JPH06172693A - Emulsion blue ink for mimeographic printing - Google Patents
Emulsion blue ink for mimeographic printingInfo
- Publication number
- JPH06172693A JPH06172693A JP35210392A JP35210392A JPH06172693A JP H06172693 A JPH06172693 A JP H06172693A JP 35210392 A JP35210392 A JP 35210392A JP 35210392 A JP35210392 A JP 35210392A JP H06172693 A JPH06172693 A JP H06172693A
- Authority
- JP
- Japan
- Prior art keywords
- blue
- oil
- emulsion
- phthalocyanine blue
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】[0001]
【産業上の利用分野】本発明は孔版印刷用エマルション
青インキに関し、詳しくは赤味の青色であり且つ高温保
存安定性に優れた孔版印刷用エマルション青インキに関
する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an emulsion blue ink for stencil printing, and more particularly to an emulsion blue ink for stencil printing which is reddish blue and has excellent high temperature storage stability.
【0002】[0002]
【従来の技術】孔版印刷方法は、周知のように孔版印刷
原紙を用い、この原紙の穿孔部を介して原紙の一方の側
より他方の側へインキを移動させることにより、紙など
の被印刷物面に印刷を行なうものである。近年、輪転孔
版印刷機にもマイクロコンピューター等による自動化が
進み、操作が簡単になってきており、これに伴い様々な
環境で印刷開始直後から良好な印刷物を入手できること
が要望されている。2. Description of the Related Art As is well known, a stencil printing method uses a stencil printing base paper, and by moving ink from one side of the base paper to the other side through a perforation portion of the base paper, a printing material such as paper is printed. Printing is performed on the surface. In recent years, a rotary stencil printing machine has become more automated by a microcomputer or the like and has become easier to operate, and accordingly, it is desired that a good printed matter can be obtained immediately after starting printing in various environments.
【0003】一方、保管条件も夏期のテント内や輸出の
際の船積みなど、高温にさらされることがあり、その際
のインキの安定性が問題となっている。従来、エマルシ
ョン青インキの顔料としては、鮮やかな赤味の青色で着
色力が大きいα型Cuフタロシアニンブルー(C.I.
Pigment Blue15)が好まれているが、該
顔料には、有機溶剤系で使用した場合結晶成長や転移を
起こし、着色力低下や流動性を著しく低下させるという
問題点がある。この点を解決するために、β型Cuフタ
ロシアニンブルー(C.I.Pigment Blue
15:3)やε型Cuフタロシアニンブルー(C.I.
Pigment Blue15:6)、顔料の表面処理
(C.I.Pigment Blue15:2)、塩素
置換(C.I.Pigment Blue15:1)の
ように、様々な方法が用いられているが、β型Cuフタ
ロシアニンブルー及び塩素置換では、インキの色相が黄
味の青色に代わってしまい鮮やかな赤味の青色が得られ
ず、またε型Cuフタロシアニンブルー及び顔料の表面
処理ではインキの色相、結晶成長や転移に関しては問題
はないが、高価であるという欠点がある。On the other hand, the storage conditions are sometimes exposed to high temperatures such as in summer tents and shipping during export, and the stability of the ink at that time is a problem. Conventionally, as a pigment for emulsion blue ink, α-type Cu phthalocyanine blue (C.I.
Pigment Blue 15) is preferred, but the pigment has a problem that when it is used in an organic solvent system, it causes crystal growth and transition, resulting in a decrease in coloring power and a marked decrease in fluidity. In order to solve this point, β-type Cu phthalocyanine blue (C.I. Pigment Blue)
15: 3) and ε-type Cu phthalocyanine blue (C.I.
Pigment Blue 15: 6), surface treatment of pigment (CI Pigment Blue 15: 2), chlorine substitution (CI Pigment Blue 15: 1), but β-type Cu When phthalocyanine blue and chlorine are substituted, the hue of the ink is changed to yellowish blue and a vivid reddish blue color cannot be obtained. Also, the surface treatment of ε-type Cu phthalocyanine blue and pigments causes the hue of the ink, crystal growth and transition. There is no problem with regard to, but it has the drawback of being expensive.
【0004】[0004]
【発明が解決しようとする課題】従って、本発明の目的
は、前記従来技術の欠点を除去し、輪転孔版印刷機にお
いて、エマルション高温(50〜70℃)安定性に優
れ、しかも赤味の青色である孔版印刷用エマルション青
インキを提供することにある。SUMMARY OF THE INVENTION Therefore, an object of the present invention is to eliminate the above-mentioned drawbacks of the prior art and to provide emulsions having excellent stability at high temperatures (50 to 70 ° C.) and a reddish blue color in a rotary printing press. Another object of the present invention is to provide an emulsion blue ink for stencil printing.
【0005】[0005]
【課題を解決するための手段】本発明によれば、油相約
10〜50重量%と水相約90〜50重量%とからなる
油中水型エマルションからなり、しかも前記油相中の青
顔料として、α型フタロシアニンブルーとβ型フタロシ
アニンブルーとを含有してなることを特徴とする孔版印
刷用エマルション青インキが提供され、また該青インキ
において、前記β型フタロシアニンブルー顔料の全顔料
に対する含有割合が、下記式(I)を満足するものであ
ることを特徴とする孔版印刷用エマルション青インキが
提供され、更に該青インキにおいて、前記油相中の有機
溶剤として、パラフィン系オイルを含有してなることを
特徴とする孔版印刷用エマルション青インキが提供され
る。 Y≧100/X+5 (I) 但し、式中Y及びXは以下の数値を表わす。 Y:全使用顔料に対するβ型フタロシアニンブルーの割
合(%) X:有機溶剤の粘度(40℃cSt)According to the present invention, a water-in-oil emulsion comprising about 10 to 50% by weight of an oil phase and about 90 to 50% by weight of an aqueous phase is used, and as a blue pigment in the oil phase. An emulsion blue ink for stencil printing is provided which comprises α-type phthalocyanine blue and β-type phthalocyanine blue, and in the blue ink, the content ratio of the β-type phthalocyanine blue pigment to all pigments is An emulsion blue ink for stencil printing is provided which satisfies the following formula (I), and further comprises a paraffinic oil as the organic solvent in the oil phase in the blue ink. An emulsion blue ink for stencil printing is provided. Y ≧ 100 / X + 5 (I) However, in the formula, Y and X represent the following numerical values. Y: Ratio of β-type phthalocyanine blue to all used pigments (%) X: Viscosity of organic solvent (40 ° C cSt)
【0006】本発明者らは、前記目的を達成するため、
種々研究の結果、油中水型エマルションの油相中の青顔
料として、特定の2種類の顔料を併用することで、赤味
の青色で且つ高温保存安定性に優れたものとなり、特に
その両顔料の使用比率を特定範囲に設定することで高温
保存安定性をより確実にするという効果を見出し、また
使用する有機溶媒としてはパラフィン系オイルが好まし
いことを見出した。本発明はそれらに基づいてなされた
ものである。[0006] The present inventors have
As a result of various studies, by using two specific pigments in combination as the blue pigment in the oil phase of the water-in-oil emulsion, a reddish blue color and excellent high temperature storage stability were obtained. The inventors have found that the use ratio of the pigment is set in a specific range to ensure the high temperature storage stability, and that the paraffinic oil is preferable as the organic solvent to be used. The present invention is based on them.
【0007】以下、本発明を更に詳細に説明する。本発
明の孔版印刷用エマルション青インキは、油相約10〜
50重量%と水相約90〜50重量%とからなる油中水
型エマルションからなるが、前記油相は、顔料成分、有
機溶剤(油成分)、樹脂、乳化剤等から構成され、また
前記水相は、水、電解質、防腐・防かび剤、酸化防止
剤、水蒸発防止剤、水溶性高分子等から構成される。こ
れらの構成成分には、エマルションの形成を阻害しない
公知のものが使用される。The present invention will be described in more detail below. The emulsion blue ink for stencil printing of the present invention has an oil phase of about 10 to 10.
A water-in-oil emulsion comprising 50% by weight and an aqueous phase of about 90 to 50% by weight, wherein the oil phase is composed of a pigment component, an organic solvent (oil component), a resin, an emulsifier, etc. Is composed of water, electrolyte, antiseptic / antifungal agent, antioxidant, water evaporation inhibitor, water-soluble polymer and the like. Known constituents that do not inhibit the formation of emulsion are used as these constituents.
【0008】本発明のエマルション青インクにおいて
は、油相中の青顔料成分として、α型Cuフタロシアニ
ンブルー(C.I.Pigment Blue15)と
β型Cuフタロシアニンブルー(C.I.Pigmen
t Blue15:3)とが併用される。このことによ
り、有機溶剤中への分散を行なっても、着色力の低下や
流動特性の低下が発生せず、赤味の青色で且つ保存安定
性に優れたものとなる。また、この両顔料の使用比率
を、前記式(I)を満足する範囲とすることによって、
より確実に高温保存安定性を向上させたものとなる。In the emulsion blue ink of the present invention, α-type Cu phthalocyanine blue (CI Pigment Blue 15) and β-type Cu phthalocyanine blue (CI Pigmen) are used as blue pigment components in the oil phase.
t Blue 15: 3). As a result, even if the pigment is dispersed in an organic solvent, the coloring power and the fluidity are not deteriorated, and it is reddish blue and has excellent storage stability. In addition, by setting the use ratio of both pigments to a range that satisfies the above formula (I),
The storage stability at high temperature is more reliably improved.
【0009】本発明で用いられる油相中の有機溶剤とし
ては、パラフィン系オイルが好ましいが、通常使用され
ている凸版印刷用、オフセット印刷用、スクリーン印刷
用等の有機溶剤、及びナフテン系オイルでもよく、例え
ば、流動パラフィン、スピンドル油、軽油、灯油、マシ
ン油、潤滑油等の鉱物油;オリーブ油、ナタネ油、ヒマ
シ油、大豆油等の植物油等が使用される。また、本発明
においては合成油も使用できる。合成油を使用する場
合、種々の化合物が利用できる。代表的な合成ビヒクル
には、ポリイソブチレン類、水素化ポリデセン類、トリ
メチロールプロパンエステル類、ネオペンチルエステル
及びペンタエリトリトールエステル、ジ(2−エチルヘ
キシル)セバケート、ジ(2−エチルヘキシル)アジペ
ート、ジブチルフタレート、フルオロカーボン類、珪素
エステル類、シラン類、リン含有酸類のエステル類、液
体尿素、フェロセン誘導体類、水素化合成油類、鎖状ポ
リフェニル類、シロキサン類及びシリコン類(ポリシロ
キサン類)、ブチル置換ビス(p−フェノキシフェニ
ル)エーテル類に代表されるアルキル置換ジフェニルエ
ーテル類、フェノキシフェニルエーテル類などが挙げら
れる。As the organic solvent in the oil phase used in the present invention, a paraffinic oil is preferable, but a commonly used organic solvent for letterpress printing, offset printing, screen printing, etc., and naphthenic oil are also usable. Often, for example, mineral oils such as liquid paraffin, spindle oil, light oil, kerosene, machine oil and lubricating oil; vegetable oils such as olive oil, rapeseed oil, castor oil and soybean oil are used. Also, synthetic oils can be used in the present invention. When using synthetic oils, various compounds are available. Representative synthetic vehicles include polyisobutylenes, hydrogenated polydecenes, trimethylolpropane esters, neopentyl esters and pentaerythritol esters, di (2-ethylhexyl) sebacate, di (2-ethylhexyl) adipate, dibutyl phthalate, Fluorocarbons, silicon esters, silanes, esters of phosphorus-containing acids, liquid urea, ferrocene derivatives, hydrogenated synthetic oils, chain polyphenyls, siloxanes and silicons (polysiloxanes), butyl-substituted bis Examples thereof include alkyl-substituted diphenyl ethers represented by (p-phenoxyphenyl) ethers and phenoxyphenyl ethers.
【0010】インキと紙との固着性、油相中の顔料の分
散性等の向上を目的として、油相中に樹脂が使用される
が、その例としては、フェノール樹脂、マレイン酸樹
脂、石油樹脂、アルキド樹脂、ゴム誘導体樹脂等が挙げ
られ、これらは単独であるいは2種類以上組み合わせ用
いられる。A resin is used in the oil phase for the purpose of improving the adhesion between the ink and the paper and the dispersibility of the pigment in the oil phase. Examples of the resin include phenol resin, maleic acid resin and petroleum. Resins, alkyd resins, rubber derivative resins and the like can be mentioned, and these can be used alone or in combination of two or more kinds.
【0011】本発明で用いられる乳化剤は、好ましくは
非イオン系界面活性剤であり、例えば、ソルビタン高級
脂肪酸エステル、ポリオキシエチレンソルビタン高級脂
肪酸エステル、脂肪酸モノグリセリド、脂肪酸ジグリセ
リド及び高級アルコール、アルキルフェノール、脂肪酸
等の酸化エチレン付加物等が挙げられる。これらを単独
であるいはHLBの異なるものを2種以上組み合わせて
安定性の高いエマルションを調製する。The emulsifier used in the present invention is preferably a nonionic surfactant, for example, sorbitan higher fatty acid ester, polyoxyethylene sorbitan higher fatty acid ester, fatty acid monoglyceride, fatty acid diglyceride and higher alcohol, alkylphenol, fatty acid, etc. And the ethylene oxide adduct thereof. These are used alone or in combination of two or more having different HLB to prepare a highly stable emulsion.
【0012】また、本発明で用いられる水相中の蒸発防
止剤兼凝結防止剤としては、エチレングリコール、ソル
ビトール、グリセリンなど多価アルコールや、ポリエチ
レングリコール等が用いられる。防腐・防かび剤として
は、例えば、芳香族ヒドロキシ化合物及びその塩素化合
物、サリチル酸、フェノール酸、p−オキシ安息香酸メ
チル、p−オキシ安息香酸エチル等、ソルビン酸、デヒ
ドロ酢酸等が用いられる。As the evaporation inhibitor and anti-caking agent in the aqueous phase used in the present invention, polyhydric alcohols such as ethylene glycol, sorbitol and glycerin, polyethylene glycol and the like are used. Examples of the antiseptic / antifungal agent include aromatic hydroxy compounds and chlorine compounds thereof, salicylic acid, phenolic acid, methyl p-oxybenzoate, ethyl p-oxybenzoate, sorbic acid, dehydroacetic acid and the like.
【0013】水相中で用いられる水溶性高分子として
は、例えば、デンプン、マンナン、アルギン酸ソーダ、
ガラクタン、トラガントガム、アラビアガム、ブルラ
ン、デキストラン、キサンタンガム、ニカワ、ゼラチ
ン、コラーゲン、カゼイン等の天然高分子;キルボキシ
メチルセルロース、メチルセルロース、ヒドロキシエチ
ルセルロース、ヒドロキシプロピルセルロース、ヒドロ
キシプロピルメチルセルロース、ヒドロキシメチルデン
プン、カルボキシメチルデンプン、ジアルデヒドデンプ
ン等の半合成高分子;アクリル酸樹脂及びポリアクリル
酸ナトリウム、ポリアクリル酸トリエタノールアミンな
どのアクリル酸樹脂誘導体、ポリビニルアルコール、ポ
リビニルピロリドン、ポリアクリルアミド、ポリエチレ
ンオキサイド、ポリビニルメチルエーテルなどの合成高
分子等が用いられる。Examples of the water-soluble polymer used in the aqueous phase include starch, mannan, sodium alginate,
Natural polymers such as galactan, tragacanth gum, gum arabic, vullan, dextran, xanthan gum, glue, gelatin, collagen, casein; kilvoxymethylcellulose, methylcellulose, hydroxyethylcellulose, hydroxypropylcellulose, hydroxypropylmethylcellulose, hydroxymethylstarch, carboxymethyl Semi-synthetic polymers such as starch and dialdehyde starch; acrylic acid resins and sodium polyacrylate, acrylic acid resin derivatives such as polyacrylic acid triethanolamine, polyvinyl alcohol, polyvinylpyrrolidone, polyacrylamide, polyethylene oxide, polyvinyl methyl ether, etc. The synthetic polymer and the like are used.
【0014】本発明のエマルション青インキの調製に当
っては、油相は、通常公知の分散機で前記顔料を分散さ
せ、それを有機溶剤あるいはその他の油相組成物で稀釈
する。稀釈には通常、公知の撹拌機が使用される。水相
には、水相組成物が通常、撹拌機により混合される。出
来上がった油相、水相は、通常公知の乳化機を使用し、
容易に乳化される。分散、稀釈、乳化等の製造方法、手
段は適宜変更できる。In the preparation of the emulsion blue ink of the present invention, the oil phase is prepared by dispersing the pigment in a generally known disperser and diluting it with an organic solvent or another oil phase composition. A known stirrer is usually used for the dilution. The aqueous phase composition is usually mixed with the stirrer in the aqueous phase. The finished oil phase and water phase are usually obtained by using a known emulsifier,
Emulsified easily. The manufacturing method and means such as dispersion, dilution, and emulsification can be changed as appropriate.
【0015】[0015]
【実施例】以下、実施例により本発明を更に詳細に説明
するが、本発明はこれらに限定されるものではない。な
お、以下に示す部及び%はいずれも重量基準である。The present invention will be described in more detail with reference to the following examples, but the present invention is not limited thereto. The parts and% shown below are based on weight.
【0016】実施例1 以下に示される処方の原料を使用した。 (顔料) α型Cuフタロシアニンブルー 4.5部 β型Cuフタロシアニンブルー 1.5部 (乳化剤) ソルビタンセスキオレエート 5部 (溶剤) パラフィン系オイル 16部 (水) イオン交換水 34.17部 (凍結防止剤) エチレングリコール 10.00部 (水溶性高分子) 1%ポリアクリル酸水溶液 28.00部 (増粘剤) 10%水酸化ナトリウム水溶液 0.83部 註)全使用顔料に対するβ型Cuフタロシアニンの割
合:25% オイル粘度:121cStExample 1 The raw materials having the formulations shown below were used. (Pigment) α-type Cu phthalocyanine blue 4.5 parts β-type Cu phthalocyanine blue 1.5 parts (Emulsifier) sorbitan sesquioleate 5 parts (solvent) Paraffin oil 16 parts (water) Ion exchange water 34.17 parts (antifreeze) ethylene glycol 10.00 Parts (water-soluble polymer) 1% polyacrylic acid aqueous solution 28.00 parts (thickener) 10% sodium hydroxide aqueous solution 0.83 parts Note) Ratio of β-type Cu phthalocyanine to all pigments used: 25% Oil viscosity: 121 cSt
【0017】顔料分散体の調整はCuフタロシアニンブ
ルー、パラフィン系オイル及び界面活性剤、更に場合に
よりアルキド樹脂を3本ロールで練肉することで行な
い、続いてオイルと顔料分散体、また、必要に応じてロ
ジン変性フェノール樹脂等のゲルワニスを少量加え、こ
れらを均一に混合撹拌機で混合したものを油相とした。
また、水相の調製は、アクリル酸ポリマーを水に一晩浸
漬し、これにエチレングリコールを加えた後、撹拌しな
がら増粘剤である水酸化ナトリウム水溶液を加えること
によって行ない、増粘したものを水相とした。次に、上
記油相に上記水相を加え乳化することによって、孔版印
刷用エマルション青インキを得た。The pigment dispersion is prepared by kneading Cu phthalocyanine blue, paraffin oil and a surfactant, and optionally an alkyd resin with three rolls, followed by oil and pigment dispersion, and if necessary. Accordingly, a small amount of gel varnish such as rosin-modified phenol resin was added, and these were uniformly mixed with a mixing stirrer to obtain an oil phase.
The aqueous phase was prepared by immersing the acrylic acid polymer in water overnight, adding ethylene glycol to it, and then adding an aqueous sodium hydroxide solution, which is a thickener, with stirring to increase the viscosity. Was used as the water phase. Next, the water phase was added to the oil phase and emulsified to obtain an emulsion blue ink for stencil printing.
【0018】実施例2〜7及び比較例 表1に記載した処方で実施例1と同様な方法で孔版印刷
用エマルション青インキを得た。また、表1に全使用顔
料に対するβ型Cuフタロシアニンの割合、有機溶剤の
種類、有機溶剤の粘度も記載した。Examples 2 to 7 and Comparative Example Using the formulation shown in Table 1, the emulsion blue ink for stencil printing was obtained in the same manner as in Example 1. Table 1 also shows the ratio of β-type Cu phthalocyanine to all the pigments used, the type of organic solvent, and the viscosity of the organic solvent.
【0019】(評価)以上のインキを用い、70℃の環
境下に保存し、ビスコテスター(リオン社製)(23
℃)にて測定し、粘度上昇の割合を高温保存安定性とし
て評価した。その結果を表1に示す。(Evaluation) The above inks were used and stored in an environment of 70 ° C., and the viscotester (manufactured by Rion) (23)
C.) and the rate of increase in viscosity was evaluated as the high temperature storage stability. The results are shown in Table 1.
【0020】[0020]
【表1】 注)○:70℃、7日後の粘度上昇の割合が1.4倍未満 △:70℃、7日後の粘度上昇の割合が1.4倍以上、2.0倍
未満 ×:70℃、7日後の粘度上昇の割合が2.0倍以上、2.5倍
未満 ××:70℃、7日後の粘度上昇の割合が2.5倍以上[Table 1] Note) ○: The rate of increase in viscosity after 70 ° C, 7 days is less than 1.4 times △: The rate of increase in viscosity after 70 ° C, 7 days is 1.4 times or more and less than 2.0 times ×: The rate of increase in viscosity after 70 ° C, 7 days Is 2.0 times or more and less than 2.5 times XX: The ratio of increase in viscosity after 70 days at 70 ° C is 2.5 times or more
【0021】[0021]
【発明の効果】請求項1の孔版印刷用エマルション青イ
ンキは、油中水型エマルションの油相中の青顔料とし
て、α型フタロシアニンブルーとβ型フタロシアニンブ
ルーとを含有するものとしたことから、有機溶剤中への
分散を行なっても、着色力の低下や流動性の低下が発生
せず、赤味の青色であって且つ高温保存安定性に優れた
ものである。The emulsion blue ink for stencil printing according to claim 1 contains α-type phthalocyanine blue and β-type phthalocyanine blue as the blue pigment in the oil phase of the water-in-oil emulsion. Even if it is dispersed in an organic solvent, the coloring power and the fluidity are not deteriorated, it is reddish blue and excellent in high temperature storage stability.
【0022】請求項2の孔版印刷用エマルション青イン
キは、前記β型フタロシアニンブルー顔料の全顔料に対
する含有割合を前記式(I)を満足するものとしたこと
から、高温保存安定性の向上をより確実にするという効
果が加わる。In the emulsion blue ink for stencil printing according to claim 2, since the content ratio of the β-type phthalocyanine blue pigment to the total pigment satisfies the above formula (I), the high temperature storage stability is further improved. The effect of ensuring is added.
【0023】請求項3の孔版印刷用エマルション青イン
キは、前記油相中の有機溶剤としてパラフィン系オイル
を含有するものとしたことから、高温保存安定性が更に
向上したものとなるという効果が加わる。Since the emulsion blue ink for stencil printing according to claim 3 contains the paraffinic oil as the organic solvent in the oil phase, there is an additional effect that the high temperature storage stability is further improved. .
───────────────────────────────────────────────────── フロントページの続き (72)発明者 成田 昌宏 宮城県柴田郡柴田町大字中名生字神明堂3 番地の1 東北リコー株式会社内 (72)発明者 大田 真之 宮城県柴田郡柴田町大字中名生字神明堂3 番地の1 東北リコー株式会社内 (72)発明者 浅田 啓介 宮城県柴田郡柴田町大字中名生字神明堂3 番地の1 東北リコー株式会社内 ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Inventor Masahiro Narita 1 in 3 Shinmeidou, Nakameisei, Shibata-cho, Shibata-gun, Miyagi Prefecture Tohoku Ricoh Co., Ltd. 1 Tohoku Ricoh Co., Ltd., 1 of 3 Shinjyodo, Tohoku Ricoh Co., Ltd. (72) Keisuke Asada In 1 Tohoku Ricoh Co., Ltd., 3rd address, Shinmeidou, Shibata-cho, Shibata-gun, Miyagi Prefecture
Claims (3)
50重量%とからなる油中水型エマルションからなり、
しかも前記油相中の青顔料として、α型フタロシアニン
ブルーとβ型フタロシアニンブルーとを含有してなるこ
とを特徴とする孔版印刷用エマルション青インキ。1. An oil phase of about 10-50% by weight and an aqueous phase of about 90-.
A water-in-oil emulsion consisting of 50% by weight,
Moreover, an emulsion blue ink for stencil printing, characterized in that it contains α-type phthalocyanine blue and β-type phthalocyanine blue as the blue pigment in the oil phase.
顔料に対する含有割合が、下記式(I)を満足するもの
であることを特徴とする請求項1に記載の孔版印刷用エ
マルション青インキ。 Y≧100/X+5 (I) 但し、式中Y及びXは以下の数値を表わす。 Y:全使用顔料に対するβ型フタロシアニンブルーの割
合(%) X:有機溶剤の粘度(40℃cSt)2. The emulsion blue ink for stencil printing according to claim 1, wherein the content ratio of the β-type phthalocyanine blue pigment with respect to all pigments satisfies the following formula (I). Y ≧ 100 / X + 5 (I) However, in the formula, Y and X represent the following numerical values. Y: Ratio of β-type phthalocyanine blue to all used pigments (%) X: Viscosity of organic solvent (40 ° C cSt)
ン系オイルを含有してなることを特徴とする請求項1又
は2に記載の孔版印刷用エマルション青インキ。3. The emulsion blue ink for stencil printing according to claim 1, wherein a paraffinic oil is contained as an organic solvent in the oil phase.