0.016 μm.
【００５３】[0053]
【発明の効果】本発明は上述のごとく構成したので、顔
料の分散安定性の高いペーストが得られる。また、該顔
料分散樹脂溶液組成物をカラーフィルターに用いた場
合、画素のコントラスト比が高いこと、さらに表面の平
坦性が高いことを特徴とするカラーフィルターを得るこ
とができる。Since the present invention is constructed as described above, a paste having high pigment dispersion stability can be obtained. When the pigment-dispersed resin solution composition is used for a color filter, a color filter having a high pixel contrast ratio and a high surface flatness can be obtained.
Claims (10)
および酸成分を含有してなる顔料分散樹脂溶液組成物に
おいて、酸成分として無機酸を含有することを特徴とす
る顔料分散樹脂溶液組成物。1. A pigment-dispersed resin solution composition comprising a pigment component, a polyamic acid component, a solvent component and an acid component, wherein the pigment-dispersed resin solution composition contains an inorganic acid as an acid component.
を特徴とする請求項１記載の顔料分散樹脂溶液組成物。2. The pigment-dispersed resin solution composition according to claim 1, wherein the inorganic acid is an acid containing a phosphorus atom.
求項１記載の顔料分散樹脂溶液組成物。3. The pigment-dispersed resin solution composition according to claim 1, wherein the inorganic acid is phosphoric acid.
または黒色顔料であることを特徴とする請求項１記載の
顔料分散樹脂溶液組成物。4. The pigment-dispersed resin solution composition according to claim 1, wherein the pigment component is a red pigment, a blue pigment, a green pigment or a black pigment.
ことを特徴とする請求項１記載の顔料分散樹脂溶液組成
物。5. The pigment-dispersed resin solution composition according to claim 1, wherein the pigment component is a red pigment or a blue pigment.
とを特徴とする請求項１記載の顔料分散樹脂溶液組成
物。6. The pigment-dispersed resin solution composition according to claim 1, wherein the solvent component is an aprotic polar solvent.
成分を含有してなる顔料分散樹脂溶液に、無機酸成分ま
たは／および溶媒成分を含有する酸溶液を添加すること
を特徴とする顔料分散樹脂溶液組成物の製造方法。7. A pigment-dispersed resin solution, characterized in that an acid solution containing an inorganic acid component and / or a solvent component is added to a pigment-dispersed resin solution containing a pigment component, a polyamic acid component and a solvent component. A method for producing a composition.
料分散液に、無機酸成分、ポリアミック酸成分および溶
媒成分を含有してなる樹脂溶液を添加することを特徴と
する顔料分散樹脂溶液組成物の製造方法。8. A pigment dispersion resin solution composition, characterized in that a resin solution containing an inorganic acid component, a polyamic acid component and a solvent component is added to a pigment dispersion liquid containing a pigment component and a solvent component. Method of manufacturing things.
成分を含有してなる顔料分散樹脂溶液に、無機酸成分、
ポリアミック酸成分および溶媒成分を含有してなる樹脂
溶液を添加することを特徴とする顔料分散樹脂溶液組成
物の製造方法。9. A pigment dispersion resin solution containing a pigment component, a polyamic acid component and a solvent component, an inorganic acid component,
A method for producing a pigment-dispersed resin solution composition, which comprises adding a resin solution containing a polyamic acid component and a solvent component.
に設けられた着色層からなる画素を有するカラーフィル
ターにおいて、該着色層が請求項１〜６記載の顔料分散
樹脂溶液組成物から得られるポリイミド着色被膜である
ことを特徴とするカラーフィルター。10. A color filter having a pixel comprising a colored layer provided in a desired pattern for each color with an arbitrary number of colors, wherein the colored layer is obtained from the pigment-dispersed resin solution composition according to any one of claims 1 to 6. A color filter, which is a polyimide colored coating film.