JP7396514B2 - 熱可塑性樹脂組成物およびそれを用いた成形品 - Google Patents
熱可塑性樹脂組成物およびそれを用いた成形品 Download PDFInfo
- Publication number
- JP7396514B2 JP7396514B2 JP2022561000A JP2022561000A JP7396514B2 JP 7396514 B2 JP7396514 B2 JP 7396514B2 JP 2022561000 A JP2022561000 A JP 2022561000A JP 2022561000 A JP2022561000 A JP 2022561000A JP 7396514 B2 JP7396514 B2 JP 7396514B2
- Authority
- JP
- Japan
- Prior art keywords
- thermoplastic resin
- resin composition
- inorganic particles
- mass
- less
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(1) 屈折率が1.50~2.00のビニル系共重合体(I)を100質量部、粒子径(D50)が1.2~2.8μmの無機粒子(II-1)を2~3質量部、および粒子径(D50)が3.6~6.4μmの無機粒子(II-2)を1~7質量部含み、前記無機粒子(II-1)と無機粒子(II-2)の合計含有量が4~10質量部であり、前記無機粒子(II-1)と無機粒子(II-2)の配合比(II-2)/(II-1)が0.3以上4.0未満である熱可塑性樹脂組成物。
(2) 前記無機粒子の屈折率が1.50~2.00である(1)に記載の熱可塑性樹脂組成物。
(3) さらに、前記熱可塑性樹脂組成物の全光線透過率が55.0~65.0%であり、ヘーズが95~100%である(1)または(2)に記載の熱可塑性樹脂組成物。
(4) さらに、前記熱可塑性樹脂組成物の密度が1100~1140kg/m3である(1)~(3)のいずれかに記載の熱可塑性樹脂組成物。
(5) さらに、前記無機粒子が硫酸バリウムである(1)~(4)のいずれかに記載の熱可塑性樹脂組成物。
(6) さらに、前記ビニル系共重合体(I)の重量平均分子量が80,000~150,000である(1)~(5)のいずれかに記載の熱可塑性樹脂組成物。
(7) (1)~(6)のいずれかに記載の熱可塑性樹脂組成物を成形してなる成形品。
本発明に用いられるビニル系共重合体(I)は、芳香族ビニル系単量体(A)およびシアン化ビニル系単量体(B)の少なくとも一方を共重合して得られるビニル系共重合体であることが好ましい。芳香族ビニル系単量体(A)を共重合することで成形性が向上し好ましい。シアン化ビニル系単量体(B)を共重合することで靭性、耐薬品性が向上し好ましい。
ここで、ビニル系共重合体(I)の屈折率は、JIS K 7142(2014)により測定される屈折率を意味する。
ここで、ビニル系共重合体(I)の重量平均分子量は、ゲルパーミエーションクロマトグラフィー(GPC)で測定されるポリスチレン換算値を言う。測定方法は、後述の実施例で記載の通りである。
本発明の熱可塑性樹脂組成物に含まれる無機粒子(II)は、異なる粒子径(D50)を有する2種類を併用する。光拡散性と光透過性の高位でのバランスのため、無機粒子(II-1)の粒子径(D50)は1.2μm以上2.8μm以下の範囲であり、好ましくは1.4μm以上2.6μm以下の範囲であり、より好ましくは1.4μm以上2.4μm以下の範囲である。無機粒子(II-2)の粒子径(D50)は3.6μm以上6.4μm以下であり、好ましくは3.8μm以上6.2μm以下の範囲であり、より好ましくは4.0μm以上6.0μm以下の範囲である。無機粒子(II)の粒子径(D50)が前記範囲外であった場合、光拡散性と光透過性のバランスが崩れ、光の濃淡(色むら)の発生や、輝度低下が発生するおそれがある。
なお、無機粒子(II)の粒子径はメジアン径(D50)を意味する。
なお、無機粒子(II)の屈折率は、文献から引用した(化学大辞典;共立出版株式会社、昭和37年7月31日初版第1刷発行)。
なお、熱可塑性樹脂組成物の全光線透過率は、熱可塑性樹脂組成物を溶融混錬してペレットを得て、射出成形により厚さ2mmの試験片を成形し、JIS K 7361-1(1997)に準拠して測定される。
なお、熱可塑性樹脂組成物のヘーズは、熱可塑性樹脂組成物を溶融混錬してペレットを得て、射出成形により厚さ2mmの試験片を成形し、JIS K 7136(2000)に準拠して測定される。
なお、熱可塑性樹脂組成物の密度は、熱可塑性樹脂組成物を溶融混錬してペレットを得て、射出成形によりJIS K 7139(2009)に規定される多目的試験片タイプA1を成形し、これを切り出したタイプB2試験片を用いて、ISO1183(2010)に準拠して測定される。
また、本発明の熱可塑性樹脂組成物は、粒子径の異なる無機粒子を特定量かつ特定比率で含むため、成形品において光透過性および光拡散性を高いレベルで両立できる。
下記測定条件にて粒度分布を求め、小粒子側からの体積累積値が全粒子体積の50%になる粒径を粒子径(D50)とした。
装置:レーザ回折・散乱式粒子径分布測定装置(日機装社製、MT3300)
溶媒:0.2質量%ヘキサメタリン酸ナトリウム水溶液
装置内の分散条件:装置内で40W、6分照射
各実施例および比較例により得られたペレットから、シリンダー温度を230℃、金型温度を60℃に設定した射出成形機を用いて、サイズ80mm×80mm×2mmの試験片を成形し、JIS K 7361-1(1997)に準拠して全光線透過率を測定した。
前記全光線透過率測定と同様の試験片を用い、JIS K 7136(2000)に準拠してヘーズを測定した。
各実施例、比較例により得られたペレットについて、ISO1133(2011年版)に準拠して、温度:220℃、荷重:10kg条件でメルトフローレートを測定した。
各実施例および比較例により得られたペレットから、シリンダー温度を230℃、金型温度を60℃に設定した射出成形機を用いて、JIS K 7139(2009)に規定される多目的試験片タイプA1を成形し、これを切り出したタイプB2試験片を用いて、ISO1183(2010)に準拠して密度を測定した。
前記密度と同条件にて成形した多目的試験片タイプA1を切り出したタイプB2試験片を用いて、ISO179/1eA(2010)に準拠してシャルピー衝撃強度を測定した。
前記密度と同条件にて成形した多目的試験片タイプA1を切り出したタイプB2試験片を用いて、ISO75-2(2013)(1.8MPa条件で測定)に準拠して測定した。
下記のより得られたビニル系共重合体(I-1)、(I-2)をそれぞれ80℃で3時間真空乾燥した後、220℃に設定した加熱プレスを用いて厚み約40μmのフィルム状サンプルを作製した。このフィルム状サンプルを試料としてアッベ屈折率計を用い、JIS K 7142(2014)に準拠して屈折率を測定した。なお、測定温度は23℃とした。
無機粒子の屈折率は、文献から引用した(化学大辞典;共立出版株式会社、昭和37年7月31日初版第1刷発行)。
下記により得られたビニル系共重合体(I-1)、(I-2)をそれぞれ約0.03g秤量し、これをテトラヒドロフラン約15gに溶解させ、約0.2質量%の溶液を得た。当該溶液を用いてGPCクロマトグラムから、ポリスチレンを標準物質として換算することにより重量平均分子量を求めた。なお、GPC測定は下記条件により測定した。
・機器:Waters2695
・カラム温度:40℃
・検出器:RI2414(示差屈折率計)
・キャリア溶離液流量:0.3ml/分(溶媒:テトラヒドロフラン)
・カラム:TSKgel SuperHZM-M(6.0mmI.D.×15cm)
TSKgel SuperHZM-N(6.0mmI.D.×15cm)
直列(いずれも東ソー(株)製)。
・標準試料:東ソー製単分散ポリスチレン。
スチレン72質量%とアクリロニトリル28質量%からなる単量体混合物を懸濁重合して得られたスラリーを、洗浄・脱水・乾燥工程を経て、重量平均分子量100,000、屈折率1.57のビニル系共重合体(I)を調製した。
メタクリル酸メチル72質量%、スチレン24質量%、アクリロニトリル4質量%からなる単量体混合物を懸濁重合して得られたスラリーを、洗浄・脱水・乾燥工程を経て、重量平均分子量110,000、屈折率1.52のビニル系共重合体(I)を調製した。
・無機粒子(II-1):硫酸バリウム、粒子径(D50)2μm、屈折率1.64
・無機粒子(II-2):硫酸バリウム、粒子径(D50)5μm、屈折率1.64
・リン系熱安定剤:商品名「アデカスタブPEP-36」、(株)ADEKA製
前記ビニル系共重合体(I)、無機粒子(II)、その他添加剤を下記表に示したとおりの質量比で配合し、スクリュー径30mmの同方向回転の二軸押出機(温度範囲:200~220℃)で溶融混練を行い、ペレットを得た。得られたペレットについて前述の評価を行った。評価結果を下記表1および表2に示す。
なお、全光線透過率は55.0~65.0%であれば良好である。ヘーズは95~100%であれば良好である。
Claims (6)
- 屈折率が1.50~2.00のビニル系共重合体(I)を100質量部、粒子径(D50)が1.2~2.8μmの無機粒子(II-1)を2~3質量部、および粒子径(D50)が3.6~6.4μmの無機粒子(II-2)を1~7質量部含み、
前記無機粒子(II-1)と無機粒子(II-2)の合計含有量が4~10質量部であり、
前記無機粒子(II-1)と無機粒子(II-2)の配合比(II-2)/(II-1)が0.3以上4.0未満である熱可塑性樹脂組成物であって、
前記熱可塑性樹脂組成物の全光線透過率が55.0~65.0%であり、ヘーズが95~100%である熱可塑性樹脂組成物。 - 前記無機粒子(II-1)および前記無機粒子(II-2)の屈折率が1.50~2.00である請求項1に記載の熱可塑性樹脂組成物。
- 前記熱可塑性樹脂組成物の密度が1100~1140kg/m3である請求項1に記載の熱可塑性樹脂組成物。
- 前記無機粒子が硫酸バリウムを含む請求項1に記載の熱可塑性樹脂組成物。
- 前記ビニル系共重合体(I)の重量平均分子量が80,000~150,000である請求項1に記載の熱可塑性樹脂組成物。
- 請求項1~5のいずれか1項に記載の熱可塑性樹脂組成物を成形してなる成形品。