JPH0623589Y2 - Elastic tricot warp knit - Google Patents
Elastic tricot warp knitInfo
- Publication number
- JPH0623589Y2 JPH0623589Y2 JP1988056221U JP5622188U JPH0623589Y2 JP H0623589 Y2 JPH0623589 Y2 JP H0623589Y2 JP 1988056221 U JP1988056221 U JP 1988056221U JP 5622188 U JP5622188 U JP 5622188U JP H0623589 Y2 JPH0623589 Y2 JP H0623589Y2
- Authority
- JP
- Japan
- Prior art keywords
- yarn
- denier
- strength
- fabric
- polyamide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【考案の詳細な説明】
(産業上の利用分野)
本考案はブラジャー、ガードルなどのファンデーショ
ン、ショーツなどのインナー、そして水着などに適する
伸縮性たて編地に関するものである。DETAILED DESCRIPTION OF THE INVENTION (Industrial field of application) The present invention relates to a stretchable warp knitted fabric suitable for foundations such as brassieres and girdles, inners such as shorts, and swimwear.
(従来の技術)
従来よりファンデーション、インナー、水着用生地とし
てナイロン繊維糸と弾性繊維糸とを交編したたて編地、
あるいはこれらの糸と吸湿性繊維糸とを交編したたて編
地は知られている。(Prior Art) A warp knitted fabric in which nylon fiber yarns and elastic fiber yarns have been knitted as a foundation, an inner, and a cloth for wearing water conventionally.
Alternatively, a warp knitted fabric in which these yarns and hygroscopic fiber yarns are interwoven is known.
最近は高級化の一方向として、生地の薄地化、天然繊維
志向による綿交編化の検討が進みつつある。しかし、薄
地化するために主素材であるポリアミド繊維糸を単に細
デニール化すると、生地の引裂強度、破裂強力が低下
し、実用に適する商品が得られず、用途面でも限定され
る。そこで、高強力ポリアミド繊維糸を用いて細デニー
ル化すると、生地の強力は維持できるものの、前記高強
力ポリアミドは通常のレジンを使用して紡糸し、延伸倍
率を大きくして得られるため、糸強力は大きくなるもの
の、伸度が低下し、ひいては生地の伸長率が低下し、更
に編立時の糸切れが発生し、品質に優れた生地とは言い
難いものであった。また、生地の薄地化のため弾性繊維
糸を細くすることも考えられるが、単に細くすると生地
の伸縮力も大巾に低下し、フィット性、緊迫力が劣るた
め実用性に欠ける。綿糸を交編した生地は、主としてフ
ァンデーション用生地に用にられるが薄地化の要望は水
着用途より強い。しかし、綿糸を付加することで薄地化
はさらに困難となっている。綿糸を細くすることも考え
られるが、弾性糸交編のたて編編成は強度的に綿番手で
80s/1程度が使用できる限界であり、これでも編成
時の糸切が多く、品質のよい安定した生地を得にくい。
現状は綿糸では単糸の場合細デニール(10〜20デニ
ール)のナイロンを綿糸にカバリングし、補強して使う
ことが多い。また、最近は双糸使い(60s/2〜140s
/2)にし、生地厚だが糸切の少ない品質の安定した生地
を作っているのが現状である。したがって、細番手綿糸
を使うことは品質面、操業面で限界がある。Recently, as one direction for high-grade products, studies are underway to make the fabric thinner and to knit cotton with a natural fiber orientation. However, if the polyamide fiber yarn, which is the main material, is thinly denier for thinning, the tear strength and burst strength of the fabric will be reduced, and commercial products will not be obtained, and the application will be limited. Therefore, when fine denier is made using high-strength polyamide fiber yarn, although the strength of the fabric can be maintained, the high-strength polyamide is obtained by spinning using a normal resin and increasing the draw ratio, so that the yarn strength is high. However, the elongation was lowered, the elongation rate of the fabric was lowered, and further the yarn breakage occurred during knitting, and it was hard to say that the fabric was excellent in quality. Further, it is possible to thin the elastic fiber yarn for thinning the fabric, but if it is simply thinned, the stretching force of the fabric is greatly reduced, and the fitting property and the tension force are poor, so that it is not practical. Fabrics made by knitting cotton threads are mainly used for foundation fabrics, but the demand for thinner fabrics is stronger than for swimwear. However, the addition of cotton threads makes it even more difficult to thin the fabric. Although it is conceivable to make the cotton thread thin, the warp knitting of the elastic yarn interlaced knitting has a strength limit of about 80 s / 1 for the cotton count. Even with this, there are many thread cuttings during knitting and the quality is good. It is difficult to obtain a stable fabric.
At present, in the case of a single yarn of cotton yarn, nylon of fine denier (10 to 20 denier) is often covered and reinforced to cover the cotton yarn. Also, recently, twin yarn maker (60s / 2 ~ 140s
/ 2), and the current situation is to make a stable fabric with a thick fabric but little thread cutting. Therefore, the use of fine count cotton threads is limited in terms of quality and operation.
以上の理由から現在はポリアミド繊維糸30デニール以
下を使用した水着、インナー、ファンデーション用の薄
地伸縮性生地で、強力、伸縮力とも実用に適し、品質の
よいものが得られていないものが実状である。For the above reasons, at present, thin stretchable fabrics for swimwear, innerwear, and foundations using polyamide fiber yarn of 30 denier or less are suitable for practical use in both strength and stretchability, and good quality has not been obtained. is there.
(考案が解決しようとする課題)
本考案は薄地でありがら、実用上、満足しうる引裂強力
や破裂強力を有し、しかも充分伸縮性があり、ファンデ
ーション、インナー、水着用途に好適である伸縮性たて
編地を提供することにある。(Problems to be solved by the invention) Although the present invention is thin, it has practically satisfactory tear strength and burst strength, and is sufficiently stretchable, making it suitable for foundation, innerwear and swimwear applications. The purpose is to provide a warp knitted fabric.
(課題を解決するための手段)
少なくとも下記A糸及びB糸から編成されてなることを
特徴とする伸縮性トリコット経編地。(Means for Solving the Problem) A stretchable tricot warp knitted fabric, which is formed by knitting at least the following A yarn and B yarn.
A糸:単糸1〜5デニール、トータル10〜30デニー
ル、相対粘度(RV)2.5〜4.0、破断強度(DT)7.0
〜10.0g/d、破断伸度30%以上のポリアミド系合成繊
維マルチフィラメント糸。Yarn A: Single yarn 1 to 5 denier, total 10 to 30 denier, relative viscosity (RV) 2.5 to 4.0, breaking strength (DT) 7.0
Polyamide-based synthetic fiber multifilament yarn having a breaking elongation of 30% or more up to 10.0 g / d.
B糸:単糸3〜15デニール、トータル20〜280デ
ニール、破断伸度350%以上のゴム状弾性繊維糸。B yarn: A rubber-like elastic fiber yarn having a single yarn of 3 to 15 denier, a total of 20 to 280 denier, and a breaking elongation of 350% or more.
本考案において意図する相対粘度(RV)が2.5〜4.0、
破断強度(DT)が7.0〜10.0g/dであるポリアミド系合
成繊維マルチフィラメント糸は2.5〜4.0の相対粘度を有
するポリアミドを溶融紡糸したのち、延伸することによ
り得られる。勿論、直接紡糸延伸法によっても得られ
る。相対粘度を大きくすることによって、これを紡糸し
た場合、これまでの紡糸スピードでは後伸び率が大き
く、巻取り不能になるため、巻取りスピードは300〜
1000m/分が好ましく、より好ましいのは300〜
500m/分である。この場合、未延伸糸は配向が進
む。該未延伸糸に、延伸倍率2.0〜4.5倍で冷延伸または
熱延伸を行ない、また紡糸ノズル下の加熱筒温度を上げ
たり、冷却風の温度を下げたりすることによって、破断
強度(DT)が7.0〜10.0g/dという非常に強度の高い高
強力ポリアミド繊維が得られる。ポリアミド繊維のマル
チフイラメント糸の太さは単糸デニールが1〜5デニー
ルであることが必要であり、トータルデニールは10〜
30デニールであることが必要である。単糸デニールが
5.0デニールを超えるとフイラメント数が少なくなるた
め、得られた編地の風合いがかたくなりよくない。ま
た、1デニール未満の場合、編地がやわらかくなりす
ぎ、編成が困難となる。好ましいのは2〜4デニールで
ある。このような高強力ポリアミド繊維を用いることに
より、糸の太さを細くしても充分な強力が得られる。た
とえば、糸太さが20デニールであっても破断強度や引
裂強度は従来のポリアミドマルチフイラメント糸の40
デニールと同等の値が得られる。又、前記高強力ポリア
ミド繊維の破断伸度(乾伸度)は30%以上であり、得
られた編地の伸長率は高く、編立時の糸切れも発生する
ことがないものとなる。30%未満であれば編地の伸長
率が劣り、ファンデーションや水着等には不向きなもの
となり、編立時の糸切れも発生し、生産性にも劣るもの
となる。ポリアミド系合成繊維マルチフィラメント糸を
構成するポリアミドは、たとえば、ポリカプロラクタム
(ナイロン6)、ポリヘキサメチレンアジパミド(ナイ
ロン66)、ポリヘキサメチレンセパクアミド(ナイロ
ン610)、ポリテトラメチレンアジパミド(ナイロン
46)、これらのポリアミドのコポリマーおよび1,4
−シクロヘキサンビス(メチルアミン)と線状脂肪族ジ
カルボン酸の縮合生成物を挙材とするポリアミド類など
である。このようなポリアミドには必要に応じて艶消し
剤、顔料、光安定剤、熱安定剤、酸化防止剤、帯電防止
剤、染色性向上剤あるいは接着性向上剤などを配合する
ことができる。該ポリアミド系合成繊維は、フイラメン
トヤーンとして用いられてもよく、また、通常の仮撚条
件で仮撚加工を行ない加工糸として用いられてもよい。The relative viscosity (RV) intended in the present invention is 2.5 to 4.0,
The polyamide-based synthetic fiber multifilament yarn having a breaking strength (DT) of 7.0 to 10.0 g / d is obtained by melt spinning a polyamide having a relative viscosity of 2.5 to 4.0 and then stretching. Of course, it can also be obtained by the direct spinning and drawing method. When this is spun by increasing the relative viscosity, the post-expansion rate is large at the conventional spinning speed, making it impossible to wind the film.
1000 m / min is preferable, and more preferably 300-
500 m / min. In this case, the orientation of the undrawn yarn proceeds. The unstretched yarn is cold-stretched or hot-stretched at a draw ratio of 2.0 to 4.5, and the breaking strength (DT) is increased by raising the temperature of the heating cylinder under the spinning nozzle or lowering the temperature of the cooling air. It is possible to obtain a high-strength polyamide fiber having a very high strength of 7.0 to 10.0 g / d. The thickness of the multifilament yarn of polyamide fiber must be 1 to 5 denier per single yarn denier, and the total denier is 10 to 10.
It should be 30 denier. Single yarn denier
When it exceeds 5.0 denier, the number of filaments decreases, and the texture of the obtained knitted fabric becomes hard, which is not good. If it is less than 1 denier, the knitted fabric becomes too soft and knitting becomes difficult. Preferred is 2-4 denier. By using such a high-strength polyamide fiber, sufficient strength can be obtained even if the thickness of the yarn is reduced. For example, even if the yarn thickness is 20 denier, the breaking strength and tear strength are 40% of those of the conventional polyamide multifilament yarn.
A value equivalent to denier is obtained. Further, the breaking elongation (dry elongation) of the high-strength polyamide fiber is 30% or more, the elongation of the obtained knitted fabric is high, and the yarn breakage during knitting does not occur. If it is less than 30%, the elongation rate of the knitted fabric will be poor, it will be unsuitable for foundations, swimwear, etc., thread breakage will occur during knitting, and productivity will also be poor. Polyamide that constitutes the polyamide-based synthetic fiber multifilament yarn is, for example, polycaprolactam (nylon 6), polyhexamethyleneadipamide (nylon 66), polyhexamethylenesepacamide (nylon 610), polytetramethyleneadipamide. (Nylon 46), copolymers of these polyamides and 1,4
-Polyamides containing the condensation product of cyclohexanebis (methylamine) and linear aliphatic dicarboxylic acid. A matting agent, a pigment, a light stabilizer, a heat stabilizer, an antioxidant, an antistatic agent, a dyeability improver or an adhesion improver can be added to such a polyamide, if necessary. The polyamide-based synthetic fiber may be used as a filament yarn, or may be used as a textured yarn by performing false twisting processing under normal false twisting conditions.
ゴム状弾性繊維糸としては天然ゴム、合成ゴムあるいは
ポリウレタン系合成繊維糸、ブタジエンラバー繊維糸、
ポリエステル系弾性繊維糸などが含まれるが、好ましい
のはポリウレタン系合成繊維糸である。ポリウレタン系
合成繊維糸としてはポリエステルジオール、ポリエーテ
ルジオール、ポリカーボネートジオールのようなポリマ
ージオールとポリイソシアネートおよび低分子鎖伸長
剤、所望により末端停止剤を反応させて得られるポリウ
レタンエラストマーが例示される。また、カバリンフ
糸、裸糸のいずれでもよいが、好ましくは裸糸である。
また、ゴム状弾性繊維糸はトータルデニールが同じで
も、それを構成する単糸デニールの太さを細くすると、
原糸自体の伸度は低下するが、伸長時の応力は増加する
ので、高応力化が好ましい。しかしながら、弾性糸の製
造時の操業性などを加味すると、トータルデニールが2
0〜280デニール、単糸デニールが3〜15デニー
ル、破断伸度が350%以上のフイラメントであること
が必要である。トータルデニールが20デニール未満で
は、得られる生地の伸縮力が少なすぎ実用的でなく、ま
た、トータルデニールが280デニールを超えると本考
案の主目的である薄地化の妨げとなる。また、破断伸度
が350%未満では、得られる生地の伸縮性が少なくな
り実用的でない。好ましい破断伸度は350〜500%
である。As the rubber-like elastic fiber yarn, natural rubber, synthetic rubber or polyurethane synthetic fiber yarn, butadiene rubber fiber yarn,
Polyester-based elastic fiber threads are included, but polyurethane-based synthetic fiber threads are preferable. Examples of polyurethane-based synthetic fiber yarns include polyurethane elastomers obtained by reacting a polymer diol such as polyester diol, polyether diol, and polycarbonate diol with a polyisocyanate, a low molecular chain extender, and optionally a terminal terminating agent. Further, either Kabarinfu yarn or bare yarn may be used, but bare yarn is preferred.
In addition, even if the rubber-like elastic fiber yarn has the same total denier, if the thickness of the single yarn denier that constitutes it is reduced,
Although the elongation of the raw yarn itself is lowered, the stress at the time of elongation is increased, and therefore it is preferable to increase the stress. However, the total denier is 2 when the operability at the time of manufacturing the elastic yarn is added.
It is necessary that the filament is 0 to 280 denier, the single yarn denier is 3 to 15 denier, and the breaking elongation is 350% or more. When the total denier is less than 20 denier, the stretchable force of the obtained fabric is too small to be practical, and when the total denier exceeds 280 denier, the thinning which is the main purpose of the present invention is hindered. Further, if the breaking elongation is less than 350%, the stretchability of the obtained fabric is reduced, which is not practical. Preferred breaking elongation is 350-500%
Is.
尚、本考案において、相対粘度および破断強度は次の方
法によって測定した値をいう。In the present invention, the relative viscosity and the breaking strength are values measured by the following methods.
相対粘度
96.3±0.1重量%の試薬特級濃硫酸中に重合体濃度が1
0mg/mlになるように試料を溶解させてサンプル溶液を
調整し、20℃±0.05℃の温度で水落下秒数6〜7秒の
オストワルド粘度計を用い、溶液相対粘度を測定する。
測定に際し、同一の粘度計を用い、サンプル溶液を調整
した時と同じ硫酸20mlの落下時間T0(秒)と、サン
プル溶液20mlの落下時間T1(秒)に比より、相対粘
度RVを下記の式を用いて算出する。Polymer concentration is 1 in concentrated reagent grade sulfuric acid with relative viscosity 96.3 ± 0.1% by weight.
The sample solution is prepared by dissolving the sample to 0 mg / ml, and the relative viscosity of the solution is measured at a temperature of 20 ° C. ± 0.05 ° C. using an Ostwald viscometer with a water drop time of 6 to 7 seconds.
In the measurement, using the same viscometer, the relative viscosity RV is calculated from the ratio of the drop time T 0 (second) of 20 ml of sulfuric acid and the drop time T 1 (second) of 20 ml of the sample solution, which are the same as when the sample solution was adjusted. It calculates using the formula of.
RV=T1/T0
破断強度
原糸1本の状態で東洋ボールドウイン製テンシロンによ
り測定する。(g/d)
上記した如きポリアミド系合成繊維マルチフイラメント
糸とゴム状弾性糸とをそれぞれ筬に配してトリコット経
編地を編成するが、必要により吸湿性繊維糸を加えたた
て編地であってもよい。吸湿性繊維糸としては、綿、羊
毛、麻など天然繊維からなる紡績糸、またはレーヨン、
キュプラ、アセテートなどの紡績糸が好ましい。また、
品質、操業性繊維のため、双糸使いが好ましい。トリコ
ットタイプの編組織としては従来使われている編組織が
使用できるが、好ましくはダブルデンビー、ハーフコー
ドタイプがよい。また、ファンデーション、ショーツ用
などの用途では、必要に応じ、前述の地組織に綿糸など
吸湿性繊維糸を挿入した組織が望ましい。更に、ゴム状
弾性糸のトータルデニールは20〜70デニールが好ま
しい。編成時の条件、染色加工条件などは従来の方法が
そのまま活用できる。RV = T 1 / T 0 Break strength Measured with Tensilon manufactured by Toyo Baldwin in the state of one original yarn. (G / d) A polyamide-based synthetic fiber multifilament yarn and a rubber-like elastic yarn as described above are arranged on a reed to knit a tricot warp knitted fabric, but a hygroscopic fiber yarn is added to the warp knitted fabric if necessary. May be As the hygroscopic fiber yarn, spun yarn made of natural fibers such as cotton, wool and hemp, or rayon,
Spun yarns such as cupra and acetate are preferred. Also,
The use of twin yarn is preferred because of its quality and operability. As the tricot type knitting structure, a knitting structure which has been conventionally used can be used, but a double denby type or a half cord type is preferable. In addition, in applications such as foundations and shorts, a structure in which a hygroscopic fiber yarn such as cotton yarn is inserted into the above-mentioned ground structure is desirable if necessary. Further, the total denier of the rubber-like elastic yarn is preferably 20 to 70 denier. Conventional methods can be used as they are for knitting conditions, dyeing processing conditions, and the like.
(実施例)
以下、実施例により本考案を説明するが、本考案はこれ
に拘束されるものではない。(Example) Hereinafter, the present invention will be described with reference to examples, but the present invention is not limited thereto.
実施例、比較例1および比較例2
第1表に示す糸使い、編条件によって編地を編成し、得
られた生機を染色加工して仕上げた。加工工程は次の通
りである。Example, Comparative Example 1 and Comparative Example 2 A knitted fabric was knitted according to the knitting conditions and the yarns shown in Table 1, and the obtained raw fabric was dyed and finished. The processing steps are as follows.
リラックス→脱水→プレセット→精練漂白→湯洗→染色
→湯洗→仕上げセット
得られた編地の性質は第2表に示す通りであった。Relaxation → dehydration → presetting → scouring bleaching → hot water washing → dyeing → hot water washing → finishing set The properties of the obtained knitted fabric were as shown in Table 2.
第2表から明らかなように、本考案である実施例は厚み
が薄いにもかかわらず、実用上合格とされている破裂強
度を有し、このため、編地の用途に制約を受けることが
ない。また、伸長率も大きい。 As is clear from Table 2, the embodiment of the present invention has a burst strength which is considered to be practically acceptable, though the thickness thereof is thin, and therefore, the use of the knitted fabric may be restricted. Absent. The expansion rate is also high.
なお、実施例中の物性の測定は次のように行なった。The physical properties in the examples were measured as follows.
1.破裂強度:JIS L−1018A法 (ミューラレン形法)に準拠する。1. Bursting strength: JIS L-1018A method Complies with (Mullaren method).
2.厚み:DIAL THICKNESS GAUGEを使用する。2. Thickness: Use DIAL THICKNESS GAUGE.
3.伸長力、伸長率
・インストロン形引張試験機使用
下降速度 30±2cm/min
・試験片:2.5cm×16.0cmの試験片を、たて、よこ、方
向にそれぞれ2枚採取して使用
・伸長力:試験片を引張間隔10cmとして引張試験機に
取り付け、機械を操作し、伸長率80%時の応力を読み
とる。2回の平均値を示す。3. Elongation force, elongation rate-Instron type tensile tester Descent rate 30 ± 2cm / min-Test piece: 2.5cm x 16.0cm test piece, 2 pieces each in vertical, horizontal and direction are used and extended Force: A test piece is attached to a tensile tester with a tension interval of 10 cm, the machine is operated, and the stress at an elongation rate of 80% is read. The average value of 2 times is shown.
・伸長率:伸長力測定と同様に試験片を取り付け機械を
操作し、2.25kg荷重時の伸度を読みとる。2回の平均値
を示す。-Extension rate: Attach the test piece and operate the machine in the same way as the extension force measurement, and read the extension rate under a load of 2.25 kg. The average value of 2 times is shown.
(考案の効果)
本考案の伸縮性たて編地は薄地であり、しかも破裂強度
が大きく、伸長率の大きいものであった。(Effect of the Invention) The stretchable warp knitted fabric of the present invention is a thin fabric, and has a high burst strength and a high elongation rate.
第1図はこの考案の実施例の意匠図である。 A:ナイロン繊維糸 B:スパンデックス糸 C:綿糸 FIG. 1 is a design diagram of an embodiment of the present invention. A: Nylon fiber yarn B: Spandex yarn C: cotton thread
Claims (1)
てなることを特徴とする伸縮性トリコット経編地。 A糸:単糸1〜5デニール、トータル10〜30デニー
ル、相対粘度(RV)2.5〜4.0、破断強度(DT)7.0
〜10.0g/d、破断伸度30%以上のポリアミド系合成繊
維マルチフィラメント糸。 B糸:単糸3〜15デニール、トータル20〜280デ
ニール、破断伸度350%以上のゴム状弾性繊維糸。1. A stretchable tricot warp knitted fabric comprising at least the following A yarn and B yarn. Yarn A: Single yarn 1 to 5 denier, total 10 to 30 denier, relative viscosity (RV) 2.5 to 4.0, breaking strength (DT) 7.0
Polyamide-based synthetic fiber multifilament yarn having a breaking elongation of 30% or more up to 10.0 g / d. B yarn: A rubber-like elastic fiber yarn having a single yarn of 3 to 15 denier, a total of 20 to 280 denier, and a breaking elongation of 350% or more.