JP7486985B2 - 織編物およびその製造方法 - Google Patents
織編物およびその製造方法 Download PDFInfo
- Publication number
- JP7486985B2 JP7486985B2 JP2020043195A JP2020043195A JP7486985B2 JP 7486985 B2 JP7486985 B2 JP 7486985B2 JP 2020043195 A JP2020043195 A JP 2020043195A JP 2020043195 A JP2020043195 A JP 2020043195A JP 7486985 B2 JP7486985 B2 JP 7486985B2
- Authority
- JP
- Japan
- Prior art keywords
- woven
- fabric
- knitted fabric
- mass
- carbon atoms
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
即ち、本発明は、下記に掲げる(i)~(vi)を要旨とするものである。
(i)ポリエステル系繊維布帛の少なくとも一方の表面に、下記一般式(1)に示すビニル系化合物が重合したビニル系ポリマーからなる被膜Aと、炭素数が6以下のパーフルオロアルキル基を含む共重合体又はアクリル系ポリマーおよび架橋剤を含有する被膜Bとが、この順に積層されてなる織編物であって、
[一般式(1)中、R1及びR2は同一又は異なる水素原子又はメチル基を示し、R3は 炭素数2~5のアルキレン基を示し、nは10以上の整数を示す。]
下記(I)~(III)を満足する、織編物。
(I)JIS L 1096のG法に従って30回洗濯を行い、JIS L1092スプレー法にて測定された撥水性が2級以上である。
(II)JIS L 1096のG法に従って30回洗濯を行い、AATCC118法に 従って測定された撥油性が2.5級以上である。
(III)JIS L 1096のG法に従って30回洗濯を行い、JIS L1094 摩擦帯電圧法に従って測定された制電性が、タテ方向およびヨコ方向の何れについても2 000V以下である。
(ii)前記ビニル系化合物の分子量が600以上である、(i)の織編物。
(iii)織編物の構成繊維の質量に対して、前記ビニル系ポリマーが0.5~5質量% 含まれる、(i)または(ii)の織編物。
(iv)織編物の構成繊維の質量に対して、前記炭素数が6以下のパーフルオロアルキル 基を含む共重合体又はアクリル系ポリマーが0.2~2.0質量%含まれる、(i)~( iii)の何れかの織編物。
(v)(i)~(iv)の何れかの織編物の製造方法であって、ポリエステル系繊維布帛の少なくとも一方の表面に、上記一般式(1)に示すビニル系 化合物、および重合開始剤を含む水溶液を接触させ、次いで蒸気加熱処理を行い、炭素数が6以下のパーフルオロアルキル基を含む共重合体又はアクリル系ポリマーおよ び架橋剤を含む水溶液を浸漬させる、織編物の製造方法。
(vi)前記蒸気加熱処理を行った後、かつ炭素数が6以下のパーフルオロアルキル基を 含む共重合体および架橋剤を含む水溶液を浸漬させる前に、高速液流処理を行う、(v)の織編物の製造方法。
本発明の織編物は、ポリエステル系繊維からなる布帛(本明細書においては、「ポリエステル系繊維布帛」と称する)の少なくとも一方の表面に、下記一般式(1)に示すビニル系化合物が重合したビニル系ポリマーからなる被膜Aと、炭素数が6以下のパーフルオ ロアルキル基を含む共重合体又はアクリル系ポリマーおよび架橋剤を含有する被膜Bとが、この順に積層されてなる。
[一般式(1)中、R1及びR2は同一又は異なる水素原子又はメチル基を示し、R3は 炭素数2~5のアルキレン基を示し、nは10以上の整数を示す。]
このような構成を有することにより、本発明の織編物は、洗濯耐久性に優れた撥水撥油性 、制電性を満足するものとなる。
本発明におけるポリエステル系繊維布帛とは、ポリエチレンテレフタレート、ポリ乳酸、ポリブチレンテレフタレート、ポリプロピレンテレフタレートなどのポリエステル樹脂から得られる繊維(ポリエステル系繊維)を含む布帛である。ポリエステル系繊維布帛は、洗濯耐久性の観点から、該布帛中にポリエステル系繊維を50質量%以上含有するものであることが好ましく、より好ましくは80質量%以上含有するものである。また、ポリエステル系繊維の繊度、フィラメント数、断面形状等は、特に限定されるものではなく、用途等に応じて適宜に選択することができる。
被膜Aはビニル系ポリマーからなるものであり、ビニル系ポリマーは上記一般式(1)に示すビニル系化合物が重合してなるものである。ビニル系ポリマーからなる被膜Aが積層されていることにより、布帛表面が親水化されて本発明の織編物に制電性を付与することができる。
被膜Bは、上記したように炭素数が6以下のパーフルオロアルキル基を含む共重合体と架橋剤とを含有する。
被膜Bは、上記したようにアクリル系ポリマーと架橋剤とを含有する。
アクリル系モノマーとしては、パーフルオロアルキル基を含まない非フッ素系のものが好ましく、中でも下記一般式(3)のようなものが挙げられる。
A1:H、CH3
A2:炭素数1~30の直鎖状または分岐状のアルキル基で示される非フッ素単量体から誘導される繰り返し単位を含む非フッ素アクリル系セグメント
ここで、「(メタ)アクリル酸エステル」とは「アクリル酸エステル」又はそれに対応する「メタクリル酸エステル」を意味し、「(メタ)アクリル酸」、「(メタ)アクリルアミド」等においても同義である。
例えば、架橋剤の固形分80質量%、加工使用量0.3g/L、マングル絞り率60%の場合は、0.8×0.003×0.6×100=0.14(質量%)となる。
(I)JIS L 1096のG法に従って30回洗濯を行い、JIS L1092スプレー法にて評価された撥水性が2級以上であり、3級以上であることが好ましい。これにより、撥水性の洗濯耐久性に優れることの指標となる。
(II)JIS L 1096のG法に従って30回洗濯を行い、AATCC118法に従って評価された撥油性が2.5級以上であり、3級以上であることが好ましい。これにより、撥油性の洗濯耐久性に優れることの指標となる。
(III)JIS L 1096のG法に従って30回洗濯を行い、JIS L1094摩擦帯電圧法に従って評価された制電性が2000V以下であり、1000V以下であることが好ましい。これにより、制電性の洗濯耐久性に優れることの指標となる。
本発明の製造方法は、ポリエステル系繊維布帛の少なくとも一方の表面に、上記一般式(1)に示すビニル系化合物、および重合開始剤を含む水溶液を接触させ、
次いで蒸気加熱処理を行い、
炭素数が6以下のパーフルオロアルキル基を含む共重合体又はアクリル系ポリマーおよび架橋剤を含む水溶液を浸漬させるものである。
1.試料
測定に供すべき試料として、JIS L 1096のG法に従って、30回洗濯をしたもの(以下、「HL30」と称する場合がある)と、当該洗濯前のもの(以下、「初期」と称する場合がある)との2種を用意した。これら2種類の試料について、評価を行った。
JIS L 1096のG法に従って30回洗濯を行い、JIS L1092スプレー法に従って評価した。
JIS L 1096のG法に従って30回洗濯を行い、AATCC118法に従って評価した。
JIS L 1096のG法に従って30回洗濯を行い、JIS L1094摩擦帯電圧法に従って評価した。
ビニル系ポリマーの付着量(質量%)={(W1-W0)/W0}×100
W0:ポリエステル系繊維布帛の単位面積当たりの質量
W1:ビニル系ポリマーが付着したポリエステル系繊維布帛の単位面積当たりの質量
6.パーフルオロアルキル基を含む共重合体又はアクリル系ポリマーの付着量
パーフルオロアルキル基を含む共重合体又はアクリル系ポリマーの付着量(質量%)={(W2-W0)/W0}×100×(W3/1000)×(W4/100)
W0:ポリエステル系繊維布帛の単位面積当たりの質量
W2:パーフルオロアルキル基を含む共重合体又はアクリル系ポリマーが付着したポリエステル系繊維布帛の単位面積当たりの質量
W3:パーフルオロアルキル基を含む共重合体又はアクリル系ポリマーの使用量
W4:パーフルオロアルキル基を含む共重合体又はアクリル系ポリマーの固形分
経糸としてポリエステルマルチフィラメント加工糸(167dtex/48f)を用い、緯糸としてポリエステルマルチフィラメント加工糸(334dtex/96f)を用いて、綾織物(経糸密度:128本/2.54cm、緯糸密度:58本/2.54cm、目付:180g/cm2)を製織した。この綾織物に対して通常の方法で精練し、テンター(市金工業社製)にて190℃で30秒間プレセットを行った。次いで、液流染色機(「サーキュラーMF」、日阪製作所製)を用いて、下記染色処方で、温度130℃、時間30分の条件で染色し、目付220g/m2の白色の綾織物を得た。
<染色処方>
・蛍光染料 1%o.m.f
・酢酸(48%) 0.2cc/l
・水 残部
なお、蛍光染料は、「Hakkol STR」(昭和化学工業社製)を使用した。
<処方1>
NKエステル14G(新中村化学工業社製、上記一般式(1)にて示すビニル系化合物、n=14、分子量736、R1=CH3、R2=CH3、R3=CH2CH2):10g/L
重合開始剤(過硫酸アンモニウム):0.5g/L
水:残部
<処方2>
上記一般式(2)にて示す炭素数6のパーフルオロアルキル基を有する共重合体を含む水溶液:NKガードS-09(日華化学社製、固形分濃度20質量%)50g/L
架橋剤:ベッカミンM-3(大日本インキ社製、N-メチロールメラミン:有効成分濃度(固形分濃度)80質量%)0.3g/L
触媒:キャタリストACX(大日本インキ社製、アミノアルコール塩酸塩:有効成分濃度35質量%)0.1g/L
水:残部
実施例1の処方1の水溶液を、下記処方3の組成に変えた以外は、実施例1と同様におこなった。
<処方3>
NKエステル14G(新中村化学工業社製、上記一般式(1)にて示すビニル系化合物、n=14、分子量736):20g/L
重合開始剤(過硫酸アンモニウム):1.0g/L
水:残部
実施例1の処方1の水溶液を、下記処方4の組成に変えた以外は、実施例1と同様におこなった。
<処方4>
NKエステル23G(新中村化学工業社製、上記一般式(1)にて示すビニル系化合物、n=23、分子量1136、R1=CH3、R2=CH3、R3=CH2CH2):10g/L
重合開始剤(過硫酸アンモニウム):0.5g/L
水:残部
実施例1の処方1の水溶液を、下記処方5の組成に変え、処方2の水溶液を下記処方6に変えた以外は、実施例1と同様におこなった。
<処方5>
NKエステル14G(新中村化学工業社製、上記一般式(1)にて示すビニル系化合物、n=14、分子量736):40g/L
重合開始剤(過硫酸アンモニウム):2.0g/L
水:残部
<処方6>
上記一般式(2)にて示す炭素数6のパーフルオロアルキル基を有する共重合体を含む水溶液:NKガードS-09(日華化学社製、固形分濃度20質量%)60g/L
架橋剤:ベッカミンM-3(大日本インキ社製、N-メチロールメラミン:有効成分濃度(固形分濃度)80質量%)0.3g/L
触媒:キャタリストACX(大日本インキ社製、アミノアルコール塩酸塩:有効成分濃度35質量%)0.1g/L
水:残部
実施例1の処方2の水溶液を、下記処方7の組成に変えた以外は、実施例1と同様におこなった。
<処方7>
上記一般式(2)にて示す炭素数6のパーフルオロアルキル基を有する共重合体を含む水溶液:NKガードS-09(日華化学社製、固形分濃度20質量%)70g/L
架橋剤:ベッカミンM-3(大日本インキ社製、N-メチロールメラミン:有効成分濃度(固形分濃度)80質量%)0.4g/L
触媒:キャタリストACX(大日本インキ社製、アミノアルコール塩酸塩:有効成分濃度35質量%)0.1g/L
水:残部
実施例1の処方1の水溶液をラジカル重合させた後、高速液流処理に代えてロープ洗浄機(木村鉄工所社製)を用いた洗浄とした以外は、実施例1と同様に行った。
実施例1の処方2の水溶液を、下記処方8の組成に変えた以外は、実施例1と同様におこなった。
<処方8>
アクリル系ポリマーを含む水溶液:ユニダインXF-5003(ダイキン社製、固形分濃度30質量%)50g/L
架橋剤:ベッカミンM-3(大日本インキ社製、N-メチロールメラミン:有効成分濃度(固形分濃度)80質量%)0.3g/L
触媒:キャタリストACX(大日本インキ社製、アミノアルコール塩酸塩:有効成分濃度35質量%)0.1g/L
水:残部
実施例2の処方2の水溶液を、下記処方9の組成に変えた以外は、実施例2と同様におこなった。
<処方9>
アクリル系ポリマーを含む水溶液:ユニダインXF-5003(ダイキン社製、固形分濃度30質量%)70g/L
架橋剤:ベッカミンM-3(大日本インキ社製、N-メチロールメラミン:有効成分濃度(固形分濃度)80質量%)0.3g/L
触媒:キャタリストACX(大日本インキ社製、アミノアルコール塩酸塩:有効成分濃度35質量%)0.1g/L
水:残部
実施例1の処方1の水溶液を、下記処方10の組成に変えた以外は、実施例1と同様におこなった。
<処方10>
NKエステル9G(新中村化学工業社製、上記一般式(1)にて示すビニル系化合物、n=9、分子量536、R1=CH3、R2=CH3、R3=CH2CH2):10g/L
重合開始剤(過硫酸アンモニウム):0.5g/L
水:残部
実施例1の処方2の水溶液を、下記処方11の組成に変えた以外は、実施例1と同様におこなった。
<処方11>
上記一般式(2)にて示す炭素数6のパーフルオロアルキル基を有する共重合体を含む水溶液:NKガードS-09(日華化学社製、固形分濃度20質量%)50g/L
水:残部
実施例1の処方1の水溶液をラジカル重合させた後、蒸気加熱処理を行わない以外は、実施例1と同様におこなった。
これに対して、比較例1の織編物においては、上記一般式(1)にて示すビニル系化合物としてn=9であるものを用いたために、撥水撥油性と制電性との何れにも劣るものであった。
比較例2の織編物においては、被膜Bにおいて架橋剤を用いていないために、撥水撥油性に劣るものであった。
比較例3の織編物においては、ビニル系化合物をラジカル重合させた後に、蒸気加熱処理を行わなかったために制電性に劣っていた。
Claims (6)
- ポリエステル系繊維布帛の少なくとも一方の表面に、
下記一般式(1)に示すビニル系化合物が重合したビニル系ポリマーからなる被膜Aと、炭素数が6以下のパーフルオロアルキル基を含む共重合体又はアクリル系ポリマーおよび架橋剤を含有する被膜Bとが、この順に積層されてなる織編物であって、
[一般式(1)中、R1及びR2は同一又は異なる水素原子又はメチル基を示し、R3は炭素数2~5のアルキレン基を示し、nは10以上の整数を示す。]
下記(I)~(III)を満足する、織編物。
(I)JIS L 1096のG法に従って30回洗濯を行い、JIS L1092スプレー法にて測定された撥水性が2級以上である。
(II)JIS L 1096のG法に従って30回洗濯を行い、AATCC118法に従って測定された撥油性が2.5級以上である。
(III)JIS L 1096のG法に従って30回洗濯を行い、JIS L1094摩擦帯電圧法に従って測定された制電性が、タテ方向およびヨコ方向の何れについても2000V以下である。 - 前記ビニル系化合物の分子量が600以上である、請求項1に記載の織編物。
- 織編物の構成繊維の質量に対して、前記ビニル系ポリマーが0.5~5質量%含まれる、請求項1または2に記載の織編物。
- 織編物の構成繊維の質量に対して、前記炭素数が6以下のパーフルオロアルキル基を含む共重合体又はアクリル系ポリマーが0.2~2.0質量%含まれる、請求項1~3の何れか1項に記載の織編物。
- 請求項1~4の何れか1項に記載の織編物の製造方法であって、ポリエステル系繊維布帛の少なくとも一方の表面に、上記一般式(1)に示すビニル系化合物、および重合開始剤を含む水溶液を接触させ、次いで蒸気加熱処理を行い、
炭素数が6以下のパーフルオロアルキル基を含む共重合体又はアクリル系ポリマーおよび架橋剤を含む水溶液を浸漬させる、織編物の製造方法。 - 前記蒸気加熱処理を行った後、かつ炭素数が6以下のパーフルオロアルキル基を含む共重合体又はアクリル系ポリマーおよび架橋剤を含む水溶液を浸漬させる前に、高速液流処理を行う、請求項5に記載の織編物の製造方法。