JPH0834163A - Production of printing tape and thermal recording tape cassette - Google Patents

Abstract

PURPOSE:To obtain a printing tape enhanced in chemical resistance and mechanical strength and not generating the deterioration of a thermal recording layer caused by the transmission of oxygen by applying reversal printing to the thermal recording layer of a recording material directly or through a thin heat-resistant protective layer. CONSTITUTION:A thermal recording material 2 is obtained by providing a thermal color forming layer 5 on the single surface of a base material 4 and providing a heat- resistant protective layer 6 on the surface opposite to the base material of the thermal color forming layer 5. A support 3 is formed by providing pressure-sensitive adhesive layers 8a, 8b on both surfaces of a thin base material 7 and providing a release liner 9 on the pressure-sensitive adhesive layer 8b on the side not coming into contact with the thermal recording material 2. In producing a printing tape subjected to printing, thermal reversal printing is applied to the thermal color forming layer 5 on the side of the heat-resistant protective layer 6 by a thermal head 10 while the thermal recording material 2 is pressed to a roller 11 on the side of its base material 4 and the printed thermal recording material 2 and the support 3 are subsequently pressed by the rollers 12 arranged above and below them to be mutually bonded to produce the printing tape 1.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は、事務用・学習用のファ
イルや各種器具等に貼り付けられ、または差し込むなど
して取り付けられる印字ラベルの作製法およびこれに用
いられる感熱記録テープカセットに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for producing a printed label which is attached to or attached to an office / learning file, various instruments, etc., and a thermal recording tape cassette used therefor.

【０００２】本発明のカセットはサーマルヘッド等の印
字部を有するプリンターに装填され、情報・画像が感熱
記録される。また、本発明にて得られる印字テープは堅
牢性、耐薬品性及び耐溶剤性にすぐれる。The cassette of the present invention is loaded into a printer having a printing portion such as a thermal head, and information / images are heat-sensitive recorded. Further, the printing tape obtained by the present invention has excellent fastness, chemical resistance and solvent resistance.

【０００３】[0003]

【従来の技術】サーマルヘッドなどを用い電気信号にて
制御された熱による記録方法には、加熱によりインクリ
ボンの色材が転写されて記録を行う熱転写記録と、加熱
により発色して記録を行う感熱記録とがある。2. Description of the Related Art Recording methods using heat, such as a thermal head, which are controlled by electric signals, include thermal transfer recording in which the color material of an ink ribbon is transferred by heating and recording, and recording by coloring in heat. There is a thermal recording.

【０００４】熱転写記録には、さらに加熱によりインク
リボンのインクが溶融し記録紙に転写が行われる溶融型
と、インク中の染料だけが昇華して記録紙に転写する昇
華型とがある。In thermal transfer recording, there are a melt type in which the ink of the ink ribbon is further melted and transferred to the recording paper by heating, and a sublimation type in which only the dye in the ink is sublimated and transferred to the recording paper.

【０００５】昇華型熱転写記録では、加えられた熱エネ
ルギー量に応じて染着濃度が変わり階調が表現できる利
点があるが、比較的記録速度は遅く、記録コストも高い
ため、ピクトリアルカラーハードコピー用に限定して用
いられている。Sublimation type thermal transfer recording has the advantage that the dyeing density changes depending on the amount of heat energy applied and gradation can be expressed, but since the recording speed is relatively slow and the recording cost is high, it is a pictorial color hard disk. It is used only for copying.

【０００６】これに対して、溶融型熱転写記録は比較的
記録速度が速く、記録コストが安い。また、画質的にも
文字情報やグラフなど図形情報を記録するには充分であ
ることから、各種のワープロやプリンタ用として最も普
及している。On the other hand, the melting type thermal transfer recording has a relatively high recording speed and a low recording cost. Also, since it is sufficient for recording graphic information such as character information and graphs in terms of image quality, it is most widely used for various word processors and printers.

【０００７】また近年、レタリングマシン、テープライ
ター、ラベルプリンターなどと呼ばれる装置が普及しつ
つある。これらは粘着加工されたテープ状受像紙に印字
を行なうものであり、この印字されたテープを事務用フ
ァイル、各種製品、備品に貼りつけるものであるが、こ
のような装置にも溶融型熱転写方式が採用されている。
このようなレタリングまたはラベル用途には、堅牢性、
耐溶剤性、耐薬品性が特に必要であるが、熱溶融型熱転
写記録に用いられている従来のワックス系のインクでは
充分な堅牢性が得られず、かつ耐薬品性も低い。In recent years, devices called lettering machines, tape writers, label printers, etc. have become widespread. These are for printing on adhesive tape-shaped image-receiving paper, and this printed tape is attached to office files, various products, and equipment. Has been adopted.
For such lettering or label applications, robustness,
Solvent resistance and chemical resistance are particularly required, but conventional wax-based inks used for heat-melt type thermal transfer recording cannot provide sufficient fastness and have low chemical resistance.

【０００８】また、従来のワックス系インクを用い、透
明基材上にミラー反転の文字を印字し、印字面側に両面
接着テープを貼り合わせて、印字面を透明基材で保護し
たラベルを作成する装置も市販されており（特開平１−
１３５６６４号、１−１３５６７１号）、優れた堅牢
性、耐溶剤性、耐薬品性を有するが、消耗品がインクリ
ボン、透明基材および両面接着テープからなるためラン
ニングコストが高く、また装置が複雑で小型化は困難で
ある。Further, a conventional wax-based ink is used to print mirror-inverted characters on a transparent base material, and a double-sided adhesive tape is attached to the printing surface side to prepare a label with the printing surface protected by the transparent base material. A device for doing so is also commercially available (JP-A-1-
No. 135564, No. 1-135671), it has excellent robustness, solvent resistance, and chemical resistance, but since the consumables consist of an ink ribbon, a transparent base material and a double-sided adhesive tape, the running cost is high and the device is complicated. It is difficult to downsize.

【０００９】これに対して感熱記録方式では、加熱によ
って発色する感熱発色層を紙等の支持体上に設けた一般
に感熱記録紙と呼ばれる記録材料を用いる。このような
感熱記録は、他の記録方法に比べると装置が簡単であ
り、現象、定着などの操作が不要である。また、インク
リボンなど記録紙以外の消耗品が不要で、ランニングコ
ストも低く、かつ装置の小型化も容易で、発色濃度も充
分である。このためファクシミリや複写機、計測機器等
の記録材料などに広く使用されている。On the other hand, in the heat-sensitive recording method, a recording material generally called heat-sensitive recording paper is used in which a heat-sensitive color-developing layer that develops color by heating is provided on a support such as paper. Such thermal recording requires a simpler apparatus than other recording methods and does not require operations such as phenomenon and fixing. Further, consumables other than recording paper such as an ink ribbon are not required, the running cost is low, the apparatus can be easily downsized, and the color density is sufficient. Therefore, it is widely used for recording materials such as facsimiles, copiers, and measuring instruments.

【００１０】しかしながら、感熱記録紙はその材料から
明らかなように溶剤や薬品等により容易に発色成分が反
応し、あるいは消しゴムでこすったり、ツメ等でひっか
いた場合には感熱発色層が発色、損傷し記録画像が損な
われる。このような感熱記録紙の欠点を解消すべく、感
熱発色層上に保護層を設けた記録紙も提案されている。
このような記録紙はコーティングにより保護層を設けて
いるが、なお充分な堅牢性、耐溶剤性、耐薬品性を有す
るものは得られていない。また感熱発色層は高温で発色
するため、保護層の形成時に熱風乾燥を行うことができ
ず生産性が低い。さらに感熱発色層は耐溶剤性が低く保
護層コーティング時の溶剤が限定される。However, as is apparent from the material of the thermosensitive recording paper, the coloring components easily react with the solvent or chemicals, or when the thermosensitive coloring layer is rubbed with an eraser or scratched with a nail or the like, the thermosensitive coloring layer is colored or damaged. However, the recorded image is damaged. In order to eliminate such drawbacks of the heat-sensitive recording paper, a recording paper in which a protective layer is provided on the heat-sensitive color developing layer has been proposed.
Although such a recording paper is provided with a protective layer by coating, it has not yet been obtained that has sufficient fastness, solvent resistance and chemical resistance. Further, since the thermosensitive coloring layer develops color at a high temperature, hot air drying cannot be performed when the protective layer is formed, and the productivity is low. Furthermore, the thermosensitive coloring layer has low solvent resistance, and the solvent for coating the protective layer is limited.

【００１１】上記の欠点を解消する感熱記録紙およびそ
の製造法として、特開平５−３１８９１２号に開示の技
術も知られている。ここに記載された感熱記録紙はその
表面が保護フィルムで覆われているため極めて優れた堅
牢性、耐薬品性、耐溶剤性を有する。また、このような
製造法によれば、感熱記録紙の感熱発色層コーティング
時以外は高温乾燥を行うことが可能となり生産性が高
い。As a heat-sensitive recording paper and a method for producing the same, which solves the above-mentioned drawbacks, the technique disclosed in Japanese Patent Laid-Open No. 5-318912 is also known. Since the surface of the thermal recording paper described here is covered with a protective film, it has extremely excellent fastness, chemical resistance and solvent resistance. Further, according to such a production method, high temperature drying can be performed except when the thermosensitive color developing layer is coated on the thermosensitive recording paper, and the productivity is high.

【００１２】[0012]

【発明が解決しようとする課題】しかしながら、かかる
感熱記録紙では印字の鮮明性の点から、保護フィルムの
厚さは１６μｍ程度が限度であり、保護フィルムが薄い
ため、機械的特性が充分でなく、衝撃等により破損した
り、また、酸素透過性が高いため、印字が消去するとい
う不都合が生じる。However, in such a thermal recording paper, the thickness of the protective film is limited to about 16 μm from the viewpoint of printing clarity, and the mechanical properties are not sufficient because the protective film is thin. In addition, there is a problem that the print is erased due to damage due to impact or the like and high oxygen permeability.

【００１３】本発明は耐久性の高い印字テープの作製法
およびこれに用いられるテープカセットを提供すること
を目的とする。An object of the present invention is to provide a method of producing a printing tape having high durability and a tape cassette used for the method.

【００１４】[0014]

【発明が解決するための手段】したがって、本発明は、
透明性を有する可撓性基材および該基材の片面に設けら
れた感熱発色層を含む感熱記録体の感熱発色層に反転印
字を行った後、この感熱記録体の感熱発色層側に、表面
が感圧接着性を有する支持体を貼付してなる印字テープ
の作製法を提供するものである。Accordingly, the present invention is
After performing reverse printing on the thermosensitive color developing layer of the thermosensitive recording medium including a transparent flexible base material and a thermosensitive color developing layer provided on one surface of the substrate, on the thermosensitive color developing layer side of the thermosensitive recording medium, The present invention provides a method for producing a printing tape having a support having a pressure-sensitive adhesive surface.

【００１５】また、本発明は、（ｉ）透明性を有する可
撓性基材および該基材の片面に設けられた感熱発色層を
含むロール状の感熱記録体、（ｉｉ）前記感熱記録体を
巻戻し、印字部を通して繰り出す機構、（ｉｉｉ）表面
が感圧接着性を有するロール状の支持体、および（ｉ
ｖ）印字後の前記感熱発色層に支持体を貼付して繰り出
す機構、とを有する感熱記録テープカセットを提供する
ものである。The present invention also provides (i) a roll-shaped thermosensitive recording medium comprising a transparent flexible substrate and a thermosensitive coloring layer provided on one surface of the substrate, and (ii) the thermosensitive recording medium. A mechanism for rewinding and unwinding through the printing unit, (iii) a roll-shaped support having a pressure-sensitive adhesive surface, and (i)
v) A heat-sensitive recording tape cassette having a mechanism in which a support is attached to the heat-sensitive color-developing layer after printing and is fed out.

【００１６】さらに本発明は、感熱発色層と接触する支
持体がゴムを主成分とする感圧接着剤層を有する感熱記
録テープカセットをも提供するものである。The present invention further provides a heat-sensitive recording tape cassette in which the support contacting with the heat-sensitive color forming layer has a pressure-sensitive adhesive layer containing rubber as a main component.

【００１７】本発明にて得られる印字テープは、耐久性
が高く、用いた支持体に応じて、ファイルなどに張り付
けたり、差し込んで固定したり、あるいは接着剤などを
用いて器具に取り付けることができる。The printing tape obtained by the present invention has high durability and can be attached to a file or the like, fixed by inserting it, or attached to an instrument using an adhesive or the like, depending on the support used. it can.

【００１８】以下、図を参照しながら、本発明を詳細に
説明する。The present invention will be described in detail below with reference to the drawings.

【００１９】図１は、本発明の印字テープの作製法の一
具体例を示す模式的な断面図である。図１において、印
字テープ１は感熱記録体２と支持体３を貼付することに
よって得られる。感熱記録体２は、基材４の片面に感熱
発色層５を設け、さらに該感熱発色層の基材と反対の面
に耐熱保護層６を設けてなる。FIG. 1 is a schematic cross-sectional view showing a specific example of the method for producing the printing tape of the present invention. In FIG. 1, a printing tape 1 is obtained by pasting a thermosensitive recording medium 2 and a support 3 on each other. The thermosensitive recording medium 2 is provided with a thermosensitive coloring layer 5 on one surface of a substrate 4 and a heat-resistant protective layer 6 on the surface of the thermosensitive coloring layer opposite to the substrate.

【００２０】一方、支持体３は薄葉基材７の両面に感圧
接着剤層８ａおよび８ｂを設け、前記感熱記録体２と接
しない側の感圧接着剤層８ｂには剥離ライナー９を設け
てなる。On the other hand, the support 3 is provided with pressure sensitive adhesive layers 8a and 8b on both sides of the thin substrate 7, and a release liner 9 is provided on the pressure sensitive adhesive layer 8b which is not in contact with the thermal recording medium 2. It becomes.

【００２１】印字、印画を行った印字テープを作製する
には、感熱記録体２の基材４側よりローラー１１にて押
圧しながら、耐熱保護層６側から感熱発色層５にサーマ
ルヘッド１０にて感熱反転印字を行う。次いで、印字さ
れた感熱記録体２と支持体３を、これらの上下に配した
ローラー１２によって押圧して感熱記録体と支持体を貼
付し、印字テープ１を製造する。In order to produce a printing tape on which printing and printing are performed, the heat-sensitive protective layer 6 side and the thermosensitive coloring layer 5 and the thermal head 10 are pressed from the heat-resistant protective layer 6 side while being pressed by the roller 11 from the base material 4 side of the thermosensitive recording medium 2. Thermal reverse printing. Then, the printed thermal recording medium 2 and the support 3 are pressed by the rollers 12 arranged above and below them to attach the thermal recording medium and the support, and the printing tape 1 is manufactured.

【００２２】さらに図２は、前記印字テープの作製に適
した本発明の感熱記録テープカセットの一具体例を示す
断面図である。Further, FIG. 2 is a sectional view showing a specific example of the thermal recording tape cassette of the present invention, which is suitable for producing the printing tape.

【００２３】図２において、感熱記録テープカセット２
０は、主に前記感熱記録体２を巻いたスプール２１と前
記支持体３を巻いたスプール２２とから構成されてい
る。In FIG. 2, the thermal recording tape cassette 2 is shown.
Reference numeral 0 mainly comprises a spool 21 around which the thermosensitive recording medium 2 is wound and a spool 22 around which the support 3 is wound.

【００２４】前記各スプールはスプール軸２３ａ、２３
ｂにそれぞれ設置されており、図中の矢印の方向へ各々
回転する。感熱記録体のスプール軸２３ａの回転によ
り、感熱記録体２が繰り出され、ガイド２４を介して印
字部２５に達する。印字部２５において、感熱記録体２
はサーマルヘッド２９により、図中下方より感熱反転印
字され、さらに感熱記録テープカセット２０の外部へ向
けて繰り出される。The spools have spool shafts 23a, 23
They are respectively installed in b and rotate in the directions of the arrows in the figure. The rotation of the spool shaft 23a of the thermosensitive recording medium causes the thermosensitive recording medium 2 to be drawn out and reaches the printing unit 25 via the guide 24. In the printing unit 25, the thermal recording material 2
Is subjected to heat-sensitive reversal printing from below in the drawing by the thermal head 29, and is further fed out of the heat-sensitive recording tape cassette 20.

【００２５】一方、支持体３もスプール軸２３ｂの回転
によりローラー２６およびガイド２７を介して繰り出さ
れ、印字後の感熱記録体２の感熱発色層に接する。その
際、感熱記録体２と支持体３がローラー３０により押圧
されて、接着し、印字テープ２８が作製される。On the other hand, the support 3 is also fed out by the rotation of the spool shaft 23b through the roller 26 and the guide 27, and comes into contact with the thermosensitive coloring layer of the thermosensitive recording body 2 after printing. At that time, the thermal recording medium 2 and the support 3 are pressed by the roller 30 and adhered to each other, and the printing tape 28 is manufactured.

【００２６】本発明において使用される感熱記録体の基
材は、無色あるいは有色透明な可撓性基材であって、該
基材を介して裏面に形成された印字像（記録像）が表面
から視認できるものであれば特に限定されない。例え
ば、無色あるいは染料等の着色剤をその系中に混合する
か、あるいはその表面に塗布などの被覆手段によって有
色透明としたプラスチックフィルムが好適に使用され、
例えば、ポリエチレンフィルム、ポリエステルフィル
ム、ポリプロピレンフィルム、ポリ塩化ビニリデンフィ
ルム、ポリビニルアルコールフィルム、ポリ塩化ビニル
フィルム、ポリカーボネートフィルム、ナイロンフィル
ム、ポリスチレンフィルム、エチレン−ビニルアルコー
ル共重合体フィルムなどが挙げられる。また、薄葉不織
布、薄葉紙などに光散乱防止処理をして実質的に透明化
したシート状物であってもよい。The base material of the thermosensitive recording medium used in the present invention is a colorless or colored transparent flexible base material, and the printed image (recorded image) formed on the back surface through the base material is the front surface. It is not particularly limited as long as it is visible from the outside. For example, a colorless or transparent plastic film mixed with a colorant such as a dye in the system, or colored and transparent by a coating means such as coating on the surface is preferably used.
Examples thereof include polyethylene film, polyester film, polypropylene film, polyvinylidene chloride film, polyvinyl alcohol film, polyvinyl chloride film, polycarbonate film, nylon film, polystyrene film, ethylene-vinyl alcohol copolymer film and the like. Further, it may be a sheet-like material obtained by substantially thinning a thin nonwoven fabric, a thin paper, etc. by light scattering prevention treatment.

【００２７】該基材の厚みは実質的に制限されないが、
機械的強度、酸素透過率などの点から２０μｍ以上、好
ましくは２５〜７５μｍの範囲である。２０μｍ未満で
はハンドリングが困難であり、７５μｍを超えると可撓
性に劣り、印字性が低下する恐れがある。Although the thickness of the base material is not substantially limited,
From the viewpoint of mechanical strength, oxygen permeability, etc., the thickness is 20 μm or more, preferably 25 to 75 μm. If it is less than 20 μm, it is difficult to handle, and if it exceeds 75 μm, the flexibility may be poor and the printability may be deteriorated.

【００２８】さらに、印字後の印字耐久性、未印字部の
被り（着色）現象を抑えるため、前記基材の一方に酸素
遮断性の高い、ポリ塩化ビニリデンやポリビニルアルコ
ール、（エチレン−酢酸ビニル）共重合体けん化物など
をコーティングするのが好ましい。Furthermore, in order to suppress the printing durability after printing and the fog (coloring) phenomenon in the unprinted portion, one of the above-mentioned substrates has a high oxygen barrier property, such as polyvinylidene chloride or polyvinyl alcohol, (ethylene-vinyl acetate). It is preferable to coat it with a saponified copolymer.

【００２９】本発明の感熱記録体に設けられる感熱発色
層としては、加熱により発色する公知の組成物をいずれ
も用いることができ、発色剤である電子供与性染料前駆
体およびこれと反応して発色する有機酸との組み合わせ
のほか、ジアゾ化合物およびこれとカップリングして発
色するカップリング化合物の組み合わせなどを用いるこ
とができる。As the heat-sensitive color forming layer provided in the heat-sensitive recording material of the present invention, any known composition capable of forming a color by heating can be used, and an electron-donating dye precursor which is a color forming agent and a reaction with the same can be used. In addition to a combination with an organic acid that develops a color, a combination of a diazo compound and a coupling compound that forms a color upon coupling with the diazo compound can be used.

【００３０】本発明印字テープの発色剤として用いられ
る電子供与性染料前駆体としては、従来公知のものがい
ずれも用いられてよい。代表的には、トリアリールメタ
ン系、ジフェニルメタン系、キサンテン系、スピロピラ
ン系などが挙げられるが、キサンテン系電子供与性染料
前駆体は多色性を有しているので好ましい。As the electron-donating dye precursor used as the color former for the printing tape of the present invention, any conventionally known one may be used. Typical examples thereof include triarylmethane-based, diphenylmethane-based, xanthene-based, and spiropyran-based, and the xanthene-based electron-donating dye precursor is preferable because it has polychromaticity.

【００３１】前記電子供与性染料前駆体と反応して発色
を生ずる有機酸としては、芳香族カルボン酸誘導体やフ
ェノール誘導体などが挙げられる。Examples of the organic acid that reacts with the electron-donating dye precursor to produce a color include aromatic carboxylic acid derivatives and phenol derivatives.

【００３２】芳香族カルボン酸誘導体としては、２−フ
ェニルメトキシ−ナフタリン−６−カルボン酸フェニル
メチルエステル、２−ｐ−メチルフェニル−ｍ−ナフタ
リン−６−カルボン酸フェニルメチルエステル、２−ｐ
−メチルフェニル−ｍ−ナフタリン−６−カルボン酸−
ｐ−メチルフェニルメチルエステルなどが挙げられる。Examples of the aromatic carboxylic acid derivative include 2-phenylmethoxy-naphthalene-6-carboxylic acid phenylmethyl ester, 2-p-methylphenyl-m-naphthalene-6-carboxylic acid phenylmethyl ester and 2-p.
-Methylphenyl-m-naphthalene-6-carboxylic acid-
Examples thereof include p-methylphenylmethyl ester.

【００３３】フェノール誘導体としては、４−ヒドロキ
シジフェノキシド、α−ナフトール、メチル−４−ヒド
ロキシベンゾエート、４−ｔｅｒｔ．−オクチルカテコ
ール、４，４’−ｓｅｃ．−ブチリデンジフェノール、
４−ｔｅｒｔ．−ブチルフェノール、β−ナフトール、
４−ヒドロキシアセトフェノール、２，２’−ジヒドロ
キシジフェノール、２−ｔｅｒｔ．−ブチルフェノー
ル、ビスフェノールＡなどが挙げられる。As the phenol derivative, 4-hydroxydiphenoxide, α-naphthol, methyl-4-hydroxybenzoate, 4-tert. -Octylcatechol, 4,4'-sec. -Butylidenediphenol,
4-tert. -Butylphenol, β-naphthol,
4-hydroxyacetophenol, 2,2'-dihydroxydiphenol, 2-tert. -Butylphenol, bisphenol A and the like.

【００３４】電子供与性染料前駆体と有機酸との配合割
合は、前者１重量部に対して、後者０．２〜１０重量
部、好ましくは０．５〜５重量部、さらに好ましくは１
〜２重量部である。The compounding ratio of the electron-donating dye precursor and the organic acid is 0.2-10 parts by weight, preferably 0.5-5 parts by weight, more preferably 1 part by weight with respect to 1 part by weight of the former.
~ 2 parts by weight.

【００３５】また、他の発色剤としてジアゾ化合物およ
びそれとカップリングして発色するカップリング化合物
の組合わせを用いてもよい。ジアゾ化合物としては、４
−ジアゾ−１−ジメチルアミノベンゼン、４−ジアゾ−
１−ジエチルアミノベンゼン、４−ジアゾ−１−ジプロ
ピルアミノベンゼンなどが挙げられる。一方、これらの
カップリング化合物としては、β−ナフトール、レゾル
シン、フロログルシン、２，３−ジヒドロキシナフタレ
ンなどが挙げられる。また、反応促進のため、塩基性物
質の雰囲気下でカップリングを行ってもよい。As another color former, a combination of a diazo compound and a coupling compound which forms a color by coupling with the diazo compound may be used. 4 as the diazo compound
-Diazo-1-dimethylaminobenzene, 4-diazo-
1-diethylaminobenzene, 4-diazo-1-dipropylaminobenzene and the like can be mentioned. On the other hand, examples of these coupling compounds include β-naphthol, resorcin, phloroglucin, and 2,3-dihydroxynaphthalene. In addition, the coupling may be performed in an atmosphere of a basic substance to accelerate the reaction.

【００３６】ジアゾ化合物とカップリング化合物との配
合割合は、前者１重量部に対して、後者０．２〜１０重
量部、好ましくは０．５〜５重量部であり、１〜２重量
部が実用的である。The compounding ratio of the diazo compound and the coupling compound is 0.2 to 10 parts by weight, preferably 0.5 to 5 parts by weight, and 1 to 2 parts by weight with respect to 1 part by weight of the former. It is practical.

【００３７】上記発色材料は、保存性や発色感度の制御
などの点から、その一部または全部をカプセル化しても
よい。カプセル化法および材料は公知の方法、材料を用
いることができる。また、加熱時の反応を促進するため
の発色助剤や安定化のための酸安定剤を併用してもよ
い。The color forming material may be partially or entirely encapsulated from the viewpoint of storage stability and control of color developing sensitivity. As the encapsulation method and the material, known methods and materials can be used. Further, a color forming aid for accelerating the reaction during heating and an acid stabilizer for stabilization may be used in combination.

【００３８】上記発色材料は、一般に液状にして記録層
の形成に用いられるが、塗液の製造は結合剤（バインダ
ー）を用いたインキ状態とするのが好ましい。The above color-forming material is generally used in the form of a liquid for forming the recording layer, but it is preferable that the coating liquid is prepared in an ink state using a binder.

【００３９】結合剤（バインダー）としては、ポリスチ
レン、ポリブチルメタクリレート、ポリビニルアルコー
ル、変性ポリビニルアルコール、ポリビニルピロリド
ン、メチルセルロース、カルボキシメチルセルロース、
アラビアゴム、カゼイン、スチレン−ブタジエンラテッ
クス、ポリ酢酸ビニル、スチレン系樹脂、スチレン−ア
クリル系共重合体などが使用される。As the binder (binder), polystyrene, polybutyl methacrylate, polyvinyl alcohol, modified polyvinyl alcohol, polyvinylpyrrolidone, methyl cellulose, carboxymethyl cellulose,
Gum arabic, casein, styrene-butadiene latex, polyvinyl acetate, styrene resin, styrene-acrylic copolymer and the like are used.

【００４０】発色材料と結合剤（バインダー）との配合
割合は、前者１重量部に対して、後者０．２〜５重量
部、好ましくは０．５〜２重量部であり、０．７〜１．
５重量部が実用的である。The compounding ratio of the color forming material and the binder is 0.2 to 5 parts by weight, preferably 0.5 to 2 parts by weight, and 0.7 to 7 parts by weight with respect to 1 part by weight of the former. 1.
5 parts by weight is practical.

【００４１】感熱発色層の厚みは、０．５〜２０μｍ、
好ましくは１〜１０μｍ、さらに好ましくは１〜８μｍ
（いずれも固形分量）である。The thickness of the thermosensitive coloring layer is 0.5 to 20 μm,
Preferably 1-10 μm, more preferably 1-8 μm
(Both are solid contents).

【００４２】発色材料として水分散物を用いる場合は、
発色材料、結合剤（バインダー）および界面活性剤のご
とき分散助剤を含むものが用いられ、従来公知の材料及
び調製方法が用いられてよい。When an aqueous dispersion is used as the coloring material,
A material containing a coloring aid, a binder and a dispersion aid such as a surfactant may be used, and conventionally known materials and preparation methods may be used.

【００４３】このように構成された感熱記録層の基材と
反対の面には、サーマルヘッドにより記録時のスティッ
キングを向上させる目的で有機物質若しくは無機物質か
らなる耐熱保護層を設けてもよい。このような有機物質
としては、シリコーン樹脂、フッ素樹脂、エポキシ樹脂
などの耐熱性を有し、かつ滑性を有するものや、ウレタ
ンアクリレート樹脂、エポキシアクリレート樹脂などの
紫外線硬化型樹脂類が好ましい。また、無機物質として
は、Ａｌ₂Ｏ₃、ＳｉＯ₂、ＳｉＯ、ＭｇＯ、ＺｎＯなど
が挙げられ、これらはスパッタ法、真空蒸着法などによ
り耐熱保護層とされる。該保護層の厚みは、０．０５〜
１０μｍ、好ましくは０．５〜５μｍ、さらに好ましく
は０．５〜３μｍである。保護層の厚みが０．０５μｍ
未満では、スティッキング防止効果がなく、一方、１０
μｍを超えると印字性が低下する。A heat-resistant protective layer made of an organic substance or an inorganic substance may be provided on the surface of the heat-sensitive recording layer thus constructed, which is opposite to the substrate, for the purpose of improving sticking during recording by a thermal head. As such an organic substance, those having heat resistance and lubricity such as silicone resin, fluororesin and epoxy resin, and ultraviolet curable resins such as urethane acrylate resin and epoxy acrylate resin are preferable. In addition, examples of the inorganic substance include Al ₂ O ₃ , SiO ₂ , SiO, MgO, and ZnO, which are used as a heat-resistant protective layer by a sputtering method, a vacuum deposition method, or the like. The thickness of the protective layer is 0.05 to
The thickness is 10 μm, preferably 0.5 to 5 μm, and more preferably 0.5 to 3 μm. Thickness of protective layer is 0.05 μm
If it is less than 10, there is no sticking prevention effect, while on the other hand, 10
If it exceeds μm, the printability deteriorates.

【００４４】前記印字テープに用いられる支持体として
は、例えば、プラスチックフィルム、ゴム、金属、紙、
布、不織布などの材料が挙げられ、印字部のコントラス
トを向上させる配色を有するものが選択される。支持体
の厚みは、１０〜２００μｍであることが好ましい。支
持体の厚みが１０μｍ未満では、ハンドリング性に劣
り、一方、２００μｍを超えると柔軟性に欠ける。これ
ら支持体を前記感熱記録体に重ね合わせるには、公知の
接着剤、粘着剤を用いることができる。The support used for the printing tape is, for example, plastic film, rubber, metal, paper,
Materials such as cloth and non-woven fabric can be used, and one having a color arrangement that improves the contrast of the printed portion is selected. The thickness of the support is preferably 10 to 200 μm. When the thickness of the support is less than 10 μm, the handling property is poor, while when it exceeds 200 μm, the flexibility is poor. A publicly known adhesive or pressure-sensitive adhesive can be used to overlay these supports on the thermosensitive recording medium.

【００４５】感圧接着性を有する他の支持体としては、
例えば、酢酸ビニルの含有量が１０重量％以上のエチレ
ン−酢酸ビニル共重合体などの接着性を有する樹脂を単
体で用いてもよい。Other supports having pressure-sensitive adhesiveness include:
For example, an adhesive resin such as an ethylene-vinyl acetate copolymer having a vinyl acetate content of 10% by weight or more may be used alone.

【００４６】さらに、支持体として感圧接着剤層と剥離
ライナーとを有する支持体を用いてもよい。このような
剥離ライナーとしては、例えば、ポリエチレンの如く表
面離型性を有するものを用いてもよく、紙、あるいはポ
リエチレン以外のプラスチックのごとき表面離型性を有
さない基材の表面をシリコーン樹脂、フッ素樹脂のよう
な低接着性樹脂で被覆処理したものなどを用いてもよ
い。該剥離ライナーは、剥離作業性、ハンドリングなど
の点から３０〜５００μｍの厚みのものが使用できる。Further, a support having a pressure sensitive adhesive layer and a release liner may be used as the support. As such a release liner, for example, one having surface releasability such as polyethylene may be used, and the surface of a base material having no surface releasability such as paper or plastic other than polyethylene may be used as a silicone resin. Alternatively, those coated with a low adhesive resin such as a fluororesin may be used. As the release liner, a release liner having a thickness of 30 to 500 μm can be used from the viewpoints of release workability and handling.

【００４７】一方、感圧接着剤層は、感圧接着剤のみか
らなっていてもよく、また、プラスチックフィルム、ゴ
ム、金属、紙、布、不織布などの薄葉基材の両面に、感
圧接着剤層を設けたものであってもよい。このような感
圧性接着剤は、感熱記録層に悪影響を及ぼさないことが
好ましく、例えば、アルキル基の炭素数が２〜１２のア
クリル酸アルキルエステルと該エステルとの共重合可能
なビニル単量体とを前者５０〜１００重量％、後者５０
〜０重量％の範囲で重合してなる共重合物であって、重
合度が９５重量％以上、望ましくは９７重量％以上のも
のが好ましい。また、他の好ましい組成としては、例え
ば、天然ゴム、ブチルゴム、ポリイソブチレンゴム、ス
チレン−イソブチレン−スチレンブロックポリマー、ス
チレン−ブタジエン−スチレンブロックポリマ−などの
ゴム類単体、又はこれに石油系樹脂、ロジン、キシレン
樹脂などの粘着性付与樹脂をゴム類１００重量部に対し
て３〜２００重量部、好ましくは１５〜１２０重量部配
合してなるものが挙げられる。粘着性付与樹脂の配合量
が３重量部より少ないと、添加効果がなく、一方、２０
０重量部を超えると目的とする接着性が得られない。On the other hand, the pressure-sensitive adhesive layer may be composed of only the pressure-sensitive adhesive, and may be pressure-sensitively adhered to both sides of a thin film substrate such as plastic film, rubber, metal, paper, cloth and non-woven fabric. It may be provided with an agent layer. Such a pressure-sensitive adhesive preferably does not adversely affect the heat-sensitive recording layer. For example, a vinyl monomer copolymerizable with an alkyl acrylate whose alkyl group has 2 to 12 carbon atoms and the ester. And the former 50 to 100% by weight, the latter 50
It is a copolymer obtained by polymerization in the range of from 0 to 0% by weight, and the degree of polymerization is preferably 95% by weight or more, and more preferably 97% by weight or more. Other preferable compositions include, for example, natural rubber, butyl rubber, polyisobutylene rubber, styrene-isobutylene-styrene block polymer, styrene-butadiene-styrene block polymer, and other rubbers alone, or a petroleum resin, rosin. And a tackifying resin such as xylene resin in an amount of 3 to 200 parts by weight, preferably 15 to 120 parts by weight, based on 100 parts by weight of rubbers. If the compounding amount of the tackifying resin is less than 3 parts by weight, there is no effect of addition, while 20
If it exceeds 0 parts by weight, the desired adhesiveness cannot be obtained.

【００４８】上記感圧接着剤において、長期間にわたっ
て感熱記録層に悪影響を与えない接着剤としては、実質
上、接着剤中に残存モノマーや架橋成分がないスチレン
−イソブチレン−スチレンブロックポリマー、スチレン
−ブタジエン−スチレンブロックポリマーなどのゴムを
主成分とする感圧性接着剤が最も好ましい。このような
感圧接着剤層の厚みとしては、５〜２００μｍであるこ
とが好ましい。厚みが５μｍ未満では接着力が充分に発
揮できず、一方、２００μｍを超えると経済的でない。Among the above pressure-sensitive adhesives, as an adhesive which does not adversely affect the heat-sensitive recording layer for a long period of time, styrene-isobutylene-styrene block polymer, styrene- Most preferred are rubber-based pressure sensitive adhesives such as butadiene-styrene block polymers. The thickness of such a pressure-sensitive adhesive layer is preferably 5 to 200 μm. If the thickness is less than 5 μm, the adhesive strength cannot be sufficiently exhibited, while if it exceeds 200 μm, it is not economical.

【００４９】[0049]

【実施例】以下に本発明の実施例を示す。EXAMPLES Examples of the present invention will be shown below.

【００５０】［実施例１］下記の組成の感熱発色剤を１
５時間、ボールミルで分散、調整し、得られた溶液を透
明ポリエチレンテレフタレートフィルム（ＰＥＴ、５０
μｍ、コロナ処理品）上に乾燥被膜が５μｍになるよう
にワイヤーバーで塗工した。 ［組成］ （配合量） ３−ジブチルアミノ−６−メチル−７−フェニルアミノフルオラン ７．７重量部 ビスフェノールＡ １５．５重量部 ポリスチレン １６．０重量部 ポリブチルメタクリレート １．４重量部 シクロヘキサン ５９．４重量部 次いで、ポリジメチルシロキサンを含有するポリオレフ
ィン系樹脂をシクロヘキサンに溶解した液を、前記塗工
面に乾燥被膜が２μｍになるようにワイヤーバーで塗工
し、耐熱保護層を形成した。このようにして得られた感
熱記録体を一定の幅にスリットし、ロール状に巻いたス
プールを作製した。Example 1 A thermosensitive color developing agent having the following composition was used.
Disperse and adjust with a ball mill for 5 hours, and obtain the solution by using a transparent polyethylene terephthalate film (PET, 50
μm, corona-treated product) was coated with a wire bar so that the dry film had a thickness of 5 μm. [Composition] (Blending amount) 3-dibutylamino-6-methyl-7-phenylaminofluorane 7.7 parts by weight Bisphenol A 15.5 parts by weight Polystyrene 16.0 parts by weight Polybutyl methacrylate 1.4 parts by weight Cyclohexane 59 .4 parts by weight Next, a solution obtained by dissolving a polyolefin resin containing polydimethylsiloxane in cyclohexane was applied to the applied surface with a wire bar so that the dry film had a thickness of 2 μm to form a heat-resistant protective layer. The thermosensitive recording material thus obtained was slit into a certain width, and a spool wound into a roll was produced.

【００５１】一方、厚さ６μｍの透明コリエチレンテレ
フタレート（ＰＥＴ）の片面に、スチレン−ブタジエン
−スチレン（ＳＢＳ）系粘着剤を乾燥後１５μｍとなる
ように形成し、その面と反対側にはアクリル系粘着剤１
５μｍ、さらに両面離型処理をした剥離ライナーを貼り
合わせて支持体となる両面接着テープを作製した。さら
にこの両面接着テープを上記感熱記録体と同様にスリッ
トし、ロール状に巻いてスプールを作製した。On the other hand, a styrene-butadiene-styrene (SBS) -based adhesive was formed on one surface of transparent 6-μm-thick transparent coryethylene terephthalate (PET) so as to have a thickness of 15 μm after drying. System adhesive 1
A release liner having a thickness of 5 μm and further subjected to a release treatment on both sides was attached to prepare a double-sided adhesive tape as a support. Further, this double-sided adhesive tape was slit in the same manner as the thermosensitive recording medium and wound into a roll to prepare a spool.

【００５２】上記感熱記録体の感熱発色層側からサーマ
ルヘッドにてミラー反転印字し、両面接着テープのＳＢ
Ｓ系粘着剤面と貼り合わせた。その結果、透明ＰＥＴと
両面接着テープの間にサンドイッチされた感熱発色層の
所望の部分のみが発色した印字テープが作製された。こ
のテープは裏側の剥離ライナーを剥がすことにより、所
望の被着体へ貼り合わすことができた。Mirror reversal printing was performed with a thermal head from the thermosensitive coloring layer side of the thermosensitive recording medium, and SB of a double-sided adhesive tape was used.
It was attached to the S-based adhesive surface. As a result, a printing tape was produced in which only a desired portion of the thermosensitive coloring layer sandwiched between the transparent PET and the double-sided adhesive tape was colored. This tape was able to be attached to a desired adherend by peeling off the release liner on the back side.

【００５３】この印字テープは５０μｍの透明ＰＥＴで
カバーされているため、発色した文字が表面からの薬剤
により消色せず、耐摩擦性にも優れていた。また、発色
剤として用いられているロイコ染料の酸化劣化が透明な
ＰＥＴによる酸素遮断により少なくなり、良好な耐光性
が得られるようになった。Since this printing tape was covered with transparent PET having a thickness of 50 μm, the colored characters were not erased by the chemicals from the surface and were excellent in abrasion resistance. Further, the oxidation deterioration of the leuco dye used as the color former is reduced by the oxygen blocking by the transparent PET, and good light resistance can be obtained.

【００５４】［実施例２］下記の組成の感熱発色剤を３
０時間ボールミルで分散、調整し、得られた溶液を透明
ポリビニルアルコールフィルム（７５μｍ）上に乾燥被
膜が５μｍになるようにワイヤーバーで塗工した。 ［組成］ （配合量） ３−ジブチルアミノ−６−メチル−７−フェニルアミノフルオラン ７．７重量部 ビスフェノールＡ １５．５重量部 変性ポリビニルアルコール水溶液（固形分１０％） ３００重量部 次いで、変性ポリビニルアルコール水溶液にステアリン
酸亜鉛分散物を添加した耐熱保護層を乾燥被膜が２μｍ
になるように形成した。このようにして得られた感熱記
録体を一定の幅にスリットし、ロール状に巻いたスプー
ルを作製した。この感熱記録体を、実施例１と同様に、
印字後、両面接着テープと張り合わせて印字テープを作
製した。Example 2 A thermosensitive color developing agent having the following composition was used.
The mixture was dispersed and adjusted with a ball mill for 0 hours, and the resulting solution was coated on a transparent polyvinyl alcohol film (75 μm) with a wire bar so that the dry film thickness was 5 μm. [Composition] (Blending amount) 3-dibutylamino-6-methyl-7-phenylaminofluorane 7.7 parts by weight Bisphenol A 15.5 parts by weight Modified polyvinyl alcohol aqueous solution (solid content 10%) 300 parts by weight Next, modified 2 μm dry coating of heat-resistant protective layer made by adding zinc stearate dispersion to polyvinyl alcohol aqueous solution
Was formed. The thermosensitive recording material thus obtained was slit into a certain width, and a spool wound into a roll was produced. This thermosensitive recording medium was prepared in the same manner as in Example 1.
After printing, a double-sided adhesive tape was adhered to produce a printing tape.

【００５５】この印字テープの剥離ライナーを剥がし、
所望の被着体に貼り合わせた。この印字テープは発色し
た文字のうえに７５μｍのポリビニルアルコールフィル
ムがカバーされた形となっており、耐薬品性が極めて優
れると共に、耐光性に関しても良好であった。Peel off the release liner of this printing tape,
It was attached to a desired adherend. This printing tape had a color-developed character covered with a polyvinyl alcohol film of 75 μm, and thus was extremely excellent in chemical resistance and light resistance.

【００５６】［実施例３］実施例１に示す感熱記録体お
よび両面接着テープをそれぞれ１２ｍ／ｍ幅にスリット
してスプールを作製した。これをキングジム社製インク
リボンカセット（テプラ用）に各々挿入し、該インクリ
ボンカセットのインクリボンを除去した後、反転印字を
行った。その結果、発色した文字が印字された、接着テ
ープ付きの印字テープが作製された。このテープを所望
の被着体に貼り合わせた後、各種有機溶剤で擦過性を調
べたが、文字の消色もなく極めて耐久性のよいものが得
られた。Example 3 The thermosensitive recording medium and the double-sided adhesive tape shown in Example 1 were slit into a width of 12 m / m to prepare a spool. This was inserted into an ink ribbon cassette (for Tepra) manufactured by King Jim Co., Ltd., the ink ribbon of the ink ribbon cassette was removed, and then reverse printing was performed. As a result, a printing tape with an adhesive tape, on which colored characters were printed, was produced. After adhering this tape to a desired adherend, the rubbing property was examined with various organic solvents. As a result, it was possible to obtain a very durable one without decoloring characters.

【００５７】［比較例１］基材として耐熱性処理済みの
ＰＥＴ（厚さ６μｍ）を用い、耐熱未処理面側に感熱発
色層を乾燥後の厚みが約７μｍになるようにワイヤーバ
ーで塗布・乾燥した以外はすべて実施例１と同様に行
い、印字テープを作製した。Comparative Example 1 Heat-resistant treated PET (thickness 6 μm) was used as a substrate, and a heat-sensitive color developing layer was applied to the heat-resistant untreated surface side with a wire bar so that the thickness after drying was about 7 μm. A printing tape was prepared in the same manner as in Example 1 except that it was dried.

【００５８】該感熱記録テープの基材であるＰＥＴ側か
らサーマルヘッドにてミラー反転しない文字を印字し、
剥離紙を剥がして被着体に貼り合わせ、印字テープの耐
久性をチェックした。Characters which are not mirror-inverted are printed by a thermal head from the PET side which is the base material of the thermal recording tape,
The release paper was peeled off and adhered to the adherend, and the durability of the printing tape was checked.

【００５９】カバーされたフィルムの厚さが６μｍと薄
く、鋭利なもので表面をこするとフィルムが引き裂かれ
た。また、印字エネルギーを大きくすると薄いＰＥＴの
耐熱性が不十分で印字部のＰＥＴが破損し、耐薬品性が
低下した。また、６μｍのＰＥＴの酸素バリヤー性が不
十分であり、酸素劣化があるため、印字の耐久性が不十
分であった。The film covered was as thin as 6 μm, and the film was torn when the surface was rubbed with a sharp object. Further, when the printing energy was increased, the heat resistance of the thin PET was insufficient, the PET of the printed part was damaged, and the chemical resistance was lowered. In addition, the oxygen barrier property of 6 μm PET was insufficient and there was oxygen deterioration, so the printing durability was insufficient.

【００６０】［比較例２］実施例１において、両面とも
アクリル系粘着剤の両面接着テープを使用した以外は、
すべて実施例１と同様にして印字テープを作製した。得
られた印字テープは、アクリル系粘着剤に含有の成分に
より、発色した文字が消色した。特に昇温・加湿保存時
の消色が顕著であった。[Comparative Example 2] In Example 1, except that a double-sided adhesive tape having an acrylic adhesive on both sides was used.
A printing tape was produced in the same manner as in Example 1. In the obtained printing tape, the colored characters were decolored due to the components contained in the acrylic adhesive. In particular, the discoloration during storage at elevated temperature and humidification was remarkable.

【００６１】[0061]

【発明の効果】本発明によれば、記録体の感熱記録層に
直接あるいは薄層の耐熱保護層を介して反転印字されて
いるので、記録体を構成する無色あるいは有色透明な可
撓性基材の厚みには実質的に制限されず、耐薬品性、機
械的強度にも優れ、しかも酸素透過による感熱記録層の
劣化のない印字テープが得られる。さらにインクリボン
を用いるタイプに比してリボン繰り出し機構が不要であ
るので装置が簡略化できる。According to the present invention, since the reversal printing is carried out directly on the heat-sensitive recording layer of the recording medium or through the thin heat-resistant protective layer, a colorless or colored transparent flexible group constituting the recording medium is formed. The thickness of the material is not substantially limited, and a printing tape having excellent chemical resistance, mechanical strength, and deterioration of the heat-sensitive recording layer due to oxygen permeation can be obtained. Further, as compared with the type using an ink ribbon, a ribbon feeding mechanism is not required, so that the device can be simplified.

【図面の簡単な説明】[Brief description of drawings]

【図１】本発明印字テープの作成方法の一具体例を示す
模式的な断面図であるFIG. 1 is a schematic cross-sectional view showing a specific example of a method for producing a printing tape of the present invention.

【図２】本発明の感熱記録テープカセットの一具体例を
示す断面図である。FIG. 2 is a cross-sectional view showing a specific example of the thermal recording tape cassette of the present invention.

【符号の説明】[Explanation of symbols]

１ 印字テープ ２ 感熱記録体 ３ 支持体 ４ 基材 ５ 感熱発色層 ６ 耐熱保護層 ７ 薄葉基材 ８ａ 感圧接着剤層 ８ｂ 感圧接着剤層 ９ 剥離ライナー １０ サーマルヘッド １１ ローラー １２ ローラー ２０ 感熱記録テープカセット ２１ 感熱記録体スプール ２２ 支持体スプール ２３ａ スプール軸 ２３ｂ スプール軸 ２４ ガイド ２５ 印字部 ２６ ローラー ２７ ガイド ２８ 印字テープ ２９ サーマルヘッド ３０ ローラー DESCRIPTION OF SYMBOLS 1 Printing tape 2 Thermosensitive recording medium 3 Support 4 Base material 5 Thermosensitive coloring layer 6 Heat-resistant protective layer 7 Thin leaf base material 8a Pressure-sensitive adhesive layer 8b Pressure-sensitive adhesive layer 9 Release liner 10 Thermal head 11 Roller 12 Roller 20 Thermal recording Tape cassette 21 Thermal recording medium spool 22 Support spool 23a Spool shaft 23b Spool shaft 24 Guide 25 Printing section 26 Roller 27 Guide 28 Printing tape 29 Thermal head 30 Roller

───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.⁶ 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｇ０９Ｆ 3/10 Ｂ Ｂ４１Ｍ 5/18 Ｈ (72)発明者 三原 尚史 大阪府茨木市下穂積１丁目１番２号 日東 電工株式会社内 (72)発明者 菅原 英男 大阪府茨木市下穂積１丁目１番２号 日東 電工株式会社内─────────────────────────────────────────────────── ─── Continuation of front page (51) Int.Cl. ⁶ Identification number Internal reference number FI Technical display location G09F 3/10 B B41M 5/18 H (72) Inventor Naofumi Mihara 1-chome Shimohozumi, Ibaraki-shi, Osaka 1-2 No. Nitto Denko Corporation (72) Inventor Hideo Sugawara 1-2 1-2 Shimohozumi, Ibaraki City, Osaka Prefecture Nitto Denko Corporation

Claims (3)

【特許請求の範囲】[Claims] 【請求項１】 透明性を有する可撓性基材および該基材
の片面に設けられた感熱発色層を含む感熱記録体の感熱
発色層に反転印字を行った後、この感熱記録体の感熱発
色層側に、表面が感圧接着性を有する支持体を貼付して
なる印字テープの作製法。1. A thermosensitive coloring layer of a thermosensitive recording medium comprising a transparent flexible substrate and a thermosensitive coloring layer provided on one surface of the substrate, after reverse printing is performed on the thermosensitive coloring layer, the thermosensitive recording medium is heat-sensitive. A method for producing a printing tape in which a support having a pressure-sensitive adhesive surface is attached to the color forming layer side. 【請求項２】（ｉ）透明性を有する可撓性基材および該
基材の片面に設けられた感熱発色層を含むロール状の感
熱記録体、（ｉｉ）前記感熱記録体を巻戻し、印字部を
通して繰り出す機構、（ｉｉｉ）表面が感圧接着性を有
するロール状の支持体、および（ｉｖ）印字後の前記感
熱発色層に支持体を貼付して繰り出す機構、とを有する
感熱記録テープカセット。2. A roll-shaped thermosensitive recording medium comprising (i) a transparent flexible substrate and a thermosensitive coloring layer provided on one surface of the substrate, and (ii) rewinding the thermosensitive recording medium. A heat-sensitive recording tape having a mechanism for feeding through a printing section, (iii) a roll-shaped support having a pressure-sensitive adhesive surface, and (iv) a mechanism for sticking the support onto the thermosensitive coloring layer after printing and feeding it. cassette. 【請求項３】 感熱発色層と接触する支持体がゴムを主
成分とする感圧接着剤層を有する請求項２の感熱記録テ
ープカセット。3. The thermosensitive recording tape cassette according to claim 2, wherein the support contacting with the thermosensitive coloring layer has a pressure sensitive adhesive layer containing rubber as a main component.