JPH07238127A - Curable polyphenylene ether film - Google Patents
Curable polyphenylene ether filmInfo
- Publication number
- JPH07238127A JPH07238127A JP3108194A JP3108194A JPH07238127A JP H07238127 A JPH07238127 A JP H07238127A JP 3108194 A JP3108194 A JP 3108194A JP 3108194 A JP3108194 A JP 3108194A JP H07238127 A JPH07238127 A JP H07238127A
- Authority
- JP
- Japan
- Prior art keywords
- polyphenylene ether
- film
- resin
- ether resin
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、硬化性ポリフェニレン
エーテルフィルム、これを硬化して得られる硬化フィル
ムおよびこれと金属箔とから成る積層体に関する。本発
明のフィルムおよび積層体は、硬化後において優れた耐
屈曲性、耐薬品性、誘電特性、耐熱性を示し、電気産
業、電子産業、宇宙・航空機産業等の分野に用いること
ができる。特に片面、両面、セミリジッドプリント基
板、フレキシブルプリント配線板用フィルムとして用い
ることができる。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a curable polyphenylene ether film, a cured film obtained by curing the same, and a laminate comprising the same and a metal foil. The film and laminate of the present invention exhibit excellent flex resistance, chemical resistance, dielectric properties and heat resistance after curing, and can be used in the fields of electric industry, electronic industry, space / aircraft industry and the like. In particular, it can be used as a film for one side, both sides, a semi-rigid printed circuit board, a flexible printed wiring board.
【０００２】[0002]
【従来の技術】近年、通信用、民生用、産業用等の電子
機器の分野における実装方法の小型化、高密度化への指
向は著しいものがあり、それに伴って材料の面でも、よ
り優れた耐熱性、寸法安定性、電気特性が要求されつつ
ある。例えばフレキシブルプリント配線板用フィルムと
しては、従来からカプトン（Ｄｕ Ｐｏｎｔ社製）に代
表されるポリイミドがフィルムとして用いられてきた。
これは各種の性能をバランスよく有するものの、誘電特
性が悪く、かつ吸湿率が大きいという欠点を持ってい
る。この欠点を改善したフィルムとしてポリフェニレン
スルフィドおよびポリエーテルイミド等の熱可塑性樹脂
フィルムが開発されたが、これらのフィルムは吸湿率は
小さいがガラス転移温度が低く耐熱性に劣るという欠点
を持っている。以上の問題を解決する新しい材料として
ポリフェニレンエーテルが近年注目をあびている。この
樹脂は、低誘電率かつ低吸湿率であり、かつ耐熱性に優
れるという特性を持っている。しかしながら、耐薬品性
が劣っているので用途が限定されていた。2. Description of the Related Art In recent years, there has been a remarkable trend toward miniaturization and high density of mounting methods in the field of electronic devices for communication, consumer use, industrial use, etc. In addition, heat resistance, dimensional stability, and electrical characteristics are being demanded. For example, as a film for a flexible printed wiring board, a polyimide represented by Kapton (manufactured by Du Pont) has been conventionally used as a film.
Although it has various performances in a well-balanced manner, it has the drawbacks of poor dielectric properties and high moisture absorption. Thermoplastic resin films such as polyphenylene sulfide and polyether imide have been developed as films that have improved this drawback. However, these films have a drawback that they have a low moisture absorption rate but a low glass transition temperature and poor heat resistance. In recent years, polyphenylene ether has attracted attention as a new material for solving the above problems. This resin has the properties of low dielectric constant and low moisture absorption, and excellent heat resistance. However, its use was limited because of its poor chemical resistance.
【０００３】耐薬品性を改良する目的で、ポリフェニレ
ンエーテルに不飽和基を導入した硬化性ポリフェニレン
エーテル系ポリマーが開発されている。しかしながら、
フィルムの硬化後の性質は難燃性が劣っていた。For the purpose of improving chemical resistance, a curable polyphenylene ether polymer in which an unsaturated group is introduced into polyphenylene ether has been developed. However,
The property of the film after curing was inferior in flame retardancy.
【０００４】[0004]
【発明が解決しようとする課題】本発明は以上のような
事情を鑑みてなされたものであり、不飽和基を含むポリ
フェニレンエーテルの優れた誘電特性、耐熱性を損なう
ことなく、かつ硬化後において優れた難燃性を示す硬化
ポリフェニレンエーテルフィルムおよび積層体を提供し
ようとするものである。The present invention has been made in view of the above circumstances, and does not impair the excellent dielectric properties and heat resistance of polyphenylene ether containing an unsaturated group, and after curing. It is intended to provide a cured polyphenylene ether film and a laminate having excellent flame retardancy.
【０００５】[0005]
【課題を解決するための手段】本発明者らは上述のよう
な課題を解決するため難燃剤に着目し鋭意検討を重ねた
結果、本発明の目的に沿った特定の難燃剤を見出し本発
明を完成するに至った。本発明は次に述べる３つの発明
より構成される。すなわち本発明の第１は、不飽和結合
基を含むポリフェニレンエーテル樹脂１００重量部およ
び難燃剤Ｎ−トリブロモフェニルマレイミド１０〜５０
重量部からなる硬化性ポリフェニレンエーテルフィルム
を提供する。Means for Solving the Problems As a result of intensive investigations by the present inventors, in order to solve the above-mentioned problems, the inventors have found a specific flame retardant which meets the purpose of the present invention. Has been completed. The present invention comprises the following three inventions. That is, the first aspect of the present invention is to use 100 parts by weight of a polyphenylene ether resin containing an unsaturated bond group and 10 to 50 flame retardants N-tribromophenylmaleimide.
A curable polyphenylene ether film comprising 1 part by weight is provided.
【０００６】本発明の第２は、上記第１発明の硬化性ポ
リフェニレンエーテルフィルムを硬化して得られた硬化
ポリフェニレンエーテルフィルムを提供する。本発明の
第３は、上記第２発明の硬化ポリフェニレンエーテルフ
ィルムと金属箔とからなる積層体を提供する。以上３つ
の発明について以下に詳しく説明する。A second aspect of the present invention provides a cured polyphenylene ether film obtained by curing the curable polyphenylene ether film of the first aspect. A third aspect of the present invention provides a laminate comprising the cured polyphenylene ether film of the second aspect and a metal foil. The above three inventions will be described in detail below.
【０００７】まず本発明の第１である硬化性ポリフェニ
レンエーテル系樹脂フィルムについて説明する。本発明
に用いられる不飽和基を含むポリフェニレンエーテル樹
脂とは、ポリフェニレンエーテル類に対して側鎖として
炭素−炭素二重結合および／または炭素−炭素三重結合
を含む官能基を導入したものを指す。その例としては、
次の一般式（Ｉ）で表されるポリフェニレンエーテル樹
脂と一般式（ＩＩＩ）のアルケニルハライドおよび／ま
たは一般式（ＩＶ）のアルキニルハライドの反応生成物
から成る樹脂であって、First, the curable polyphenylene ether resin film, which is the first aspect of the present invention, will be described. The polyphenylene ether resin containing an unsaturated group used in the present invention refers to a polyphenylene ether in which a functional group containing a carbon-carbon double bond and / or a carbon-carbon triple bond is introduced as a side chain. For example,
A resin comprising a reaction product of a polyphenylene ether resin represented by the following general formula (I), an alkenyl halide of the general formula (III) and / or an alkynyl halide of the general formula (IV):
【０００８】[0008]
【化１】 [Chemical 1]
【０００９】[0009]
【化２】 [Chemical 2]
【００１０】Ｘおよび／またはＹ、下記アルケニル基お
よび／またはアルキニル基がそれぞれ共有的にポリフェ
ニレンエーテル樹脂に結合している樹脂を挙げることが
できる。Mention may be made of resins in which X and / or Y and the following alkenyl groups and / or alkynyl groups are covalently bonded to the polyphenylene ether resin.
【００１１】[0011]
【化３】 [Chemical 3]
【００１２】一般式（Ｉ）のポリフェニレンエーテル樹
脂について説明すると、Ｑの代表的な例としては、次の
４種の一般式で表される化合物群が挙げられる。Explaining the polyphenylene ether resin of the general formula (I), typical examples of Q include the following four kinds of compounds represented by the general formula.
【００１３】[0013]
【化４】 [Chemical 4]
【００１４】具体例として、As a concrete example,
【００１５】[0015]
【化５】 [Chemical 5]
【００１６】[0016]
【化６】 [Chemical 6]
【００１７】等がある。一般式（Ｉ）中のＪで表される
ポリフェニレンエーテル鎖中には、該ポリフェニレンエ
ーテル樹脂の耐熱性、熱安定性を低下させない限りにお
いて以下に述べる単位または末端基のうち一種または二
種以上が含まれていてもよい。 ｉ）次の一般式で表される単位であって（ＩＩ）以外の
もの、Etc. In the polyphenylene ether chain represented by J in the general formula (I), one or two or more of the units or terminal groups described below are contained unless the heat resistance and heat stability of the polyphenylene ether resin are reduced. May be included. i) a unit represented by the following general formula other than (II),
【００１８】[0018]
【化７】 [Chemical 7]
【００１９】ｉｉ）次の一般式で表される単位、Ii) a unit represented by the following general formula,
【００２０】[0020]
【化８】 [Chemical 8]
【００２１】ｉｉｉ）次の一般式で表される末端基、Iii) an end group represented by the following general formula:
【００２２】[0022]
【化９】 [Chemical 9]
【００２３】ｉｖ）上記式（ＩＩ）および一般式（Ｖ）
〜（ＶＩＩ）の単位または末端基に対し、スチレン、メ
タクリル酸メチルなどの不飽和結合を持つ重合性モノマ
ーをグラフト重合させて得られる単位または末端基。一
般式（Ｖ）の単位の例としては、Iv) The above formula (II) and general formula (V)
Units or terminal groups obtained by graft-polymerizing a polymerizable monomer having an unsaturated bond such as styrene or methyl methacrylate to the units or terminal groups of (VII). As an example of the unit of the general formula (V),
【００２４】[0024]
【化１０】 [Chemical 10]
【００２５】等が挙げられる。一般式（ＶＩ）の単位の
例としては、And the like. Examples of the unit of general formula (VI) include:
【００２６】[0026]
【化１１】 [Chemical 11]
【００２７】等が挙げられる。一般式（ＶＩＩ）の末端
基の例としては、And the like. Examples of the terminal group of the general formula (VII) include:
【００２８】[0028]
【化１２】 [Chemical 12]
【００２９】等が挙げられる。次に一般式（ＩＩＩ）の
アルケニルハライドの具体的な例を挙げると、アリルク
ロライド、アリルブロマイド、アリルアイオダイド、４
−ブロモ−１−ブテン、トランス−および／またはシス
−１−ブロモ−２−ブテン、トランス−および／または
シス−１−クロロ−２−ブテン、１−クロロ−２−メチ
ル−２−プロペン、５−ブロモ−１−ペンテン、４−ブ
ロモ−２−メチル−２−ブテン、６−ブロモ−１−ヘキ
セン、５−ブロモ−２−メチル−２−ペンテン等があ
る。And the like. Next, specific examples of the alkenyl halide of the general formula (III) will be listed below: allyl chloride, allyl bromide, allyl iodide, 4
-Bromo-1-butene, trans- and / or cis-1-bromo-2-butene, trans- and / or cis-1-chloro-2-butene, 1-chloro-2-methyl-2-propene, 5 -Bromo-1-pentene, 4-bromo-2-methyl-2-butene, 6-bromo-1-hexene, 5-bromo-2-methyl-2-pentene and the like.
【００３０】一般式（ＩＶ）のアルキニルハライドの具
体的な例を挙げるとプロパルギルクロライド、プロパル
ギルブロマイド、プロパルギルアイオダイド、４−ブロ
モ−１−ブチン、４−ブロモ−２−ブチン、５−ブロモ
−１−ペンチン、５−ブロモ−２−ペンチン、１−ヨー
ド−２−ペンチン、１−ヨード−３−ヘキシン、６−ブ
ロモ−１−ヘキシン等がある。Specific examples of the alkynyl halide of the general formula (IV) include propargyl chloride, propargyl bromide, propargyl iodide, 4-bromo-1-butyne, 4-bromo-2-butyne, 5-bromo-1. -Pentyne, 5-bromo-2-pentyne, 1-iodo-2-pentyne, 1-iodo-3-hexyne, 6-bromo-1-hexyne and the like.
【００３１】これらのアルケニルハライドおよびアルキ
ニルハライドは、一種のみあるいは二種以上をあわせて
用いることができる。本発明に用いられる不飽和基が導
入されたポリフェニレンエーテル樹脂は、例えば特公平
５−８９３１号、同５−８９３０号、同５−８９３２号
同５−８９３３号、特開平２−２３２２６０号、同２−
２３３７５９号に開示された方法に従い、一般式（Ｉ）
のポリフェニレンエーテル樹脂を有機金属でメタル化
し、続いてアルケニルハライド（ＩＩＩ）および／また
はアルケニルハライド（ＩＶ）で置換反応することによ
り製造することができる。These alkenyl halides and alkynyl halides can be used alone or in combination of two or more. Examples of the polyphenylene ether resin having an unsaturated group used in the present invention include JP-B-5-8931, JP-A-5-8930, JP-A-5-8932 and JP-A-5-8933, and JP-A-2-232260. 2-
According to the method disclosed in US Pat.
Can be produced by metallizing the polyphenylene ether resin of (1) with an organic metal and then subjecting it to a substitution reaction with an alkenyl halide (III) and / or an alkenyl halide (IV).
【００３２】本方法に従って製造されるポリフェニレン
エーテル樹脂は、少なくとも次の２種ないし３種の構造
式で表される単位より構成される。The polyphenylene ether resin produced according to the present method is composed of at least two or three units represented by the following structural formulas.
【００３３】[0033]
【化１３】 [Chemical 13]
【００３４】さらには上記の他、次の単位を含むことも
ある。In addition to the above, the following units may be included.
【００３５】[0035]
【化１４】 [Chemical 14]
【００３６】上記一般式（ＶＩＩＩ）に由来するハロゲ
ンの含量は、該ポリフェニレンエーテル樹脂を基準とし
て０以上（Ｍが水素原子の場合）３０重量％以下の範囲
であり、より好ましくは０以上２０重量％以下の範囲で
ある。本発明に用いられる不飽和基が導入されたポリフ
ェニレンエーテル樹脂中には、必ずしもハロゲンが含ま
れる必要はない。しかしながらハロゲンが特に塩素、臭
素である場合には、本発明の硬化性ポリフェニレンエー
テル系樹脂組成物に難燃性を付与できるという効果があ
る。難燃性を付与する場合好ましいハロゲンの含量は１
重量％以上である。しかし３０重量％を越えるとポリフ
ェニレンエーテル樹脂自体の熱安定性が低下するので好
ましくない。The content of halogen derived from the above general formula (VIII) is in the range of 0 or more (when M is a hydrogen atom) 30% by weight or less, more preferably 0 or more and 20% by weight, based on the polyphenylene ether resin. % Or less. The unsaturated group-introduced polyphenylene ether resin used in the present invention does not necessarily need to contain halogen. However, when the halogen is chlorine or bromine, there is an effect that flame retardancy can be imparted to the curable polyphenylene ether resin composition of the present invention. When imparting flame retardancy, the preferred halogen content is 1
It is more than weight%. However, if it exceeds 30% by weight, the thermal stability of the polyphenylene ether resin itself is deteriorated, which is not preferable.
【００３７】上記の方法で得られる不飽和基が導入され
たポリフェニレンエーテル樹脂の好ましい例としては、
以下に述べるポリフェニレンエーテル系樹脂とアリルブ
ロマイド、アリルクロライド、プロパルギルブロマイ
ド、プロパルギルクロライドの反応生成物からなる樹脂
を挙げることができる。ポリフェニレンエーテル系樹脂
としては、２，６−ジメチルフェノールの単独重合で得
られるポリ（２，６−ジメチル−１，４−フェニレンエ
ーテル）、ポリ（２，６−ジメチル−１，４−フェニレ
ンエーテル）のポリスチレングラフト共重合体、２，６
−ジメチルフェノールと２，３，６−トリメチルフェノ
ールの共重合体、２，６−ジメチルフェノールと２，６
−ジメチル−３−フェニルフェノールの共重合体、２，
６−ジメチルフェノールを多官能性フェノール化合物Preferred examples of the unsaturated group-introduced polyphenylene ether resin obtained by the above method include:
The resin which consists of the reaction product of polyphenylene ether-type resin and allyl bromide, allyl chloride, propargyl bromide, and propargyl chloride described below can be mentioned. Examples of the polyphenylene ether resin include poly (2,6-dimethyl-1,4-phenylene ether) and poly (2,6-dimethyl-1,4-phenylene ether) obtained by homopolymerization of 2,6-dimethylphenol. Polystyrene graft copolymer of 2,6
-Copolymer of dimethylphenol and 2,3,6-trimethylphenol, 2,6-dimethylphenol and 2,6
-Dimethyl-3-phenylphenol copolymer, 2,
6-Dimethylphenol is a polyfunctional phenol compound
【００３８】[0038]
【化１５】 [Chemical 15]
【００３９】の存在下で重合して得られた多官能性ポリ
フェニレンエーテル樹脂、例えば特開昭６３−３０１２
２２号、特開平１−２９７４８号に開示されているよう
な一般式（Ｖ）および（ＶＩ）の単位を含む共重合体、
例えば特願平１−１３５７６３号に開示されているよう
な一般式（Ｖ）の単位および一般式（ＶＩＩ）の末端基
を含む樹脂等を挙げることができる。A polyfunctional polyphenylene ether resin obtained by polymerization in the presence of, for example, JP-A-63-3012.
No. 22, a copolymer containing units of the general formulas (V) and (VI) as disclosed in JP-A-1-29748,
For example, a resin containing a unit of general formula (V) and an end group of general formula (VII) as disclosed in Japanese Patent Application No. 1-135763 can be mentioned.
【００４０】本発明の硬化性ポリフェニレンエーテルフ
ィルムに用いられる不飽和基を含むポリフェニレンエー
テル樹脂の他の例としては、次のような繰り返し単位を
含む樹脂を挙げることができる。Other examples of the polyphenylene ether resin containing an unsaturated group used in the curable polyphenylene ether film of the present invention include resins containing the following repeating units.
【００４１】[0041]
【化１６】 [Chemical 16]
【００４２】具体的な例としては、米国特許第３４２２
０６２号に開示されているような２−アリル−６−メチ
ルフェノールと、２，６−ジメチルフェノールの共重合
体、米国特許第３２８１３９３号に開示されているよう
な２，６−ジアリル−４−ブロモフェノールと２，６−
ジメチル−４−ブロモフェノールの共重合体、特公昭６
３−４７７３３号に開示されているような２，６−ジプ
レニルフェノールと２，６−ジメチルフェノールの共重
合体、同じく２，６−ビス（２−ブテニル）フェノール
と２，６−ジメチルフェノールの共重合体、同じく２，
６−ジシンナミルフェノールと２，６−ジメチルフェノ
ールの共重合体、特開昭５８−２７７１９号の開示され
ているような２−プレニル−６−メチルフェノールの単
独重合体、同じく２−プレニル−６−メチルフェノール
と２，６−ジメチルフェノールの共重合体、同じく２−
（２−ブテニル）−６−メチルフェノールの単独重合
体、同じく２−（２−ブテニル）−６−メチルフェノー
ルと２，６−ジメチルフェノールの共重合体、同じく２
−シンナミル−６−メチルフェノールの単独重合体、同
じく２−シンナミル−６−メチルフェノールと２，６−
ジメチルフェノールの共重合体等が挙げられる。A specific example is US Pat. No. 3,422.
Copolymers of 2-allyl-6-methylphenol with 2,6-dimethylphenol as disclosed in 062, 2,6-Diallyl-4- as disclosed in U.S. Pat. No. 3,281,393. Bromophenol and 2,6-
Copolymer of dimethyl-4-bromophenol, Japanese Patent Publication No. 6
A copolymer of 2,6-diprenylphenol and 2,6-dimethylphenol as disclosed in 3-47733, also of 2,6-bis (2-butenyl) phenol and 2,6-dimethylphenol. Copolymer, also 2,
A copolymer of 6-dicinnamylphenol and 2,6-dimethylphenol, a homopolymer of 2-prenyl-6-methylphenol as disclosed in JP-A-58-27719, and also 2-prenyl-6. -A copolymer of methylphenol and 2,6-dimethylphenol, also 2-
A homopolymer of (2-butenyl) -6-methylphenol, a copolymer of 2- (2-butenyl) -6-methylphenol and 2,6-dimethylphenol, and a homopolymer of 2
-Cinnamyl-6-methylphenol homopolymer, also 2-cinnamyl-6-methylphenol and 2,6-
Examples thereof include a dimethylphenol copolymer.
【００４３】また米国特許第４６３４７４２号に開示さ
れたポリ（２，６−ジメチル−１，４−フェニレンエー
テル）の２，６位のメチル基をビニル基に変換して得ら
れる樹脂、同じくポリ（２，６−ジメチル−１，４−フ
ェニレンエーテル）のフェニル基の３，５位にビニル基
を導入して得られる樹脂も本発明に用いられる不飽和基
を含むポリフェニレンエーテル樹脂の好ましい例の一つ
である。A resin obtained by converting the methyl group at the 2,6-position of poly (2,6-dimethyl-1,4-phenylene ether) disclosed in US Pat. No. 4,634,742 into a vinyl group, also poly ( A resin obtained by introducing a vinyl group into the 3,5-position of the phenyl group of (2,6-dimethyl-1,4-phenylene ether) is also a preferable example of the polyphenylene ether resin containing an unsaturated group used in the present invention. Is one.
【００４４】本発明において用いられる不飽和基を含む
ポリフェニレンエーテル樹脂の不飽和基の含量の範囲
は、次式の定義に従った場合０．１モル％以上１００モ
ル％以下、より好ましくは０．５モル％以上５０モル％
以下が好適である。The range of the unsaturated group content of the polyphenylene ether resin containing an unsaturated group used in the present invention is 0.1 mol% or more and 100 mol% or less, more preferably 0. 5 mol% or more and 50 mol%
The following are preferred:
【００４５】[0045]
【数１】 [Equation 1]
【００４６】不飽和基の含量が０．１モル％未満では硬
化後の耐薬品性の改善が不十分となるので好ましくな
い。逆に１００モル％を越えると硬化後において非常に
脆くなるので好ましくない。また本発明において用いら
れる不飽和基が導入されたポリフェニレンエーテル樹脂
の分子量については、３０℃，０．５ｇ／ｄｌのクロロ
ホルム溶液で測定した粘度数ηｓｐ／ｃが０．１〜１．
０の範囲にあるものが良好に使用できる。If the unsaturated group content is less than 0.1 mol%, the chemical resistance after curing is insufficiently improved, which is not preferable. On the contrary, if it exceeds 100 mol%, it becomes very brittle after curing, which is not preferable. Regarding the molecular weight of the unsaturated group-introduced polyphenylene ether resin used in the present invention, the viscosity number ηsp / c measured with a chloroform solution at 30 ° C. and 0.5 g / dl is 0.1 to 1.
Those in the range of 0 can be used favorably.
【００４７】本発明で用いられる難燃剤Ｎ−トリブロモ
フェニルマレイミドは、次の構造式で表される。The flame retardant N-tribromophenylmaleimide used in the present invention is represented by the following structural formula.
【００４８】[0048]
【化１７】 [Chemical 17]
【００４９】難燃剤の添加量は、不飽和基を含むポリフ
ェニレンエーテル樹脂１００重量部に対し、１０〜５０
重量部であり、好ましくは、１０〜４０重量部、特に好
ましくは１０〜３０重量部である。添加量が５０重量部
を越えると、硬化フィルムの屈曲性が劣り好ましくな
い。また、添加量が１０重量部未満では、難燃性が得ら
れない。The amount of the flame retardant added is 10 to 50 relative to 100 parts by weight of the polyphenylene ether resin containing an unsaturated group.
Parts by weight, preferably 10 to 40 parts by weight, particularly preferably 10 to 30 parts by weight. If the amount added exceeds 50 parts by weight, the flexibility of the cured film is poor, which is not preferable. If the amount added is less than 10 parts by weight, flame retardancy cannot be obtained.
【００５０】本発明の不飽和基を含むポリフェニレンエ
ーテル樹脂と難燃剤を混合する方法としては、２者を溶
媒中に均一に溶解させる溶液混合法が利用できる。溶液
混合に用いられる溶媒としては、ジクロロメタン、クロ
ロホルム、トリクロロエチレンなどのハロゲン系溶媒、
ベンゼン、トルエン、キシレン等の芳香族系溶媒または
テトラヒドロフランが単独で、あるいは二種以上を組み
合わせて用いられる。As a method for mixing the polyphenylene ether resin having an unsaturated group of the present invention and the flame retardant, a solution mixing method in which the two are uniformly dissolved in a solvent can be used. As the solvent used for solution mixing, a halogen-based solvent such as dichloromethane, chloroform or trichloroethylene,
Aromatic solvents such as benzene, toluene and xylene, or tetrahydrofuran are used alone or in combination of two or more.
【００５１】本発明の硬化性ポリフェニレンエーテルフ
ィルムの製造方法は特に限定されないが、通常の溶媒成
膜法（キャスティング法）、スピンコート法等が利用で
き、０．１〜１０００μｍの厚みのものが製造できる。
得られたフィルムは、赤外吸収スペクトル法、高分解能
固体核磁気共鳴スペクトル法等の方法を用いて樹脂組成
物を解析することができる。The method for producing the curable polyphenylene ether film of the present invention is not particularly limited, but the usual solvent film-forming method (casting method), spin coating method, etc. can be used, and the one having a thickness of 0.1 to 1000 μm is produced. it can.
The resin composition of the obtained film can be analyzed by methods such as infrared absorption spectroscopy and high resolution solid state nuclear magnetic resonance spectroscopy.
【００５２】本発明のフィルムは、上記の難燃剤の他に
その用途に応じて所望の性能を付与する目的で本来の性
質を損なわない範囲の量の添加剤を配合して成膜するこ
とができる。添加剤としては、酸化防止剤、熱安定剤、
帯電防止剤、可塑剤、顔料、染料、着色剤などが挙げら
れる。また、ポリフェニレンエーテルをはじめとする熱
可塑性樹脂、あるいは他の熱硬化性樹脂を一種または二
種以上配合することも可能である。本発明の第２の硬化
ポリフェニレンエーテルフィルムは、以上に述べた硬化
性ポリフェニレンエーテルフィルムを硬化することによ
り得られるものであり、熱、光、電子線等による方法を
採用することができる。The film of the present invention may be formed by adding, in addition to the above-mentioned flame retardant, an additive in an amount within a range that does not impair the original properties for the purpose of imparting desired performance depending on its use. it can. As additives, antioxidants, heat stabilizers,
Antistatic agents, plasticizers, pigments, dyes, colorants and the like can be mentioned. It is also possible to blend one or more thermoplastic resins such as polyphenylene ether or other thermosetting resins. The second cured polyphenylene ether film of the present invention is obtained by curing the above-mentioned curable polyphenylene ether film, and a method using heat, light, electron beam or the like can be adopted.
【００５３】加熱による硬化の温度は、１００〜３５０
℃、より好ましくは１５０〜３００℃範囲で選ばれる。
また時間は１分〜５時間程度、より好ましくは１分〜３
時間である。本発明の第３である積層体は、上記第２発
明の硬化ポリフェニレンエーテルフィルムと金属箔より
構成される。ここで用いられる金属箔としては、例えば
銅箔、アルミニウム箔等が挙げられる。その厚みは特に
限定されないが、５〜２００μｍ、より好ましくは５〜
１００μｍの範囲である。The temperature for curing by heating is 100 to 350.
C., more preferably in the range of 150 to 300.degree.
The time is about 1 minute to 5 hours, more preferably 1 minute to 3 hours.
It's time. The third laminate of the present invention comprises the cured polyphenylene ether film of the second invention and a metal foil. Examples of the metal foil used here include copper foil and aluminum foil. The thickness is not particularly limited, but is 5 to 200 μm, and more preferably 5 to
It is in the range of 100 μm.
【００５４】本発明の積層体の製造方法は特に限定され
ないが通常、フィルムを金属箔で挟み、加熱加圧下でプ
レス成形する方法が用いられる。The method for producing the laminate of the present invention is not particularly limited, but usually a method of sandwiching a film with a metal foil and press-molding under heating and pressurization is used.
【００５５】[0055]
【実施例】以下、本発明を一層明確にするために実施例
を挙げて説明するが、本発明の範囲をこれらの実施例に
限定するものではない。以下、物性測定方法を示し、実
施例に用いた各成分を参考例１〜３に示す。 （１）難燃性 ＵＬ−９４に準拠 （２）耐薬品性 銅箔を除去したフィルムを次に挙げる薬品にそれぞれ２
３℃５分間浸漬し、外観の変化を目視により観察した。 ・塩素系溶剤：１，１，１−トリクロロエタン ・アルコール：イソプロピルアルコール ・アルカリ：水酸化ナトリウム水溶液（２Ｎ） ・酸：塩酸（２Ｎ） （３）ハンダ耐熱性 ＪＰＣＡ規格に準拠し、一部銅箔を除去したフィルムを
２６０℃のハンダ浴中に５秒間浮かべ、外観の変化を目
視により観察した。 （４）屈曲性 サンプルは、銅箔を除去したフィルムで幅１５ｍｍとし
た。これをＪＩＳ規格Ｃ５０１６に準拠し、耐折性試験
機により連続的に屈曲させ、フィルムが切断するまでの
屈曲回数を測定した。なお耐折性試験機の折り曲げ面の
曲率半径は０．３８ｍｍである。EXAMPLES Hereinafter, the present invention will be described with reference to examples in order to further clarify the present invention, but the scope of the present invention is not limited to these examples. Hereinafter, a method for measuring physical properties will be shown, and each component used in Examples will be shown in Reference Examples 1 to 3. (1) Flame retardance Compliant with UL-94 (2) Chemical resistance A film obtained by removing a copper foil is added to each of the chemicals listed below as 2
It was immersed at 3 ° C. for 5 minutes, and the change in appearance was visually observed. -Chlorine-based solvent: 1,1,1-trichloroethane-Alcohol: isopropyl alcohol-Alkali: Sodium hydroxide aqueous solution (2N) -Acid: Hydrochloric acid (2N) (3) Solder heat resistance Based on JPCA standards, some copper foil The film from which was removed was floated in a solder bath at 260 ° C. for 5 seconds, and the change in appearance was visually observed. (4) Flexibility The sample was a film from which the copper foil was removed and had a width of 15 mm. According to JIS C5016, this was continuously bent by a folding endurance tester, and the number of times of bending until the film was cut was measured. The bending radius of the folding surface of the folding endurance tester is 0.38 mm.
【００５６】[0056]
【参考例１】 不飽和基を含むポリフェニレンエーテル樹脂 平均置換率１４％、粘度数はηｓｐ／Ｃ＝０．６２（３
０℃，０．５ｇ／ｄｌ、クロロホルム溶液）のアリル基
置換ポリフェニレンエーテル（Ａ−ＰＰＥと略す）を特
公平５−８９３０号に開示された公知の方法に従ってη
ｓｐ／Ｃ＝０．５６のポリ（２，６−ジメチル−１，４
−フェニレンエーテル）より合成した。Reference Example 1 Polyphenylene ether resin containing unsaturated group Average substitution rate 14%, viscosity number ηsp / C = 0.62 (3
An allyl group-substituted polyphenylene ether (abbreviated as A-PPE) at 0 ° C., 0.5 g / dl, chloroform solution) was prepared according to the known method disclosed in JP-B-5-8930.
poly (2,6-dimethyl-1,4) with sp / C = 0.56
-Phenylene ether).
【００５７】[0057]
【参考例２】 不飽和基を含むポリフェニレンエーテル樹脂 平均置換率５％、ηｓｐ／Ｃ＝０．４０（３０℃，０．
５ｇ／ｄｌ、クロロホルム溶液）のプロパギル基置換ポ
リフェニレンエーテル（Ｐｒ−ＰＰＥと略す）を特公平
５−８９３０号に開示された公知の方法に従ってηｓｐ
／Ｃ＝０．５６のポリ（２，６−ジメチル−１，４−フ
ェニレンエーテル）より合成した。Reference Example 2 Polyphenylene ether resin containing unsaturated group Average substitution rate 5%, ηsp / C = 0.40 (30 ° C., 0.
5 g / dl, chloroform solution) of a propargyl group-substituted polyphenylene ether (abbreviated as Pr-PPE) according to a known method disclosed in JP-B-5-8930.
It was synthesized from poly (2,6-dimethyl-1,4-phenylene ether) with /C=0.56.
【００５８】[0058]
【参考例３】 開始剤 ２、５−ジメチル−２、５−ジ（ｔ−ブチルパーオキシ
ン）ヘキシン−３（日本油脂 パーヘキシン２５Ｂ；Ｐ
Ｈ２５Ｂと略す）[Reference Example 3] Initiator 2,5-dimethyl-2,5-di (t-butylperoxine) hexyne-3 (NOF Perhexin 25B; P
(Abbreviated as H25B)
【００５９】[0059]
【実施例１〜４】参考例１で合成した不飽和基を含むポ
リフェニレンエーテル４２ｇに、ＰＨ２５Ｂを１重量
部、難燃剤を表１に示した添加量で添加し、トリクロロ
エチレン１００ｍｌに溶解させガラス板上にキャストし
成膜した。このフィルムを１３０℃、４時間エアーオー
ブン中で乾燥させて得られたフィルムの厚さは約６５μ
m であった。乾燥フィルムの両面に厚さ３５μm の銅箔
を置き、２００℃、３０分、圧力４４ｋｇ／ｃｍ2 の条
件でプレス成形し、銅箔と接着させ、硬化させた。Examples 1 to 4 To 42 g of polyphenylene ether containing an unsaturated group synthesized in Reference Example 1, 1 part by weight of PH25B and a flame retardant were added in the amounts shown in Table 1, and dissolved in 100 ml of trichloroethylene to prepare a glass plate. A film was formed by casting on top. The film obtained by drying this film in an air oven at 130 ° C. for 4 hours has a thickness of about 65 μm.
It was m. A copper foil having a thickness of 35 μm was placed on both sides of the dried film, press-molded under the conditions of 200 ° C. for 30 minutes and a pressure of 44 kg / cm 2 , adhered to the copper foil and cured.
【００６０】こうして得た銅張フィルムの諸物性の測定
結果を表１に示す。また、銅箔とフィルムとのピール強
度はすべての実施例で１．７Ｋｇ／ｃｍ以上で銅箔はフ
ィルムと良く接着していた。更に、得られたフィルムの
誘電率は、全ての実施例で、２．６であった。Table 1 shows the measurement results of various physical properties of the copper clad film thus obtained. The peel strength between the copper foil and the film was 1.7 kg / cm or more in all the examples, and the copper foil was well adhered to the film. Furthermore, the dielectric constants of the obtained films were 2.6 in all the examples.
【００６１】[0061]
【実施例５〜８】参考例２で合成した不飽和基を含むポ
リフェニレンエーテル４２ｇに、ＰＨ２５Ｂを１重量
部、難燃剤を表１に示した添加量で添加し、トリクロロ
エチレン１００ｍｌに溶解させガラス板上にキャストし
成膜した。このフィルムを１３０℃、４時間エアーオー
ブン中で乾燥させて得られたフィルムの厚さは約６５μ
m であった。乾燥フィルムの両面に厚さ３５μm の銅箔
を置き、２００℃、３０分、圧力４４ｋｇ／ｃｍ2 の条
件でプレス成形し、銅箔と接着させ、硬化させた。Examples 5 to 8 To 42 g of polyphenylene ether containing an unsaturated group synthesized in Reference Example 2, 1 part by weight of PH25B and a flame retardant were added in the amounts shown in Table 1, and dissolved in 100 ml of trichloroethylene to prepare a glass plate. A film was formed by casting on top. The film obtained by drying this film in an air oven at 130 ° C. for 4 hours has a thickness of about 65 μm.
It was m. A copper foil having a thickness of 35 μm was placed on both sides of the dried film, press-molded under the conditions of 200 ° C. for 30 minutes and a pressure of 44 kg / cm 2 , adhered to the copper foil and cured.
【００６２】こうして得た銅張フィルムの諸物性の測定
結果を表１に示す。また、銅箔とフィルムとのピール強
度はすべての実施例で１．７Ｋｇ／ｃｍ以上で銅箔はフ
ィルムと良く接着していた。更に、得られたフィルムの
誘電率は、全ての実施例で、２．６であった。Table 1 shows the measurement results of various physical properties of the copper clad film thus obtained. The peel strength between the copper foil and the film was 1.7 kg / cm or more in all the examples, and the copper foil was well adhered to the film. Furthermore, the dielectric constants of the obtained films were 2.6 in all the examples.
【００６３】[0063]
【比較例１〜２】参考例１または２で合成した不飽和基
を含むポリフェニレンエーテルを用い、表１に示した組
成で、実施例と同様の操作を行い、フィルムを作成し
た。これらの銅張フィルムの諸物性の測定結果を表１に
示した。難燃剤の添加量が１０重量部より少ない場合、
難燃性が得られない。Comparative Examples 1 and 2 Using the polyphenylene ether containing an unsaturated group synthesized in Reference Example 1 or 2, the composition shown in Table 1 was used, and the same operations as in Examples were carried out to prepare films. Table 1 shows the results of measurement of various physical properties of these copper-clad films. If the amount of flame retardant added is less than 10 parts by weight,
Flame retardance cannot be obtained.
【００６４】[0064]
【比較例３〜４】参考例１または２で合成した不飽和基
を含むポリフェニレンエーテルを用い、表１に示した組
成で、実施例と同様の操作を行い、フィルムを作成し
た。これらの銅張フィルムの諸物性の測定結果を表１に
示した。難燃剤の添加量が多すぎる場合、屈曲性が劣化
してしまうことが明らかとなった。[Comparative Examples 3 to 4] Using the polyphenylene ether containing an unsaturated group synthesized in Reference Example 1 or 2, the composition shown in Table 1 was used, and the same operations as in Examples were carried out to prepare films. Table 1 shows the results of measurement of various physical properties of these copper-clad films. It was clarified that when the amount of flame retardant added was too large, the flexibility deteriorated.
【００６５】[0065]
【表１】 [Table 1]
【００６６】[0066]
【発明の効果】本発明のポリフェニレンエーテルフィル
ムは、適した難燃剤を用い、添加量が最も適しているた
め、フィルムの持つ屈曲性を損なうことなく優れた難燃
性を発揮する。さらに優れた誘電特性、耐熱性、耐薬品
性、銅との接着性を備えている。INDUSTRIAL APPLICABILITY The polyphenylene ether film of the present invention uses a suitable flame retardant and the addition amount is most suitable, so that it exhibits excellent flame retardancy without impairing the flexibility of the film. It also has excellent dielectric properties, heat resistance, chemical resistance, and adhesion to copper.
【００６７】従って、本発明のポリフェニレンエーテル
フィルムは、誘電材料、絶縁材料、耐熱材料等として用
いることができる。特に片面、両面フレキシブルプリン
ト基板用フィルムとして好適に用いられる。また、銅箔
との接着性に優れているため接着剤を必要としないで直
接銅箔と本発明のフィルムを積層できるので、いわゆる
２層型フレキシブルプリント基板として使用できる。Therefore, the polyphenylene ether film of the present invention can be used as a dielectric material, an insulating material, a heat resistant material and the like. In particular, it is preferably used as a film for a single-sided or double-sided flexible printed circuit board. Further, since it has excellent adhesiveness to the copper foil, the copper foil and the film of the present invention can be directly laminated without the need for an adhesive, and thus it can be used as a so-called two-layer flexible printed board.
Claims (3)
テル樹脂１００重量部および難燃剤Ｎ−トリブロモフェ
ニルマレイミド１０〜５０重量部からなる硬化性ポリフ
ェニレンエーテルフィルム。1. A curable polyphenylene ether film comprising 100 parts by weight of a polyphenylene ether resin containing an unsaturated bond group and 10 to 50 parts by weight of a flame retardant N-tribromophenylmaleimide.
ーテルフィルムを硬化して得られた硬化ポリフェニレン
エーテルフィルム。2. A cured polyphenylene ether film obtained by curing the curable polyphenylene ether film according to claim 1.
テルフィルムと金属箔とからなる積層体。3. A laminate comprising the cured polyphenylene ether film according to claim 2 and a metal foil.