JPH0228625B2 - Futoeki - Google Patents
FutoekiInfo
- Publication number
- JPH0228625B2 JPH0228625B2 JP25285885A JP25285885A JPH0228625B2 JP H0228625 B2 JPH0228625 B2 JP H0228625B2 JP 25285885 A JP25285885 A JP 25285885A JP 25285885 A JP25285885 A JP 25285885A JP H0228625 B2 JPH0228625 B2 JP H0228625B2
- Authority
- JP
- Japan
- Prior art keywords
- antifreeze
- corrosion
- test
- sodium
- glycol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
(産業上の利用分野)
本発明は液冷式内燃機関の冷却水の凍結防止に
使用するグリコール類、水および腐食抑制剤とか
らなる不凍液に関する。さらに詳しくは自動車エ
ンジンの冷却液として、凍結防止の他に、防錆、
防食等の自動車エンジンの冷却系統の機能維持に
効果を発揮する不凍液に関するものである。 (従来の技術) 従来、液冷式内燃機関、たとえば自動車エンジ
ンの冷却液は寒期の凍結を防止するためアルコー
ル類またはグリコール類を主剤とし、これに各種
の腐食抑制剤を添加して不凍性および防食性を兼
ね備えた不凍液が使用されている。 (発明が解決しようとする問題点) 一般的に使用されるアルコール類としてはメチ
ルアルコール、エチルアルコール、イソプロピル
アルコール等が、グリコール類としてはエチレン
グリコール、プロピレングリコール、ヘキシレン
グリコール、グリセリン等が単独あるいは混合し
て用いられている。これらの中で特にモノエチレ
ングリコールを主剤とする不凍液が自動車エンジ
ンの冷却系統の冷却液として使用される。 モノエチレングリコール水溶液の場合、30容量
%で−15.5℃、50容量%で−37.0℃までの凍結防
止効果が得られる。 アルコール類またはグリコール類は空気と接触
することにより酸化され、酸性のアルコール類ま
たはグリコール類の酸化物が生成する。50〜100
℃の高温度の条件ではアルコール類またはグリコ
ール類の酸化物の生成は、なおいつそう促進され
る。この酸性のアルコール類またはグリコール類
は内燃機関の冷却系統、特に自動車エンジンを構
成する各種金属の腐食を著しく促進する。内燃機
関の冷却系統を構成する各種金属の腐食は腐食生
成物析出付着による熱伝導率の低下あるいはラジ
エーター管部の閉塞等が起りエンジンのオーバー
ヒートを起こす原因となる。 アルコール類またはグリコール類を主成分とす
る不凍液はアルコール類またはグリコール類その
ものに防食効果がないため腐食抑制剤が添加され
る。 防食剤としては、ホウ砂、亜硝酸ソーダ、リン
酸、硅酸塩、安息香酸ナトリウム、メルカプトベ
ンゾチアゾールのナトリウム塩、ベンゾトリアゾ
ール、メチルベンゾトリアゾール、トリエタノー
ルアミン、ジエタノールアミン、モノエタノール
アミン、トリイソプロパノールアミン、ジイソプ
ロパノールアミン、モノイソプロパノールアミ
ン、シクロヘキシルアミン、エチレンジアミン、
ヒドラジン、ピリジン、モルホリン等から選ばれ
る少なくとも一種添加したものが使用される。こ
れらの中で代表的なものは、ホウ砂、トリエタノ
ールアミンのリン酸塩、安息香酸ソーダ、亜硝酸
ソーダおよびケイ酸ソーダを挙げることができ
る。ホウ砂は鋳鉄製エンジンの防食剤として有効
とされ多用されてきたが、近年省資源、省エネル
ギーのために自動車部品の軽量化に伴いアルミニ
ウム部品が採用されるに及びアルミニウム材質に
対する防食性に欠点を有することが問題となつて
きた。 ホウ砂が添加されたエチレングリコール水溶液
は、自動車エンジンの冷却系統に使用された場
合、エンジンのシリンダーヘツドやシリンダーブ
ロツクの材質であるアルミ合金を腐食し、その腐
食生成物がラジエーターを閉塞することが知られ
ている。 一方、トリエタノールアミンのリン酸塩は鉄系
及びアルミニウム材に対して防食性が優れ、ホウ
砂に代る防食剤として使用されてきたがその後ト
リエタノールアミンと亜硝酸塩の共存によりニト
ロソアミンを生成するという報告がなされてお
り、アミン類と亜硝酸塩の共存を避けることが望
ましい。また、安息香酸ソーダは単独ではこれら
防食剤に代るだけの効果は期待できない。 これに対してケイ酸ソーダも腐食抑制剤として
有効であるが、長時間の貯蔵中にケイ酸ソーダが
ゲル化分離しやすいという問題がある。 即ち、本発明の目的とするところは、アミン類
を含まない組成物にて特にアルミニウム防食性に
優れた不凍液を提供することにある。そして本発
明者らは鋭意検討の結果、グリコール類および水
とからなる不凍液において、 (A) リン酸類、 (B) 芳香族多塩基酸類、 (C) モリブデン酸塩またはタングステン酸塩、 (D) 防食剤および (E) 一般式(1) H(OA)oOH …(1) (ただし、AはC2〜C3のアルキレン基、n
は2〜10の数)で示されるポリグリコール を含有し、PHが6.5〜9.0の範囲であることにより
本発明の目的を達成することができた。 (問題点を解決するための手段) 本発明はグリコール類および水とからなる不凍
液において、 (A) リン酸類、 (B) 芳香族多塩基酸類、 (C) モリブデン酸塩またはタングステン酸塩、 (D) 防食剤および (E) 一般式(1) H(OA)oOH …(1) (ただし、AはC2〜C3のアルキレン基、n
は2〜10の数)で示されるポリグリコール を含有し、PHが6.5〜9.0の範囲であることを特徴
とする不凍液に関するものである。 本発明のリン酸類としては、リン酸およびその
塩類が挙げられる。正リン酸のほかにリチウム、
ナトリウム、カリウム等のアルカリ金属の第1〜
第3塩を用いることができる。添加量は不凍液の
原液に対して0.1〜5.0重量%、好ましくは0.5〜
3.0重量%である。 本発明の芳香族多塩基酸類としては、フタル
酸、イソフタル酸、テレフタル酸、ヘミメリツト
酸、トリメリツト酸、トリメシン酸、ピロメリツ
ト酸等のベンゼン多カルボキシル基置換体を用い
ることができる。また、これらの芳香族多塩基酸
の塩も使用できる。芳香族多塩基酸類の添加量は
0.05〜1.0重量%、好ましくは0.1〜0.5重量%であ
る。 本発明のモリブデン酸塩およびタングステン酸
塩としては、ナトリウム塩、カリウム塩等のアル
カリ金属塩が用いられる。モリブデン酸塩および
タングステン酸塩の添加量は不凍液の原液に対し
0.10〜1.0重量%、好ましくは0.3〜0.7重量%であ
る。 本発明の防食剤としては、亜硝酸塩、硝酸塩、
ケイ酸塩、バナジン酸バナジン酸塩、安息香酸ソ
ーダ、p−ターシヤリブチル安息香酸ソーダ、メ
ルカプトベンゾチアゾールソーダ、メチルベンゾ
トリアゾール、ベンゾトリアゾール等から選ばれ
る少なくとも一種添加したものが使用される。こ
れらの中で代表的なものは、硝酸塩、メルカプト
ベンゾチアゾールソーダ、メチルベンゾトリアゾ
ール、安息香酸ソーダを挙げることができる。防
食剤の添加量は不凍液の原液に対し0.05〜7.0重
量%、好ましくは0.1〜5.0重量%である。 本発明の一般式(1) H(OA)oOH …(1) (ただし、AはC2〜C3のアルキレン基、n
は2〜10の数)で示されるポリグリコール としてはジエチレングリコール、トリエチレング
リコール、テトラエチレングリコール、ポリエチ
レングリコール(平均分子量200〜300)、トリプ
ロピレングリコール、ポリプロピレングリコール
(平均分子量200〜400)、エチレングリコールまた
はジエチレングリコールのエチレンオキシドおよ
びプロピレンオキシド付加物(ランダムまたはブ
ロツク)およびこれらの混合物が挙げられる。こ
れらのうちで好ましいものはジエチレングリコー
ル、トリエチレングリコール、テトラエチレング
リコール、ポリエチレングリコール(平均分子量
200〜300)である。 本発明の一般式(1) H(OA)oOH …(1) (ただし、AはC2〜C3のアルキレン基、n
は2〜10の数)で示されるポリグリコール の添加量は不凍液の原液に対し1〜30重量%、好
ましくは5〜15重量%の範囲である。 不凍液のPH調整は通常の塩基性物質が使用でき
るが、好ましくはリチウム、ナトリウム、カリウ
ム等のアルカリ金属の水酸化物が用いられる。必
要に応じてリン酸等の酸性物質も使用できる。PH
の調整範囲としては6.5〜9.0、好ましくは7.0〜
8.0である。PHがこの範囲より高いとアルミニウ
ムに対する防食性が劣り、低い場合には鉄の腐食
が起こるため、上記範囲内に調整すべきである。 本発明の不凍液はシリコンオイル、鉱油、アル
コール、高級脂肪酸エステル等の消泡剤およびス
ケール防止剤を添加することができる。 (作 用) 本発明の不凍液は後述する実施例および比較例
の結果より明らかな如く、グリコール類および水
とからなる不凍液において、 (A) リン酸類、 (B) 芳香族多塩基酸類、 (C) モリブデン酸塩またはタングステン酸塩、 (D) 防食剤および (E) 一般式(1) H(OA)oOH …(1) (ただし、AはC2〜C3のアルキレン基、n
は2〜10の数)で示されるポリグリコール を含有し、PHが6.5〜9.0の範囲であることにより
アルミニウムに対する腐食防止効果が著しく改善
されるものである。 本発明の不凍液は後述する実施例および比較例
の結果より明らかな如く、グリコール類および水
とからなる不凍液において、各配合成分は必須で
ある。各配合成分はつぎの作用がある。 (A) リン酸類 :アルミニウムおよび鉄の耐蝕性を改善させ
る。 (B) 芳香族多塩基酸類 :PHの上昇を抑制することができる。 (C) モリブデン酸塩またはタングステン酸塩 :アルミニウムおよび鉄の耐蝕性を改善させ
る。 (D) 防食剤 :金属全体の防食性能を向上させる。 (E) 本発明の一般式(1) H(OA)oOH …(1) (ただし、AはC2〜C3のアルキレン基、n
は2〜10の数)で示されるポリグリコール :アルミニウムの耐蝕性が改善され、鉄のピツ
チングが起る問題がない。 本発明の不凍液のPHが6.5〜9.0の範囲にするこ
とによりアルミニウムの耐蝕性が改善され、鉄の
ピツチングが起る問題がない。 (実施例) 次に本発明の不凍液について比較例および実施
例を挙げてさらに詳細に説明するが、本発明はこ
れだけに限定されるものではない。 〔A〕 金属腐食試験方法[JIS−K−2234(不凍
液)] アルミニウム鋳物、鋳鉄、鋼、黄銅、はんだ、
銅の各金属試験片を用い、調合水(硫酸ナトリウ
ム148mg、塩化ナトリウム165mg及び炭酸水素ナト
リウム138mgを蒸溜水1に溶解したもの)で30
容量%に希釈した不凍液に浸し、乾燥空気を100
±10ml/minの流量で送り込みながら、不凍液温
度を88±2℃で336時間保持した。試験前後の各
金属片の質量を測定し質量の変化を求めた。 〔B〕 伝熱面腐食試験方法 (1) 試験装置 円板状のテストピースの上面が不凍液に接
し、下面よりヒーターにて加熱できるように
し、テストピースを介して熱が不凍液の方に移
動するようにした装置で行なつた。 (2) 試験方法 テストピースは、#320耐水研磨紙で平面状
になるように研磨する。 テスト液は蒸留水または純水で25容量%に調
製する。この溶液中には塩素イオンとして
100ppmになるように塩化ナトリウムを加える。 装置に試料を注入した後、空気で0.5Kg/cm2
Gに加圧する。 試験終了後、テストピースは付着沈澱物を除
き、乾燥後精秤する。 (3) 試験条件 テストピース :アルミニウム鋳物 (AC2A) テストピースの温度:135±1℃ 不凍液濃度:25容量%水溶液 不凍液液量:500ml テスト時間:168時間(連続) (4) 試験項目 テストピース外観 テストピースの質量変化 質量の変化は次式から求めた。 C=(m2−m1)/S ここに、 C:質量の変化(mg/cm2) m1:試験前の試験片の質量(mg) m2:試験後の試験片の質量(mg) S:試験前の試験片の全表面積(cm2) 試験後の液相 PH 実施例 1〜7 表−1の配合物を水道水5重量部またはモノエ
チレングリコール95重量部に表−1の配合比にて
溶解し、両液を混合した。 各サンプルについてつぎの試験および測定を行
なつた。 〔A〕 金属腐食試験 〔B〕 伝熱面腐食試験 結果は表−1の通りであつた。 比較例 1〜6 実施例1〜7と同様に表−1の配合比にて調製
したサンプルを試験した。結果は表−1の通りで
あつた。
使用するグリコール類、水および腐食抑制剤とか
らなる不凍液に関する。さらに詳しくは自動車エ
ンジンの冷却液として、凍結防止の他に、防錆、
防食等の自動車エンジンの冷却系統の機能維持に
効果を発揮する不凍液に関するものである。 (従来の技術) 従来、液冷式内燃機関、たとえば自動車エンジ
ンの冷却液は寒期の凍結を防止するためアルコー
ル類またはグリコール類を主剤とし、これに各種
の腐食抑制剤を添加して不凍性および防食性を兼
ね備えた不凍液が使用されている。 (発明が解決しようとする問題点) 一般的に使用されるアルコール類としてはメチ
ルアルコール、エチルアルコール、イソプロピル
アルコール等が、グリコール類としてはエチレン
グリコール、プロピレングリコール、ヘキシレン
グリコール、グリセリン等が単独あるいは混合し
て用いられている。これらの中で特にモノエチレ
ングリコールを主剤とする不凍液が自動車エンジ
ンの冷却系統の冷却液として使用される。 モノエチレングリコール水溶液の場合、30容量
%で−15.5℃、50容量%で−37.0℃までの凍結防
止効果が得られる。 アルコール類またはグリコール類は空気と接触
することにより酸化され、酸性のアルコール類ま
たはグリコール類の酸化物が生成する。50〜100
℃の高温度の条件ではアルコール類またはグリコ
ール類の酸化物の生成は、なおいつそう促進され
る。この酸性のアルコール類またはグリコール類
は内燃機関の冷却系統、特に自動車エンジンを構
成する各種金属の腐食を著しく促進する。内燃機
関の冷却系統を構成する各種金属の腐食は腐食生
成物析出付着による熱伝導率の低下あるいはラジ
エーター管部の閉塞等が起りエンジンのオーバー
ヒートを起こす原因となる。 アルコール類またはグリコール類を主成分とす
る不凍液はアルコール類またはグリコール類その
ものに防食効果がないため腐食抑制剤が添加され
る。 防食剤としては、ホウ砂、亜硝酸ソーダ、リン
酸、硅酸塩、安息香酸ナトリウム、メルカプトベ
ンゾチアゾールのナトリウム塩、ベンゾトリアゾ
ール、メチルベンゾトリアゾール、トリエタノー
ルアミン、ジエタノールアミン、モノエタノール
アミン、トリイソプロパノールアミン、ジイソプ
ロパノールアミン、モノイソプロパノールアミ
ン、シクロヘキシルアミン、エチレンジアミン、
ヒドラジン、ピリジン、モルホリン等から選ばれ
る少なくとも一種添加したものが使用される。こ
れらの中で代表的なものは、ホウ砂、トリエタノ
ールアミンのリン酸塩、安息香酸ソーダ、亜硝酸
ソーダおよびケイ酸ソーダを挙げることができ
る。ホウ砂は鋳鉄製エンジンの防食剤として有効
とされ多用されてきたが、近年省資源、省エネル
ギーのために自動車部品の軽量化に伴いアルミニ
ウム部品が採用されるに及びアルミニウム材質に
対する防食性に欠点を有することが問題となつて
きた。 ホウ砂が添加されたエチレングリコール水溶液
は、自動車エンジンの冷却系統に使用された場
合、エンジンのシリンダーヘツドやシリンダーブ
ロツクの材質であるアルミ合金を腐食し、その腐
食生成物がラジエーターを閉塞することが知られ
ている。 一方、トリエタノールアミンのリン酸塩は鉄系
及びアルミニウム材に対して防食性が優れ、ホウ
砂に代る防食剤として使用されてきたがその後ト
リエタノールアミンと亜硝酸塩の共存によりニト
ロソアミンを生成するという報告がなされてお
り、アミン類と亜硝酸塩の共存を避けることが望
ましい。また、安息香酸ソーダは単独ではこれら
防食剤に代るだけの効果は期待できない。 これに対してケイ酸ソーダも腐食抑制剤として
有効であるが、長時間の貯蔵中にケイ酸ソーダが
ゲル化分離しやすいという問題がある。 即ち、本発明の目的とするところは、アミン類
を含まない組成物にて特にアルミニウム防食性に
優れた不凍液を提供することにある。そして本発
明者らは鋭意検討の結果、グリコール類および水
とからなる不凍液において、 (A) リン酸類、 (B) 芳香族多塩基酸類、 (C) モリブデン酸塩またはタングステン酸塩、 (D) 防食剤および (E) 一般式(1) H(OA)oOH …(1) (ただし、AはC2〜C3のアルキレン基、n
は2〜10の数)で示されるポリグリコール を含有し、PHが6.5〜9.0の範囲であることにより
本発明の目的を達成することができた。 (問題点を解決するための手段) 本発明はグリコール類および水とからなる不凍
液において、 (A) リン酸類、 (B) 芳香族多塩基酸類、 (C) モリブデン酸塩またはタングステン酸塩、 (D) 防食剤および (E) 一般式(1) H(OA)oOH …(1) (ただし、AはC2〜C3のアルキレン基、n
は2〜10の数)で示されるポリグリコール を含有し、PHが6.5〜9.0の範囲であることを特徴
とする不凍液に関するものである。 本発明のリン酸類としては、リン酸およびその
塩類が挙げられる。正リン酸のほかにリチウム、
ナトリウム、カリウム等のアルカリ金属の第1〜
第3塩を用いることができる。添加量は不凍液の
原液に対して0.1〜5.0重量%、好ましくは0.5〜
3.0重量%である。 本発明の芳香族多塩基酸類としては、フタル
酸、イソフタル酸、テレフタル酸、ヘミメリツト
酸、トリメリツト酸、トリメシン酸、ピロメリツ
ト酸等のベンゼン多カルボキシル基置換体を用い
ることができる。また、これらの芳香族多塩基酸
の塩も使用できる。芳香族多塩基酸類の添加量は
0.05〜1.0重量%、好ましくは0.1〜0.5重量%であ
る。 本発明のモリブデン酸塩およびタングステン酸
塩としては、ナトリウム塩、カリウム塩等のアル
カリ金属塩が用いられる。モリブデン酸塩および
タングステン酸塩の添加量は不凍液の原液に対し
0.10〜1.0重量%、好ましくは0.3〜0.7重量%であ
る。 本発明の防食剤としては、亜硝酸塩、硝酸塩、
ケイ酸塩、バナジン酸バナジン酸塩、安息香酸ソ
ーダ、p−ターシヤリブチル安息香酸ソーダ、メ
ルカプトベンゾチアゾールソーダ、メチルベンゾ
トリアゾール、ベンゾトリアゾール等から選ばれ
る少なくとも一種添加したものが使用される。こ
れらの中で代表的なものは、硝酸塩、メルカプト
ベンゾチアゾールソーダ、メチルベンゾトリアゾ
ール、安息香酸ソーダを挙げることができる。防
食剤の添加量は不凍液の原液に対し0.05〜7.0重
量%、好ましくは0.1〜5.0重量%である。 本発明の一般式(1) H(OA)oOH …(1) (ただし、AはC2〜C3のアルキレン基、n
は2〜10の数)で示されるポリグリコール としてはジエチレングリコール、トリエチレング
リコール、テトラエチレングリコール、ポリエチ
レングリコール(平均分子量200〜300)、トリプ
ロピレングリコール、ポリプロピレングリコール
(平均分子量200〜400)、エチレングリコールまた
はジエチレングリコールのエチレンオキシドおよ
びプロピレンオキシド付加物(ランダムまたはブ
ロツク)およびこれらの混合物が挙げられる。こ
れらのうちで好ましいものはジエチレングリコー
ル、トリエチレングリコール、テトラエチレング
リコール、ポリエチレングリコール(平均分子量
200〜300)である。 本発明の一般式(1) H(OA)oOH …(1) (ただし、AはC2〜C3のアルキレン基、n
は2〜10の数)で示されるポリグリコール の添加量は不凍液の原液に対し1〜30重量%、好
ましくは5〜15重量%の範囲である。 不凍液のPH調整は通常の塩基性物質が使用でき
るが、好ましくはリチウム、ナトリウム、カリウ
ム等のアルカリ金属の水酸化物が用いられる。必
要に応じてリン酸等の酸性物質も使用できる。PH
の調整範囲としては6.5〜9.0、好ましくは7.0〜
8.0である。PHがこの範囲より高いとアルミニウ
ムに対する防食性が劣り、低い場合には鉄の腐食
が起こるため、上記範囲内に調整すべきである。 本発明の不凍液はシリコンオイル、鉱油、アル
コール、高級脂肪酸エステル等の消泡剤およびス
ケール防止剤を添加することができる。 (作 用) 本発明の不凍液は後述する実施例および比較例
の結果より明らかな如く、グリコール類および水
とからなる不凍液において、 (A) リン酸類、 (B) 芳香族多塩基酸類、 (C) モリブデン酸塩またはタングステン酸塩、 (D) 防食剤および (E) 一般式(1) H(OA)oOH …(1) (ただし、AはC2〜C3のアルキレン基、n
は2〜10の数)で示されるポリグリコール を含有し、PHが6.5〜9.0の範囲であることにより
アルミニウムに対する腐食防止効果が著しく改善
されるものである。 本発明の不凍液は後述する実施例および比較例
の結果より明らかな如く、グリコール類および水
とからなる不凍液において、各配合成分は必須で
ある。各配合成分はつぎの作用がある。 (A) リン酸類 :アルミニウムおよび鉄の耐蝕性を改善させ
る。 (B) 芳香族多塩基酸類 :PHの上昇を抑制することができる。 (C) モリブデン酸塩またはタングステン酸塩 :アルミニウムおよび鉄の耐蝕性を改善させ
る。 (D) 防食剤 :金属全体の防食性能を向上させる。 (E) 本発明の一般式(1) H(OA)oOH …(1) (ただし、AはC2〜C3のアルキレン基、n
は2〜10の数)で示されるポリグリコール :アルミニウムの耐蝕性が改善され、鉄のピツ
チングが起る問題がない。 本発明の不凍液のPHが6.5〜9.0の範囲にするこ
とによりアルミニウムの耐蝕性が改善され、鉄の
ピツチングが起る問題がない。 (実施例) 次に本発明の不凍液について比較例および実施
例を挙げてさらに詳細に説明するが、本発明はこ
れだけに限定されるものではない。 〔A〕 金属腐食試験方法[JIS−K−2234(不凍
液)] アルミニウム鋳物、鋳鉄、鋼、黄銅、はんだ、
銅の各金属試験片を用い、調合水(硫酸ナトリウ
ム148mg、塩化ナトリウム165mg及び炭酸水素ナト
リウム138mgを蒸溜水1に溶解したもの)で30
容量%に希釈した不凍液に浸し、乾燥空気を100
±10ml/minの流量で送り込みながら、不凍液温
度を88±2℃で336時間保持した。試験前後の各
金属片の質量を測定し質量の変化を求めた。 〔B〕 伝熱面腐食試験方法 (1) 試験装置 円板状のテストピースの上面が不凍液に接
し、下面よりヒーターにて加熱できるように
し、テストピースを介して熱が不凍液の方に移
動するようにした装置で行なつた。 (2) 試験方法 テストピースは、#320耐水研磨紙で平面状
になるように研磨する。 テスト液は蒸留水または純水で25容量%に調
製する。この溶液中には塩素イオンとして
100ppmになるように塩化ナトリウムを加える。 装置に試料を注入した後、空気で0.5Kg/cm2
Gに加圧する。 試験終了後、テストピースは付着沈澱物を除
き、乾燥後精秤する。 (3) 試験条件 テストピース :アルミニウム鋳物 (AC2A) テストピースの温度:135±1℃ 不凍液濃度:25容量%水溶液 不凍液液量:500ml テスト時間:168時間(連続) (4) 試験項目 テストピース外観 テストピースの質量変化 質量の変化は次式から求めた。 C=(m2−m1)/S ここに、 C:質量の変化(mg/cm2) m1:試験前の試験片の質量(mg) m2:試験後の試験片の質量(mg) S:試験前の試験片の全表面積(cm2) 試験後の液相 PH 実施例 1〜7 表−1の配合物を水道水5重量部またはモノエ
チレングリコール95重量部に表−1の配合比にて
溶解し、両液を混合した。 各サンプルについてつぎの試験および測定を行
なつた。 〔A〕 金属腐食試験 〔B〕 伝熱面腐食試験 結果は表−1の通りであつた。 比較例 1〜6 実施例1〜7と同様に表−1の配合比にて調製
したサンプルを試験した。結果は表−1の通りで
あつた。
【表】
【表】
(発明の効果)
本発明のグリコール類および水とからなる不凍
液において、 (A) リン酸類、 (B) 芳香族多塩基酸類、 (C) モリブデン酸塩またはタングステン酸塩、 (D) 防食剤および (E) 本発明の一般式(1) H(OA)oOH …(1) (ただし、AはC2〜C3のアルキレン基、n
は2〜10の数)で示されるポリグリコール を含有し、PHが6.5〜9.0の範囲であることにより
アルミニウムに対する腐食防止効果が著しく改善
されるものである。
液において、 (A) リン酸類、 (B) 芳香族多塩基酸類、 (C) モリブデン酸塩またはタングステン酸塩、 (D) 防食剤および (E) 本発明の一般式(1) H(OA)oOH …(1) (ただし、AはC2〜C3のアルキレン基、n
は2〜10の数)で示されるポリグリコール を含有し、PHが6.5〜9.0の範囲であることにより
アルミニウムに対する腐食防止効果が著しく改善
されるものである。
Claims (1)
- 【特許請求の範囲】 1 グリコール類および水とからなる不凍液にお
いて、 (A) リン酸類、 (B) 芳香族多塩基酸類、 (C) モリブデン酸塩またはタングステン酸塩、 (D) 防食剤および (E) 一般式(1) H(OA)oOH …(1) (ただしAはC2〜C3のアルキレン基、nは
2〜10の数)で示されるポリグリコール を含有し、PHが6.5〜9.0の範囲であることを特徴
とする不凍液。