JPH07304937A - Polyester film for magnetic recording medium - Google Patents
Polyester film for magnetic recording mediumInfo
- Publication number
- JPH07304937A JPH07304937A JP9724594A JP9724594A JPH07304937A JP H07304937 A JPH07304937 A JP H07304937A JP 9724594 A JP9724594 A JP 9724594A JP 9724594 A JP9724594 A JP 9724594A JP H07304937 A JPH07304937 A JP H07304937A
- Authority
- JP
- Japan
- Prior art keywords
- particles
- film
- polyester
- laminated
- polyester film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】[0001]
【産業上の利用分野】本発明はポリエステルフィルムに
関するものであり、特に使用耐久性、スリット加工性に
優れた磁気記録媒体、特にビデオテープに好適なポリエ
ステルフィルムに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a polyester film, and more particularly, to a polyester film suitable for a magnetic recording medium which is excellent in use durability and slit workability, particularly a video tape.
【0002】[0002]
【従来の技術】ポリエステルフィルムとしては、フィル
ム加工性、走行性などを改善するため、フィルム表面に
突起を形成するため、炭酸カルシウムやコロイダルシリ
カなどの不活性粒子を含有せしめたフィルムが知られて
いる(たとえば特開昭59−171623号公報)。2. Description of the Related Art Polyester films are known to contain inert particles such as calcium carbonate and colloidal silica in order to form projections on the film surface in order to improve film processability and running property. (For example, JP-A-59-171623).
【0003】[0003]
【発明が解決しようとする課題】しかし、特にポリエス
テルフィルムを磁気記録媒体用として用いる場合には、
磁気記録媒体製造工程での磁性体塗布・カレンダー工程
などで工程速度の増大にともない、接触するロールなど
によってポリエステルフィルム表面、特に微細な突起を
有するフィルム表面が削りとられたり、傷がつくという
欠点が最近問題となっている。また、磁性体を塗布後ス
リットしビデオテープに加工する段階で、フィルム切断
面で切り粉が発生し、磁性面へ付着することにより映像
が悪化する問題点が見られる。また、従来のものでは、
高速転写などのダビングの増速化にともない、ダビング
時の画質低下のために、画質すなわちS/N(シグナル
/ノイズ比)も不十分という欠点があった。これらの欠
点を解決するため、例えば含有せしめる粒子の形状や粒
径のバラツキを規制する方法(たとえば特開平2−49
033号公報)などが試みられているが効果は不十分
で、最近の品質要求には満足できなかった。さらに、2
種類の粒子を組み合わせる方法(例えば特開平2−21
6031号公報)が試みられ、その原料は常法によりエ
ステル交換触媒として酢酸マンガンを用い、重合触媒と
して三酸化アンチモンを用いて得たと記載されている
が、かかる最近の品質要求を十分に満足するには至って
いない。不活性粒子と含有金属の関係について検討を重
ねた結果、フィルム中において、含有する特定粒径範囲
の不活性粒子量に対して特定範囲量のマンガン化合物を
共存させることにより、磁気記録媒体用フィルムの品
質、特にスリット特性が大幅に改善できることを見出だ
し本発明に至った。However, especially when a polyester film is used for a magnetic recording medium,
With the increase of process speed in the magnetic material coating / calendering process in the magnetic recording medium manufacturing process, the polyester film surface, especially the film surface with fine projections, is scratched or scratched by the contacting rolls. Has become a problem recently. In addition, there is a problem in that, when the magnetic material is applied and then slit and processed into a video tape, chips are generated on the cut surface of the film and adhere to the magnetic surface to deteriorate the image. Also, in the conventional one,
There is a drawback in that the image quality, that is, the S / N (signal / noise ratio), is insufficient because the image quality is deteriorated during dubbing as the speed of dubbing such as high-speed transfer is increased. In order to solve these drawbacks, for example, a method of controlling variations in the shape and particle size of particles to be contained (for example, JP-A-2-49).
No. 033 gazette) has been tried, but the effect is insufficient, and the recent quality requirements cannot be satisfied. Furthermore, 2
A method of combining different types of particles (for example, Japanese Patent Laid-Open No. 2-21
No. 6031) was tried and the starting material was obtained by using manganese acetate as a transesterification catalyst and antimony trioxide as a polymerization catalyst by a conventional method, but these recent quality requirements are sufficiently satisfied. Has not reached. As a result of repeated studies on the relationship between the inert particles and the contained metal, a film for a magnetic recording medium was obtained by allowing a manganese compound in the specified range to coexist with the amount of the inert particles in the specified particle size range contained in the film. It was found that the quality, especially the slit characteristics, can be greatly improved, and the present invention has been completed.
【0004】すなわち、本発明はかかる従来の問題を解
決し、特に高速工程で、フィルム表面が削りとられたり
フィルム表面に傷がつきにくく(以下、耐スクラッチ性
という)するとともに、フィルムを切断加工する時に、
切断面で切り粉の発生の少なく(以下スリット特性とい
う)、さらに高速ダビング時などの画質低下の少ない、
すなわち電磁変換特性のよい(以下電磁変換特性に優れ
るという)、優れた表面特性をもつ磁気記録媒体用ポリ
エステルフィルムを提供することを目的とする。That is, the present invention solves such a conventional problem, particularly in a high speed process, the film surface is less likely to be scraped or scratched (hereinafter referred to as scratch resistance), and the film is cut and processed. When
Less generation of chips on the cut surface (hereinafter referred to as slit characteristics), and less deterioration of image quality during high-speed dubbing,
That is, an object of the present invention is to provide a polyester film for a magnetic recording medium, which has good electromagnetic conversion characteristics (hereinafter referred to as excellent electromagnetic conversion characteristics) and excellent surface characteristics.
【0005】[0005]
【課題を解決するための手段】この目的に沿う本発明
は、平均粒径が0.1〜2μmの不活性粒子を0.05
〜3重量%含有し、かつ該不活性粒子1gに対し0.0
1×10-3〜0.4×10-3モルのマンガン化合物を含
有する磁気記録媒体用ポリエステルフィルムから成る。According to the present invention for this purpose, an inert particle having an average particle diameter of 0.1 to 2 .mu.m is added to 0.05.
% To 3% by weight and 0.0 per 1 g of the inert particles.
It is composed of a polyester film for a magnetic recording medium containing 1 × 10 −3 to 0.4 × 10 −3 mol of a manganese compound.
【0006】本発明を構成するポリエステルは、ポリエ
チレンテレフタレート、ポリエチレン2・6−ナフタレ
ートなどであり、該ポリエステルはホモポリエステルで
あっても、コポリエステルであってもよい。共重合成分
の例としては、アジピン酸、セバチン酸、フタル酸、イ
ソフタル酸、5−ナトリウムスルホイソフタル酸、トリ
メリット酸などの多価カルボン酸成分、あるいは、ジエ
チレングリコール、テトラメチレングリコール、ヘキサ
メチレングリコール、プロピレングリコール、ネオペン
チルグリコール、ポリオキシアルキルグリコール、p−
キレングリコール、1,4−シクロヘキシルジメタノー
ルなどの多価アルコール成分などが挙げられる。また、
熱安定剤、改質剤、酸化防止剤などを含んでいても何等
差し支えない。The polyester constituting the present invention is polyethylene terephthalate, polyethylene 2.6-naphthalate, etc. The polyester may be a homopolyester or a copolyester. Examples of the copolymerization component include polycarboxylic acid components such as adipic acid, sebacic acid, phthalic acid, isophthalic acid, 5-sodium sulfoisophthalic acid and trimellitic acid, or diethylene glycol, tetramethylene glycol, hexamethylene glycol, Propylene glycol, neopentyl glycol, polyoxyalkyl glycol, p-
Examples thereof include polyhydric alcohol components such as xylene glycol and 1,4-cyclohexyldimethanol. Also,
It does not matter if it contains a heat stabilizer, a modifier, an antioxidant and the like.
【0007】さらに、その固有粘度は0.5以上が好ま
しく、さらに好ましくは0.55以上である。Further, its intrinsic viscosity is preferably 0.5 or more, more preferably 0.55 or more.
【0008】本発明のポリエステルフィルムは、平均粒
径が0.1〜2μmの不活性粒子を0.05〜3重量%
含有することが必要である。平均粒径は好ましくは0.
2〜1.5μm、さらに好ましくは、0.2〜1μmの
粒子であり、含有量は好ましくは0.15〜1.5重量
%、さらに好ましくは0.2〜1.0重量%である。平
均粒径が0.1μm以下、含有量が0.05重量%以下
では充分な走行特性を得るには不十分であり、平均粒径
が2μm以上、含有量が1.5重量%以上では良好な電
磁変換特性が得られない。The polyester film of the present invention contains 0.05 to 3% by weight of inert particles having an average particle size of 0.1 to 2 μm.
It is necessary to contain. The average particle size is preferably 0.
The particle size is 2 to 1.5 μm, more preferably 0.2 to 1 μm, and the content is preferably 0.15 to 1.5% by weight, more preferably 0.2 to 1.0% by weight. When the average particle size is 0.1 μm or less and the content is 0.05% by weight or less, it is insufficient to obtain sufficient running characteristics, and when the average particle size is 2 μm or more and the content is 1.5% by weight or more, it is good. Electromagnetic conversion characteristics cannot be obtained.
【0009】ここで、不活性粒子は一種である必要はな
く、2種類以上の不活性粒子の混合系であっても良い。
さらに、含有する不活性粒子の粒径は均一であることが
好ましく、特に粗大な粒子を含まないことが電磁変換特
性、耐スクラッチ性がより一層良好になるので望まし
い。必要に応じ、サンドグラインダーなどによる分散処
理、遠心沈降処理などによる分級処理、さらに濾過など
の方法を用いる。不活性粒子の種類は特に限定されるも
のでないが、上記の好ましい粒子特性を満足するには、
炭酸カルシウム、コロイダルシリカ、有機高分子微粒
子、アルミナ、ジルコニア、酸化チタンなどの粒子が用
いられる。炭酸カルシウムは合成法によって製造された
ものが粒径分布が均一であり好ましく、コロイダルシリ
カもアルコキシド法、水ガラス法などで製造された球形
なシリカ粒子が粒径分布が均一で好ましい。有機高分子
微粒子としては、例えばポリスチレン、架橋ポリスチレ
ン、スチレン・アクリル系架橋粒子、シリコーン粒子、
など一部がポリエステルに不溶な粒子が挙げられる。好
ましくは、ブチルアクリレート−ジビニルベンゼン共重
合体、エチルベンゼン−ジビニルベンゼン共重合体、2
−エチルヘキシルアクリレート−エチレングリコールジ
メタアクリレート共重合体などの架橋微粒子が挙げら
れ、さらにそれ以上のモノマー成分からなる共重合体で
あっても良い。また、その耐熱性は熱天秤による熱分解
温度(10%減量)が350℃以上であることが好まし
い。Here, the number of the inert particles need not be one, and may be a mixed system of two or more kinds of the inert particles.
Furthermore, it is preferable that the particle diameter of the inert particles contained is uniform, and it is particularly preferable not to include coarse particles because the electromagnetic conversion characteristics and scratch resistance are further improved. If necessary, methods such as dispersion treatment using a sand grinder, classification treatment such as centrifugal sedimentation treatment, and filtration are used. The type of inert particles is not particularly limited, but to satisfy the above preferable particle characteristics,
Particles of calcium carbonate, colloidal silica, organic polymer fine particles, alumina, zirconia, titanium oxide and the like are used. Calcium carbonate produced by a synthetic method is preferable because it has a uniform particle size distribution, and colloidal silica is also preferable because spherical silica particles produced by an alkoxide method, a water glass method or the like have a uniform particle size distribution. Examples of the organic polymer fine particles include polystyrene, crosslinked polystyrene, styrene / acrylic crosslinked particles, silicone particles,
Part of the particles are insoluble in polyester. Preferably, butyl acrylate-divinylbenzene copolymer, ethylbenzene-divinylbenzene copolymer, 2
Examples thereof include crosslinked fine particles such as an ethylhexyl acrylate-ethylene glycol dimethacrylate copolymer, and may be a copolymer composed of more monomer components. The heat resistance is preferably such that the thermal decomposition temperature (10% reduction) by a thermobalance is 350 ° C. or higher.
【0010】とくにこれらの有機高分子微粒子、炭酸カ
ルシウムは単独または併用して含有することで良好な効
果が得られれ、他の粒子でも平均粒径などの本発明の要
件を満足することにより充分本発明の効果を発揮しうる
が、不活性粒子の少なくとも一部に、炭酸カルシウムま
たは有機高分子微粒子を用いる場合、特にスリット特性
に良好な効果が得られる。Particularly, these organic polymer fine particles and calcium carbonate are contained alone or in combination to obtain a good effect, and other particles can be sufficiently prepared by satisfying the requirements of the present invention such as the average particle diameter. Although the effect of the invention can be exerted, particularly when calcium carbonate or organic polymer fine particles are used for at least a part of the inert particles, a good effect can be obtained particularly for slit characteristics.
【0011】これらの不活性粒子は、粒子表面を界面活
性剤、高分子化合物などで処理あるいはコーティングし
て用いることも何等さしつかえない。特に重合過程での
分散性の改良、フィルム中でのポリエステルとの親和性
改良のため、界面活性剤などで処理しポリエステルに対
する親和性を改善する方法が好ましく採用される。These inert particles may be used by treating or coating the surface of the particles with a surfactant, a polymer compound or the like. In particular, in order to improve the dispersibility in the polymerization process and the affinity with the polyester in the film, a method of improving the affinity with the polyester by treating with a surfactant is preferably adopted.
【0012】また、本発明の効果を阻害されない範囲
で、カルシウムおよびリチウム元素などを含む析出内部
粒子を併用して含有せしめても何等さしつかえない。[0012] In addition, precipitation internal particles containing elements such as calcium and lithium may be used in combination as long as the effects of the present invention are not impaired.
【0013】また、本発明の不活性粒子とは別に、微細
な粒子を併用して含有することにより、さらに好ましい
結果が得られる。これらの微細粒子としては5〜50n
mの粒子径を有する多数の一次粒子からなる凝集体粒子
が好適であり、例えばジルコニア、シリカ、アルミナな
どを主成分とする凝集体粒子の併用により、耐スクラッ
チ性改良などの相乗効果が期待できる。併用にあたって
は本発明の効果を阻害しないように、凝集体二次粒子径
が少なくとも0.5μm以下、望ましくは0.2μm以
下の凝集体粒子を0.5重量%以下添加することが好ま
しい。Further, in addition to the inert particles of the present invention, by containing fine particles in combination, more preferable results can be obtained. 5 to 50n for these fine particles
Aggregate particles composed of a large number of primary particles having a particle size of m are suitable, and for example, a synergistic effect such as scratch resistance improvement can be expected by the combined use of the agglomerate particles containing zirconia, silica, alumina or the like as a main component. . In combination, it is preferable to add 0.5% by weight or less of aggregate particles having an aggregate secondary particle diameter of at least 0.5 μm or less, preferably 0.2 μm or less so as not to impair the effects of the present invention.
【0014】本発明においては、含有する平均粒径が
0.1〜2μmの不活性粒子1gに対し0.01×10
-3〜0.4×10-3モルのマンガン化合物を含有するこ
とが必要である。In the present invention, 0.01 × 10 is added to 1 g of the inert particles having an average particle diameter of 0.1 to 2 μm.
It is necessary to contain -3 to 0.4x10 -3 mol of the manganese compound.
【0015】本発明者らは磁気材料用途、とくにビデオ
テープにおける電磁変化特性の向上について検討を重
ね、特にビデオテープの品質特性として重要なドロップ
アウト(映像信号の欠落)を減少するにはテープの表面
が傷がつきにくくし耐スクラッチ性を向上し表面での削
れによる粉などの発生を減少することに加え、テープ化
工程でのスリット切り粉がテープ上に付着することによ
る影響も極めて大きいことを確認した。このため、さら
に検討を重ねた結果、含有する不活性粒子を適正化する
とともに、特定量のマンガン化合物を含有することで電
磁変換特性を満足させ、同時にスリット特性を向上でき
ることを見出だし本発明に至ったものである。The inventors of the present invention have conducted extensive studies on the improvement of electromagnetic change characteristics in magnetic material applications, particularly in video tapes, and in particular, in order to reduce dropouts (missing video signals), which are important as quality characteristics of video tapes, The surface is less likely to be scratched, scratch resistance is improved, the generation of powder due to scraping on the surface is reduced, and the effect of slit cutting powder adhering to the tape during the tape forming process is also extremely large. It was confirmed. Therefore, as a result of further studies, it was found that while appropriately optimizing the inert particles to be contained, by satisfying the electromagnetic conversion characteristics by containing a specific amount of manganese compound, it is possible to improve the slit characteristics at the same time. It has come.
【0016】ここで含有するマンガン化合物はフィルム
中おいて均一に存在していることが好ましく、実質的に
粒子として確認できない0.05μm以下の微小粒子と
して、好ましくは0.01μm以下の微小粒子、さらに
好ましくは実態的に粒子として観察されずフィルム中に
含有されていることが好ましい。マンガン化合物が0.
05μmを越える粒子として存在すると効果が少なく、
スリット特性を改善できない場合がある。マンガン化合
物としては酢酸マンガン、修酸マンガンなどの有機酸
塩、塩化マンガン、硫酸マンガンなどの無機塩などポリ
エステルと相溶性の良好な化合物が好ましいが、相溶性
の劣る酸化マンガン、炭酸マンガンなどであっても添加
にあたって十分に微細分布させ効果を得ることができ
る。さらに、マンガン化合物は触媒として添加するもの
であってもよい。The manganese compound contained here is preferably present uniformly in the film, and as fine particles of 0.05 μm or less, which cannot be substantially confirmed as particles, preferably 0.01 μm or less, More preferably, it is contained in the film because it is not actually observed as particles. Manganese compound is 0.
When present as particles exceeding 05 μm, the effect is small,
In some cases, the slit characteristics cannot be improved. As the manganese compound, compounds having good compatibility with polyester such as organic acid salts such as manganese acetate and manganese oxalate, inorganic salts such as manganese chloride and manganese sulfate are preferable, but manganese oxide and manganese carbonate having poor compatibility are preferable. However, the effect can be obtained by sufficiently finely distributing the additives. Further, the manganese compound may be added as a catalyst.
【0017】さらに、マンガン化合物の含有量は平均粒
径が0.1〜2μmの不活性粒子1gに対し0.01×
10-3〜0.4×10-3モルであることが必要であり、
好ましくは、0.03〜0.3×10-3モルで、さらに
は0.05〜0.25×10-3モルが好ましい。含有量
が0.01×10-3未満ではスリット特性の改良効果が
なくなり、0.4×10-3モルを越えるとポリマ色調が
劣化し好ましくない。Further, the content of the manganese compound is 0.01 × with respect to 1 g of the inert particles having an average particle size of 0.1 to 2 μm.
It is necessary to be 10 −3 to 0.4 × 10 −3 mol,
The amount is preferably 0.03 to 0.3 × 10 −3 mol, more preferably 0.05 to 0.25 × 10 −3 mol. When the content is less than 0.01 × 10 −3 , the effect of improving the slit characteristics is lost, and when it exceeds 0.4 × 10 −3 mol, the polymer color tone is deteriorated, which is not preferable.
【0018】マンガン化合物は、フィルムの原料として
用いるポリエステル中に含有させておくことが好まし
く、例えば、あらかじめマンガン化合物を多量に含有す
るマスターポリマを準備しておき、フィルム製造工程の
原料ポリマ調合工程で他の原料ポリマと混合する方法が
好ましい。さらにポリエステルの製造工程あるいは製造
に供されるポリエステルのオリゴマー合成段階で触媒な
どと同様に添加することによっても達成でき、さらに、
粒子を含有するマスターポリマの製造工程で、添加する
粒子調製工程であらかじめ粒子スラリーの中に添加する
方法も好ましく採用できる。The manganese compound is preferably contained in the polyester used as a raw material for the film. For example, a master polymer containing a large amount of the manganese compound is prepared in advance, and the raw material polymer blending step in the film manufacturing step is performed. The method of mixing with another raw material polymer is preferable. Furthermore, it can be achieved by adding the same as a catalyst in the step of synthesizing polyester or synthesizing the oligomer of polyester to be used for production.
A method of preliminarily adding to the particle slurry in the step of preparing particles to be added in the step of producing the master polymer containing particles can also be preferably adopted.
【0019】フィルムの形態は単層のフィルムであって
も積層構造のフィルムであっても良く、特に限定される
ものではないが、積層構造のフィルムの場合に添加する
不活性粒子により効率良く優れた表面特性が容易に得ら
れ有利である。The form of the film may be a single-layer film or a film having a laminated structure, and is not particularly limited, but it is excellent in efficiency due to the inert particles added in the case of a film having a laminated structure. It is advantageous that the surface characteristics are easily obtained.
【0020】ここで、積層構造フィルムを例としてさら
に詳細に説明する。積層フィルムは、少なくとも2層構
造であって、3層あるいは4層以上の構造であっても良
く、さらに3層構造の場合が本発明の効果を発現させる
点で好ましい。Here, the laminated structure film will be described in more detail as an example. The laminated film may have at least a two-layer structure, and may have a three-layer structure or a four-layer structure or more, and a three-layer structure is preferable from the viewpoint of exhibiting the effect of the present invention.
【0021】本発明における不活性粒子は、積層部のフ
ィルム表面に微細な突起を形成するとともに、該粒子が
削り取られにくいようにするため、積層部の厚みに対す
る積層部に含有される粒子の平均粒径の比が0.2〜5
0の範囲とすることが好ましく、さらには0.5〜10
の範囲内にあることが好ましい。積層部の基層部に対す
る厚みの比率は40%以下とすることが積層部に含有す
る粒子による表面突起形成効果を発現させる点で好まし
く、さらには20%以下が好ましい。The inert particles in the present invention form fine projections on the film surface of the laminated portion and, in order to prevent the particles from being scraped off easily, the average of the particles contained in the laminated portion with respect to the thickness of the laminated portion is Particle size ratio is 0.2-5
The range of 0 is preferable, and 0.5 to 10 is more preferable.
It is preferably within the range. The thickness ratio of the laminated portion to the base layer portion is preferably 40% or less from the viewpoint of exhibiting the effect of forming surface protrusions by the particles contained in the laminated portion, and more preferably 20% or less.
【0022】基層部のポリエステルは実質的に粒子を含
まないポリエステルであってもよいし、粒子を含んでい
ても良い。粒子を含んでいる場合の粒子種としては特に
制限されるものでなく、例えば、無機粒子として炭酸カ
ルシウム、シリカ、カオリン、アルミナ、硫酸バリウ
ム、酸化チタンなどポリエステルに不溶な微細粒子でも
良いし、また、架橋ポリスチレンなどの有機粒子が含ま
れていても良いし、カルシウムあるいはリチウムなどを
含む内部粒子を含んでいても良い。The polyester of the base layer portion may be a polyester which does not substantially contain particles, or may contain particles. The type of particles in the case of containing particles is not particularly limited, for example, calcium carbonate as an inorganic particle, silica, kaolin, alumina, barium sulfate, may be fine particles insoluble in polyester such as titanium oxide, or Alternatively, organic particles such as crosslinked polystyrene may be contained, or internal particles containing calcium or lithium may be contained.
【0023】基層部ポリエステルに含まれる粒子は、積
層部によってなされる表面形成を実質的に阻害しないこ
とが望ましく、含有粒子の最大粒子径は積層部に含まれ
る最大粒子径の少なくとも2.0倍以下とするのが好ま
しく、さらには1.5倍以下にするのが好ましい。2.
0倍を越えると基層部の粒子の影響を積層部で隠蔽でき
ず、粗大突起発生の原因となる場合がある。また、積層
部ポリエステルは該積層フィルムあるいは他の品種の生
産段階などで発生する非製品部分などを主体とする回収
原料を含んでいても良い。It is desirable that the particles contained in the base layer part polyester do not substantially interfere with the surface formation performed by the laminated part, and the maximum particle size of the contained particles is at least 2.0 times the maximum particle size contained in the laminated part. The ratio is preferably below, and more preferably 1.5 times or less. 2.
If it exceeds 0 times, the influence of the particles in the base layer cannot be covered by the laminated portion, which may cause the generation of coarse protrusions. In addition, the polyester in the laminated portion may contain a recovered raw material mainly composed of a non-product portion generated in the production stage of the laminated film or other varieties.
【0024】基層部に本発明における0.1〜2μmの
不活性粒子を0.05〜3重量%の範囲内に含有させて
いる場合、該不活性粒子1gに対し0.01×10-3〜
0.4×10-3モルのマンガン化合物を含有させること
で、本発明のスリット特性を得ることができる。マンガ
ン化合物は積層部および基層部の両方に含有させてるこ
とで本発明の効果が得られるが、積層部および基層部の
どちらかの一方に含有させることが好ましい。さらに積
層部において突起形成のための不活性粒子とともにマン
ガン化合物を含有させ、スクラッチ特性と耐スクラッチ
特性および電磁変換特性を両立させる場合がより好まし
い。When the base layer portion contains the inert particles of 0.1 to 2 μm of the present invention in the range of 0.05 to 3% by weight, 0.01 × 10 −3 per 1 g of the inert particles. ~
By containing 0.4 × 10 −3 mol of the manganese compound, the slit characteristics of the present invention can be obtained. The effect of the present invention can be obtained by including the manganese compound in both the laminated portion and the base layer portion, but it is preferable to include the manganese compound in either one of the laminated portion and the base layer portion. Further, it is more preferable to include a manganese compound together with the inactive particles for forming the protrusions in the laminated portion to achieve both scratch characteristics, scratch resistance characteristics and electromagnetic conversion characteristics.
【0025】本発明においては、磁性剤との接着性の改
良、帯電防止などのために、帯電防止剤などの塗布層を
少なくとも片面に設けても何等差し支えない。In the present invention, a coating layer of an antistatic agent or the like may be provided on at least one side in order to improve the adhesiveness with a magnetic agent and prevent electrification.
【0026】磁気記録媒体として十分な走行性を得るた
めにはフィルム表面の粗さが適性であることが必要であ
り、フィルム表面の中心線平均表面粗さRaは5〜50
nm、好ましくは8〜30nm、さらに好ましくは10
〜25nmである。In order to obtain sufficient runnability as a magnetic recording medium, it is necessary that the roughness of the film surface is appropriate, and the center line average surface roughness Ra of the film surface is 5 to 50.
nm, preferably 8 to 30 nm, more preferably 10
Is about 25 nm.
【0027】本発明を構成する磁気媒体用ポリエステル
フィルムは、常法により二軸配向することが好ましく、
厚みは3〜30μmが好ましく、さらには5〜20μm
の範囲のものが好ましく適用される。The polyester film for magnetic media constituting the present invention is preferably biaxially oriented by a conventional method,
The thickness is preferably 3 to 30 μm, more preferably 5 to 20 μm
Those in the range of are preferably applied.
【0028】次に、本発明のフィルムの製造方法を複合
フィルムの場合を例に説明する。基層部ポリエステルの
少なくとも片面に本発明の積層部ポリエステルが共押出
により積層され、シート状に形成された後二軸に延伸さ
れ、二軸延伸積層ポリエステルフィルムとされる。ここ
で共押出による積層とは、積層部および基層部のポリエ
スル原料をそれぞれ異なる押出装置で押出し、口金から
積層シートを吐出する前にこれらを積層することをい
う。この積層は、シート状に成形、吐出するための口金
内(例えばマニホールド)で行っても良いが、前述のご
とく積層厚みが薄いことから、口金に導入する前のポリ
マ配管内で行うことが好ましい。特に、ポリマ管内の積
層部を、矩形に形成しておくと、幅方向に均一に積層で
きるのでとくに好ましい。ポリマ管内矩形積層部で積層
された溶融ポリマは、口金内マニホルドでシート幅方向
に所定幅まで拡幅され、口金からシート状に吐出された
後、二軸に延伸される。したがって、たとえ二軸配向後
の積層フィルムが極薄であっても、ポリマ管内矩形積層
部では、積層部ポリマをかなりの厚さで積層することに
なるので、容易にかつ精度良く積層できる。2または3
台の溶融押出機、2または多層用の合流ブロックあるい
は口金を用いることにより、2層あるいは3層以上の積
層シートを得ることができる。合流ブロックを用いる場
合は積層部分を前述のごとく矩形のものしておくことが
上記の積層フィルムを安定して、幅方向に斑なく工業的
に生産するのに有効である。Next, the method for producing the film of the present invention will be described by taking the case of a composite film as an example. The laminated polyester of the present invention is laminated by coextrusion on at least one surface of the base layer polyester, formed into a sheet, and then biaxially stretched to obtain a biaxially stretched laminated polyester film. Here, the lamination by co-extrusion means that the polyester raw materials of the laminated portion and the base layer portion are extruded by different extruders, respectively, and these are laminated before the laminated sheet is discharged from the die. This lamination may be performed in a die for forming and discharging into a sheet (for example, a manifold), but since the lamination thickness is thin as described above, it is preferable to perform it in a polymer pipe before being introduced into the die. . Particularly, it is particularly preferable that the laminated portion in the polymer tube is formed in a rectangular shape because the laminated portion can be uniformly laminated in the width direction. The molten polymer laminated by the rectangular laminated portion in the polymer tube is widened to a predetermined width in the sheet width direction by the manifold in the die, discharged from the die in a sheet shape, and then biaxially stretched. Therefore, even if the laminated film after biaxial orientation is extremely thin, since the laminated portion polymer is laminated at a considerable thickness in the polymer tube rectangular laminated portion, it can be laminated easily and accurately. 2 or 3
By using a melt extruder on a table, a confluent block for two or multiple layers, or a die, a laminated sheet of two layers or three or more layers can be obtained. When the confluent block is used, it is effective to make the laminated portion rectangular as described above in order to stably produce the laminated film described above and to produce it industrially without unevenness in the width direction.
【0029】次に、この積層未延伸シートを二軸延伸
し、二軸配向せしめる。二軸延伸の方法は同時二軸延
伸、逐次二軸延伸のいずれあってもよいが、長手方向、
幅方向の順に延伸する二軸延伸法の場合がフィルムを安
定して、幅方向に斑なく、工業的に製造するのに有効で
ある。逐次二軸延伸法の場合、長手方向の延伸を、2段
階、特に3段階以上に分けて、40〜150℃の範囲
で、かつ、1,000〜5,000%/分の延伸速度
で、3〜5倍行う方法が有効である。幅方向の延伸温
度、延伸速度は80〜160℃、1,000〜2,00
0%/分の範囲が好適である。延伸倍率は3〜10倍が
好適である。また必要に応じて長手方向、幅方向の少な
くとも1方向に再延伸することもできる。次にこのフィ
ルムを熱処理する。この場合の熱処理条件としては、幅
方向に、弛緩、微延伸、定長下のいずれかの状態で、1
40〜250℃の範囲、0.5〜60秒間が好適であ
る。Next, this laminated unstretched sheet is biaxially stretched and biaxially oriented. The biaxial stretching method may be either simultaneous biaxial stretching or sequential biaxial stretching, but in the longitudinal direction,
The case of the biaxial stretching method in which the film is stretched in the width direction in order is effective for industrially producing the film stably without unevenness in the width direction. In the case of the sequential biaxial stretching method, the stretching in the longitudinal direction is divided into two stages, particularly three stages or more, in the range of 40 to 150 ° C., and the stretching speed of 1,000 to 5,000% / min. A method of performing 3 to 5 times is effective. The stretching temperature and the stretching speed in the width direction are 80 to 160 ° C. and 1,000 to 2,000.
A range of 0% / min is preferred. The stretching ratio is preferably 3 to 10 times. If necessary, it can be re-stretched in at least one of the longitudinal direction and the width direction. The film is then heat treated. In this case, the heat treatment condition is as follows: in the width direction, one of relaxation, fine stretching, and under constant length is used.
The range of 40 to 250 ° C. and 0.5 to 60 seconds are preferable.
【0030】本発明のフィルムを製造する積層部原料と
して粒子を含むチップが用いられるが、その代表的な方
法としては、実質的に粒子を含まないポリエステルチッ
プに、粒子を含んだマスターチップを任意の比率でブレ
ンドして原料とする方法が好ましく利用できる。例え
ば、炭酸カルシウム、コロイダルシリカ、有機高分子粒
子などをエチレングリコールのスラリーとした後、必要
に応じてサンドグラインダーなどで粉砕処理を行い、さ
らにスーパーデカンターなどを用いての分級処理を併用
することにより、本発明の粒子径、粒子径分布の粒子ス
ラリーを準備できる。特に、コロイダルシリカ、架橋有
機粒子など粒子の製造段階で実質的な球形均一粒径に製
造可能なものについては、粉砕処理、分級処理などを省
略し直接粒子スラリーを準備できる。Chips containing particles are used as a raw material for the laminating part for producing the film of the present invention. As a typical method, polyester chips substantially free of particles and master chips containing particles are optionally used. The method of blending in the ratio of and using as a raw material can be preferably used. For example, calcium carbonate, colloidal silica, organic polymer particles, etc. are made into a slurry of ethylene glycol, and then crushed with a sand grinder, etc., if necessary, and further combined with classification using a super decanter, etc. The particle slurry having the particle size and particle size distribution of the present invention can be prepared. In particular, for particles such as colloidal silica and crosslinked organic particles that can be manufactured to have a substantially spherical uniform particle size at the particle manufacturing stage, the particle slurry can be directly prepared by omitting the crushing treatment and the classification treatment.
【0031】このスラリーを通常のポリエステル重合工
程で添加し、重合反応を完結することによりマスターチ
ップが準備できる。粒子マスターチップの粒子濃度は特
に制限されるものではないが1〜5%であると好都合で
ある。もちろん粒子マスターチップの調製は前述の重合
時添加法でなく、例えば実質的に粒子を含まないポリエ
ステルチップと粒子径、粒子径分布を調整した粒子を直
接溶融混練する方法によっても達成できる。A master chip can be prepared by adding this slurry in a usual polyester polymerization step to complete the polymerization reaction. The particle concentration of the particle master chip is not particularly limited, but is preferably 1 to 5%. Needless to say, the preparation of the particle master chip can be achieved not by the above-mentioned addition method at the time of polymerization but by, for example, a method of directly melt-kneading the polyester chip substantially containing no particles and the particles of which particle size and particle size distribution are adjusted.
【0032】マンガン化合物の添加方法としては、上記
粒子含有ポリエステルの重合工程で、例えばジメチルテ
レフタレートとエチレングリコールとのエステル交換反
応時、あるいは引き続き行われる重合反応時に添加して
も良い。この場合、不活性粒子のエチレングリコールス
ラリーに含有させておいても良い。また、マンガン化合
物を多量に含有するいわゆるマンガン含有マスターポリ
マを準備しておき、製膜原料調整時に粒子マスターポリ
マ、無粒子マスターポリマなどと適宣混合することによ
っても達成できる。The manganese compound may be added in the step of polymerizing the polyester containing particles, for example, during the transesterification reaction of dimethyl terephthalate and ethylene glycol, or during the subsequent polymerization reaction. In this case, the inert particles may be contained in the ethylene glycol slurry. It can also be achieved by preparing a so-called manganese-containing master polymer containing a large amount of a manganese compound and appropriately mixing it with a particle master polymer, a particle-free master polymer, or the like at the time of preparing the film-forming raw material.
【0033】本発明の特性値の測定方法および効果の評
価方法は次のとおりである。The method of measuring the characteristic value and the method of evaluating the effect of the present invention are as follows.
【0034】(1)粒子の平均粒径 フィルムの表面からポリエステルをプラズマ低温灰化処
理法(例えばヤマト科学製PR−503型)で除去し粒
子を露出させる。処理条件はポリエステルは灰化される
が、粒子はダメージを受けない条件を選択する。これを
走査型電子顕微鏡(SEM)で観察し、粒子の画像をイ
メージアナライザー(例えばケンブリッジインスツルメ
ント製QTM900型)で処理し、観察箇所を変えて多
数の粒子について測定し平均粒径を測定する。(1) Average Particle Diameter of Particles Polyester is removed from the surface of the film by a plasma low temperature ashing method (for example, PR-503 type manufactured by Yamato Scientific Co., Ltd.) to expose the particles. The processing conditions are selected such that polyester is incinerated but particles are not damaged. This is observed with a scanning electron microscope (SEM), the image of the particles is processed with an image analyzer (for example, QTM900 type manufactured by Cambridge Instruments), and the observation points are changed to measure a large number of particles to measure the average particle size. .
【0035】凝集状の粒子については、上記方法で凝集
をなしている一次粒子および凝集されてなる二次粒子径
について測定する。また、B.E.T法による粒子の比
表面積を求め、この比表面積から粒子を球としたときの
粒径(=6/(粒子密度×比表面積))を平均一次粒子
径とすることができる。また、必要に応じ、例えば重合
時に添加前の粒子について同様に走査顕微鏡での測定も
採用でき、遠心沈降式の粒度分布測定器による測定値も
採用できる。With respect to the agglomerated particles, the primary particles agglomerated by the above method and the secondary particle diameter agglomerated by the above method are measured. In addition, B. E. The specific surface area of the particles is determined by the T method, and the particle diameter when the particles are spheres (= 6 / (particle density × specific surface area)) can be taken as the average primary particle diameter from this specific surface area. Further, if necessary, for example, the particles before addition during polymerization can be similarly measured by a scanning microscope, and the value measured by a centrifugal sedimentation type particle size distribution measuring device can also be adopted.
【0036】(2)粒子の含有量 ポリエステルは溶解し、粒子は溶解しない溶媒を選択
し、粒子を溶媒から遠心分離し、粒子の量の全体重量に
対する比率(重量%)を持って粒子含有量とする。場合
によっては赤外分光法、蛍光X線分析法などの併用も有
効である。さらに、必要に応じフィルムをミクロトーム
で切断し、透過型電子顕微鏡で測定し、単位面積あたり
の粒子像の割合を求めることにより、該ポリエステルに
対する粒子添加量を算出すことができる。(2) Content of particles A solvent in which polyester is dissolved and particles are not dissolved is selected, and the particles are centrifuged from the solvent, and the content of particles is adjusted to the total weight (% by weight). And In some cases, combined use of infrared spectroscopy, fluorescent X-ray analysis, etc. is also effective. Further, if necessary, the film is cut with a microtome, measured with a transmission electron microscope, and the ratio of the particle image per unit area is determined, whereby the amount of particles added to the polyester can be calculated.
【0037】(3)最表層部の厚さ 2次イオン質量分析装置(SIMS)を用いて、フィル
ム中の粒子の内、最も高濃度の粒子に起因する元素とポ
リエステルの炭素元素の濃度比(M+ /C+ )を粒子濃
度とし、ポリエステルA層の表層から深さ(厚さ)方向
の分析を行う。表層では表面という界面のため粒子濃度
は低く表面から遠ざかるにつれて粒子濃度は高くなる。
本発明の場合は深さ[I]で一旦極大値となった粒子濃
度がまた減少し始める。この濃度分布曲線をもとに極大
値の粒子濃度の1/2になる深さ[II](ここでII
>I)を積層厚さとした。なお、フィルム中に最も多く
含有する粒子が有機高分子粒子の場合はSIMSでは測
定が難しいので、表面からエッチングしながらXPS
(X線光電子分光法)、IR(赤外分光法)あるいはコ
ンフォーラル顕微鏡などで、その粒子のデプスプロフィ
ールを測定し、上記同様の手法から積層厚さを求めても
良い。さらに上記のデプスプロフィールからではなく、
フィルムの断面観察あるいは薄膜段差測定器などによっ
て求めることもできる。(3) Thickness of outermost layer portion Using a secondary ion mass spectrometer (SIMS), the concentration ratio of the element derived from the highest concentration of particles in the film and the carbon element of polyester ( The particle concentration is defined as M + / C + ) and analysis is performed in the depth (thickness) direction from the surface layer of the polyester A layer. At the surface layer, the particle concentration is low due to the interface of the surface, and the particle concentration increases as the distance from the surface increases.
In the case of the present invention, the particle concentration once reaching the maximum value at the depth [I] starts to decrease again. Based on this concentration distribution curve, the depth [II] (where II
> I) was the laminate thickness. It should be noted that when the most abundant particles in the film are organic polymer particles, it is difficult to measure with SIMS, so XPS while etching from the surface.
(X-ray photoelectron spectroscopy), IR (infrared spectroscopy), a confocal microscope, or the like may be used to measure the depth profile of the particles, and the layer thickness may be determined by the same method as above. And not from the depth profile above,
It can also be obtained by observing the cross section of the film or a thin film step measuring instrument.
【0038】(4)フィルムの中心線平均表面粗さ(R
a) JIS−B−0601に従い小坂研究所製触針型表面粗
さ計BE−3Eを用い、カットオフ0.25mm,測定
長4mmで中心線平均表面粗さ(Ra)を測定した。(4) Center line average surface roughness (R
a) The center line average surface roughness (Ra) was measured at a cutoff of 0.25 mm and a measurement length of 4 mm using a stylus type surface roughness meter BE-3E manufactured by Kosaka Laboratory in accordance with JIS-B-0601.
【0039】(5)固有粘度[η](単位はdl/g) オルソクロルフェノール中、25℃で測定した溶液粘度
から、下記式から計算される値を用いる。 ηsp/C=[η]+K[η]2 ・C ここで、ηsp=(溶液粘度/溶媒粘度)−1、Cは溶
媒100mlあたりの溶解ポリマ重量(g/100m
l、通常1.2)、Kはハギンス定数(0.343とす
る)。また、溶液粘度、溶媒粘度はオストワルド粘度計
を用いて測定した。(5) Intrinsic viscosity [η] (unit: dl / g) The value calculated from the following formula is used from the solution viscosity measured at 25 ° C. in orthochlorophenol. ηsp / C = [η] + K [η] 2 · C where ηsp = (solution viscosity / solvent viscosity) -1, C is the weight of dissolved polymer per 100 ml of solvent (g / 100 m)
1, usually 1.2), and K is the Huggins constant (0.343). The solution viscosity and the solvent viscosity were measured using an Ostwald viscometer.
【0040】(6)マンガン化合物の測定 蛍光X線分析装置または原子吸光法により測定した。マ
ンガン化合物の含有形態については、ポリマまたはフィ
ルムをミクロトームで切断し、切断面について元素分析
機能を持つ電子顕微鏡(SEM−XMA)で観察、含有
粒子について元素分析しマンガン化合物主体の粒子であ
るか否か、およびその粒子径について確認した。(6) Measurement of manganese compound It was measured by a fluorescent X-ray analyzer or an atomic absorption method. Regarding the content form of the manganese compound, the polymer or film is cut with a microtome, and the cut surface is observed with an electron microscope (SEM-XMA) having an elemental analysis function. And its particle size were confirmed.
【0041】(7)耐スクラッチ性 25℃相対湿度60%の雰囲気下で、外形6mmの固定
軸(表面粗さ0.2S)に1/2インチ幅のテープ状フ
ィルムを角度θ=π/3radで接触させ、250m/
分の早さで走行させる。入り口テンションT1 を90g
とし、100m走行後のフィルムをアルミ蒸着して、ス
クラッチきずの本数、幅の大きさおよび白粉の発生状態
を微分干渉顕微鏡で観察した。全くスクラッチ傷が見ら
れずかつ白粉の発生のないものを耐スクラッチ性:5、
スクラッチ傷が3本/mm未満でかつ白粉の発生が殆ど
ないものを耐スクラッチ性:4、スクラッチ傷が3〜1
0本/mmで幅の大きいものもあり、かつ白粉がかなり
発生しているものを耐スクラッチ性:3、スクラッチ傷
が10本/mm以上で幅も大きく、かつ白粉が著しく発
生しているものを耐スクラッチ性:2、それ以外を耐ス
クラッチ性:1と判定した。耐スクラッチ性が5または
4であれば実用上問題なく使用できる。(7) Scratch resistance In a atmosphere of 25 ° C. and 60% relative humidity, a tape-shaped film having a width of 1/2 inch is attached to a fixed shaft (surface roughness 0.2S) having an outer diameter of 6 mm at an angle θ = π / 3rad. 250m /
Drive at the speed of a minute. 90 g of entrance tension T 1
Then, the film after running for 100 m was vapor-deposited with aluminum, and the number of scratches, the size of the width, and the generation state of white powder were observed with a differential interference microscope. Scratch resistance: 5, with no scratches and no white powder
Scratch resistance: 4, scratches less than 3 lines / mm and almost no white powder generated, scratches 3-1
Some of them have a large width of 0 lines / mm and have a considerable amount of white powder. Scratch resistance: 3, scratches of 10 lines / mm or more, a large width, and a large amount of white powder. The scratch resistance was judged to be 2, and the other scratch resistance was judged to be 1. If the scratch resistance is 5 or 4, it can be used practically without any problem.
【0042】(8)電磁変換特性およびスリット特性 フィルムに下記組成の磁性塗料をグラビヤロールにより
塗布し、磁気配向させ、乾燥させる。さらに、小型カレ
ンダー装置(スチロールロール/ナイロンロール、5
段)で温度70℃、線圧200kg/cmでカレンダー
処理後、70℃で48時間キュアリングする。この原反
を50m/分の速度で1/2インチ幅に切断スリット
し、パンケーキを作成した。(8) Electromagnetic conversion characteristics and slit characteristics A magnetic coating material having the following composition is applied to a film by a gravure roll, magnetically oriented, and dried. In addition, a small calendar device (styrene roll / nylon roll, 5
(Stage) at a temperature of 70 ° C. and a linear pressure of 200 kg / cm, followed by calendaring at 70 ° C. for 48 hours. This raw fabric was cut and slit into a 1/2 inch width at a speed of 50 m / min to prepare a pancake.
【0043】 (磁性塗料の組成) ・Co含有酸化鉄(BET値50m2 /g) :100重量部 ・塩化ビニル/酢酸ビニル共重合体 : 10重量部 ・ポリウレタンエラストマ : 10重量部 ・ポリイソシアネート : 5重量部 ・レシチン : 1重量部 ・メチルエチルケトン : 75重量部 ・メチルイソブチルケトン : 75重量部 ・トルエン : 75重量部 ・カーボンブラック : 2重量部 ・ラウリン酸 :1.5重量部 このパンケーキから長さ1mを採取し、コイル状に巻き
清浄なビーカーに入れ、切断面3mmを純水に浸し、5
0KHZ超音波で2分間処理し、切断面起因の切り粉を
純水中に洗い落とした。この純水について粒子計数装置
(HIAC・CL−5型、野崎産業)で3〜20μmの
粒子数を計測し、切り粉数とした。切り粉数は少ないほ
ど好ましいが、50個/m以下であれば実用上問題なく
使用でき、20個/m以下であればさらに好ましく、と
くに良好なダビング特性が得られる。(Composition of magnetic paint) Co-containing iron oxide (BET value 50 m 2 / g): 100 parts by weight Vinyl chloride / vinyl acetate copolymer: 10 parts by weight Polyurethane elastomer: 10 parts by weight Polyisocyanate: 5 parts by weight Lecithin: 1 part by weight Methyl ethyl ketone: 75 parts by weight Methyl isobutyl ketone: 75 parts by weight Toluene: 75 parts by weight Carbon black: 2 parts by weight Lauric acid: 1.5 parts by weight Long from this pancake Take 1m of length, wind it in a coil and put it in a clean beaker.
It was treated with 0KHZ ultrasonic waves for 2 minutes, and the cutting chips resulting from the cut surface were washed off in pure water. About this pure water, the number of particles of 3 to 20 μm was measured with a particle counter (HIAC CL-5 type, Nozaki Sangyo Co., Ltd.) to obtain the number of chips. The smaller the number of chips is, the more preferable. However, if it is 50 pieces / m or less, it can be practically used without any problem, and if it is 20 pieces / m or less, it is more preferable, and particularly good dubbing characteristics are obtained.
【0044】さらに、上記のパンケーキから長さ250
mをVTRカセットに組み込み、VTRカセットテープ
とした。このテープを家庭用VTRを用いてシバソク製
のテレビ試験波形発生器(TG7/U706)により1
00%クロマ信号を記録し、その再生信号からシバソク
製カラーノイズ測定機(925D/1)でクロマS/N
を測定し画質を判定した。Furthermore, from the above pancake, length 250
m was incorporated into a VTR cassette to obtain a VTR cassette tape. Using a VTR for home use, this tape was recorded by a TV test waveform generator (TG7 / U706) made by Shibasoku.
Chroma S / N is recorded with a Shiba Soku color noise measuring device (925D / 1) by recording a 00% chroma signal and reproducing it.
Was measured to determine the image quality.
【0045】[0045]
(1)炭酸カルシウム含有マスターポリマの製造 平均粒子径0.85μmの合成炭酸カルシウムをスーパ
ーデカンターで遠心分級処理し、粗大粒子を除去した。
このスラリーを2μmのフィルターで精密濾過を行い、
粗粒の少ない炭酸カルシウムのエチレングリコールスラ
リーを準備した。スラリー中の炭酸カルシウムの平均粒
子径は0.80μmであった。ジメチルテレフタート1
00部、エチレングリコール70部、酢酸マグネシウム
・4水塩0.04部および酸化アンチモン0.04部を
反応器に仕込み、内温を145℃から徐々に上げながら
エステル交換反応を行った。エステル交換交換反応率が
97%となった時点で、安定剤としてトリメチルフォス
フェート0.04部および先に準備してある炭酸カルシ
ウムのエチレングリコールスラリー20部を添加した。
次いで反応生成物を重合反応器に移し、高温真空下(最
終内温290℃)にて常法に従い重縮合反応を行い、固
有粘度0.62の炭酸カルシウム粒子を2重量%含有す
るポリエチレンテレフタレートを得た。(1) Production of Calcium Carbonate-Containing Master Polymer Synthetic calcium carbonate having an average particle diameter of 0.85 μm was subjected to centrifugal classification with a super decanter to remove coarse particles.
This slurry is microfiltered with a 2 μm filter,
An ethylene glycol slurry of calcium carbonate with few coarse particles was prepared. The average particle size of calcium carbonate in the slurry was 0.80 μm. Dimethyl terephthalate 1
00 parts, 70 parts of ethylene glycol, 0.04 parts of magnesium acetate / tetrahydrate and 0.04 parts of antimony oxide were charged into the reactor, and the transesterification reaction was carried out while gradually raising the internal temperature from 145 ° C. When the transesterification rate reached 97%, 0.04 parts of trimethyl phosphate as a stabilizer and 20 parts of an ethylene glycol slurry of calcium carbonate prepared previously were added.
Then, the reaction product is transferred to a polymerization reactor and subjected to polycondensation reaction under a high temperature vacuum (final internal temperature of 290 ° C.) according to a conventional method to obtain polyethylene terephthalate containing 2% by weight of calcium carbonate particles having an intrinsic viscosity of 0.62. Obtained.
【0046】平均粒子径0.40μmの炭酸カルシウム
含有マスターポリマも、上記と同様な方法で得た。A calcium carbonate-containing master polymer having an average particle size of 0.40 μm was also obtained by the same method as described above.
【0047】(2)凝集体粒子含有マスターポリマの製
造 酸化ジルコニウム(一次粒子径0.03μm、二次粒子
径0.11μm)をエチレングリコールの10重量%ス
ラリーとし、サンドグラインダーで4時間分散処理を行
い、このスラリーを1μmのフィルターで精密濾過し
た。ジメチルテレフタート100部、エチレングリコー
ル70部、酢酸マグネシウム・4水塩0.04部および
酸化アンチモン0.04部を反応器に仕込み、内温を1
45℃から徐々に上げながらエステル交換反応を行っ
た。エステル交換交換反応率が97%となった時点で、
安定剤としてトリメチルフォスフェート0.04部およ
び先に準備してある酸化ジルコニウムのエチレングリコ
ールスラリー20部を添加した。次いで反応生成物を重
合反応器に移し、高温真空下(最終内温290℃)にて
常法に従い重縮合反応を行い、固有粘度0.62の酸化
ジルコニウム粒子を2重量%含有するポリエチレンテレ
フタレートを得た。同様に、酸化アルミニウム(一次粒
子径0.02μm、二次粒子径0.09μm)について
処理を行い、上記同様に重合し、固有粘度0.62の酸
化アルミニウム粒子を2重量%含有するポリエチレンテ
レフタレートを得た。(2) Production of Master Polymer Containing Aggregate Particles Zirconium oxide (primary particle diameter 0.03 μm, secondary particle diameter 0.11 μm) was made into a 10 wt% slurry of ethylene glycol and dispersed in a sand grinder for 4 hours. This slurry was microfiltered with a 1 μm filter. 100 parts of dimethyl terephthalate, 70 parts of ethylene glycol, 0.04 part of magnesium acetate / tetrahydrate and 0.04 part of antimony oxide were charged into the reactor, and the internal temperature was adjusted to 1
The transesterification reaction was carried out while gradually raising the temperature from 45 ° C. When the transesterification rate is 97%,
0.04 parts of trimethyl phosphate as a stabilizer and 20 parts of the zirconium oxide ethylene glycol slurry prepared above were added. Then, the reaction product was transferred to a polymerization reactor and subjected to polycondensation reaction under high temperature vacuum (final internal temperature of 290 ° C.) according to a conventional method to obtain polyethylene terephthalate containing 2% by weight of zirconium oxide particles having an intrinsic viscosity of 0.62. Obtained. Similarly, aluminum oxide (primary particle diameter 0.02 μm, secondary particle diameter 0.09 μm) was treated and polymerized in the same manner as above to obtain polyethylene terephthalate containing 2% by weight of aluminum oxide particles having an intrinsic viscosity of 0.62. Obtained.
【0048】(3)コロイダルシリカ含有マスターポリ
マの製造 平均粒子径0.45μmの水ガラス法で合成した実質的
に球形のコロイダルシリカの10%エチレングリコール
スラリーを調整し、1μmのフィルターで精密濾過し
た。このスラリーを炭酸カルシウム含有マスターポリマ
の調整と同様に重合し、固有粘度0.62のコロイダル
シリカ粒子を2重量%含有するポリエチレンテレフタレ
ートを得た。(3) Production of Master Polymer Containing Colloidal Silica A 10% ethylene glycol slurry of substantially spherical colloidal silica synthesized by the water glass method having an average particle size of 0.45 μm was prepared and microfiltered with a 1 μm filter. . This slurry was polymerized in the same manner as in the preparation of the calcium carbonate-containing master polymer to obtain polyethylene terephthalate containing 2% by weight of colloidal silica particles having an intrinsic viscosity of 0.62.
【0049】(4)無粒子ポリマの製造 上記重合法において、粒子のエチレングリコールスラリ
ーを添加することなく、エステル交換交換反応および重
縮合反応を行い、実質的に不活性粒子を含まない固有粘
度0.62の無粒子ポリエチレンテレフタレートを得
た。(4) Production of particle-free polymer In the above-mentioned polymerization method, transesterification and polycondensation reactions are carried out without adding ethylene glycol slurry of particles to obtain an intrinsic viscosity of substantially no inert particles. 0.62 particle-free polyethylene terephthalate was obtained.
【0050】(5)有機高分子微粒子含有マスターポリ
マの製造 ベントタイプ二軸押出機を使用して、無粒子ポリエチレ
ンテレフタレートを溶融状態とし、最終的なポリマ中の
含有量が1重量%になるように、有機高分子微粒子とし
て0.45μmのジビニルベンゼン共重合体粒子(ジビ
ニルベンゼン55%、エチルビニルベンゼン45%の共
重合品)の水スラリーを添加、ベント口を10Torr
の真空度に保持し、ポリマ温度280℃でで溶融混練押
出して、ジビニルベンゼン共重合体粒子含有ポリエチレ
ンテレフタレート(固有粘度0.615)を得た。(5) Production of Master Polymer Containing Organic Polymer Fine Particles Using a bent type twin-screw extruder, the particle-free polyethylene terephthalate is melted so that the final content in the polymer is 1% by weight. To the above, an aqueous slurry of 0.45 μm divinylbenzene copolymer particles (copolymerized product of divinylbenzene 55% and ethylvinylbenzene 45%) as organic polymer particles was added, and the vent port was set to 10 Torr.
The vacuum degree was maintained, and the mixture was melt-kneaded and extruded at a polymer temperature of 280 ° C. to obtain polyethylene terephthalate (intrinsic viscosity 0.615) containing divinylbenzene copolymer particles.
【0051】(6)マンガン含有マスターポリマの製造 ジメチルテレフタート100部、エチレングリコール7
0部、酢酸マグネシウム・4水塩0.04部および酸化
アンチモン0.04部を反応器に仕込み、内温を145
℃から徐々に上げながらエステル交換反応を行った。エ
ステル交換交換反応率が98%となった時点で、酢酸マ
ンガン・4水塩0.40部およびトリメチルフォスフェ
ート0.40部を添加した。次いで反応生成物を重合反
応器に移し、高温真空下(最終内温290℃)にて常法
に従い重縮合反応を行い、固有粘度0.62のマンガン
化合物を多く含むマンガン含有ポリエチレンテレフタレ
ートを得た。このポリマをミクロトームで切断し、切断
面について元素分析機能を持つ電子顕微鏡(SEM−X
MA)で観察した結果、マンガンを主成分として含有す
る粗大粒子は観察されず、マンガン化合物はポリマ中で
相溶解または微分散されていることが確認された。(6) Manganese-containing master polymer 100 parts dimethyl terephthalate, ethylene glycol 7
The reactor was charged with 0 part, 0.04 part of magnesium acetate / tetrahydrate and 0.04 part of antimony oxide, and the internal temperature was adjusted to 145
The transesterification reaction was carried out while gradually raising the temperature from ° C. When the transesterification rate reached 98%, 0.40 part of manganese acetate tetrahydrate and 0.40 part of trimethyl phosphate were added. Then, the reaction product was transferred to a polymerization reactor and subjected to polycondensation reaction under a high temperature vacuum (final internal temperature of 290 ° C.) according to a conventional method to obtain a manganese-containing polyethylene terephthalate containing a large amount of a manganese compound having an intrinsic viscosity of 0.62. . This polymer was cut with a microtome, and the cut surface had an electron microscope (SEM-X
As a result of observation with (MA), coarse particles containing manganese as a main component were not observed, and it was confirmed that the manganese compound was phase-dissolved or finely dispersed in the polymer.
【0052】実施例1 上記で準備した0.8μmの炭酸カルシウム含有ポリ
マ、凝集体粒子酸化ジルコニウム含有ポリマ、無粒子ポ
リマおよびマンガン含有マスターポリマを混合し、0.
80μmの炭酸カルシウムを0.60%、酸化ジルコニ
ウムを0.30%含有し、さらにマンガンを炭酸カルシ
ウム1gに対し0.15×10-3モル含有する積層部用
原料を準備した。Example 1 The 0.8 μm calcium carbonate-containing polymer, aggregate particle zirconium oxide-containing polymer, particle-free polymer and manganese-containing master polymer prepared as described above were mixed, and
A raw material for a laminated part containing 0.60% of 80 μm calcium carbonate, 0.30% of zirconium oxide, and 0.15 × 10 −3 mol of manganese per 1 g of calcium carbonate was prepared.
【0053】これらのポリエチレンテレフタレート原
料、すなわち、粒子マスターポリマ、マンガン含有ポリ
マおよび無粒子のポリマををそれぞれ表1のとおり種
類、量を変えて混合し、180℃で3時間減圧(3To
rr)乾燥し、これを積層部原料とした。These polyethylene terephthalate raw materials, that is, the particle master polymer, the manganese-containing polymer, and the particle-free polymer were mixed in different types and amounts as shown in Table 1, and the mixture was depressurized (3To) at 180 ° C. for 3 hours.
rr) It dried and this was made into the laminated part raw material.
【0054】さらに、無粒子ポリマ50部とフィルム回
収原料50部を混合し、基層部原料を準備した。この基
層部原料を測定した結果、フィルム回収原料に含まれる
粒子などため、含有している粒子量は、平均粒子径0.
8μmの炭酸カルシウムが0.25%および平均粒子径
0.4μmのシリカが0.08%であった。Further, 50 parts of the particle-free polymer and 50 parts of the film recovery raw material were mixed to prepare a base layer raw material. As a result of measuring the raw material for the base layer, particles contained in the raw material for film recovery and the like have an average particle diameter of 0.
0.25% of 8 μm calcium carbonate and 0.08% of silica having an average particle size of 0.4 μm.
【0055】積層部原料および基層部原料をそれぞれ1
80℃で3時間減圧(3Torr)乾燥し、基層部原料
を押出機1に供給し310℃で溶融し、さらに積層部原
料を押出機2に供給し280℃で溶融した。これらのポ
リマを矩形積層部を備えた合流ブロックで口金に入る前
に合流積層し、静電印加キャスト法を用いて表面温度4
5℃のキャスティング・ドラムに巻き付けて冷却固化
し、基層部ポリエステルの両面に積層ポリエステルを積
層した3層構造の未延伸フィルムを作った。この未延伸
フィルムを80℃で長手方向に4.5倍延伸した。この
延伸は2組づつのロ−ルの周速差で、2段階で行った。
この一軸延伸フィルムをステンタを用いて延伸速度2,
000%/分で100℃で幅方向に4.0倍延伸し、定
長下で200℃にて5秒間熱処理し積層二軸配向ポリエ
チレンテレフタレートフィルムを得た。このフィルムは
それぞれの押出機の吐出量の調節により、基層部厚さ1
2.0μmでその両面に0.90μmの積層部を有して
いた。1 for each of the laminated part raw material and the base layer raw material
It was dried under reduced pressure (3 Torr) at 80 ° C. for 3 hours, the base layer raw material was supplied to the extruder 1 and melted at 310 ° C., and the laminated portion raw material was further supplied to the extruder 2 and melted at 280 ° C. These polymers are combined and laminated in a confluent block having a rectangular laminated section before entering the mouthpiece, and the surface temperature is 4
It was wound around a casting drum at 5 ° C. and cooled and solidified to prepare an unstretched film having a three-layer structure in which laminated polyester was laminated on both surfaces of the base layer polyester. This unstretched film was stretched 4.5 times in the longitudinal direction at 80 ° C. This stretching was carried out in two stages with the difference in peripheral speed between each pair of rolls.
Stretching speed of this uniaxially stretched film using a stenter
It was stretched 4.0 times in the width direction at 100 ° C. at 000% / min and heat-treated at 200 ° C. for 5 seconds under a constant length to obtain a laminated biaxially oriented polyethylene terephthalate film. This film has a base layer thickness of 1 by adjusting the discharge rate of each extruder.
It had a laminated portion of 2.0 μm and 0.90 μm on both sides thereof.
【0056】このフィルムの諸物性を評価した結果、フ
ィルム表面粗さは12.0nmであった。さらに耐スク
ラッチ性は5、スリット特性は8個/m、電磁変化特性
は;0.5dBで極めて良好なフィルム特性であった。As a result of evaluating various physical properties of this film, the surface roughness of the film was 12.0 nm. Furthermore, the scratch resistance was 5, the slit characteristic was 8 / m, and the electromagnetic change characteristic was 0.5 dB, which was a very good film characteristic.
【0057】実施例2〜6、比較例1〜3 粒子含有ポリマ、マンガン含有ポリマおよび無粒子のポ
リマをそれぞれ表1のとおり種類、量を変えて混合し、
180℃で3時間減圧(3Torr)乾燥し、このを積
層部原料とした。さらに、別に基層部原料として表1の
とおり種類、量を変えて混合し、180℃で3時間減圧
(3Torr)乾燥し、このを基層部原料とした。実施
例1と同様な方法で得られたフィルムの各パラメーター
およびフィルム品質は表1に示した通りであり、これら
が本発明に規定した範囲内の場合には、良好な耐スクラ
ッチ性、スリット特性、電磁変換特性が得られており、
そうでない場合に目的とする効果が得られなかった。Examples 2 to 6 and Comparative Examples 1 to 3 Particle-containing polymers, manganese-containing polymers and non-particle-containing polymers were mixed in the types and amounts shown in Table 1, respectively,
It was dried under reduced pressure (3 Torr) at 180 ° C. for 3 hours, and this was used as a raw material for the laminated portion. Further, as the raw material for the base layer, the types and amounts were changed as shown in Table 1 and mixed, and dried under reduced pressure (3 Torr) at 180 ° C. for 3 hours to obtain a raw material for the base layer. The respective parameters and film quality of the film obtained by the same method as in Example 1 are as shown in Table 1, and when these are within the range specified in the present invention, good scratch resistance and slit property are obtained. , Electromagnetic conversion characteristics have been obtained,
If not, the desired effect was not obtained.
【0058】[0058]
【表1】 [Table 1]
【0059】[0059]
【発明の効果】以上説明したように、本発明のポリエス
テルフィルムは良好な耐スクラッチ性、スリット特性を
示すため、磁気媒体用、特にビデオテープに最適なポリ
エステルフィルムを得ることができ、高品質なビデオテ
ープを提供することが可能である。As described above, since the polyester film of the present invention exhibits good scratch resistance and slit characteristics, it is possible to obtain a polyester film most suitable for magnetic media, especially for video tapes, and it is of high quality. It is possible to provide a videotape.
フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 FI 技術表示箇所 G11B 5/704 Continuation of the front page (51) Int.Cl. 6 Identification number Office reference number FI technical display location G11B 5/704
Claims (4)
を0.05〜3重量%含有し、かつ該不活性粒子1gに
対し0.01×10-3〜0.4×10-3モルのマンガン
化合物を含有することを特徴とする磁気記録媒体用ポリ
エステルフィルム。1. An inert particle having an average particle diameter of 0.1 to 2 μm is contained in an amount of 0.05 to 3% by weight, and 0.01 × 10 −3 to 0.4 × 10 per 1 g of the inert particle. A polyester film for a magnetic recording medium, which contains a manganese compound in an amount of -3 mol.
くとも一層に配置してなる磁気記録媒体用複合ポリエス
テルフィルム。2. A composite polyester film for a magnetic recording medium, wherein the polyester film according to claim 1 is arranged in at least one layer.
/または有機高分子微粒子である請求項1または2に記
載の磁気記録媒体用ポリエステルフィルム。3. The polyester film for a magnetic recording medium according to claim 1, wherein the inert particles are calcium carbonate and / or organic polymer fine particles.
ポリエステルフィルムで、かつ積層部の厚さに対する不
活性粒子の平均粒径の比率が0.2〜50の範囲である
磁気記録媒体用複合ポリエステルフィルム。4. A magnetic recording comprising a three-layer structure, wherein the laminated portion is the polyester film according to claim 1, and the ratio of the average particle diameter of the inert particles to the thickness of the laminated portion is in the range of 0.2 to 50. Composite polyester film for media.